[Trans. No. Place Date Vol. Page 1. Wilkes-Barre, Pa.* May, '71.. 1 3 2. Bethlehem. Pa Aug., '71.. 1 10 8. Troy, N. Y Nov., '71.. 1 1S 4. Philadelphia, PaFeb., '72.. 117 5. New York, N. Y.*May: '78.. 120 5. Pittsburgh, PaOct., '72.. 125 7. Boston, MassFeb., '78.. 128 8. Philadelphia, Pa.* May, '78.. 2 3 9. Easton, POct., '78.. 27 10. New York. N. YFeb.. '74.. 2 11]

Jan 1, 1946

By G. P. Tiwari

Recrystallization and grain growth in thoria dispersed nickel and nichrome were recently studied by Webster as a function of temperature and deformation. The unexpected part of these results was that specimens which had received heavier deformation developed greater resistance to recrystallization. Retardation of recrystallization was accompanied by the formation of voids around thoria dispersion. To explain these results, Webster suggested that the formation of void around the particles increased the effective size of thoria particles. This resulted in greater impediment to the grain-boundary migration and as a consequence the recrystallization of the matrix is retarded. In the present note an alternative and more probable explanation for the effect of voids on recrystallization is presented. The exact mechanism of void formation in thoria dispersed nickel or nichrome is not known. However, it is reasonably certain that it must be preceded by the stress concentration in the matrix around thoria dispersion during the deformation.'' The resulting stress concentration must be sufficient enough to supply the surface energy for the new surfaces created. Further, the decrease in the strain energy of the matrix surrounding the potential void nucleus must be larger than the surface energy of the newly created surface. The release of strain energy due to formation of crack results in a strain free cylinder of the material around the voids.13 If the void formation is not localized, at few points only (as is the case here), this process may lead to considerable amount of release of strain energy of the matrix. The pattern of recrystallization behavior of single phase homogeneous matrix as well as the matrix having a second phase dispersion is same except for the fact recovery and recrystallization are more clearly delineated.14 In general, the recrystallization temperature is lowered (i.e., recrystallization is easier) with increase in the amount of cold work. This is due to the increase in stored energy in the matrix with increasing amount of deformation. If somehow there is a relaxation of strain energy in the matrix, the recrystallization should become difficult because of the decrease in the amount of stored energy available for recrystallization. Since the formation of voids leads to a decrease in the strain energy of matrix, the recrystallization of the matrix would be inhibited due to the formation of voids during deformation prior to recrystallization. It has been observed by earlier workers15'16 that the presence of preexisting voids in a matrix retards the recrystallization. The essential issue here is how do the voids act to produce this effect. If the voids influence recrystallization only by blocking the grain boundary migration, then the effect should be maximum when they are present almost exclusively along grain boundary. These conditions are obtained during high temperature deformation. However, the voids produced due to creep along grain boundary are not able to prevent recrystallization17 suggesting that they are not effective in blocking grain boundary movement. Recently it was shown by Davies and Williams that the voids can act as sinks for vacancies." As a result the processes dependent on vacancy diffusion like recovery, recrystallization, dislocation climb, and so forth, will be hindered. This fact may be responsible for inhibition of recrystallization during subsequent deformation and annealing cycles. It is to be noted here that there is a large difference between the density of voids in creep experiments and the other experiments where retarding effect of voids on recrystallization is seen. The voids in former may number up to l04 to l05 per sq cm whereas in latter cases the voids density is typically around 1010 to 1013 per sq cm. It appears that the decrease in supply of vacancies in creep is insufficient to adversely affect the recrystallization due to low void population. The author is grateful to P. Das Gupta and S. P. Ray for helpful discussions. Author's Reply D. Webster Tiwari appears to have misunderstood the nature of grain boundary-particle interactions. Tiwari (quoting Cahn) states that second phase particles become more effective as they become smaller, therefore as the voids in TDNiC make the thoria particles effectively bigger their ability to resist grain boundary movement is impaired. This particle size argument was originally proposed in the form of an equation by Zener 20 years agol9 and is not necessarily valid as is discussed below. However, assuming it is valid, it predicts a greater boundary restraining effect by smaller particles simply because their combined cross sectional area is greater at a constant volume. If the number of particles remains the same and their effective size increases, as in the present case, Zener's equation predicts a greatly reduced grain size. This is because the effect

