By Thomas Watson

Introduction THE occurrence of zircon in pegmatites of acidic composition is recorded by many observers both in this country and abroad, and they form one of the most important geologic modes of occurrence of the mineral.' As is well known, commercially the most important American locality for zircon is near Zirconia in Henderson County, North Carolina, where many tons of the mineral have been obtained from a kaolinized pegmatite dike 100 ft. wide and traced for 1 ½ miles along the direction of strike N. 50° E. Zircon may be developed in pegmatites as inclusions in the principal rock-forming minerals, chiefly quartz and feldspar, and as a separate megascopic constituent in the form of grains and crystals not exceeding, as a rule, 2 in. in size, and usually smaller. In the Henderson County, North Carolina, pegmatite, zircon occurs in prismatic crystals with pyramidal terminations measuring up to 30 mm. in diameter, associated chiefly with the feldspar. In some of the apatite veins of Canada, which are closely allied to pegmatite dikes, zircon is reported in crystals upward of 6 in. in length and 2 in. 'and more in thickness. Zircon in large masses occurs in Virginia in the well-known pegmatites near Amelia in Amelia County, and near Gouldin in Hanover County. Both localities are in the middle eastern portion of the Piedmont Plateau province, and are separated by a distance of about 40 miles in a northeast-southwest direction. The rocks of both areas, including the pegmatite bodies, are in an advanced stage of decay, and, the hard and moderately fresh rocks are concealed beneath a cover of variable thickness of rock decay derived by the normal processes of weathering. Exposures, there-

Jan 7, 1916

C. W. MERRILL*—Mr. Hughes' paper not only is very well presented but is most timely in that it covers a subject of vital interest to the United States. Tin is one of the strategic metals which has not been found here in appreciable quantities. The total United States tin output since the first recorded production over 100 years ago would not supply current consumption for a fortnight. On the consumption side, tin is extremely important in national defense because of its use in tin plate which, in the form of tin cans, makes it possible to feed properly the armies that the United States recruits from its civilian population in emergencies. Moreover, the internal combustion engines so important in powering tanks, planes, and other war machines, require large quantities of tin alloys for bearings and for soldering. These considerations, along with the fact that Malaya, historically, has been the leading source of tin to the United States, make the kind of information that Mr. Hughes has presented so ably. a matter of vital interest. Your Chairman, Mr. Romanowitz, in his introduction, referred to the fact that I had been a member of the United States delegations to the three meetings of the International Tin Study Group. Some comments on the Group's objectives and deliberations may be of interest. When it appeared that the International Tin Committee, the prewar producer's cartel, might soon revive its operations and extend its control agreement beyond the expiration date of Dec. 31, 1946, the United States Government became interested in some kind of an international trade organization concerned with tin which would give the consumers' interest equal representation with the producers' interests. An international meeting was called in London in October 1946 to consider this problem. I did not attend that meeting hut the result of the meeting was the organization of the International 'Tin Study Group which

Jan 1, 1950

By C. H. Mathewson

COPPER and the copper-base solid solutions readily form twin crystals when plastically deformed at a suitably elevated temperature or annealed after cold deformation. In fact, no feature of the microstructure of these materials is more prominent or characteristic than these straight-sided bands or simple lines of division which sometimes come from groups of thin polysynthetic lamellae, penetrating part way or wholly through the parent grain substance, but often divide the grain into a few or perhaps only two crystallographically related parts. Nearly always the bands as seen in the usual microscopic examination of a specimen come into vivid contrast with the adjacent crystalline material owing to the inherent difference in orientation. Bands which under special conditions of orientation cannot be seen with vertically incident light are often visible under oblique illumination and, when this fails, contrasting effects usually may be obtained by using polarized light. There is no longer any doubt that these synthetic banded structures obtained in the ordinary course of working and annealing are due to twinning of the spinel type which was observed long ago in a number of metals crystallizing in the isometric system.1 It has been customary in metallurgical literature to designate these synthetic twins, which grow into prominence during an annealing process, as "annealing twins" without regard to the actual mode of their formation, which is, indeed, obscure and with scant recognition of the fact that prior deformation is essential, no twins having been observed in metal of known unstrained history. This is questionable; especially in view of. the fact that in a number of metals and minerals, reorientation into the twin configuration is known to occur as a result of a simple shearing mechanism along the recognized twinning planes and the

