Search Documents

By R. J. Sherman, M. R. Achter

IT has often been reported that coatings may strengthen single crystals and polycrystalline specimens of coarse grain size. This note reports the effect of a surface layer of fine grains on the creep-rupture properties of coarse grained nickel 99.8 pct pure. Sheet specimens were machined from cold-rolled material, finished by surface grinding and annealed at 1230°C in vacuum for 4 hr. Half of them were re-ground on faces and sides and annealed at 925"C for 1 1/4 hr. The double grind-anneal treatment produced a structure consisting of a surface layer of fine grains of 0.02 mm diam on a coarse-grained substrate of grains of 0.40 mm diam. Comparison with specimens which received only the single grind showed that the second grind-anneal did not alter the structure of the substrate. Several modifications were made in specimen design to eliminate erratic rupture behavior outside of the gage length. In the final design the gage section, oriented parallel to the rolling direction, was 1.00 in. long, 0.4 in. wide, and 0.0625 in. thick. End tabs were pinned in place. Although other configurations (welded end tabs, transverse orientation, and wider gage section) showed similar effects of a layer of fine grains, because of the erratic rupture behavior, only the data from the final design are reported here. Creep tests were performed at 650°C in air and in a vacuum of 10~5 mm Hg. Creep rates were measured from the movements of the lever arm. Since the broken sheet specimens could not be fitted together, elongations at fracture measured by means of gage marks, do not include the necked portions adjacent to the fracture. Results of the creep tests with and without the fine grained surface are given in Table I. An explanation for the lower strength in air than in vacuum has been proposed previously in terms of the reduction of crack propagation energy by gas adsorption.l In both environments the fine-grained layer produced a small decrease in minimum creep rate and, except for the shortest test in air, a substantial increase in rupture life. The elongation values at rupture, as they are measured here, do not demonstrate an appreciable effect of the grain structure but do show much smaller ductilities in air than in vacuum. Greater elongations maybe associated with the finegrained layer, however, especially in vacuum, in creep curves such as those in Fig. 1. Duplicate tests were not run to determine the re-producibility of the data. It is felt, however, that, in view of the consistent behavior, the prolongation of rupture life may be attributed to the effect of the fine-grained surface. In the data not reported be-

Jan 1, 1962

By Milton F. Goodrich

The idea of using water-only cyclones to scalp clean coal from the feed to other devices has recently been gaining in popularity. 1,2,6 An indication of this popularity is that water-only cyclone scalping is already employed in a few commercial plants. Water-only cyclones scalp the feed to a heavy media vessel in the Warwick plant,3 to Deister tables in the Rowland plant,4 and to a heavy media cyclone circuit in the Amherst Coal Company's McGregor plant.5 Despite this trend, we found surprisingly little information in the literature on the performance of water-only cyclone scalping. Therefore, we undertook a study of its technical merits, limiting our investigation to a water-only cyclone scalper in conjunction with heavy-media cyclones. We felt this to be a reasonable combination of equipment, since both processes operate well on the same size coal. First, we developed simple mathematical relationships revealing general characteristics of the system. Next, we compared the clean coal yield and quality obtainable by the system on four different coals with that obtainable by heavymedia cyclone circuit alone and water-only cyclones middlings recirculation circuit alone. This was done by using computer program to simulate the operation of the three systems. Finally, we considered the effect that implementation of the system would have on a typical preparation plant circuit. The System The system chosen for study [(shown schematically in Fig. 1)] comprises two stages: a primary stage (PI) consisting of water-only cyclones, and a secondary stage (P2) consisting of heavy media cyclones. The water-only cyclones separate raw coal at a low specific gravity, producing a relatively small amount of high quality clean coal and a refuse containing much good coal. This refuse is then recleaned in the secondary stage, where the sharper separation of heavy media cyclones, operated at a higher specific gravity, reclaims additional clean coal. Finally, the clean coal from both stages is combined as the system's clean coal, while the refuse from the secondary stage becomes the system's refuse output. Theoretical Analysis Two assumptions lie behind the following theoretical analysis. The first assumption is that partition curves can represent not only the performance of each stage but also the performance of the system as a whole. These curves show partition number as a function of specific gravity, where partition number is either the percent or fraction of a raw coal with a given specific gravity reporting to clean coal. The second assumption is that these curves are independent of the raw coal characteristics. At any specific gravity the system's partition number is solely a function of the partition numbers of each stage. For convenience, we use the following variables in describing this relationship: g = specific gravity, PS(g) = the partition number of the system at specific gravity g, P1(g) = the partition number of the primary stage at specific gravity g, P2(g) = the partition number of the secondary stage at a specific gravity g. For this system, we can show algebraically that the relationship is: [Ps (g) = PI (g) + (1- P1(g)) P2 (9)(1)] With this equation the system's partition curve can be determined if the partition curves of each stage are known. By definition, the partition numbers P1(g) and P2(g) must each be less than, or equal to, one. Placing these constraints on Eq. (1), we arrive at the relations: [Ps(g) % P1(g) and Ps(g) % P2(g)(2)] Thus, at any specific gravity the system's partition number is always greater than that of both stages. [Figure 2] shows typical partition curves. Curve I represents the primary stage, which consists of water-only cyclones operating at a separating gravity of 1.3. (The separating gravity or the

