By E. Asselin, P. Sauve, H. Salomon-de-Friedberg

"Residues from the CESL Copper process were leached using the CESL Gold process. The kinetics of reaction were confirmed to be fast with over 50% of the gold consistently extracted within 2 minutes of leaching. Final gold extractions under the conditions tested here were between 80-90% obtained within 90 minutes. A model for the CESL Gold process was developed. This model is slightly different based on whether the copper concentrate leach residue was ground or unground prior to leaching: the gold leaching rate constant is approximately twice as fast for the ground samples. Unground residues had a P80 of 13 ?m whereas ground residues had a P80 of 10 ?m. The model predicts a 43% decrease in leaching time for ground residue versus unground residue to achieve the same extraction under otherwise identical conditions. The model was more accurate for the ground samples. INTRODUCTIONTeck's CESL Process (Jones, 1996) was developed to provide an economically attractive alternative to traditional copper smelting. It has since evolved to also deal with copper concentrates containing valuable impurities such as nickel and undesirable ones, such as arsenic, while reducing downstream costs. Effective recovery of gold and silver is essential to the economics of the CESL Process. The Brook Hunt 2007 copper concentrate assay data (Wood-Mackenzie, 2007) were examined to determine the ratio of gold plus silver value relative to the contained copper. As indicated in Figure 1 below, nearly two-thirds of concentrates have 10% or more of their total value tied up in their precious metals content.CESL has extensively examined the recovery of gold and silver at bench, pilot and demonstration scale, which has culminated in the present CESL Gold Process (Barr et al., 2007). The process targets the precious metal contained in the leach residues produced in the copper portion of the flowsheet. This residue has two primary components which influence downstream processing. The major iron-rich fraction (-75 wt%) of the residue is a mixture of various forms of iron oxide precipitates including hematite and jarosite (Sahu and Asselin, 2011). The iron fraction ranges from amorphous to crystalline in nature depending on the compound precipitated, upstream operating conditions and feed material composition. The lesser, but by no means less important, fraction is a mixture of elemental sulphur and unreacted sulphides (principally pyrite).Elemental sulphur formed during the oxidative leach of the copper concentrate reacts with cyanide to form thiocyanate (SCN-) making a traditional cyanide leach approach too costly. Since the SCN formation reaction strongly depends on contact time with the CESL residues (Po, 2007) short contact times were preferred. This factor guided the development work towards the eventual room temperature, pressure cyanidation process which results in near complete gold dissolution in 90 minutes. A recent CESL gold demonstration campaign treating 1.5 t/d of residue from the copper oxidation step achieved an average gold extraction of 91% (96% maximum)."

Jan 1, 2012

By Jerry M. Whiting, Neil J. Duncan

"Does Canada need a mining industry? Isn't it a chronically depressed collection of businesses that pollute the air and water and tear up the countryside? Wouldn't it be better if Canada's investors devoted their attention to high-technology endeavours, tourism, and other relatively pleasant tasks?Probably the answer to whether Canada needs a mining industry in the 21st century is to look at the real mining industry that is in operation today. The facts indicate that mining is a very important contributor to Canada. It has certainly encountered some challenging times during periods of recession, and it face s severe and continuing problems of cost and competition in world markets. However, uneconomic mines have been closed, others suspended, and productivity has risen dramatically with employment at 77 000, down from 101 000 in 1981. The country's metal and non-metal mines, metallurgical plants and semi-fabricated metals industries employed an estimated 378000 workers in 1986, and paid wages than any other sector of the Canadian economy. This effort resulted in the production of 60 different metals, non-metals and structural minerals valued at $13.5 billion.The trade aspects of the mining industry are of paramount importance. If there is a reason for this situation to change during the next century. it eludes the authors. Canada has the well-developed expertise to discover, evaluate, develop, operate and profit from existing and new businesses based in an enormous area endowed with a nearly unbelievable variety of mineral resources. Many countries throughout the world must rely on producers like Canada, if they are to maintain and/or improve their standard of living."