Jan 1, 1930

By F. O. Blackwell

It is roughly estimated that some three hundred companies in the United States engaged in mining and the kindred arts now employ electricity in their operations. As all these plants have been installed within the last few years, it is evident that mining engineers have been quick to appreciate the great advantages of the use of electricity and adopt it for their many requirements. In

Jan 1, 1894

By T. K. Prentice

ABSTRACTED AND REVIEWED BY E. W. DAVIS,* MEMBER A.I.M.E. THE January-February number of the Journal of the Chemical Metallurgical and Mining Society of South Africa is made up entirely of a discussion of Ball Wear in Cylindrical Mills. Following the principal paper by T. K. Prentice are several remarkably pertinent and carefully prepared discussions. Few persons in this country would be likely to see this publication, and since the information presented is new and of current interest, it seems desirable to abstract and review this publication for the benefit of the members of the A.I.M.E. The purpose of the investigation is stated in the first two paragraphs of Prentice's paper, as follows: Early in 1941, The Chamber of Mines Steel Products, Limited, initiated a series of tests under semi-working scale conditions to determine, if possible, those physical and chemical properties of a ball which make it resistant to wear when used in a cylindrical mill as a grinding medium, with the primary object of incorporating those beneficial qualities in the balls being produced at their works. This paper describes the tests carried out and discusses the results obtained. From these results it was possible to formulate a new theory relating to ball wear in cylindrical mills. This theory is presented in the second portion of this paper. PRACTICAL BALL-MILL TESTS IN A CYLINDRICAL MILL Part I of the paper begins with a discussion of the methods used for the manufacture of grinding balls in South Africa. The following paragraph is of particular interest. The cast steel ingots, 4 ¼ - in. square by 3 ft. 6 in. long, are re-heated in a gas-fired sloping stationary-hearth furnace and then rolled in a six-pass continuous mill into 2 5/8 in. round billets. Some of these billets are then removed and cut into suitable lengths for forging into 4 in., 3 ½ in., 3 in. or 2 ½ in. balls by means of three Drop and two Beché hammers, but the greater number, whilst still at about 1,000 ºC., pass directly into a set of scroll rolls which produce, in an ingenious manner, finished 3 in. balls direct from the 2 5/8 in. billets. Except in special cases, all balls are allowed to cool in the atmosphere and are not water quenched. Details of the Tests In order to enable the reader to evaluate properly the results and conclusions in the rest of the paper and in the discussions following the paper, most of the information presented by the author under this heading is quoted: ….. The testing unit was a nominal 30 in. diameter and 18 in. long centre discharge Denver Ball Mill. The ore pulp to the ball mill comprised a small portion of the normal feed to one of the fourteen City Deep 5 ft. 6 in. X 22 ft. tube mills, and the grinding media consisted of the balls under test plus other balls to give the desired load. The running time of the test-mill was divided into approximately equal periods of five days 13 ½ hours each. The usual procedure was to examine and make up the load

