By A. B. Tanner

The effects of radon in drillholes on gamma-ray logs have been described by L. S. Hilpert and C. M. Bunker1 Since these effects may cause drastic error in the evaluation of uranium deposits, it is useful to know the conditions under which significant amounts of radon tend to accumulate in drillholes. In the studies described here, atmospheric conditions were found to dominate in the control of the behavior of radon in drillholes in the vicinity of a uranium orebody. The site of the investigation was in McKinley County, New Mexico, about 12 miles north of Grants. Drillholes of 4 1/4-in. diam, on 25-ft and 100-ft centers, penetrate ore in dry rock at a depth of about 100 ft. A geologic log of the drillhole of primary interest is shown in Fig. 1. Gamma-ray logs revealed three zones of ore-grade mineralization in the Todilto limestone. A 6-ft zone, the lowest of the three, assayed 0.20 pct U3O8 by chemical analysis. The limestone ores in this area contain disseminated uraninite and some yellow and orange secondary minerals. Only radon"", a member of the uranium'" series, was measured in this investigation. Radon is one of the chemically inert noble gases and is radioactive by alpha particle emission with a half life of about four days. In this discussion, amounts of radon are expressed in microcuries (1 microcurie equals 37,-000 disintegrations per sec) and concentrations of radon are expressed in microcuries per liter of drillhole air. Samples of air were obtained by lowering a sampling device (Fig. 2) into a drillhole and actuating the device at the desired depth. It was then raised to the surface and the sample was transferred to a storage tube. Within two days the sample was transferred to an ionization chamber, and the activ- ity of radon and its short-lived daughter products was measured at radioactive equilibrium with a vibrating-reed electrometer. The measurements were corrected back to the time of collection and involve errors estimated generally not to exceed + 5 pct to —15 pct. Radon Behavior in a Covered Hole: Fig. 3, a typical log of radon concentration vs depth in the covered drillhole, was made by using values of radon concentration at discrete depths. Continuous logs of alpha-particle radiation in the drillholes showed that such radon logs depict the continuous variation of radon concentration with depth quite accurately. Three features of radon logs were noted: 1) maximum

Jan 1, 1960

By G. E. McElroy

Much attention has been directed to mine-air flow in recent years, more especially in Great Britian where there is frequent reference to a theory of fluid flow developed by English engineers. Briefly stated, this theory is that for similar passages of the same relative roughness, in which fluid flow occurs, the conditions of flow are exactly the same for W D V equal values of the product where W = density of the fluid, D = diameter of the passage through which flow occurs, V = mean velocity of flow, and p = absolute viscosity of the fluid flowing. This, the "Reynolds Criterion" of fluid flow, had its origin in the work of Reynolds1 more than 40 years ago. Later, Rayleigh2 amplified the theory which has been conclusively proved for small pipes by the experiments of Stanton and Panne13 over a large flow range, and by Lacey4 over a somewhat more limited range. Concordant results on small pipes have also been obtained by numerous other investigators with single fluids over more or less limited ranges of flow. According to this theory, results in one medium, such as water, are immediately applicable to another, such as air; and experimental results on models are (theoretically, at least) applicable to full-scale designs. This is of great importance in aeronautics and can be of considerable value in mine ventilation research. Hodgson, in a recent paper,6 has outlined the application of this theory to mine-air flow and recent English experiments6 on the resistance of a timbered mine airway have been expressed in this form.

