By Luben Xie, Lin Hu, Qiang Wang, Min Gan, Tao Jiang, Wenqi Li, Xiaohui Fan, Zhiyuan Yu

"Crystal precipitation behavior of calcium ferrite (CF) during iron ore sintering process along with the effect of cooling rate, SiO2 and Al2O3 on crystalline condensation were studied. The results show that CF, has strong ability of precipitation. The precipitation is barely affected by extenal factors. It begins to precipitate when the liquid phase cools down to about 1200oC. CF could crystallize rapidly at the cooling speed of 150 °C /min. Furthermore, decreasing of the cooling rate favors the development of crystal. Binder phase transformed from CF system to silicate system when SiO2 content was increased to 5~6%, with a constant basicity (R) 2.0. Increasing Al2O3 content could promote the precipitation of CF and the development of crystal.IntroductionCrystalline condensation is the last stage of sinter mineralization. It includes the processes that crystalline substance and amorphous substance precipitate from high temperature solution phase and the consolidation of material when melt cools down. During the crystallization process, minerals precipitate following the order from high to low melting point coupled with the decreases of free energy. Most of binder phase minerals and part of iron oxides crystallize in this process, which have an important influence on mineral composition and microstructure of sinter. They finally determine the sinter strength and metallurgical properties."

Jan 1, 2011

By Takeo Fujino, Nobuaki Sato, Yarong Wang, Kohta Yamada

"Ternary mixed sulfides of some transition metals MTS3 (M=Ba, ·Pb, T=Ti, Zr) were synthesized by a relatively low temperature process using sulfur melt. The mixture of starting materials, such as, metals and/or binary sulfides and a large excess of sulfur was reacted in a vacuum-sealed Pyrex or quartz ampoule at 350- 600 °C for one to three weeks. After the reaction, the remaining sulfur was completely removed by a process composed of filtration of sulfur melt and followed dissolution in CS2• The binary sulfides impurities coexisted in the products were removed by rinsing the products in water and acetone. By using the above method, BaTiS3, PbTiS3 and BaZrS3 'Were obtained in pure form. The effect of addition of halides on the yields of these ternary sulfides were also discussed.IntroductionThere have been a vast number of studies on the preparation and physical and /or chemical properties of mixed metal oxides. As is well known, some of such compounds exhibit excellent materials properties, causing them for use in mechanical, electronic, magnetic and chemical devices. Not a few mixed metal sulfides show similar physico-chemical properties to those of the corresponding mixed metal oxides. However, the study of the mixed sulfide crystals is rather sparse mainly due to difficulties in preparing these compounds. In various methods which have been adopted for preparing mixed sulfides, the simplest method would be the solid-solid reaction of the component binary sulfides or elements. However, there are always diffusional constraints with regard to the reactions in solid phases causing it necessary to heat the reactants at sufficiently high temperatures, viz. 800-1200°C. On the other hand, some mixed sulfides are unstable at high temperatures or to change their materials properties due to sulfur nonstoichiometry and structural modification depending on temperature, i.e., synthesis of such compounds needs to be made at lower temperatures. Processing in alkali halide melts is hopeful to overcome the above problems but to obtain the halide melts the temperatures above ~ 600 °C is needed. Low temperature reaction has been carried out for the preparation of Hg1.24TiS4, which was formed by the ·combination of TiS2 and molten Hg metal at 320°C[l]. Reaction of WS2 with LiBH4 melt at 350°C yielded LixWS2[2]. These sophisticated methods, however, can be applied only to the vary special cases."

Jan 1, 2000

By Jintao Gao, Zhancheng Guo, Chong Li

A new approach to enrich MFe and RO phase from the converter slag by super gravity was investigated. The samples obtained by the gravity coefficient G=600 and cooling rate V=5K/min from 1623K to 1373K appeared significant stratification and the MFe gathered at the bottom of sample. With the help of metallographic microscopy and X-ray diffraction, it is found that large quantity of white RO phase gathered at the lower part of the sample as the concentrate, with volume fraction appearing gradient distribution along the direction of super gravity, while the upper part was mainly composed of dicalcium silicate as the tailing. The mass fractions of the FeO, MgO and MnO in the concentrate are up to 40.46%, 6.9% and 3.91%, while that in the tailing are just 11.65%, 2.15% and 1.55%. The recovery ratios of FeO, MgO and MnO in the concentrate are 60.35%, 58.45% and 72.24%, respectively.

