By C. C. Pretorius, S. Ramjee, R. J. Mostert

The study investigates the effect of prior corrosive exposure on crack growth resistance behaviour of thin sheet (3 mm thick) aluminium alloy 2024-T3 at slow strain rates. Compact tension specimens were exposed to standard corrosive environments that simulate accelerated atmospheric corrosion attack. Two corrosive environments were considered – an exfoliation corrosion (EXCO) solution and a 3.5 wt% sodium chloride solution. The unloading compliance R-curves of the two-hour EXCO-exposed specimens revealed a significant degradation of approximately 11% in the crack growth resistance behaviour (Kc_e values) compared to the baseline (air-exposed) values. Furthermore, secondary intergranular crack formation was also revealed in the plastic zone ahead of, and adjacent to, the crack tip of these specimens; which formed during the crack growth resistance loading. It is postulated that the observed degradation of the Kc_e values of the EXCO-exposed material is due to hydrogen embrittlement since the exposure times for the EXCO evaluation were limited to ensure that uniform corrosion dominated; that is, significant penetration of corrosion damage and pitting due to localized corrosive attack did not occur. The sodium chloride-exposed specimens revealed a similar degradation (13%) after 24 hours exposure. However, slight intergranular corrosive attack and isolated pitting were observed on the exposed surfaces prior to crack growth resistance loading, resulting in notch effects that could assist in crack growth. Pitting and intergranular corrosion were, however, not observed at the pre-crack tip. The relative contributions of the notch effects and the hydrogen embrittlement during the degradation of the KR performance are, therefore, unclear.

Apr 1, 2021

By E. Öğretici, S. Kahraman

The indirect estimation of intact rock properties is particularly useful for preliminary investigations in engineering projects. In this paper we examine the usability of electrical resistivity, a nondestructive measurement, for the prediction of physical and mechanical rock characteristics. Physico-mechanical tests (uniaxial compression, Brazilian tensile, density, and porosity tests) and electrical resistivity measurements were performed on specimens of 36 rock types. Before the resistivity tests, the specimens were completely saturated with saline solution. Evaluation of the test results showed that there are medium or strong correlations between resistivity and rock properties. There are also strong or stronger correlations between the two parameters for the rock classes. The regression equations developed were statistically tested, and their validity was confirmed. The results were also compared with previous studies. The conclusion is that electrical resistivity measurement can be used for reliably estimating physical and mechanical rock characteristics.

Aug 8, 2024

By J. A. Theron

"This paper provides guidelines on performing mass and energy balance modelling involving coal and coal derivatives. Usually, the inputs to a pyrometallurgical process would be specified in terms of elements and compounds. Reliable thermochemical data is more widely available for species involving uniquely defined, relatively smaller molecules. However, in the case of coal, the molecules are extremely large and not uniquely defined. Consequently, modelling processes involving coal and its derivatives have several potential pitfalls. These are outlined in the present paper. The main findings are as follows:•,Coal proximate analysis should not be regarded as absolute; it could vary with several parameters, including heating rate •,For modelling, the use of ultimate analyses should be considered a preferable option to proximate analyses, where, ‘fixed carbon’ and ‘volatiles’ are not defined in terms of chemical composition •,Significant errors could be made if the larger molecules are neglected during calculation of the calorific value (CV) of coal gas (the gas liberated when coal is heated in the absence of oxygen) •,For elemental analyses, the oxygen content (which is calculated by balance) should be checked to ensure it is within the expected range •,For representation of sulphur in coal, double-counting due to SO3 in the ash analysis should be avoided •,Potentially, oxygen in coal could be represented as O2, H2O, CO, or CO2; however, use of some of these species without considering the experimentally determined gross CV results in significant errors in the energy balance. If coal enthalpy is calculated from elemental analyses without correction, representation of coal oxygen as H2O(l) gives reasonable accuracy (up to 6.9% error for a set of South African coals). Coal volatiles could be represented by a complex mixture of compounds, even using different oxygen-containing species than the abovementioned four, provided the enthalpy is corrected •,It is recommended that an ‘enthalpy correction value’ is incorporated in energy balances involving combustion, devolatilization, or conversion of coal and coal derivatives, e.g. coke, char, or tar. That would imply that proximate analysis, elemental analysis, as well as the gross CV would be required for all solid or liquid coal-derived substances being modelled. No other correction due to the form of carbon being different than graphite should be used, as that would imply doublecounting some effects."

