By Maurice L. Pinel, Thomas Wright, Thomas T. Read

The erroneous, but until recently widely prevalent, belief that iron castings were first made in Europe in the fourteenth century has been adequately refuted in a number of earlier papers;1, ll, l² but except for an unpublished metallographic study by the late William Campbell, and a phosphorus analysis by T. A. Wright of the metal of the Han dynasty cast-iron stove described by Laufer,2 nothing was known of either the chemical composition or the metallographic structure of the metal of any ancient iron casting, although data on castings of recent manufacture are abundantly available. The metal of the stove, which had been buried in a grave for at least 15 centuries, was so corroded that it seemed inadvisable to publish the results on it until morc and better specimens from other ancient castings could be obtained. During a journey through China, extending from Peking in the north to Canton in the south and Cheng-tu, Ssu-chuan, in the west, in the late summer and autumn of 1936, one of us (T. T. Read) was fortunate enough to obtain, and bring home for study, nine castings, all more than 1000 years old, of which the date of manufacture is precisely known because of inscriptions cast in them, another that lacks a dated inscription, but of which the date, as explained below, can be otherwise established, and a specimen from the largest iron casting ever made," which is also dated. The period covered by this suite of specimens extends from 502 to 1093 A.D. In addition, a sample was obtained from a casting of date unknown, but which was certainly cast before 1000 A.D. and possibly as early as the third century A.D. A detailed description of these specimens is as follows: I. 502 A.D. A pair [right and left) of recumbent lions (Fig. 1). Base 7¼ by 113/8 in., height over-all 5½in, weight 26 Ib. each. The tranblation of the inscription on the base is: "Made on the twenty-fourth day of the seventh month of the third pear of Ching Ming of Great Wei" (Sept. 11, 502 A.D.).

Jan 1, 1938

By Maurice L. Pinel, Thomas Wright, Thomas T. Read

The erroneous, but until recently widely prevalent, belief that iron castings were first made in Europe in the fourteenth century has been adequately refuted in a number of earlier papers;1, ll, l² but except for an unpublished metallographic study by the late William Campbell, and a phosphorus analysis by T. A. Wright of the metal of the Han dynasty cast-iron stove described by Laufer,2 nothing was known of either the chemical composition or the metallographic structure of the metal of any ancient iron casting, although data on castings of recent manufacture are abundantly available. The metal of the stove, which had been buried in a grave for at least 15 centuries, was so corroded that it seemed inadvisable to publish the results on it until morc and better specimens from other ancient castings could be obtained. During a journey through China, extending from Peking in the north to Canton in the south and Cheng-tu, Ssu-chuan, in the west, in the late summer and autumn of 1936, one of us (T. T. Read) was fortunate enough to obtain, and bring home for study, nine castings, all more than 1000 years old, of which the date of manufacture is precisely known because of inscriptions cast in them, another that lacks a dated inscription, but of which the date, as explained below, can be otherwise established, and a specimen from the largest iron casting ever made," which is also dated. The period covered by this suite of specimens extends from 502 to 1093 A.D. In addition, a sample was obtained from a casting of date unknown, but which was certainly cast before 1000 A.D. and possibly as early as the third century A.D. A detailed description of these specimens is as follows: I. 502 A.D. A pair [right and left) of recumbent lions (Fig. 1). Base 7¼ by 113/8 in., height over-all 5½in, weight 26 Ib. each. The tranblation of the inscription on the base is: "Made on the twenty-fourth day of the seventh month of the third pear of Ching Ming of Great Wei" (Sept. 11, 502 A.D.).

Jan 1, 1938

By Charles H. Fulton

There are comparatively few accurate data on the melting-or the freezing-point temperature of metallurgical slags, or on related physical phenomena, such as fluidity near the melting-point, specific heat, latent heat, etc. With the exception of the work of H. 0. Hofman,' and some older work by R. Akerman, P. Gredt, and H. M. Howe, no information is available that is of direct interest to the metallurgist. Hofman's valuable work is the only one that refers to slags produced in the metallurgy of copper and lead. The classic work of J. H. L. Vogt,2 who views slags from the standpoint of physical mixtures (solutions in which the entities are minerals), has opened up a new field in the study of slags, and has placed the investigation of such properties as melting-temperatures, etc., on a rational basis. The recent work of A. L. Day, E. T. Allen, and W. I?. White, of the Carnegie Institution, at Washington, and of European investigators3 on certain systems of silicate minerals confirms the value of the investigation of silicate series from this standpoint, and it is my aim to apply this method to metallurgical slags, in order to gain exact data of value in metallurgy. The work recorded in the present paper is the result of an investigation of reverberatory-furnace slags made for a Western smelting company to determine exactly the influence of change in composition, within comparatively narrow limits, on the melting-point. For a general discussion concerning the mineralogical character of slags and the principles on which this investigation is based, reference should be made to other work: for the subject is too large to be stated in this paper, except very briefly in the following outline:

Jan 1, 1913

By T. E. Eagan, W. R. McCrackin

IN dealing with segregation in babbitt, and its effect on the final cast structure, which is a bearing, it is obviously impossible to cover all of the compositions manufactured. Each composition, of course, will exhibit certain specific types of segregation. However, as examples,, two compositions of babbitt are presented: one a tin-base of well-known analysis and the other a lead-base, which in the past few years has found wide usage. Bearings usually are cast either statically or centrifugally; therefore the effect of these two methods on segregation is presented. EXPERIMENTAL PROCEDURE A slab of babbitt 1/2 in. thick by 5 in. wide and 17 in. long was cast, using a book mold with the long edge vertical. An A.S.T.M. grade 2 babbitt was used (3.5 per cent copper, 7.5 per cent antimony, remainder tin), to which 0.10 per cent tellurium had been added. Unfortunately, no metal without tellurium was available. The mold to hold the babbitt was heated to approximately 300°F., the temperature being judged by the babbitter. The pouring temperature of the babbitt was 875°F. (470°C.). One slab was made by allowing the babbitt to cool without stirring. The other slab was stirred during the entire cooling cycle. This stirring consisted of a vigorous churning or puddling into the mold until complete solidification had taken place. Three samples were removed from these slabs. One was taken at the extreme bottom, another half way to the top, and another at the extreme top, all at the center of the width. Chemical, macroscopic and microscopic examination was made of all samples. Table I shows the chemical analyses obtained at the described positions [ ] in the slab. The analyses show no serious amount of gravity segregation. Microscopic examination from edge to edge of the slab showed little change in structure. From top to bottom there was a progressive coarsening of the grain size in the stirred slab but little change in the slab that was not stirred (Fig. I). No definite exhibit of segregation could be detected. In line with our experimental study on the tin-base babbitts, we cast an almost duplicate slab using A.S.T.M. Alloy No. 15, containing 0.9 to 1.25 per cent tin, 14.75 to 15.5. per cent antimony, 0.80 to 1.25 per cent arsenic and 0.4 per cent copper. The slab was 16 in. long and 3/8 in. thick, cast with the long side vertical. One slab was allowed to cool normally and the other was stirred continually during cooling. The pouring temperature of the babbitt was

Jan 1, 1944

By Herbert H. Uhlig

Although the mechanical properties of high-carbon manganese-iron alloys, particularly the Hadfield manganese steels, have been established, the literature discloses discrepancies in the reported properties for the low-carbon alloys. Hadfieldla summarized the existing data up to 1927, including the investigations of Guillet, Arnold, Strauss, Burgess and Aston, and reported his own values for alloys containing for the most part from 0.06 to 0.I5 per cent carbon. He noted: From these comparisons it wil! be seen that while there is a broad and general agreement as to the character of the alloys at the different manganese percentages, there are disparities in individual cases, especially as regards the degree of toughness or brittleness displayed by an alloy with certain percentages and with particular types of treatment. These differences are not always readily explainable.lb His data showed that alloys containing 4 to 10 per cent manganese water-quenched from Iooo°C. were brittle and hard with maximum brittleness at about 7 per cent. Slight improvement in ductility was obtained with compositions from 10 to 17 per cent manganese. Alloys containing up to 17 per cent manganese slowly cooled rather than quenched from 87o°C., he found, were slightly improved in ductility with significant improvement in alloys analyzing 4.1 and 4.8 per cent manganese. Recently Walters, Kramer and Loring2 reported mechanical properties for alloys made up from electrolytic manganese and ingot iron and containing from 0.02 to 0.04 per cent carbon. They showed that a tempering treatment at 54o°C. (Iooo°F.) for one hour significantly improved the ductility of compositions ranging from 6.7 to &apos; 20.7 per cent manganese. The differences of these compared with Hadfield&apos;s results they considered to originate in this tempering treatment plus the fact that Hadfield&apos;s alloys contained higher carbon and phosphorus (0.06 to 0.I5 per cent C; 0.06 to 0.07 per cent P compared with 0.02 to 0.04 per cent C, <o.ooI per cent P). In this paper it is shown that of the low-carbon alloys (0.02 to 0.03 per cent) containing from 3.3 to 21.5 per cent manganese moderately or rapidly quenched from IOOO°C. some are brittle or ductile, depending on presence or absence of hydrogen. Hydrogen is readily absorbed at high temperatures, and much of it is retained when the alloys are cooled to room temperature. The presence of hydrogen in the range of composition from 10 to 18 per cent manganese is a major factor in determining relative ductility. At 22 per cent manganese, and also at compositions below 10 per cent manganese, factors other than or in addition to hydrogen play a role. These are discussed. Also data are presented to show that hydrogen absorbed by the high-carbon alloys of Hadfield composition is without effect on their mechanical properties.

