Search Documents

By WU Jian-hui

Keywords: metallic material; nickel powder; thermal decomposition; precursor; fibrillar powder; nanometer scale; passivation treatment The precursor thermal decomposition process of fibrillar nanometer scale nickel powder and passivation treatment of obtained powder are investigated, and the composition and morphology of the products are characterized by use of IR, TGA/DTA, XRD and SEM. The results show that the precursor morphology is a decisive factor to the product morphology of the nickel powder. The morphology of the product derived at low decomposing temperature is irregular. The nickel powders produced at the temperature higher than 480 coheres seriously. The product particles are reunited with the decomposition time prolong. The powder prepared under the optimal condition is fibrillar like woolen yarn; the grain diameter is less than 50nm.

Jan 1, 2005

By Shenghui Guo, Ying Lei, Wei Li, Jinhui Peng, Libo Zhang, Yu Li

"In this work, the Panzhihua low grade ilmenite and graphite were milled for 1, 2, 4 and 8 h firstly, then the temperature rising behavior of milled sample in microwave field were studied. The average heating rate of samples milled for 1, 2, 4, 8 h were 1.86, 4.08, 2.82, and 2.32 K/s; Before optimize the microwave reduction process, several experiments were conducted in order to confirm the parameters range. After milled for 4 or 8 h and reduced above 930 oC, the Fe metallization are higher than 90%; Then the optimization was investigated by using response surface methodology (RSM), the significance of predict model and each terms were analyzed, and the optimization parameters were given as: milling time is 4 h; reduction temperature is 1001 or 1070oC; the holding time is 37.5 or 26.9 min. Under these conditions, the Fe metallization given by predict model is 91 or 92 %.IntroductionThere is about 9.66 billion tons of Vanadic Titan-magnetite deposits in Panzhihua, China. In this reserve, there is about 8.73×108 t of TiO2, accounting for 90.54% of the Chinese reserves, and 35.17% of the international reserves and ranking first in the world. [1] Titanium mineral deposits are classified into Rock type and Placer type. Rock type is the igneous mineral, which have high content of FeO (Relative to Fe2O3) and gangue. The Panzhihua ilmenite is a typical rock type ilmenite ore. The higher contents of MgO, CaO, SiO2 and the complex mineralogy are making its direct reduction progressively more difficult."

Jan 1, 2011

By Andrea R. Kim, Ramana G. Reddy

Electrodeposition of cobalt from cobalt chloride using the urea and the choline chloride ionic liquid (2:1 molar ratio) was studied to search the optimized parameters for the higher current efficiency. The cyclic voltammetry was tested with 0.2 MCoCl2 using various scan rates to determine the reduction potential in Urea/ChCl at 323 K. Based on the data from cyclic voltammetry test, the transfer coefficient and the diffusion coefficient were calculated as 0.22 and 3.38 × 10−6 cm2/s, respectively. The parameters for electrodeposition of cobalt were various temperatures (323 –383 K), applied potentials (2.4 –3.3 V), and concentration of CoCl2 (0.2–0.5 mol/L). Current efficiency and energy consumption were calculated to investigate the optimal condition for the electrodeposition of cobalt. The highest current efficiency (95%) was obtained under the temperature 323 K, the applied voltage 2.7 V, and concentration 0.5 mol/L of CoCl2. Scanning electron microscope (SEM) and X-ray diffraction (XRD) were used for the characterization of cobalt deposits.