Jan 1, 2016

By Hye-Sung Kim, Dong-Wha Kum, Gyeungho Kim

"Mechanical alloying is an effective way to finely distribute inert dispersoids in AI-TM (TM is a transition metal element) systems. It is considered that high melting point aluminides are formed by precipitation from the supersaturated aluminum matrix. The analysis is based on the fact that much higher content of TM than the solubility limit can be dissolved in alpha aluminum during the high energy ball milling. Nonetheless, the role of undissolved TM particles affecting the formation of aluminides is not suitably considered. In this paper, authors present experimental observation on the formation of Ab3Ti particles from mechanically alloyed AI-Ti alloys in the hyper-peritectic region. This study showed that, in the mechanically alloyed AI-20wt%Ti specimen, intermediate phase of cubic Ab3Ti and tetragonal AIz4Tis formed at 300 - 400°C and 400 - 500°C, respectively, before the MA-state reaches to the global equilibrium at higher temperatures. The formation behavior of Lh- Ab3Ti is interpreted by interdiffusion of Al and Ti in solid state based on the fact that large amount of nano-sized Ti particles exist in the milled powder. Present analysis indicated undissolved Ti particles of nanosize should have played an important role initiating the formation of Ab3Ti phase during annealing.IntroductionInterest in the hyper-peritectic AI-Ti alloys is based on industrial demand for high-modulus and high-temperature aluminum alloys. Earlier works on hyper-peritectic AI-Ti alloys with 4 to 12wt%Ti show that these alloys are strong at ambient temperature and maintain high strength above 300°C when titanium-trialuminide (e.g., Ab3Ti) is finely distributed in the aluminum matrix [1,2]. High melting point and high stiffness with low density of AbTi make the AI-Ti alloys strong with greater thermal stability while keeping weight savings as much as possible. Titanium in aluminum shares other merits of transition metal additions because Ti solubility in Al is low (i.e., 1.l5wt%Ti at 665°C and virtually zero below 400°C), and fine dispersion of Ab3Ti particles is readily accomplished and resists grain coarsening effectively."

Jan 1, 1996

By S. N. Sinha

The distribution coefficients of lead and silver between copper and matte phases have been measured at two different temperatures. Experiments covered the ranges of 0.009-1.8, 0.07-0.13, and 0-11 wt pct lead, silver, and iron in matte, respectively. The distribution coefficients of lead have been measured at 1405 and 1505 K and correlated with lead and iron concentrations in metallic copper and matte. The values of the distribution coef¬ficient of lead between copper and iron-free matte, at infinite dilution of lead, have been determined to be 3.60 and 4,06 at 1505 and 1405 K, respectively. The distribution coefficient of silver between copper and iron-free matte is independent of silver concentrations and has been measured to be 2.13 and 2.21 at 1400 and 1500 K, respectively. For an iron-bearing matte, the distribution coefficient of silver has been correlated with iron concentration in the matte at both 1400 and 1500 K. From the measured values of distribution coefficients, the Raoultian activity coefficients of PbS and AgS0.5 in copper-saturated matte have been calculated. At infinite dilution, the following equations correlating the Raoultian activity coeffici¬ents of PbS and AgS0.5 with matte- composition and temperature have been obtained: log Y° PbS =1.515 + 1080/T 0.14 NFes lbS Fog YAgS = -0.074 - 425/T + 0.09 NFes. - 0.5

Jan 1, 1983

Steel Ladle in Bhilai Steel Plant, SAIL, India, passes through VAD & LF-RH route and this exposes refractory lining to a severe operating conditions. Ladles are lined with in-house manufactured MgO-C refractories. Lining life used to be 35 heats, out of which 18-20 heats were through VAD/LF-RH, hence, ladle availability had become a constraint. Laboratory studies were carried-out to optimize granulometry and composition. Granulometry was developed by adopting Andearssen packing model. A suitable plasiticiser was identified to eliminate inconsistency caused due to variation in resin quality and weather condition. It reduced variation in green bulk density from 6 to 1.3%. Abrasion and slag erosion studies were conducted, which shows that with increase of carbon, abrasion resistance decreases and corrosion resistance improves. Based on these studies, graphite in slag zone was increased from 10 to 12.5% and in metal zone it was reduced to 7.5%. Different process parameters of brick making were optimized to make MgO-C bricks of maximum bulk density with reduced coke porosity. Modified bricks have bulk density of 2.99-3.02 g/cc and coke porosity of 9.5-10.5%. Further, shape of the bricks were changed from side arch to mini keys and thickness was increased from 80 to 100 mm. Mini key bricks are pressed from sides, thus eliminating variation in thickness which is critical dimension for dry joints. These modifications improved average lining life of steel ladles to 64 heats, which includes 37-40 secondary heats. Maximum life obtained is 87 heats.

