By J. E. Lawver, J. L. Wright, H. R. Kokat

Mesabi semitaconite and oxidized taconite ores that cannot be concentrated by froth flotation can be rendered amenable to flotation through partial concentration in a high-in tensity wet magnetic separator. Since 1964, a method for accomplishing this precon-centration has been under development at the Minnesota Mines Experiment Station, where several hundred tons of ore have been successfully processed. This paper is an analysis of the performance of the separators used at the Station. At present the United States is producing about 85 million tons of iron ore a year, and nearly 55 million tons of this comes from Minnesota. Nearly half of Minnesota's production is in the form of magnetite taconite pellets —the remainder being wash ore and gravity concentrates. As the demands of the blast furnace operators become more stringent - and they are becoming more so yearly — these demands are met by improved iron ore beneficiation technology. Furthermore, there is no doubt that as magnetite taconite, gravity ores, and wash ores are exhausted, new processes will be developed to produce a product comparable to magnetite taconite pellets from Minnesota's vast reserves of oxidized taconite and semitaconite. The magnetite taconite ores are rather easily bene-ficiated by conventional, low-intensity (500- to 1400-gauss) magnetic separators, followed, in some plants, by froth flotation of the magnetic concentrates.

Jan 1, 1969

By Gregoire Gutzeit

THE development reported in this paper was begun by the author a number of years ago, while he was a lecturer on complex chemistry and metallurgy at the University of Geneva, Switzerland, and in charge of that institution's research laboratory. Completion of the development and reduction to practice did not occur until last year at the Westport mill, laboratories and testing plant of the Dorr Company, where this method is now in general use for identifying and localizing the mineral constituents of both metallic and nonmetallic ores. It has proved to be a practical tool of the metallurgical staff at the Westport mill, devising unusual milling flowsheets for complex and refractory ore bodies. In a number of instances the findings have been successfully used as fundamental factors in the design and specification of complete metallurgical plants. Seven examples of the use of this method in solving practical milling problems are included in this paper. GENERAL OUTLINE The microscopic study of an ore, at first only of scientific interest, has proved extremely useful both in practical geology and in ore dressing. The binocular magnifying lenses for rough observation of the products of an ore-dressing plant have been in use for a long time; but only within the last few years has a systematic microscopical examination of ore samples become a normal tool of any research laboratory dealing with ore-dressing problems. Such an investigation avoids considerable loss of time as well as empirical trials and useless experimentation. It will generally indicate the correct grinding and often will suggest the proper method of treatment. The petrographic determination of transparent minerals in thin sections, or even in grains, has been perfected, and very accurate methods have been devised to meet any requirement, such as Feodorof's rotating stage on the petrographic microscope. Almost all transparent minerals can be positively identified by their optical properties; i.e., isotropism, anisotropism, color, pleochroism, refractory index, cleavage, crystal form, birefringence, and others. The identification of opaque minerals is a much more difficult problem and can be done only by using polished specimens. Unfortunately, most of the valuable metallic ores, and even some of the nonmetallic ones, are not transparent; therefore it has been necessary to develop a special technique for the determination of these minerals. Some optical properties-for instance, isotropism, anisotropism, color, cleavage, reflecting power-are often adequate in roughly classifying the mineral. Only "reflecting power" is a measurable value, provided special photometric equipment (ocular photometer or Orcel's photoelectric cell) is available. The other optical properties mentioned are more or less relative,

Jan 1, 1942

By D. Hnrrington

THE Dust Symposium was attended by approximately 100 persons, nearly all of whom remained from the starting hour (2 p. m.) until the use of the auditorium was demanded for another meeting at 5:30 p. in. In calling the meeting to order, D. Harrington made a few remarks as to the importance of the health dust problem in mining as well as in general industry and expressed gratification that the subject is now out in the open and that mining people are desirous of ascertaining the facts. B. F. Tillson acted as chairman of the meeting. The milling executive who desires to know what to do to prevent his workers from being unduly exposed to the dust hazard can get much out of the paper by D. E. Cummings, who has been doing much work in mines trying to keep -the dust in the air within safe limits. His recommendations indicate that the main protection of the worker in mines is by adequate ventilation, supplemented by the extensive use of water in drilling, as well as in water curtaining to condition air both in regard to dust content and to temperatures. Blasting was shown to be one of the chief causes for dust and it was recommended that whenever feasible all blasting should be delayed to the end of the working shift.