Mar 1, 2017

By H. Kung, T. R. Jervis, M. Nastasi, T. E. Mitchell

"A systematic study of the structure-mechanical properties relationship is reported for nanolayered composites of MoSh-SiC, Mo-MoSh, Mo-MoShNx, MoSi2-MoSi2Nx, and Mo-MoShMoSi2Nx (x=3-4) synthesised by sputtering techniques. These composites have been studied by nano-indentation and cross-sectional TEM as a function of annealing temperature. As-deposited layers are amorphous except for Mo. With increasing annealing temperature, first MoSh and then SiC crystallize, while the hardness progressively increases until the layers start to spheroidize and grain growth sets in at 900ºC. For the case of Mo-MoSi2, the layers react and the composite deteriorates rapidly. However, MoSi2Nx remains amorphous up to 1000ºC, suggesting that it could act as a diffusion barrier between Mo and MoSi2. In fact the Mo. MoSi2Nx, MoSi2-MoSi2Nx and Mo-MoSi2-MoSi2Nx nanolayers are found to remain stable up to such temperatures. IntroductionMolybdenum dislicide, MoSh, is a potential matrix material for high temperature structural composites due to its high melting point and good oxidation resistance at elevated temperature [1]. The two major drawbacks for structural applications are inadequate high temperature strength and poor low temperature ductility. Silicon Carbide (SiC) being hard and thermally compatible with most ceramics and intermetallic compounds, has been found to be suitable for second phase reinforcement in various structural applications and, in particular, the addition of SiC whiskers improves the high temperature yield strength of MoSi2 [2]. While most of the research in MoSb-SiC composites has been on the particulate form of SiC, laminated composites may offer unique properties. It has been shown that synthetic multilayers with alternating layers of metal and/or compounds may exhibit interesting mechanical properties [3]. Enhancement in mechanical properties by decreasing the wavelength of multilayer spacing has been studied extensively. In general, two types of strengthening have been proposed: (1) Hall-Petch strengthening [4,5], where the strength increase is inversely proportional to the square root of the layer thickness; (2) Koehler modulus strengthening [6], which increases with modulus difference and decreasing layer thickness. In the present study, we have performed a systematic study of the relationship between strength and structure in a number of different nanolayered systems based on MoSh. Layer thicknesses have been varied and their nanostructures have been varied by heat treatment. Previous work on MoSi2-SiC is summarized [7]. In an attempt to improve fracture toughness, MoSh-Mo nanolayered materials have been prepared but are found to react and deteriorate. Previous work has shown that nitrided MoSi2 (MoSi2Nx with x=3-4) is highly stable [8] and so nanolayered composites of MoSi2-MoSi2Nx and Mo-MoSi2-MoSi2Nx have been prepared to assess the' stability and mechanical properties of these composites. Preliminary results are presented."

Jan 1, 1994

By E. W. Lithgow

Commercial volumes of nickeliferous laterite ores overlie part of a 90 km long belt of peridotites in central Dominican Republic. Protores are serpentinized harzburgites and dunites, with lesser serpentinite. The ore mineralogy consists mostly of goethite, serpentine-group minerals, quartz and poorly crystallized, x- ray amorphous materials. Minor constituents are hematite, gibbsite, olivine and enstatite. In the Ore Dressing plant the mine feed is subjected initially to proper sizing and blending to produce a homogenized mix. Subsequent drying and upgrading, by selective crushing and screening of rock fragments through a Barmac circuit, complete preparation of the ore for pyrometallurgical processing.

Jan 1, 1993

By Gaballah I.

Elimination of arsenic, mercury and zinc from synthetic solutions containing H;\A.sD4. HgCI2 and ZnCI2 using modified barks was investigated. The pH range was varied from ?1 to 10. The initial concentrations of individual element were 10,100 and 1000 ppm. More than 99 % of mercury and 65 % of zinc cations were removed by the modified bark .. In this case, the modified bark reacts as a cation exchanger leading to the release of ' two protons for every HgII or ZnII fixed by this material. About 30 % of arsenic was eliminated from the solution. This 'low efficiency could be attributed to? the presence of arsenic ,as. anion. Decontamination of a treated industrial effluent containing 4 ppm of ion? metals was performed on a pilot plant scale by the modified bll(k. More than 70'% of these ion metals were eliminated.

Jan 1, 1995

By Meghan McGrath

Third generation advance high strength steels with microstructures of acicular ferrite and retained austenite were investigated and meet mechanical property goals. A good combination of strength and ductility were achieved with duplex ferrite and austenite microstructures where cementite formation was suppressed. Transformation induced plasticity (TRIP) behavior produced rapid work hardening. The mechanical properties of two hot-rolled steels with duplex microstructures were compared and had the following compositions: (1) Fe-0.14C-13.87Mn-1.42Si-3.51Al; and (2) Fe-0.06C-14.2Mn-1.85Si-2.38Al. These steels were cast, homogenized, and hot rolled at 900ºC to obtain a refined microstructure with ultimate tensile strengths and elongations to failure of 865 MPa and 39% and 1,217 MPa and 28%, respectively. The amount of metastable austenite in both compositions decreased after tensile testing from 58% and 28% to 6% and 0%, respectively. Microstructures were characterized using optical microscopy, scanning electron microscopy (SEM), and x-ray diffraction.

