By Kazuteru Tozcwa

The oxidation of several sulfide minerals in aqueous ammoniacal solution is discussed thermodynamically. The region in which Cu(NH3)2 4+ is stable has been estimated as a function of pH and concentration of total ammonia, {[NH3) + [NH4)}. In ammonia leaching when copper in sulfides is assumed to be extracted in the form of Cu(NH3)2 which will be rapidly converted to cupric ammine, thermodynamic data predict that such minerals are oxidized readily in the following order, CuS, Cu2S, CuFeS2, ZnS, NiS, Ag2S. This agrees with investigations on ammonia leaching of sulfide minerals, reported previously. The leaching of copper sulfide concentrate has been examined experimentally. Copper in a copper sulfide concentrate, in which the main constituents were chalcopyrite and pyrite, was effective¬ly extracted. The copper extraction was affected by factors such as (1) agitation intensity, (2) oxygen partial pressure, (3) NH3/Cu molar ratio, (4) leaching temperature and (5) addition of ammonium sulfate. From the results obtained in this work, it is concluded that mass transfer of oxygen plays the most important role in ammonia leaching of copper sulfide minerals.

Jan 1, 1976

By Stein Tore Johansen

Some ferro-silicon fumaces have heat-recovery equipment. Here, the recovery of electric energy from the off-gases can be increased by increasing the off-gas temperature. This is easily done by reducing the amount of air which usually is mixed into the off-gas to cool the gas mixture. If the off-gas becomes too hot problems with severe fouling or clogging of the gas channels? close to the fumace is observed~ The result is irregular stops to clean the off-gas channels. The paper focuses on the nature? of the clogging phenomena and some of the ways to avoid clogging. A detailed experimental study was carried out at the Elkem Thamshavn Plant. Theoretical studies were performed to understand the particle deposition, turbulent multiphase fluid flow and off gas combustion in the off-gas channels. The study has resulted in reduced clogging.

Jan 1, 1992

By Cailing Zhen, Jian Pan, Deqing Zhu, Xianlin Zhou, Yanhong Luo, Guixiang Huang

The grate-kiln process has been widely applied for oxide pellet production with the quick development of steel industry in China, but ring formation takes place which adversely affects the productivity and properties of fired pellets. Rotary kiln at high temperature seems a black box, and ring formation is difficult to measure directly by current technology. It’s of great importance to monitor ring formation during firing of pellets. Therefore, a method for estimating the thickness of ring formation in rotary kilns was studied, based on working out theoretically the relationship between ring thickness and the outside surface of the kiln, according to steady-state heat transfer across a cylinder, which provides a soft-sensing technique for ring formation at high temperature, and achieves stable pellet production .

Jan 1, 2015

By L. W. Beckstead

The use of acid ferric sulfate solution as a lixiviant for chalcopyrite concentrates has been of little interest from a practical standpoint due to the formation of a tenacious layer of elemental sulfur which severely impedes the reaction progress. CuFeS2 + 4Fe+3 ?Cu+2 + 5Fe+2 +2s° For example, an acid ferric sulfate leach of chalcopyrite concentrate results in only 12% copper extraction in a three hour leach at 93°C. Experimental results suggest that particle size is the only controllable variable which has a significant effect on the rate of acid ferric sulfate leaching at ambient pressure. Size reduction of the concentrate prior to leaching was exam¬ined using various methods of grinding. Of the grinding methods considered, attrition grinding was found to be the most effective. Leaching of an attritor-ground product (median particle size 0.5 microns) resulted in approximately 90% copper extraction in a three hour leach at 93°C. Energy measurements suggest that the costs associated with attrition mill¬ing are not unreasonable. Evidence indicates that "activation" or stored strain energy is not responsibile for the enhanced reaction kinetics of the finely ground concentrate, but rather the experimental results can be explained simply in terms of the increased surface area due to size reduction. Leaching reaction mech¬anisms operative in the acid ferric sulfate system are discussed and the application of ultra-fine grinding technology to other systems is considered.

