By Zhang Chuanfu

Keywords: solid solution, Ni-Co alloy powders, thermal decomposition, fibres. Synthesis of fibrous Ni-Co alloy powders was achieved by thermal decomposition of precursor of complex Ni-Co oxalates solid solutions obtained via modified coprecipitation method among intimate mixing solution of NiCl2?6H2O , CoCl2?6H2O and H2C2O4?2H2O in the presence of surfactant polyvinylpyrrolidone (PVP) and organic solvent ethanol. Scan electron microscopy (SEM), X-ray diffraction (XRD), X-Ray photoelectron spectroscopy (XPS), disperse energy X-ray analyses (EDX) were used to characterize the structure features and chemical compositions of the as-prepared fibres. The influences of decomposition conditions, including temperature, time, the flow rate of N2+H2, and the heating rate, on the morphology, average size and specific surface area of the Ni-Co alloy powders were investigated. It is found that a trend of the mutual alloying of nickel and cobalt: the formation of perfect solid solution for any compositions NixCo100-x was indicated and corresponding NixCo100-x alloys with fcc phase can be obtained under the optimal conditions.

Jan 1, 2005

By Rick Honaker

Rare earth elements (REEs) contained in coal and associated mineral matter exist in several forms including micro-dispersed minerals, ion adsorption onto clay surfaces, and chemically bound. Tests found that REEs can be effectively recovered from certain components of three coal sources by leaching under mild conditions followed by solvent extraction. A range of pH values were evaluated at solution temperatures of 25 and 75 °C. When using 1.2 M of sulfuric acid, nearly 85% recovery of the REEs was extracted from the middlings material collected from an operating plant. Acid leaching of a second middling source from another plant resulted in 60% of the total REEs being recovered under the same leaching conditions. Solvent extraction treatment of the leachate produced from six different coal sources resulted in products containing up to 50% total REEs from feedstocks starting with around 300 ppm.

By B. R. Davis, Neale R. Neelameggham, R. E. Brown

The element Calcium element has a unique place in the production of etals, intermetallics and other compounds. The unusualness arises from the fact that we have several possible reductants – metallic calcium, calcium carbide, calcium cyanamide and calcium hydride. A review of how metallic calcium is manufactured and utilized is presented. The difficulties involved in producing the metal in large quantities and price implications are noted. . Fundamental thermodynamics of how these act as reductants are shown, along with the historic application of these in metal production during the past century and a half. Alternate applications as to how to control the cost of the reductant is indicated, such as the numerous attempts in making low cost titanium utilizing direct or indirect calcium reductant.

Jan 1, 2014

By C. F. Feng, L. Froyen

"In-situ processes have emerged as new and promising techniques for metal matrix composite fabrication. They offer significant technical and economic advantages over conventional processing. One of the in-situ processing routes that have been used is reactive free sintering of a mixture of powder reactants. However, materials synthesised via this route are always porous because of density differences between reactants and products. An example are the porous Al/(TiB2+Ah03) MMCs obtained by heating powder mixtures of Al+ Ti02+B with Ti02 and B in stoichiometric ratios for forming TiB2• In this study, porous Al/(TiB2+Ah03) composites were further processed by hot-pressing at temperatures above 600°C. This processing cycle was designed so that the composites could be densified. Furthermore, the reaction kinetics of the in-situ processing are studied by means of DSC analysis measured at different heating rates. The activation energies of the three intermediate steps that are involved in the reactive processing for preparing AV(TiB2+Alz03) MMCs are determined to be 923 kJ/mole, 241 kJ/mole and 235 kJ/mole respectively.XRD proved that the hot-pressed products consist of Al, TiB2 and Al203- Properties of the products are assessed by microstructural characterisation (LOM, SEM and EDS), microhardness, Young's modulus and bending tests. The results show that good microstructures, elastic properties and strengths, as well as acceptable ductilities were achieved. For the composition 79.74wt% Al-15.95wt% Ti0z-4.31wt% B, after the reactive free-sintering and hot-pressing cycles, Young's modulus is 105 GPa, bending strength is 509 MPa and maximum strain is 5.0%; for composition 88.73wt% Al-8.87wt% Ti0z-2.40wt% B, they are 89 GPa, 311 MPa and 8.2% respectively. It can be seen that the properties of products can be tailored by adjusting the relative amounts of reactants in green samples. Furthermore, for comparison reasons, Al and a binary system Al-Ti02 were identically processed as the ternary systems. Their microstructures and properties were studied."

