Search Documents

By Alberto Oalvez, Lucya Yunus, Pengfii Tan

"Laboratory flotation tests of slow cooled converter slag have showed that 92.5% copper recovery at the copper cut-off grade of 24 - 25 % can be achieved by using a 50:50 ratio of DSP330 and SIBX (sodium isobutyl xanthate) at the natural pH of 7 and with a grinding time of 18.5 minutes. 70ìéç is the P80 achieved at this grinding time. MIBC is the frother and the solid content of the flotation feed was 46%. In the plant trials, two types of collectors at two different feed particle sizes for both the normal and slow cooled slag were operated. The particle size was controlled by the feed rate. The P80 of 75 ìçé at a feed rate between 32 - 36 t/h were tested. The plant trials have demonstrated that the copper recovery in the milling and flotation process of the slow cooled slags was improved by 3%. IntroductionIt is proposed to float the slow cooled converter slag, in the auxiliary circuit of the copper concentrator at Mount Isa, by using the processing conditions identified from several laboratory flotation tests. Among these laboratory tests, one produced a copper recovery of 4 % higher than those achieved from a normal cooled slag with the same slag feed grade and the same copper content (24 - 26 %) in the concentrate. These test conditions were selected for further studies.Laboratory Test Work and Plant TrialsThere has been a lot of work conducted under laboratory and plant conditions [1]. However, the achieved results did not justify their total implementation in the Mount Isa Copper Concentrator. Initially, the lab trials were carried out with slag cooled 100% in air; then it was changed to combined cooling for 12 h with air and 2.5 days with water sprays. The reason for this change was the shortage of space when the slag was cooled 100% in air, as it takes several days to achieve safe temperatures for its removal. The San Manuel Copper Smelter has reported that their slag was left for air cooling in pits for 8 h and then was followed by water cooling for 2-3 days [2]"

Jan 1, 2012

By Shoji Taniguchi, Lifeng Zhang

"In this paper, firstly the 3D single-phase turbulent steady fluid flow in a vessel with four baffles stirred by a single impeller is mathematically simulated. Turbulence is modeled by using the standard k - e model. Sliding-grid method is used to model the impeller. The flow domain is divided into two cylindrical, the inner one rotates at the same speed as the impeller, and the outer one is fixed with the baffles. Results indicate that the high-speed zone is near the paddles, and larger stirring speed generates larger fluid flow velocity. The calculated stirring intensity data are used to analyze the experimental results. Secondly the effects, such as filter pore size, gas flow rate and NaCl concentration, on bubble size are studied by experiment. For the particle removal rate by bubble flotation in this vessel, first order kinetics is adopted. The effects of initial number of the particles, gas flow rate, particle and bubble size, stirring speed and surface condition, on the removal rate constant are discussed, and an empirical equation is derived by experimental data. At last, a simple model is developed to study the particle attachment probability on bubble surface under turbulent flow conditions. IntroductionIt is well known that inclusions have a bad effect on steel quality. Trying to remove inclusions from liquid steel as many as possible is one of the main objects for the metallurgical workers. Lots of ways are developed to remove inclusions from liquid steel. Gas injection is an effective one. This technique is used to achieve homogeneity in the temperature and metal composition and to assist in the removal of second phase and dissolved impurities from molten steel. Gas injection is commonly applied to the secondary metallurgy processes and continuous casting, for example the ladle argon gas treatment, RH vacuum degassing, and the gas injection in the Submerged Entry Nozzles (SEN) of continuous casting mold, etc. The development of these processes focuses on achieving two conditions: fine bubbles and good mixing. Fine bubbles provide a large gas/liquid interfacial area and a high attachment probability to inclusions, and good mixing enhances the efficiency of impurity transfer."

Jan 1, 2000

By Grigore Matei

The thermodynamic properties of CU2S-FeS system are important not only in the case of copper smelting but also in the case of general pyro-mctallurgy, However there are not many reported activity data In this study, activities of FeS and CU2S in the CU2S-FeS system were calculated using the Darken's method from the activity data of the CU2S-FeS-Sb2SJ systems measured by the transportation method at 10S0°C. The activities of CU2S and FeS in the CU2S-FeS system showed negative deviation from the ideal behaviour and satisfied the relation of the Gibbs-Duhem equation,

Jan 1, 2003

By Liping Li

A comprehensive three-dimensional two-phase mathematical model was developed to represent a channel type reactor with intense bottom gas agitation. Tracer dispersion and particle tracing methods were used to conduct the analysis based on the solution of the Navier-Stokes equations. Different operational parameters, such is gas volume flow rate. bubbler separation aspect ratios and liquid Input flow rates, were investigated for the purpose of reactor optimization. The numerical calculations were compared with experimental results obtained at the University of Missouri and a good general agreement was observed. Relatively low longitudinal mixing was observed characterizing the system as a "plug-flow" type reactor, in contrast to the intense vertical mixing, under the conditions investigated. Some general mixing characteristics are also discussed In connection to the behavior of other metallurgical reactors.