Jan 1, 1944

By John N. Hobstetter

IT is widely believed that the nucleation of phase transformations in solid metals is accomplished by some type of local atomic fluctuations in the parent phase which arise from spontaneous diffusion in the metal or alloy system. Under appropriate conditions, these fluctuations are believed to be stable in the sense that the free energy of the entire system is lowered if the fluctuations, or nuclei, grow,' Under other conditions they are thought to be unstable in the sense that the free energy is lowered if they redissolve. The criterion for stability is usually taken as the size of the fluctuation. This view has been rationalized by Becker1 in terms of the free energy released by the volume of the nucleus and the free energy associated with the formation of a new surface surrounding the nucleus. The qualitative result of this reasoning is shown in Fig I where the changes in free energy for the surface and volume effects are plotted together with their sum against the radius of the nucleus. There is evidently always a critical size r. beyond which the release of free energy which is proportional to the volume always dominates the increase of free energy which is proportional to the surface area. Borelius2 has also attempted to rationalize the stability criterion for binary alloys, but in terms of the internal concentration of the fluctuations. He has found that, if surface energies are entirely ignored, the fluctuation must still reach a critical concentration if it is to become stable and avoid subsequent dilution. Although the Borelius theory fails to predict many observed nucleation phenomena such as the vanishing of the nucleation rate at the critical temperature, the major premise must certainly be valid. In this paper a reconciliation of the Becker and Borelius views is made by means of a search for nuclei which are at once stable with respect to both size and internal concentration, The increase in free energy per mole accompanying the formation of a nucleus which is just stable, ?fe, is independent of the path whereby the nucleus is brought into being. It is thus appropriate to seek critical nuclear attributes without reference to the fluctuation mechanism. The rate of nucleation, however, cannot be treated without a detailed understanding of the exact fluctuation process which produces stable nuclei. In this and succeeding papers the purpose will be to find the size, shape and internal concentration of the stable nucleus which is formed with a minimum increase in free energy in a wide variety of systems. THE NATURE OF THE NUCLEUS It is necessary to have rather detailed knowledge of the nature of a nucleus if ?Fe is to be computed. Fortunately, enough facts are known or suspected about the nucleus to make possible a detailed analysis. X ray diffraction studies have shown3

Jan 1, 1948

By E. V. Crane

A TREMENDOUS volume of the metal rolled annually into sheets, strips and coil stock finds its way to a host of stamping and manufacturing plants which are the quantity production units of the country. Considerable in volume, too, are the rolled and extruded rods which go into forging and manufacturing plants for conversion into the same general line: those widely sold metallic necessities and luxuries of the household, the office, transportation, farming and building construction. Yet, in spite of its age and its importance, the stamping trade has been doing its "engineering" largely by trial and error. Its distinctive method is shearing out and plastically working metal to finished shape in a few quick strokes with high loads and expensive tools which are warranted only by large quantities to be produced. The principal operations have many features in common with rolling and wire-drawing methods. Combinations of stresses are different, however, and details of operations are infinite in variety. An engineering study of the subject begins with stress analysis, but must go back to metallurgy for its foundation. A grouping of pressed-metal working operations according to whether the metal is (1) sheared, (2) bent, (3) drawn or (4) squeezed has proved useful. All of these groups include instances of both hot and cold operations. For discussions of metal working properties, the division between hot and cold working is taken as the recrystallization range of temperature. This, of course, brings tin, lead and often zinc into the hot-work range at or near room temperature. The outstanding hot-working press field is in forging: particularly of brass; all of which is included in the squeezing group.