Jan 1, 2010

By T. DebRoy

In recent years rapid technological advances have been achieved in the application of high energy density heat sources such as lasers and electron beams in diverse metals processing operations such as metal refining, fabrication, coating, surface modification and alloying. However, our phenomenological understanding of these new and emerging processes has not kept pace with the technological achievements. Inadequate understanding of plasma-metal interactions, the complexity of the component physical processes, and the scarcity of thermophysical data at temperatures much higher than the melting points of metals are the main difficulties in the comprehensive analysis of these processes. Several unique contemporary issues related to metals processing with high energy density beams such as rapid evaporation of alloying elements during processing and the role of plasma in influencing vaporization rate interfacial tension and species solubility in metals are discussed in this paper.

Jan 1, 1993

By S Ivanaj

Oxidation of chalcopyrite from a copper concentrate in an electrochemical cell having separate-anodic and cathodic compartments was studied by potentiodynamic, potentiostatic and galvanostatic experiments. Oxidation of chalcopyrite particles was mainly realized by in-situ electrogenerated FeIII and Cull ions. The use of an ion exchange membrane, in this experimental set, avoids the reduction of the ferric and cupric ions. The effects of particle size, current feeder potential, current intensity and pulp density were studied to optimize the oxidation parameters. Selective complete oxidation of chalcopyrite was achieved. Oxidation of pyrite was negligible. Mom than 85 % of sulfur was obtained in its elemental form. This may allow selective extraction- of copper from the chalcopyrite concentrate without sulfur dioxide emissions.

Jan 1, 1995

By Omid Lashkari

Keywords: SEED, SSM materials, Microstructural evolution, Rheology, Swirling Speed SEED (Swirled Enthalpy Equilibration Device) is established itself as a new technology amongst the many Semi-Solid Metal (SSM) processes, where swirling of the mush plays an important role in modifying the dendritic structure of as-cast parts. A range of semi solid metal structures, dendritic, rosette and/or globular morphology of primary phase, can be prepared using SEED. The current article reports on the application of rheological tests in characterizing microstructural evolution during SSM processing of 356 Al-Si foundry alloy. A simple parallel plate test machine, designed and constructed at our labs, was used to determine viscosity values for each structure and identify the optimum structure with superior die filling characteristics. Such findings have important technological and economical implications during high pressure die casting of semi- solid metals. The strain-time graphs for 356 Al-Si foundry alloy indicated lower viscosity values for globular microstructure, i.e. improved die filling.

Jan 1, 2005

By Saskia Duyvesteyn

Small ion-exchange resin particles provide faster mass transport than conventional-sized beads. Unfortunately, high pressures are needed to pump solutions through columns containing small resin particles. It is preferable to disperse fine resins in the solution being treated. Screens have been used to separate the resin from the solution, but screens do not retain fines created by attrition of the resin particles. We have developed a separation process based on flotation, which relies on the surface characteristics of the resin, instead of size. The resin is conditioned with a surfactant before dispersing it in the solution to be treated; this increases the hydrophobicity of the resin sufficiently for froth flotation, without introducing surfactant directly into the solution. The surfactant adsorbed on the resin surface does not appear to impair the kinetics of metal ion removal. A flowsheet for an effluent treatment process is proposed; other applications are clearly possible.

Jan 1, 1998

By Reed M. Izatt

SuperLig® materials are capable of individually separating Rh, Pd, and/or Pt in highly purified form (99.95 to 99.99%) from a variety of chloride-based feed streams in a single stage operation. The hydrophillicity and associated kinetics of the supported materials allow for operation at relatively high flow rates of both loading and elution in a packed bed format. Pilot and commercial systems have been operated with Rh, Pd, and/or Pt present in the feed from single digit ppm (mg/l) to tens of g/l. A dual SuperLig® system for one pass Au(CN)2- separation followed by Cu and CN- recovery for CN- recycle has also been tested up to a pilot level,

Jan 1, 1999

By Adelana Adetunji

Ilmenite ore samples obtained from Dankoli in Zamfara, North Western Nigeria has been characterized using Energy Dispersive X-ray fluorescence (EDXRF) technique, X-ray diffraction (XRD) technique and the Neutron Activation Analysis (NAA) technique. The major constituents in the ore were quantitatively found to be TiO2 and Fe2O3 in concentrations of about 60wt% and 31wt% respectively. These occur in the forms of magnesian ilmenite (Fe, Mg)(Ti, Fe)O3, pure ilmenite (FeTiO3), and barium copper yttrium oxide (Ba2Cu3YO6.56) minerals. Other constituents/impurities in minor or trace quantities include MnO, Ta2O5, Nb2O5, Wo, SnO2, Hf, Zn, V, Zr, Co, Pb, Br, Al, Rb, Y, Th and U.