Jan 1, 1935

By J. S. Kirkaldy, W. V. Youdelis

THE occurrence of concentration distributions in rapidly cooled castings with gradients of opposite sign to those expected on the basis of the constitution diagram and diffusion controlled kinetics, has long interested metallurgists. The work on inverse segregation to 1937 has been adequately reviewed by Vaughan, and to 1949 by ell-walpole. The general conclusion for unidirectional solidification, that the enrichment of the initially solidifying regions with lower melting point compositions is due to the flow-back along interdendritic channels of normally segregated residual liquid, has a very sound experimental basis. Perhaps the best experimental work and the most complete qualitative description of the process has been given by Adams.3 The authors accordingly assume the reader's understanding of the content of this paper. It appears that one of the principal deterrents to the complete understanding of the process has been the lack of an analytical description. Although a number of workers including Masing,4-6 Sauerwald,7 and Adams3 have attempted quantitative predictions,

Jan 1, 1959

By A. G. Metcalfe

THE failure to detect any change in the thermal properties of cobalt at the Curie point would appear to indicate that the apparatus may have a limited sensitivity. The Curie temperature has been determined by direct methods to be 1121+3°CP and 1131°C.3 The specific heat has been determined many times'.' and weighted values are given in Table I. The allotropic transformations in iron and titanium, used by the authors to test the experiment method, involved a volume change of the order of 3 pct on going from the close-packed to the body-centered-cubic lattice. These energy changes are likely to be much larger than those involved in a diffusionless transformation from a hexagonal to a cubic-close-packed lattice. However, it has been pointed out that thermal observations are unreliable in the detection of phase changes when these are near a Curie point.' James 0. McCaldin and Pol Duwez (authors' reply)—The sensitivity of the present technique is limited to first-order transformations, so that gradual changes in specific heat, e.g., in the vicinity of Curie points, are not detected. Furthermore, the existence of first-order transformations with latent heats much smaller than those occurring in the known allotropic transformations of iron and titanium is, we agree, still pending.

Jan 1, 1956

By G. R. Lehman

The Inspiration Consolidated Copper Co. had an orebody at Miami, Ariz., of close to 100,000,000 tons of low-grade copper ore, and the method of mining this ore most profitably was of great importance. The selection of a method was practically limited to a "top-slicing," a "shrinkage-stope" or a "caving" method. The "top-slicing" method would give a high extraction of the developed ore, at a high mining cost, and the "shrinkage-stope" or "caving" methods a lower extraction of the developed ore, at a lower mining cost. Ore-Drawing Tests To decide on the method to be used it was necessary to know about what extraction of the ore could be obtained by the "shrinkage-stope" or " caving " methods. As no definite information regarding the,question was available at the time, C. E. Mills, the general manager, thought that some information could be obtained by experimenting in drawing ore, covered with capping, from an experimental box. Some work had already been done along these lines by W. C. Browning for the Inspiration Copper Co. and by myself for the Live Oak Development Co. The idea was to represent as nearly as possible, in the experimental box, the conditions within an area of caved stopes of caved ore all ready for drawing. That is, the area was supposed to represent a semibroken mass with the capping above it in the same condition and ready to follow the ore downward as it was drawn out of the chutes under the ore. To represent the above condition, in the experimental box, crushed ore from the mine was placed in it to a given height, and red barren capping from the mine was placed on top of the ore. The Experimental Box The experimental box shown in Fig. 1 was made of wood and glass. The glass was used for the sides so that the drawing action of the outside row of chutes could be seen and noted, the latter being cut in the center by the glass sides. The length of the box was 30 in., width 20 in. and the