Jan 1, 1931

By C. Dirksen

This study investigates whether oxygen consumption during segregated forward combustion may be affected by natural convection. Linear theory indicates that thermal instability occurs in a horizontal porous medium when the modified Rayleigh number N 'Ra exceeds a critical value of about 40. Most experimental results, including those described here, indicate this value to be about an order of magnitude smaller. N ', is derived from "differential similarity" and the proper time scale factor is also obtained. The critical value of N'ra for a horizontal, water-saturated porous medium at atmospheric pressure subjected to a uertical temperature gradient was found to be about 3.0. The ambiguity in the value of N'R, arising when fluid properties cannot be assumed constant is indicated. Natural convection was observed for oblique systems below N 'Ra , while simultaneous horizontal flow did not affect N Racrit. The expected range of values for the various parameters pertaining to segregated forward combustion is indicated and the corresponding values of N 'Ra calculated. Only under very favorable conditions, such as high permeability, high pressure and low top temperature, can the critical value of N 'R, be exceeded. Thickness of the convection layer should not become too large, since the time required to obtain significant mixing is proportional to the square of the thickness. For an oblique combustion frant the conditions for significant mixing may be less strenuous. LNTRODUCTION Laboratory1,2 and field314 experiments have shown that a markedly upgraded oil can be produced by in situ forward combustion. Under certain conditions injected air may move through a high permeability, gas-saturated channel over the oil-saturated layer, while combustion takes place, exclusively, at the horizontal interface (Fig. 1). Such a channel may be a natural gas cap, or it may result from a forward combustion process in which injected air and combustion gases fingered through the top of the formation, causing a premature breakthrough at the production well. In this particular case of segregated forward combustion, the air stream moves parallel to the combustion front. Molecular diffusion and transverse mechanical dispersion will be insufficient to cause all the oxygen in the air stream to reach the combustion front. When the oxygen in the air stream is not completely consumed in the combustion process, it will reach the production well and create a serious fire hazard. In addition, the reduced efficiency may make the process economically unprofitable while also serious corrosion problems may be experienced in the production we11.3 This undesirable situation should, therefore, be prevented. However, in a situation as depicted in Fig. 1, an unstable temperature gradient exists in the gas phase. The combustion is taking place at the lower boundary at a nearly constant temperature that may be anywhere from 600 to 1,200F, depending on the conditions. The upper boundary of the gas phase is overlying, impermeable rock; its temperature might be around 100F, but may increase to 300F or higher due to conduction and convection as the combustion process continues. This represents a steep temperature gradient and it is conceivable that under those conditions free or natural convection will take place in the gas

Jan 1, 1967

By Dever Ashmead

ENGINEERS, operators, miners, and others di-rectly interested in mining will readily agree that more of well-directed illumination in mines will result in a reduction of accidents and general im-provement in the working conditions, comfort, and effi-ciency of those employed underground. Progress has been made in the amount of illumination from individual lamps carried by miners. The candle, which a great many of us can remember as the general method of lighting, was replaced by the oil lamp or torch, later by a specially prepared oil known as "Sunshine," and eventually by the carbide cap lamp. The metal mines still present a field for progress from the standpoint of general illumination, particular-ly those mines having high stopes. Attention is being more and more focussed upon the advantages of im-proved lighting in mines, in order that the underground employee may benefit as the factory workers have al-ready done. The management is vitally interested in the morale of its employees, the reduction of costly accidents and increased production, all of which, judging by results in other industries, will be sub-stantially benefitted through the means of improved general illumination. From data available to the writer, 40 to 50 per cent of the accidents in the metal mines occur at the face; they may be due to roof falls, movement of loose ore, loading of cans, handling of tools, etc. Very probably a large proportion of these accidents may be attributed to lack of light. If sufficient illumination had been present the employee could have seen what was happen-ing and taken the proper precautions. The introduc-tion of better illumination means better visibility, de-crease in accidents, and increase in efficiency.

