By Yoichi Takeda

Copper solubility in SiO2-CaO-FeOx slag equilibrated with copper matte in 10% SO2 atmosphere at 1573K was estimated. Essential parameters are activity coefficients of copper oxide and sulfide, oxygen and sulfur potentials and activity of copper in the slag-matte system. A large number of experiments provide proper parameters to calculate copper solubility in slag, A classical thcrmodynamic model postulating CuO0.5 and CuS0.5 moleculcs assists in estimating copper solubility in slag. Additions of Si02 and CaO reduce copper solubility almost in any condition. Copper loss, that is function copper solubility and slag volume, in the silica saturated SiO2-FeO. binary slag is minimally equilibrated with less than 66% copper matte while copper loss in the 50% FeO.-SiO2-CaO ternary slag saturated with 2CaOSiO2 is minimally equilibrated with over 66% copper matte. This slag composition has potential for continuous copper converting, direct copper production or high-grade matte production.

Jan 1, 2003

By Jian Wang, Hongyang Cao, Binxiu Wu, Junhong Li, Jimin Wang

"The enrichment and separation of scattered metal indium component in the pressure leaching solution with sulfuric acid from vacuum furnace germanium slag were studied by iron substitute and P204 extraction, which is supplied by shaoguan smelter. The experimental results show that the extracting power of P204 for indium from pressure leach solution is powerful. The optimal technological condition were the ratio of P204 and sulphonating serosene 3:7, phase ratio 1:3, solution pH 1.2, and extracting 5 minute. The enrichment indium solution of 21.7 g/L In at 95.2% recovery ratio was obtained by three-stage counter flow extraction and four- stage counter flow stripping.IntroductionScattered metals, such as Indium and germanium, were inriched as intermediate product or by-product during the metallurgy process of other non-ferrous metals, such as lead, zinc, copper and tin. For example, the indium and germanium were inriched in vacuum furnace germanium slag, which is the by-product of zinc vacuum distillation operation from hard zinc. It is difficult to recovery the indium from the vacuum furnace germanium slag, because the indium content is low, and the chemical composition and phase compositon were complex.Recovery indium from bearing indium zinc slag was researched extensively, such as pressure acid leaching, high temperature evaporation, solvent extraction method[l-7], acid leaching method has the advantages of high leaching rate, which can be separated hydrochloric acid, sulfuric acid and silicon fluoride acid systems. Solvent extraction method has the advantages of low production cost, fast reaction speed, high enrichment ratio, and simple operation."

Jan 1, 2013

By Katsuyoshi Kondoh

The utilization of silica particles originated in rice husks as reinforcements of magnesium composites was discussed. By using the solid state reaction of rice husk silica particles with magnesium powder, P/M magnesium based composites dispersed with the magnesium silicide (Mg2Si) and magnesium oxide (MgO) were fabricated. High-purity silica particles were originated from rice husks, one of the major agricultural wastes, via the citric acid leaching treatment and combustion in air. The effects of the silica particle characteristics such as size, crystalline and porous structures, on the reactivity of silica and magnesium to synthesize Mg2Si intermetallic were discussed. Amorphous silica was more useful for this reaction than crystalline one. The reactivity of rice husk silica was superior to that of the conventional mineral silica particles because of not only its amorphous structure but the larger specific surface area due to their pore structures. In the case of the green compact of the mixture of the rice husk silica and Mg powder, the silica particle size was not effective on the reactivity because the coarse particles were fractured into fine ones by cold compaction. The distribution of Mg2Si intermetallics of magnesium powder composites consolidated by SPS process was investigated by XRD and SEM-EDS analysis. Their mechanical and physical properties were also evaluated in detail.