Jan 1, 1917

By J. O. Betterton, W. K. Noyce

I~JTI HE work on the indium-zirconium system is part A of a larger investigation of zirconium-phase diagrams with solute elements, silver, cadmium, indium, tin, and antimony, which is intended to provide information about the metallic valency of zirconium. The system is an ideal example since the sizes of indium and zirconium atoms are nearly the same, and the solute and the solvent occur in the same row of the periodic table. The only solute from Group III B which had previously been added to zirconium was aluminum' and it was of interest to determine whether indium would dissolve appreciably in alpha zirconium and stabilize this phase in the same manner. Experimental Procedure The experimental methods used in the indium-zirconium work are similar to those described earlier for the silver-zirconium system.' Reactor Grade 1 iodide zirconium of 99.95 pct purity* and indium of 99.99 pct purity were arc cast, and then annealed in silica capsules with protective foils of zirconium and molybdenum. Annealing temperatures and times varied from 1 day at 1300°C to 43 days at 550°C. The compositions of the alloys were detcrmined by an individual chemical analysis of the actual metallographic specimens after two or more sides were examined to insure the absence of solute segregation. Calibrated thermocouples were used throughout, and the uncertainty in the temperatures reported, owing to calibration error, furnace control, and measurement of the small temperature gradients near the capsules, is believed to be well within ±2°C. Typical impurities in the alloys were found by a neutron-activation analysis of four different alloys. The results are given in Table I where the ranges of values will be seen to compare favorably with the usual values for iodide zirconium. With respect to oxygen, nitrogen, and carbon the absence of any unusual amount of these elements compared to iodide zirconium was indicated by the alloy hardness values, since hardness is increased sharply by the presence of these elements. The value for 0 pct In, obtained from the alloys by extrapolation, is 58 2 7 VPN which is in the low part3 f the normal range of hardness found in iodide zirconium. Results of the Experiments The zirconium-rich portion of the indium-zirconium phase diagram from the annealing experiments is shown in Fig. 1. Indium was found to

Jan 1, 1959

By H. S. Price, J. E. Warren

Techniques for studying the performance characteristics of heterogeneous reservoirs have been developed. The effect of permeability variation on both the steady-state and the transient flow of a single fluid has been investigated. Limited comparisons with field and laboratory data have been made. The physical models studied consist of random three-dimensional arrays of homogeneous porous blocks. The permeabilities of the individual elements are assigned according to a specific distribution function; uniform anisotropy is introduced by varying the relative dimensions of the blocks. A particular model is perturbed simply by re-arranging its elements at random. The behavior of a physical model is determined by digitally solving its numerical analogue. Based on computational experiments, subject to the restrictions implied by the assumptions that were made, the following general conclusions have been drawn. 1. The most probable behavior of a heterogeneous system approaches that of a homogeneous system with a permeability equal to the geometric mean of the individual permeabilities. 2. The effects of flow geometry and anisotropy on the most probable value of the effective permeability of a heterogeneous medium are finite but not significant. 3. The permeability determined from a pressure build-up curve lor a heterogeneous reservoir gives a reasonable value for the effective permeability of the drainage area. 4. A qualitative measure of the degree of heterogeneity and its spatial configuration are obtained from a comparative study of core analysis and pressure build-up data. It has been indicated that these conclusions are predicated on the assumption that the core analysis and the pressure build-up data represent true reservoir characteristics. Common sources of error in these data have been discussed. One of the most significant problems of reservoir engineering is that of determining the nature and the disposition of the heterogeneities that inevitably occur in petroliferous formations. It is with this problem that this paper is concerned. Extensive research, both theoretical and experimental, has provided reasonable descriptions of the physical processes that are associated with primary and secondaryrecovery mechanisms. Similar progress in the fie1d of numerical analysis and the evolution of truly high-speed digital computers have made it feasible to calculate the behavior of these mechanisms under almost any environmental conditions. It appears to be logical, then, to conclude that the mechanistic performance of any reservoir can be predicted with some confidence. Unfortunate1y, a necessary condition for the validity of this conclusion is that the formation be adequately described in a macroscopic sense. This condition cannot be satisfied ill general; therefore, a frustrating situation currently exists — it is possible to compute the effect of reservoir heterogeneity on behavior, but it is not possible to specify the heterogeneity itself. In many cases, the predicted behavior of a project is so completely dominated by irregularities in the formation's physical properties that the gratuitous assumptior, of a particular form for the variation can reduce the solution of the problem to a mere tautological exercise. While all porous media are microscopically heterogeneous, only macroscopic fluctuations need be considered since the fundamental concepts of reservoir mechanics are based on macroscopic quantities. For the simplest case in which only one physical property varies from point to point, the degree of heterogeneity that is apparent depends on three distinct factors, i.e., the nature of the property's variation (frequency distribution), its disposition (spatial distribution) and the inherent stability of the mechanism being studied. Consequently, any attempt to devise an unambiguous scale of heterogeneity must take these factors into account. Since this investigation is intended to be exploratory, it will be restricted to single-phase flow because of the simplification implied; both steady-state and unsteady-state behavior will be considered. Furthermore, to keep the number of parameters