Jan 1, 1979

By Robert J. Linney

In the latter part of the year 1943, it was decided to experiment with diamond-drill blast holes in the Old Bed magnetite mine at the Mineville mines of the Republic Steel Corporation, in sections of the ore body where vertical dimensions were large and where development for sublevel bench stopes had already been done. Other possibilities of application for this drilling method were in the reclamation of old floors and pillars in the pitching folds of the Lower Old Bed ore body and in the reclamation of large vertical pillars in the "21" Bonanza-Joker ore body. The cross sections and views of the two ore bodies will show the conditions to which the diamond-drill method has been applied. The Lower Old Bed magnetite ore body is lenticular and dips approximately 30° toward the southwest and strikes generally southeast and northwest. An intensely folded structure, which pitches generally on an axis approximately at right angles to the strike, is continuous from the uppermost old workings down to the present bottom of the mine, and probably continues with depth. On successively lower levels this folded structure becomes greater in vertical dimensions and the two folds are closer together in a horizontal dimension. As shown in Fig. I, this folded structure gives to parts of the ore body considerable vertical dimensions, which provide areas that were developed for sublevel bench stoping above a slushing drift, as shown in Fig. 2. It was in one of these previously devel-oped sublevel bench stopes, No. 26 on the 1185-ft. level, that the diamond-drill blast-hole method was applied for mining the upper sublevel. The lower sublevel was underhand-bench-drilled to the finger raises of the scram drift below. The roof of this stoping area began to break and spall on the lower sublevel, causing the roof to become inclined. Along the hanging wall of the stope this reached an elevation about half way between the two sublevels. A smooth schistose seam in the hanging wall causes the ore to break away freely. Therefore, if bench mining had been carried on in the upper sublevel, a dangerous condition of poorly supported benches would have resulted. When the drillers were slashing across the sublevel te footwall and hanging wall to make a bench, spdlling roof of the opening below would probably have carried away part of the bench, and would have left a dangerous place in which to continue underhand benching. A 6 by 8-ft. raise had been driven between the lower stope and the upper sublevel about 200 ft. from a manway. It was decided to use this raise for a starting cut and to arrange holes as shown in Fig 3, so that a slot would be opened across the ore body between the footwall and hanging wall. This slot would then be used for the purpose of breaking into the ore, by blasting vertical rings of holes drilled at right angles to the axis of the pitching folds as nearly as possible. Layouts of this slot drilling and the rings adjacent are

