Search Documents

By K. Heindlhofer

Estimates of the "plasticity" of a metal are commonly deduced from three types of test—tensile, torsion and impact. The several results have been more or less at variance, though this disparity has attracted little notice, largely perhaps because they have been expressed in different terms. The discrepancy between the results of the three tests becomes obvious when each is made at a series of low temperatures, for the temperature range within which the "plasticity" of iron largely disappears proves to be very different in the three types of test. The rather abrupt disappearance of "plasticity" of iron within a narrow temperature range cannot be due to any physicochemical change (such as a precipitation) taking place in the material at that time, because the original plasticity is immediately regained when the temperature of the material is brought above the sensitive range. Accordingly this difference in behavior shows that the "plasticity" of a metal depends upon the mode of action of the stresses which produce the deformation, and therefore upon the method of test. Analysis of the stresses leads to the conclusion that the observed plasticity of a metal is determined by the relation between its resistance to rupture by separation and its resistance to shear (slip), on the one hand, and between the effective normal and shearing stresses on the other; and that the relation between the two resistances does not in general remain constant with change of temperature, and may somehow be altered to some extent by the previous treatment of the specimen. This suggests the view that the results of none of the usual mechanical tests are directly comparable even for a single metal tested at a series of temperatures, or for a series of metals at one temperature, because the proportion of the total resistance of the metal to the test contributed by the

Jan 1, 1935

By R. Shuttleworth, R. Smith

A Knudsen effusion tnethod I~as been used lo measure the vapor pressure of pure iron in the temperature range 1000° to 1500°C. Neutron-irradiated , natural iron was used and the Mn'~proclzdced by the (n, p) reaction removed by evaporation at high temperature. The results can be represented by the equation: where pM - 1.088 x 107 atm and T, = 20,890°K. A value of 100.2 kcal per g- atom was obtained for AH;. THE vapor pressure of pure iron in the temperature range 1000" to 1500°C has been measured. Radioactive iron and a Knudsen cell technique were used and the Mn' produced by an (n, p) reaction removed by evaporation at high temperature. From the variation of vapor pressure with temperature values of the enthalpy and entropy of solid iron have been found. Previous workers2 used a Lang-muir method and measurements were made over a smaller temperature range than that in this work. EXPERIMENTAL The apparatus used was similar to that of Pyle and Shuttleworth, and McLellan and Shuttle worth. However, because of the higher temperatures the Knudsen cell was machined from tungsten bar and the flanged furnace tube was beryllia. Heating was by passing a high current (70 amp at 7 v for 1500°K) through a strip of tantalum foil laid across the top of the cell and through a turn of molybdenum wire around the furnace tube. This method of heating ensured that the top of the cell was slightly hotter than the base and prevented condensation and re-evaporation from the orifice. The temperature was measured by means of a pt/Pt 13 pct Rh thermocouple spot-welded to the base of the crucible. To ensure accurate temperature measurement the iron was in the form of a thin disc (0.75 cm diam by 0.075 cm) which lay on the base of the cell. The high-purity iron was irradiated in the Harwell pile for a week at a neutron flux of 1.2 X 10" neutrons per sq cm per sec. The isotopes fe'~ and Fe" are produced by (n! y) reactions but only Fe", half-life 45.1 days, is a emitter; Mn which is also a y emitter, half-life 300 days, is produced simultaneously by an (n,p) reaction.' Immediately after irradiation of natural iron the ratio of ~e" to Mn y activity was 100:l. However, manganese is very much more volatile than iron and almost all the y activity of the condensate is due to Mn'~. Thus it was essential to eliminate all the manganeses before any measurement of the vapor pressure of iron was made and this was done by preliminary heating for 20 hr at 1400°C. For each determination the iron was dissolved from the target with acid and the y activity compared to a known weight of iron. By means of a y-ray spectrometer the y-activity measurements were made at the 1.09-mev peak of the 17e5' spectrum where the background was of the order of 3 cpm. Despite the low specific activity of ~e" a mass of 10- " g of iron could be determined corresponding to a vapor pressure of about l0-'' atm. RESULTS The vapor pressures were calculated from the equation: Where m is the mass of iron effusing in a time t through an orifice of area a2, r is the radius of the target, Z is the distance from the orifice to the