Jan 1, 1988

By D. D. Macdonald, G. Engelhardt

The accumulation of damage due to localized corrosion [pitting, stress corrosion cracking (SCC), corrosion fatigue (CF), crevice corrosion (CC), and erosion-corrosion (EC)] in complex industrial systems, such as power plants, refineries, desalination systems, etc., poses a threat to continued safe and economic operation, primarily because of the sudden, catastrophic nature of the resulting failures. Of particular interest in managing these forms of damage is the development of robust algorithms that can be used to predict the integrated damage as a function of time and as a function of the operating conditions of the system. Because complex systems of the same design rapidly become unique, due to differences in operating histories, and because failures are rare events, there is generally insufficient data on any given system to derive reliable empirical models that capture the impact of all (or even some) of the important independent variables. Accordingly, empirical models have generally failed to provide a robust basis for predicting the accumulation of corrosion damage in complex systems under realistic operating conditions. The alternative prediction philosophy is determinism, in which the development of damage is described in terms of valid, physico-electrochemical mechanisms with the output being constrained by the natural laws. The differential damage is then integrated along the corrosion evolutionary path for the system (i.e., over the future operating "history") to yield the desired integrated damage, which is the quantity that is most useful to an operator. In this paper, we review the theory of predicting corrosion damage within the framework of Damage Function Analysis (DFA), with particular emphasis on the pitting of aluminum in chloride solutions and on the accumulation of damage from SCC in Type 304 SS components in the primary coolant circuits of Boiling Water (Nuclear) Reactors (BWRs). These cases have been selected to illustrate the various phases through which localized corrosion damage occurs.

Jan 1, 2005

By F. Doxey

Introduction In order to improve outputs and to reduce or hold mining costs, many attempts have been made to mechanize the getting and loading of coal in the major coal producing countries, and machines of various kinds and sizes have been designed and manufactured. Some of the most important are: Joy Continuous Miner Joy Coal Auger Goodman Mining Machine Lee-Norse Koal-Master Jeffrey Colmol Cardox Hordsecg Recovery Drill German Coal Plough British Coal Plough with agitated blades M. & C. Samson Stripper AB Meco-Moore Cutter Loader Joy Gloucester Getter The three last named are the chief longwall machines in use and the AB Meco-Moore and the Samson Stripper are doing a good job in their respective applications. It is understood that the Gloucester Getter recently installed in a British colliery also shows reasonable promise. It was felt, however, that to meet the conditions of the mines in Nova Scotia, any machine developed must have certain distinctive characteristics. It must: ( 1) Be able to cut and deliver coal in quantity and of the right sizes ( 2) Be easily manoeuvrable ( 3) Be suitable for longwall operations ( 4) Not interfere with timbers already set ( 5) Cut its own stable (6) Work on reasonably heavy gradients

Jan 1, 1951

By Atsuki Sado, Akira Ueno, Kazuaki Takebayashi, Kunio Watanabe

The Saganoseki Refinery of Pan Pacific Copper Co., Ltd., Japan, introduced the ISA 2000® process in 2006 to improve product quality and productivity. After resolving various technical difficulties associated with the process, a current density of 325 A/m2 and electrolytic copper production of 234 000 tons per year were realized in 2018. In recent years, Saganoseki Smelter & Refinery has promoted treatment of recycled materials in addition to copper concentrates. Accordingly, the amount and type of impurities charged to the smelting process have tended to increase. In the electrorefining process, impurities such as nickel and antimony cause anodic passivation and formation of suspended solids, respectively. Although these undesirable phenomena can be avoided by controlling impurity concentrations in the anode and electrolyte to appropriate ranges, this also limits the choice of recycled materials that can be processed by the smelter. To achieve both stable operation of the electrorefining process and flexibility in treatment of recycled materials in the smelting process, Saganoseki Refinery improved the capacity of the impurity recovery processes during 2016 to 2018. This paper describes the expansion of the purification plant to remove and recover nickel and antimony. INTRODUCTION The Saganoseki Refinery of Pan Pacific Copper Co., Ltd., Japan, introduced the ISA 2000® (wax- less permanent cathode method) in 2006 to improve product quality and productivity. Since then, the refinery has gradually increased current density, and has been committed to establishing stable operation and high productivity via various improvements related to the electrolyte filtration and additive management systems. Figure 1 shows the trends of current density and current efficiency at the refinery. Although the current efficiency temporarily dropped when the current density was raised to 322 A/m2, it consistently exceeded 97% thereafter. At present, stable operation at 325 A/m2 has been achieved and continues.