Jan 1, 2014

By F. Sundqvist, B. Skawina, J. Greberg, A. Salama, M. Astrand, P. Ekbeck

Today’s mining operations require fast reporting and rapid rescheduling based on updated information. An automatic mine scheduling system could not only quickly reschedule but also propose alternative solutions. To avoid the financial and physical risks associated with testing such a system directly in operation, it could be first evaluated via discrete event simulation models. This would offer a safe environment to evaluate different operating rules and algorithms. In this study, this is achieved by integrating automatic scheduling software with a discrete event simulation model.

Jun 1, 2021

By A. V. Rasskazova

Theoretical substantiation of leaching of clustered ultra-fine gold by the electro-photo activated cyanide and chloride solutions is given in the paper; and processes of activation of leach solution by electrolysis and photo-activation are described. Comparative experiments on electro-photo activated leaching of ultra-fine gold from refractory ores by cyanide and chloride solutions were carried out. The material for research is primary ore of the Pogromnoe deposit (Russian Federation, Trans-Baikal Territory). The ore is characterised by the minimum sulfide minerals and the organic carbon content. Gold in ores of this deposit is presented as mainly ultra-fine. Gold inclusions in quartz and silica-alumina minerals (metasomatic minerals) are ultra-fine. Sulfide minerals (2.5-3%) are presented in ore generally by pyrrhotine (gold content does not exceed 10 g/t). Standard cyanide technology provides 49.5% gold recovery. Photo-electro activated air saturated NaCN provides 69.9% gold recovery. Laboratory research of chloride-hypochlorite column leaching demonstrated that the electro-photo activated method provided 78.9 % gold recovery to pregnant leach solution. Chloride-hypochlorite photo-electro activated solution can provide higher level of gold recovery with shorter process duration (10 days) in comparison with cyanide (40 days). The final decision regarding the choice of leach solution has to be done on the basis of technical and economic calculations. Keywords: Ultra-fine gold, cluster chemical reactions, active clusters, leaching, electro-photo activation of leach solution

Jan 1, 2020

By D. -H. Park, G. -j. Kim, Y. -J. Park, C. -S. Hong, S. -Y. Choo

To evaluate the quantitative tunnel behavior influenced by characteristics of discontinuity, this pa-per executes the parametric study using 2 and 3-dimensional DEM analysis. First of all, this study finds that displacement and the stress of shortcrete are proportioned to frequency of joint and rockbolt axial force is adversely proportioned too. Secondly, it is found that the most sensitive in-put parameter used in Barton-Bandis(BB) model is residual friction angle. Finally, when joint sets are encountered at tunnel excavation face, to identify the most critical joint orientation is very crucial for a stability of tunnel. La thèse a pour but d’étudier les influences sur la stabilité du tunnel, au niveau du réseau de la discontinuité et de la valeur de sa nature aquis par le projet récemment exécuté en vue de mener à l’analyse quantitative de cette stabilité, en appliquant chaque différent paramètre comme la fréquence de diaclase, la constante de résistance des modèles de Barton-Bandis(BB) ainsi que la relation entre le sens d’excavation du tunnel et le réseau de diaclase en 3 dimensions. En fait, cette étude nous a montré que la fréquence de diaclase s’accroît proportionnellement au déplacement et à la contrainte du béton projeté. L’angle de friction résiduel s’est montré le plus sensible à la stabilité du tunnel parmi les modèles de BB. Aussi à travers l’analyse à 3 dimensions, il s’est vérifié que si l’angle de pente du groupe de diaclase est horizontal entre l’axe du tunnel et la direction, il donne une influence importante sur le comportement du tunnel. En particulier, l’influence était la plus importante sur un fond rocheux dont la diaclase horizontale est grande. Um das quantitative Verhalten des Tunnels zu bewerten, eroertert dieses Papier eine parametrische Studie mit Hilfe der DEM Analyse. Auch wird hier eine zweidimensionale Analyse von Ver-bindungen verschiedener Frequenzen in der Gesteinsmasse, eine sensitive Analyse von allen der im Barton-Bandis-Modell (BB) genutzten Parameter und eine Dreidimensional-Analyse mit ver-schiedenen dreidimensionalen geometrischen Veteilungen von Verbindungen ausgefuehrt. Erstens: Die Studie findet heraus, dass Vedraengung und Druck im Shortcrete proportional zur Frequenz von Verbindungen und Axialkraft der Steinbolzen antiproportinal ist. Zweitens: Es wird herausge-funden, dass die am meisten Sensitiven der im BB-Modell angewendeten Eingaben die am Ende uebriggebliebenen Reibungswinkel sind. Und schliesslich wird herausgefunden, dass wenn Ver-bindungsteile an der Tunnelaushoelungsoberflaeche ausgemacht werden, fuer die Tunnelstabiltaet die Identifikation der meist kritischen Verbindungsorientierung sehr bedeutungsvoll.