Jan 1, 2006

By Huaqing Xie, Qingbo Yu, Qin Qin

A novel sorption-enhanced steam reforming (SESR) process of hot coke oven gas (HCOG) was proposed for tar removal and H2 amplification, and was studied with the comparison of conventional steam reforming (SCR) process. Both of the processes could remove tar effectively and improve the H2 amount in the COG obviously. For CSR process, after the temperature and the S/HCOG ratio reached 700 °C and 2.4 respectively, the H2 amplification factor kept 4.30 around, with its concentration less than 75%. However, for SESR process, the H2 amount and concentration get improved further, with the optimal temperature moving toward low temperature. At 600 °C and the S/HCOG ratio of 2.4, the H2 amplification factor and concentration could reach 4.91 and 97.55% respectively when the CaO/C ratio was 2.0. Under the respective optimal reforming conditions of the two processes, the energy consumption of the SESR process was lower than that of CSR process.

Mar 1, 2018

By C. Liliane Carvalho

In the current study, bio-oxidation tests were carried out in shaking flasks with a flotation concentrate containing the sulphides pyrite, arsenopyrite and gudmidite. The tests were performed with mesophilic microorganisms (At. ferrooxidans) at 30 °C and also with the moderate thermophile S. thermosulfidooxidans, at 50 °C. The effects of (i) previous adaptation of the microorganisms to the concentrate, (ii) ferrous iron concentration and (iii) pulp density (2%, 4% and 6% (w/v)) on the dissolution of the sulphide were studied through arsenic extractions. S. thermosulfidooxidans was more sensitive to the pulp density in comparison to At. ferrooxidans as a reduction in sulphide oxidation was observed with the increase in the solid content to 6%. Therefore, the mesophilic strain was selected for further work, which comprised a rolling bottle experiment at 10% solids. After 40 days of bio-oxidation, the solid material was subjected to cyanidation, which revealed 85% gold extraction as compared to 21% from the original concentrate. The antimony sulphide grains in the bio-oxidized product showed similarity to what was observed in the original sample, suggesting such particles were not susceptible to the bio-oxidation process.

By Maryam Ghodrat, Bijan Samali

Disposal of waste syringes in a safe and eco-friendly way has been an issue of considerable scale for decades. The generated amount of waste syringes has escalated with the rapid growth in population and wide acceptance towards single-use medical devices. Some hospitals have their own on-site incinerators ,but recent tightening of air quality regulations and landfill levies led to the closure of manyon-site incinerators. The solution to this problem implicates the development of an environmentally-sound method that would employ these waste materials. This work investigates a thermodynamic modelling approach for incineration treatment of waste plastic syringes in Electric Arc Furnace (EAF) steelmaking. Mass balance was obtained from HSC Chemistry thermochemical package. The results indicate that the rate of iron oxide reduction in the slag is higher when coke is partially replaced by waste plastic syringes. Furthermore, the amount of dust and stack gas emission was reduced by around 0.4% and 1.25% respectively by replacing 20%-weight of pure coke with waste plastic syringes. The study demonstrates part of the coke can be successfully replaced by waste plastic syringes in electric arc furnace to provide additional energy from combustion without affecting the main process.

Mar 1, 2018

By Shigeru Ueda, Shin-ya Kitamura, Shohei Koizumi, Xu Gao

Steelmaking slag was confirmed to be a useful fertilizer for paddy growth as it efficiently supplies Ca and Si to soil water. In addition, supplement of Fe from slag fertilizer has been expected to suppress the H2S generation in paddy soil, especially for the degraded paddy soil. However, on the basis of our previous research, the Fe dissolution ability changed with slag brands, and even some brands could dissolve Fe under paddy soil pH, the supplying ability were not high. To improve Fe dissolution, we found that among various kinds of Fe-rich mineralogical phases in slag, the CaO–SiO2–FeO glassy phase showed highest water solubility of Fe. Because the CaO–SiO2–FeO glassy phase was a quenched molten phase, its dissolution behavior may depend on chemical composition, and this is important for controlling slag composition to produce fertilizer which can easily release Fe. Therefore, in this research, the CaO–SiO2–FeO glassy phase of various CaO/SiO2 ratio, Fe2+/T–Fe ratios, and FeO contents were synthesized, and the dissolution behaviors of Fe as well as other cations from these synthetic glassy phases into an aqueous solution at pH of 5 were investigated. The result showed that the dissolution ratio of Fe increased significantly by increasing Fe2+/T–Fe ratio. An increase in FeO content of glassy phase also increased the dissolution of Fe. In addition, the Fe dissolution ratio showed a local maximum with increasing CaO/SiO2 ratio.