Jan 1, 1965

By E. N. Aqua, C. M. Owens

The microstructure in cold-rolled Zircaloy-4 sheet has been characterized by transmission electron microscopy and X-ray diffraction line-broadening techniques. The rate of work hardening is measured in terms of microstrains, particle sizes, micro hardness, the tensile yield strength. The tensile yield strength of Prestrained (less than 10 pet) Zircaloy-4 sheet is found to be a linear function of the square root of the dislocation density, us predicted by work-hardening theories. ZIRCALOY is one of the most important structural alloys for nuclear reactor applications.''2 In order to understand the effects of the nuclear environment on Zircaloy structural members, the preirradiation microstructure must be characterized. This report will describe the substructure existing in cold-rolled Zircaloy-4 sheet as observed by electron microscopy and by X-ray diffractometry. I) EXPERIMENTAL PROCEDURE Commercial Zircaloy-4 strip was cold-rolled and annealed in argon at 760°C for 1 hr. The annealed sheet was again cold-rolled to a maximum of 50 pct reduction in thickness with segments of the strip being retained after 2.5, 5, 10, and 20 pct reductions. One-inch-square portions were chemically polished (50 parts HNO3, 50 parts H2O, 10 parts HF) and mounted onto lucite blocks using double-sided tape to prevent bending during handling. Thin foils suitable for transmission electron microscopy were prepared from each of the sheet samples. The sheets were mechanically polished through 600-grit paper to a 3 to 4 mil thickness and were chemically polished by immersion for 1 to 2 min in a solution containing: 50 parts HNO3, 50 parts H2O, and 10 parts HF, and rinsed in distilled water. The final metallographic procedure was to electropolish for less than 10 sec with an electrolyte of 10 parts perchloric acid and 90 parts glacial acetic acid, at 20 v, at room temperature using stainless-steel point cathodes and a vigorous stirring action. These foils were examined in a Philips EM 200 electron microscope using a 100-kv accelerating voltage.

Jan 1, 1968

By R. R. Joseph, K. A. Gschneidner

The solid solubility of magnesium in the close-packed modifications of lanthanum, cerium, praseodymium, neodymium, gadolinium, dysprosium, and lutetium was determined from approximately 250°C to the eutectoid temperature by the X-ray parametric technique. The maximum solubility at the eutectoid temperature was found to be 9.4 at. pet in La, 8.2 in Ce, 9.2 in Pr, 8.2 in Nd, 14.1 in Gd, 13.5 in Dy, and 11.5 in Lu. The solubility when compared at a homologous temperature was found to increase in a smooth manner with decreasing size factor from lanthanum to lutetium. It was found that the apparent atomic radius of magnesium when dissolved in the lanthanide solvent was constant and could be accounted for by consideration of several models dealing with departures from Vegard's law. The eutectoid temperatures for the lanthanide-rich La-Mg, Ce-Mg, and Nd-Mg systems were found to be 544", 505°, and 551°c, respectively. A study of the solid solubility of magnesium in the lanthanide metals was initiated because the valency and electron egativity difference are essentially constant and favorable for solid-solution formation, and thus one could examine the effect of size on terminal solid solutions. The size factors based on metal radii range from 14.6 pet for lanthanum to 7.5 pet for lutetium. Since the electronegativity difference is small, 0.06 unit or less, application of the Hume-~othery' and Darken and Gurry2 criteria for solid-solution formation indicates that the solubility of magnesium would be expected to be small for lanthanum (between 5 and 10 at. pet) and to increase as we proceed along the lanthanide series. A search of the literature revealed no data on the solubility of magnesium in the lanthanide metals except for the solubility of magnesium in cerium at 450oCA typical phase diagram for the lanthanide-rich end of the lanthanide-magnesium phase diagram is shown in Fig. 1. EXPERIMENTAL PROCEDURES Preparation of Alloys. The lanthanide metals used in the preparation of alloys for this investigation were prepared from the corresponding fluoride by metallothermic reduction techniques previously described by Daane.4 The chemical analyses of the metals used are listed in Table I.

Jan 1, 1965

By Philip B. Bucky

CONTENTS [PACEPACE r. What Is a Rock Burst?2 4. How Can Rock Bursts Be Predicted? . 35 Jack Spalding2Jack Spalding35 A. F. Robertson 2, 5A. F. Robertson35 W. R. Crane 2A. B. Yates and P. J. Shenon. . . . 35 G. S. Rice 2W. R. Crane 35 P. J. Shenon 2G. S. Rice 35 L. C. Graton 2B. F. Tillson 36 2. What Are the Causes of Rock Bursts? 6 5. How Can Rock Bursts Be Controlled?. 36 Jack Spalding6Jack Spalding36 A. B. Yates and P. J. Shenon . 7, 12, 29A. F. Robertson 36 A. F. Robertson 12, 28W. R. Crane37 W. R. Crane 15A. B. Yates and P. J. Shenon. . . . 37 G. S. Rice 15Oscar Weiss38 Oscar Weiss15G. S. Rice37, 42 P. B. Bucky21R. D. Hoffman42, 43 P. H. Bird 21, 26, 28R. D. Hall 42 M. K. Hubbert26R. H. Cromwell42 G. Wheeler 26. J. Shenon 42 B. F. Tillson26, 28P. B. Bucky42, 44 T. T. Read 27B. F. Tillson 42, 44 A. B. Yates 43, 44 3. How Can Rock Bursts Be Prevented? . 30P. H. Bird 43 Jack Spalding. . . . • . • • • • . 306. General Discussion . A. B. Yates and P. J. Shenon. . . . 31Jack Spalding44 A. F. Robertson32R. D. Parker49 W. R. Crane 35C. Baring Horwood 51 G. S. Rice 35P. B. Bucky 52] FOREWORD THIS symposium brings together points of view, experiences and ideas on rock bursts from a goodly portion of the globe. Some conceptions, particularly those regarding the necessity of depth, have been fairly well shattered, as we find that they are present in the water tunnels of New York, on the surface at marble quarries in Vermont, and in the coal mines of the United States, as well as in the deep mines of the South African and Kolar gold fields, and in the nickel, copper and gold mines of Canada. Their occurrence under such a variety of conditions is, therefore, a challenge,

