By Norbert L. Piret

During smelting of copper, arsenic in the feed reports to a large extent to the gas phase and some enters the anode copper. From the gas phase it is transferred during wet gas cleaning directly, or indirectly after dust processing, to aqueous solution. During the electrorefining and anode slimes processing, the anode arsenic content is also transferred to aqueous solution. Technology for the efficient removal of arsenic from process streams and cleaning of aqueous effluents is well established. However, the arsenic-bearing products, which thereby are generated, can vary widely in consistency, quality and quantity, from large amounts of gypsum contaminated with water-soluble arsenic compounds to residues with high arsenic content ' or arsenic products. Arsenic management in a copper smelter not only is involved with the duty of compliance to the gaseous and aqueous emissions standards but also should have as objective the minimization of the generation of arsenic-bearing and, in general, heavy metal-bearing solid waste. The present paper outlines options and the associated economic aspects for minimization of arsenic-bearing solid waste generation, for improvement of the environmental compatibility of the residues to be deposited and for the .production of commerciable arsenic compounds under appropriate market conditions.

Jan 1, 1999

By Ozgul Dere Ozdemir, Muge Sari Yilmaz, Sabriye Piskin, Deren Sibel Kasap

"Galvanic sludge is generated at the end of the waste water treatment process of metal plating system. The waste sludge is one of the main hazardous solid wastes produced by metallurgical industries. It is caused the harm of human health and damage of the environment due to containing reasonable amounts of toxic metals (e.g., nickel, zinc, copper, chromium, iron, lead, cadmium, etc). The concentration of those toxic metals in the wastewater might reach 30% (w/w, dry weight) making their removal and recovery an interesting issue.In this study, synthesized titanium dioxide is used as adsorbent to remove nickel in leachate of galvanic sludge. The adsorption experiments were carried out isothermally at four different temperatures. The effects of pH, temperature, and contact time on nickel adsorption efficiency were investigated, and the optimum parameters were determined from the experimental studies. The experimental results indicated that pH, temperature, and contact time played a significant role on the adsorption capacity of nickel.IntroductionRapid industrialization has caused increasing the heavy metal concentration in biosphere with the industrial wastes. These wastes are generated in various industrial processes such as electroplating. Galvanic sludge is a hazardous waste that generates from metal plating industry by chemical precipitation of heavy metals from acidic or alkaline solutions during the waste water treatment process. Heavy metals are tend to bioaccumulate thus they are treated the living organism [1-2].Galvanic sludge is mainly disposed on landfills for these reason it is a big problem for environment. Galvanic sludge containing nickel (II) is common because nickel (II) is used in electroplating process [3]. In drinking water, nickel may cause health problems if found in amounts greater than the health standard set (MCLG: 0.1 mg/L) by the United States Environmental Protection Agency (EPA). The higher concentration of nickel (II) in ingested water may cause severe damage to lungs, kidneys, gastrointestinal distress, e.g., nausea, vomiting, diarrhea, pulmonary fibrosis, renal edema, and skin dermatitis [ 4]. For these reasons, it must be treated before disposed to landfill."

Jan 1, 2011

Rotary kiln incinerators are widely used in the incineration of various types of hazardous wastes. However, the complex transport processes within the incinerator are not well understood. Due to large variations in waste types and difficulties in feed characterization, the incineration process meets great challenges in a smooth operation, and expects uncertainties in the process chemistry and emission control. In order to get better understanding of the incineration process, process simulation was made on the kiln behavior by using Computational Fluid-dynamics (CFD) to characterize gas flow, temperature distribution and waste combustion in the incinerator. Temperature measurement was conducted in an operating incinerator to validate the CFD model. This paper addresses the environmental issues related to the hazardous incineration process, and reports the recent simulation results on gas flow and mixing, combustion heat transfer, and potentials to reduce emissions.

Jan 1, 2002

By Philippe Charlier

Recycling of aluminium contained in used aseptic beverage cartons is a difficult task which has nevertheless to be tackled by our modern societies. Techniques have earlier been developed by the paper and pulp industry for the recycling of the board fibres from collected post-consumer beverage cartons. A joint technical feasibility study by Granges and a leading beverage carton producer has dealt with different techniques for handling residues from repulping facilities. The aluminium obtained can be used as raw material for the production of thin gauge foil, thus closing the recycling loop.

