By R. J. Marcotte, C. T. Eddy, R. J. Smith

THE objectives of the investigation herein reported were to determine: (I) the S-curves for certain selected cast steels, (2) whether or not the published S-curves for wrought steels are satisfactory for use on cast steels of similar composition, and (3) to prepare hardenability curves of the selected cast steels. In order to make the final comparisons between cast and wrought steel more completely tangible, it was deemed advisable not only to determine S-curves for the steels submitted in the cast condition but also to roll some of the cast-steel test bars and determine comparison S-curves on such wrought material. This procedure eliminates the composition variable and makes it possible to reveal the differences resulting from plastic deformation of the cast structure in addition to providing the comparison with published data on wrought steels. CAST STEELS The cast steels selected for the preparation of S-curves, or time-temperature transformation curves, were similar to S.A.E. series 1030, 2330, 4130 and 4330. Of these the 1030 was supplied by The Crucible Steel Casting Co., Cleveland, Ohio, and the other three by The Sawbrook Steel Castings Co., Lockland, Ohio. The steels were furnished in the as-cast condition. The manufacturers supplied the chemical analyses and the properties that could be obtained in the heat-treated condition-all of which is summarized in Table I. [ ] PROCEDURE The metallographic and dilatometric procedures and equipment were in general standard. The specific technique employed was described in a report of the Steel

Jan 1, 1945

By Thomas Fraser, Alvaro Abreu

The work described in this paper was carried out under the sponsorship of the Foreign Economics Administration and in cooperation with the Departamento Nacional da Produggo Mineral, Rio de Janeiro. The project was undertaken to obtain complete data on the variations in washability of coal to be used for coke manufacture in the steel industry and to determine the economy of preliminary hand-sorting operations. The coal-producing industry of Brazil is in that pioneering stage in which operating practices and methods are just being developed. Increased wartime demand for fuel, coincident with a drastic curtailment of foreign supplies due to lack of shipping facilities, has put a tremendous pressure on the national industry to furnish more coal. Under this incentive, production facilities are being -expanded- and new methods of operation are being tested. Such changes are being developed both by improvement of existing methods that originated in the field and by adaptation and modification of methods introduced from the United States and Europe. These mining conditions and mining practices in Brazil are typical of what the American mining engineer will find in many instances when he goes pioneering into the developing coal fields of the Southern Hemisphere. The producing coal fields of Brazil are all in the southern states of that country. The coal measures are in a band roughly paralleling the coast and extending in a generally southwesterly direction from northern Sao Paulo through the states of Paraná, Santa Catarina and Rio Grande do Sul to near the Uruguayan border in the vicinity of Bajé. The accompanying map1 (Fig. I) shows the general location of these fields and also the principal routes of movement of both national and imported coal in a late pre-war year (1940). Statistical data on production by states up to that year are given in Table I. Rio Grande do Sul is still the largest producer among the coal states; but wartime

Jan 1, 1947

By Alvaro Abreu, Thomas Fraser

The work described in this paper was carried out under the sponsorship of the Foreign Economics Administration and in cooperation with the Departamento Nacional da Produggo Mineral, Rio de Janeiro. The project was undertaken to obtain complete data on the variations in washability of coal to be used for coke manufacture in the steel industry and to determine the economy of preliminary hand-sorting operations. The coal-producing industry of Brazil is in that pioneering stage in which operating practices and methods are just being developed. Increased wartime demand for fuel, coincident with a drastic curtailment of foreign supplies due to lack of shipping facilities, has put a tremendous pressure on the national industry to furnish more coal. Under this incentive, production facilities are being -expanded- and new methods of operation are being tested. Such changes are being developed both by improvement of existing methods that originated in the field and by adaptation and modification of methods introduced from the United States and Europe. These mining conditions and mining practices in Brazil are typical of what the American mining engineer will find in many instances when he goes pioneering into the developing coal fields of the Southern Hemisphere. The producing coal fields of Brazil are all in the southern states of that country. The coal measures are in a band roughly paralleling the coast and extending in a generally southwesterly direction from northern Sao Paulo through the states of Paraná, Santa Catarina and Rio Grande do Sul to near the Uruguayan border in the vicinity of Bajé. The accompanying map1 (Fig. I) shows the general location of these fields and also the principal routes of movement of both national and imported coal in a late pre-war year (1940). Statistical data on production by states up to that year are given in Table I. Rio Grande do Sul is still the largest producer among the coal states; but wartime