Jan 1, 2003

By D. Sethuram, P. G. Koppad, S. Iyengar, R. Shobha

TiB2 and CeO2 particle-reinforced Al6061 hybrid composites were manufactured using stir casting and hot rolling techniques. The base alloy and composites were hot-rolled at 500ºC and a 50% reduction was achieved through 12 passes. The effect of varying TiB2 and CeO2 particle additions on the microstructure and mechanical properties of the Al6061 matrix was studied. Scanning electron microscopy showed uniform dispersion of both the reinforcements, with good interfacial bonding. Microhardness and tensile properties like yield and tensile strength were found to be higher for hybrid composite with 2.5% TiB2 and 2.5% CeO2 compared to Al6061 alloy and other hybrid composites. The increased tensile strength is attributed to good dispersion and interfacial bonding between the particles and Al6061 matrix. Fracture analysis using a scanning electron microscope revealed ductile fracture for the Al6061 alloy and mixed characteristics of ductile-brittle fracture for hybrid composites

Oct 1, 2021

1. Book reviews Quantitative texture analysis, edited by H. ,}. Bunge and C. Esling. Deutsche Gesellschaft fur Metallkunde, 1982. 551 pp. Reviewer: L. 1\'1.Matthews Boundary element methods in solid mechanics by S. L. Crouch and A. M. Starfield. Reviewer: J. A. C. Diering World mineral statistics 1976-1980. Produdion,' exports,' imports, by Institute of Geological Sciences. London, Her Majesty's Stationery Office, 1983. £18.00 Reviewer: R. P. King 2. New publications Canadian mines,. perspective from 1982. Mineral Bulletin MR 197. Supply and Services Canada, Hull, Quebec K1A 059, Canada. Copper' s changing cost structure, by Commodities Research Unit Ltd (31 Mount Pleasant, London, WClX OAD, England). Petrology of metamorphic rocks, by M. Suk. New York, Elsevier, 1983. 320 pp. U.S. $68.00. Applied geomorphology, by H. Th. Verstappen. New York, Elsevier, 1983.442 pp. U.S.$95.75. Tin and its uses, no. 137, by the International Tin Research Institute. Greenford, the Institute (Fraser Road, Greenford, Middlesex UB6 7AQ, England), 1983. 3. New journals Mining Science and Technology, edited by C. 0, Brawner and B. N. Whittaker, is to be published quarterly in one volume per year by Elsevier. Aluminium, published monthly by Aluminium -Verlag GmbH, P.O. Box 1207, D-4oo0 Diisseldorf 1, F.R. Germany. DM 690.00 per annum. Rock mechanics The South African Institute of Mining and Metallurgy is to hold two schools on 'Rock Mechanics in Mine Management' at the University of the Witwatersrand, Johannesburg, from 23rd to 27th January, 1984, and from 30th January to 3rd February, 1984. The Federation of Societies of Professional Engineers The Federation of Societies of Professional Engineers (FSPE) has been a member of the World Federation of Engineering Organisations (W FEO) for many years and has regularly sent delegates to the biennial conference of that organisation. Second progress report by ASRET The Professional Engineers Joint Council was estabislhed in 1960 and initially its main fWlction was to represent the interests of engineers. Explosives technology The Center for Explosives Technology Research (CETR) has been established at the New Mexico Institute of Mining and Technology (Tech) in Socorro, New Mexico. International Tunnelling Association A conference entitled 'Ita Tunnels 1984' will be held in Caracas, Venezuela, from 2nd to 7th June, 1984. Automation The IFAC Symposium on Automation for Mineral Resource Development is to he held in Brisbane (Australia) from 9th to nth July, 1985.