Jan 1, 1927

By Hsun Hu, R. S. Cline

The formation of annealing textures during the course of recrystallization in 2 pct Al-Fe crystals rolled in the (111) [112], (112) [111], and (112) [Till orientations has hem studied in detail. When the rolling texture is composed of both (111) [121] and (001)[110] components, the annealing texture consists of mainly (110) [001] and (113) [332] components. As the (001) [110] component diminishes from the surface to the interior of the rolled crystal, the relative concentration of the (113) [332] component in the annealing texture decreases accordingly, whereas that of the (110)[001] component increases with the (111)[112] component in the rolling texture. Such dependence of the annealing texture on the composition of the rolling texture is in accmdance with the oriented growth mechanism. Grain-growth characteristics during recrystallization, hence the annealing texture, can he considerablv different in (112) [111]-type crystals depending sensitively on the initial orientation of the crystal. In a previous publication,' the formation of rolling textures in 2 pct A1-Fe single crystals with initial orientations of approximately (1ll)[112], (112)[111], and (112)[111] was studied in detail. The deformation texture of these crystals consisted of either a single (111)[112] or a combination of (111)[112] and (001)[110] components in various concentrations. For the (lll)[112] crystal, the deformation texture was a single (lll)[112] up to 70 pct rolling reduction, but it became (lll)[112] plus (001)[110] after -90 pct reduction. For the (112)[113.]-type crystals, the relative concentration of the (111)[ 112] and (001)[110] components varied with the depth below the surface of the crystal, as well as with the amount of deformation. These series of specimens, having deformation textures with a range of concentration of the (111)[112] and (001)[110] components, could therefore be used for a thorough investigation of the effect of deformation-texture components on the formation of annealing textures. In a study of rolling and annealing textures in Si-Fe crystals, Dunn and Koh3 noted that the addition of a (001)[110] component to the (111)[112]-type deformation texture had practically no effect on the recrystallization texture.* According to the ori- ented growth mechanism for the formation of annealing textures, nuclei related to the deformation texture by approximately 30-deg rotation around a common [110] axis have the highest rate of growth and the resulting annealing textures generally have such an orientation relationship with respect to the deformation textures.314 It was reasoned by Dunn and Koh3 that if the oriented growth mechanism operated the recrystallization texture developed from a deformation texture containing both (111)[112] and (001)[110] components should be strongly centered around (113)[332], because (113)[332] is approximately midway between the (111)[112] and (001)[110], and is related to both of these two orientations by [110] rotations of 25 to 30 deg. Hence, nuclei of (113)[332] orientation should have a high rate of growth in the deformed matrix. However, their results were not in accord with this prediction. It was felt by the writers that a detailed study was needed to clarify the effect of deformation-texture components on annealing-texture formation. For this reason, the present investigation was conducted. EXPERIMENTAL PROCEDURE Specimens used for the present investigation were taken from the crystals rolled previously for deformation-texture studies.' In order to follow the progress of annealing-texture formation during the course of recrystallization, a single specimen was taken from each rolled crystal and its textural changes examined after successive anneals until recrystallization was complete. The specimen was carefully cut from the rolled strip with a jeweler's saw. Prior to annealing, the sawed edges were etched to remove distorted metal, while both faces of the specimen were protected from the etching solution by acid-proof plastic tape. After annealing, the specimen was etched from the "bottom" face only (the reference or "top" face of the specimen was protected by plastic tape) to one half of its original thickness, so that the texture at the surface and at the central section of the strip could be determined by the reflection technique. The

Jan 1, 1965

By AIME AIME

THIS year's Chairman of the Mineral industry Education Division is, like his predecessors, no novice in that field, having been in 1928 Chairman of the Engineering Education Committee which labored so well that it was enlarged into a Division of the Institute's activities . For almost a quarter of a century lie has been a dean in mining and engineering schools, with considerable experience before that as a teacher. A native-born New Englander (June 23, 1881), he naturally went to Massachusetts Institute of Technology where he received the Bachelor's degree in mining in 1904. Just why a Fitchburg. Massachusetts boy yearned to he a mining engineer he has never explained, but why should any boy ever have to explain why lie wants t? be a mining engineer? Like the old rhyme about the reasons why a man should drink, "any other reason why" is adequate..

Jan 1, 1945

By Robert E. Green, Kenneth Reifsnider

A microscopic X-ray diffraction technique was employed for the simultaneous study of the behavior of several families of lattice planes, whose local orientatiotz changes are manufestations of internal distortions resulting from specimen deformation. Photographs taken using aluminum were single crystals 1/64 in. In diam are presented which illustrate the appearance of various types of deformation- or growth- induced structural variations. Slip and lattice bending were detected in tensile tests for strains as small as 0.1 pct. Evidence of deformation bands, lineage structure, and void formation wns also shown. AmONG the most important methods of studying internal stresses in metals is the utilization of various X-ray techniques. The general subject of X-ray metallography has been treated in a most excellent manner by Taylor,1 and the use of X-rays for the direct observation of imperfections in crystals has recently been reviewed in an article by Newkirk2 and in the book edited by Newkirk and Wernick.3 Since the inception of metallographic X-ray analysis, there have been numerous technological developments and refinements, each with its particular advantages and disadvantages and, acrording to these, its particular applications. X-ray diffraction techniques can be divided into two general categories, that of X-ray diffraction microscopy and that of X-ray diffraction macroscopy. In the former are included such methods as those of Berg-Barrett, Lang, and Schultz2,3 which are concerned with microscopic imperfections such as dislocations. The second category includes all work concerned with the study of the condition of a crystal lattice structure as indicated by the marroscopic detail in its diffraction patterns. An example of this is the study of the diffraction manifestations of inhomogeneous plastic deformation as manifested by formation of deformation bands and inhomogeneous lattice rotations. The method used in the present investigation was an X-ray diffraction macroscopy technique. The geometry and analytical aspects of the method were similar to those of Julien and Cullity.4,5 The source was collimated with a single slit in a manner simi- lar to the "parallel beam'' method of Barth and Hosemann6 except that a continuous spectrum of radiation was employed. The apparatus produced large-beam transmission Laue patterns of thin cylindrical aluminum-wire crystals, which were deformed either in tension or torsion. Although the conventional X-ray target and interposed slit were not capable of the high resolution obtainable with a fine-focus X-ray source as employed in a microfocus apparatus, resolution was a secondary consideration in our technique, and was sacrificed to obtain sufficient intensity along a sizable length of the specimen. By using a grid indexing technique similar to that of Barth,7 we were able to study several diffraction lines from various planes simultaneously. The results of these tests give additional information with regard to the inhomogeneous deformation of single crystals, and the indexing procedure used provides a correlation between portions of the test specimen and portions of a diffracted beam. EXPERIMENTAL TECHNIQUE The experimental arrangement used is shown schematically in Fig. 1. A source of continuous X radiation from a vertically mounted Machlett X-ray tube possessing a copper target and operated at 20 kv and 10 ma was passed down a horizontal lead tube 80 cm long which terminated in an adjustable vertical brass slit. The slit opening was adjusted to correspond with the diameter of the test specimen. In front of the brass slit it was possible to place a screen wire mesh, one horizontal strand of which was a lead wire which served as a fiduciary mark, the screen itself serving as an indexing system as will be described later. Behind the screen was the test specimen which consisted of an aluminum single crystal wire 1/64 in. in diameter and 3 in. long. These 3-in.-long crystals were cut from