Jan 1, 1996

By Georgios N. Anastassakis, Nickolaos Georgiou

"Soil contamination by oil as well as by other organic pollutants poses a major problem to the environment. Various methods have been used to remove organic contaminants from soil, such as: biological, thermal, chemical and physical. Methods based on Mineral Processing principles have also been used (cyclone separation, gravimetric separation, attritioning and washing). This paper studies the possibility to remove a rich-in-contaminant soil fraction by applying flotation. The contaminated soil was artificially prepared by mixing soil with diesel fuel. Sodium dodecylsulfate (SDS) and a tertiary amine (TA) were used as collectors. The effect of collector quantity added and conditioning time was studied. The results showed that the removal of a rich-in-contaminant soil is feasible while a clean fraction is also obtained. In several cases, the removal of oil-contaminated soil approaches or reaches 100%. Introduction Human activities are intimately associated with environmental pollution to the air, water and soil, as well. Soil pollution from inorganic and organic compounds is of equal importance with that of air and water, as it results in soil degradation and its concomitant problems with respect to meeting the human needs (house building, agriculture etc). Heavy metals along with their compounds are encountered among the most usual soil inorganic pollutants. The corresponding organic soil-pollutants are oil, oil-derivatives, pesticides, various aromatic (benzene, phenols, cresols, toluene etc) and poly-aromatic (naphthalene, anthracene etc) hydrocarbons, as well as various other organic compounds (pyridine, cyclo-hexane etc). Oil remains the basic energy source sharing 38% of the global needs, being followed by coal and gas with a share of 26 and 21% correspondingly [1]. The entire activities related with oil production, transport and consumption promote pollution in the air, water and soil. Consequently, soil pollution from oil is favoured at refineries, storage sites (due to possible pipe and tank leakage, tank cleaning works, loading and transportation) and, finally, at the oil-selling sites. Oil (or diesel-oil) fuel is a mixture of hydrocarbons, with 10-20 carbon atoms in the chain of each. It is mainly composed of paraffins, naphthenes and various aromatic compounds. In general, oil is composed of 20-30% in aromatic compounds, 5-6% in naphthenes and the rest is paraffins [1]."

Jan 1, 2008

By Akira Yazawa, Kazuo Koike, Mitsuhisa Hino

"The vapor pressures of MS (PbS, SnS and Sb2S3) in the molten Cu2S-MS, FeS-MS pseudo-binary and Cu2S-FeS-MS ternary systems were measured by means of a transportation method in the temperature range of 1323 and 1423K to calculate MS activities in the sulfide melts. The activities of MS in these systems show negative deviation from ideal behavior except the FeS binary systems which exhibit nearly ideal behavior in the homogeneous melts. The activities of the Cu2S-FeS pseudobinary system, which is fundamentals of the copper matte, were estimated from the activity values in the ternary systems and exhibit negative deviation from ideality.The distribution behavior of tin between the ·matte and silica saturated fayalite slag was investigated under the controlled partial pressures of S02 at l 523K. It was found that, in general, tin is distributed in the both phase, while tin is concentrated to the slag phase with increasing copper content in the matte. The activity coefficient of SnO in the slag was calculated based on the distribution ratio combined with the activity coefficient in the Cu2S-FeS system.IntroductionThe thermodynamic properties related to the Cu2S-FeS system and the Cu2S-FeS-MS systems (where MS can be PbS, SnS, Sb2S3, As2S3, Bi2S3, etc.) is required to be better understanding of the copper smelting process. However, thermodynamic analysis such as the distribution of impurities among the gas, slag and matte phases is difficult due to lack of thermodynamic data. In this study, the vapor pressures of MS (PbS, SnS and Sb2S3) in the Cu2S-MS, FeS-MS. and Cu2S-FeS-MS systems were measured by a transportation method. The distribution behavior of tin between the matte and silica saturated fayalite slag was also investigated. The results in the present experiments are useful to analyze thermodynamically the behavior of component in the copper matte smelting."