Jan 1, 1983

By B. L. Eggers

This study investigates the application of computed order tracking with subsequent rotation domain averaging and statistical analysis, to the drag gearbox of a dragline used in a mining environment. Computed order tracking is a fault detection method developed to deal with the varying speed conditions often found in industry and has been proven effective in laboratory conditions. Its application to real situations, however, requires some adjustment to deal with issues such as inadequate speed data and the fact that the drag gear rotates in two directions. This provides a unique opportunity to observe the performance of the order tracking method in a bi-directional rotating environment, allowing an investigation of the relationships between the results obtained from each operating direction. A monitoring station was set up aboard the dragline and data was captured twice daily for a period spanning approximately one year. The data captured consisted of accelerometer and proximity sensor data. The key on the shaft triggers the proximity sensors, allowing speed and direction to be measured. The measured speed is interpolated by using various speed interpolation techniques. Then the interpolated speed is used to complete the order tracking procedure that resamples the vibration data with reference to the speed. The results indicate that computed order tracking can be successfully employed in real environments. Furthermore it is shown that the rotation direction that opens the gear-tooth crack gives a better indication of incipient failure. It is therefore important not to disregard either direction when monitoring rotating machinery of this kind.

Jan 1, 2007

By H. von Blottnitz, B. E. Isheloke

Mining is a significant economic activity in most Southern African Development Community (SADC) countries, and mineral beneficiation has been identified, and controversially discussed as one of the possibilities for industrialisation. With many member countries being economically too small to muster the human and financial resources which beneficiation requires, the recently adopted Regional Mining Vision (RMV) envisages interventions at a regional level. An opportunity arose to ask industry role players to what extent the SADC appears to support regional beneficiation policy interventions undertaken by member countries, and what the challenges are in undertaking beneficiation regionally, as a complement to, or substitute for country-specific beneficiation policies. Twenty-five semistructured interviews were conducted with experts from SADC member countries during the 2019 Mining Indaba. Participants were divided on whether beneficiation should be carried out nationally or in the SADC region. While beneficiation could support value-keeping, key challenges were found to be infrastructure development (i.e. energy, water), scarce skills, access to technology and related costs, but also lack of free trade and movement. We submit that a more integrated beneficiation strategy for the SADC region, as is being developed through the RMV, would indeed be relevant in the future. Keywords: Mineral beneficiation, regional integration, beneficiation policy interventions, African mining vision, mining, SADC

Jan 1, 2020

By P. C. Pistorius, M. P. Maphutha, J. D. Steenkamp

Advanced high-strength steels (AHSS) are sophisticated materials being developed by the steel industry to mitigate challenges related to the performance of motor vehicles. To meet the requirements of AHSS, the ferromanganese alloys (FeMn) utilized in the production of the steel are required to contain acceptable levels of unwanted impurities, i.e. P, S, N, H, and C. The focus of the current study was to investigate dephosphorization of ferromanganese to produce a low-P alloy that could be effectively utilized in the production of AHSS. The study involved conducting laboratory-scale testwork to study the efficiency of CaO-based slag systems to dephosphorize FeMn alloys. The addition of Na2O, CaF2, and BaO to MnO-CaO-SiO2 slag was considered. The test work was carried out in a 25 kW induction furnace at temperatures of 1350°C, 1400°C, and 1450°C. The P partition coefficient (Lp) remained small at <1, which is an indication that dephosphorization had not been achieved. The baseline slag, comprising 40%CaO-40%SiO2-20%MnO, reported higher Lp values. Addition of Na2O and CaF2 did not show any further benefit. Substituting half of the CaO by BaO, resulted in similar Lp values to those of the baseline slag under conditions of 1350°C and 1450°C at 30 minutes. In summary, based on the Lp values obtained, the conditions investigated with the CaO-based slags appeared to have been unfavourable for dephosphorization of FeMn alloys, as most of this impurity element remained in the alloy.