Jan 6, 1928

By Walter Crafts, C. M. Offenhauer

IN the course of study of the heat-treatment of low-alloy steels, the behavior of alloy carbides at subcritical temperatures was found to vary from that indicated by published investigations. In order to establish the ranges of formation of carbides in low-chromium steels, a series of steels containing up to 0.60 per cent carbon and 7.5 per cent chromium has been investigated with respect to the type of carbide formed after quenching and tempering at subcritical temperatures. The types of carbide formed as products of austenite transformation to pearlitic and pseudomartensitic structures have also been determined. There have been numerous investigations of the carbides in chromium steels and diagrams of the iron-chromium-carbon system.1 Westgren, Phragmén and Negresco2 identified the following carbides in chromium steels: [Cementite Fe3C (containing up to about 15 per cent Cr) Trigonal carbide Cr7C3 (containing up to about 55 per cent Fe) Cubic carbide Cr4C (or Cr23C3) (containing up to about 25 per cent Fe) Orthorhombic carbide . Cr3C2 (containing only a few per cent Fe)] The most complete information on the iron-chromium-carbon system was supplied by Tofaute, Sponheuer and Bennek3 and by Tofaute, Küttner and Büttinghaus.4 By means of dilatometric and microscopic studies, sections of the diagram were established. This diagram showed the presence of the special carbide Cr7Ca in steels containing about 2.5 per cent to 12 per cent chromium in low-carbon steels and from about 5 to 20 per cent chromium in r per cent carbon alloys from A1 to room temperature. The present investigation has shown that a carbide inversion from Fe3C to Cr7Ca occurs in chromium steels containing more than about 1 per cent chromium after hardening and tempering at subcritical temperatures above about 500°C. The type of carbide observed to be more stable in quenched and tempered specimens was also found to be produced by direct austenite transformation in corresponding ranges of temperature and composition. EXPERIMENTAL PROCEDURE The steels used in these experiments were made in magnesia-lined crucibles in high-frequency furnaces and were poured into 2-in. ingots. The ingots were forged into 1-in. round bars, and all heat-treatments were conducted on specimens of this section .size. Sections of the bar stock 8 in. long were hardened in air, oil or water depending on the composition, after heating to a temperature sufficiently high to dissolve the carbides. The low-carbon and low-chromium steels were not entirely martensitic after quenching, and contained some ferrite and pseudomartensite. No pearlite was observed in the microstructures after auenchine. The quenched bars were cut into

Jan 1, 1942

By M. G. Corson

INFORMATION regarding the use of manganese alloys has hitherto been incomplete and available only from widely scattered sources. This paper attempts a systematic description of properties and uses of alloys other than manganese bronze, manganin and duralumin, which are probably the only non-ferrous alloys associated with manganese in the minds of most metallurgists.1 PROPERTIES OF MANGANESE Manganese can react either acid or basic; it is hard to obtain in the pure state; it has two different crystalline lattice structures, both of the cubic system, one stable above 850° C. and the other below 650° C., both coexisting in the intermediate range. Although the commercial product is hard and brittle, the pure metal seems to be ductile. In fact Zhemchuzhny, in Russia, was able to obtain ductile manganese and draw it to fine wires by the simple expedient of adding about 3 per cent. copper to the alumino-thermic product. Copper most probably brings the silicides, aluminides, nitrides and carbides present in the commercial product into a much less harmful form of distribution. One industrial use that can be foreseen for wrought manganese articles is as anodes for electrolytic processes in sulfate and nitrate solutions, particularly with high voltages. A practically insoluble skin of manganese peroxide is likely to form in such cases and an insoluble and strong anode material will be available. MANGANESE AS A SCAVENGER Because of its activity manganese might become the most efficient scavenger and refiner of copper, were it not for the fact that 0.01 per cent.

Jan 1, 1928

By Geo Ashley

THE following paper is intended to be suggestive only, and to open the way for discussion and further observation. Its preparation was requested only two days before the time limit set for the submission of the papers comprising this symposium. Thus no time existed for detailed studies so it is largely a memorandum of such facts as have come incidentally to the notice of the writer in the study of coal in the field. The field study of sulfur in coal has received very little special attention or description from coal students. The presence of sulfur concretions is noted in hundreds of descriptions, and certain benches of a coal bed may be described as "sulfury" or the presence and position of sulfur bands may be noted in coal sections in connection with sampling. It may be accepted that some sulfur is present in all coal. The amount varies greatly in different regions, in different beds, and in the same bed in different areas. The anthracite of Rhode Island comes the nearest of any coal known to the writer of being free from sulfur, several analyses of that coal showing less than 0.1 per cent. Subbituminous coals in Colorado in a few places have close to 0.2 per cent. of sulfur on the dry-coal basis and in other states subbituminous coals approach this lower limit. Bituminous coals seldom run under 0.4 per cent. of sulfur on the dry basis, though in a few places dry bituminous coals in Colorado and Washington have between 0.3 and 0.4 per cent. The better known bituminous coals have almost everywhere over 0.4 per cent. The best of the Pocahontas and New River coals run close to 0.4 per cent., but there is very little commercial coal in Pennsylvania, Ohio, Indiana, Illinois, Kentucky, or the other states that runs under 0.5 per cent. on the dry basis. From these minimum figures, the amount will range up to 5 or 6 per cent. or higher if visible sulfur is not excluded. It must be remembered that the usual -analysis of a coal bed is not intended to give the total proportion of sulfur in the bed but the amount in the coal after the removal of the more obvious and larger sulfur masses.

