Waste Recycling In The Metallurgical Industry; The Case Of Metal Extraction From Non-Ferrous Smelter Slag Using Aqueous Sulphur Dioxide

Over 2 million tonnes of smelter slags containing Co, Ni and Cu are produced and stockpiled in Canada each year. Smelters also produce SO2 an air pollutant. Recycling these materials will maximize the value of natural resources and minimize possible environmental impacts of industrial operations. The objectives of this research were to understand the characteristics of slag, the reaction of slag with SO2(aq) and to develop a novel method for extracting Co, Ni and Cu from slag using SO2. The properties of slags from different smelters were studied, with emphases on the form of Co, Ni, Cu and Fe. Leaching experiments were carried out in a batch reactor. The parameters investigated included concentration of SO2(aq), stirring speed, particle size, temperature and pH. O2 was introduced into the reactor to study its effect on the system. The amount of each of Co, Ni and Cu in all the slags was less than 1%, while Fe was between 30% and 45%. The form of Co and Fe was primarily oxide, however, significant portions of Ni and Cu were present as sulphides. SO2(aq) alone, was effective in leaching Co and Fe. Cu dissolution was negligible due to precipitation. The presence of O2 improved Cu and Ni extraction. SO2(aq) was found to be more effective in leaching slag than H2SO4 at the same pH. The leaching process was modelled using the shrinking core model. A scheme was proposed for the extraction of Co, Ni and Cu from slag using SO2(aq). The process makes efficient use of SO2, separates Co and Cu at an early stage, and minimizes the consumption of base during Fe separation.