Jan 1, 2006

By J. W. Bridge

Triaxial compression tests at various confining pressures and temperatures, as well as tangent modulus tests using ultrasonic waves, were conducted for wax-coated granular composite materials. The material used is a surface for Thoroughbred horse racing. The purpose of these tests is to examine how track shear strength and tangent modulus at a range of loads respond to changing temperatures. Previous work has shown that a wide range of operational temperatures are experienced which have been reproduced in the lab. Using differential scanning calorimetry, it is confirmed that these operational temperatures correspond to distinct thermal transition regions for the wax that is used to coat the sand in these surfaces. Preliminary results show that both shear strength and tangent modulus are sensitive to temperature changes with maximum strength and modulus correlating with major DSC wax transition regions.

Jan 1, 2010

By Pinakin C. Chaubal

An industry ? university consortium was set up to develop advanced tools necessary to understanding of the various phenomena occurring in the hearth of the modern iron making blast furnace. The major driver for this work was to provide the technological support required to extend campaign life of blast furnaces, which, by current agreement is tied to the life of the furnace hearth. The hearth wear is significantly affected by the hot metal velocity, temperature distribution and refractory temperatures. Due to the difficulty in making measurements inside the hearth, novel approaches to gain a fundamental understanding of the detailed physical and chemical processes in the hearth must be developed. The approach used in this project was to develop a 3-D CFD (Computational Fluid Dynamics) model coupled with extensive validation efforts. The CFD model is being utilized (1) to understand the phenomena in the hearth, (2) to understand the impact of changes in the internal conditions of the hearth on wear patterns; and (3) to design a monitoring/controlling system for prolonging campaign. In this paper, the results will be reviewed.

Jan 1, 2006

By Aichun Zhao, Rui Wang, Yihong Li, Yanping Bao, Yafeng Ji, Jiansheng Liu, Xiao Hu, Qingxue Huang

The slag entrapment under different conditions of 80t blowing argon ladle furnace was investigated by physical simulation. The water was used to simulate liquid steel and liquid paraffin was for slag. The processing of slag entrapment under different blowing structures was analyzed and the critical velocity and critical droplets diameter of describing it was obtained. Based on the experiments, the relationship between the interface flow velocity and the critical blowing rate CBR was deduced. In the real process, it is suggested that the bottom blowing rate is from 40 L/min to 180L/min when the interface tension is 0.12~1.2 N/m during the soft argon blowing.

Jan 1, 2016

Segregation roasting tests were carried out on Zaire cobalt oxide ores assaying about 2% Co and 3.5 to 6.5% Cu. The major parameters tested during the laboratory investigations were temperature, dosage and type of reducing agent, dosage and type of chloridizing agent, and particle size. Results showed that standard conditions suited to the segregation of copper ores, i.e. low temperature and low dosages of reducing and chloridizing agents, resulted in the segregation of copper only, while conditions suited to the segregation of lateritic nickel, i.e. higher temperature and increased dosages of reducing and chloridizing agents, led to a successful segregation of both copper and cobalt. Under the best conditions, 88% of the cobalt and 98% of the copper could be recovered in a concentrate assaying 32.5% Cu and 8.5% Co. Alternatives to process such a concentrate are briefly reviewed.

Jan 1, 1993

By Carl W. Lam

The increased obsolescence rate of electronic products has made it evermore pertinent to understand the potential environmental impact of materials choices to help guide electronic waste (e-waste) management and promote awareness of high burden materials. Methods for screening for the performance of materials and their potential burden on human health and the environment can be used to comparatively select constituents of present and prospective electronic products. These methods should be able to yield more robust information when linked to other decision-making strategies where integrated data on consumer preferences, production quantities, and regulatory initiatives are sparse or unavailable. A framework is presented here for generating metrics of ecological toxicity, human health toxicity (cancer and non-cancer categories) and global resource consumption for evaluating environmental impact of materials (specifically metals) in electronic products. The time-dependent impact trends of United States? printed wiring board (PWB) metals usage, principally derive