Jan 1, 1946

By Robert J. Linney

IN the latter part of the year 1943, it was decided to experiment with diamond-drill blast holes in the Old Bed magnetite mine at the Mineville mines of the Republic Steel Corporation, in sections of the ore body where vertical dimensions were large and where development for sublevel bench stopes had already been done. Other possibilities of application for this drilling method were in the reclamation of old floors and pillars in the pitching folds of the Lower Old Bed ore body and in the reclamation of large vertical pillars in the " 21 " Bonanza-Joker ore body. The cross sections and views of the two ore bodies will show the conditions to which the diamond-drill method has been applied. The Lower Old Bed magnetite ore body is lenticular and dips approximately 30° toward the southwest and strikes generally southeast and northwest. An intensely folded structure, which pitches generally on an axis approximately at right angles to the strike, is continuous from the uppermost old workings down to the present bottom of the mine, and probably continues with depth. On successively lower levels this folded structure becomes greater in vertical dimensions and the two folds are closer together in a horizontal dimension. As shown in Fig. 1, this folded structure gives to parts of the ore body considerable vertical dimensions, which provide areas that were developed for sublevel bench stoping above a slushing drift, as shown in Fig. 2. It was in one of these previously developed sublevel bench stopes, No. 26 on the 1185-ft. level, that the diamond-drill blast-hole method was applied for mining the upper sublevel. The lower sublevel was underhand-bench-drilled to the finger raises of the scram drift below. The roof of this stoping area began to break and spall on the lower sublevel, causing the roof to become inclined. Along the hanging wall of the stope this reached an elevation about half way between the two sublevels. A smooth schistose seam in the hanging wall causes the ore to break away freely. Therefore, if bench mining had been carried on in the upper sublevel, a dangerous condition of poorly supported benches would have resulted. When the drillers were slashing across the sublevel to footwall and hanging wall to make a bench, spalling roof of the opening below would probably have carried away part of the bench, and would have left a dangerous place in which to continue underhand benching. A 6 by 8-ft. raise had been driven between the lower stope and the upper sublevel about 200 ft. from a manway. It was decided to use this raise for a starting cut and to arrange holes as shown in Fig. 3, so that a slot would be opened across the ore body between the footwall and hanging wall. This slot would then be used for the purpose of breaking into the ore; by blasting vertical rings of holes drilled at right angles to the axis of the pitching folds as nearly as possible. Layouts of this slot drilling and the rings adjacent are

Jan 1, 1945

By Jacques Steininger, Robert E. England

Single crystals of ZnTe and ZnTe1-,Sex with x up to 0.13 have been grown from the elements by temperature gradient solution zoning using excess tellurium as a solvent. Best results have been obtained with charges with the compositions 45/55 at. pct Zn, Te, for ZnTe and increasing amounts of selenium for ZnTe1-xSex. The temperature in the molten zone was maintained at about 1070°C with a gradient of about 10°C per cm. Chemical analyses of quenched ZnTe ingots show tellurium concentrations in the molten zone as high as 70 pct with concentration differences across the zone of 1 to 2 at. pct Dark dots which are observed by transmitted light microscopy in as-grown crystals can be removed by annealing in zinc vapor at 900 C. INTEREST in wide band gap semiconductors has led to a new study of ZnTe and ZnTel-xSex crystal growth. ZnTe is the only II-VI compound with a wide band gap (2.3 ev) that can be made p type with low resistivity. Attempts to make it n type with low enough resistivity to be useful for p-n junctions have so far been unsuccessful.1 ZnSe has a band gap of 2.65 ev but can be made n type only. However, ZnTel-xSex solid solutions with x as low as 0.36 have been made both highly n and p type2 with a minimum band gap around 2.12 ev3 at room temperature and appear to hold the best promise for efficient injection electroluminescence in the visible. ZnTe has the lowest melting point of the zinc chal-cogenides (1295°C) and consequently attempts have been made to grow crystals from both the liquid and the vapor phase.4 Complicated apparatus is required for growth from stoichiometric melts because of the high vapor pressures of the elements at the melting point of ZnTe and because of the problem of quartz devitrification. Small crystals have thus been grown in high-pressure equipment by Fischer5 and by Narita et a1.6 with pressures of the order of 50 atm of argon to prevent excessive evaporation from the melt. Large crystals of ZnTe can be obtained by growth from the vapor phase4 but they often present numerous dislocations and inclusions. An improvement in the quality of vapor- grown ZnTe crystals was reported by Albers and Aten7 by equilibration of mixtures of small crystals with compositions lying on either side of the solid single-phase field at fixed temperature. The same technique was later applied by Aten8 to the growth of ZnTe1-xSex crystals with less than 1 pct inhomo-geneity. Because of the higher liquidus temperatures of the solid solutions and the high vapor pressure of selenium, previous attempts to grow ZnTel-xSex from the melt have been limited and unsuccessful.9 The phase diagram of the Zn- Te system is reproduced in Fig. 1, based on data from Kobayashi10 and Kulwicki.11 Carides and Fishher12 have reported lower liquidus temperatures on the tellurium-rich side, but their data would require confirmation. The liquidus temperature on the tellurium-rich side decreases rapidly with increasing tellurium concentration and the Te2 vapor pressure over the liquidus also decreases accordingly.'3 The decrease in liquidus temperature and vapor pressure therefore makes it possible to use conventional apparatus if there is a sufficient excess of tellurium in the melt. Single crystals of ZnTe have thus been grown by Kucza,14 in a modified Bridgman technique, from solutions containing up to 60 at. pct of Te by lowering unsupported quartz ampoules through a temperature gradient at about 1200°C. Under these conditions, the phase diagram indicates that the entire charge is initially molten. Crystal growth can therefore proceed by normal freezing and rejection of excess tellurium into the melt. The modified Bridgman technique has several major limitations. Because of the rejection of excess tellurium into the melt during freezing, the melt composition and the temperature at the growth interface vary continuously. They tend to follow the liquidus until the eutectic which is very close to pure tellurium (447°C, >99 pct Te). Since the solidus composition also varies with temperature,15 crystals grown by this method are inhomogeneous. They present small variations from stoichiometry which may affect their structure and physical properties. The simultaneous increase in tellurium content and decrease in melt temperature also combine to reduce the rate of diffusion of tellurium away from the growth interface, thereby causing constitutional supercooling and possibly dendritic growth. To minimize these effects, the initial melt composition is in practice kept relatively close to stoichiometry (less than 60 pct Te). This however limits the possibilities of operating at low temperatures and pressures. This paper describes a modified method of crystal growth by temperature gradient solution zoning (TGSZ) which is an adaptation of the temperature gradient zone-melting technique developed by pfann16 and of the traveling solvent method of Mlavsky and weinstein.I7 The TGSZ method now applied to the growth of ZnTe and ZnTel-xSex crystals is characterized by its very simple experimental arrangement and sample preparation technique. Unlike the modified Bridgman technique, there is no increase in the tellurium concentration in the melt and therefore it is possible to operate at lower temperatures and pressures. This method is also suitable for maintaining a constant temperature at the growth interface.