Jan 1, 2000

By Bogidar Mihaylov

A laboratory study was conducted on continuous precipitation of copper, cadmium, mercury and arsenic using thiourea, thioacetamide, sodium sulfide and ammonium sulfide as precipitating agents. Depending on the experimental conditions the metals precipitate with the sulfide donors at different orders and rates. These differences were employed as a basis of several techniques for continuous separation of copper and arsenic, cadmium and arsenic, mercury and copper, and copper, mercury and arsenic. The separation of the metals from industrial waste solutions was also studied. The precipitates obtained were inspected using x-ray diffraction, scanning electron microscope, atomic absorption spectrometer and plasma particle counter.

Jan 1, 1992

By Chao Li, Lim Hongxu, Yuyue Wang, Xie Yang

"A intergrated process of sulfuric acid leaching, sodium chloride leaching, lead chloride crystallization, lead hydroxide synthesis and roasting was carried out for the recovery of lead, cadmium, copper and zinc from lead smelting dust containing various metals. The results showed that the separation of cadmium, zinc and copper from dust could be obtained after sulfuric acid leaching and corresponding leaching rate were 92.12%, 90.25% and 88.26% respectively. The subsequent sodium chloride leaching carried out for lead with optimized parameters as: sodium chloride concentration 250g/L, leaching temperature 90°C, leaching time 2h, pulp density 33g/L, 0.12mol/L CaCh; The lead compounds crystallization rate reached 86.67%, and then transferred into mPbO·nH2O, the product of 98.66% ß-PbO could be obtained through roasting under 502°C. In the end, a feasible method of ß-PbO preparation from lead containing dust was put forward.IntroductionThe pyro-metallurgy flue dust from smelting lead activities are often stockpiled and pose potential environmental risks due to the heavy toxic elements, such as Pb, Cd, As, Cu, Cl, and Zn which are contained in the dust. With the rapid depletion of rich ore resources in recent years, it has become increasingly more financially attractive to recover valuable metals from previously stockpiled dust, while simultaneously reducing the potential of environmental pollution from toxic elements contained in the dust. Nowadays, pyro-metallurgical and hydrometallurgical routes or both combined methods can be developed to treat secondary materials such as lead ash, leach residues etc. By comparison the hydrometallurgical processes are often considered more eco-friendly.Some chloride leaching processes for recovering lead have been employed using either NaCl, or MgC2 and CaCl2, or FeCl3 [1] The effectiveness of the brine leaching method is based on the formation of complex metal chlorides in concentrated chloride solutions [2] Similarly, Other metals such as zinc, cadmium and copper contained in the flue dust are often treated with sulfuric acid, hydrochloric acid, ammonium solution and sodium hydroxide etc. as lixiviants [3] The metals from leach solutions thus has been obtained by precipitation, ion exchange, solvent extraction or replacement [4]"

Jan 1, 2014

By G. G. Krishna Murthy

Interactions of wustite and hematite pellets with Fe-C melts were investigated experimentally by examining the effect of pellet size and bath temperature on the reduction rates of the pellets. Experiments were carried out in the temperature range 1473-1923 K. A flash X-ray equipment was used to obtain images of the melt surface during its reaction with an oxide pellet. The reduction rates were calculated using experimentally estimated time for complete reaction of a pellet, tR. The value of tR was determined employing gas mass flow rate, or pressure rise in the sealed furnace, versus time traces. The value of tR was the same for both wustite and hematite pellets of equal weight at or above 1723 K and it decreased with increasing melt temperature. But the reduction rate was substantially lower at temperatures below 1651 K, the melting point of wustite. The rates were defined as the rate of moles of oxygen removed from the pellet per unit area of bath free surface and it was found that the bath surface area affects the reduction rates. It was established that the overall reaction followed nth-order rate kinetics with the values of n falling between 0.3 and 0.4 for temperatures above the melting point of wustite. The apparent activation energy determined using the apparent rate constants obtained from the experimental data was 76.2 + 27.7 kJ/mol-O.