By Friedrich Wellmer

INTRODUCTION The Ramsbeck Pb/Zn Mine is located in the northern Sauerland area of West Germany, 150 km N of Frankfurt and 120 km E of Cologne. This is a vein deposit which has been worked from the middle of the 19th century to 1974. About 15 million tons of ore were mined and milled. The ore district contains several vein deposits and is roughly 14 km in length and 4 to 5 km in width. The host rocks are strata of Lower Middle Devonian age. The strata strike 60° to 70° NE and where overturned have a dip steeper than the veins (Fig. 1). The galena-sphalerite mineralization is in quartz veins, which are mineralized where they cut the "Main Ramsbeck Quartzite" horizon, a very competent host rock. Vein structures strike at 65º to 75º, dip about 20° to 25º SE and cut the quartzite at approximately 60 m intervals. The main or "steep veins" within each vein structure dip at 10º to 80° SE with an average of 30° and are offset by thrust faults dipping 5º N to 40° S with an average of 5º S. "Flat veins" usually weakly mineralized occur in the thrust faults between the "steep veins", thus forming the overall step-like vein structure. The mineralization is very irregular and changes a- long strike and down dip. It consists of thin veins of pure sphalerite and galena with quartz and pyrite. The thicknesses of the pure sphalerite and galena veins

Jan 1, 1977

Paralleling recent experiments in the U. S., the Mines Branch of the Department of Mines and Technical Surveys in Ottawa has developed a laboratory process for recovering cell-grade alumina from aluminiferous shale. Mines Branch Research Report R45 (1959) entitled The Alum-Amine Process For The Recovery of Alumina From Shale by G. Thomas and T. R. Ingraham states " . . . With the recent resurgence in Canada, and in the United States, of attempts to recover cell-grade alumina from clays and shales, the Mines Branch undertook to review certain processes that had been tried with marginal success . . . In particular, it seemed quite possible that some recent developments in organic chemistry, relating to uranium technology, might be utilized for the removal of the last traces of iron from intermediate products to permit the attainment of a satisfactory grade of alumina." This introductory paragraph explains the authors' approach toward development of an alumina recovery process from shale. The following is an abstract of their successful laboratory experiments.

Jan 3, 1960

By George B. Clark

THE " Munroe effect" of shaped explosive charges was discovered by Charles E. Munroe more than 50 years ago (in 1888), but it was not until World War II that it was put to any practical use. Both Allied and Axis armies used the principle effectively in bazooka projectiles, artillery projectiles and in fixed shaped charges. The first two were used primarily to combat tanks and other armor and the latter to assault pillboxes and other fixed concrete emplacements. Many engineers and others who saw the military application of the jet effect of shaped charges believed application would be possible in many industrial fields where blasting is used, such as mining and quarrying. Some work has already been done on the problem of making shaped charges applicable to mining operations. Experimentation conducted at the National Tunnel and Mines' was directed primarily along the lines of use of shaped charges for secondary blasting in connection with long-hole stoping methods. Experimentation initiated earlier and conducted by the author2 at the University of Utah on a more scientific basis was directed at revealing the basic principles of the functioning of shaped charges, as well as the feasibility of using them in mining operations after the principles of their operation had been clearly defined. It was found that: (I) a given design of charge required an optimum standoff to make it most effective, either in penetrating solid rock or steel (see Fig 3); (2) for a given design of charge there exists an optimum ratio of charge diameter to charge height above which the increase in effectiveness of the charge decreases rapidly (see Figs 4 and 5); (3) partial confinement has the effect of making charge performance much more consistent; (4) the higher power and higher velocity explosives tested are much more effective than relatively low-strength explosives; and (5) shaped charges may be adaptable to mining operations in secondary breakage and drilling blasting holes. Fig I is a diagrammatic sketch of the action of a shaped charge for two types of cavities, while Fig 2 shows the approximate manner in which the jets are believed to be formed when an explosive wave encounters the cavity, approaching it from the top. The experimentation already completed has laid the foundation for further research in the study of shaped charges. Standoff effects, effect of the strength of explosives and other features have been fairly well established. Such elements in the design of shaped charges as (I) geometry of cavity liners, (2) relative horizontal dimensions of explosive column, (3) effect of