Jan 1, 1998

By E. Oshilna

The Mitsubishi process has many advantages pertaining to economical and environmental matters. These advantages have led to the installations of the Mitsubishi process in constructing new smelters: The Mitsubishi process utilizes highly oxygen enriched blast air and uses a special lime slag in the C?furnace. These characteristics change the . distribution of Impurities from other processes which use P.S. converters, Recently an Increased amount of secondary materials which contain impurities Is being treated at Naoshima Smelter. In order to cope with an Increment of the Impurities load and maintain the cathode quality, many Improvements have been Implemented. This paper discusses the impurities behavior In the Mitsubishi process and describes the measures taken to treat an Increased ?amount of secondary materials:

Jan 1, 1998

By Liang Sha

In this study, adsorption of copper by chemically modified orange peel was investigated. A conspicuous change occurs in the surface morphology of the biomass due to modification, which is depicted by SEM images. Equilibrium isotherms and kinetics were obtained and the effects of various factors, including solution pH, contact time, initial metal ions concentration and temperature, were studied by batch experiments. Kinetics was found to be best-fit pseudosecond- order equations. Equilibrium was better described by Langermuir isotherms rather than Freudlich isotherms. At 25?, pH5.30, the maximum adsorption capacity was 70.67mg?g-1 . With increase of temperature, adsorption efficiency decreased. The biosorbent was suitable for repeated use for more than five cycles.

Jan 1, 2009

By Ko-ichiro Ohno

It is recently recognized that the iron reduction and melting as well as the slag separation of a composite of granular iron ore and coal are completed in a very short period of about 10 minutes when the composite is rapidly heated up to approximately 1673K. These phenomena are expected to be applied to a new iron-making process. The mechanism of iron ore reduction and iron-slag separation during rapid heating has not yet been revealed and the fundamental research has just started. Carburization of the reduced iron is regarded as one of the most important steps in this process. In the present work, the composite was prepared from four kinds of coal or graphite as a carbon source and electrolytic iron powder as a completely reduced iron ore. The temperature at which the liquid formation and iron carburization occurred was monitored. Direct observation of smelting reduction behavior was made by a confocal laser-scanning microscope combined with the infrared image-heating furnace to clarify the effect of molten ash on iron carburization. It was found that the meltdown temperature of composite became lower as the melting temperature of coal ash decreased. From the observed result, it was presumed that the liquid slag would act as an important media for the carbon transfer from coal to iron. The carburization mechanism during the smelting reduction was estimated as follows. When slag containing iron oxide melted down and contacted carbon, iron oxide in the slag was reduced and the formation of the metallic iron particle as well as the its carburization occurred simultaneously at the slag-carbon interface. Carburized iron particle was carried from slag-carbon to slag-iron interfaces due to the slag convection flow caused by the difference of the interfacial tension between the carbon-slag and iron-slag interfaces. Carburization of reduced iron could proceed with a repeat of the above-mentioned process.

Jan 1, 2003

By Sergio N. Monteiro

Polymeric matrix composites reinforced with coir fibers are being used in many industrial applications such as automobile interior panels and cushions. These composites have relatively low mechanical strength due to the weak fiber/matrix interface. The objective of the present work was to investigate the effect of a surface alkali treatment of the curaua fiber on the mechanical behavior of polyester composites with different amounts of these fibers. The treatment, also known as mercerization, was performed with distinct concentrations, 0.1 and 10% of NaOH at 1 min and 1 hour, before incorporation of the coir fibers into the polyester composite. The results showed no significant change in comparison to similar untreated coir fiber composites. A microstructure analysis revealed that, in addition to reducing the hydrophilic characteristic of the fiber,the treatment also affects the surface morphology and impairs the fiber/matrix interfacial strength.