Jan 1, 1942

By Albert Wiggin

THE copper-bearing sulphide ores from the mines in Butte, Mont., which are for the most part concentrated at the Boston & Montana duction Works in Great Falls and at the Washoe Reduction Works in Anaconda, contain the following minerals of economic value: Chalcocite, Cu2S; enargite, Cu3AsS4; cupriferous pyrite; bornite, Cu3FeS3; covellite, CUS; tetrahedrite, 4 CuS2Sb2S3; and tennantite, Cu8AsS7;. All of the ores carry a high percentage of pyrite. Many of the above sulphides are argentiferous and also carry from 10 to 20 cts. per ton in gold. The gangue is quartz and highly altered granite, with sphalerite and galena and more rarely barite and hubnerite as accessory minerals. An average chemical analysis of the second-class ore concentrated at Great Falls and Anaconda would be as follows: Copper 3.2 to 3.4 per cent. Silver 2. 3 to 3.0 oz. per ton. Gold 0.0-1 to 0.15 oz. per ton. Si02.. 55 to 60 per cent. FeO 12 to 15 per cent.. Sulphur 12 to 1.5 per cent. Al2O3, S to 10 per cent. CaO 0.5 to 0.8 percent. As203, 0.5 to 0.6 percent. Lead 0.2 to 0.3 percent. Before describing the Great Falls flow sleet as installed, at Anaconda, a brief history of the Great Falls concentrator will be given, including a description of the various concentrating machines and systems which have been tested in the search for a flow sheet which would give a higher recovery of copper.

Jan 8, 1913

By R. G. Turner, M. G. Hubbard, A. E. Dukler

Gas phase hydrocarbons produced from underground reservoirs will, in many instances, have liquid phase material associated with them, the presence of which can affect the flowing characteristics of the well. Liquids can come from condensation of hydrocarbon gas (condensate) or from interstitial water in the reservoir matrix. In either case, the higher density liquid phase, being essentially discontinuous, must be transported to the surface by the gas. In the event the gas phase does not provide sufficient transport energy to lift the liquids out of the well, the liquids will accumulate in the wellbore. The accumulation of the liquid will impose an additional back pressure on the formation that can significantly affect the production capacity of the well. In low pressure wells the liquid may completely kill the well; and in the higher pressure wells there can occur a variable degree of slugging or churning of the liquids, which can affect calculations used in routine well tests. Specifically, the calculated bottom-hole pressures used in multirate backpressure tests will be erroneous if the well is not removing liquids on a continuous basis, and gas:liquid ratios observed during such a test may not be correct. Several authors1,3,8,14 have suggested methods to determine if the flow rate of a well is sufficient to remove liquid phase material. Vitter14 and Duggan' proposed that wellhead velocities observed in the field would be adequate for keeping wells unloaded. Jones8 and Dukler3 presented analytical treatments resulting in equations for calculating, from physical properties, the minimum necessary flow rate. An analysis of these studies indicates the existence of two proposed physical models for the removal of gas well liquids: (1) liquid film movement along the walls of the pipe and (2) liquid droplets entrained in the high velocity gas core. Although there probably is a continuous exchange of liquid between the gas core and the film, they will be treated separately for the purposes of this study. The development and comparison of these separate models with experimental data will permit the determination of which, if either, is the controlling mechanism for the removal of liquids from gas wells. The Continuous Film Model Liquid phase accumulation on the walls of a conduit during two-phase gas/liquid flow is inevitable due to the impingement of entrained liquid drops and the condensation of vapors. The movement of the liquid on the wall is therefore of interest in the analysis of liquid removal from gas wells. If the annular liquid film must be moved upward along the walls in order to keep a gas well from loading up, then the minimum gas flow rate necessary to accomplish this is of primary interest. The analysis technique used follows Dukler2 and Hewitt5 and involves describing the profile of the velocity of a liquid film moving upward on the inside of a tube. The minimum rate of gas flow required to move the film upward is then calculated.