Jan 1, 1992

By Leo Brewer, Kazuyoshi Shimakage, Mamoru Mitomo, Toshiyuki Nishimura, Yoichiro Uemura, Shinji Hirai

"In the synthesis process of ß -La2S3 via the sulfurization of La2O3 powder using CS2 gas, La2O2S was formed. This occurred at an initial stage of the reaction for sulfurization temperatures below 973K, and ß -La2S3 was also formed at a shorter period for higher sulfurization temperatures. It was found that the oxygen content in ß -La2S3 powders decreased gradually with an increase in sulfurization temperature. On the other hand, the carbon content in these powders increased gradually with an increase in the sulfurization temperature. Though it has been reported that ß -La2S3 was transformed to Y -La2S3 at 1723K± 50K, the sintered compact of double-phase Y -La2S3 and ß. -La2S3 was formed at a rather higher temperature of 1973K when the synthetic powder of ß -La2S3 containing a high amount of oxygen was used. However, phase transformation of -La2S3 to Y -La2S3 progressed preferentially with a decrease in the oxygen content of synthetic ß -La2S3 powder. The Seebeck coefficient of the sintered double-phase Y -La2S3 and -La2S3 was higher than that of the single-phase Y -La2S3, reported previously.Introduction La2S3 exists in three polymorphic forms that are similar to a series of Ce2S3, Pr2S3 and Nd2S3: a, ß , and Y'. The a -La2S3, which is stable at low temperature, is irreversibly transformed to ß -La2S3 of various compositions in the solid-solution range between La2S3 and La3S4, at 923 ± 50K. The -La2S3 may also be an oxysulfide of La10S14O2. Moreover, the ß .-La2S3 phase is transformed to Y -La2S3 ,which has a Th3P4 structure, at 1573 ± 100K. The melting point of Y -La2S3 is 2398 ± 30K where this temperature is similar to those of common refractory materials such as silica and alumina. Therefore, it can be predicted that y -La2S3 which has a high melting point and a thermodynamic stability due to the strong affinity of La for S, would have &high refractory character and chemical inertness in many molten metals. The y -La2S3, colored vivid faint yellow is stable up to 623K in air, where oxidation starts. y -La2S3 is frequently used as pigments for plastics and paints3. Furthermore, Y -La2S3 which is a semiconductor, is considered to be useful as a thermoelectric conversion materials, because it has a high Seebeck coefficient."

Jan 1, 2000

By Tetsuya Uda

Our recent achievements of rare earth separation technique[1,2] and new process idea for rare earth magnet recycling[3] are reviewed, (1) Binary chloride mixtures of rare earths were separated by a new selective reduction-vacuum distillation process. According to our experimental results, apparent separation factors were 8.1 for the Pr-Nd chloride mixture and 570 for the Nd-Sm chloride mixture. These values are much higher than conventional solvent extraction methods. (2) A study of recycling process of magnet sludge was carried out. The rare earths in the neodymium magnet sludge were extracted by chlorination with FeCI2, An activated carbon was used as a de-oxidation reagent Metallic iron in the sludge was not chlorinated because the iron monochloride is not stable, The extracted rare earth chlorides were easily separated from Fe-alloy and the excess of FeCh by vacuum distillation, 96 % of neodymium and 94 % of dysprosium in the sludge were extraeted into chloride phase, By the vacuum distillation, a mixture of neodymium and dysprosium trichlorides of 99.2 % purity was recovered, On the other hand, the rare earth chlorides can be converted to the corresponding oxides by a pyrohydrolysis reaction accompanied by a formation of HCl gas, The HCI gas can chlorinate metallic iron to FeCh, Therefore, a new recycling process for rare earth magnet waste can be realized as a chlorine circulation type process. During the process, only carbon and water are consumed and there are no toxic pollutants, Moreover, the obtained rare earth oxide can be directly used as raw material in the conventional oxide electrolysis process,

Jan 1, 2003

By Sang-Su Lee

This paper shows the application of the porous plug system in the Mitsubishi continuous copper smelting and converting process. This system has already been adopted and utilized in the steel industry to enhance productivity. Recently, some copper smelters have adopted this system but the results have not been satisfactory. The porous plug system was installed at the anode furnace in December 2001 to reduce the oxidation time and decrease the oil consumption. A good effect was that the nitrogen stirring of the melt through porous plugs improved the melt heat transfer. As the result of the enhancing heat transfer the oil consumption and the build-up inside the furnace were actually decreased. But until now the oxidation time has not been sufficiently reduced. In the future, further research and tests are needed in order to increase the productivity and save costs.