Jan 1, 1947

By E. S. Bartlett, D. N. Williams

QUANTITATIVE values for the oxidation rate of unalloyed molybdenum in air at temperatures above the melting point (1460°F) of the characteristic oxide are contained in the literature as a result of previous investigations. Lustman' reported values corresponding to 0.36 in. penetration per day (IPD) at 1500 and 1600°F in still air, noting essentially no variation in rate with temperature. Jones, Spretnak, and Speiser' reported values corresponding to 0.14 and 0.13 IPD at 1500 and 1800°F, respectively, in still air, attributing the decreased oxidation rate at higher temperatures to a lesser accumulation of the corrosive molten oxide on the surface at the higher temperature as a result of increased volatilization rate. Harwood3 ecently summarized work in the field, presenting generalized data corresponding to 0.48 to 0.96 IPD at 1800°F and 0.55 to 0.83 IPD at 1700°F in slowly flowing air. In a recent program at Battelle, it became desirable to know more about the characteristic oxidation behavior of molybdenum under varying conditions of temperature and atmosphere. Using oxidation-test apparatus designed for dynamic, continuous recording of weight change during testing,' values for the oxidation rate of molybdenum were obtained at temperatures from 1400 to 2150°F. In addition the effect of air flow on the oxidation rate was studied briefly at temperatures of 1600, 1800, and 2000°F. Exhaust of the contaminated atmosphere from the oxidation chamber was effected by an impeller pump attached to a 3/16-in.-diam opening in the oxidation chamber. The volumetric exhaust rate (cubic feet per hour) was normally maintained slightly in excess of the input rate to avoid condensation of MOO,,' on the sample suspension rod. The entering atmosphere was preheated prior to admission to the oxidation chamber by a 1 1/2-in.-diam cup packed with shredded asbestos. The experimental data are presented in Table I. Comparing conditions 2 and 3 (taking into account the temperature difference) and conditions 8 and 9. shows that in the absence of forced exhaust an atmosphere of moving air results in greater oxidation rate than a stagnant atmosphere. The use of forced exhaust, as shown by comparing conditions 3 and 4 and conditions 14 and 15: resulted in an even greater increase in oxidation rate. By virtue of the size of the atmosphere input and exhaust openings, it was calculated that the exhaust velocity was about 60 times that of the input velocity for essentially equal volumetric flow rates. Because of the proximity (about 3/4 in.) of the exhaust port to the specimen, it is logical to assume that cleansing of the atmosphere immediately surrounding the specimen was accomplished much more efficiently by the exhaust flow than by the input flow at a constant-volumetric flow rate. Also, it can be seen by comparing conditions 4 through 7 and conditions 11 through 13 that increasing the rate of atmosphere flow (by increasing input velocity with a proportional increase in exhaust velocity) above some optimum value has little, if any, further effect on the oxidation rate. These results suggest that there is a maximum oxidation rate for molydenum at a given temperature which is obtained when conditions are maintained such that the partial pressure of MOO3 in the atmosphere surrounding the specimen is at a low value. By controlling the partial pressure of MOO, surrounding the sample, it is possible to control the rate of volatilization of MOO:, from the surface. This, in turn, affects the rate of oxidation, since the thickness of the MOO3 layer determines the amount of oxygen which will be able to reach the reaction surface.' When the liquid oxide layer is less than some critical thickness, i.e., when the volatilization rate is high, enough oxygen is transported to the active surface to permit oxidation to proceed at the maximum rate allowed by the kinetics of the oxidation reaction. However, if the volatilization of MOO,, is suppressed, the thickness of the layer of MOO3 on the surface increases, and the diffusion of oxygen through the oxide layer becomes the rate-controlling step in the oxidation process. The lack of agreement between the present results and those of previous investigators is presumed to be due to differences in removal of the oxidation product (Moo,) from the immediate vicinity of the sample. By comparing conditions 1, 5, 10, 12 and 14, it is seen that when forced exhaust was used the oxidation rate of molybdenum increased with increasing temperature. A rapid increase was observed between 1400 and 1600°F, attributable to the effects

Jan 1, 1959

By Walter Gaby

L. C. GRATON, Cambridge, Mass.-May I ask, in connection with one point in the summary, to what extent the author regards actinolite equivalent to tourmaline as an index of high-temperature and presumably magmatic conditions of deposition of the accompanying sulphides? W. E. GARY.-I merely advanced the idea that the mineral actinolite might have some such significance. In the copper deposit at Braden in South America, the ore occurs in an andesite breccia which is cemented by a matrix of sulphides, quartz, and tourmaline. Tourmaline is a high-temperature mineral, and when we find it associated with ores, these are regarded as having come from a volcanic or deep-seated source, hence a primary hypogenetic deposit. Thus we can count on greater continuation of the ore with depth than in some other kinds of deposit, and I thought that the actinolite, being also a high-temperature mineral, might have some such bearing in the case of Mount Morgan. I did not advance this idea as a final conclusion from a study of such phenomena, but thought that it might bear some discussion in view of the fact of the peculiar occurrence of this mineral in a notable orebody. It also occurs with the copper ores at Ducktown, Tenn., and in both cases may only be due to general regional metamorphism.