Jan 1, 2019

Operationalizing the Ruggie Framework in a Mining Context Ruggie?s 3 Pillars: The State?s duty to Protect Policies, regulation, adjudication The Corporation?s responsibility to respect Acting with due diligence to avoid infringing Addressing adverse impacts when involved in abuses Access to Remedy ??even the most concerted efforts cannot prevent all abuse.?

May 1, 2013

By R. del Villar, A. R. Laplante

"This article presents four grinding simulation programs, written in Applesoft BASIC. The firs t two calculate residence time distributions (RT Ds) for open and closed loops mills. The third program calculates the select ion functions from the RTD, breakage function and particle size distribution (PSD) o f the feed and discharge. Two linear regression programs are also included to calculate the breakage function. These results are used in the fourth program to simulate continuous or batch grinding kinetics.The modelling approach presented is the size discrete, time continuous matrix formulation presented by Reid (1965) from concepts originally proposed by Epstein (1948). It is at the present time the most widely accepted phenomenological model of grinding kinetics and is standard textbook material (Austin et 01., 1982; Kelly and Spottiswood, 1982, p. 152). The concepts of RTDs and tracer testing originated from chemical engineering theory and practice, and are well presented in Leven spiel (2n d Ed . 1972 , Ch. 9) .Applesoft* was chosen because it is compatible with many micro computers. It is also one of the simplest and least powerful BASIC versions. Thus it can easily be adapted to other more complex BASIC versions.Open Loop Residence Time Distributions (Program RTDOPEN)As mixing, channelling, stagnation and short-circuiting all affect slurry motion in tumbling mills, transport characteristics are very complex an d cannot be derived from fundamental principles. Fortunately , as grinding follows first order kinetics, transport characteristics for the purpose of grinding simulation ca n be represented by the RTD of the slurry phase . It is normally determined using liquid tracers, as it has been demonstrated and is commonly accepted that in industrial ball mill s, the RTD of the so lid phase is particle size independent and equal to that of the liquid phase."

Jan 1, 1985

By Michael P. Davies

Mine waste facilities, and in particular tailings impoundments, are one of the highest risk aspects of any mining venture. There are far too many recent examples of how real and/or perceived physical or environmental impact from one of these facilities has had enormous economic impact on both the specific project and the overall parent mining company. In many cases, such dramatic impacts have followed a period where a due diligence of the mine had been carried out (e.g. in an acquisition, merger or similar) or an internal or otherwise audit had taken place. Consequently, it is suggested that there is a need for an audit/due diligence framework to assist those processes in terms of assessing mine waste facilities. This paper presents a recommended framework for completing either an audit or due diligence assessment of mine waste facilities under a number of typical scenarios. The framework will be of relevance to reviews carried out prior to mine construction, during operations and for mines that have been in a care and maintenance position and are to be re-opened. Concepts of risk management are introduced as an essential part of the recommended framework. The paper should be of value to current and prospective mine owners involved in stewarding an area of significant risk to viability of their mining venture. The paper should also interest prospective lenders to these ventures.