Jan 1, 1976

By T. T. Chen, J. E. Dutrizac

"Grooved cast Pb-Ag anodes are used by some zinc refineries to improve current efficiency. It was found that the manganese oxide scale formed on a grooved Pb-0.75% Ag anode consists mainly of MnO2, which occurs characteristically in rhythmically banded colloform structures and adheres to a layer of ""Pb02+PbS04"" that oxidized from the anode. The relatively homogeneous and nearly fracture-free morphology of the ""Pb02+PbS04"" layer suggests the relatively uniform corrosion of the anode. Deposition of the Mn oxide initially follows the contours of the anode surface, but the grooves eventually become filled with Mn oxide and gypsum. Hydrous Mn oxides and amorphous Mn oxides are believed to be also present in the manganese oxide scale. Tiny particles of PbS04 and SrS04, together with gypsum, other impurities and micro-pores, tend to concentrate in the grooves.IntroductionManganese is a common impurity in hydrometallurgical zinc processing circuits. The manganese originates from sphalerite (Zn,Fe,Mn)S and from the Mn02 added to the leaching circuit to oxidize ferrous ions [1]. Manganese in the sphalerite follows Zn through the roasting, leaching and purification processes, and is present as Mn(II) in the purified ZnS04 solution. The Mn in the added Mn02 is reduced to Mn(II) during the oxidation of the ferrous ions present in the leach solutions. In both cases, MnS04 is generated, and the MnS04 accumulates in the purified solution. In the cellhouse, Zn is plated at the cathodes to produce high quality metal. The Mn(II) is partly oxidized at the anode surface to Mn(IV), and the Mn(IV) precipitates as a scale on the surface of the anode and as a sludge on the bottom of the electrolysis cells. The presence of a thin layer of manganese oxide scale on the surface of the Pb-Ag anode can minimize the corrosion of lead and, accordingly, reduce the contamination of the electrodeposited zinc. However, a heavy manganese scale build-up can cause ""staining"" of the zinc deposits and reduced current efficiencies. Consequently, periodic anode cleaning to remove excess manganese oxide scale is carried out routinely in commercial operations."

Jan 1, 2011

By F. Leclerc, V. Rebeyrolle, M. Revil-Baudard, A. Jardy, M. Založnik, H. Combeau

"Since the quality of Vacuum Arc Remelted ingots is linked to their chemical homogeneity and metallurgical structure, a modeling study of the solidification during VAR has been undertaken. It is based on the solution of the coupled transient heat, momentum and solute transport equations during the remelting of a cylindrical ingot. Solidification mechanisms implemented in the model include a full coupling between energy and solute transport in the mushy zone, and accounting for nucleation and finite diffusion of solutes at the microscopic scale, in both solid and liquid phases. This modeling can be applied to actual multi-component alloys. In this paper, the macrosegregation in Zircaloy 4 ingots is investigated. To validate the model, one single melt of a homogeneous electrode has been specifically performed. The comparison between the predicted macrosegregation and the experimental results shows the importance of accounting for solutal convection to forecast properly the macrosegregation in remelted ingots.IntroductionVacuum Arc Remelting of zirconium alloy ingots is a key step in the manufacturing process of fuel assembly components in nuclear reactors. The control of the chemical homogeneity is indeed fundamental to ensure the quality and the in-reactor performance of the final products. Despite the use of electromagnetic stirring to homogenize the liquid melt composition, chemical heterogeneities develop in the mushy zone during the solidification stage. One of the main challenges for zirconium producers, as well as titanium producers, is to master the VAR process in order to control the macrosegregation in remelted ingots. Macrosegregation results from the association of microsegregation and transport phenomena. The latter are primarily due to the flow in the liquid and mushy parts. It is now well established [1-4] that the hydrodynamics of the melt pool in a VAR ingot depends on the combined action of the followings: thermal and solutal buoyancy, self-induced electromagnetic force and the periodic centrifugal force caused by the angular movement generated by the stirring. However, for zirconium alloy ingots, the effects of thermal and solutal buoyancy forces on macrosegregation through their influence on the flow in the mushy zone have not been clearly identified."

Jan 1, 2012

By D. M. Hausen

A refractory siliceous low-grade silver ore (265 g/t Ag) from a prospect in Sonora, Mexico was investigated mineralogically and metallurgically to evaluate extraction of the silver by conventional methods. Approximately half of the silver was recoverable, occurring as coarsely crystalline acanthite (70-300 Am) that was liberated in material crushed to minus 10 mesh. The remaining silver is refractory and occurs mostly as finely locked (-2 to 0.2 Am) acanthite in cherty quartz, and as minor amounts of finely disseminated stylotypite or freibergite in fluorite. The mineralogic data have thus served to explain the 50-60% recovery of silver by flotation and cyanidation.