Jan 12, 1916

By D. T. Novick, M. B. Bever, B. Roessler

Ordered and disordered specimens of the alloy CusAu were cold worked and then annealed at 2880, 310°, and 340°C, together with disordered unworked specimens. me resistivity decreased during annealing mainly as a result of ordering; the resistivity measurements suggest that in cold-worked specimens the growth of antiphase domains is impeded. The strength properties increased during annealing at 288 "C; in cold-worked specimens this increase was lo a level above that for cold-worked specimens which had not been annealed. X-ray diffraction showed that after annealing for a few hours at 288ºC, the long-range order increased to a constant value; additional annealing at 288ºC resulted in the growth of antiphase domains in which the degree of order was constant. Changes in peak breadth and particle size confirmed that in cold-worked specimens the major effects of cold work were not eliminated during annealing at 288 "C, although a slight recovery process occurred. When a specimen of the alloy Cu3Au is heated to a temperature below the critical temperature (388ºC), long-range ordering tends to occur in a specimen containing less than the equilibrium amount of order characteristic of that temperature Ideally, a specimen of Cu3Au contains no long-range order if it has been quenched from above the critical temperature. Long-range order is reduced by cold work. If cold-worked specimens are heated, restoration processes such as recovery and recrystallization may occur,

Jan 1, 1963

By R. A. Flinn, R. D. Pehlke, D. R. Glass, P. O. Hays

Knowledge of the depth of penetralion of an oxygen jet into the bath of the oxygen converter and of the correlation of penetration with driuing pressuve, lance heighl, and nozzle throat area is vital to the understanding of converter operation. If the penetration is too shallow, then severe and hazardous slopping takes place. On the other hand, if the jel penetrates entirely Lhvough lhe bath for an apprcciublc period of time, bottom damage occurs. In addilion to measurement of the penetralion of the jel, knou~ledge of the circulatory movement in the bath is also of interest in order to evaluale various theories oj-concerter operating behavior which have been published. In this investigation, experimental converters were buill of IOU- , 300-, and 4000-lb capacity. Four independent methods were used to determine penelralion: the onset of bottom marking, a nitrogen bubbler probe, observation througlt an optical syslew built into the oxygen lance, and direcl viewing of the jet issuing from the bottom of the vessel. Good correlation zuas obtained, and empirical relalions for pvedicling perletration were found. These relations were conjzrmed by bottom marking tests in 55- and 110-ton vessels. Within the operaling conditions employed in these tests, the depth to which a single oxygen jet penetrated zuas found lo vary according to the relatiorl ThE technical literature is replete with data concerning the successful use of the basic oxygen furnace or converter in steelmaking. Experimental data are lacking, however, on the vital factors of the depth of penetration of the jet into the bath and the induced circulation. Commercial operating conditions usually have been the result of cut and try experiments in lance manipulation until satisfactory results were obtained. There have been, however, two hotly argued opposing theories concerning desirable depth of penetration and these are exemplified by the Schwarz and Miles patents1,2 on one hand and the Suess patent3 on the other. The Schwarz patent teaches that the jet, issuing from the nozzle at supersonic speed, penetrates deeply "so that the reactions between the iron and the oxygen and between the oxygen and the rest of the smelting components take place in the center of the bath". Specific operating suggestions are given by Miles.2 By contrast, the Suess patent calls for surface Circulalion was investigated by lour methods: by direct observation in 200-lb open baths, by the use of graphite rudders in the 300- and 4000-lb converlers, by direct observalion through an oplical system in the lance, and by various models al room temperature. All were in excellent agreement and indicated that the motion of the bath ulas up at the center, radially outluavd at the surface, and down at the sides. Experi-ments in small and in commercial vessels indicate that it is essential to operate with a jet penetration of approximately 50 pct of the bath depth. Surface blowing results in low oxygen eficienty and in hazardous conditions which may render the process inopeuable. RejYactory dartzage al the bottom of the vessel is only encountered when the jet penetrates to the bottom, and this can be avoided by properly applying the penetration formula. The application of this en/pirical formula in commercial peraations is best when limited to combinations of lance size, pressure, and height which are typically encounteved in the use of a single-hole lance. blowing so that "...the oxygen jet does not penetrate deeply into the molten metal bath and is confined to an impingement area at the central portion of the bath surface". These references are given merely to illustrate the basic differences between the two schools of thought and to point out the need for measurement of penetration for the sake of the operator. For example, it is shown later that inefficient and even dangerous conditions can arise if improper blowing conditions are used. Differences are also evident between the two schools of thought as to the mixing, circulation, and agitation which is to be accomplished by the jet. The Schwarz patent states that "surface contact is not sufficient in most cases to bring about quick reaction, the same as the blowing of the gas over the bath surface or the mere blowing of the gas onto the bath surface". The patent goes on to call for active mixing. In contrast the claims of the Suess patent call for "discharging a stream of oxygen ... to an extent to avoid material agitation of the bath by the oxygen stream". In this patent the circulation is said to be downward in the center and up at the sides of the vessel. A number of investigators4-12 have explored penetration and circulation in transparent models. In general, it is agreed in these tests that the circulation is upward at the center (along the sides of the jet cavity),