Jan 1, 2003

By Sang-Su Lee

This paper shows the application of the porous plug system in the Mitsubishi continuous copper smelting and converting process. This system has already been adopted and utilized in the steel industry to enhance productivity. Recently, some copper smelters have adopted this system but the results have not been satisfactory. The porous plug system was installed at the anode furnace in December 2001 to reduce the oxidation time and decrease the oil consumption. A good effect was that the nitrogen stirring of the melt through porous plugs improved the melt heat transfer. As the result of the enhancing heat transfer the oil consumption and the build up inside the furnace were actually decreased. But until now the oxidation time has not been sufficiently reduced. In the future, further research and tests are needed in order to increase the productivity and save costs.

Jan 1, 2003

By M. J. Adam

The U.S. Bureau of Mines is investigating the partitioning of selected complex minerals into simple phases using sulfidation reactions. Successful partitioning of complex mineralogy to simple phases may afford an opportunity to improve selective extraction of mineral constituents of economic value. The research has shown that complex minerals, such as chalcopyrite (CuFeS2) and pentlandite [(Fe,Ni)9Se]' may be partitioned to the simpler phases covellite (CuS) plus pyrite (FeS2) and vaesite (NiS2) plus pyrite (FeS2), respectively. Demonstrations of these reactions were verified through long-react ion-time (24 h or more) experiments, but basic rate investigations and modeling were not included in the previous research. This report describes research aimed at determining the rate at which the complex mineral CuFeS2 converts to the simple sulfides CuS plus FeS2. Small samples of CuFeS2 were blended with elemental S prior to thermal treating under an He atmosphere for time periods up to 4 h. Products from each treatment period were characterized using metallography, chemical analysis, X-ray diffraction (XRD), and scanning electron microscopy (SEM). Results of the investigation revealed a rapid conversion of CuFeS2 to CuS plus FeS2 early in thermal treatment periods. As the reaction occurred, a CuS rimming of particles was observed which separated the reacting species (CuFeS2 and S) and caused a considerable decrease in transformation rate.

Jan 1, 1991

By Pedro Lobarinhas

In the present work a two dimensional computational model is derived for the description of the time dependent heap leaching process. The flow inside the heap is calculated using the diffusion equations for the flow in porous media. The soil conductivity is also estimated assuming a close packed structure for the grain packing inside the heap. These equations, with appropriate boundary conditions, are solved using a time step splitting scheme. From this calculation the amount of leaching reagent in contact with the ore at any position inside the heap can be calculated and, once coupled with appropriate reaction equations, the amount of metals extracted can be computed and leaching agent concentration updated. The model is tested with available experimental data and the results have shown to be in a very good agreement. The model predicts all the transient features of the data.

Jan 1, 1999

By Congcong Yang, Jian Pan, Deqing Zhu, Yang Zhong

A study of pelletization of one imported chromite concentrate with coarse site, poor ballability and refractory roasting performance was conducted in small scale tests, and high pressure grinding rollers (HPGR) was used to improve the pelletization. The mechanism of HPGR was revealed by means of SEM images and optical microscopy. Compared with the ball milling pretreatment, HPGR pretreatment can not only enhance the ballability of pellet feed but also drop the roasting temperature. Fired pellets, containing proper chemical compositions with high compressive strength of 2917N/pellet and good metallurgical performances, have been manufactured. The mechanism of HPGR reveals that chromite particle surface turns to more irregular after HPGR treatment and more new surface being formed because of more cracks, sharp corners and edges appearing, resulting in higher surface chemical activity, all of which improve the ballability of the chromite concentrate and contribute to the consolidation of fired pellets.

Jan 1, 2015

By Takashi Fujii

In the OG (Osaka Gas) process which includes a fusion process of sewage disposal sludge in coke bed knowledge of molten and fluid properties of the sludge are most important to controll the process in good condition. Thus, the softening and melting temperatures and viscosity were measured by the sessile drop technique and a rotating viscometer. Obtained results are summarized as follows: Melting character of sludge slag is varied according to their composition, but closely related to CaO/SiO2 ratio in ordinary sludge and to CaO/(Cr2O3,+Al2O3+P2O5) ratio in Cr2O3 containing sludge. Fluid property of sludge slag has a correlation with optical basicity or Riboud parameter, However, the correlation is poorer than that of metallurgical slags. Especially, chromium oxide containing sludge shows high viscosity and behaves somewhat different manner from ordinary sludge.