May 1, 2007

By Ken J. Brouwer

Stillwater Mining Company commenced construction and development of the East Boulder underground mine in 1998. This new PGM mine is situated adjacent to the East Boulder River approximately 35 miles south of Big Timber, Montana. Project planning and development incorporated detailed collaboration between the regulatory agencies, concerned citizens and mine personnel. A unique ?good neighbour agreement? was established with a local environmental group who have become actively involved in the review of ongoing site development and the implementation of environmental and compliance monitoring. Environmental management systems allow for integrated management of tailings, waste rock and water in order to minimize surface disturbances and to prevent adverse impacts to the East Boulder River. Long-term site development plans contemplate implementation of comingled waste rock and paste tailings. Water management capabilities allow biological treatment of all excess mine water in order to reduce nitrogen loadings prior to land application disposal by means of spray evaporation, snow making and land application. The comprehensive waste and water management plans have also been integrated with staged mine development and interim reclamation requirements.

May 1, 2002

By Mei-Yan Yang, Ltd. Yunnan Yuntong Zinc Co., Yong-Xiang Li, Xing-Zheng Dai, Hong-Liang Wang, Meng-Yang Huang, Peng Zeng, Guo-Feng Li

"The removal of iron asgoethite from the high iron bearing solutions generated in zinc hydrometallurgy using a strong airflow device was investigated. The influence of oxygen flow, copper ion concentration, temperature and reaction time on iron precipitation as goethite was studied. The optimum conditions were: oxygen flow 0.2-0.35m3/h, copper ion concentration 0.25-0.5g/L, temperature 80-90oC, zinc oxide powder neutralizing agent and a reaction time of5to 7hours. Under the optimal conditions, the Fe2+concentration was reduced to 0.025g/L after iron precipitation, and the goethite residue contained 38.7wt.%Fe. The SEM and XRD analyses showed that the iron was present as well formed FeOOH crystals in the iron residue, and the amount of iron sulphate was very low. Production practice shows that, when the average iron concentration in the feed solution was 11.61g/L and 4.08g/L after precipitation, the weight of iron removed was 1,439kg/day. When the average iron concentration in the feed solution was 14.51g/L and 2.73g/L after precipitation, the weight of iron removed was 2,454kg/day. This represents a ~70 percent increase in iron removal.INTRODUCTIONThe objective of iron removal is to produce a small volume of iron residue, and our industrial goethite process meets this requirement. The high Fe(II) solution in our reactor isoxidized/hydrolyzed to precipitate goethite and the precipitate is sent to a pyro metallurgical furnace for final residue treatment. Some literature discusses (DengYong-guiet al., 2008;Meiguang-guiet al., 2001;Zhongzhu-qianet al., 1980) research on iron hydrolysis; one of the reported rate limiting parameters was the low availability of the oxidant when using air and another was the inhomogeneous air distribution. There are two iron hydrolysis-goethite precipitation methods; the Electrolytic Zinc process (EZ) and the Vieille Montagne process (VM) (Lei Xiang, 2006; Xuguo-qiang, 2007;ZhaoYonget al.,2005). The EZ method hydrolyzes the Fe3+directly to FeOOH. The weakness of the EZ process is the low recovery rate of the associated minor metals. The VM method reduces the iron to the ferrous state and then oxidizes the Fe(II)to Fe(III),with simultaneous hydrolysis/precipitation of the Fe(III) as FeOOH. Before iron hydrolysis, the minor metals, such as indium, could be selectively precipitated, because Fe(II)requires a high pH for hydrolysis. So the VM method has a high recovery rate for the minor metals. There levant goethite precipitation reaction is:"