Jan 1, 1968

By S. R. Goodman, Hsun Hu, R. S. Cline

The quenching technique has been used to study phase relations in the composition area 2FeO.SiO2-FeO-SiO2-MnO.Si02-ZMnO.SiO2 of the system iron oxide-manganese oxide-silica under strongly reducing conditions such as exist in a gas mixture consisting of equul parts of carbon dioxide and hydrogen. Liquidus and solidus temperatures of most mixtures in the composition area studied are in the range of 1173° to 1345°C. EQUILIBRIUM relations existing among the oxides of iron, manganese, and silicon are of particular interest in two areas of steelmaking: slags and ingot inclusions. Mixtures of these oxides represent about 90 pct of the slag in the acid steelmaking process, and so dominate the chemistry of the whole refining process. These constituents also play an important role in the early slags existing at the time of the "lime boil" in the basic open hearth process. If these slags are liquid, they "wet" the lumps of lime rising from the bottom of the bath, and react with them. A liquid slag rich in CaO is then formed at the very beginning of the refining. Because the temperature is still low, all conditions for a good dephosphoriza-tion are fulfilled at this stage of the operation. Metal deoxidized with ferromanganese or silico-manganese is likely to contain, as inclusions, phases made up from among the oxides of iron, manganese, and silicon. A knowledge of stability relations existing among the phases present in this system, therefore, enables one to predict the hardness of the inclusions encountered. Moreover, because the shape of the inclusions in steel has a profound influence on the physical properties of the metal, it is important to establish whether or not the oxidic material is present as liquid or crystalline phases during heating and rolling of the steel (-1150 to 1350°C). A knowledge of melting relations in synthetic mixtures of iron oxide, manganese oxide, and silica will give a clue to these problems. Methods for determining such relations and the results obtained are described iln this paper. I) PREVIOUS WORK A number cf previous studies have dealt with the three "binary"* systems bounding the system iron oxide-mangar,.ese oxide-silica. The system iron oxide-silica was studied by Bowen and shairerl in 1932. Their data were obtained by equilibration of mixtures in contact with metallic iron. Phase relations for the system iron oxide-silica ill atmospheres of different oxygen pressures car1 be derived from data on the system FeO-Fe2O3-SiO2 as determined by Muan.2 The diagram shown iri Fig. l is a section of this system in an atmosphere of CO2 and H2 in ratio 1:l. The system manganese oxide-silica has also been the subject of several investigations. Most of the early studies suffered from a lack of proper control of the atmosphere under which the equilibrations were carried mt. Phase diagrams for the system at two well defined levels of oxygen pressures have been determined recently. Glasser3 determined stability relations in an atmosphere consisting of carbon dioxide and hydrogen in ratio 5:1, diagram Fig. 2, and Muan4 studied phase relations in the system in air.

Jan 1, 1962

By Arthur F. Colombo

The selective flocculation, desliming and flotation process developed by the U.S. Department of the Interior, Bureau of Mines, as part of its goal of maintaining an adequate supply of minerals to meet national economic and strategic needs is described. The application of the selective flocculation and cationic flotation process to three oxidized taconites from the western Mesabi Range in Minnesota is discussed. Data from the operation of a 408-kilogram-per-hour (900 lb/hr) pilot plant employing reclaimed water are summarized for the three types of oxidized taconites.