Jan 1, 1995

By Chai Liyuan

This paper focused on the preparation of porous ceramic pellets for microorganism carriers. A new method for the process was developed using simple gel-casting and bubble-in-water-in-oil type of multiphase double emulsion. The globules, consisting of a foamed sepiolite slurry suspension, were dispersed and consolidated in spherical shape in liquid paraffin as gelation progressed. The green pellets were sintered at 1100°C. The influence of surfactants, extension ratio and impeller revolution rate on the process and characteristics of the pellets was investigated. The pellet size was in the range of 1~4mm and determined directly by impeller revolution rate. The fine cell diameter of porous ceramic was in the range of 100~500m and the micropore diameter was less than 5m. The inner macropores were interconnected and extend to the external surface. It is impossible to analyze a result by SEM micrographs and digital camera.

Jan 1, 2006

By Jukka S. Sulanto

Outokumpu has applied its well -known copper Fl ash Smelling Process also for smelting su1phide lead . concentrates. The lead in the Flash Smelting Furnace slag is recovered by reducing the oxygen potential of the slag in an electric furnace by injecting reductant into the slag bath. A series of tests have been carried out in a 1000 KVA electric furnace? adjacent to a pilot Flash Smelting Furnace. The furnace has been fed continuously with molten Flash Furnace Slag. The feed rate has varied from 0.5 to 3.1 MTPH (0.55 - 3..4 STPH) depending on the feed rate and the quality of concentrate to the Flash Smelting Furnace. The inlet slag contained 15 to 40% of lead and the cleaned slag 1. 5 to 3. 0%. The lead recovery from sol id raw material was tested in the same continuous process by feeding lead calcine into the furnace. Feed rate was 0.7 to 0.95 MTPH (0.8 - 1.05 STPH) and the calcine contained 33 to 34% of Pb. Several reduction agents and procedures were tested. The process proved to be suitable for continuous recovery of lead from solid oxide raw materials.

Jan 1, 1990

By Henry Hu, Alfred Yu

"A numerical model has been developed to simulate heat and mass transfer phenomena occurring during a novel magnesium reduction process-the vertical retort technology. The model was based on the control - volume finite difference approach. Simulations were run to determine the effect of various processing parameters on magnesium reduction cycle time. The model predicted temperature distributions, heating curves, recovery ratio of magnesium, and total process times. The predictions were used to optimize the magnesium reduction process including dimensions of the retort, geometries of the reactant compounds, and productivities. The results indicate that the implementation of the optimized processing parameters significantly decreases the reduction time, and consequently increases the production rate as well as lowers the energy consumption.IntroductionMagnesium consumption has been growing considerably in the past decade [1]. Of the total magnesium production, 30% is produced by the thermal reduction (Pidgeon) process, and it is anticipated to be still the main technology for producing magnesium in future [2]. One of the advantages of the Pidgeon process is that it is capable of producing high purity magnesium demanded by both the automotive and aerospace industries. However, the inefficiency of heat and mass transfer taking place in the horizontal Pidgeon reduction process results in low productivity, high energy consumption, labor-intensive operation, large floor space and high capital investment. This limits the production scale of a horizontal Pidgeon reduction process [3].Vertical reduction processTo overcome the shortcomings of the horizontal magnesium reduction process, a novel vertical magnesium reduction process [3] for large-scale production has been developed, in which heat and mass transfer in the retort is enhanced. The new process shortens reduction time, reduces energy consumption and increases productivity. The vertical reduction system is comprised of a vertically-placed retort, a heating furnace and a vacuum system. A section of the vertical retort is illustrated in Figure 1. Since the retort is set vertically, instead of horizontally, the entire procedure of loading the reactants material in the new process is different from the one for the horizontal reduction process."

Jan 1, 2001

By Hiroaki Nakano, Kenji Hara, Shunsuke Kawano, Takeshi Ohgai, Michiaki Ikeda, Hisaaki Fukushima, Shinji Yamashita, Tetsuya Akiyama, Hisayuki Kaku