Jan 1, 1965

By T. B. Counselman

AN iron blast furnace of 1000 tons daily capacity will produce about 100,000 cu; ft. per minute of blast-furnace gas. This contains about 25 per cent of carbon monoxide, and has a B.t.u. value of about 95. This gas-is used primarily for heating the stoves of the blast furnace, and secondarily, under boilers, for steam production. Occasionally it is also used in gas engines. The raw gas coming out of the furnace carries about 10 grains of flue dust per cubic foot of gas, under best operating conditions. With the furnace "rolling" or slipping, this quantity may temporarily be greatly increased. This dust would, of course, deposit on the checkers of the stoves, or plug the burners under the boilers; therefore the gas must be cleaned.

Jan 1, 1936

By A. J. Ardell

SASS and cohenl (S-C) have recently reported some transmission electron microscope observations of an interesting effect which they call "veining". They observed veining in thin foils of solution-treated and (in certain cases) aged samples of a Ni-10.3 at. pct Ti-0.6 at. pct A1 alloy (assumed equal to 10.9 at. pct Ti). S-C suggest that veining in solution-treated samples is due to the selective electrolytic etching of titanium-rich regions in alloys which are otherwise homogeneous. They associate the veins with the discrete titanium-rich regions detected in a magnetic study of aging in this system by Ben Israel and Fine,' and they also suggest that the initial strengthening of aged Ni-Ti alloys is due to these titanium-rich regions, rather than the formation of the coherent precipitate (Ni3Ti, L12 crystal structure).

Jan 1, 1970

By Warren E. Wilson

The transportation of solids in pipe lines is a matter of deep concern in many fields of engineering. Much experimental and theoretical work has been done in an effort to devise means of designing pipe lines that will satisfactorily transport given solid loads, but there remain many unanswered questions in this field. The present discussion will be confined to a rather narrow portion of this field and will endeavor to point out certain factors that may well be considered when comparing the relative economy of various installations. The data have been presented previously but a new interpretation was prompted by a suggestion in a paper by Professor O'Brien,1 of the University of California, that the friction work per pound of dry material should be considered in determining the relative efficiency of various installations. This method of considering relative economy in various pipe lines leads to some rather unexpected conclusions, especially with reference to the economy of large pipe sizes. A previous suggestion by the writer3 concerning the economy of a rather peculiar type of installation is strengthened. It is not believed that the considerations set forth herein apply directly in the case of dredge lines, where economy is largely a matter of a high rate of pumping in order to reduce the unit overhead charge. However, it is believed that some value may be gained from these considerations in cases involving the disposal of a fixed amount of solids per unit time with a minimum expenditure of energy and at a low cost for replacement of worn pipes. Such situations are not uncommon in the disposal of mill tailings and the disposal of solids deposited from irrigation waters. It was found that data leading to general conclusions for various pipe sizes were not available but certain definite trends are indicated and methods of analyzing available data are presented in the hope that they may be of assistance in preparing engineering estimates on designs of pipe lines of the type described above. Energy Requirements Carrying out the idea contained in ' Professor O'Brien's paper concerning the method of computing energy required to transport solids, the following analysis leads to some rather interesting conclusions. Let us represent: Solids load in term of mass per unit time by W Ratio of mass of suspended solids to total mass of mixture flowing by p Volume rate of flow of mixture by Q Length of pipe by L slope of energy grade line by s Mass per unit volume of solids by m. Mass Per unit volume of liquid by mi Mass per unit volume of mixture by mm We then have as an expression for the solids load: W = pQmm The work done per unit mass, P, on the mixture to move it along the pipe the