Jan 1, 1947

By C. H. Chou, Albert Sauveur

The following experiments were conducted in order to study the influence of the rate of cooling through and below solidification on the dendritic structure (macrostructure) and microstructure of some hypo-eutectoid steel. The steel selected was of commercial grade and had the following composition: C, 0.40 per cent.; Mn, 0.85; Si, 0.70; P, 0.099; S, 0.043. After melting in vacuum in an Arsem furnace, the various samples were allowed to solidify and to cool to room temperature as indicated in Fig. I. Samples were thus obtained representing all possible combinations of slow and fast cooling through the various ranges of temperatures indicated, namely: (I) zone of solidification or primary crystallization, (2) zone of granulation, and (3) zone of secondary crystallization. The location of the different temperature zones in the iron-carbon equilibrium diagram is shown in Fig. 2. The authors adopted Belaiew's notations. The designations of the various samples readily indicate their treatment, as will be apparent from Table 1. Sample SSS.—This sample was slowly solidified and cooled to room temperature in the crucible in which it was melted. The dendritic (macro) structure is shown in Fig. 3. The dendrites an: sharp and dis-

Jan 1, 1930

By K. P. Mukherjee, K. P. Gupta, J. Bandyopadhyaya

Even though a lot of work has been done in the past to establish phase equilibrium in the Cu-Si system a re cent investigation casts some doubt about the existence and crystal structure of some of the phases that form in the composition range of 15 to 25 at. pct Si in Cu. The present investigation was carried out using high temperature X-ray diffraction technique along with other standard techniques to study the phases in this composition range. The high temperature 6 phase appears to be tetragonal with parameters a,, = 8.815A, c, = 7.903A, and co/ao = 0.896. The reported bcc E phase exists at room temperature and at least up to 780°C and appears to undergo a transformation near 600°C. The phase appears to be cubic but not of the bcc type. The ? phase appears to undergo a transformation, as has been indicated by earlier investigators, and the low temperature form of .? phase is tetragonal with parameters a, = 7.267A, co = 7.8924, and co/ao = 1.086. THE Cu-Si binary system has been investigated by several investigators1" and several intermediate phases,?,e,?' at lower temperatures and ?,ß,0,e, and ? at higher temperatures, were observed between terminal solid solutions of copper and silicon. Even though the existence of the e phase and the transformation in the ? phase were reported in many early works, in a recent study of this system Nowotny and Bittner6 doubted the existence of the e phase and phase at 550°C. Among the high temperature phases, the 6 phase was reported to have a complex cubic structure with parameter a, = 8.805A.7 Nowotny and Bittner, however, suggested that the structure of the 6 phase might be of CsCl type. In order to check these contradictory reports the present study was taken up to investigate the Cu-Si binary system in the composition range of 17 to 25 at. pct Si. EXPERIMENTAL PROCEDURE Weighed amounts of copper (99.99 pct) and silicon (99.9 pct) were induction melted in recrystallized alumina crucibles under argon gas atmosphere. The alloys containing 17, 18, 20, 21, 21.2, 22, and 24 at. pct Si were annealed in evacuated and sealed quartz capsules at 700°C for 3 days and subsequently water quenched. Other than this annealing, the 21.2 at. pct Si and 24 at. pct Si alloys were annealed at 550°C for 10 days, the 17 at. pct Si alloy was annealed at 750°C for 3 days, and the 22 and 24 at. pct Si alloys were annealed at 780°C for 2 days. All annealing temperatures were controlled to within *l°C. Alloys after quenching were subjected to metallographic and X-ray diffraction investigation. A solution containing 5 g FeC13 + 10 cc HCl + 120 cc H2O diluted with six times its volume with water was used as etching reagent. A 114.6 mm diam Debye Scherrer camera was used for obtaining diffraction patterns. The 17, 21.2, and 24 at. pct Si alloys were subjected to high temperature diffractometry using a Tempress Research High temperature attachment and a GEXRD VI diffractometer. For the 6 phase (17 at. pct Si alloy) powder specimen from a 750°C annealed alloy was reheated to 750°C in the high temperature attachment for 1½ hr before taking a diffraction trace. A 550°C annealed and slowly cooled phase (24 at. pct Si) alloy was first reheated to 550°C. a diffraction trace was made after annealing it for 2 hr, and subsequently it was heated to 716OC and kept at this temperature for 2 hr before taking a diffraction trace. For the e phase (21.2 at. pct Si alloy) a 550°C annealed and slowly cooled specimen was heated first to 425°C and annealed at this temperature for 2 hr before taking a diffraction trace. Subsequently, the specimen temperature was raised to 495", 540°, 603", 635", 682", 720°, and 748°C and homogenized at each temperature for 1 hr before taking diffraction traces. The powder specimen temperature was controlled to within +2oC at each temperature and argon gas, purified by passing it at slow rate through a fused CaC12 column, hot (800°C) copper and titanium chips and finally through a P2O5 column, was used to prevent oxidation of the powder. For all X-ray work copper-radiations at 25 kv, 15 ma (for Debye Scherrer technique), and 40 kv, 20 ma (for diffractometer tech-nique) were used. RESULTS AND DISCUSSION At 700°C the alloys containing 17 to 21 at. pct Si showed two phases while the 21.2 at. pct Si alloy was found to be single phase. The X-ray diffraction patterns of the two-phase alloys were consistent with the phase (ßP-Mn type structure) and the phase (21.2 at. pct Si) patterns. The diffraction patterns of the 17 at. pct Si alloy quenched from 750" and 700°C were identical. According to the accepted Cu-Si phase dia-gram4,5,10 the 17 at. pct Si alloy at 750°C should be in the (k + 6) two-phase region and very close to the -phase boundary. The identical patterns possibly resulted from the decomposition of the 6 phase on