Jan 1, 1944

By Herbert H. Uhlig

Although the mechanical properties of high-carbon manganese-iron alloys, particularly the Hadfield manganese steels, have been established, the literature discloses discrepancies in the reported properties for the low-carbon alloys. Hadfieldla summarized the existing data up to 1927, including the investigations of Guillet, Arnold, Strauss, Burgess and Aston, and reported his own values for alloys containing for the most part from 0.06 to 0.I5 per cent carbon. He noted: From these comparisons it wil! be seen that while there is a broad and general agreement as to the character of the alloys at the different manganese percentages, there are disparities in individual cases, especially as regards the degree of toughness or brittleness displayed by an alloy with certain percentages and with particular types of treatment. These differences are not always readily explainable.lb His data showed that alloys containing 4 to 10 per cent manganese water-quenched from Iooo°C. were brittle and hard with maximum brittleness at about 7 per cent. Slight improvement in ductility was obtained with compositions from 10 to 17 per cent manganese. Alloys containing up to 17 per cent manganese slowly cooled rather than quenched from 87o°C., he found, were slightly improved in ductility with significant improvement in alloys analyzing 4.1 and 4.8 per cent manganese. Recently Walters, Kramer and Loring2 reported mechanical properties for alloys made up from electrolytic manganese and ingot iron and containing from 0.02 to 0.04 per cent carbon. They showed that a tempering treatment at 54o°C. (Iooo°F.) for one hour significantly improved the ductility of compositions ranging from 6.7 to &apos; 20.7 per cent manganese. The differences of these compared with Hadfield&apos;s results they considered to originate in this tempering treatment plus the fact that Hadfield&apos;s alloys contained higher carbon and phosphorus (0.06 to 0.I5 per cent C; 0.06 to 0.07 per cent P compared with 0.02 to 0.04 per cent C, <o.ooI per cent P). In this paper it is shown that of the low-carbon alloys (0.02 to 0.03 per cent) containing from 3.3 to 21.5 per cent manganese moderately or rapidly quenched from IOOO°C. some are brittle or ductile, depending on presence or absence of hydrogen. Hydrogen is readily absorbed at high temperatures, and much of it is retained when the alloys are cooled to room temperature. The presence of hydrogen in the range of composition from 10 to 18 per cent manganese is a major factor in determining relative ductility. At 22 per cent manganese, and also at compositions below 10 per cent manganese, factors other than or in addition to hydrogen play a role. These are discussed. Also data are presented to show that hydrogen absorbed by the high-carbon alloys of Hadfield composition is without effect on their mechanical properties.

Jan 1, 1944

By William Marsh Baldwin

[Two of the most useful and important equations available to the metallurgist for the study of plastic deformation of metals are the Huber-von Mises-Hencky1-3 and the St. Venant7-10 equations. HUBER-VON MISES-HENCKY EQUATION The Huber-von Mises-Hencky equation answers the question: When does plastic flow occur in metal that is subjected to a multi-axial stress? It occurs, according to this equation, when the three principal stresses,? al, a2, and a3 satisfy the equation: (s1 - s2)2 + (s 2 - s 3)2 + (s 1 ? s3)2 = 2K2 [I] Here K is the yield strength of the material as determined in an ordinary tensile test. If the quantities a1, a2, and a3 are assigned to the coordinates of a Cartesian three-dimensional system, this expression describes a cylinder whose axis of symmetry is inclined at equal angles to the three coordinate axes4,5 (Fig. I). The radius of this cylinder is v2/3K. For the purpose of simplicity, it is sometimes advantageous to ascribe the values s 1/K = si, s 2/K = s2, s 2/K = s3 to the three coordinate axes instead of the principal stress alone. In this case, Eq. I becomes (s1 - S2)2 + (S2 - S3)2 + (Sl - S3)2 = 2 [2] and the radius of the cylinder becomes 2/3v. In the latter method of representation, a point lying inside the cylinder indicates that the metal will react elastically, whereas a point lying on the cylindrical surface indicates that the metal will behave plastically. Some of the geometric features of this cylinder are worthy of study. Let us inquire first as to what interpretation may be placed upon what we will choose to call the "circles of latitude" of the cylinder (L in Fig. I) and the "meridians" of the cylinder (M in Fig. I). Circles of Latitude Circles of latitude are formed by allowing a plane, passing perpendicular to the cylinder axis, to intersect with the cylinder. Any point, P, on this circle is presumed to have the coordinates s1, s2, and s3. The coordinates of the point resulting from the intersection of the plane and the cylinder axis will be a, a, and a (since the cylinder axis is equally inclined to the three coordi¬nate axes). Let us now pass a line through the point on the circle and the point on the axis.]