Jan 1, 1948

By Warren E. Wilson

The transportation of solids in pipe lines is a matter of deep concern in many fields of engineering. Much experimental and theoretical work has been done in an effort to devise means of designing pipe lines that will satisfactorily transport given solid loads, but there remain many unanswered questions in this field. The present discussion will be confined to a rather narrow portion of this field and will endeavor to point out certain factors that may well be considered when comparing the relative economy of various installations. The data have been presented previously but a new interpretation was prompted by a suggestion in a paper by Professor O'Brien,1 of the University of California, that the friction work per pound of dry material should be considered in determining the relative efficiency of various installations. This method of considering relative economy in various pipe lines leads to some rather unexpected conclusions, especially with reference to the economy of large pipe sizes. A previous suggestion by the writer3 concerning the economy of a rather peculiar type of installation is strengthened. It is not believed that the considerations set forth herein apply directly in the case of dredge lines, where economy is largely a matter of a high rate of pumping in order to reduce the unit overhead charge. However, it is believed that some value may be gained from these considerations in cases involving the disposal of a fixed amount of solids per unit time with a minimum expenditure of energy and at a low cost for replacement of worn pipes. Such situations are not uncommon in the disposal of mill tailings and the disposal of solids deposited from irrigation waters. It was found that data leading to general conclusions for various pipe sizes were not available but certain definite trends are indicated and methods of analyzing available data are presented in the hope that they may be of assistance in preparing engineering estimates on designs of pipe lines of the type described above. Energy Requirements Carrying out the idea contained in ' Professor O'Brien's paper concerning the method of computing energy required to transport solids, the following analysis leads to some rather interesting conclusions. Let us represent: Solids load in term of mass per unit time by W Ratio of mass of suspended solids to total mass of mixture flowing by p Volume rate of flow of mixture by Q Length of pipe by L slope of energy grade line by s Mass per unit volume of solids by m. Mass Per unit volume of liquid by mi Mass per unit volume of mixture by mm We then have as an expression for the solids load: W = pQmm The work done per unit mass, P, on the mixture to move it along the pipe the

Jan 1, 1948

By Herbert H. Kellogg, Hugo Vasquez- Rosas

Recently the long-chain primary amines have been used extensively for the flotation of silicate minerals. The use of amines to float sulphide minerals has been investigated by several authorsl-5-l8 but most of this work has been done with the short-chain (less than six carbon atoms) primary amine compounds or the more expensive secondary, tertiary and quaternary amines. Perhaps the fact that the long-chain amines are good collectors for the common gangue minerals has led investigators to omit them from consideration as collectors for the selective flotation of metallic sulphides. The work reported in this paper was designed to investigate the use of a typical long-chain amine salt, laurylamine hydro-chloride, as a collector for the flotation of galena-sphalerite ores. The results show that laurylamine hydrochloride (LAmHCl), when used in small amounts, is a good collector for the selective flotation of sphalerite and galena from the common gangue minerals. The differential flotation of sphalerite from galena was not accomplished but the amine flotation of sphalerite after the standard xanthate flotation of galena is possible. The experimental work reported herein is not complete enough to be able to say whether amine flotation of lead-zinc ores would prove superior to xanthate flotation, or whether the method is even applicable to a more complex ore than the one used for this work. However, the apparent reagent costs for the flotation operations described in this paper seem to be less than for xanthate flotation. This fact alone should be sufficient to encourage the millman to investigate the use of these amine reagents, especially as these reagents are available on a commercial scale at a reasonable price. This paper has as its secondary purposes to illustrate how contact-angle measurements have aided in this investigation, and to bring forward some evidence concerning the mechanism of the collecting action of primary amines. Contact-angle Tests The contact-angle measurements were made by the method described by del Giudice6 and used in recent work by Taggart and his collaborators.7-9 The mineral specimens for the contact-angle tests were carefully chosen, to avoid cracks and inclusions of other minerals. All specimens were mounted in "transoptic" plastic mounts and the surfaces were cleaned by polishing with levigated alumina on a cloth-coverkd glass polishing wheel. Distilled water was used on the lap during the polishing and at all subsequent steps in the contact-angle tests. The mounted mineral specimens were handled with glass forceps and special care was exercised to prevent exposure of the clean surface to air or any other source of contamination.

Jan 1, 1947

By Herbert H. Kellogg, Hugo Vasquez- Rosas

Recently the long-chain primary amines have been used extensively for the flotation of silicate minerals. The use of amines to float sulphide minerals has been investigated by several authorsl-5-l8 but most of this work has been done with the short-chain (less than six carbon atoms) primary amine compounds or the more expensive secondary, tertiary and quaternary amines. Perhaps the fact that the long-chain amines are good collectors for the common gangue minerals has led investigators to omit them from consideration as collectors for the selective flotation of metallic sulphides. The work reported in this paper was designed to investigate the use of a typical long-chain amine salt, laurylamine hydro-chloride, as a collector for the flotation of galena-sphalerite ores. The results show that laurylamine hydrochloride (LAmHCl), when used in small amounts, is a good collector for the selective flotation of sphalerite and galena from the common gangue minerals. The differential flotation of sphalerite from galena was not accomplished but the amine flotation of sphalerite after the standard xanthate flotation of galena is possible. The experimental work reported herein is not complete enough to be able to say whether amine flotation of lead-zinc ores would prove superior to xanthate flotation, or whether the method is even applicable to a more complex ore than the one used for this work. However, the apparent reagent costs for the flotation operations described in this paper seem to be less than for xanthate flotation. This fact alone should be sufficient to encourage the millman to investigate the use of these amine reagents, especially as these reagents are available on a commercial scale at a reasonable price. This paper has as its secondary purposes to illustrate how contact-angle measurements have aided in this investigation, and to bring forward some evidence concerning the mechanism of the collecting action of primary amines. Contact-angle Tests The contact-angle measurements were made by the method described by del Giudice6 and used in recent work by Taggart and his collaborators.7-9 The mineral specimens for the contact-angle tests were carefully chosen, to avoid cracks and inclusions of other minerals. All specimens were mounted in "transoptic" plastic mounts and the surfaces were cleaned by polishing with levigated alumina on a cloth-coverkd glass polishing wheel. Distilled water was used on the lap during the polishing and at all subsequent steps in the contact-angle tests. The mounted mineral specimens were handled with glass forceps and special care was exercised to prevent exposure of the clean surface to air or any other source of contamination.