Jan 1, 1970

By A. L. Jamieson, H. Rosenthal

The action of mercury on stressed brass to produce cracks was known before Moore, Beckinsale and Mallinson1 showed that actual season cracking did not occur spontaneously but could be induced by ammonia. These investigators studied other substances, including diphenylamine, without finding that anything other than ammonia could cause season cracking Grimston2 reported season cracking in cartridge cases stored in wooden boxes wetted with dilute sulphuric acid pickling solution. Season cracking associated with sulphur dioxide, water vapor and air has been reported by Johnston,3 although he reported that trimethylamine and pyridine did not cause cracking. Jevons4 has ascribed season cracking of brass in certain instances to trimethylamine, "aldehyde amine," "ketone amine" and pyridine, but no experimental work was done evidently to prove this definitely. Pyridine was investigated by Morris,5 who found it to have considerable cracking power. In the present investigation, the object was a qualitative evaluation of a number of representative amines with respect to their ability to cause season cracking. Thus it was desired only that an appreciable vapor pressure of each amine be obtained in order to make the test as severe as possible, without attempting to test equivalent concentrations for comparative purposes. MEthods Specimens TWO types of specimen were used: 1. Unannealed 70-30 brass CUPs formed from 0.040-in. thick sheet. Height of cup Was 13/8 in. and diameter was 17/8 inches. 2. First draw pieces of caliber .50 cartridge cases in the unannealed condition (70-30 brass)- The cups were representative of a thin wall and thin base specimen, whereas the draw pieces have a thick base (1/4 in.) and a thick wall (approximately 3/32 in.). Both types of specimens contained high residual stress and cracked in less than one minute in a solution of I per cent mercurous nitrate and I per cent nitric acid provided that this was receded by a 30-sec. pickle in 40 per cent nitric acid. Specimens were prepared as follows: (1) degreased in trichlorethylene, (2) rinsed in H2O, (3) pickled 5 min. in 10 per cent by volume H2SO4 (1.84 SP. gr.), (4) rinsed in H2O, and (5) dried. Amirtes Tested In selecting the amines, representatives of the three series of amines, and one series of substituted amines were chosen. The aliphatic series was represented by the methyl and ethyl primary, secondary and tertiary amines. These are the simplest aliphatic amines. For the aromatic series, the phenyl primary, secondary and tertiary amines were selected as being the simplest. The heterocyclic series was represented by pyridine, which is a simple heterocyclic base (tertiary amine).

Jan 1, 1944

[59H1-Water Law and Its Significance to the Mining Industry by Wells A Hutchins 59H2-Relation of Land Subsidence to Groundwater Withdrawals in the Upper Gulf Coast Region, Texas by Leonard A Wood and A G Winslow 59F3-Hydraulic Mining of Gilsonite and Its Application to Coal Mining by J H Baker 59H4-Recovery of Phosphates by In Situ Fluid Mining by Sylvain J Pirson 59F5-Coal Cleaning Plant Design for Minimum Operating Labor by Wm M Bertholf and John D Price 59F6-Coke Combustibility A Neglected Characteristic by J D Price 59B7-Union Carbide's Uranium Operation at Maybell, Colorado by K W Lentz and F T Temple 59H8-A Rapid Method for Estimating Alumina in Feldspathic Sands by Hugh H Bein 59H9-Water Laws as Related to Dredging in Idaho by Robert A Lothrop, Richard B Porter, and Robert P Porter 58B19-Separation and Washing of Alumina Process Residue by Morton Handelman 59B11-Feed Preparation and Froth Modification for Fatty Acid Flotation by Carl C Martin and Burt C Mariacher 59B12-Design Requirements for Tailing Disposal in the Southwest by E Vern Given 59B13-Semi-Dome Shaped Buildings for Bulk Storage by Edward E Ives and William L Payne]