Jan 1, 1946

The University of Chicago Press, 5750 Ellis Ave , Chicago, Ill This Press publishes books on a wide variety of subjects of scientific interest, as well as several journals Only a few books on geology have been published, however, and the Journal of Geology. The Journal of Geology: A semiquarterly standard American publication in the geological field. $6 per year, single copies, $1, back numbers, within the past five years, $6 per volume Books on geology: The origin of the earth, by T. C Chamberlin, $2 50, Two solar families, by T. C Chamberlin, $2 50, Quantitative classification of igneous rocks, by W. Cross, J. Iddings, L V Pirsson and H. S Washington, $1.75; Studies in minor folds, by C. E. Decker, $1 50; An introduction to the study of ore deposits, by F. H Hatch, $3, A descriptive petrography of the igneous rocks, by A. Johannsen, $4 50, Essentials for the microscopical determination of rock¬forming minerals and rocks, by A. Johannsen (revised ed ) $3, Outlines of geologic history, with special reference to North America, edited by R D. Salisbury, 8150

Jan 1, 1933

New York Meets first Wednesday after first Tuesday of each month. J. E. JOHNSON, JR., Chairman EDGAR RICHARD, Vice-Chairman D. M. LIDDELL, Secretary, 7 Wall St., New York, N. Y. C. A. BOHN, Treasurer JOHN V. N. DORR LEWIS W. FRANCIS Boston Meets first Monday of each winter month. R. L. AGASSIZ, Chairman JAMES G. CARLETON, Vice-Chairman E. E. BUGBEE Secretary-Treasurer, Mass. Inst. of. Technology, Cambridge, Mass. W. E. C. EUSTIS G. A. PACKARD Columbia Holds four sessions during year. Annual meeting in September or October. W. H. LINNEY, Chairman OSCAR LACHMUND, Vice-Chairman LYNDON K. ARMSTRONG, Secretary-Treasurer, P. O. Drawer 2154, Spokane, Wash. STANLY A. EASTON S. SHEDD Puget Sound Meets second Saturday of each month SIMON H. ASH, Chairman I. F. LAUCKS, Vice-Chairman PERCY E. WRIGHT, Secretary-Treasurer, 2012 L. C. Smith Bldg., Seattle. Wash. GLENVILLE A. COLLINS JOHN N. POTT