Jan 1, 1947

By M. C. Fuerstenau, D. W. Fuerstenau

Studies of the collection of alkali and ammonium halides utilizing vacuum flotation techniques and contact angle measurements show that ionic size controls the flotation of techniquesthese halides with amine salts measurementsas collector. Contact angles of air bubbles on sylvite in saturated brines were withaminemeasured salts asascollector.a function of such variables as collector addition, length of collector chain, and pH of the brine. No contact occurs between halite and an air bubble in brines containing dodecylammonium acetate as collector. LONG-CHAINED aliphatic amine salts have been used for the separation of sylvite (KCl) from halite (NaCl) by flotation.1,2 It is puzzling how these two minerals, which are so similar chemically and crystallographically, can be separated by this method. Gaudin" has postulated that the difference in floatability of halite and sylvite with salts of primary amines depends on ionic size: In the case of amine flotation, the cation would attach itself to the chloride. I have a speculation there, which I cannot prove, that the ammonium group, that is the —NH3 group in the amine, floats potassium chloride because the dimensions of this grour, as it has been measured in other compounds is almost identically the dimensions of the potassium ion, quite different from the sodium ion, and so it fits where potassium had been, in place of it and not attached to it. Apparently, because an aminium ion (RNH3+) is much larger than a sodium ion, it cannot fit into the lattice of halite. Taggart also has speculated that ionic size may control the floatability of sylvite.4 The object of this experimental investigation has been to test this hypothesis and to study what controls the adsorption of cationic collectors at the surface of sylvite. Since collection is to be approached from the viewpoint of ionic size, the ionic radii that are of interest in this work are presented in Table I. The values of the ionic radii of the ions listed in Table I, except NH4+, are those given by Pauling." Several different values for the radius of the ammonium ion have been given, but that of Goldschmidt6 seems to be preferred. The radius of the charged head of a dodecylammonium ion is assumed to be the same as that for the ammonium ion. Little experimental work has been reported in the technical literature concerning the separation of sylvite from halite by flotation. Guyer and Perren studied the separation by flotation of 50 pct binary mixtures of NaCl, KC1, NH,Cl, NaNO3, KNO3, K2SO4, and Na,SO, using either oleic acid or a sodium sul-fonate as collector.' It is possible to measure floatability under actual flotation conditions where all three phases, air- water-mineral, are present by vacuum flotation tests and contact angle measurements.9 Both of these techniques were used in the experimental approach in this paper. Experimental Method and Materials The vacuum flotation tests were run with glass-stoppered pyrex graduated cylinders. Twenty-five ml graduates were used to test the floatability of all salts studied except rubidium and cesium salts. For each test distilled water containing the desired collector concentration was saturated with the salt to be floated. Sufficient salt (—48 mesh) was added to leave about 2 ml of solids in the bottom of the graduate. After the graduate had been agitated several minutes to saturate the solution with air, a vacuum was applied. If the salt were floatable in the collector solution, the gas bubbles attached themselves to the particles, and the particles floated to the surface. In determining the floatability of the expensive Rb and Cs halides, the experiments were run in 10 ml graduates with about 11/2 ml of collector solution initially. Contact angles were measured in the usual manner except that the solutions had to be previously saturated with the mineral to avoid dissolution of the crystal. Solutions for studying contact angles were made by adding the desired amount of collector to a saturated brine, giving the collector concentration in molarity. The mixture was agitated until dissolution of the collector was complete, with the exception of those concentrations greater than about millimolar. At these high concentrations complete dissolution of the collector was impossible. The face of the mineral to be tested was a freshly cleaved crystal of halite or sylvite. The mineral was placed in the brine and conditioned with collector for at least 15 min, which was found to be long enough to obtain a maximum value for the contact angle. The temperature remained constant during each experiment. The experiments were run at 24°C ±2°C. For contact angle measurements, a crystal of halite from Carlsbad, N. M., was used. Several samples of sylvite were used in this work: a crystal of sylvite from Stassfurt, Germany; a crystal from Carlsbad, N. M.; and a crystal of chemically pure potassium chloride. Saturated brines were made from reagent grade chemicals and distilled water.