Jan 1, 2009

A novel pressure leaching process for platinum group metal (PGM) feedstocks is described. The process is particularly well suited for treatment of ores or concentrates that are too low grade for economic processing by the conventional smelting/leaching process. Operating conditions have been identified under which gold, the PGM's and the base metals dissolve simultaneously in a pressure leaching autoclave. The product of this leaching process can then be treated by one of several flowsheets, of which the preferred will likely involve solid/liquid separation, followed by precipitation (or adsorption on activated carbon) of gold and the PGM's, followed by copper solvent extraction/electrowinning. Depending on the concentrations of nickel and cobalt, the copper raffinate would either be partially recycled to the autoclave to allow NilCo concentrations to build up, or it would proceed directly to a Ni/Co refinery. This paper deals with the pressure leaching process and the recovery of gold and the PGM's from the pressure leach product.

Jan 1, 2000

By Jing Zhan, Tian-zu Yang, Wei-feng Li, Li-Hua Jiang, Shi-yan Xu, Jian-yang Huang, Chuan-fu Zhang, Yan-qing Fan

The amount and activity of coal, reduction temperature and other parameters of the process of bottom-blown reduction of liquid high lead slag were investigated in laboratory. Methods to strengthen the bottom-blown reduction process were studied by industrial production. The results were in the follows: the reduction temperature was 1150℃; reduction time was 1.5h; the reductant was anthracite; lead content in slag was controlled to 2%; the rate of coal was 7% and gasification loss of coal in high temperature was severe; liquid lead slag reduction rate was faster with coal; prolonging the reaction size had little effect on reducing lead in slag; the size of the reactor can be further reduced.

Jan 1, 2015

By R. D. Pehlke

The history and present status of continuous casting of steel are reviewed, including a genera 1 description of current processes. Plant layout, process development and elements of machine component design are outlined, and key steps in integration into a stee-1 production system are detailed. Recent productivity advances and improvements in quality are described. Process developments are reviewed, and some future avenues for this technology are considered.

Jan 1, 1985

By Tiejun Chun, Jian Pan, Deqing Zhu, Vinicius Mendes

"Fine manganese fines are characterized by large amount and low price compared to lump manganese ores. However, fine manganese must be agglomerated as EAF (electric arc furnace) feed. In this paper, high quality fired pellets were produced by simulating grate-kiln process to supply the feed for EAF from some imported manganese ore fines containing high combined water. Manganese ore fines assaying 44.47wt%Mn, 5.89wt%Fe, 12.09%LOI and with 72.7wt% ranging between 0.5mm and 8mm, are pretreated up to the particle size of 84.7wt% passing 0.074mm by HPGR (high press grinding roller) twice in open circuit. The finely ground manganese fines were mixed with 1.2wt% bentonite, balled at 15% moisture for 7min in disc pelletizer. The drop numbers, compressive strength and thermal shock temperature of green balls reach 11 times/0.5m, 11 N/pellet and 360oC, respectively. After the green balls drying in the oven, the dry pellets were preheated at 1050oC for 12 min and then fired at 1300oC for 12 min in electric tube furnace. The compressive strength of fired pellets reaches 2621 N/pellet. Therefore, these pellets are high quality burden for blast furnace or EAF due to high mechanical strength and high Mn grade of 49.11wt% and low detrimental elements.IntroductionManganese, mainly using as deoxidizing agent, desulfurization agent and alloying elements, is widely used in the steel company. With the rapid development of iron and steel industry in China, domestic manganese ores cannot meet the requirement, resulting large quantities manganese ores import to China [1-4]. Compared to lump manganese ores, fine manganese ores containing high combined water are characterized by large amount and low price. However, they must be agglomerated as EAF (electric arc furnace) feed. There are three ways to agglomerate the manganese fine ores, sintering, briquetting and pelletizing [5-6]. Compared to the other two methods, pelletizing technology possesses the following superiorities, such as uniform size distribution of product, stabilizing chemical composition of product and lower energy consumption in producing. Therefore, pelletizing is a superior way to treat the fine manganese ores [7]. The systematic research of producing manganese oxide pellets by fine manganese ores containing high combined water was studied in this paper."