Jan 1, 2010

By Rodney J. Ishak

The reduction of Mn3O4 to MnO has been investigated in a thermobalance apparatus. The charge was composed of manganese ore (decomposed by heating/calcination or pre-reduction to mainly Mn304) and coke. The material was charged to a crucible, which was suspended in the balance. CO-gas was distributed through a grid in the bottom of the crucible. Two sizes of ores were used; 2.4-4.8 mm and 6.7-9.5 mm. Coke particles were in the size range 4.8-6.7 mm. Experiments were conducted in the 900-1100°C temperature range. The composition of the product gas was monitored continuously. External mass transport between bulk gas and particle surface does not seem to limit the rate of reduction. Assuming that both diffusion through product layer and chemical reaction at the interface between MnO and Mn304 are rate controlling, the data was tried both in a shrinking core model and in a grain model using regression. The grain model gives the best physical description of the process, because the reactant is in fact a porous medium. With this model the effective diffusivity was calculated to be in the 1.5-6.10-5 m2/s range. The pore size was mainly between 0.1 and 10 um.

Jan 1, 2003

By Junli Xu, Xianwei Hu, Kaiyu Xie, Liangxing Li, Zhongning Shi, Zhaowen Wang, Bingliang Gao, Aimin Liu

Al-Ti master alloys were prepared by aluminothermic reduction between the dissolved titanium dioxide and aluminum in cryolite melts at 960oC. The kinetic analysis by differential scanning calorimetry indicated that the apparent activation energy of the reaction of reducing titanium dioxide by aluminium is 22.3 kJ/mol, and the reaction order is 0.5. The products were analyzed by means of X-ray diffraction, X-ray fluorescence, scanning electron microscopy and energy dispersive spectrometer. Results from X-ray diffraction showed that the phase compositions of produced alloys are Al and Al3Ti. In addition, Al-Ti master alloys containing 2-6 mass% Ti were formed at different reduction time of 2-5h in aluminothermic reduction experiment.

Jan 1, 2015

By C. T. Philipp

Recycling of waste is much preferred over disposal. This paper discusses the Enviroscience, Inc. (ESI) process, now being commercialized by MetWool, Inc., to recycle hazardous wastes using an extractive metallurgical process which is followed by vitrification of non-reducible metal oxides. In this process, volatile and reducible metals are reclaimed as their respective oxides and elements.

Jan 1, 1995

By Takeshi Yoshikawa

For the sake of effective control of titanium-compound inclusions in the steel-making processes, especially for stainless steel production, the influences of alloying elements of chromium, nickel, manganese, molybdenum, copper and oxygen on the thermodynamic property of titanium in molten iron were investigated at 1873K. At a certain titanium potential controlled by the coexistence of Ti3O5 and Ti2O3 doubly saturation of steels, the interaction parameters between alloying elements and titanium in molten iron were determined as follows. [ ] From the investigations on the equilibrium of titanium deoxidation in molten iron, the activity coefficient of titanium and the first order interaction parameter between oxygen and titanium were determined as follows. [ ] Also, deoxidation equilibrium for titanium in molten 304 stainless steel was measured and compared with the calculated results using the determined interaction parameters.

Jan 1, 2006

By Sung-Mo Jung

Experiments were carried out on a system with artificially prepared slags in a graphite crucible, in order to examine the possibility of recycling BOF slags produced in the steelmaking process. More than 80% of FeO and P2O5 was reduced within 20 minutes and the FeO reduction rate was greater than that of P2O5. P2O5 reduction began after more than 60% of FeO was reduced. Increasing slag basicity enhanced the reduction of FeO and P2O5. Temperature also improved slag reduction. The overall reduction rate was controlled by the chemical reaction at the slag/carbon interface. The reduction rates of FeO and P2O5 were second and first order with respect to their respective contents. Most of the reduced phosphorous is believed to vaporize in the form of P2 gas.

Jan 1, 2006

By Shadia Ikhmayies

Thermo-Calc software was used to investigate the phase diagram of the calcium silicon (Ca–Si) system for the range of Si mass percent 0–100, and temperature range T = 200–1800 K. The melting points of Ca and Si deduced from the phase diagram are very close to the values obtained experimentally. Three stable intermediate solid phases were found, which are Ca2Si, CaSi, and CaSi2, where the first one appeared in the Ca rich side of the phase diagram, and the third one in the Si rich side. In addition, three eutectic points were found at Si mass percents of 3.95, 33.00, 62, and temperatures T = 1048.7, 1519.14, 1308.5 K respectively. Atomic Si (Diamond structure) is found mixed with CaSi2 intermediate phase for temperatures less than 1305 K, and mixed with a liquid CaSi for higher temperatures. These results are important for thermodynamic and metallurgic studies of these intermediate phases.