"Ni-Fe alloys have an inverse magnetostrictive effect (Villari effect) in which its permeability varies according to the ·applied strain. This alloy film has a potential for application as force sensors such as torque sensors, tension sensors and so on. Electrodeposition is promising as a technique for preparing Ni-Fe alloy film because of its convenience and economy. In this paper, the effects of electrolysis conditions on the magnetic properties of electrodeposited Ni-Fe alloy films were investigated. Hysteresis loops of Ni-Fe alloy films on copper substrates from sulfate bath were measured by a vibrating sample magnetometer (VSM). The films of low coercivity, which were preferred when used as a force sensor were obtained by introducing certain additives to the sulfate type bath.INTRODUCTIONNi-Fe alloys show an inverse magnetostrictive effect (Villari effect) that their permeability varies depending on the applied strain. The films of this alloy have a potential for application as force sensors such as torque sensors, tension sensors and so on. The authors et al. tried to prepare Ni-Fe alloy films using the sputtering technique, and produced a prototype of Ni-Fe alloy torque sensor [I]. The sensitivity was higher in the torque sensor thus produced than the strain gauge type one, and this torque sensor enables non-contacted detection. It showed excellent durability and reliability. However, the formation of Ni-Fe alloys by sputtering requires higher costs and brought an another problem that the shape of the substrate on which the film was formed was considerably limited. This causes a hindrance to the wide-range application of the force sensors. Electrodeposition is promising as the technique for preparing Ni-Fe alloy films because of its convenience and economy. In this paper, the effects of the conditions of electrodeposition on the magnetic properties of Ni-Fe alloy films were studied."

Jan 1, 2000

By Juergen Antrekowitsch, Stephan R. Steinacker

The main aim of the electric furnace treatment in the primary copper industry is the reduction of valuable metals such as zinc, lead or copper itself. On the one hand legal restrictions for the further use of the treated slag are constantly getting stricter while on the other every type of loss in the oxidic phase leads to economic disadvantages. In order to fully understand and to improve the process, kinetics during the reduction play an essential role. In the first part, this paper highlights the theoretical background of the reduction process, while the following chapters present experimental aspects and results from laboratory scale trials at the Montanuniversitaet Leoben. In addition, the comparison between the chemical reaction and the diffusion model plays a continuously important role. By investigating the reducibility of electric furnace slag, process adaptions and ameliorations are developed.

Jan 1, 2016

By Zhongming Ren

"A new process of near net shape continuous casting of metal pipe has been put out. The specialty of the process is that no inner core is used. The principle of the process has been presented, and the effect of several factors on the thickness of the pipe has been investigated experimentally and numerically. It is shown that the temperature and the level of the molten metal, cooling intensity of the mold, and the velocity of casting influenced the thickness of the pipe apparently. In order to improve evenness of the thickness of the pipe, the mold was dedicatedly designed, and special methods were taken. By this process, a metallic material like ""bamboo"" was fabricated.IntroductionMetal pipe is a widely used material. Up to now, many processes have been put out to produce the pipe. However, the processes are usually expensive and inefficient. For instance, the welding pipe, which is most widely used, is produced through continuous casting of slab, rolling of the slab into sheet, and welding, with several times of heating and processing. Continuous casting of pipe can not produce small diameter of pipe, which is mostly needed, due to the inner core. Even though. OCC process is novel in fabricating the pipe with small diameter, it is inefficient. In this paper, the no-inner core continuous casting of pipe was proposed. With this process, pipe with small diameter can be produced efficiently. The influence of several parameters on the thickness and evenness of piper wall. With this process, a ""bamboolike"" pipe was fabricated.ExperimentThe experimental apparatus is shown in Fig. I. It is composed of mold, furnace, melt level adjuster, and dummy pipe. In the process, the level of the melt was adjusted at a proper position, then the mold along with the dummy pipe was inserted into the melt in a certain depth. The melt in the mold began solidifying, forming a solid shell. After that, the dummy pipe was pulled upward in a certain speed, drawing the solid shell out of the mold. Thus, a pipe was continuously cast."

Jan 1, 2000

By Hua Hou, Xiaofeng Niu, Wei Liang

"The explicit finite difference (EFD) method is used for calculating the casting temperature field during solidification. Because the time step is limited, the computational efficiency of the EFD method is lower. In order to improve the computational efficiency, a fourth-order in space and second-order in time model based on the equivalent specific heat method and the alternating direction implicit (ADI) method is established. The degree of similarity between the simulation results and the experimental results is analyzed. The results show that the simulation results of this high order mathematical model are close to the experimental results.IntroductionThe 3D heat transfer equation of temperature field during solidification process is as the following: [1-3]."