Jan 1, 1969

By John Dasher

Extrapolation is a useful technique, but it can be overdone. Seldom is it justified to study over a range of 1 to 6 and extrapolate the results to 150,000. It is especially dangerous if the extrapolation is based on a false assumption. The authors assume settlers scale-up by residence time rather than by area, admit their result (a settler depth of 7 m) is "unreasonable" and suggest longer, wider, shallower settlers might be better. Various authors have noted for a copper-LIX system a total flow basis of 2 gpm per sq ft for sizing settlers. The results of this are compared with those in the paper in [Table 7]. The authors note that flooding of their settlers was never approached. Thus the smallest unit calculated is understandably twice too big. The largest however, is 5% of the required size. I note that the figures in [Table 6] for 1/min/cm2 are based on plan area rather than cross section as titled and are wrong by l0 4. A flow of 2050 1/min/cm2 is about Mach I. It is also 10 5/3 or 46.5 times that of the little one, although the abstract says the design was based on constant flow rate per unit cross section.

Jan 1, 1977

By J. A. Botin, K. H. Singh

INTRODUCTION The Alfredo underground mine is one of the three mining operations of Rio Tinto Minera, S.A., all near the community of Rio Tinto in Huelva province of southwest Spain. The other two operations are Corta Atalaya open pit (Pyrite ore) and Cerro Colorado open pit (Copper ore 1. Underground mining of Alfredo Mine for pyrites started in the nineteenth century and continued without interruption until 1979 when it was discontinued due to economical reasons. In 1972, a new project was started for the mining of copper bearing ores on the footwall of the pyrite deposit. This copper ore is locally named “Cloritas” and it forms a nearly vertical and tabular shaped orebody which forms an envelope at the footwall of the San Dionisio pyrite orebody. Mining of the Cloritas commenced in 1975 using cut and fill stoping. In 1977, the original project was completely revised which led to the introduction of a bulk mining system to achieve a planned production of 3,000 tonnes of ore per day. This paper covers the economic and planning aspects of the mine and discusses the evolution of the mining method for the Cloritas orebody. A GENERAL DESCRIPTION OF THE CLORITAS OREBODY The “Masa San Dionisio” (figure 1 ) is a massive sulphide orebody located in the town of Rio Tinto, about 90 kilometres west of Sevilla, Spain. Extensive vein-type sulphide mineralization exists in the volcanic host rocks of the Masa San Dionisio. Within this area of stockwork veins, there is a higher concentration of copper in the form of chalcopyrite in a zone adjacent to and paralleling the contact with the massive sulphides. This copper envelope is locally referred to as the "Cloritas Orebody” and the ore within it is called "Cloritas”. The main zone of the Cloritas orebody, (figure 11, is tabular and nearly vertical having a length of 375-400 m east-west, a thickness of 20-50 m north-south, and a vertical extension of 500 m from the surface. In addition to this area, there is a second less important low grade area called zone 2A located to the north of the main zone below 26 Level which, in some sections, is not fully separated from the main zone. MINING METHODS Mining in Rio Tinto area can be traced back to the Phoenecians and the Romans. Modern day mining started with the demand for sulphuric acid during the last half of the nineteenth century. By 1971, more than 33 million tonnes of pyrite had been mined out of Alfredo Mine, (San Dionisio Orebody), using labor intensive drift and fill methods and also by open pit method. During the last decade, underground mining of the pyrite had become uneconomic due to lower prices and a slackening demand for pyrite, and the underground mining operations for pyrite were finally stopped in 1979. In 1971, a major change in the long range mining plans for Masa San Dionisio was established. Between 1971 and 1975, underground mining of pyrites was progressively reduced while open pit extraction was increased in