Jan 11, 1917

By F. Garofalo

It has been shown by various investigators that during constant stress creep the dependence of minimum creep rate, 6,, on stress, o, is given by em = A onat low stress levels, md by 6, = A&apos; exp [ß s] at high stress levels. In these relations A, n, A&apos;, and ß are constant at constant temperature. A single relation has been found which satisfies conditions for both high and low stresses and agrees well with experimental results. This relation is 2, = AN (sinh a s)n, where A" is a constant at constunt temperature and a = p/n. This relation also satisfies the linear relation, 6, = k s, found at temperatures near the melting point at low stresses. EXPERIMENTAL creep results have led to a number of empirical relationships between minimum creep rate, 6,, and the applied stress, s. Under conditions of constant stress it is generally found that at low-stress levels,&apos;-&apos; the dependence of minimum creep rate is given by 6, = Asn. At high-stress levels&apos;74 the experimental results fit the relation, 6, = A&apos; exp [po l. In these relations A, n, A&apos; and ß are constant at constant temperature. A model based on climb-of-edge dislocations from a pile-up array leads to a relation similar to that found experimentally at low stresses.&apos; On the other hand. theories based on chemical-reaction rate,5 nonconservatively moving dislocation jogs, and jog migration and climb-of-edge dislocations4 lead to a relation similar to that found experimentally at high stresses. No difference in mechanism between low and high stress levels has been clearly defined; it is questionable whether such a difference really exists. In any event, the major argument usually given in substantiation of a change in mechanism from low to high stresses is that no single relation exists for defining the stress dependence of the creep rate over wide ranges in stress. However, such a relation has been found and is of the form, dm = A" (sinh a s)n, where A" is a constant at con- stant temperature and a = ß/n. This relation agrees well with experimental results over wide ranges in stress and temperature for copper, aluminum, an A1-3.1 pct Mg alloy, and an austenitic stainless steel. STRESS DEPENDENCE OF MINIMUM CREEP RATE At low stress levels the minimum creep rate, gm, depends on the stress, 0, under conditions of constant stress creep through the relation em=Aon [1] The quantities A and n have been defined previously. In the range in which this relation applies, a linear dependence is found in a log em,-log o plot. Above the stress range of application of relation [I], the minimum creep rate increases much mar; rapidly than predicted by relation [I]. This behavior is shown in Fig. 1 for a series of creep tests on copper4 at various temperatures ranging from 673 o to 973°K. Relation [I] is satisfied at the lower stresses, although the results at 973°K are quite limited. In all cases the transition beyond the applicable range of relation [I] is a gradual one indicating no abrupt change in mechanism. For all test temperatures, values of n have been determined from the results in Fig. 1. These are reported in Table I under Alog tm/hlog o. At high stress levels the stress dependence of minimum creep rate under conditions of constant stress is given by im = A&apos; exp [ß a] 2] All factors have been defined previously. In a log em-0 plot, relation [2] predicts a linear function. Experimentally, a pronounced deviation from the prediction of relation [2] is found at lower stresses. As the stress is lowered, the minimum creep rate decreases more rapidly than predicted by relation [2]. This shown for copper in Fig. 2. Again it is found that the transition from high to low stresses is gradual and no really sharp change is found. Values of p determined from the high stress results are given in Table I. The dependence of minimum creep rate on stress at constant temperature for all ranges in stress

Jan 1, 1963

Jan 1, 1970

By Nicholas J. Grant, Hanna Ibach, Bill C. Giessen

The system Ta-Rh was investigated over the entire comnposition range using metallogvaphic and X-ray techniques as well as thermal analysis. Terminal solubility limits, solidus temperatures, and the crystal structures of two new intermediate phases were determined. There are five intermediate phases: o, tetragonal, isostructural with o(Fe-Cr); a1, orthorhomnbic : a2, orthorhombic, isostructural with CozSi; 0 3, a high -temperature phase of unknozun structure; and a TaRh3, cubic, AuCu3 structure. a, aL, a,, and a melt peritectically; and a TaRh, has a maximum melting point. Five peritectic and one eutectic reactions occur. THE Ta-Rh phase diagram has not been fully treated in the literature; however, two inter metallic phases have been described.&apos;-&apos; This study attempts to work out the diagram covering the details of phase boundaries as well as the crystallography of the intermediate phases. EXPERIMENTAL METHODS Starting materials were tantalum powder of 99.8 pct purity, supplied by National Research Corp., Cambridge, Mass., and rhodium powder of 99.9 pct purity, supplied by Bishop Co., Malvern, Pa. Analyses as given by the manufacturers are presented in Table I. In addition to the spectroscopic analysis, an oxygen analysis has been made of the tantalum powder. After preliminary trials, the standard procedure employed in making the alloys was as follows (see Ref. 4 for further details). The powders were weighed, mixed manually, compacted under 16,000 psi, and arc-melted at not more than 500 amp under thoroughly titanium gettered welding-grade argon of 400 mm Hg pressure. The gettering process was repeated after each melt. It had been shown previously5 that under these conditions no oxygen pick-up exceeding 0.001 pct in a hafnium button could be detected. The buttons, ranging from 5 to 10 g in weight, were inverted or, if possible, crushed and remelted three times. Melting presented no difficulty, except for tantalum-rich al- loys, which showed considerable spashing during melting. The average weight loss of 1 wt pct rose to 2.5 wt pct in these cases. Subsequent melting, however, resulted in losses of less than 0.1 wt pct. The melts obtained frequently showed small in-homogeneities, mostly in the tantalum-rich part of the system below 25 at. pct Rh. This was not due to insufficient blending of the elements, but to crystallization taking place from the cooled bottom. This condition was not improved by further re-melting; therefore the following precautions were taken. Cross sections of as-cast buttons were made. For the investigation only buttons were used where these inhomogeneities did not exceed 1 at. pct (estimated from the amounts of haSeS resent). In addition, only the center portions of such buttdns were utilized to minimize errors. Smaller buttons showed smaller concentration gradients and were used as a check. Finally, all alloys were homogenized to eliminate coring (see below). After this, the error in alloy composition due to inhomogeneity was cl at. pct. In order to confirm the concentrations of the alloys and to provide an impurity check, wet-chemical analyses and oxygen-fusion analyses of four key alloys were carried out. The results, together with the concentrations as calculated with the weight balance method, are presented in Table 11. It was found that for three alloys the agreement is very good (< 0.2