Jan 1, 2009

By G. A. Brooks, R. W. Matusewicz, Nazmul Huda

"A computational fluid dynamic (CFD) model of a conventional tuyere blown slag fuming furnace has been developed in Eulerian multiphase flow approach. The model was developed by coupling CFD with kinetics equations developed by Richards et al. for zinc fuming furnaces. The model integrates submerged coal combustion and chemical reactions with the heat, mass and momentum interfacial interaction between the phases in the system. The model predicts the velocity, temperature field of the molten slag bath, generated turbulence, vortex and coal utilization behavior from the slag bath. The highest coal penetration distance was found to be at l/L = 0.2, where / is the distance from the tuyere tip and L is the total length (2.44m) of the modeled furnace. The model also predicts that 10% of the injected coal bypasses the tuyere gas stream un-combusted and carried to the free surface, which contributes to ZnO reduction near the free surface.IntroductionSignificant metal values are often discarded with slag in the form of metal oxide produced by the smelting industries. These metal values can be recovered from the slag by proper treatment. Zinc slag fuming is such a process, where a reductant source (usually coal) is injected in the molten slag bath to reduce dissolved ZnO from the bath into metallic zinc vapour. The process can be carried out in either conventional tuyere blown furnace or top submerged lance (TSL) smelting furnace. Conventional slag fuming processes are carried out on batch basis in a rectangular tuyere blown furnace. Approximately 50 tonnes of charge (either molten slag or solid slag) is fed to the furnace at the beginning of each fuming cycle. Two opposing sets of submerged tuyeres are employed to inject air and pulverized coal into the molten slag bath to carry out combustion and reducing reactions."

Jan 1, 2012

By Beatryz C. Mendes, Igor K. R. Andrade, Roseli O. G. Martins, Gustavo H. Nalon, Rita de C. S. S. Alvarenga, Leonardo G. Pedroti, Carol F. R. Santos, Marcelo A. Alves

This work presents an experimental investigation of the influence of concrete blocks and mortar’s compressive strength on the flexural bond strength, normal to the bed joints, of concrete structural masonry. Third-point beam tests were performed on concrete prisms, considering two different kinds of concrete blocks (compressive strength of 5.9 and 8.2 MPa) and six different cement-lime mortar compositions (compressive strength around 30, 70, and 120% of the blocks’ net area compressive strength). Units’ absorption and mortar’s initial flow and water retentivity were not varied, but remained within the suitable range for use in structural masonry. For both types of concrete blocks, it was observed an increase on the prism’s flexural bond strength with the increase of the mortars’ compressive strength. A lower mortar’s water-cement ratio led to higher bond strength. When fixing the ratio between mortar’s and concrete block’s compressive strength, it was noticed that the increase on the blocks’ strength contributed to a slight increase on the masonry’s flexural bond strength, except when using high strength mortar, in which the increase was significantly greater.

Mar 1, 2018

By N. L. Piret

Reprocessing of low zinc-bearing residuals with a zinc content of less than 10%, originating from the iron and steel industry, has been given more and more attention in the last few years, due to the potential landfill liability and the increasing cost of disposal by dumping. Whereas, recycling of hazardous electric arc furnace dust is already being performed commercially on a large scale in the U.S., Japan and Western Europe, almost no reprocessing takes place in the case of these low grade zinc-bearing materials. In blast furnaces and basic oxygen furnaces dusts and / or sludges are generated at a rate of 1 to 2 % of the respective production. The technologies for the retreatment of these types of materials, either commercially available or still being developed are briefly described hereafter. They involve internal recycling, upgrading by physical separation methods, separate hydrometallurgical processing and pyrometallurgical treatment. Their scope and limitations are critically assessed in terms of technological applicability, economic feasibility and environmental compatibility. Since, the possibtlity of achieving economic profitability is unlikely with this type of material, the main criteria for acceptability of the treatment process are: generation of a iron-rich material, suitable for treatment by the iron/steel industry, acceptance of the non--ferrous metal-bearing sub-product by zinc smelters, generation of non-hazardous waste materials.