Jan 1, 1970

By L. W. McKeehan, W. C. Elmore

THE magnetic powder method, long used for roughly mapping magnetic fields, has recently been refined 1,2 for investigating the microscopic variations in the surface magnetization of ferromagnetic crystals. Bitter' first discovered regular powder patterns connected with the crystal structure of such specimens. Several other investigators3 have used Bitter's original technique, with slight modifications, to study the variation of the patterns with variations in the magnetizing field applied parallel to the surface, and their dependence upon the state of strain, of polish and of crystal cut. All of the explanations of these patterns on metallic ferromagnetics have been couched in general terms. In a preliminary report we have described an improvement in the powder technique which led us to the discovery of a new effect throwing considerable light on the magnetic secondary structure of alpha iron4 and of nickel' single crystals. We now report additional evidence confirming the existence and stability of a magnetic block secondary structure. SPECIMENS The following list describes the specimens used in the present investigation. DESIGNATION DESCRIPTION A1 Silicon ferrite furnished to us by Dr. W. E. Ruder, of the General Electric Co., for which he gave the following typical analysis: C, 0.05; P, 0.038; 5, 0.026; Mn, 0.15; Si, 3.24. Disk, 0.60 cm. diameter, about 0.05 cm. thick.

Jan 1, 1935

By E. G. Williams

Manganese-ore has been found upon the Isthmus of Panama throughout' a region of nearly three hundred square miles, over the greater part of which, however, it is known only in small bodies without commercial value. Only six mines, controlled by two companies, have actually shipped ore, although a large area has been taken up in miningelaims. The ore-bearing region extends along the coast of the Carib. bean Sea, beginning on the west near Puerto Bello and extending easterly about 35 miles toward Point San Blas. Ore has been discovered in the interior, at a maximum distance of about 10 m. from the coast. Fig. 1 is a map of a portion of the Isthmus

Jan 1, 1903

Papers in Classes A-Metal Mining, B-Milling and Concentration, H-Indus¬trial Minerals, and I-Mining Geology are distributed in MINING TECHNOLOGY, which is issued every other month. Papers in Classes C-Iron and Steel Division, D¬-Nonferrous Metallurgy and E-Institute of Metals Division are distributed in METALS TECHNOLOGY, which is issued twice quarterly. Papers in Class G-Pe¬troleum Division are distributed in PE¬TROLEUM TECHNOLOGY, which is issued every other month. TECHNICAL PUBLICA¬TIONS in Classes F-Coal Division, J¬-Mineral Industry Education Division, K¬-Mining Administration, and 1-Geophysics, are issued as separate pamphlets. Contributions are papers that when printed or mimeographed are available but only on request.