Jan 1, 1981

By H. E. Elliott, R. S. Busk, A. T. Peters

ONE of the problems of the fabricator of metals and alloys is the propensity of some composition ranges toward abnormal grain growth during certain stages of fabrication. In this respect magnesium alloys are no exception among alloys. Fortunately, convenient foundry control methods have been developed by which the abnormal grain growth possible in certain magnesium-alloy castings can be suppressed. An unusual characteristic of magnesium alloys, however, is that castings of some composition ranges are subject to local grain growth during heat-treatment without the necessity of intentional mechanical stressing of the part prior to heat-treatment. This effect occurs only under certain critical casting conditions, and only in certain alloys of greater than about 8.5 per cent aluminum content, such as C alloy (Mg, o per cent Al, 2 per cent Zn, 0.2 per cent Mn) and G alloy (Mg, i0 per cent Al, 0.2 per cent Mn). The first observation of this phenomenon in cast magnesium alloys occasioned much surprise, since it is not observed in other metals. Jeffries and Archer' have stated that "the grain size of cast metals, provided they have not been plastically deformed, cannot be changed by heating below the melting point." The study of the conditions leading to abnormal grain growth in cast magnesium alloys, and of the mechanism of this phenomenon, has led to some very interesting observations. Perhaps the most significant of these was the observation that stresses originating from cooling contraction in magnesium-alloy castings are the only stresses necessary, under certain conditions, to cause local recrystallization and subsequent grain growth in the casting during heat-treatment. of abnormal local grain growth was a definite problem in the production foundry on C alloy sand castings. Illustrated (Fig. r) is a picture of a casting scrapped because of this defect. A mottled effect is produced in coarse-grained areas by suitable etching solutions. The properties of metal in the affected area are much impaired by such grain coarsening. Ultimate tensile strengths of half the normal value have been measured in metal of this nature. In this paper are described the techniques that have been developed by The Dow Chemical Co. for studying, and in large measure solving, this production problem. Also discussed are studies of the mechanism by which excessive grain coarsening occurs, and the fundamental conditions that produce this effect. The abnormal grain growth discussed in this paper will be referred to as "germination," since this term has been defined' as any process leading to an abnormally coarse grain size. This paper deals only with abnormal local grain growth that may occur during the solution heat-treatment of certain magnesium-alloy castings, as dis-