Jan 1, 1992

By Yang Guangqing, Shao Jiugang, Zhang Jianliang, Wan Dan, Fu Yuandi, Guo Hongwei

"Resource of metallurgical coke is becoming scarce, and although coke can be partially replaced by pulverized coal injection, there are many restrictions for further increase in coal ratio. Mixed charge of ore and lump coal from top to replace more coke was studied in this paper. Softening-melting property of the burden was affected by charge of lump coal. Softening-melting properties of mixed charge of ore and coke, mixed charge of ore and lump coal were tested respectively. Results show: the property of the burden mixed with coke is superior to the burden mixed with lump coal; lump coal would not deteriorate softening-melting property of the burden and some of them can even improve softening-melting property of the burden. Top charge of lump coal would not deteriorate softening-melting process, and this should be a new way to increase coal consumption to decrease coke rate.IntroductionThe blast furnace is still the predominant process for the reduction of iron ore and will probably remain so for the next decades. Metallurgical coke is becoming scarce and expensive, so the cost of hot metal can be decreased by reducing the consumption of metallurgical coke[l]. Coke can be partially replaced by pulverized coal injection, currently the highest rate of pulverized coal reached 266kg/tHM, most of blast furnace PCR is about 150kg/tHM, and it is very difficult to further increase of PCR. Nut coke is charged into blast furnace mixed with iron ore, not only for improving utilization of metallurgical coke, but also for lowering the coke rate. Presently the majority of blast furnaces in the world use nut coke although its amount is very different: from 10-20 to 70--100 kg/tHM and more[2-4].The effect ofnut coke in blast furnace is extensively researched, and the main conclusions recommend: to improve gas permeability of cohesive layer in blast furnace, to promote reduction of iron burden, protect metallurgical coke from the solution in the shaft due to higher reactivity of nut coke. There is no special requirement for the strength of nut coke[5-8]. Nut coke is also used for sintering fuel, which may lead to the shortage of the nut coke charging into blast furnace. So lump coal mixed with iron ore is considered to be charged into the blast furnace, not only to reduce the cost of grinding coal, but also to increase the use amount of coal."

Jan 1, 2013

By Xin Li, Zurui Hu, Fuming Zhang

High blast temperature is one of the important technical characteristics of modern blast furnace (BF), which is also an important technical approach for the green development of ironmaking. Increase blast temperature can improve and promote the BF operation smooth and stable, reduce coke rate, fuel consumption and CO2 emission. Top combustion hot blast stove technology has been applied in Shougang Jingtang’s 5500 m3 BF for 8 years. Under the condition of burning single BF gas, high efficiency energy conversion and over 1250 °C high blast temperature have achieved. The combustion and heat transformation process were researched by numerical simulation technology to optimize the structure design. The high efficiency annular ceramic burner and checker brick were developed and applied, the flue gas waste heat was recovered and reused to preheat the combustion air and gas. Prominent achievement of high blast temperature under the condition single BF gas burning has been realized.

Mar 1, 2018

By Noel A. Warner

Modern steelmaking is based on direct use of oxygen in high intensity batch reactors. A totally new approach is proposed in this paper, based on the view that pursuit of high intensity is unlikely to lead to successful coal-based continuous steelmaking. By substituting carbon dioxide and water vapor as the oxidants rather than using oxygen directly, the intensity is greatly reduced. Accordingly. subsurface formation of carbon monoxide bubbles can be avoided by careful manipulation of the three participating rate processes, gaseous diffusion, interfacial chemical kinetics and liquid phase mass transfer. Steelmaking can then be carried out without explosive ejection of molten droplets and the generation of micro-spray but rather in a controlled and fumeless fashion. The vital component is the introduction of generic melt circulation technology. Three melt circulation loops in series are envisaged. Starting with a composite feed of iron ore fines, pulverized coal and lime flux, a metallized solid raft floating on molten iron is propelled out of the ironmaking loop onto the first of two downstream steelmaking loops. In the first, a liquid slag is formed, primary decarburization is undertaken not with oxygen but rather with CO2 and H2O and the melt is desulfurized. The semi-product stream enters the third melt circulation loop, where open-channel decarburization is effected along with dephosphorization to yield a low carbon steel product. Alternatively, the melt leaves the last loop to irrigate a packed tower countercurrent to argon at around 100 mbar to continuously produce ultra-low carbon (ULC) steel.