Jan 1, 1957

By S. W. Poole, J. A. Rosa

The object of this investigation was to determine the distribution of chemical elements within a large, killed alloy-steel ingot, by sulphur printing and quantitative chemical analysis. With regard to segregation in steel ingots, the factors of melting practice, pouring temperatures, mold design, etc., and the mechanics of solidification and its attendant functions, have been the subject of intensive study over a period of years by many investigators. Notable among these is the Sub-committee of the No. 5 Committee of the British Iron and Steel Institute. For an exposition of the many problems awaiting the researcher on the heterogeneity of steel ingots, the methods of attacking these problems, together with some of the answers, the reader is referred to the nine reports and numerous papers of that committee and its membership. Steelmaking Data Melt.—The heat was made in a 70-ton direct arc-type basic electric furnace. Furnace charge consisted of nickel-chromium-molybdenum steel, most of it in the form of heavy mill scrap. All of the scrap was charged cold. The standard double-slag method was employed, the heat being finished under a strong carbide slag. Aluminum was used as the deoxidizing agent. Tapping tempera- ture, as observed with an optical pyrometer, was 3000°F. Detail of Mold and Ingot Size.—Details of the ingot mold and the ingot itself are given in Fig. I. Teeming.—Teeming temperature of the subject ingot as observed with an optical pyrometer was 2830°F. The ingot was top-poured directly through a 1 1/2-in. nozzle and required 7 min., 44 sec. to fill up to the hot top. An additional 2 min., 30 sec. were required to fill the hot top. The ingot was stripped hot and charged with the remainder of the heat into an annealing furnace. There it was given the standard annealing cycle used for these ingots. Subsequent heat-treatments are described elsewhere in this paper. Sectioning and Preparation for Sulphur Printing Because of previous favorable experience in sectioning ingots up to 21 1/2 in. square with an oxyacetylene torch, it was decided to use this method to section the subject ingot. The ingot was preheated to 900°F. for 12 hr. It was then placed on a steel bed in a horizontal position so that the longitudinal axis was level and parallel to the track of the motor-driven torch carrier. Two cuts were made, one 2 in. above the longitudinal axis and the other 2 in. below. The time required to make each cut was approximately 75 min. The cutting operation is shown in Figs. 2 and 3. The 4-in. thick slab was mmediately charged into a furnace standing at 1200F.

Jan 1, 1945

By G. E. McElroy

MUCH attention has been directed to mine-air flow in recent years, more especially in Great Britian where there is frequent reference to a theory of fluid flow developed by English engineers. Briefly stated, this theory is that for similar passages of the same relative roughness, in which fluid flow occurs, the conditions of flow are exactly the same for equal values of the product W D V/ µ, where W = density of the fluid, D = diameter of the passage through which flow occurs, V = mean velocity of flow, and µ = absolute viscosity of the fluid flowing. This, the "Reynolds Criterion" of fluid flow, had its origin in the work of Prof. Osborne Reynolds' more than 40 years ago. Later, Lord Rayleigh amplified the theory2 which has been conclusively proved for small pipes by the experiments of Stanton and Pannel3 over a large flow range, and by Lacey4 over a somewhat more limited range. Concordant results on small pipes have also been obtained by numerous other investigators with single fluids over more or less limited ranges of flow. According to this theory results in one medium, such as water, are immediately applicable to another, such as air; and experimental results on models are (theoretically, at least) applicable to full-scale designs. This is of great importance in aeronautics and can be of considerable value in mine ventilation research. Hodgson, in a recent paper,5 has outlined the application of this theory to mine-air flow and recent English experiments" on the resistance of a timbered mine airway have been expressed in this form.

Jan 10, 1926

By Roswell Johnson

THE Manual of the Oil and Gas Industry, under the Revenue Act of 1918, published by the Treasury Department for the guidance of oil companies in preparing their estimates of future recoverable oil for the purpose of calculating depletion, gives the first large public collection of comparative decline curves for the whole country. It is a matter of both scientific and practical interest to so arrange these data that the pools can be readily compared. There are certain difficulties in such a comparison, however: 1. The economic limit varies from 50 to 2000 bbl. a year in different pools taken. (2) Because of this variation in economic limit, the range of data shown makes comparison possible only for wells of intermediate size. In order to be as inclusive as possible, I have taken as an expression of the rate of decline the amount of oil produced in the period during which a well drops from 3000 to 2000 bbl. a year.. No period of smaller production could be used because of the high economic limit in California; and no period of larger production and yet include the small well areas of the Appalachian. As it is, the Lima-Indiana wells are excluded. In a few instances, curves were extrapolated to obtain the reading, where the curve seemed regular enough to warrant it. In general, the amount of oil, in barrels, produced while a well declined from 3000 bbl. to 2000 bbl. a year is shown in Table 1.