Jan 1, 1945

By M. S. Abrahams

Germanium has been rolled in the temperature range of 700o to 800°C. The thickness has been decreased by as much as a factor of four, from a thickness of 0.032 in. to a thickness of 0.008 in. For deformations below 60 pet, the true strain per pass is found to be a constant; from the temperature dependence of this slope, an activation energy of about 2.5 ev is obtained. This energy agrees with that for dislocation climb in germanium . For reductions greater than 60 pet, complete rings are seen in the Lave photographs, new grains are observed in the microstructure, considerable softening occurs, and the hole mobility is very low. This evidence indicates that the recrystallization of gertnanium has occurred. GERMANIUM has been deformed in many ways1 including tension, compression, torsion, and bending since Gallagher2 first described its plastic nature at elevated temperatures. All of these studies indicate that the glide plane in germanium is (111) and that the glide direction is (110). Rolled germanium specimens were used by Kolm, Warekois, and Kulin3 in their X-ray study of deformed semiconductors, but no information is given on the rolling itself. The present experiments deal with the rolling of germanium at various temperatures and for different orientations. In all previous deformation studies, the phenomenon of recrystallization (i.e., the transformation of a single crystal into a polycrystal) in germanium has not been observed4 despite relatively large deformations at elevated temperatures. The proposed reason4 for this was that sufficient energy could not be stored in the deformed germanium lattice. In contrast to the earlier studies this work will present evidence indicating that recrystallization occurs in germanium during rolling at an elevated temperature. I) EXPERIMENTAL PROCEDURE A) Test Specimens. The samples used for rolling were in the form of rectangular parallelepipeds measuring 0.3 in. long, 0.06 in. wide, and 0.035 in. high. They were cut from an undoped single-crystal ingot of p-type germanium with a resistivity of 24.4 ohm-cm, a Hall mobility of 2300 sq cm v-' sec-l, and a hole concentration of 1.1 x 1014 cm"3 at room temperature. The surfaces of the specimens were metallographically polished prior to rolling. The initial dislocation density of the samples was about 10' cm-' as determined by etching in CP4. Two different specimen orientations were used. In the first case, the direction of rolling was parallel to (251), the surfaces in contact with the rolls were of the form (1021, and the normal to the third face was parallel to (211). The corresponding di-

Jan 1, 1964

By P. M. Robinson, M. B. Beaer

The heat of formation at 0°C of the intermetallic compound AgMg as a function of composition has been determined by tin-solution calorimetry. In this technique, the heat of formation is determined as the difference in the heat effects, at infinite dilution, on dissolution of the compound and a mixture of its components added alternately to liquid tin from a reference temperature, such as 0°C. The experimental technique and method of calculation have been described elsewhere.' The compound AgMg is a 0 electron compound with a CsCl structure.2 In nonstoichiometric compositions of the compound, atoms of the excess component are substituted on the AgMg lattice.3,4 The homogeneity range is approximately 43 to 52 at. pct Mg at room temperature and 38 to 65 at. pct Mg at 500Oc.2 Single-phase alloys outside the homogeneity range at room temperature can be prepared by quenching. The specimens used in this investigation contained from 39.0 to 54.8 at. pct Mg. They were made available, together with analyses, by the Research Laboratory of the General Electric Co. Metallographic examination of the quenched specimens containing 39.0 and 54.8 at. pct Mg gave no indication of the presence of a precipitated phase. The measured heats of formation are listed in Table I. In a calorimetric run, four to six additions each of a specimen and the corresponding mixture of the components were made. One or two calorimetric runs were carried out with each composition depending on the amount of samples available. The limits stated in the table represent the experimental precision and not the absolute accuracy of the measurements. Thermodynamic investigations of the compound AgMg have been made by Trzebiatowski and Terpilowski 5 and Kachi.6,7 The heats of formation at 500°C derived from the combined electromotive-force values of these investigators8 are more exothermic than the heats of formation at 0°C reported here, Fig. 1. The differences cannot be explained by the difference in temperature. This is shown by the published heat capacity of the stoichiometric compound, which obeys the Kopp-Neumann rule from 0" to 500oC.9 The heats of formation derived from equilibrium data are generally considered to be less accurate than those determined by calorimetric methods because small errors in the change of the equilibrium values with temperature have a large effect on the calculated value of the heat of formation. The heats of formation derived from the combined published electromotive-force values reach a maximum at 56.0 at. pct Mg.8 Kachi reports a maximum of -4.7 kcal per g-atom at the stoichiometric composition.7 The present results also indicate a maximum at or near the stoichio metric composition, Fig. 1.

Jan 1, 1964

By H. E. Rowen

As high grade iron ore deposits dwindle and costs rise, sintering becomes more and more important. The steel industry is now faced with beneficiation problems once peculiar to nonferrous work. Succeeding articles describe recent advances in this field. Here is presented the first chapter of a history still being written. SINTERING, for the purpose of this discussion, is defined as the art of burning a solid fuel with 90 to 95 pct ash content. Considering problems of combustion involved in keeping a home furnace burning properly with 12 to 20 pct ash in the fuel, it is evident that combustion represented by the definition has to be right or nothing is going to happen. Our forefathers discovered that many ores containing metals essential to the steadily rising standards of living were associated with elements such as sulfur and arsenic, which had to be removed before refining. This they did by utilizing the solid fuels they had available-the sulfur or other readily combustible components-to create roasting heat. One of the early methods is demonstrated in an old woodcut of the roast heap, Fig. 2. Ore was broken into chunks, piled on an ignition layer of solid fuel-logs in this case-and then. ignited. The sulfide ores roasted as the sulfur burned out. As shown in the background, the countryside was rapidly denuded of all vegetation by the great quantities of SO2 and other liberated gases.