Jan 1, 2011

A three?stages countercurrent fluidized bed prototipe reactor to neutralize the SO2from smelter gases has been developed. For gases with 8 vol-%SO2, at 800°C and for 4 h mean reaction time of the limestone, the capture of SO2 is 99%, with off gases with 0.07 vol-%. For 2 vol-%SO2, the total capture of SO2 can be obtained at 750°C and 4 h reaction time. The calcine obtained contain a blend of unreacted limestone and calcium sulphatewith minor amounts of residual lime.

Jan 1, 2006

By G. Diáz

A basic technology coping with a wide range of secondary zinc sources has been developed. The process combines an electrowinning stage, a solvent-extraction unit and a leaching procedure. The acidity generated in zinc electrowinning, transferred by the organic solvent to the aqueous raffinate, is reused to leach the zinc secondary materials. The basic process recovering zinc is described in detail. The route recovering other valuable metals such as copper, cadmium and lead associated with zinc is also described. This non-ferrous metals recovery route is advisable for either ecological and/or economical reasons. Main results of an experimental program aiming at the demonstration of the suitability of the process for several feed materials are summarized. Waelz oxides, galvanizing ashes and EAFD coming from different sources were tested in laboratory and continuous pilot plant campaigns. High zinc recovery, low reagents and utilities consumption, and effluents meeting environmental regulation were confirmed. The paper also includes the main results of a feasibility study of an industrial "base case". A mixed raw material and Spanish EAFD and 20,000 ta of zinc ingots production were chosen. The SGH zinc recovery from secondary raw material by means of the clean, safe and profitable Modified Zincex Process has been demonstrated. This reliable technology is ready for industrial application.

Jan 1, 1995

By R. B. Nourse

The depressed market for Ferrochrome worldwide has forced most producers in this industry to scale down production. Inevitably, many furnaces have been mothballed for prolonged periods, awaiting an upturn in the Ferrochrome market. In contrast, the Platinum industry is experiencing relative stability combined with good prices and they have been looking for cash cows to take advantage of these market conditions. It is, therefore, rather convenient that Platinum and Ferrochrome producers are virtually neighbours in the Bushveld complex of South Afiica, since there is an abundance of spare furnace capacity around (albeit for Ferrochrome). Against this backdrop, Pyromet Technologies (Pty) Ltd, who are currently designing a slag cleaning furnace for Anglo Platinum, was requested to perform pilot scale testwork on a 200kW furnace, in order to establish the suitability to process platinum concentrate and converter slag in a furnace designed for Ferrochrome. This paper provides an overview of the configuration, test conditions, operation and results achieved during the testwork. It also discusses the critical issues, such as refractory consumption, copper cooling and electrical parameters that need to be addressed when converting a Ferrochrome Smelter into a Sulphide Smelter.