Jan 1, 1970

[Alphabetic Section: The letter immediately following a member's name indicates grade: M-member, A-associate, J-junior. The numerals following member's grade indicate year of election. The letter following year of election indicates primary divisional affiliation: A. Mining & Exploration F. Coal B. Minerals Beneficiation G. Petroleum C. Iron and Steel H. Industrial Minerals D. Extractive Metallurgy J. Council of Education E. Institute of Metals K. Council of Economics Geographic Section: An asterisk (*) preceding a member's name indicates availability for consulting work:]

Jan 1, 1961

PRESIDENT AND DIRECTOR EUGENE MCAULIFFE OMAHA, NEBR. PAST PRESIDENTS AND DIRECTORS HERBERT G. MOULTON NEW YORK, N. Y. JOHN R. SUMAN HOUSTON, TEXAS TREASURER AND DIRECTOR H. T. HAMILTON NEW YORK, N. Y. VICE PRESIDENTS AND DIRECTORS ERLE V. DAVELER NEW YORK, N. Y. W. M. PEIRCE PALMERTON, PA. PAUL D. MERICA NEW YORK. N. Y. LEROY SALSICH DULUTH, MINN. CHESTER A. FULTON NEW YORK, N. Y. L. E. YOUNG PITTSBURGH, PA.

Jan 1, 1942

As one surveys the extensive taconite operations on the Mesabi Range, he may find it difficult to believe that only 15 years ago, the iron ore mining industry here was staring at its own imminent demise. Due to the high demands for iron ore during World War II the postwar period of 1946-1950, and the subsequent "police action" in Korea, there was rapid consumption of the Mesabi's already depleted ores, and some economists were giving the Range only 20-25 years of life. In the 13-year period 1941-1953, more than 850 million tons of iron ore were shipped to steel mills, an amount almost equal to the total production during the preceding 30 years. Proven ore reserves dropped from 1.1 billion tons in 1940 to 8.3 million tons in 1954, the largest decrease being recorded in the famed direct shipping ores.

Jan 9, 1968

By James Douglas

The Copper Queen mine was opened in 1880 by Messrs. Martin, Ballard & Reilly, and the first copper-furnace was blown-in on August 20th of that year. Prior to that summer nothing but prospect-work had been done on the copper Queen and on a number of adjacent claims. In fact, it was a small deposit, not of copper-ore, but of cerussite, which still remains undeveloped, on the western slope of the Queen hill, which

Jan 1, 1900

Arizona Bureau of Mines and College of Mines and Engineering, University of Arizona, Tucson, Ariz. Lists of the maps and bulletins available will be sent upon request to G M Butler, Director, Arizona Bureau of Mines, Tucson, Ariz Bulletin 119, A resume of the geology of Arizona, by N. H Darton, is sold for $1, postpaid Fourteen other bulletins, any five of which may be had free of charge (additional numbers may be purchased for 10 cents each) are available as follows - 106, A geological reconnaissance of the Tucson and Amole Mountains, by Olaf P Jenkins and Eldred D Wilson, 114, Fluorspar, by M A Allen and G M Butler, 120, Gold and copper deposits near Payson, Arizona, by Carl Lausen and Eldred D Wilson, 122, Quicksilver resources of Arizona, by Carl Lausen and E D. Gardner, 123, Geology and ore deposits of the Courtland?Gleeson region, Arizona, by Eldred D Wilson; 125, The mineral industries of Arizona, by J B Tenney, 126, Asbestos deposits of