Jan 1, 1992

By Cyro Takano

This paper is a contribution to fundamentals data on the equilibrium metal/slag for refining silicon in relation to Ca and Al as impurities. Silicon containing 0.1% Al and no Ca was placed in contact with a slag of various contents of CaO, SiO2 and Al2O3. Slag Al2O3 contents were 11.4%, 25.1% and 29.6%, keeping the ratio %CaO/%SiO2 constant and equal to ~0.53. The experiments were conducted at 1550oC, in a graphite crucible with argon atmosphere. The equilibrium was observed with low and medium content of Al2O3. The derived activities coefficients of Ca and Al in dilute solution of Si presented good correlation with those of the literature. Parallel reactions with formations of SiO(g) and CO (g) were also observed.

Jan 1, 2006

By Y. Y. Sheng

Plume flows created by gas injection into liquid metals have been studied extensively, however the dynamics of bubbles within the plume have not received adequate attention, particularly for large, irregular bubbles, characteristic of the processing of liquid metals. The present model uses a combined Eulerian-Lagrangian approach in which an estimated void fraction distribution is used to calculate the liquid flow field with a conventional Eulerian scheme. The trajectories of bubbles are then computed in a Lagrangian manner using the estimated flow field, and experimentally measured information on bubble drag coefficients', lateral migration due to lateral lift forces and interaction with turbulent eddies, and variation in bubble size due to break-up. Turbulence in the two-phase zone is modeled with a modified k-e model with extra source terms to account for the second phase which have been recently determined by the present authors. The computed void fraction and turbulent liquid flow field distributions are in good agreement with experimental measurements.

Jan 1, 1993

By Henrik Gudbrandsen, Geir Martin Haarberg, Ana Maria Martinez, Karen S. Osen, Sverre Rolseth

"The Several approaches were tried for developing an electrochemical route for producing high purity silicon from molten salts. K2SiF6 and metallurgical grade silicon were used as the source of silicon. Molten LiF-KF and pure KF with additions of K2SiF6 were used as electrolytes at temperatures from 550 - 900 oC. Silicon was cathodically deposited and anodically dissolved in the fluoride electrolytes. High electrorefining efficiency was obtained for many elements after electrolysis experiments at constant potential or constant current. The main challenge was to reduce the contents of boron and phosphorus. Another difficulty was to remove inclusions of solidified electrolyte. The lowest energy consumption was estimated to be ~ 3 kWh/kg Si, while the best current efficiency for Si deposition was found to be ~ 95 %.IntroductionSilicon is the most important material for photovoltaic power generation devices because of high feasible efficiency, low ecological impact and slow degradation. Development of a new and less expensive route for producing silicon of the desired quality is necessary in order to make solar cells competitive. Electrochemical routes may be an alternative possibility, and many laboratory studies have been reported over the past few decades. Most of the studies have been performed in molten salts, chloride or fluoride, at moderate temperatures so that solid silicon was deposited at the cathode. The production of high purity silicon has shown an annual increase of about 25 %, due to the increasing demand of solar grade silicon (SoG-Si). For future increased use of solar energy it is important to develop alternative, more energy efficient and cheaper processes for SoG-Si production compared to the Siemens process.Common silicon sources have been SiO2 and K2SiF6 for electrowinning and MG-Si in the case of electrorefining. A serious challenge is to find an oxygen evolving anode for electrolytes containing dissolved oxides. Especially at moderate to high temperatures and in molten fluoride electrolytes this is a difficult task.Many experimental results have been reported in molten chloride electrolytes. Nohira et al. [1-3] and Chen et al. [4] cathodically deposited silicon by electrodeoxidation of solid SiO2 in molten CaCl2 by potentiostatic electrolysis. An alternatice approach is to use electrorefining of low-cost metallurgical grade silicon (MGSi) to produce SOG-Si. In previous studies [5], an MG-Si anode was used, and silicon was successfully electrodeposited on a molybdenum wire in a CaCl2 based melt. It was found that the anode was strongly passivated due to the precipitation of silicon. Also, some deposits detached from the molybdenum wire because of the poor adherence to the cathode.Considering the Cu-Si alloy which has a good segregation effect for some impurities, and should not passivate, could be a good candidate anode for electrorefining. [6]."

Jan 1, 2014