Sep 1, 2021

By S. Shi, X. Xia, F. Xuesai, Z. Shen, D. Han

The hydrodynamic characteristics of a mechanical flotation cell’s transportation zone have significant impact on its metallurgical performance, especially on coarse particles recovery efficiency. However, how to define and adjust the transportation zone was seldom investigated by researchers. In this paper a method will be introduced to define the boundary of the transportation zone by PIV measurement. It is found that the transportation zone can be extended upwards by enlarging the entire rotor-stator assembly from the bottom of tank and increasing the jet angle of the impeller. Two control methods have been validated in industry tests on KYF-160m3 and KYF-320m3 air-forced mechanical flotation cells. The result shows coarse particles recovery are both improved distinctly. It is suggested that enlarging the top transport boundary is able to helpful to reduce the floating distance of bubbleparticle aggregates, which contribute to improve coarse particle recovery in large flotation cells. Key Words: Flotation cell; Transportation zone; Coarse particles flotation

Jan 1, 2020

By P. G. H. Pistorius, D. S. Konadu, G. Lubbe

The aim of this investigation was to determine whether the composition of a shielded-metal arc-welding electrode coating affected the low-temperature impact toughness of austenitic stainless-steel weld metal. It is generally accepted that increases in the δ-ferrite and nitrogen contents result in a decrease in toughness at low temperatures. Weld metal from electrodes with a basic coating also generally exhibit better toughness than those from rutile (acidic) electrodes. An increase in basicity was expected to decrease the number and size of inclusions, which in turn provides a tougher weld metal. Three commonly available potassium–rutile E308L electrodes were used, complying with the E308L-16 and E308L-17 specifications. Analysis of the electrode coatings showed very similar chemistry and basicity. Significant differences in the inclusion contents of the weld metals were observed: the E308L-17 weld metal had a lower inclusion content (1.4% by volume) than the E308L-16 weld metal (3.7%). The former had higher impact toughness at all temperatures, despite a slightly higher nitrogen content. Regression analysis confirmed that the inclusion content had a significant effect on the impact toughness at all temperatures.

Jul 2, 2022

By W. P. Channon, J. B. See

The reduction of fluxed and non-fluxed manganese, ores by ferromanganese silicide by W. P. CHANNON, B.Se. (Eng.), M.Sce. (Eng.) Wits. (Visitor) and J. B. SEE, B.Sce. Hons., Ph.D. (New South Wales), M.I.M., M.I.M.M. (Member) In South Africa, medium-carbonferromanganese is produced by the silicothermic reduction of slags containing MnO. Because of its importance in the production of refined ferromanganese, a study was made of the reaction between a premelted South African Mamatwan manganese ore and various ferromanganese silicide reducing alloys, with and without fluxing agents. Because the reaction is highly exothermic, temperature appeared to have little effect on the rates of manganese transfer to the metal and silicon transfer to the slag, and an apparent equilibrium was rapidly approached. Limits were determined for the favourable effects of fluxing additions, and manganese recoveries were found to decline as the ratio of CaO to MgO decreased as a result of the addition of basic flux. The recovery of manganese passed through a maximum, and subsequently decreased for variations in the ratio of alloy to ore. The results obtained, when used in conjunction with other physicochemical data related to this slag-metal system, suggest optimum slag compositions for the efficient manufacture of medium-carbon ferromanganese from Mamatwan ore.