Jan 1, 1933

By K. S. Krishnam, A. G. Guy

VOLUME 6 of the Transactions of the Baikov Institute of Metallurgy, Moscow, is devoted to the subject of "the experimental and theoretical study of the physical characteristics of dilute solid solutions,11 and summarizes work that has been done largely in the years 1958-9. In view of the attention that Soviet investigators have given to this subject, it seemed useful to carry out an independent experimental investigation in an effort to judge the scientific basis and practical significance of this field of study. The present note is a preliminary report of this investigation. The first property studied by the Soviet group was X-ray spectra of solid-solution alloys.' An anomaly observed at low concentrations (--0.05 at. pct) of the alloying element led to the theory that each impurity atom in a transition-metal base alloy is the center of a "block" of affected atoms with a radius of about 10"7 cm. This theory was further developed in a later paper.2 By this time similar anomalies had been found in diffusion coefficients3 and in thermal expansion.4 The entire development up to 1959 was reviewed in a comprehensive paper, and further theoretical ideas were also published at this time. Finally, the volume mentioned above was published in 19607 giving new experimental data on anomalies in optical properties and Hall constant, and a new theoretical treatment also appeared.' Although western scientists have done both theoretical work, summarized recently by Friedel,9 and considerable experimental work on dilute solid solutions, there is little support for the marked anomalies reported in the Soviet papers. Of the physical properties studied by the Soviet investigators, thermal expansion was chosen for the present investigation because of the relative ease of obtaining the necessary precision of measurement. A Leitz dilatometer was used for this purpose, and a special technique involving interchanging of the two specimens being compared permitted a precision of 0.05 x X in average thermal expansion over the range 27° to 600°C. The specimens were heated and cooled in vacuum or in a protective atmosphere at a rate of 50 °C per hr. Ferrovac E iron was used as the comparison specimen and in every case had a coefficient of expansion higher than (or equal to) that of the alloy. Since unintentional impurities are an important factor in studies of dilute alloys, special attention was given to the purity of the iron and the alloys used. The alloys were the same of those used by Abrahamson10 and by Michalak," and their preparation is described in these references. Chemical analyses of the Ferrovac E iron and of typical Fe-W and Fe-Mo alloys are given in Table I. The purity of the iron and alloys is undoubtedly higher than in the

Jan 1, 1962

By S. E. Bronisz, Dana L. Douglass

a Uranium was deformed by cold rolling, and the effects of this plustic deformation on the microstruc-ture of the metal were observed by the technique of transmission elecbon microscopy. The recrystalli-zation of selected cold-wmked samples was also studied by this method. The samples were prepared for examination by electrolytic thinning in a standard metallographic electrolyte which has not been previously reported as being used in producing thin foils of uranium. The microstructural changes observed in the a uranium were generally similar to those seen by optical microscopy. The changes in the microstructure of a uranium following cold work and recrystallization treatments have been the subjects of several studies employing optical and X-ray techniques.12-19 These studies indicated that twinning was the redominant mode of deformation at room temperature20 and that the regions of high energy associated with the deformation twins were preferred sites for the initiation of recrystallization.15,18, Recently several workers have prepared thin foils of uranium suitable for examination by transmission electron microscopy.'-lo The foils thus prepared have been used to study fission fragment damage; a particular dislocation reaction,' and gas precipitation." At this laboratory the microstructural changes occurring during the cold working and recrystallizing of a uranium samples have been studied by using transmission electron-microscopy techniques. The foils used in this work were electrolytically thinned in a polishing bath not reported previously in the literature as being used for this purpose. EXPERIMENTAL PROCEDURE The uranium used in this investigation was depleted a uranium sheet 4 mils thick. The results of a spectrochemical analysis of this material are shown in Table I. The as-received uranium was cut into strips, 1 in. wide by 5 in. long, and annealed in vacuo at 600°C for 2-1/2 hr. The resulting microstructure consisted of relatively uniform, equiaxed grains having diameters of 10 to 50 p. Cold Working. The cold-worked samples were prepared by rolling several of the annealed uranium strips to various thicknesses. The strips were reduced 3.5 ± 0.5, 6.0 ± 0.6, 10.0 ± 0.5, 19.5 ± 1.0, and 28.5 ± 2.0 pct in thickness. It was not possible to achieve these reductions with a single pass through the rolling mill, so the strips were turned end for end during the rolling procedure. The cold-rolled strips were stored in dry ice until samples from them could be thinned and examined (within 24 hr after rolling). Annealing. The samples used in studying the re-crystallization behavior of a uranium were obtained by annealing sections of the strips which had been reduced 10.0 and 28.5 pct. These samples were sealed in evacuated Pyrex capsules and were annealed in a tube furnace at temperatures from 200" to 600°C and for times from 1/2 to 2 hr, see Table l. Thinning: The samples from the rolling and heat treatments were prepared for examination in the electron microscope by electropolishing in a bath composed of 25 g chromic acid, 133 ml glacial acetic acid, and 25 ml water. This electrolyte has been used and recommended for preparing specimens for optical metallography It was necessary to mask the edges of the sample with a stop-off paint in order to prevent preferential attack in these areas. The paint used was made by dissolving polystyrene in benzene. The electrolytic cell consisted of a cylindrical stainless-steel cathode placed in a beaker containing the electrolyte, with the sample as the anode positioned at the cell axis. The temperature of the electrolyte was held below 15°C by cooling with liquid