Jan 1, 2003

By Jewel A. G. Gomes

Electrocoagulation (EC) has been performed with Al-Fe electrode system with changing polarity for the removal of arsenic from water. The removal process has been studied using ICP-AES and Anodic Stripping Voltammetry with a wide range of arsenic concentration (1-1000 ppm) at various pH (4-10) and residence times (1-60 min). Electrochemically generated by-products have been analyzed using XRD, FTIR, XPS, SEM/EDS and Mössbauer Spectroscopy. Results revealed expected crystalline iron oxides (magnetite (Fe3O4), lepidocrocite (FeO(OH)), iron oxide (FeO)) and aluminum oxides (bayerite (Al(OH)3), diaspore (AlO(OH)), mansfieldite (AlAsO4?2(H2O)), as well as some interaction between the phases. The amorphous or ultra-fine particular phase was also found in the floc. The substitution of Fe3+ ions by Al3+ ions in the solid surface has been observed, indicating an alternative removal mechanism of arsenic in these metal hydroxides and oxyhydroxides by providing larger surface area for arsenic adsorption via retarding the crystalline formation of iron oxides.

Jan 1, 2006

By Sheikh Abdul Rezan, M. N. Ahmad Fauzi, Yong Jing Hui, NORLIA BAHARUN, Noor Izah Shoparwe, Srimala Sreekantan

In this paper, the effect of carbon reductant on carbothermal reduction and nitridation of copper-doped titanium oxide (Cu–TiO ) was investigated.

Mar 1, 2017

By W. H. (Bill) Jay

The destruction of cyanide creates a significant impost on the financial returns of gold mines. These losses increase substantially when ores containing cyanide-soluble copper are treated. Failure to remove or destroy free or WAD cyanide before it is discharged into tailings dams has, on a number of occasions, led to significant fish, bird and animal deaths. Thus, the retention of cyanide within the leach circuit and the recovery or removal of stable metal cyanide complexes needs to become standard practice for all gold mining operations. Furthermore, reducing cyanide purchases will minimise the quantity of cyanide transported to the mine site thereby reducing the opportunity for spillage of this chemical. Many different physical and chemical methods have been investigated for the removal of cyanide from process solutions. All cyanide destruction methods create a financial impost on the economic viability of the gold mine. To reduce these costs, the recycle of cyanide and the economic recovery of the metals solubilised by cyanide is of prime importance. The alternative methods currently in use, or under consideration for the treatment of copper cyanide, entail high reagent costs, produce the recovered metal in a contaminated form and require the safe handling of hydrogen cyanide. These processes will be briefly discussed within this report Environmental and financial benefits are enhanced by recent laboratory and pilot plant studies conducted by Oretek Limited. The Oretek CPC process for the recovery of copper and the recycle of cyanide from copper cyanide-containing solutions does not require pH adjustment to the alkaline cyanide leach conditions. Copper ions are coordinated to a water-soluble and/or an organic soluble polychelating agent under alkaline conditions and the cyanide ions are displaced Membrane separation, or phase separation of the polychelated copper from the cyanide ions enables the cyanide ions to be recycled and the copper to be directly electrowon from the polychelating polymer. The polychelating polymer is then recycled. Ion exchange resins and solvent extraction systems which may be incorporated into the above process will also be discussed in detail.