Jan 1, 2016

By S. Onuki, T. Ando, M. Tejima, R. Enomoto, Y. Okada

"Al–Si–Cu–Mg die casting alloys are widely used in the automotive industry, and recent advancements in high pressure die casting technology enable heat treating products to achieve desirable properties. However, CO2emissions associated with die-casting production lines should be reduced to address the global warming issue. In this study, the relation between the microstructures and thermal stability of precipitates formed during isothermal aging at 423, 485, and 558 K of Al-11.0 mass%Si-1.8 mass%Cu-0.2 mass% Mg (JIS ADC12) was investigated using Vickers hardness tests and transmission electron microscopy (TEM). The hardness tests and TEM results showed that Si compounds and Al–Cu compounds enhanced the mechanical properties of the alloy and that the predominant compound affecting the mechanical properties differed between specimens treated at 423 K and those treated at 558 K. Moreover, additional aging at 423–458 K resulted in a material with a Vickers hardness higher than that of the isothermally single-aged material. Differential scanning calorimetry, differential elemental analysis, and selected-area diffraction analysis using TEM suggested that the combination of Al–Cu compounds precipitated at low aging temperatures and Si compounds precipitated during preliminary aging increased the mechanical strength, resulting in a maximum hardness of 130 HV.INTRODUCTIONAl–Si–Cu–Mg die casting alloys have well-balanced mechanical properties, machinability, and cast ability. These alloys are therefore widely used in the automotive industry because of their superior characteristics, accounting for>90% of the aluminum used in die casting production. As a substitute for iron-based materials, these alloys have contributed to the development of lightweight vehicles.Dong et al. (2014) reported that the heat treatment of die casting materials is effective for changing their dimensions under high temperatures as a result of the precipitation of solid-solution elements. Recent advancements in high pressure die casting technology have led to the application of heat treatments of Al–Si–Cu–Mg alloy products to reduce fuel consumption and satisfy customer needs. Although attempts to reduce CO2emissions have focused on fuel consumption in cars and fuel efficiency regulations have become increasingly strict in recent years, CO2discharged from production lines should also be reduced without adversely affecting the properties of the product. Heat treatments for artificial aging after solution treatment (T6 treatment) and after casting (T5 treatment) are CO2discharge sources, which together with a holding furnace account for >80 % of the CO2discharged during the casting process."

Jan 1, 2018

By Y. Guglielmi, C. Gout, P. Henry, P. Dick

The key questions about fault reactivation in shales concern the potential enhanced fluid displacement through a previously low-permeability aseismic shale formation. Here we selected a critically-stressed fault cross-cutting the underground research facility of Tournemire (France) which is located in Toarcian shales. Several inclined boreholes were drilled across the 8.5 m thick fault zone characterized by a fractured damage zone (FDZ) and a central 2.4 m thick complex core (FC) made of multiple shear bands with gouge intercalated with highly fractured lenses. The fault was pressurized using a straddle packer system defining a 2.4m long injection chamber normal to the fault surface. Three fault zone intervals were tested, two in the fault damage zone and one in the fault core. A three-dimensional displacement sensor set in the chamber allowed continuous synchronous coupled monitoring of fault movements, injection pressure and flow rate. An anticlockwise 0.22-to-0.05 mm fault slip was captured associated with a 10-to-100 hydraulic aperture increase of the fault. Preliminary analyses of the experiments show that leakage in the fault zone is controlled by strength and stress magnitude contrasts between the fault core and the fault damage zone. Fault damage zone discontinuities display a much higher peak static friction angle than the fault core shear zones, respectively of 34 and 22° that could be related to complex interactions between healing and sealing processes. Fault core leakage is much more dependent on strain than on effective stress variations. Discontinuous, pulse-like leakage, develops following complex failure processes that may simultaneously take place in the gouge zones and along the large pre-existing discontinuities. Such results may be of importance in evaluating fault seal integrity in oil and gas exploration, production or CO2 storage or underground excavations monitoring.

Jan 1, 2015

By S. Kashani-Nejad

The kinetics of the thermal decomposition of samples of Mg2(OH)3Cl.2H2O that were obtained by a novel leaching technique applied to a commercial magnesium electrolysis feed were investigated under ambient atmosphere. Thermogravimetric (TG) Analysis showed that decomposition of Mg2(OH)3Cl.2H2O exhibited a single intermediate stage wherein crystalline water was lost at roughly 108 °C. Conversion of the resulting Mg2(OH)3Cl to MgO, HCl and 1120 occurred at temperatures above 398 °C. Thermal decomposition of anhydrous Mg2(OH)3Cl was seen to be consist of two stages. Both stages exhibit first order kinetics with respect to the weight percent of Mg2(OH)3Cl remaining in the sample. However, the rates of decomposition in the two stages were significantly different. Detailed analysis of the kinetic data suggested that the rate of decomposition of Mg2(OH)3C1 was controlled by the rate of removal of the gases released. The change in decomposition rate during the course of the experiments was explained by HCI being released in stage 1 and followed by release of H2O in stage 2.