Jan 9, 1919

By Stuart H. Ingram

DEFINITION THE term lightweight aggregate implies material which may be substituted for the usual rock, sand and gravel commonly used as the major part of concrete, but distinguished by being much lighter in weight. BACKGROUND The art of making and using concrete is old and well developed. Research and experience have pretty well determined the qualities necessary in its constituents, and time has tested theories and applications. Elaborate specifications and tests have been devised and generally adopted governing all phases of concrete work, from selection of material, through engineering design and down to mixing and placing. Standard practices have become routine to executives and laborers, and operations have been simplified and costs lowered. Though many lightweight aggregates meet the basic specifications necessary for usefulness, their physical qualities are so different that they frequently will not pass standard tests, and some of them cannot be mixed and placed with the usual formulas for water and slump. As a rule their use produces a concrete with a lower modulus of elasticity which requires design change, and being produced in much smaller quantities than ordinary aggregate, production costs are higher. This latter works in a vicious circle to restrict their use and maintain prices that are not competitive, except as against each other. INCREASED DEMAND In spite of such handicaps consumption has grown steadily for the past two decades and is apparently growing even faster today. It is evident that lightweight concrete must have better qualities, and be sufficiently better to overcome the higher cost and the other difficulties and disadvantages pertinent to the use of a new and different material in an old industry. Hence the study of its main ingredient should be of interest to all engineers. Our group has a double interest in the subject since most of the materials which have been used as sources of lightweight aggregate are either mined, or are by-products of mining operations. We are directly interested in their production as well as their use, and since available supplies of materials suitable are limited, the increasing use, and rising demand, make the discovery of new sources, or the development of processes to adapt other natural materials to this use, a promising field; and one in which our profession should take an active part. RECENT DEVELOPMENT Descriptions of ancient work contain references to the use of spalls of tuffs or pumice in concrete masonry, but it is only since the nineteen twenties that serious attempts have been made to produce and market lightweight aggregates. A period of rapid advance in theory and practice in cements, mortars and con-

Jan 1, 1947

By Nathaniel Arbiter

INTRODUCTION Almost seventy-five years ago problems in the recovery of sulfides from then designated slime fractions were the impetus for the development of flotation. The fall-off in recovery by gravity methods below about 200-mesh, and the shift from coarser vein deposits to more disseminated ores, particularly for copper, provided the background for flotation's rapid advances. Although the ensuing years have witnessed major improvments both in flotation reagents and in flotation machines, many problems are still with us. And since, with the exception of the unique leaching of chalcocite ores at Inspiration, flotation is still the exclusive mainstay for primary recovery of all base metal sulfides, the solution of these problems as they arise is vital to the well-being of the mining industry. Before considering the problems themselves, it will be useful to review the current status of sulfide flotation in the United States. The last comprehensive survey by the Bureau of Mines in 1975 (1) showed sulfide ore tonnages treated from 1960 to 1975 as summarized in Table 1; Table 2 gives similar data for the flotation of all non-sulfide ores. Noteworthy is the leveling off in sulfide ore tonnages in 1970-1975, with a probable further decline in the past three years, and the sharp drop in the number of plants floating sulfide ores. In contrast, the tonnages of non-sulfide ores floated, as well as the number of individual plants, has continued to increase. In spite of these trends, two-thirds of the total tonnage of the ores to which flotation is applied is still represented by sulfides. Average grades of sulfide ores in 1975 were: about 0.6 percent for copper; near 5 percent for lead; and near 3 percent for zinc. Recoveries averaged in the low 80's for copper; about 95 percent for