Jan 3, 1977

By J. G. M. Mukoya, B. Adebayo

"This work was carried out to determine the influence of rock properties and drilling machine parameters on the penetration rate at the SJ pit of Rössing Uranium Mine, Namibia. Rock properties (uniaxial compressive strength, tensile strength, and modulus of elasticity) of samples collected were determined in the laboratory. Drilling experiments were conducted in which feed pressure, air pressure, rotary speed, weight on the bit, and torque were varied to measure their effect on the penetration rate. The uniaxial compressive strength varied from 90–180 MPa for layered marble-quartzite and banded gneiss. Increases in feed pressure, weight on the bit, and rotary speed beyond the optimum level led to a decrease in penetration rate and caused the drill bit to ‘stall’. Results of the study revealed that penetration rate increases with an increase in the feed pressure and air pressure. After reaching a maximum value, the penetration rate begins to decrease despite increasing feed pressure. A very high torque causes the drill bit to stall, since the feed pressure is too high and the air pressure is not sufficient to remove the cuttings from blast-hole at maxium bailing velocities. The average penetration rate varied from 19 to 45 m/h for phase 2 of the pit, and from 17 to 68 m/h for phase 3. The optimum drilling machine parameters obtained in phase 2 and phase 3 were slightly lower than those currently being used at the mine. The trials of the optimum machine parameters will assist in reducing the cost of drilling, which varied from N$29.48 to N$36.31 per metre for the tricone bit. IntroductionDrilling and blasting contribute most to the operational cost in opencast mining and have the potential to influence the cost of downstream operations (Aipanda, 2011). The drillability of rocks depends not only on the rock properties, but also on the drilling tools and operational variables. In rotary drilling, rotational speed, thrust, and flushing are the operational variables, and are known as the controllable parameters. Rock properties and geological conditions are the uncontrollable parameters. Although, many attempts have been made to correlate drillability with rock properties, the rock characteristics affecting rotary drilling have not been entirely defined (Hartman, 1962; Kahraman, Bilgin, and Feridunoglu, 2003). The drill bit is forced into a rock surface from the rotary power head, hence creating stresses and cracks at the bit-rock interface. The performance of a particular bit in any formation i"

May 1, 2019

1. Book review Economics of mineral exploration in Australia, by Brian W. Mackenzie and Michel L. Bilodeau. Australian Mineral Foundation (Private Bag 97, Glenside, South Australia 5065). 198pp. $A58. $A45 for students. Reviewer: D.G. Krige 2. Recent publications Combustion of coal liquid mixtures, by G.F. Morrison. London, lEA Coal Research, 1983, 52 pp. Hafnium: physico-chemical properties of its compounds and alloys. Vienna, International Atomic Energy Agency, 1981. 408 pp. 620 Austrian schillings. Canadian mines handbook 1984-85, edited by CD. Gardiner. Toronto, The Northern Miner, 1984. 500 pp. $24. Drilling equipment in Canadian mining and exploration- opportunities for the industry, by AJ. Jakubek. Toronto, Micromedia Limited (144 Front Street, Toronto M5J IG2, Canada), 1984. Research report 1984. Port Melbourne, Division Mineral Chemistry, Commonwealth Scientific and Industrial Research Organization, 1984. 190 pp. Surface engineering Wear is an unavoidable problem in virtually all products of the engineering industry, from the minute bearings of instruments to the cutting surfaces of earth-moving plant. Safety in mines About 50 papers will be presented at the 21st International Conference of Safety in Mines Research Institutes at Sydney from 21st to 25th October, 1985. Some 250 delegates from 30 nations are expected to attend. Professional development seminars March 18th-21st, 1985 Underground Blast-hole Mining May Ist-3rd, 1985 Mineral Processing of Gold Ores May 6th-10th, 1985 Mineral Comminution Systems May 13th-15th, 1985 Processing of Metallurgical Residues Analytical chemistry The Second Symposium on Analytical Chemistry in the Mining, Exploration and Processing of Materials is to be held in Pretoria from 15th to 19th April, 1985.