Jan 1, 1998

By C. Isaac Garcia, Sihai Jiao, Anthony J. DeArdo

"A practical model based on the Hill analysis has been developed to calculate the Lankford value of interstitial free (IF) steels and its distribution in different rolling directions, by considering only a few selected texture components. The Texture Intensity Ratio (TIR), i.e. (111 ) /(100), was used in the model to describe texture. By using the new TIR parameter, the texture-based prediction models can be used more easily to predict the Lankford value in a rather straightforward way.IntroductionThe deep drawing capacity of sheet steels is generally indicated by the Lankford value, which is mainly determined by the texture in steels1. Traditionally, various models derived from the Taylor model are employed to calculate the Lankford value from the texture2-4. In such models, the plastic deformation of steel is assumed to be the result of the slip of dislocations in certain slip systems, i.e., by either pencil glide or restraint glide. The slip direction is the <111> direction. In the case of pencil glide, the slip is thought to be possible in all crystal planes with the <111> crystal direction. Assuming the material is elongated in the X1-direction by d n and compressed in the X2 and x3-direction by qd n and (l-q)d n, respectively, corresponding to a deformation tensor"

Jan 1, 2001

By Hideaki Tokuyama

Recovery of Ni from acidic wastewater of metal surface treatment has been investigated for reuse of the metal and water. Ion exchange equilibria between Ni ion and a strong acid cation resin, DIAION SKIB, and effective diffusivity in resin particle have been studied and they related to the concentration of HCI. The amount of adsorbed Ni for unit quantity of resin decreases with the increase in HCI concentration. This trend is remarkable for acid concentration above 0.1 kmol/m3,. The exchanging ratio of Ni2+ to H+ in resin particle is I/2 and the values of equilibrium coefficient K and maximum exchange capacity Q are I.62 and 3.16 keq/m3 -dry resin, respectively. Effective diffusivity D. determined from the observed breakthrough curve increases with increasing concentration of DC!. A prototype of moving bed has been developed and applied for the recovery of Ni from model solutions of wastewater prepared by mixing HCl and NiCl2. This apparatus allows us to control the resin flow rate by changing the cross sectional area of hole I the Teflon plate installed at the bottom of resin bed. Characteristics of Ni recovery have been clarified under various liquid flow rates. In any case for Q1, Ni ion has been effectively recovered on SKIB resin and the removed fraction was more than 99.5 %. Higher loading ratio of ion is attained at larger liquid flow rate.

Jan 1, 2003

By Xiang Zhang, Junjie Liu, Zhibo Tong, Langsha Shao, Guojun Ma

The aqueous mineral carbonation process that leaching alkaline earth metals from industrial residues by ammonium salt and carbonation thereafter is one of the potential technologies for CO2 sequestration. In this paper, the effect of particle size of waste slag on the leaching rate of metals under a microwave field and effect of microwave irradiation on the carbonation process were investigated. It was found that the initial leaching ratio of Ca decline seriously with the particle size of EAF slag increasing, and the Ca leaching ratio is relatively low during 120 min leaching. The lower leaching ratio of Ca with large particle size is due to the existence of a silica product layer produced on the surface of calcium silicates. Moreover, due to the microwave irradiation, the leaching ratio of calcium and the crystallization rate of calcium carbonate increase, though the particle size and distribution range of calcium carbonate reduce.

Mar 1, 2018

By Cang Daqiang, Li Yu, Liu Xiaoming, Zong Yanbin

"Utilization of high-quality heat in melting slag is a great challenge for iron and steel industry. In the paper, a new method is put forward to concurrently utilize heat and slag by converting the melting slag directly into high valued materials, slag glass-ceramic. A glassceramic with a higher basicity of 0.7 than traditional basicity of 0.45 was prepared from steelmaking slag in order to utilize more hot melting slag. Effects of Alz03 on its crystallization processes were researched by XRF, DTA, XRD and SEM. Results show that Alz03 in glassceramic would have great effected on its property. When the Alz03 content ranges within 12%-15%, glass-ceramics with basicity of0.7 could reach the best performances. The change of dominant phase in glass ceramics from akermanite and wollastonite to akermanite and gehlenite would significantly degrade its mechanical property. An increase of Al2O3 content leads to a rise of the viscosity and crystallization activation energy of the glass, while results in increasing sintering temperature and crystallization temperature of glass, which contributed to its fully crystallization and densification process.IntroductionSteel slag is a by-product under a process of converting iron to steel at above 1600°C, and 0.1-0.15 ton molten steel slag would be discharged for producing per ton of steel in the process. The discharged steel slag at 1600°C has heat of 68 kgce/t. In 2012, China's steel output reached 716 million tons, and produces about 100 million tons of steel slag and 68,000 tee of heat in it [1,2]. But at present, utilization of both slag and its heat at 1600°C is a great challenge for iron and steel industry.Dry granulation of melting steel slag by air and then recovering the heat of the hot air are a traditional technology which have not yet been put into practice for very low heat conductivity of the slag and low efficient of heat exchange among the different processes [3,4]. Therefore, a new method for high efficient utilization of both steel slag and its high temperature sensible heat is put forward [5,6], which is on-line reducing and extracting iron from molten steel slag and then directly preparing glass-ceramic by use of the residual molten slag."