Jan 1, 2004

By Donald Roberts

"Parameters f or design and development of an emergency hoist system (Fig. I) were submitted to Timberland Equipment Limited of Woodstock, Ontario by the Potash Corporation of Saskatchewan Mining Limited.The unit is the first of its kind in Canada. Not only does it comply with the province of Saskatchewan's mining regulations, but has the added advantage of being completely mobile and self-contained.As well as being useful in the mining industry, the mobile hoist unit could be used in other emergency situations such as rescuing people trapped in wells.JustificationRevisions to the Mines Regulations under Section 13 of the Occupational Health and Safety Act, 1977, of the Province of Saskatchewan stipulate as follows:"" Section 410 .04(4) The Mine Employer shall make adequate provision at every mine where any worker is hoisted in a shaft not equipped with a manway to enable an y such worker trapped in a conveyance in the shaft to be rescued . "" It was not possible to equip the shafts at PCS Mining' s Divisions with "" manways"" and therefore an alternative was required.BackgroundThe Potash Corporation of Saskatchewan Mining Limited, a subsidiary of the Potash Corporation of Saskatchewan, operates four potash mines. Of these, three, Cory, Rocanville and Lanigan Divisions are wholly owned while the fourth, Allan Division, is 40% owned by Kidd Creek Mines Ltd., but managed by PCS Mining. The four underground operations all have a service and production shaft.From 1979 to 1981 the PCS Mining Division, along with Central Canada Potash, were developing an idea to use the existing ground-mounted timberland hoist at Lanigan as an emergency hoist. This hoist was used in the past for rope-up work at both Rocanville and Lanigan and other potash mine s. The Department of Labour at this time had concerns about the time it would take to load, t ran sport and re-install the hoist on a foundation when needed for an emergency. Weight and size made this particular unit very cumbersome for transporting.In addition, the speed at which this hoist operates is too slow for rescue work. When the Department of Labour expressed concern that this unit would be unsuitable for these rea sons, a search for a suitable unit was initiated.The project responsibility for procuring an emergency hoist for the Potash Corporation of Saskatchewan Mining Limited was assigned to the author, a shaft/ hoist specialist a t PCS Mining."

Jan 1, 1986

In April, 1961, a large pillar was removed by blasthole mining methods at Inco's Murray mine. More than half a million pounds of explosives were used to break 2,120,000 tons of ore in a single underground blast. The 5, 10 2-inch boreholes, involving 435,815 feet of drilling, were loaded over a three-week period, using conventional explosives and short-period electric caps. From this blast, more than half a million tons of ore have been removed to date (April, 1962) through slusher trenches situated in the footwall of the ore body. T HE Ontario Division of The International Nickel Company of Canada, Limited, operates six underground mines and two open pits in the Sudbury district in the north-central part of the Province. This paper describes the removal of a large pillar at the Murray mine (Figure 1), where 2,120,000 tons of ore were broken in a single underground blast by the blasthole mining method. This is the largest underground blast achieved to date (April, 1962) at Inco mines.