Jan 1, 1961

By H. Rosenthal, A. L. Jamieson

The action of mercury on stressed brass to produce cracks was known before Moore, Beckinsale and Mallinson1 showed that actual season cracking did not occur spontaneously but could be induced by ammonia. These investigators studied other substances, including diphenylamine, without finding that anything other than ammonia could cause season cracking Grimston2 reported season cracking in cartridge cases stored in wooden boxes wetted with dilute sulphuric acid pickling solution. Season cracking associated with sulphur dioxide, water vapor and air has been reported by Johnston,3 although he reported that trimethylamine and pyridine did not cause cracking. Jevons4 has ascribed season cracking of brass in certain instances to trimethylamine, "aldehyde amine," "ketone amine" and pyridine, but no experimental work was done evidently to prove this definitely. Pyridine was investigated by Morris,5 who found it to have considerable cracking power. In the present investigation, the object was a qualitative evaluation of a number of representative amines with respect to their ability to cause season cracking. Thus it was desired only that an appreciable vapor pressure of each amine be obtained in order to make the test as severe as possible, without attempting to test equivalent concentrations for comparative purposes. MEthods Specimens TWO types of specimen were used: 1. Unannealed 70-30 brass CUPs formed from 0.040-in. thick sheet. Height of cup Was 13/8 in. and diameter was 17/8 inches. 2. First draw pieces of caliber .50 cartridge cases in the unannealed condition (70-30 brass)- The cups were representative of a thin wall and thin base specimen, whereas the draw pieces have a thick base (1/4 in.) and a thick wall (approximately 3/32 in.). Both types of specimens contained high residual stress and cracked in less than one minute in a solution of I per cent mercurous nitrate and I per cent nitric acid provided that this was receded by a 30-sec. pickle in 40 per cent nitric acid. Specimens were prepared as follows: (1) degreased in trichlorethylene, (2) rinsed in H2O, (3) pickled 5 min. in 10 per cent by volume H2SO4 (1.84 SP. gr.), (4) rinsed in H2O, and (5) dried. Amirtes Tested In selecting the amines, representatives of the three series of amines, and one series of substituted amines were chosen. The aliphatic series was represented by the methyl and ethyl primary, secondary and tertiary amines. These are the simplest aliphatic amines. For the aromatic series, the phenyl primary, secondary and tertiary amines were selected as being the simplest. The heterocyclic series was represented by pyridine, which is a simple heterocyclic base (tertiary amine).

Jan 1, 1944

E L. DEGOLYER, our new president, though a petroleum geologist by profession, has always s been associated with mining, for soon after his birth at Greensburg, Kan., on Oct. 9, 1886, his parents moved to Joplin, and when he went, in the course of time, to the University of Oklahoma, he intended to follow his course there with another at a mining school. He became a field assistant in the U. S. Geo-logical Survey, however, while still an undergradu-ate, and after field experi- ence in Montana, Wyoming, North Dakota, Colorado and Oklahoma, he went to Mexico as geologist for the Mexican Eagle Oil Co. This was in 1909, and as a result he was unable to complete his work for his degree until 1911. In Mexico, he located the Potrero de Llaño No. 4, one of the world's largest oil wells, and also the dis- covery well in the Naran- jos pool; and the Colorado School of Mines conferred the honorary degree of : Doctor of Science on him in 1925. On his return from Mexico, he engaged in the consulting business, specializing in financial ap- praisement, the Union and Marland companies being among his clients. In 1919, he organized the Amerada Petroleum Co., with the backing of Lord Cowdray. Last year, control of the company was purchased by an American group, headed by Dillon, Read and Co. Mr. DeGolyer is n o w president of the company. He is also vice-president and general manager of the Rycade Corp, the Rycade Oil Corp., and president of the Geophysical Re-search search Corp. The l a t t e r represents the practical appli-cation of his inter-est in the use of the torsion balance in the locating of salt domes, in which he has pioneered, the Nash dome being the first oil field in America actually brought into production by these methods.

Jan 3, 1927

By Willard C. Lacy

Survival of the mining industry as a viable economic entity in the United States is being seriously threatened by declining grades of ore reserves, rising operational and capital costs, and increased governmental taxes, restrictions, and subsidizing of third world competition. Discovery of major high-grade deposits is becoming increasingly unlikely. International competitiveness of the U.S. deposits will depend upon 'Yankee Ingenuity, ' innovations in mining methods, metallurgical treatment, and financial arrangements, and a viable national strategy. This will require not only effective management for control of operations, but management that encourages breakthroughs in technology, financing, labor relations, and in public and governmental understanding. The mine geologist and the exploration geologist both have important roles to play in all aspects of this fight for survival of the industry.

Jan 1, 1985

Executive JOHN M. LOVEJOY, Chairman ERLE V. DAVELER G. B. WATERHOUSE WISER JUDSON WILLIAM WRAITH J. V. W. REYNDERS, Consultant Finance HENRY KRUM, Chairman PAUL D. MERICA R. M. ROOSEVELT H. G. MOULTON, Consultant Admissions. RALPH M. ROOSEVELT, Chairman GEORGE D. BARRON, Vice-chairman JOHN L. CHRISTI PHILIP KRAFT W. A. SINSHEIMER

Jan 1, 1936

THE CHAIRMAN (EDWIN LUDLOW, Lansford; Pa.).-Mr. Wang's paper reminded me that some years ago I was asked if I would not go into the Tien Tsin district and take charge of Americanizing a Chinese mine. They said the trouble was that, while wages were only 9 c. a day, the coke cost $2 a ton delivered to the cars. Reading Mr: Wang's paper would indicate the need of a little Americanization in the Manchurian field. Wages are only 40 c: a day, yet the cost is $3.60 a ton. An efficiency engineer would have an excellent opportunity in that field. T. T. READ, New York, N. Y.-It is always true that low-priced labor is inefficient, wherever we find it; for example, in Japan, where wages are low, but not so low as in Manchuria, working costs are not relatively much lower than ours. Mr. Padshah, describing his experience in India, once told me that, while wages were only about one-fifth as high