Jan 1, 2014

By Yuanbo Zhang, Zijian Su, Bingbing Liu, Guanghui Li, Tao Jiang

With the depletion of rich manganese ores, high-Fe content manganese ores are becoming the mainstream resources for manganese extraction. Reduction roasting-magnetic separation process is reported as a relatively effective route to realize the separation of manganese and iron. This study investigated the phase transformation of MnO2 and Fe2O3 briquettes (molar ratio 1:1) roasted under various temperatures and CO–CO2 atmospheres. Results showed that when the CO content was in the range of 0–10 vol%, MnxFe3−xO4 (x = 0−1) phase was formed and its content increased with the rising of temperature. The formation of ferromagnetic MnxFe3−xO4 with strong magnetism resulted in an inferior separation of manganese and iron by magnetization roasting-magnetic separation process. With the increase of CO content to over 25 vol%, the MnxFe3−xO4 content decreased while the content of feebly magnetic substance (MnO)y(FeO)1−y(y = 0−1) increased. Further increasing the CO content to over 80 vol%, (MnO)y(FeO)1−y was reduced to MnO and metallic iron.

Mar 1, 2017

By E. Gutierrez-Miravete

A computational method for the simulation of mold filling processes is described. The method is based on the representation of the flowing or deforming medium as a collection of mutually interacting parcels of material. Instantaneous positions of individual material parcels are calculated by numerical integration of the dynamic equations, subject to appropriate initial and boundary conditions. So far, the method has been used to produce qualitative simulations of some flowing and deforming systems encountered in mold filling technology, and our findings are summarized herein. In all cases, individual material particle motions can be followed in detail, allowing critical examination of potentially problematic mold design features.

Jan 1, 1992

By Paul L. Wichlacz

A mathematical model of growth and ferrous iron oxidation for attached bacteria was applied to rotating biological contactor (RBC) units treating acidic mine drainage. The model describes attached bacterial growth as a saturation function, where the rate of substrate utilization is determined by a maximum substrate oxidation rate constant, a half saturation constant, and the concentration of substrate within the RBC. The maximum oxidation rate constant was proportional to flow rate and the substrate concentration in the reactor varied with influent substrate concentration. The model was tested at three separate sites and with three different size RBC units. The ability of the model to predict the rate of iron oxidation under all test conditions was significant. The accuracy of the model was found to be affected by unit size and vary with specific test site.

Jan 1, 1985

By R. C. Hubli

A chemical model has been developed to investigate the dissolution of sulphide minerals in brine solutions containing copper and iron chlorides. The model has been employed to study the dissolution .of synthetic NiS using different initial concentrations of Cu(II), Cu(I), Fe(III) and temperature. The speciation of copper with particular reference to the formation of hydroxy-chlorides as a function of total chloride and H+ has been computed. The model predictions are in agreement with experimental results. It has been found that addition of Fe(III) results in the maintenance of a high Cu(II)/Cu(I) ratio leading to enhanced rates of dissolution and suppresses the loss of Cu(II) due to the formation of hydroxyl-complexes.

Jan 1, 1997