Jan 1, 1963

By Salim Akhtar

The operation of a mineral processing plant with a complex flowsheet is represented by a mathematical operator. Such a representation permits a quantitative evaluation and monitoring of the separation processes in different sections of a processing plant, and gives an overall separation efficiency of the plant.

Jan 1, 1975

By D. J. MacKinnon, J. M. Brannen

Smooth, compact, dendrite free 24-h zinc deposits have been electrowon from zinc chloride electrolyte using a diaphragm cell. The cell consisted of sealed anode compartments containing DSA anodes separated from an open cathode compartment by Dynel cloth membranes. Fresh electrolyte was fed to the cathode compartment where zinc deposition onto an aluminum cathode was aided by air sparging. The catholyte passed through the diaphragms into the anode compartments from which chlorine gas and spent anolyte were withdrawn. Standard electrolysis conditions were: 15 g/L Zn, 0.12 M HCI, I5 mg/L tetrabutylammonium chloride (TBACI) as the addition agent, 35°C, and 323 A/m2 (30 ASF) current density. The effect of variations in these conditions on the morpohology orientation, current efficiency, and energy requirement for 24-h zinc deposits was determined. The effect of total chloride ion concentration on the zinc deposit was studied by adding various amounts of NaCl to the electrolyte.

Jan 1, 1983

By William H. Emmons

Jan 1, 1912

[ ]

Jan 1, 1946

[Trans. No. Place Date Vol. Page 1. Wilkes-Barre, Pa.*...May, '71.. 1 3 2. Bethlehem, Pa Aug., '71.. 1 10 3. Troy, N. Y Nov., '71, , 1 13 4. Phildelphia, Pa Feb., '72.. 1 17 5. New York, N. Y. May, '72 120 6. Pittsburgh, Pa Oct., 7. Boston, Mass Feb., '73.. 1 28 8. Philadelphia, Pa.* ... May, '73.. 2 3 9. Easton, Pa Oct., '73.. 2 7 10. New York, N. Y Feb., '74.. 2 11 11. St. Louis, Mo.* May, '74.. 3 3 12. Hazleton, Pa Oct., '74.. 3 8 13. New Haven, Conn.... Feb., '75.. 3 15]

Jan 1, 1940

By J. Chipman, J. C. Fulton

Reduction of silicon from blast-furnace-type slags by carbon-saturated iron is a very slow reaction even under conditions of rapid stirring. Equilibrium under atmospheric pressure of carbon monoxide was approached from both sides, and the silica-silicon relation was established at temperatures of 1425º to 1700°C for slags containing up to 20 pct Al2O3. Silicon carbide is formed by reaction of graphite with high silica slags and the conditions for its formation were determined. Activities of SiO2 and of CaO in their binary solutions at 1600°C were determined. The effects on the activity of SiO2 were established for additions of 10 to 20 pct AI2O3 and of 10 pct MgO. STUDIES of chemical reactions between blast-*>-5 furnace slags and metal have been focussed on the transfer of sulphur from metal to slag. The important role which silica reduction plays in this process' has led to a study of the transfer of silicon from slag to metal and the equilibrium represented by the equation SiO2 (in slag) + 2C (graphite) = Si + 2CO (g). [I.] The authors2 have published an account of the experimental method employed in attacking this problem and of three series of experimental results at 1600°C. This paper contains data on some additional compositions and extends the observations to cover the temperature range 1425° to 1700°C. The data are used to determine the activity of silica in the slags. As in the earlier experiments, the atmosphere was carbon monoxide which flowed through the furnace at 150 ml per min. In certain heats designated in the tables and figures, the gas was bubbled through the melt using a graphite tube. The latter increased in porosity during a run and in some cases bubbling ceased as indicated by cessation of surging. Some results were discarded for this reason. Experimental Results The new data are shown in Tables I through V and both old and new data are plotted in Figs. 1