Jan 1, 1979

By H. F. Perkins

CORROSION as an economic problem is growing rapidly in importance not only because it entails a replacement of corroded parts, but because it interrupts operation and causes hazards of damage and injury through failures of corroded equipment. Nearly all industries are interested in this subject. This paper, although concerned chiefly with corrosion in a complete refinery on the sea coast, discusses many of the various forms of chemical decomposition, most of which are found universally. The petroleum refining industry, in the writer's opinion, is seriously afflicted by the presence of sulfur in nearly all crude oils. The complete removal of sulfur from the crude as it enters the plant would cause such a relief from corrosion that this problem for research would seem to demand active attention. Next to sulfur the most troublesome corrosive agent is the saltmagnesium chloride, found in the water associated with crude oil, the last traces of which are so difficult to remove. This is much less serious, however, than the sulfur. Refinery corrosion can be tabulated as follows: Causes of Corrosion and Places of Attack in a Refinery CORROSIVE ELEMENTS MATERIAL ATTACKED Air: Pipe lines Moisture Tanks COQ Electric fixtures Sulfur gases Still towers Chlorine Condenser boxes Other acid-forming gases Ladders and stairs Smoke stacks Steel buildings All exposed metal Water: Alkali Fire lines and hydrants Acids Cooling water lines Air Condensers and coolers Other dissolved gases Boiler tubes Steam Steam pipes and valves Turbines Oil Sulfur compounds Tanks, pipes, valves, stills, towers MgCl2-Hydrochloric acid Condensers Air contamination

Jan 12, 1926

By J. B. Mudd

Introduction It is difficult to think of any activity on which mankind has been more dependent than mining, and certainly there is much evidence in almost every part of the world of old workings that clearly demonstrate that man from earliest times has dug and toiled to take from the earth precious stones, metals and materials that from time to time have been essential or of value to him. In step with social development and industrial and technological advances the tempo of mining activity, regulated only by the laws of supply and demand, has quickened and in this century has accelerated rapidly in keeping with its dramatic development. Indeed, the rate of change of events has been such that if it were to continue to accelerate as fast as it has over the past decade there is reason to wonder how the insatiable demands for metals and minerals are to be met in the years that lie ahead. Shallow mines containing high-grade ore deposits either have been or are being rapidly mined out and their place can only be taken in general by ore lying at greater depth, or by ore of low grade, situated for the most part in remote and in underdeveloped areas. The cost of exploration and development is rising at an alarming rate, with the result that the expenditure now required to bring a mine to production far exceeds anything previously contemplated. It is estimated that the total capital required to maintain existing operations and develop new ones during the next 5 years will be of the order of $50,000 million and of this, new capital to bring new mines to production will be of the order of $3,000 million. Today no single mining finance company can, from its own resources, find all the money for a major mining development, and as a consequence there has been a strong trend toward joint ventures and to the formation of multinational consortiums. International lending institutions already play an important part in financing many new mining projects and their participation provides the financial umbrella under which other lenders can invest with greater security. There is little doubt that to finance the costly ventures in the future, governments and international lending agencies, banks and finance

Jan 1, 1971

Some years ago it was my good fortune to inspect some coal properties in Germany, and the most striking impression I received on my trip was that in that country every one in the coal industry, miners and operators, was proud of the fact-not apologetic about it-and that industrially coal was looked upon as a King. The explanation, of course, was that at least 90 per cent of the entire mineral value produced in Germany was from coal, and that it was the very foundation of the nation's industrial life. The feeling was so different from that existing in the United States among those engaged in producing coal that it made a profound impression on me, and many times since then I have speculated about the reasons for the difference in opinion in the two countries. Here, of course, our units are much smaller and more numerous, there is not so large a proportion of technically trained men, and we have the American trait of depreciating the things we do at home; but among those not actively