Mar 1, 2018

By María Cristina Ruiz

Enargite rich copper concentrates can not be treated by conventional smelting/converting technology and thus nonconventional methods such as leaching must be used. Since enargite (Cu3AsS4) is a hard to dissolve mineral in acidic solutions, pyrite, a common impurity in copper concentrates, could be used to increase the enargite dissolution rate. On this matter, we present in this work experimental data on the pressure leaching of a mixed enargite-pyrite concentrate in H2SO4-O2. The results show that the dissolution of enargite from the mixed concentrate is considerably faster than the dissolution of pure enargite mineral. The leaching rate increases significantly with temperature. Over 98% of enargite was dissolved in leaching 64 micron size particles at 200 ºC and 100 psi of partial pressure of oxygen in just 30 minutes. A change in the partial pressure of oxygen from 50 to 150 psi showed also a large influence in the leaching rate.

Jan 1, 2010

By Toshiyuki Hashida, Victor M. Lopez-Hirata

"Small-punch tests and determination of fracture toughness JIC were conducted at 4 and 77 K on new cryogenic JN1, JJ1 and JK2 austenitic stainless steels, after isothermal aging. Equivalent fracture strain ?qf determined by measuring the reduction of thickness in the small-punch test specimen. A linear dependence of JIC on ?qf was found in these new materials. Regression analysis of experimental data produced the following linear relation JIC = 1304.1 ?qf + 8.09 [kJm-2]. An analysis of present work relation was pursued on the basis of material properties and evaluation method of he. Results showed that the slope value has a strong dependence on material yield strength and JIC evaluation method. This linear relation is useful for the evaluation of fracture toughness JIC, measuring the equivalent fracture strain ?qf by means of small-punch test. Thus it can be useful for assessing the degradation of fracture toughness in small areas such as, the heat-affected zone in welded components.IntroductionCryogenic structural materials for superconducting magnets of fusion nuclear reactor are required to possess a good combination of strength and toughness. The mechanical properties are required beyond the capability of conventional austenitic stainless steels [1]. New cryogenic JN1, JJ1 and JK2 austenitic stainless steels were developed by the Japan Atomic Energy Research Institute (JAERI) [1]. The structure of superconducting magnets is constructed by welding of 200 = thick plates of these steels, which are solution treated at high temperatures and then water-quenched to avoid intergranular precipitation. However, the welding process involves heating and cooling [2], which cause microstructural changes in both base metal and weld. In this heterogeneous microstructure, it is important to estimate the fracture toughness of these materials at cryogenic temperatures. Therefore, it is necessary to evaluate the effect of aging process on the fracture toughness behavior of these new steels. To determine the cryogenic fracture toughness, the elastic-plastic JIC value has been co=only used [2]; however, the specimen size is much larger than heat-affected zones in welded components. Small-punch (SP) testing method, employing miniature specimens, has permitted to evaluate the fracture toughness behavior at different temperatures in different nuclear reactor materials [3,4]. Mao et al. [5,6] and Misawa et al. [7] found a linear relation between JIC value and equivalent fracture strain ?qf, determined by SP method in non-ferrous alloys and ferritic steels at room temperature and austenitic stainless steels at 4 and 77 K, respectively. So that, this kind of correlation would be very useful to assess the fracture toughness JICe values by means of SP test in small zones of welded components."

Jan 1, 2012

By Zhang Chuanfu

Keywords: modified coprecipitation method, Ni-Co alloy powders, solid-solution oxalate, growth mechanism Homogeneous solid-solution oxalates of Ni2+ and Co2+ ions were synthesized by modified coprecipitation method and the composition and morphology of the fibrous solid-solution oxalates precursor were characterized by XRD, IR, DTA/TG and SEM analysis. The effects of feeding methods, pH values, precipitation temperature, reactant concentration, addition surfactant, alcohol washing and drying process on the morphology and dispersion of the precursor were investigated in detail. The experimental results showed that the coprecipitated powders have characteristics that are different from those of the mechanical mixtures with the same stoichiometry. Based on the observations of precursors growth and SEM morphology of the precursor, the oriented attachment was proposed for the well-aligned growth of the fibrous Ni-Co alloy precursor particles.

Jan 1, 2005