Jan 1, 1964

For the benefit of those of our members who are considerable holders of securities,but owing to their isolated situations are not in close touch with the metropolitan market and current quotations, we are publishing two very interesting graphs, showing the course of the bond and stock markets in New York over a long period. These graphs are furnished through the courtesy of the financial department of the New York Tribune.

Jan 11, 1919

Aalde, Kaare. (&apos;40) Gen&apos;I Del., Bisbee. Ariz. Aase, Glenn D., (&apos;40) Univ. of North Dakota. Grand Forks. N. D. Abadesco, Enrique A., (&apos;39) College of Engrg.. Univ. of the Philippines. Manila, P. I. Abbott. John L., (&apos;40) Colorado School of Mines. Golden. Colo. Abdul-Ahad, A., (&apos;39) Montana School of Mines. Residence Hall, Butte. Mont. Abreu, Ovidio M., (&apos;38) Univ. of Nevada, Reno, Nev. Acomb, Allen. (&apos;41) Louisiana State Univ., Box 1970, University. La. Acosta S., Gonzalo. (&apos;40) Univ. of Texas, Univ. Sta., Box 1785. Austin, Tex. Adam, Howard W., (&apos;41) Montana School of Mines. Butte, Mont. Adams, Albert, (&apos;381 New Mexico School of Mines, Socorro. N. M. Adams. Charles W., (&apos;39) Michigan College of Min. & Tech., Houghton, Mich. Adams. H. Travis, (&apos;39) 316 South -5th St., Bur¬bank. Calif. Adams, Jack L., (&apos;39) Univ. of Oklahoma, Nor¬man. Okla. Adams. John W., (&apos;41) Colorado School of Mines, Golden. Colo. Adams. Lewis J.. (&apos;39) 402 Del Mar Blvd., Corpus Christi, Tex. Adams, Rob L., (&apos;40) Agricultural & Mech. Col¬ lege of Texas. Box 600, College Sta., Tex. Adamson. Charles R., (&apos;41) Univ. of Utah, Salt Lake City. Utah.

Jan 1, 1941

By R. E. Radabaugh, J. M. Brown, J. S. Merchant

The Gilman district is on the northeast flank of the Sawatch Range in central Colorado. It has yielded a total of 10,000,000 tons of ore having a value of over $250,000,000. Paleozoic sediments intruded by a Tertiary quartz latite sill and unconformably overlying Precambrian intrusives and metasediments comprise the country rock of the area. The sediments strike northwesterly and dip 8° to 12° northeasterly. Structures in the Precambrian are related to the Homestake shear zone of the Colorado mineral belt. Only minor folding and faulting occur in the sediments. The principal ore bodies are massive sulfide replacement deposits in carbonate rocks. They consist of long, pipe-like mantos in the completely dolomitized Mississippian Leadville Limestone and funnel-shaped chimneys of copper- silver ore cutting across the Mississippian and Devonian strata. Mineralization is continuous from the chimneys into the mantos. The principal ore bodies are roughly in the shape of a four-tined fork which points up dip. Smaller manto deposits occur in the Cambrian Sawatch Quartzite, and fissure veins are present in the Precambrian rocks. The principal minerals in the mantos are marmatite and galena in a gangue of pyrite and manganosiderite. The chimneys consist of a central core of pyrite with erratically distributed chalcopyrite, tetrahedrite, freibergite, and occasional galena with a shell of zinc ore on the outer margin. Both the chimneys and the mantos are surrounded by imperfect shells of manganosiderite and sanded dolomite. The mineralization is of Laramide age. Hydrothermal alteration affects all rock units to varying degrees. Clay mineral alteration halos occur around the ore bodies. Hydrothermal solutions have developed sanded rock, rubble filled channels, and banded zebra textures, principally in the Leadville Limestone. Structural control of the ore bodies is not well defined. Both the location of the district and the chimneys are probably related to basement structures. The mantos are largely controlled by stratigraphic factors and a pre-Pennsylvanian karst topography in the Leadville Limestone, which were modified by hydrothermal activity, and by weak zones of northeasterly trending faults.