Jan 1, 1935

By W. L. Watts

The existence of petroleum in California has been known for many years. From time immemorial the California Indians used this mineral, in the form of asphaltum, for various purposes. In the early history of the State the Catholic fathers utilized it for roofing their missions and other buildings. It is said that in 1855 or 1856 Andreas Pico distilled petroleum on a small scale for the San Fernando Mission. He obtained his crude oil from Pico canon, near Newhall, in Los Angeles county; and he was probably the first refiner of petroleum in this State. In 1856 a company commenced work at the La Brea ranch, in Los Angeles county, and tried to refine the crude oil. In 1857 an attempt was made to produce illuminating-oil from crude petroleum at Carpenteria, in Santa Barbara county; and there are records of similar attempts in other localities previous to 1860; but none of them were successful. The first scientific report on petroleum in California was made by Prof. B. Silliman, who published his researches in 1865. He spoke favorably of the possibility of obtaining petroleum in remunerative quantities in this State, and gave the results of his experiments in the fractional distillation of California petroleum. The next decade was marked by a considerable oil-excitement in California; and a great many companies mere formed for the purpose of petroleum-mining and for distilling crude oil. In most instances these companies did not meet with success; but it must be remembered that the pioneer oil-miners did not

Jan 1, 1900

By E. P. Pfleider, W. D. Lacabanne

ROTARY-percussive drilling is a new method of drilling hard rock. Designed to give variations in thrust, revolutions per minute, and torque ranges, these drills combine the high efficiency of the rotary system in soft rocks with an increasing amount of percussive action in rocks more difficult to fragment. Fundamentals of the rotary, percussive, and combination systems have been described in detail in various papers-most recently by C. Fairhurst and W. D. Lacabanne1-but there is still much basic work to be done on the interplay of actions in the rotary-percussive system to enable the drill designer to achieve the highest efficiencies. Whereas the original units struck light blows of only 15 to 30 ft-lb, adequate for medium hard rocks, the present trend is to piston blows of 50 to 65 ft-lb in order to cope with the granites and other rocks having Shore hardnesses of 75 or more.

Jan 7, 1957

Before hostilities between the colonies and Great Britain began in 1775, most of the coal used in the northern colonies undoubtedly came from England, with some supplies for New England coming from Nova Scotia; in New York and Philadelphia the supply came from England with some from the Virginia mines. Table 4 shows data obtained from the Public Records Office, London, for the years 1768-1772. This table supplements Table 3, which records only a few shipments from Richmond in 1768 and 1769; as there was no coal shown in imports coastwise in 1769 in Table 4, and only two small shipments in 1769 in Table 3, there may have been a cessation of shipments then, for some reason not now known. In Table 5 are incorporated all the data in the first two, with a few earlier years, and an attempt is made to estimate the amount used during the period by allowing for coal exported. With the small total tonnages a carryover from one year to another makes a large difference in the annual figures, but over the period the result may be fairly indicative of the amount of coal used before the Revolution. According to present day ideas the quantity of coal used during that war was very small, but apparently it was badly needed for the manufacture of the small amount of munitions made in those troublous days. As Philadelphia was the leading city along the Atlantic coast, and as the southeastern part of Pennsylvania was the leader in making iron, as well as making rifles, it is natural that the first call for coal came from there. At first, procuring supplies such as coal, powder and sulphur was handled by a Committee of Safety, which later became a Council of Safety and later this committee's functions were turned over to a Board of War, functioning with the military organization of the colony. . The organizations of the several colonies were slightly different, but Pennsylvania, Maryland and Virginia followed this scheme generally. Later in the war the Congress began to make arms for the troops, and it is difficult now, with the few records available, to tell when the state functions ceased and those of Congress began. On December 5th, 1775, the Committee of Safety

Jan 1, 1942