Jan 1, 1955

By A. U. Seybolt, J. L. Walter

The effects of the addition of 0.5 pct ThO2 (by volume) on the grain structure and texture of heavily rolled tungsten sheet were studied. Powder metallurgy ingots were rolled to sheet, 0.001 in. thick, and samples were annealed at temperatures from 1200" to 2500°C. The heating rate to the anneal temperature was varied from 3°C per min to 6500°C per min. The orientations of the largest grains were determined by X-ray diffraction. The disposition and loss of the ThO2 particles were determined by electron transmission microscopy and the activation energy for remozlal of the thorium was measured by mass spec-troscopy. Heating rates below about 800 C per min produced large, highly elongated grains. Higher heating rates produced much smaller, less elongated grains. The grain structure and texture of the slowly heated samples were identical to the structures and textures of heavily rolled tungsten foil conventionally doped with aluminum, silicon, and potassium but the recrystallization temperature was about 200°C lower. There was stringer-like dispersion of larger ThO2, particles superimposed on a uniform dispersion of fine particles. The particles increased in size and decreased in number with time at temperature. The loss of particles was accompanied by formation of grain boundary voids and surface pits. The activation energy for removal of the ThO2 was about 40 kcal per mole. THE addition of small amounts of aluminum, silicon, and potassium to tungsten has a profound effect on the grain structure of heavily rolled sheet1 or drawn wire."4 Thus, "doped" tungsten sheet, rolled to 0.001 in. and recrystallized, develops a structure consisting of large, highly elongated grains of a specific preferred orientation.' It has been shown that the elongated grain structure was caused by a dispersion of particles, identified as mullite (Al6si2O13),1,4 in strings parallel to the rolling direction in sheet or to the wire axis. Identical results were obtained for iron which was doped with glass and rolled to 99 pct reduction of thickness and recrystallized.5 Again, the glass particles were disposed in strings parallel to the rolling direction. The strings retarded boundary migration in the lateral direction but grain growth was able to proceed relatively unhindered along the direction parallel to the strings.1,5 In both the doped tungsten and the glass-doped iron, the particles were highly plastic during the high-temperature deformation. Since mullite melts at about 1800°C and the glass employed melts at about 810ºC, the particles were probably molten during the recrystallization anneals (above 1800°C for the doped tungsten and 850°C for the glass-doped iron). There are indications in the literature that particles not plastic at hot-working temperatures (up to about 1550°C for tungsten) may also impart elongated grain structures by primary recrystallization of worked alloys. Examples are dispersions of tantalum carbide in chromium,6 and ThO2 in nickel where elongation ratios of recrystallization grains of up to 20:l were obtained.7 Strings of ThO2 particles in W-ThO2 wire have been seen by Rieck.8 In view of the available evidence, it was of interest to extend the previous studies of doped tungsten and glass-doped iron to include W-ThO2 sheet materials. Of specific interest was the grain structure, preferred orientation, recrystallization temperature, and disposition of the thoria particles. EXPERIMENTAL PROCEDURE A) Material Preparation. About 380 g of blue tungsten oxide (approximate composition WO3) was wet with a sufficient amount of aqueous solution of Th(N03)4 to provide 0.5 vol pct ThO2. The wet mixture was stirred to distribute the doping material uniformly throughout the powder. Stirring was continued while the mixture was heated until it was completely dry. The dried, doped mixture was then reduced to tungsten powder by heating at 850°C for 2 hr in a stream of dry hydrogen. The doped tungsten powder was hydropressed in a rubber sack at pressures of 50,000 psi to produce an ingot approximately 2 cm diam by about 5 cm long. Next, the pressed cylinder was heated in hydrogen for 2 hr at 1350°C to render it strong enough for machining. The cylinder was machined to a square cross section of 1.6 by 1.6 cm with rounded corners. Finally, the bar was heated for 2 hr at 2150°C in hydrogen to provide a sufficiently dense mate rial to withstand the hot-rolling operation. Prior to rolling, the ingot was reduced in thickness by about 20 pct by forging at 1550°C. This served to increase the density of the material and to widen it slightly for better rolling characteristics. The forged ingot was then rolled at 1550°C to a reduction of 45 pct of thickness, following which the rolling temperature was reduced to 1300°C and the slab rolled, with several reheats, to 0.050 in. Further reduction was accomplished at 800°C in tungsten sheet packs to a total reduction of about 99.85 pct. B) Annealing Treatment and Observation of Structure. Small samples of the rolled foil were annealed in one of two ways. Some of the samples were suspended in a covered tungsten can and annealed at temperatures from 1200" to 2200°C for various times in vacuum of l0-7 to 10-6 mm Hg. The can was heated by induction and temperatures were determined by optical pyrometry