Jan 1, 1991

By Sijun Li, Bingyu Zhang, Haitao Zhou, Zhendong Zhang, Guofei Si, Xianghua Liu

"Hot compression test of Nb microalloyed coiled tubing steel is performed on Gleeble3500 at 1123K—1373K and strain rate from 0.001 to 5s-1. It is found that flow softening occurs and the flow curves exhibit a peak with a characteristic of dynamic recrystallization (DRX) and change with temperature and strain rate significantly. The peak stress and peak strain are dependent on the Zener-Hollomon relationship with activation energy of 390 KJ/mol. On the basis of Avrami equation and the Zener-Hollomon parameter, it is obtained that the dynamic recrystallization kinetics equation with which the calculated and measured recrystallization fraction is very close. On the results of hot compression test, the Nb microalloyed coiled tubing steel is rolled by Thermo-Mechanical-Control-Processing (TMCP), and it is obtained that the yield strength and tensile strength of Nb microalloyed coiled tubing steel are 565MPa and 685MPa respectively, and the elongation percentage is 30.1%.IntroductionCoiled tubing is widely used in oil field for well logging, well completion, drilling, work over and other operation in various fields to solve a number of conventional operating techniques problem which are difficult resolved, and it plays a more and more important part in exploration and production at oil field. [1] It will improve the efficiency of exploration and exploitation, studying, developing and using coiled tubing technology. Therefore, the development of domestic coiled tubing materials and manufacturing technology are great significance. It is well known that Coiled tubing has relatively poor working conditions and complex force state. So, the coiled tubing needs satisfier a kind of high strength, high plasticity, and corrosion resistant under complex oil gas condition. As the coiled tubing technology developed, the level of the coiled tubing steel is from CT55 originally to CT90 and CT100, and the corresponding tensile strength is 483MPa-758MPa. [2, 3]"

Jan 1, 2012

By Shulan Wang, Xuan Liu, Li Li

"Electrochemistry of Fe(III) in 69CaCl2-12CaF2-19KF and 81CaCl2-19KF (mole percentage, %) was investigated at 827 oC on molybdenum electrode by cyclic voltammetry, chronoamperometry and galvanostatic electrolysis using Fe2O3 as the Fe(III) source. The reduction of Fe(III) to Fe was conducted in one step and controlled by diffusion process. Fe(III) shown greater reduction rate and diffusion coefficient in molten 81CaCl2-19KF than in 69CaCl2- 12CaF2-19KF. Galvanostic electrolysis of Fe was performed in both molten salts with a cylindrical cathode rotating at 200 r/min and dendritic iron deposit was obtained.Keywords: iron; electrolysis; electrochemistry; molten saltIntroductionThe production of iron and steel causes huge emissions of CO2. Iron electrowinning in molten salts with dissolved Fe2O3 using an inert oxygen evolving anode is an alternative process to reduce or eliminate the formation of CO2. Research on novel process of producing metal has been reported recently [1-2] by using CaCl2 as the main electrolyte and dissolving CaO in CaCl2 due to the high solubility of CaO in the melt. This process has been used in preparing many active metals and alloys [3-14]. In the present work, the electrochemical behavior of iron in CaCl2-KF was studied and transport property of iron ion in the melt was discussed.ExperimentalCaCl2,CaF2 and KF (in analytical purity) were dried in air for 48 h. Mixed salts used in experiments were placed in a graphite crucible (??58 mm inner diameter). The graphite crucible together with the salts was heated at 473 K for 12 h in a furnace with flowing Ar (99.99%) before further heating. Temperature inside the furnace was measured by an S type thermocouple. Electrochemical measurements, such as cyclic voltammetry and chronocoulometry, were performed in a three electrode cell by EG&G PAR273A potentiostat/galvanostatand. Galvanostatic electrodepositon of iron was conducted in a two electrode cell. Molybdenum (??2 mm) and iron (??5 mm) were used as the working electrode (WE) and the reference electrode, respectively. A graphite crucible and a magnetite rod (??25 mm ) consisted of 100% magnetite and sintered at 950 oC in argon atmosphere for 2 h with electrical conductivity of 366 O-1m-1 at room temperature were used as the counter electrodes in the galvanostatic electrolysis experiment. Carbon (??10 mm) was used as the counter electrode in electrochemical measurement. The deposits were washed in distilled water bubbled with argon and dried in air before being characterized by X-ray diffraction (PW3040/60 diffractometer) and scanning electron microscope (SEM, SSX-550)."