Jan 4, 1918

By N. A. Gokeen, M. Ohtani

EFFECT of elements on the solubility of carbon in liquid iron is useful in calculating and correlating a number of thermodynamic properties as shown elsewhere in detail.' Kitchener, Bockris, and spratt2, and later Turkdogan and Hancock3 have investigated the effect of sulfur on the solubility of carbon at various temperatures and concentrations. For any chosen sulfur concentration, the solubility of carbon reported by Kitchener et al. is considerably lower than that by Turkdogan and Hancock. It was therefore felt that a reinvestigation of this problem was necessary. EXPERIMENTAL METHOD An alloy of Fe-C-S .was prepared with electrolytic iron and ferrous sulfide melted by induction in a graphite crucible, 4 in. high 1 1/2 in. ID under a CO-atmosphere. The temperature, held at 1500" ± 5°C in all experiments, was measured with a Pt-Pt + 10 pct Rh thermocouple immersed into the melt. In order to assure saturation with carbon, the melt was stirred with a graphite rod. After approximately 1 hr at 1500 °C, a sample was obtained by sucking the melt into a silica tube, 4 mm ID. The sample was then analyzed for carbon and sulfur by usual methods. RESULTS The results are presented in Table I and plotted in Fig. 1 with the individual values of Turkdogan and Hancock.3 Scattering in the data is equivalent to 3 pct or less in carbon analysis. The broken line represents the empirical equation obtained by Kitchener et al. from their data. It is evident that the present data are in good agreement with those of the former investigators but in disagreement with the latter. The cause for this discrepancy cannot be readily offered since the experimental methods in the three investigations were nearly identical. Additional evidence corroborating the author's results may be presented in the following manner. The difference between the solubilities of carbon in the ternary Fe-C-X melt with a small concentration of any element X, and in the binary Fe-C melt is %?C = %CIII-%CII [1] where %?C is the change in solubility, and %CIII and %CII are the solubilities in the ternary and the binary systems respectively. The value of %Cii

Jan 1, 1961

By T. E. Leontis

The specific effect of various rare-earth metals on the room- and elevated-temperature properties of magnesium has been evaluated. Alloys containing didymium exhibit the highest tensile and compressive strengths at room and elevated temperatures. All the rare-earth metals increase the creep resistance of extruded magnesium at temperatures in the range of 400° to 600°F, but the degree of enhancement depends on the temperature and on the concentration of the added metal. THE effects of rare-earth metals on the properties of sand-cast magnesium were discussed in some detail in earlier paper by the author.' The present paper deals with the effect of the same alloying elements on the properties of extruded magnesium. This investigation also had as its aim the development of a wrought alloy having a better combination of room-temperature strength and ductility and elevated-temperature strength and creep resistance than is found in magnesium-Mischmetal-manganese alloys, which have been reported earlier.2-5 The only known attempt to study wrought magnesium alloys containing pure cerium instead of Mischmetal was made by Mellor and Ridley.6 They found that in the form of rolled bars there is a definite, optimum cerium content for creep resistance at 200 °C and that the creep resistance of these alloys at 200 °C is significantly Improved by heat treatment at 550" to 580"C. In the present investigation the compositional variation in mechanical properties of the following alloy systems is presented: I—magnesium-Misch-metal. 2—magnesium-cerium-free Mischmetal. 3— magnesium-didymium. 4—magnesium-cerium. 5— magnesium-lanthanum. Alloys containing predominately praseodymium are not included in this series because of the lack of this material. Experimental Procedures The alloying ingredients used in preparing the alloys described herein are the same as those reported in the earlier paper.' Cerium-free Mischmetal is the rare-earth mixture remaining when the cerium is removed from Mischmetal, which contains all the rare-earth metals as they occur naturally in mon-azite sand, the ore from which Mischmetal is produced. Removal of both cerium and lanthanum from Mischmetal leaves what is commonly called "didym-ium," consisting predominantly of neodymium and praseodymium. Although the composition of the particular batch of each metal used may differ somewhat from the analysis presented previously, these differences are not great enough to warrant repeat- ing the specific composition of each material. The electrolytic magnesium used as the starting material in these alloys has the same typical analysis as that given in the earlier paper.' The alloys were prepared in small laboratory melts applying all the necessary precautions for alloying rare-earth metals with magnesium described by Marande.' Most melts were large enough to cast one 3 in. diam billet 10 in. long. In a few cases, particularly the didymium-containing alloys, the lack of sufficient amounts of the rare-earth metal limited the size of the billet to 6 to 8 in. All billets were scalped to a diameter of 2 15/16 in. and faced to a length of 9 ¼ in. as limited by the size of the extrusion container. The alloys were extruded into ½ in. diam rod on a 500-ton direct-extrusion press using a 3 in. container. The details of the extrusion step are: billet preheat, 925°F (2 hr); container temperature, 900°F; die temperature, 900°F; extrusion speed, 10 ft per min; reduction ratio, 36:1; and percent reduction, 97.3. The lower melting point of alloys containing didymium' necessitated reduction of the extrusion speed to 5 ft per min in order to prevent hot shorting during extrusion. Adequate lengths were cropped from both ends of each extruded rod to assure that all the material used for tests was extruded under uniform conditions. Tensile and compressive properties at room temperature are reported in the several conditions of heat treatment. The ASTM designations are used to distinguish these conditions as follows: T5—Direct age at 400°F (16 hr) T4—Heat treat at 950°F (4 hr) for alloys containing didymium T4—Heat treat at 1050°F (4 hr) for all other alloys T6—T4 + age at 400 °F (16 hr) The lower heat-treating temperature for alloys containing didymium is necessitated by the lower melting point of these alloys. All heat treatments were conducted in electrically heated, circulating-air furnaces. A protective atmosphere containing 0.5 to 1.0 pct sulphur dioxide was used for the high temperature heat treatments. Tension and creep specimens 6 Yz in. long and compression specimens 1½ in. long were cut from the extruded rod. A reduced section of ? in. diam was machined on the tension specimens, whereas on the creep specimens a reduced section of 0.450 in. diam