Jan 1, 1943

By I. E. Rosenzweig

GEOPHYSICAL prospecting by earth-resistivity methods is frequently applied to investigation of structural problems in geology. Fig. 1 indicates a scheme of the general arrangement used in these methods of measurements. The battery (or generator) E is connected with two "current electrodes" II and 12. The current of intensity J, supplied by this battery, passes through the earth between these elec- FIG. 1.-GENERAL ARRANGEMENT OF APPARATUS. trodes. A potential difference U will be measured between two other electrodes V1 and V2, called "potential electrodes." According to the configuration of electrodes (Fig. 1), the resistivity of a homogeneous soil results from the formula p = 2pcaU/J [1] where c=1/a/b11 - a/b12 ? (a/b21-a/b22) [2]

Jan 1, 1938

By George Smith

ChillaQoe is situated in latitude 17" S., about 138 miles from the port of Cairns, with which it is now connected by rail. A township has been established on the banks of Chillagoe creek, a perennial stream of irregular volume crossing the field almost at rightrangles, nearly midway between the mining-camps of Calcifer and Mungana, which have been formed at the southeastern and western extremes of the field respectively. This situation was selected because of the water-supply and its proximity to the site most suitable for the erection of reductionworks. By its central position it commands the whole of the mines. The altitude above sea-level is about 1200 ft., whereas that of Calcifer and Mungana is 1400 ft.—a difference sufficient to account for a materially higher temperature at Chillagoe. The surrounding limestone bluffis add by radiation to the heat, and, at the same time, prevent the cool breezes from passing freely through the town; consequently, the temper* ture, which is high throughout the year, and especially so during the summer months, is here ge~ierally very oppressive also. The general trend of the field is southeast and northwest, and its length about 18 miles, with an average width of 5 miles; the approximate area is thus 90 sq. miles. The surrounding mineral-district is, however, much more extensive, and numerous other mines, sprcad over wide areas and producing a variety of minerals, exist in the same or parallel belts of mineralized country, of which Chillagoe proper covers but a very small portion. Immense bluffs of limestone, wollastonite and conglomerate, rising in places to nearly 300 ft., and so~netimes nearly a quarter-mile across, give the field a very picturesque and interesting appearance. The limestone has been classified as Devo-

Jan 1, 1904

By J. S. Ross

Few Canadians realize the role of their domestic industrial minerals industry because it is over-shadowed in production value by a large metallic minerals industry. But since 1960, Canada has had a reasonably well balanced, mature industrial minerals industry; and although the nation's sparsely scattered population has not been able to support an industrial minerals industry in a manner comparable to the domestic and foreign support given the metal mining sector, Canada is, nevertheless, exporting large quantities of higher priced nonmetallic minerals. Production of many of the basic minerals had been firmly established long before 1960, but it was not until the late 1950's that the output of cement, salt, titanium dioxide pigment and slag, sulfur, gypsum and sodium sulfate reached relatively high levels. Shortly after 1960, the significant potash and lithium chemicals industries were established and their effect is just now being realized.

Jan 11, 1964

By J. Q. Ehrgott

INTRODUCTION The U. S. Army Engineer Waterways Experiment Station (WES), under sponsorship of the Defense Atomic Support Agency, has recently developed a unique dynamic high-pressure triaxial testing device (DHT). The device permits acquisition of both axial and lateral deformation data while undisturbed soil and/or rock specimens are subjected to various states of controlled impulsive-type stresses produced by varying both the axial stress and the radial stress rapidly with time. The device is used to develop controlled dynamic pressure pulses within the triaxial chamber fluid on soil or rock test specimens to 3 inches in diameter. Controlled dynamic axial pulse loads are delivered to the specimen by a piston driven by an existing pneumatic ram loader (SECO). The DHT consists of a triaxial cell and a pressure supply and decay system which permits the chamber pressure to be varied with time. Together the DHT and SECO operate in a testing program so as to provide time varying confining pressures and axial loads to test specimens at independently controlled but synchronized programmed rise, hold, and decay times. Rise time is defined as the time from zero load or pressure to peak load or pressure; hold time is the time of constant peak load or pressure; and the decay time is the time from peak load or pressure to zero load or pressure. The maximum dynamic confining pressure attainable is approximately 15,000 psi and the fastest rise and decay times are 3 millisecond (msec) and 20 msec, respectively. This paper presents a description of the DHT, the necessary support equipment, and details of the measurement system. Performance evaluation tests conducted on clay siltstone and a Cretaceous sandstone are presented since the results demonstrate some of the capabilities of the device and show some of its characteristics.