Jan 1, 1985

By M. E. Rossi

All large-scale applications of conditional simulations intend to benefit from the ‘correct’ (or’ accurate’) characterization of uncertainty, adequately describing the variability observed from the data and its impact on the final objective. This paper discusses a number of relevant issues that highlight the extent to which, in reality, a model of uncertainty is dependent on the random function model chosen. Often in the presence of large number of conditioning data most available random function models will provide similar models of uncertainty. When conditioning is scarce, the resulting models of uncertainty will vary more widely, since the final output will depend mostly on the underlying assumptions of the model chosen. The application described in this paper is taken from a large porphyry Cu operation in northern Chile, and it demonstrates the impact of several variables on the resulting models of uncertainty. In particular, some of the decisions involved include the number of conditioning data and the underlying Random Function model used (Gaussian or indicator-based). Also, implementation-specific parameters must be decided upon, such as grid size used, random number generator, simple or ordinary kriging, multiple-grid simulation, and simulation of irregular three-dimensional bodies (as opposed to regular grids). Some practical guidelines are proposed to deal with these decisions.

Jan 1, 2003

By W. R. Matizamhuka

"The consolidation of nano-sized composite materials presents a challenge using conventional hot pressing methods. Spark plasma sintering (SPS) technology has shown great promise in the successful sintering of nanoreinforced composite materials. This qualitative review seeks to impart knowledge gathered, and progress made over the years on the consolidation of nanocomposite materials using SPS technology. The review is aimed at introducing this technology to the South African science and engineering community. Emphasis is on improving the mechanical properties of structural ceramic nanocomposite materials, which over the years have shown great promise in a wide range of applications, including transport, energy, mining, and the environment. Although success has been achieved within the laboratory for research purposes, there are still great opportunities to commercialize the technology for the production of larger components with more complex shapes.IntroductionSince the pioneering work of Niihara and Nakahira (1991) over a decade ago there have been extensive attempts to harness the potential of nanostructural metals, ceramics, and composites in a number of applications (Niihara and Nakahira, 1991; Selaho et al., 1997; Sekino and Niihara, 1995; Khalil, 2012; Aalund, 2008). It is generally realized that reducing the grain size of materials to nanoscale offers a significant improvement in properties. Attempts to synthesize nanostructured compacts by conventional sintering methods have not succeeded owing to the uncontrollable high rates of grain growth driven by long dwelling times at the sintering temperatures and large powder surface areas (Sergueeva et al., 2009; Gua, Khora, and Chieng, 2004; Tang et al., 2009). Following the development of spark plasma sintering (SPS) technology, it is now possible to process nanocrystalline materials with controlled grain growth. SPS, also referred to as the field-assisted sintering technique (FAST) or pulsed electric current sintering (PECS), was developed with the aim of improving on the well-established hot pressing (HP) technology (Kessel and Hennicke, 2007;"