Jan 1, 1952

By E. T. Turkdogan

This is a compilation and a critical review of the data on the Fe-Ca-0 ternary system. Using the results on the reductiorz-equilibria, an oxygen potential diagram is drawn for the greater part of the system. A number of univariant systems and invariant points, not determined experimentally, are evaluated by making use of the theorem on univariant curves intersecting at an invariant point. The formation of solid solutions and ternary compounds and the crystal structures of some of the phases in the composition-diagram are given for a feu! temperatures. DURING the past thirty years there has been a continued interest in the study of the Fe-Ca-0 system. A detailed literature survey made by white1 in 1943 indicated that further work was required to clarify the phase relationships; in fact, the work carried out in the subsequent years, reviewed by Burdese2 in 1954, made a valuable contribution to a better understanding of this subject. Most of the data were obtained by the step-wise reduction of mixtures of iron oxides and calcium ferrites. However, there is some uncertainty about the phase relationships in this system, arising mainly from insufficient use of thermodynamic concepts in the construction of phase diagrams. In this paper an attempt is made to establish the invariant points from the available data. OXYGEN POTENTIAL DIAGRAM Schenck and coworkers3,4 were the early investigators who studied part of this system by the step- wise reduction method and suggested the formation of two ternary compounds, CaO.FeO.Fe2O3 and 2Ca0.5Fe0.2Fez03, the latter being referred to as point X. They also deduced from their results that the phases Y (8.74Ca0.32.5Fe0.8.74Fe2O3 and Z (2.02CaO-97.98FeO) were formed near the w?stite corner of the system. Martin and voge15 postulated the existence of the compounds CaO.9FeO and 4Ca0.3Fe3O4; the former is very close to the composition of point Z and the latter to that of CaO.FeO-Fe2O3. The most valuable contribution to the presen knowledge on this system was made by Cirilli and Burdese6-8 who showed by X-ray and chemical anal yses that there were two ternary compounds, CaO-Fe0.Fe2O3 and CaO.3FeO-FezO3; the former is the same as that suggested by Schenck et al. and the latter is close to their point X. The results of Cirilli and Burdese show that the phases Y and Z postulated by Schenk et al. are solid solutions of calcium oxide in w?stite. In most of the above-mentioned reduction-equilibria measurements carbon monoxide-carbon dioxide mixtures were used and in a few cases hydrogen-water vapor mixtures were employed. Using the

Jan 1, 1962

By Alicia O'Reardon

DIFFIDENTLY, because don'ts are rarely greeted with cheers; humbly, because I, myself, have never lined up with the irreproachables, I venture on the subject of manners for the mining camp matron. Mining camps can be divided roughly into two types-the large, opulent settlement that blooms like the rose about a strong mine in full operation; and the puny group of adobe huts, or calamina shacks, or even canvas tents flung down in the wilderness to shelter the gay pioneers of a shining prospect or the shattered survivors of a lost hope. Of the first, I know nothing; but in the second, I have spent some of my best years, and from its curious code of morals and manners, its comic hates and its unreasoning loves, its high impatience and its engulfing kindness, I have charted the narrow .and pitted path which must be trod by the woman who would success¬fully live therein.