Jan 1, 1971

By Myrick N. Bolles

The concentration of gold and silver in mattes low in copper, and the subsequent separation and recovery of either or both of these metals, is a question the satisfactory solution of which has long vexed metallurgists. It covers a broad and important department of metallurgical science and brings in its train a series of attendant problems continuing from the initial operations of concentration to the final recovery of " values."

Jan 1, 1905

By Stephen Krickovic

THERE is today no proven continuous mining machine that can be used under all the varying conditions found in most bituminous coal mines. During the last five years, however, both the machines and methods of using them have been improved. Coal operators can now exercise a fair degree of selectivity, except those who must struggle with thick and hard partings and operate in seams less than 40 in. thick. It must be realized, then, that more than one type of continuous miner may be used advantageously in the same coal mine. Although this appears to violate the standardization generally sought after, the gain can more than offset added maintenance and, to a lesser degree, operating problems. It is equally important to realize that most coal mines will require one or more conventional loader setups in the plan of total mechanization. Seam variations, adverse physical conditions, and special designs of main headings for haulage and ventilation, to name only three reasons, may render 100 pct use of continuous miners uneconomical. Of course, this situation may change. In one mine, prior to 1954, machines that ripped coal from the face achieved only average results, as compared to the impressive performance of boring-type units in another coal mine. A boring-type unit was therefore selected for the first mine in the belief that the chance of success would be greater if it were used in a combined cutting and wedging operation, cutting a full face in its forward movement. The miner was located in a part of the mine where a special projection could be readily developed, a solid area scheduled for mining according to the overall progress plan. All openings surrounding the particular area were carefully investigated for the presence of sulfur balls. Fig. 1 (opposite) shows the representative seam section, containing the several pyritic bands 1/4 to 1/2 in. thick; a characteristic Pittsburgh seam parting averaging 5 to 6 in. of slate, coal, and slate; and the occasional py-rite lenses 2 to 3 in. thick. Under normal conventional mining methods, the top 10 or 12 in. and the bottom 4 in. are left in place to offer roof protection

Jan 1, 1958

CONTENTS PAGE HESSE, A. W,-Safeguarding Coal-mining Operations against Danger from Oil and Gas Wells. Discussed by A. W. Hesse, T. G. Fear, George H. Ashley, George S. Rice, W. E. Fohl, R. V. Norris, S. A. Taylor, F. B. Tough, C. W. Gibbs, A. Hurlburt, S. W. Meals 1 DAWSON, THOS. W.-Belt Conveying of Coal at H. C. Frick Coke Company Mines. Discussed by F. F. Jorgensen, Thos. W. Dawson, Graham Bright, A. W. Hesse 13 OTTO, HENRY H.-Ultimate Recovery from Anthracite Coal Beds. Discussed by R. V. Norris, S. A. Taylor, Henry H. Otto, Douglas Bunting, Graham Bright, Howard N. Eavenson, J. B. Warriner 15 HOSLER, Rush N.-Schedule Rating Coal Mines in Pennsylvania for Compensation Insurance Rates. Discussed by E. A. Holbrook, W. W. Adams 17 ARCHBALD, HUGH.-Application of Gaussian Curve to Mining Industry. Discussed by Donald A. Laird, T. T. Read 19 ASH, SIMON H.-System of Coal Mining in Western Washington. Discussed by Eli T. Conner, Simon H. Ash 21 MILLER, J. S.-Method of Mining a Steeply Pitching Anthracite Vein by Successive Skips. Discussed by Eli T. Conner, J. S. Miller, J. B. Warriner 22 HARRINGTON, GEORGE B.-New Orient, an Unusual Coal Mine. Discussed" by George S. Rice, Eli T. Conner, John A. Garcia, George B. Harrington, F. F. Jorgensen, Graham Bright, W. M. Hoen, George N. Simpson, W. C. Adams, R. W. McNeill, Chas. C. Whaley, Carl Scholz, E. T. Gott, Andrews Allen 23 PERROTT, G. ST. J.-Properties of Liquid-oxygen Explosives. Discussed by George S. Rice 48 Safeguarding Coal-mining Operations against Danger from Oil and Gas Wells Discussion of the paper of A. W. HESSE, presented at the New York Meeting, Feb-ruary, 1925, and issued, as Paper No. 1412-F, with MINING AND METALLURGY, February, 1925. A. W. HESSE.-The well under investigation, No. 101, Fig. 2, was started about Sept. 5, 1921, and drilled-in in November. The first hole was started with a 13-in. bit and reached the Pittsburgh coal at a depth of 563 ft.; at 602 ft. the 10-in. casing was run in and the well was continued with a 10-in. bit and 1400 ft. of 8-in. casing was put in. It was then continued to a depth of 1770 ft. and 6-in. casing put in; then continued to a depth of 2555 ft. where the gas was struck. As the well produced only about 100,000 cu. ft. per day. 2-in. tubing was used to conduct the