Jan 1, 2014

By V. V. Geikhman

The paper updates the Plant experience in the development and implementation of an advanced environmentally friendly zinc production technology complying with the technological and economic level of producers in the world and the standards of maximum permissible gas emissions stipulated by the Russian legislation. General water recycling engineering allowed to ensure 95.6% water rotation level. All solid wastes formed during treating zinc concentrate are processed into marketable products or semiproducts and sold. As a result of implementing innovation techniques production at the Chelyabinsk Zinc Plant is non-waste.

Jan 1, 2006

By John Snowberger III, J. Brent Hiskey

The electrochemical dissolution of super alloys containing different amounts of rhenium was investigated. The initial part of the investigation focused on the anodic dissolution of rhenium from second-generation (3% Re) and third-generation (6% Re) nickel based alloys. Exploratory electrochemical tests were conducted to evaluate solution chemistries and to establish fundamental dissolution behavior of the alloys. These included rotating disc electrode (RDE) cyclic voltammetry, linear sweep voltammetry, and chronoamperometry tests. Electrolytes comprising sulfuric acid, hydrochloric acid, and ammonium sulfate were examined. Of these, a 0.1 M HCl solution proved to be extremely effective for electrochemical dissolution of samples of CMSX-4, CMSX-10, and SC-180 alloys. This paper discusses in detail the electrochemical behavior of these alloys.

Jan 1, 2014

By Bart Blanpain, Tom Peter Jones, Muxing Guo, Liugang Chen, Huayue Shi

Fayalite based slag is formed during the smelting process of secondary copper resources. It was found that with the presence of high ZnO, the slag became viscous, causing a slag tapping problem. In the present paper, the phase relations of the slag system ZnO-“FeO”-SiO2-Al2O3- CaO (ZnO = 0-12 wt%, Al2O3% = 0-15 wt%, CaO = 0-1.5 wt%, with iron saturation) at 1150 °C is studied by using quenching technique followed by phase identification and compositional analysis of equilibrated samples. The dependence of FeO and Al2O3 solubility in the liquid slag on the chemical composition of slag is characterized. Based on the experimental data, the solid fraction of the slag, which may considerably, influences the slag viscosity, at the tapping temperature can be reasonably estimated and, therefore an appropriate modification of the slag composition can be made.

Jan 1, 2016

By Jan Steinhoff

The design options of a gravity separator are still limited and rely on the study of settling behavior. A methodology will be presented where an experimentally given inlet droplet size distribution (DSD) is the basis for the calculation of the dispersion layer in a gravity separator. A pilot-scale continuous gravity separator is presented and CFD (computational fluid dynamic) results are validated. A transmitted light measurement technique for the determination of the DSD is presented up to a holdup of 15% dispersed phase. The resulting DSD was in the range of 20–2000 μm depending on flow rate and phase ratio. Furthermore, correlations of the real DSD with the settling behavior of the dispersion in a settling cell are discussed. The new approach to the description of gravity separators will be presented and the applied CFD methods showed good results with the system water/paraffin.

By Joseph C. Milbourne

Tetra Technologies CCIX? (continuous countercurrent ion exchange) system has been involved in a wide range of uranium concentration, separation and purification applications over the past 40 years. Uranium ion exchange applications have ranged from the treatment of copper heap leach solution containing 5 parts per million of uranium to the treatment of high strength sulfuric acid solutions containing several thousand parts per million of uranium. The flexibility and the countercurrent mode of operation and other unique features of the CCIX? have resulted in successful uranium recovery from these solutions and many others.

Jan 1, 1995

By Donald R. Sadoway

The viability of treating certain forms of hazardous waste by direct electrolysis in molten oxides is under investigation. Secondary residue or waste mud produced in the course of chromate chemical production is the focus of attention in this study. The goal is to reduce the water soluble hexavalent chromium either to insoluble trivalent chromium or to chromium metal. Electrolysis tests have been conducted in a high temperature cell containing chromate sludge dissolved in an electrolyte composed of Al2O3, SiO2, CaO, and MgO. Oxygen production on a carbon-free anode has been confirmed.