Jan 1, 2013

By V. B. Telles, D. C. R. Espinosa, J. A. S. Tenório

"The purpose of this work was to study the reutilization of the steelmaking dust, derived from steel production in the electric arc furnace (EAF), in iron ore sintering process aiming zinc elimination. In each sintering process were collected sintered samples, these materials were analyzed by chemical analysis using atomic absorption spectrophotometry in order to determine the zinc content. Samples of not sintered mixtures were also characterized by chemical analysis aiming to determine the initial amounts of zinc, i.e. in order to check the zinc amounts present in the mixture before the sintering process. The comparation among the zinc contents of samples sintered and not sintered allowed to determine the elimination of zinc during the experiments. Results showed that the zinc elimination in the process is proportional to the ratio reducer/waste. The zinc removal was lower when the reducer/waste ratio was decreased.IntroductionThe electric arc furnace dust (EAFD) is a residue generated in the steelmaking process using electric arc furnace. Aproximately 30% of all steel produced (in the year 2009) was obtained through electric arc furance (EAF). In the United States of America the percentage of this process in the total crude steel production was about 62% in 2009, while in 2000 this percentage was only 47% [1].The iron ore sintering is a process that reuses wastes generated in metallurgical industries. However, the materials used must be physical and chemical characteristics compatible with the blast furnaces.The quantity of zinc, cadmium, chrome and other metals present in the EAFD depends on the quality of the scrap used to feed the EAF and the type of steel that it is been made [2,3]. The reuse of EAFD waste is interesting to steelmaking processes because of its iron content. However the presence of zinc inside a blast furnace is undesirable since the zinc oxide can be deposited on the blast furnace walls and in the drivers of gas output, interrupting the flow. Another part of the zinc oxide can form deposits on the refractory lining of the blast furnace [4,5]."

Jan 1, 2012

By Hideki Yamamoto

A new technology to convert fluoride gas (C2H2F4 ; R-134a) contained in the exhaust gases from semiconductor manufacturing plants and refrigerators directly into a harmless substance have been established, thus, presenting a new concept for the disposal of fluoride gases such as CFCs that are associated with the global warming. Experimental results verify that chemical reactions with metal compounds can take place at substantially lower temperatures of 700- 800K as compared with combustion. treatment temperatures of 1200-1500K. The reaction product is mainly metal fluoride, which chemically is a harmless material. Furthermore, this process is compact, easily controlled, safe and has low running costs. This paper deals with a new chemical reaction method for the harmless disposal of gases effecting the global warming.

Jan 1, 2003

By Hideki Yamamoto

A new technology to convert fluoride gas (C2H2F4 : R-134a) contained in the exhaust gases from semiconductor manufacturing plants and refrigerators directly into a harmless substance have been established, thus, presenting a new concept for the disposal of fluoride gases such as CFCs that are associated with the global warming. Experimental results verify that chemical reactions with metal compounds can take place at substantially lower temperatures of 700- 800K as compared with combustion treatment temperatures of 1200-1500K. The reaction product is mainly metal fluoride, which chemically is a harmless material. Furthermore, this process is compact, easily controlled, safe and has low running costs. This paper deals with a new chemical reaction method for the harmless disposal of gases effecting the global warming.

Jan 1, 2003

By D. C. Azubike

Wolframite (FeWO4) usually having cassiterite (SnO2) as a major impurity is a primary source of tungsten. Its direct reduction/carburisation with carbon in the temperature range 1000-1400°C, and with hydrogen at 600-900°C followed by carburisation with CO at 900°C are described. Depending on the conditions and reactants employed, Fe, Fe2W, B-Sn,WC, W2C, Fe3W3C and Fe6W6C are the products. Tin was found to inhibit the overall reduction and carburisation reactions significantly. The potential for either efficient separation of iron and tungsten or a one-stage production of an iron-based metal carbide composite is discussed.

Jan 1, 1992

By R. K. F. Lam

Unacceptable levels of impurity were noted in high purity chromium melting. Analysis of recent melting data determined that oxygen content in chromium is the critical parameter. Thermodynamics studies identify zirconia to be the most stable oxide in the presence of liquid chromium, followed by alumina and silica. Iron oxide reacts readily with liquid Cr. A certain degree of chemical reaction between liquid chromium and oxides does occur, contamination by the crucible is therefore unavoidable. Equilibrium constants indicate that a chromium oxide addition decreases 'ceramic dissolution and reduces impurity contamination. Safe operating conditions with oxygen content between 1190 ppm and 2500 ppm were identified. Additions of chromium oxide (Cr2O3) of 161 grams and 264 grams to liquid chromium yielded acceptable levels of impurity, and oxygen content was respectively increased to 1624 ppm and 2 179 ppm. A new process of melting high purity chromium with chromium oxide addition for controlling the activity of Cr2O3 is recommended.