Jan 6, 1925

By Orlando Romig

PART I-PREPARATION OP METALLIC SINGLE CRYSTALS WITH ESPECIAL REFERENCE TO SINGLE CRYSTALS OP ZINC? As metals and alloys are composed, of, an aggregate of allotriomorphic crystals or grains, each possessing an individual orientation, the physical characteristics of a metal or an alloy are closely related to the properties of the individual crystals. The preparation and study of single metallic crystals are, therefore, matters of considerable importance. The advent of the X-ray spectrograph as a valuable metallurgical tool has magnified the importance of this subject, because the interpretation of some X-ray spectrographs is difficult unless single crystals are used in these studies. PREVIOUS WORK The first paper, as far as the writer knows, on the behavior or preparation of single crystals of metals is by Baker.1 He describes the behavior of extruded wires of sodium and potassium. These wires, when pulled in tension, instead of I showing the usual conical fracture common to most metals, had a chisel-shaped fracture when they were broken. I and II, Fig. 1, have a similar fracture. Baker checked his results by preparing single crystal wires from molten sodium and potassium and observing their properties. He prepared the wires by filling glass tubes, under oil, with the molten metal. The surfaces of the strained wires showed slip bands of remarkable clearness of which photographs are shown in his paper. He concluded that these wires were single crystals and "that the portions of the metal brought into play are cubes. Such cubes, when placed so that a plane through 'two opposite edges was parallel to the axis of the wire, would allow of lateral contraction by faces gliding over one another in one direction only and not in the direction at right angles."

Jan 1, 1927

By H. E. McKinstry

Movement on a fracture of irregular shape can cause local widening of the fissure and thereby offer freer channelways for circulation of ore-depositing solutions. This influence: coupled with large areas of wall rock available for reacting with ore solutions in brecciated and shattered ground can account for locally active deposition of metals and the resulting ore shoots. Such irregularities in the fracture system may be caused by local variations in the strength of rocks and by pre-existing lines of weakness, especially if these stand at favorable angles to certain components of the fracturing stress. Therefore correct interpretation of the mechanics of fracturing should permit deductions as to structurally favorable places on unexplored portions of the vein system. Introduction It has long been recognized that movement on a curved or irregular fault surface is capable of separating the walls in certain portions of the fault, but until very recent years the importance of this mechanism as a factor in localizing ore shoots has escaped proper recognition. A short time ago W. H. Newhouse' presented a careful analytical study of displacements and their corresponding open spaces. For reasons that will be discussed later, it frequently happens that portions of the vein which are favorably oriented are not merely wider but also richer than the average. In many cases the widening with its accompanying richness coincides with very minor changes in the dip or strike of the vein, irregularities that commonly escape notice unless the vein is mapped in detail and a careful geometrical analysis made. While the relationship between the width of the vein and the changes in dip or strike has been recognized as a matter of observation, the irregularities have been accepted as more or less the result of accident. There has been very little effort except in isolated cases to find out the causes of these changes in dip or strike. Yet it is clear that if the causes can be recognized and expressed in terms of geologic structure the geologist will know where to look for repetitions of these favorable conditions either on extensions of the same vein or on adjoining veins. Any lack of understanding of the causes is due to the limitations of our ability to interpret our observations and not to the sheer capriciousness of