Jan 1, 1968

By Bunting S. Crocker

Bunting S. Crocker (Executive Vice President, Kilborn Engineering Ltd., Toronto, Ont., Canada)-This is an interesting report on laboratory-scale testing with pebble charges in 12-in.-diam mills, and the author correctly concludes that useful laboratory testing can be done. In the opening paragraphs he states, "laboratory pebble-milling tests have been considered too difficult to perform and not relevant enough to the actual grinding situation"!! This is definitely not so! The writer published detailed tests done in a 12-in.-diam mill comparing pebble and steel balls in 1952 6 and again in 1954 7. We note that our review paper in 1963 was the only one mentioned in the References. The author states that "a smooth lining is more frequently used in commercial-scale pebble grinding." The writer has designed some 22 plants treating 134,000 tpd in North America and Australia. He has also visited pebble installations in Norway, Sweden, Finland, and South Africa. All these plants correctly use heavier lifters than would be considered standard for ball mills of a similar size. Smooth liners are not recommended in wet ore treating plants. In the 1952 paper6 it was clearly demonstrated in the test work that the individual ore pebbles had to be the same weight-not the same diameter or size-as the steel balls if comparable grinding results were to be obtained. In the tests performed in this study most of the pebbles "passed 50-mm round hole screen openings and remained on a 40-mm round hole sieve. Correspondingly most of the ball mill experiments were performed with 50 or 40-mm steel balls". Thus, the balls and pebbles were essentially the same size or diameter. This means we are comparing apples and oranges. When the feed being ground is fine enough the pebbles will be superior. When the feed is coarse the steel balls will be the better. This is similar to grinding tests in which two sizes of steel balls are compared. In the middle of the article, "Crocker5 has reported that equal weights of pebbles and steel balls achieve the same grinding capacities under similar conditions …", then he proceeds to question this postulate. In the eight reports that I have published, I have never made this statement. What I have said is "for comparable grinding, the individual pebbles in the mill charge should be the same weight as the individual steel balls." This is not the first time that I have been misquoted on this point! It is most unfortunate that this test work has been done with a ball and pebble of the same diameter and not the same weight. It is impossible to properly evaluate the results. I also regret the fact that the screen analyses of the tests were not shown. Many of us who have been 40 years or less in the grinding game can easily read screen analyses at a glance. We can tell whether the top meshes are being ground by the ball charge, etc., etc. The graphs are fine for the summary or to illustrate conclusions but are often misleading in the report itself. However, we do agree that useful pebble grinding tests can be done in a 12-in. mill.

Jan 1, 1973

By C. P. Kempter, H. L. Brown

Recently Chang determined heat content values of tantalum monocarbide and tungsten monocarbide from 325" to985°Kand 326" to 912"K, respectively, and, using other published data, made certain solid-state calculations for these two compounds. Chang expressed his Cp values in units of cal per "g-atom alloy" OK. We consider this poor usage since l) tantalum monocarbide and tungsten monocarbide are not alloys, and 2) an atom of an alloy does not exist. However, one may convert his values to units of cal per mole OK by merely doubling them. For TaC he calculated a Nernst-Lindemann parameter of 9.07 x lo-&apos; "g-atom per cal". We have refined the calculation of this parameter and have arrived at a much lower value. Rather than approximating the true coefficient of volume expansion, a,, as three times the true coefficient of linear expansion, a, we calculated u, from the TaCo.99, lattice expansion data of Fries and Wahman.38 At 25°C a, = 14.3 x 10s per OC. The molar volume was calculated to be 13.32 cu cm per mole at 25°C. From the lattice compression data of Champion and Drickamer~&apos; for "TaC,.,," we determined the room-temperature compressibility to be 3.5 x 10-l3 sq cm per dyne by plotting l/Vo (aV/ap) vs applied pressure. (Since the lowest pressure at which Champion and Drickamer reported a relative volume was 20 kbars, one may calculate an approximate compressibility only. Chang calculated a compressibility of 3.175 x 10-l3 sq cm per dyne from the same data.) We also used twice Chang&apos;s value of Cp = 4.38 cal per "g-atom alloy" OK for the molar heat capacity at 25°C. From these four values we calculated a Nernst-Lindemann parameter of 5.8 x 10-l4 mole per erg or 2.4 x lo- &apos; mole per cal, and a Cdil value of 2.3 x 10&apos; ergs per mole OK. In the case of tungsten monocarbide no isothermal compressibility has been reported; however, one may calculate an approximate Nernst-Lindemann parameter by using the adiabatic compressibility reported by Brown, Armstrong, and Kempter." Using the WC lattice expansion data of Mauer and Bolz~l we calculated a, to be 12., x l0-&apos; per OC. The molar volume was calculated to be 12.5 cu cm per mole. We used twice Chang&apos;s value of Cp = 4.18 cal per "g-atom alloy" OK for the molar heat capacity at 25°C. From these four values we calculated an approximate Nernst-Lindemann parameter of 2 x lo-&apos; mole per cal, which is much