Jan 1, 1997

By T. T. Chen

The manganese oxide scales, consisting mainly of MnO2, characteristically occur in banded colloform structures which adhere to porous layers of PbSO4 and PbO2 that oxidized from the rolled Pb-0.7% Ag anodes. Hydrous Mn oxides, Mn3O4 and amorphous Mn oxides are believed to be also present. Tiny particles of gypsum, PbSO4, SrSO4 and AgCl are entrapped in the colloform masses. The gypsum originated from the Zn electrolyte; strontium carbonate was added to the ZnSO4 solution to control Pb, and silver originated from the anodes. Some of the colloform bands contain minor amounts of Pb, implying a limited degree of dissolution of the Pb during electrolysis. Other colloform bands incorporate trace amounts of Zn. Colloform structures permeated with silica gel are presumably caused by the high silica content of the electrolyte.

Jan 1, 2009

By A. J. Paul

Traditionally, 16"/50 caliber projectile shells have been fabricated from forged steel. The Naval Surface Warfare Center (NAVSWC) has determined that cost savings of approximately 60% (-$4.7M/year) as well as improved shell fragmentation can be achieved by casting these shells from austempered ductile iron. One of the technical concerns arising out of this material substitution is the role of the casting process in controlling the quality of the cast shells. Optimizing the process through proper orientation of the mold, placement of chills, superheat, etc., can minimize shrinkage porosity and, consequently, flaw size. For this purpose, the mold filling and subsequent solidification of the projectiles was simulated using a 3-D, fully transient, coupled fluid flow and heat transfer model based on finite differences. Several casting orientations were investigated and the casting parameters were varied to optimize the process and minimize casting defects. A comprehensive software tool, which was developed using state-of- the-art visualization techniques, has been used to analyze the process of casting. Emphasis is placed on the use of this visualization tool as an aid to the foundry engineer for process optimization.

Jan 1, 1992

By S. P. Song

A computational methodology based on the coupled finite element and boundary methods is developed to predict the free surface shapes of electrically conducting liquids supported by the electromagnetic field. The work is an extension of our previous FEIBE model for induction calculations. The free surface algorithm is developed using the Weighted Residual Method, the very same used for nonlinear finite element formulation. This allows the treatment of field computation and free surface prediction in the same manner, thus making easier the formulation of the magnetically-supported free surface problems. Like other nonlinear algorithms, the boundary/finite element free surface scheme is also iterative owing to the fact that free surface shapes are unknown a priori. But the numerical scheme is robust and efficient and is capable of handling rather complex free surface deformations. Computational algorithms will be given and are tested by comparing with other solutions whenever available. Computed results of magnetically-supported free surface shapes are presented for magnetic levitation under microgravity and floating zone refining processes under normal gravity.

Jan 1, 1996

By Hiroaki Kawamura, Takeshi Yoshikawa, Kazuki Morita, Yutaka Yanaba

"To develop an alternative metallurgical process for phosphorus removal in the production of solar-grade silicon (SOG-Si), slag treatment of metallurgical-grade silicon (MG-Si) was conducted, followed by acid leaching. Phosphorus-doped silicon alloy or MG-Si containing certain amounts of phosphorus and calcium was reacted at 1723 K and 1773 K with CaO--CaF2 of several compositions. Phosphorus removal from the molten silicon into the slag phase was confirmed by reduction to phosphide ions, P3-, and phosphate ions, P3-. These ions were separately determined using a wet chemical analysis method developed by ourselves. The highest phosphorus distribution ratio obtained was 2. 7 after reaction for 18 h with 17.5 mass% CaO--CaF2 slag. We then conducted acid leaching of the silicon and achieved removal of a large fraction (over 90 % ) of the phosphorus, which was much higher than that obtained by ordinary oxidizing slag treatment.IntroductionIn recent years, the production of solar cells has been increasing rapidly. Because of this, the demand for solar-grade silicon (SOG-Si) has also been growing rapidly. The development of lower-cost mass production processes is therefore needed to provide silicon feedstock. Phosphorus is one of the impurities in metallurgical-grade silicon (MG-Si). Because of its large segregation coefficient (kp = 0.35) [l ], it is difficult to remove phosphorus using a solidification refining process. Vacuum melting is considered to be a promising method for removing phosphorous from MG-Si [2], but the issues of high cost and large energy consumption have still to be resolved.Slag treatment is often used to remove impurity elements by oxidizing reactions during general oxidation refining processes. For example, phosphorus in molten steel is removed into a slag phase as phosphate ions, PO4 3-l-, by the following reaction:"

Jan 1, 2013