Jan 1, 1941

By H. E. McKinstry

Movement on a fracture of irregular shape can cause local widening of the fissure and thereby offer freer channelways for circulation of ore-depositing solutions. This influence: coupled with large areas of wall rock available for reacting with ore solutions in brecciated and shattered ground can account for locally active deposition of metals and the resulting ore shoots. Such irregularities in the fracture system may be caused by local variations in the strength of rocks and by pre-existing lines of weakness, especially if these stand at favorable angles to certain components of the fracturing stress. Therefore correct interpretation of the mechanics of fracturing should permit deductions as to structurally favorable places on unexplored portions of the vein system. Introduction It has long been recognized that movement on a curved or irregular fault surface is capable of separating the walls in certain portions of the fault, but until very recent years the importance of this mechanism as a factor in localizing ore shoots has escaped proper recognition. A short time ago W. H. Newhouse' presented a careful analytical study of displacements and their corresponding open spaces. For reasons that will be discussed later, it frequently happens that portions of the vein which are favorably oriented are not merely wider but also richer than the average. In many cases the widening with its accompanying richness coincides with very minor changes in the dip or strike of the vein, irregularities that commonly escape notice unless the vein is mapped in detail and a careful geometrical analysis made. While the relationship between the width of the vein and the changes in dip or strike has been recognized as a matter of observation, the irregularities have been accepted as more or less the result of accident. There has been very little effort except in isolated cases to find out the causes of these changes in dip or strike. Yet it is clear that if the causes can be recognized and expressed in terms of geologic structure the geologist will know where to look for repetitions of these favorable conditions either on extensions of the same vein or on adjoining veins. Any lack of understanding of the causes is due to the limitations of our ability to interpret our observations and not to the sheer capriciousness of

Jan 1, 1941

By S. R. Goodman, Hsun Hu

A study has hem made of the formation of annealing textures in an 18-8 austenitic stainless steel (Type 304L) from various deformation textures obtained by rolling at different temperatures. When the deformation texture is a mixture of the ferritic type and the brass type owing to the pres -ence of both martensitic ferrite and retained aus-tenite in the specimen, recrystallization takes place by the growth of the existing austenite phase. In a previous report,' it was shown that the rolling texture of austenitic stainless steel (Type 304L) changed gradually from the brass type to the copper type with increasing temperature of deformation above 200°C. These changes are similar to those in high-purity silver2,3 and electrolytic copper;4 a brass-type texture is favored at low rolling temperatures, whereas a copper-type texture is favored During the course of rolling -texture transition from the brass type to the copper type, the subsequent recrystallization textures change accordingly. The orientation relationship between the annealing textures and the various rolling textures, being consistent with previous observations on various fcc metals, can be described as [Ill] rotations of approximately 25 to 40 deg. Carhide precipitation may influence the annealing textures. at high rolling temperatures. Furthermore, the annealing textures in high-purity silver5 and electrolytic copper4 were found to depend entirely on the prior deformation texture. From a copper-type rolling texture a strong cube texture will form upon recrystallization, whereas from a brass-type rolling texture the annealing texture will be quite different from the cube orientation. In an earlier comm~nication,6 the formation of a strong cube texture in 18-8 austenite stainless steels (Types 304 and 304L) was reported briefly by the authors. The present paper constitutes the results of a complete study of the annealing textures obtained from a

Jan 1, 1965

By Robert F. Mehl

THE solid solutions which aluminum forms with copper, and with magnesium and silicon, are not extensive, and accordingly could not be expected to form Widmanstätten figures profusely nor with great ease. A study of the Widmanstätten figures in these systems seemed desirable, however, because of the interest which these alloys bear towards age-hardening theories resulting from the necessary relationship between the age-hardening phenomena and the atomic processes leading to the formation of Widmanstätten figures.1 ALLOYS OF ALUMINUM WITH COPPER The most accurate determination f the solid solubility, of copper in aluminum seems to be that by Dix and Richardson,2 whose results are represented in Fig. 1. According to this work, aluminum dissolves 5.6 weight per cent of copper at 548°, and less than one per cent at room temperature. Judging from the constitutional diagram, this solid solution on cooling tends to precipitate the compound CuAl2, and this conclusion has been confirmed experimentally by Schmid and Wassermann .3

Jan 1, 1932