Jan 1, 1920

By ME ME

IT just so happens that we do our best thinking while painting wood- work and last Saturday while finishing up the screens (the bugs come late where we live) the paint very nearly ran out. By adding turpentine, it just stretched. It was pretty thin for the job though, which made us think that that is just about what the situation is going to be in the mining industry if something isn't done to increase the number of enrollments in engineering curricula. Engineers are going to be spread too thin for the job at hand.

Jan 8, 1951

By J. F. Abel

It can be concluded that rock mechanics instrumentation, geologic mapping, and operations research in combination will produce an accurate estimate of tunnel support requirements for establishing a steel-set load prediction model. This estimate can be used to increase safety and to reduce tunneling costs. Unnecessary supports can be eliminated; overloaded or insufficient supports can be replaced on a more scientific basis than previously possible. Only a limited number of measurements are required to develop a steel set load prediction model. The results of this study can be applied generally; but, every tunnel must be considered as a separate problem. The construction and geologic variables which were found to be significant in the prediction of rock loads in this tunnel were: steel section modulus, set blocking points, percentage of alteration, relative degree of faulting, relative water condition, distance to the nearest fault, and average joint spacing. INTRODUCTION A combined engineering geology and rock mechanics program was performed throughout the Straight Creek tunnel pilot bore in Colorado in order to develop a technique for estimation of steel tunnel support loads. The technique involves the construction of a statistical model from measured steel set loads, geologic and construction factors. The aim of the investigation was to produce a set of charts, based on these factors, which could be used by a trained man equipped with a hand lens and measuring tape, to specify a safe and economical steel size and set spacing. In order to be of practical value the measured parameters had to be rapidly measurable and capable of quantification. It was apparent from the beginning that quantitative values for many of the geologic factors would have to be arbitrary. It was impossible to ascertain in advance which of the readily determi-nable geologic and construction factors significantly affect steel set loading. As the investigation progressed the number of observations was systematically reduced in order to determine the minimum amount of data which would be necessary for a significant mathematical model. This paper presents an analysis of all the variables measured at each instrumented steel set. The statistical significance of the measured variables was determined. On the basis of this determination, a mathematical model was constructed and charts were prepared to select and space the steel tunnel supports at any given point in the tunnel. Once the effect of geologic and construction factors on set loading is sufficiently established, it is possible to exert close control over the selection of steel tunnel support size and spacing. The magnitude of this rock mechanics program can be appreciated when it is known that there were 44 instrumentation stations for which steel set loads were measured. For each of these sets there were three construction variables recorded, and nine geologic parameters determined (Table I). A rough approximation of the cost for both the collection and reduction of the data would be $50,000. This is in addition to the cost of geologic mapping.

Jan 1, 1967

By H. L. Gilbert, H. A. Johansen, R. G. Nelson

High purity electrolytic chromium plate has been hydrogen-reduced and arc-melted under inert atmosphere to give sound ingots. These ingots may be hot forged to break the as-cast structure and then worked at 500°C to finished form. An intermediate and final high temperature anneal gives best ductility and grain refinement. HE increasing interest in refractory metals for I use in high temperature gas turbines, jets, and rockets has led to great efforts in exploiting the fifth and sixth groups of transition elements. Much of the interest has centered upon production of metals that can be worked and fabricated by normal means to produce various engine parts or components having the high temperature characteristics of oxidation resistance and high creep strength required for such uses. If these pure elements do not exhibit all of the desired characteristics, it may be possible to obtain a high purity alloy that will. Since, in all cases, development of these transition elements has depended to a large extent upon removal of oxygen and nitrogen as a means for producing ductile metal, the hypothesis has been accepted that oxygen is the normal embrittling material in a high grade electrolytic chromium metal. Various methods have been employed in an effort to remove this oxygen by direct or indirect attack.' Many workers have endeavored to produce pure chromium through reduction of the oxide by carbon or active metals, while others have recommended fusion electrolysis of chromium salts or reduction of these salts by active metals, such as sodium or calcium. Hydrogen reduction of the oxide or chloride and thermal dissociation of the iodide have been reported to give high purity metal. Experimental Work The U. S. Bureau of Mines, Northwest Electro-development Laboratory, has systematically re-examined the more promising methods and developed two which produce metal having ductility at temperatures lower than heretofore described. It has been found' that oxide-free chromium chlorides in a NaCl-KCl carrier salt may be mag- nesium-reduced and the byproduct salts distilled off in vacuo to give a high purity chromium sponge. Fusion analysis conducted under the supervision of W. W. Horton of Knolls Atomic Power Laboratory showed the oxygen and nitrogen both to be below 10 parts per million on a selected sample. A small amount of carbon is carried over in the final metal from the chlorination and reduction steps which are carried out in graphite crucibles. This trace of carbon is not detrimental to hot ductility. A more practical method for producing ductile metal is through hydrogen reduction of high purity electrolytic chromium. Normal electrolytic chromium will, if "developed" for a few minutes at 1100°C in high vacuum, be found by the method of Adcock:; to contain about 1 pct chromium sesquioxide (Cr2O3). This small amount of oxygen may be effectively reduced by hydrogen.2, 4 The method employed was to crush electrolytic chromium plate in a gyratory crusher to pass 60-mesh; finer crushing appears to offer no advantage. A nitric acid leach removed the iron picked up during crushing. The leached powder was rinsed until neutral with distilled water and vacuum-dried.