Jan 1, 2016

By R. Tabanrad

This article examines the stability analysis of intake tunnels of Karun III dam & power plant. The tunnels have been excavated with a 3-dimensional and fairly complicated geometry in Pabdeh weak formation rocks at Zagros region. Due to the particular excavation geometry and inapplicability of plane-strain status, the stability of these excavations has been analyzed using both the 3D elastic software Examine 3D and the 2D non-elastic software UDEC simultaneously. The geomechanical parameters have been estimated by back analyzing the measured displacements from instruments, which were installed in the tunnels, and the parameters have been used in non-elastic numerical model. The results of the analysis show that the strains occurred in surrounding rock mass are less than the allowable failure strain and that the tunnels are stable. In addition, considering the results of non-elastic 2D analysis, the areas with unstable potentiality were identified and after the instability occurred at the areas predicted by the model , it was stopped up to the allowable strain limit through installing additional support . Bei diesem Artikel handelt es sich um eine Analyse der Festigkeit der Eingangstunnel des Damms und Elektrizitätswerks “Karoon III”.Die Tunnel haben drei Dimensionen und eine sehr schwierige Form und sind in brüchigen Felsen in “Pabedeh ,in Zagrossgebirge”eingebohrt.Aufgrund besonderer Form der Bohrung wurde ihre Festigkeit durch elastische dreidimensionale Soft-ware analysiert,die gleichzeitig die drei-und zweidimensionale unelastische Soft-ware UDEC benutzt hat.Die geometrische Parameter sind mit Ausnützung der Analyse berechneter eingesetzter Versorgungen,die in Tunnel aufgebaut sind,bewertet.Und diese Parameter sind in Zahlen-Analyse benutzt.Die Ergebnisse dieser Analyse zeigen,dass die Drücke an Felsen weniger als problematischer Grad der Drücke sind und die Tunnel fest sind.Ausserdem wurde mit einem Einblick auf die Ergebnisse der unelastischen zweidimensionale Analyse die eventuellen unfesten Teile bestimmt.Nach entstandener Unfestigkeit an diesen Teilen wurde die problematischeDrücke für Aufbau mehrere Anlagen gestoppt. Cet article examine l&apos;analyse de la stabilité de tunnels de la prise de Karoun barrage III et centrale électrique. Les tunnels ont été excavés avec une 3 dimensionnel et compliqué géométrie dans Pabedeh que la formation faible balance à région Zagros équitablement. Dû à la géométrie de l&apos;excavation particulière et inapplicabilite de statut de tension plane, la stabilité de ces excavations a été analysée en utilisant les deux le 3D logiciel élastique Examen 3D et le 2D logiciel non - élastique UDEC simultanément. Les paramètres du geomechanical ont été estimés en analysant le déplacement mesuré d&apos;instruments qui ont été installés dans les tunnels et les paramètres en arrière a été utilisé dans les modèles numériques non - élastique. Les résultats de l&apos;analyse montrent que les tensions se sont produites dans masse du roc environnante est plus petit que la tension de l&apos;échec admissible et que les tunnels sont stables. De plus, les régions avec potentialité instable ont été identifiées étant donné les résultats de 2D analyse non - élastique, et après que l&apos;instabilité se soit produite aux régions prédites par le modèle, il a été arrêté jusqu&apos;à la limite de la tension admissible à travers installer du support supplémentaire.

Jan 1, 2003

By W. U. Reimold, R. Armstrong, R. G. Charlesworth

For many years rockbursts have plagued the mining industry. Although much research has gone into studying this phenomenon only a small proportion of it has been on the actual source mechanism. A study was recently carried out to compliment the previous work done on the micro-structure of these features and to compare it to the micro-structures seen on shatter cones, from meteorite impacts. Both optical and electron-microscopy were used during the study. Samples were collected from rockburst sites by the CSIR Miningtek Rockburst Investigation Unit, and from the collar of the Vredefort Impact Crater. In the optical-microscopy study, the pinnate fractures observed in previous studies were seen in the shatter cones, through all the material. In the rockburst samples, the fractures were observed only in the quartz grains. Quartz micro-crystals were present in the rockburst samples and appeared to be the product of comminution rather than crystallisation. Cataclasite was present on rockburst and shatter cone fracture surfaces. The observations of the shatter cone surfaces with the scanning electron microscope are in agreement with previous work, including the observed presence of melt features, spherules and spheroidal material. The deformation in the rockburst samples is concentrated in the quartz grains, highly complicated with brittle features like sub-conchoidal structures and step structures present. A quartz spherule was identified on one rockburst sample and rhombic-dodecahedra type micro-crystals were present and seen fracturing off quartz grains. It is clear that the rockburst and shatter cone fracture surfaces are quite different; the shatter cone deformation is equally distributed across the sample and involves plastic-deformation, while the deformation in the rockburst material is concentrated in the quartz grains and, with the exception of spherule formation, is brittle. This study agreed with the current explanation for the formation of the rhombic-dodecahedra, and disproved the possibility of it being coesite or fine-grained meta-chert. Although there is no definite evidence of the mechanism of formation of the spherule, it is believed to be the product of vaporization and condensation, and the presence of this material indicates the extreme conditions under which this event occurred.

Jan 1, 2003