Mar 1, 2017

"Many industrial processes involve materials that are subject to temperature change and thermal stress. Examples range from the casting of large metallic products to the cooling and reliability of small electronic components. Thermally induced stress is a major concern as it can lead to material damage and product failure. Material properties, thermal and mechanical, and process conditions such as the size and location of a feeder in metals casting, or the power dissipation in a computer chip, will govern the magnitude of these stresses. Temperature may also be influenced by fluid flow, for example, the airflow over a computer chip in a laptop will govern the rate of heat extraction, hence the temperature gradients in the chip and the evolving thermal stresses.This paper provides details on the governing equations for heat transfer (temperature) and solid mechanics (stress), their degree of coupling, and the numerical techniques used to solve them. Three examples are discussed to illustrate the use thermomechanical modelling. These also provide an insight into the degree of coupling required between the equations. The first example, involves thermal cycling of electronic components where a prescribed temperature field is applied. As temperature is known, this example only requires the solution of the stress equation. The second example also involves the modelling of an electronic component where the temperature field is also calculated. In both of these examples, the stress calculation is dependent on the temperature field, but the temperature calculation is not dependent of the solution of the stress equation (one-way coupling). The final example provides details on modelling the metals casting process. Both the temperature and stress equations are solved but, unlike the previous two examples, in this case the temperature field is dependent on the results from the stress calculation (two-way coupling)."

Jan 1, 2001

By R. D. Lrwin, W. M. Mullins, S. Venugopa, J. C. Malas

"Physical models for acoustic emission (AE) are introduced and expressions are derived to predict AE activity from such parameters as applied stress, strain and strain-rate. These models are then incorporated into a visco-plastic finite-element simulation program, and the acoustic emission event rate generated during metal forming operations are predicted. Simulation results are presented for upsetting operations on a typical C-Mn type steel for various friction and die geometry conditions. The AE model predictions compare well with the limited available experimental results reported in the literature and demonstrate that AE signatures can be reliably simulated. The signatures predicted for metal forging are fairly insensitive to processing parameter changes. This suggests that AE event rate monitoring may not be well suited to process monitoring for forging. However, the size of the features is conjectured to influence the frequency content of the AE signals. Thus, since current simulations include only the ability to predict the number of events for a set of processing conditions, future work is required to simulate the duration and magnitude of acoustic events. Fourier analysis techniques may then be applied to investigate correlation with microstructural features.IntroductionThe open loop control system method for deformation processing design, as described by Malas et al. [1 ], consists of several steps in series to achieve the final design. The first step uses microstructure development models to determine the optimum deformation path to achieve the desired final microstructure. The second step, the process model, calculates the processing parameters required to achieve this deformation path. Finally, the metal-working system uses the required processing parameters to produce the part. Figure 1 shows this in block diagram form"

Jan 1, 1997

By L. Xia

Sodium silicate(s), also known as “water glass”, are one of the oldest and most widely used industrial chemicals. Its first use in Canadian operations can be traced back to around 1925, which coincided with early use of xanthates in mineral flotation. Silicate functions as a sulphide and non-sulphide gangue mineral dispersant, depressant and modifying reagent in grinding and flotation operations. It is believed that soluble sodium silicate promotes selectivity of value added sulphides against gangue minerals, resulting in both grade and recovery improvement. This paper seeks to link improved grade/recovery to the interaction characteristics of minerals and the sodium silicate. A systematic study was performed with individual mineral species, an artificially designed model ore and the feed ore from a copper flotation operation. The function of sodium silicate was evaluated in the context of colloidal chemistry and linked to mineral surface chemistry. Measurement of pulp rheology and mineral zeta potential identified that sodium silicate works as a dispersant. The dispersion is accomplished by increasing a mineral’s net surface charge, resulting in a change in slurry viscosity. Bench scale laboratory flotation tests suggest that better dispersion leads to a diminished interaction of chalcopyrite with gangue. The improved Cu grade and recovery then are likely in response to an increased accessibility to collector along with a linked increase in particle bubble attachment resulting in better separation efficiency. ToF-SIMS surface chemical analysis of the flotation samples found a higher proportion of sodium silicate on minerals from the flotation tailings relative to the concentrates. Moreover, attachment of sodium silicate appears to be mineral specific; the data indicates that sodium silicate favours the surface of gangue phases over the value sulphides.