Jan 1, 1980

By John A. Church

AT a time when the treatment of gold and silver ore9 by fusion, in opposition to the mill-process, is attracting so much attention in this country, it may be useful to consider what is done in a well-conducted foreign work. For this purpose I will ask the reader to accompany me to Lend, in Austria, a small but thoroughly organized

By Charles Prasky

ABOUT five years ago the Bureau of Mines began a study, at Minneapolis, of the various methods for beneficiating the low-grade manganese deposits of the Cuyuna range. Several samples of green carbonate slate from the Cuyuna range, containing about 7 pct Mn and about 28 pct Fe, were obtained for this study. The component minerals in the carbonate slate formation were so intimately associated that mineral dressing methods were not suitable for concentrating manganese to a ferrograde product. Although upgrading of manganese and iron minerals has been effected by flotation methods, it appears that manganese cannot be separated from iron except by chemical means. Because the flotation studies at Minneapolis were carried out simultaneously with the hydrometallurgical studies, only crude slate was available for process testing. An important economic consideration in selecting any one of the several chemical methods proposed for recovering ferrograde manganese is the availability of the chemical reagent. Fortunately, large tonnages of sulfur are available on the Cuyuna range in low-grade pyrite and pyrrhotite deposits that are readily concentrated by flotation to a suitable feed for a sulfide roasting furnace as indicated by a Bureau of Mines investigation in 195 0-1951.1 The roasted residue from the sulfide concentrates is a potential source of marketable iron oxide. Therefore, if these sulfide deposits were employed in recovering manganese, utilization of two heretofore unused mineral deposits would be accomplished. Laboratory investigations of several proposed leaching processes were made as a preliminary step in the investigation of hydrometallurgical methods for the treatment of Cuyuna carbonate slate using sulfur as a chemical reagent. From results obtained in the laboratory tests, these leaching processes did not appear entirely suitable for treating Cuyuna carbonate slate. The method developed at the North Central Experiment Station and selected for a more intensive pilot-plant investigation has been termed the differential high-temperature sulfatizing process. Essentially, this sulfatizing process consists of the following steps, described in the order in which the small-scale pilot-plant investigations were made. The first and perhaps most significant step in the process consists of a sulfate roast. Carbonate slate is roasted in an atmosphere of sulfur dioxide gas and air. The overall chemical reaction for converting manganese carbonate to a sulfate at a high temperature in a sulfur dioxide atmosphere follows MnCO8 + SO2 + 1/2 0, = MnSO4 + CO2 (H077°O = —64,180 cal per g mol) .' The need for concentrated sulfuric acid is avoided. Fine grinding is not essential. Removal of carbon dioxide from the slate during roasting produces a more porous structure and permits easier permeation by the sulfatizing gas mixture. The temperature limits for this conversion of manganese have been established as 600" and 850°C. Iron sulfate is unstable and is not formed at these temperatures; phosphorus is not converted to a water-soluble form; and polythionates are not formed. The second step in the process consists simply of a water leach of the sulfatized product. Manganese sulfate in the sulfatized product is dissolved in water. Iron, phosphorus, and calcium remain in the leach residue as water-insoluble products. The third and final step consists of the recovery of ferrograde manganese oxide from manganese sulfate leach solution. Water is evaporated from the leach solution, and impure monohydrate crystals of manganese sulfate are recovered. The moist crystals are formed into pellets or extrusions and thermally decomposed to produce a ferrograde manganese

Jan 1, 1958

By J. E. Coyne, L. E. Tanner, J. E. Boyd

In recent investigations of the isothermal transformations of the retained 0 phase in a titanium alloy having 13 pct V, 11 pct Cr, and 3 to 4 pct Al, there have been indications that the w transition phase is the initial decomposition product at temperatures below about 950°C (510 c).' This metastable phase, found in a number of titanium-base alloys rich in stabilizing elements and known to have an adverse effect on their ductility and toughness, is not easily observed by the usual experimental techniques. Since wis coherent with the /3 matrix,495 distinct interphase boundaries are not revealed metallographically. However, in some cases, an etching effect (i-e., a "mottled" /3 surface) poorly resolved by light microscopy has been found to correspond with the presence of w.6 X-ray diffraction examination has generally been the most suc- cessful means for identifying this phase and crys-tallographic determinations have been made.4'5 Dynamic elastic modulus7 and electrical resistivity measurementse have also aided in the identification of w. In the current study, the electron microscope was utilized to examine microstructures in aged Ti-13V-11Cr-3A1 that were unresolvable by light microscopy techniques. Using negative parlodion replicas (shadowed with chromium at 27 1/2 deg) examination was made of various transformation

Jan 1, 1962