Jan 1, 1954

By L. L. Wyman

Previous studies1 by the writer dealing with the embrittlement of copper have been concerned with the behavior of various pure and deoxidized coppers when exposed to an oxidation-reduction cycle, and the consequent evaluation of these materials on the basis of their resistance to this action. No attention was devoted to the variations in penetration of embrittlement with time, when these copper materials are exposed to a strong reducing gas, such as hydrogen, nor to the variations in oxygen penetration, with time and temperature, into the "pure" coppers. The cause of the embrittlement is the reduction of the oxygen in the copper by the hot reducing gas, so that a consideration of time, temperature, the occurrence of hydrogen and oxygen must be given. For the purpose of differentiating some of the involved factors, the present work may be divided into two separate series of experiments. The first of these deals with the oxidation of purified coppers under various conditions and then the subjection of these to a standard hydrogen treatment. The second series concerns the reduction, under different conditions, of tough-pitch coppers of several oxygen contents. The resulting data will give the rates of oxidation, and of reduction, for the materials involved. The first series of experiments will reveal how rapidly copper may become oxidized, while the second series will indicate how rapidly embrittlement will penetrate into an oxygen-containing copper when it is exposed to hydrogen at different temperatures. Materials For the purpose of determining these variables, three types of material were selected, to cover the extremes in the ranges of materials commercially obtainable. The first class of materials is represented by an oxygen-free copper, as well as the high-purity vacuum-melted copper2 used in previous work. These materials were selected to determine the variation of oxidation with time and temperature, by oxidizing these coppers under various combinations of these factors, and noting the effect as indicated by a

Jan 1, 1934

By C. S. Smith, Chih-Chung Wang

TURNBULL and his collaborators1,2 have developed the theory of homogeneous nucleation as applied, inter alia, to solidification of liquid metals. Vonnegut³ and Turnbull4 have shown that if a liquid metal is subdivided into small droplets a vast majority of them will undercool very considerably before solidification, generally to as low as about 0.8 of the freezing temperature on the absolute scale. The nuclei effective at small degrees of supercooling in bulk metal seem to be internal or surface heterogeneities, relatively small in number. If the metal is subdivided, those droplets that happen to contain such nuclei will solidify at a temperature not greatly below the true freezing point, but only a small part of the whole volume will be affected and the majority of the drops will under-cool to the much lower temperature at which homo- geneous nucleation occurs as a result of fluctuations. It occurred to one of the authors that an appropriate subdivision to give effective freedom from random nuclei is produced during the solidification of many alloys that contain a minor amount of a phase of low melting point, and that one might then expect marked undercooling of the distributed phase. Experimental: The alloys selected for initial study were copper with minor amounts of lead and bismuth, and aluminum with tin. In all these alloys, the major component freezes at a temperature not much below that of the pure metal, and there is little further change in constitution on cooling until the lower melting point constituent freezes in an almost pure state. Cooling curves were taken using the controlled heat flow method permitting approximate specific heats to be obtained. Chromel-alumel thermocouples were used, with the standard emf tables, since extreme precision was not needed. The crucible (3/4 in. id, 5/16 in. wall) was made of B & W K-20 insulating brick. It held about 10 cc of the alloy being investigated. The cooling rate was 2.5" to 2.9°C per min under a controlled temperature difference of 20°. Approximate specific heats were computed from the inverse rate curves together with data from a blank run and from a standard run with a copper cylinder of known heat capacity. The alloys for investigation were made from high-purity metals (99.99+pct) and cast into graphite molds. The castings were machined to fit the crucible and to provide a hole for the inner thermocouple. Cooling curves were taken after heating to a temperature about 50" above the melting point of the minor, lower melting-point, constituent. Results The lead phase in an alloy of copper with 5 pct lead did not undercool more than 3" below the melting point of lead (327°C) either as cast or after annealing to produce a new dispersion of the liquid phase. A copper-zinc-lead alloy with 23.75 pct zinc and 5 pct lead undercooled more but showed no thermal effect below 319°C. A cast alloy of copper with 5 pct bismuth undercooled to 249°C (M.P. bismuth 27l °C), but once solidification started it was completed at the same temperature. This was anticipated, since the bismuth forms a nearly continuous phase between the grains of copper, and a solid crystal nucleated anywhere would rapidly* con- sume the entire network of liquid, unless the physical continuity of the liquid were broken through volume changes, inadequate fluidity, or gas evolution. Similar arguments apply in the case of copper-lead alloys, where the lead-rich liquid forms a network along grain edges, though not grain faces. In both cases there would be a few isolated particles

Jan 1, 1951