Jan 1, 1936

By Barry D. Lichter, Pierre Sommelet

High-temperature heat contents of InSb, GaSb, and AlSb were measured over the temperature range 400" to 1450°K using a diphenyl ether drop calorimeter. Smoothed ualues of the thermal properties, H$ - H:9s, have been derived and are tabulated at even temperature intervals. The heats of fusion of the three compounds were determined as, respectively, 5707 *100, 7780 * 100, and 9800 5 3011 cal per g-atorn at the determined melting points of 797" l°, 985" * , and 1330" * 5°K. The calculated entropies of fusion are, respectively, 7.16 0.12, 7.90 * 0.11, and 7.37 * 0.23 cal per deg per g-atotn. The heat capacities increase substantially on tnelting in contrast to the behauior of structurally related germanium and silicon. Deriations from the Kopp-Neumann rule are negative for solid compounds and positive for the liquid phases. Previously obsevrrd "post melting" in InSb is confirmed. The high-temperature thermal properties of 111-V compounds are presently not well-established, despite the technical importance of these semiconducting cbmpounds. Uncertainties in available heats of fusion and heat contents have seriously hampered thermo-chemical evaluations' and thermodynamic analyses of phase equilibria2"" in these systems. This paper reports results of high-temperature heat content investigations of InSb, GaSb, and AlSb measured in the range 400" to 1450°K employing a diphenyl ether drop calorimeter. Similar measurements for InAs and GaAs will be reported in a following publication.~ EXPERIMENTAL PROCEDURES Samples. High-purity samples of the compounds InSb and GaSb were supplied in the form of crushed crystal fragments by Dr. Carl Thurmond of the Bell Telephone Laboratories and in the form of single crystals by Dr. A. Strauss of the M.I.T. Lincoln Laboratory. Single-crystal samples of semiconductor-grade AlSb were supplied by Dr. W. P. Allred of the Bell and Howell Research Center. Chemical analyses indicated that all compounds were stoichiometric to *0.1 at. pct, which is within the experimental uncertainties of the analyses. Samples were crushed, weighed, and encapsulated in evacuated, thin-walled, fused silica capsules. The capsules were nearly identical in external shape, 2 cm by 2 cm diam, but varied in weight due to differences in wall thickness. One sample of AlSb was contained in a thin-walled, high-purity alumina cup encapsulated in silica and used for heat content determinations of liquid AlSb. The capsule materials showed no visual evidence of reaction with any of the compounds. The sample and capsule weights are given in Table I. Calorimeter. A Bunsen-type calorimeter, similar in design to a previously described instrument6 but employing diphenyl ether (C6H5)'0 as the calorimetric substance, was used for measurements of heat contents above 300.0°K, the melting point of diphenyl ether. Heat input to the calorimeter caused isothermal melting of diphenyl ether, and the resulting increase in volume was measured by displacement of mercury from the calorimeter into a 200 cm horizontal, calibrated capillary, 1.25 * 0.01 mm diam, or into a weighed beaker. The advantages of diphenyl ether over water have been previously pointed out7 and include: i) an increase by a factor of 3.5 in sensitivity as measured by the ratio of the volume change to the enthalpy change on fusion, ii) the smaller required extrapolation from the melting point to the standard temperature of 298.17"K, and iii) the positive volume change on fusion of diphenyl ether in contrast to the contraction which occurs on fusion of ice. Diphenyl ether was purified by fractional crystallization to 99.95 mol pct as determined from the melting point depression with fraction crystallized. During assembly of the calorimeter, the ether was repeatedly outgassed under high vacuum to remove dissolved air. The calorimeter receiving vessel consisted of an 8-in.-long by 1:-in.-diam copper tube with twelve horizontal 3-in.-diam radiator "fins" for dissipating heat to the surrounding mantle of diphenyl ether. Before forming the mantle the chamber surrounding the receiving vessel contained 3300 cu cm of liquid diphenyl ether above 250 cu cm of mercury which was

Jan 1, 1970

By J. E. Schiller, S. E. Khalafalla

To improve technology for treating process water, US Bureau of Mines research has shown that magnesium oxide (MgO) has many advantages over lime or caustic soda for precipitating heavy metals. Sludge produced by MgO occupies only 0.2-0.3 times as much volume as the precipitate made wing a soluble base. While a settled, lime-formed precipitate is easily resuspended, the MgO-metal hydroxide sludge becomes cemented together on standing. Settling of the metal hydroxides from a dilute suspension is more complete than precipitates formed with other bases. Virtually any metal that can be precipitated by raising the pH can be treated using MgO. A three fold to fourfold stoichiometric excess of solid reagent is added. The mixture is reacted for five to 10 minutes. Polymer is added, and settling or filtration completes the process. Because of the greater cost of MgO compared with lime, large-scale practice of this technology will probably be limited to water containing 50 mg/L (3 gr per gal) or less of dissolved metals. For such dilute solutions, chemicals are not a large fraction of total treatment costs, so more desirable sludge properties might justify higher chemical expenses. While the MgO process is technically suitable for widespread application, the extent to which it is adopted will probably be determined by a trade-off between the greater cost of MgO compared with lime and the superior properties of the precipitates and their corresponding ultimate disposal costs.

Jan 1, 1985