Jan 1, 2002

By Yuanbo Zhang, Qian Li, Helei Zhang, Heng Yu, Guanghui Li, Tao Jiang

"Large reserves of specularite iron ores have been found all over the world, which is characterized by high total iron grade, low gangues content, as well as low commercial price. However, it has not been widely used in sinter or pellet production due to its inferior sintering and roasting behaviors. It has shown that the proportion of specularite ores was increased as high as 40%~50% and good results was achieveed by using Composite Agglomeration Process (CAP), an innovative agglomeration process invented by Central South University. But the mineralization of specularite is still unknown during composite agglomeration processing. In this paper, the induration characteristic of specularite ore is studied by simulating CAP in laboratory, as well as microstructure analysis of CAP product. The results show that specularite pellet is mainly indurated through recrystallization of Fe2O3, calcium ferrite within high basicity sinters matrix interweaves with the recrystallized Fe2O3 on the surface of the pellet, which forms an integral microstructure, and ensures high strength of CAP product for ironmaking.IntroductionLarge reserves of specularite iron ores have been found all over the world, especially in Minas Gerais of Brazil, Xuanhua city and Anshan city of China, Elba island of Italy, St.Gotthard of Switzerland, Cumberland of Britannic, and so on. The specularite ores have a smooth surface, as well as a good crystallization and dense texture. When specularite is used to produce pellets, the specularite ore grains are difficult to adhere onto green ball due to its poor ballability. Moreover, specularite pellet requires high roasting temperature over 1300°C [1]. When specularite ore is used in sintering, the permeability of sintering bed gets bad and the quality of sinter is diminished. The practice in a few sintering plants finds that the output and strength of sinter decrease with the increase of specularite proportion, and the consumption of coke increases [2-4]. Therefore, the utilization of specularite has been limited. Composite Agglomeration Process (CAP) is an innovative technology invented by Central South University [5-7]. The process has the following merits: making reasonable utilization of different iron ore resources; improving the quality and output of sinters; manufacturing sinters with low basicity; significantly reducing energy consumption, etc[8-9]. It has been shown that large proportion specularite ores, as high as 40%~50% can be used well by CAP [10], but the mineralization of specularite pellet is still unknown during composite agglomeration processing. In this investigation, the induration characteristics of specularite ore pellets is studied by simulating CAP in laboratory, and the phase composition and microstructure of CAP product are also characterized by using microscope and Leica image analyzer (Germany, Leica DM RXp)."

Jan 1, 2011

By Volker Uhlenwinkel

The design of a free fall atomizer as well as the process parameters affect the particle mass flux distribution in the spray cone. The mass flux distribution is important in spray forming because of its influence on the deposit shape and enthalpy input into the deposit. In this article the effect of different process parameters on the mass flux distribution is shown. Furthermore, different melts were atomized with the same atomizer. An empirical correlation will be introduced to predict the mass flux in the spray cone. This correlation will be compared with experimental results.

Jan 1, 1999

By J. W. Perez

A simple exponential model has been developed (Perez and Aplan. Process Mineralogy, VI, 1986) to describe the fractional yield of a given species out of a locked assemblage: Fractional Yield of Species A = a e X/U where 'X' is particle size and 'a' and 'U' are constants. In the present study, the general validity of this model has been further demonstrated. experimentally, for the liberation of coal and pyrite out of various raw coals and beneficiated fractions using a variety of crushing devices. Using data from the literature, the model is also shown to be applicable to the liberation of sulfide minerals out of ores.

Jan 1, 1987

By C. S. Ek

Tests have been performed to recover silver and lead from residues produced after a super-hot leaching in a zinc hydrometallurgical plant operating with jarosite precipitation. When this residue is leached in ammoniaammonium sulfate or in diethylenetriamine solutions, lead dissolution is not complete and its recovery from the aqueous solutions is either difficult, due to the operating conditions, either expensive due to the amount of added reagents. In both cases, silver is partly dissolved, partly left in a new residue still containing lead and baryum sulfates. The best treatment seems to include a selective flotation producing first a silver concentrate assaying about I % Ag, then a 50 % lead concentrate collecting the baryum salts, and a final quartz-gypsum tailing. Metal recoveries can reach 50 % and 80 %, respectively.

Jan 1, 1989

By E G. Prado

We have confirmed on bench scale the removal of chlorides and alkalies (+95%) and over 2/3 of the zinc, lead and cadmium from EAF dusts. This has been achieved with arrononium acetate solutions alone, or with combinations of water wash, amonia-ammonium carbonate and ammonium acetate solutions. Also confirmed are the process routes for the recovery of the aforementioned elements into marketable products. The technology involves the complete recycling of the reagents. The FAF residue is returned to the electric furnace without risk of impurities buildup. Commercial scale testing with the recycled dust was satisfactory, including quality of the slag and its behavior during the melting stage. A cursory feasibility evaluation is presented.