Jan 1, 1963

By Gerald S. Cole

It used to be that a science/engineering presentation on "light weight" at a metallurgy conference, would relate to the materials science, processing, component fabrication and applications of aluminum, magnesium and titanium. Within the automotive industry, light weight now includes how to "lighten up", how to lightweight, or how to mass reduce vehicle components and systems. Increasingly stringent global emissions-reduction requirements require increasing vehicle fuel efficiency; mass reduction is an enabler to achieve this. While light metals certainly are the basis, a host of other materials can be used to optimize mass reduction while meeting vehicle performance, safety and cost requirements. New grades of ultrahigh strength steels and even nanosteels can be thinned down and save over 1/3 the mass vs conventional mild steels. A compacted graphite cast iron engine can be made lighter than an aluminum one. Aluminum components in vehicles were only castings; now aluminum stampings, forgings and extrusions are becoming more visible components of mass reduction. Lower mass high temperature polymers, and carbon fiber polymer composites now replace aluminum and steel. These materials often require specialized processing and manufacturing techniques to produce a component, including superplastically formed twin roll cast sheet aluminum and magnesium, and hot stamped/in-mold quenched steels. The assembly of hybrid structures requires unique joining/bonding, and corrosion-inhibiting techniques that might include sophisticated structural adhesives. This thinking "light" presentation, will conclude with a discussion of U.S. and Canadian government engineering and research support for mass reduction, including the proposed $148 M American Lightweight Materials Manufacturing Innovation Institute.

Jan 1, 2014

By R. B. Smith, D. C. Brady

"A review of the major renovation of the fifty-year old C-I headframe facilities at NERCQ's Con Mine, Yellowknife, N. W.T. is provided. The project was complete with only two 3-day shutdowns of the facility .Work consisted of four major phases: structural reinforcement of the adjoining mill building prior to dismantling; relocation of virtually all mine and mill utilities which transited the headframe collar en route from the adjacent powerhouse; dismantling of the entire headframe facility and portion of the mill building, including the removal of asbestos siding; and erection of a new headframe, idler rower, collarhouse and mill wall.This paper describes the work and methods used by NERCQ, J.S. Redpath Mining Consultants Limited, Acres International Limited, and others to bring the project to a successful completion. The history of the project is discussed from the planning phase through construction, including; design, procurement, and construction scheduling. The paper discusses the unique elements of the project, the problems encountered, and the methods used to achieve success.IntroductionThe Con Mine is a 800 tpd gold operation located in Yellowknife, Northwest Territories. Originally owned and operated by Cominco Limited , the Con Mine was sold in December 1986 to NERCO Minerals Company, and officially renamed NERCO Con Mine, Ltd. The Con Mine has been in operation for over 50 years. The first gold brick ever produced in the Northwest Territories was poured at the Con Mine in 1938. The original C-1 shaft was sunk in 1937 to a depth of 235 ft. In 1941 the shaft was deepened to a depth of 950 ft, and the original timber head frame was replaced with a steel structure. Following the discovery of the Campbell Shear in 1946, the C-l shaft was again deepened to its present depth of 2443 ft. Over the years, mine production gradually moved deeper and further from the C-l shaft."

Jan 1, 1991

By J. R. del Castillo, J. Ruiz, N. Kuyucak, J. Chavez

Environmental Impact Assessment (EIA) and Feasibility Studies (FS) were carried out to evaluate the potential use of treated acid mine drainage (AMD) occurring at the Kingsmill Tunnel in the Central Andes of Peru. The 11-km long tunnel drains the underground works of the Morococha Mining District and discharges about 1.25 m3/sec of AMD directly into the Yauli River, which is located within the Amazon Basin. The communities living downstream cannot use the Yauli River water due to its low pH and elevated concentrations of metals (e.g., Cu, Zn, Fe, Mn, As, Cd) and sulfate. Studies carried out for this project included technical feasibility, EIA, economic viability and social impact assessment phases. During the "Technical Feasibility" phase, the treated AMD was produced by simulating a high density sludge (HDS) lime neutralization/precipitation process and was evaluated for various potential uses. Mining companies located in Morococha, in particular Centromin Peru S.A., and the Water Works Company of the City of Lima (Sedapal) collaborated with Golder Associates during the studies. The Canadian International Development Agency (CIDA) provided the financial assistance. The results of the physical, chemical, biological and toxicological analyses demonstrated that the treated AMD could be used for supplementing the drinking water supply of Lima and for agricultural (e.g., irrigation and livestock) and recreational purposes. Process design and scale-up parameters were also determined for the implementation of the full-scale treatment facility to the site. The use of the treated AMD as a drinking water supplement would be economically feasible.