Jan 1, 1970

By AIME AIME

MEXICO embraces one of the great metal and petroleum producing provinces of the world. In this respect its history dates back to the overthrow of the Aztec empire by a Spanish force under Hernando Cortes between 1519 and 1.521. Even before then, its richness in silver and other minerals was not unknown. But it was a treasure house for the Spanish conquerors until the country became independent in 1821. It has been computed that in the 400 years following 1521, Mexico yielded 1.55,000 metric tons of silver, worth $3,000,000,000, two-thirds of the entire world production. In 1935 the country accounted for 36 per cent of the world's silver output, 14 per cent of its antimony (in 1934), 13 per cent of its lead, 3 per cent of its zinc and copper, and 21/2 per cent of its petroleum. Contrary to the impression of some, its gold output is now comparatively small, though important in the past. Its oil, as well, formerly hulked much larger than now, in 1921 being one-fourth of the world output.

Jan 1, 1936

By H. I. Smith

The technical and safety press have devoted much space in support of or in opposition to the use of booster and auxiliary fans in coal mines. The Mine Safety Board of the U. S. Bureau of Mines has given the matter consideration, and the Mine Ventilation Committee of the A. I. M. E. is now seeking a discussion of the merits and demerits of such fans to guide it in formulating recommendations. In this paper I will set up some principles on which I believe most engineers will agree and from which we may work toward a decision, though as to what that decision shall be there may be a difference in opinion. Before stating the points on which I believe there is accord, I will distinguish between booster and auxiliary fans. Definition of Booster and Auxiliary Fans In discussing underground fans G. S. Rice1 distinguishes between those used to increase the amount of air passing a given point and those used to augment the ventilation locally. He describes a booster fan as one which is installed to handle the entire air current passing a given

Jan 1, 1927

NEW MEMBERS The following list comprises the names of those persons who became members during the period Dec. 10, 1915 to Jan. 10, 1916. ANDERSON, FRANK BASIL, Min. Engr., Sampler, Copper Queen Cons. Min. Co., Bisbee, Ariz. BAILEY, LEWIS NEWTON, Min. -Engr 4227 St. James Place, Sail Diego, Cal. BELL, JAMES E., Min. Engr., Care Chile Exploration Co., Chuquicamata, Chile, South America. BONILLAS, YGNACIO SAFFORD, Min. Geol., Copper Queen Cons. Min. Co., Bisbee, Ariz. BRADLEY, GEORGE OLIVER, Mech. Engr Hobart Bldg., San Francisco, Cal. CLARK, GEORGE L., Min. Engr Vipond Mine, Schumacher, Ont., Canada. CONKLING, RICHARD A., Geol., Roxana Petroleum Co. of Oklahoma, Tulsa, Okla. GOHRING, W. B.. Geol., Supt. of Mines, Calumet and Arizona Min. Co., Warren, Ariz.

Jan 2, 1916

By I. Iwasaki, K. Adam

During wet grinding the electrochemical interactions between grinding media and pyrrhotite not only accelerate media wear but also adversely affect the suede mineral's flotation response. A possible remedy of the adverse effects on floatability by applying electric potentials to grinding media was examined. Flotation tests, Auger electron spectroscopy, and X-ray photoelectron spectroscopy were used to study pyrrhotite surface properties. Although anodic polarization of the steels increased metal loss by corrosion, pyrrhotite flotation recovery was increased. In the case of cathodic polarization, flotation recovery improved somewhat in a narrow range of overpotentials. At higher cathodic overpotentials, however, mineral floatability was progressively lowered although the corrosive wear of grinding media might be reduced.

Jan 1, 1985