Jan 1, 1969

By D. M. Davidson, P. F. Kerr

The Permian Cutler Formation in Kane Creek, Utah bears uranium ore in fissure-type vertical veins. This fissure vein formation and its associated host rock bleaching, weak argillic alteration, and base-metal sulfide mineralization along with the development of hydrothermal minerals, a 60 m.y. isotopic Pb/U age, and well-crystallized uraninite&apos;s structural control, give evidence of ore deposition in a hydrothermal environment consistent with Laramide mineralization. Mica polymorph studies indicate first, that temperature during the hydrothermal alteration or subsequent ore deposition did not exceed 200°; hence Cutler deposits are classified telethermal; and secondly, that rock alteration and ore deposition are closely related both in time and space, as is seen in argillic alteration sequence. Ore deposition in an alkaline to slightly acid reducing environment is postulated. Ore textures and mineral associations and distributions also indicate that carbonate complexes may have been transported with the deposing ores. Bleached rock formations are not primary strati-graphic phenomena. Bleaching, or changes in ferric iron content, results from a chemical process involving reduction and conversion of hematite to a soluble aqueous ion. Nearby Chinle bedded deposits (Moss Rack sandstone), containing shale lenses, fossil wood, organic debris and minor fractures, overly the Cutler formation. Chinle ores have a single reported isotopic age of approximately 200 m.y. Their chemical environment is assumed similar to that of the Cutler ores, though slightly more acidic. Two genetic, paradoxically divergent interpretations of the bedded deposits are derived from available spectrographic, petrographic, X-ray and chemical analyses. Kane Springs canyon is located southwest of Moab, Utah, south of the Colorado River and northwest of the Lisbon Valley mining district (Fig. 1). Uranium deposits occur along the northeast flank of a Kane Creek salt anticline where two geologic formations bear ore, the Permian Cutler and the Triassic Chinle. The Cutler deposits&apos; fissure vein formation is an unusual occurrence in the Colorado Plateau. The Chinle deposits appear to be of the normal sedimentary type. Associated with the vein deposits are a number of features, including argillic alteration of sedimentary strata. The minerals of these deposits and their associated features have been studied in detail in a two year program entailing both field and laboratory techniques. STRATIGRAPHY A stratigraphic section of the lithologic units in the Kane Creek area is given in Table I.

Jan 1, 1967

By Ogden Malin

IN conducting the manufacture of extruded brass rods and brass forgings it has been noticed that there is considerable variation in the physical properties, particularly the machinability of different rods and forgings, even though the composition, working temperatures and method of manufacture remain the same. It is the purpose of this paper to attempt to establish the cause and extent of this variation, and also to determine whether variations in composition within certain defined limits influence hardness and machinability to any marked degree. The writer believes that this variation probably is due to the variation in grain size of the metal, therefore the microstructure of several compositions under various conditions of working were examined in an effort to establish this as a fact.

Jan 1, 1932

By William R. Chedsey

ALTHOUGH few changes can be reported in educational methods at the mineral technology schools during 1940, other events have taken place of direct interest to, and that will have a profound effect upon, mineral industry education on the United States. In the erection of new buildings, some notable changes have been made on the campus, The U.S. Bureau of Mines Experiment Station at the University of Utah, Salt Lake City, was dedicated on May 20. The construction and equipment of this building cost between $300,000 and $400,000. It will be the general headquarters for the metallurgical division of the Bureau and will have a pronounced effect upon the mineral industries research program at the University.

Jan 1, 1941