Jan 1, 2004

By David A. Fawcett

"This paper presents a summary compilation of current Canadian coal research projects in the areas of exploration, mining and preparation. The compilation forms the basis for a review of present operations and technology, and of current research efforts. General research areas, requirements and priorities are suggested along with a discussion on achieving the research goals in terms of funds, facilities and staff. The current level of research funding in these areas is assessed. IntroductionCanada's coal production is expected to undergo major expansion over the next two decades in response to domestic demands on coal for electrical power generation, industrial uses and conversion to synthetic .fuels, and in response to export demands for both thermal and metallurgical coal s. Surface mining will continue to dominate, but underground mining will contribute an increasing proportion to total production.In Canada, coal research, particularly in the areas of exploration, mining and preparation (E, M & P), has been limited. Increased impetus has recently been given to this research with expansion of CANMET's activities and with the establishment of the Coal Mining Research Centre (CMRC). University researchers are branching into coal research; strata mechanics and preparation are popular in mining-related fields.With the increase in number of organizations and individuals involved in coal research, a means of keeping abreast of the ongoing work is necessary. An annual summary of the status of and developments in current research assists in providing this information. The CMRC prepared such a summary for Canadian coal E, M & P research in 1979 and it received favourable response, justifying the effort. A 1980compilation has been prepared and pro vides the basis for this paper; it is presented with a brief discussion on background, format and content.The compilation forms a basis for an examination of the current status of Canadian technology in E, M & P and of the ongoing research in each area. General research requirements are reviewed and programs and tasks are suggested, followed by a discussion of research goals in term s of priorities and achievement. An assessment is made of the level of research funding in Canada, with comparisons drawn from the United States, the United Kingdom and Australia."

Jan 1, 1980

By A. Danaei, A. McLean, M. Barati, C. Ravindran

"The aluminum industry generates about 90 million tonnes of red mud each year. Previous research shows it could be utilized as a refining flux with a high capacity to absorb phosphorus and sulphur from hot metal in the steel industry. The present study was undertaken to evaluate the melting properties of such fluxes, as it affects the effectiveness of the flux. The results show that the melting behavior of red mud is strongly affected by lime addition and the characteristic melting/softening temperatures reach minimum VALUES (at 32.7 wt% CaO. From these findings, a correlation was established between melting behavior and optical basicity. This allows one to adjust the composition of the flux based on the process requirements. INTRODUCTIONThe aluminum industry generates about 90 million tonnes of bauxite residues each year. This residue is usually red in color because it contains a substantial amount of iron oxide. The red mud, as it is called, is a solid waste with a high concentration of sodium oxide, high pH (10 to 13), and high alkalinity, and thus is harmful to many forms of life. Traditionally, the material is stored in large tailings ponds within the plant’s vicinity (Power, Grafe, & Klauber, 2009). Development of solutions for safe disposal or preferably using this residue for other industrial processes or applications could help restore polluted locations and eliminate a negative impact on the environment (Haake, 1988; Power et al., 2009; Yan & Xuegong, 2010).The mineralogy and chemical composition of red mud depends on the quality of the bauxite and refining process parameters. In general, it consists of iron oxide (Fe2O3), aluminum oxide (Al2O3), titanium oxide (TiO2), sodium oxide (Na2O), silicon oxide (SiO2), and calcium oxide (CaO) (Power et al., 2009). Like most ores and soils, bauxite can contain trace quantities of metals such as arsenic, beryllium, cadmium, chromium, lead, manganese, mercury, nickel, and naturally-occurring radioactive materials, such as thorium and uranium. Most of these trace elements stay in the residue (Power et al., 2009)."

Jan 1, 2012