Jan 1, 1992

By Björn Lindquist

Boliden has developed a number of specialised technologies for smelter gas handling and effluent treatment. These technologies will be described. Special attention will be given to the high-pressure venturi, Editube wet electrostatic precipitator, mercury removal processes, and two-stage effluent treatment.

Jan 1, 2002

By A. Rosenfeld

The feasibility of applying laser induced optical emission spectroscopy to the high speed sorting of mixed alloy aluminum scrap is investigated. The basic spectroscopy for analysing aluminum alloys for the major alloying elements over their full concentration ranges is established. Materials handling issues are also described and the components of an overall sorting system are presented.

Jan 1, 1995

By Versiane A. Leão

The hydrochloric leaching of chrysotile tailings and soapstone powders) is discussed. This two materials are magnesium compounds associated with carbonates and iron oxides. In this work the chemical and physical characterization of formers is presented and the thermodynamic analyses of leaching is carried out. Magnesium extraction is almost complete for chrysotile tailings while, for soapstone powders, one can be reached 60%. The behavior of iron and calcium impurities is discussed.

Jan 1, 1997

By James C. Sever

"With the advent of high energy costs and increasing concern for the environment leading to the incorporation the C02 life cycle as a criteria for the material used in a finished product, it is beneficial to analyze the plant and the process used in producing a raw material in order to identify practical, economic energy recovery opportunities. To this end a study was made of the proposed Nevada Clean Magnesium, Inc. Tami-Mosi reduction facility. Each source of waste heat is listed together with the assessment for potential co generation or direct recovery. The overall impact on energy requirement and C02 generation is provided.IntroductionHistorically metal reduction plants, large consumers of energy, do not recover waste heat. This occurred for many reasons:• Energy costs were low and the capital for a co-generation system could not be justified;• Waste heat sources contained entrained solids or liquids which would inhibit efficient energy recovery;• The exit temperature for the heat source was too low for efficient use by aaqueous Rankine cycle system.The business environment has now changed adding impetus to the recovery of energy previously discarded. Power costs have greatly increased. Global warming and the impact of carbon dioxide on the environment has become an issue which could impact the permitting of a plant. Technology improvements especially the development of a scaling environment waste heat boiler [l] and the development of the organic cycle Rankine cycle recovery system enable up to 70% energy recovery from ""low grade"" heat sources [2].With the inception of Nevada Clean Magnesium, Inc. 's (formerly Molycor Gold Corporation, Inc.)Northern Nevada Tami-Mosi project [3], an opportunity was presented to incorporate energy optimization from the initial design phase."

Jan 1, 2013

By John P. Hager

One possible approach for the recovery of mercury from acid plant blow-down sludge in smelters is the use of a vacuum retort reactor for the vaporization of the mercury with subsequent collection of metallic mercury in an attached condenser. An experimental study was undertaken to investigate the vaporization of mercury when present as a compound in the Hg-S-O and Hg-Se systems. A transpiration reactor was modified to operate under reduced pressure and with a continuous flow of inert sweep gas. A water-cooled cold finger was inserted into the exit end of the reactor to provide for the rapid quenching of the exit gases and the collection of the mercury. Rates of vaporization were measured at several temperatures for each compound and were generally found to be constant at a given temperature and reactor pressure. The results were used to determine the minimum operating temperature for 100% vaporization of the compound in 60 minutes. For Hg2SO4, HgSO4, and HgSO/2HgO the required temperatures. for a reactor pressure of 50 Torr. were determined to be 634°, 622°. and 603°C. respectively. For HgO, HgSe, and HgS the required temperatures were 557°. 451°. And 382°C. respectively. For HgS the rate of vaporization was also measured at a reactor pressure of 1 00 Torr. The rate of vaporization was found to be slower resulting in an increased vaporization temperature of 423°C. It was also determined that the mercury vapor present in the exit gas stream can back-react with the other gas species to a significant extent and can result in very little condensed metallic mercury. For the vaporization of both HgS and HgSe. the mercury vapor was found to have back-reacted to the extent that virtually none of the vaporized mercury was collected in metallic form. For the vaporization of Hg2S04? HgS04, and HgSO4*2HgO the amount of metallic mercury recovered varied from approximately 50% for HgS04*2HgO to approximately 10% for Hg2S04 and HgS04. Only for HgO was the recovered mercury in primarily elemental form. The application of the results to the operation of a vacuum retort and condenser system is discussed.

Jan 1, 2001