Jan 1, 1961

By E. A. Wieselmann

This chapter presents a successful approach for achieving mine entry stability at the Cane Creek potash mine by the utilization of closure measurements. The mine is located in southeastern Utah (Fig. l). Mining is being conducted at depths in excess of 3000 ft under structurally complex geologic conditions typical of the Paradox salt basin. The closure measurement systems described have definite application for determining relative entry stability in other nonelastic rocks which are similar in behavior to potash. Similar types of closure measurements have been taken in various underground openings throughout the United States, Canada, arid Europe. Application of this closure data has previously met with varying degrees of success as a tool for design of under- ground openings in both elastic and nonelastic media.1-32 Closure measurements can be made easily and economically and they provide a practical solutiori to a practical problem. They are in-situ measurements which do not necessarily require laboratory correlation. Simple closure measurements have special significance in potash because "steady-state" ' closure rate, or creep, of the entries is measured. These closure rates can be utilized because nonelastic media such as potash will never achieve absolute stability around a mine entry. The potash will tend to creep or deform until all entries are closed and the overburden stress is redistributed over what was previously the mine area. The time for this ultimate effect to occur is dependent on a number of mining and geologic variables. Percentage of mine extraction, mining

Jan 1, 1972

The Engineers Society of Western Pennsylvania, William Penn Hotel, Pittsburgh, Pa. K. F. Treschow, Secretary Since 1880 this society has been publishing Proceedings containing papers on a wide variety of engineering and related subjects The Proceedings are issued monthly throughout the year (except for the months of August and September each year) and the monthly Proceedings from February of one year to and including January of the next are also collected in volumes The latest is vol 47, for 1931 The rate of subscription for the monthly Proceedings is $5 per year throughout the Postal Union, single copies (monthly), 50 cents each The price of the yearly volumes from vol 17 to date is $5 each, unbound. The Secretary will quote prices for

Jan 1, 1933

By Henri V. Reibell

Deep open pit optimization supposes very long and sedious calculations in order to assign the best shape of the pit and the best bottom level, which will give the biggest profit. Computers give the possibility to make these calculations. More over, they allow to multiply trial calculations so that it is possible to obtain more reliable results. The paper does not expose the computer program but only the way in which mining engineers can use it.

Jan 1, 1969

By K. P. Gupta

In ternary systems containing silicon and transition elements, silicon was found to stabilize the a phase.1 At 1000°C a broad a-phase region was found in the Cr-Mn-Si system,1 which extends very close to the Mn-Si binary line (within about 3 at. pct Cr). Later investigation showed that, if chromium was replaced by small amounts (3 to 5 at. pct) of v,1 Ti, Nb, Ta, Mo, or w,1 the a phase or the R phase was again stabilized. Whether stabilization of complex crystal structures is possible by small additions of iron, cobalt, or nickel to Mn-Si is not known. Investigation of the Co-Mn-Si system4 shows the presence of several ternary phases, but at cobalt concentrations higher than 10 at. pct. In the present work the ternary systems Fe-Mn-Si and Co-Mn-Si were investigated at low iron and cobalt concentrations (< 7 at. pct Fe or Co) in search of phases of complex crystal structure. Experimental Procedure. The alloys were pre-pared by induction melting Co (99.8 pct), Si (99.9 pct), electrolytic Fe (99.88 pct), and Mn (99.9 pct) in recrystallized alumina crucibles under an inert atmosphere of argon gas. The alloy specimens were wrapped in molybdenum foil, sealed in argon-filled (at 1/2 atm) silica capsules and annealed for 72 hr at 1000" 1°C, and water-quenched. The use of argon-filled capsules was found to reduce the losses during annealing and the molybdenum foil prevented reaction of the manganese with silica. The total weight loss due to annealing and melting was found to be less than 1 pct for each alloy. The alloys were not analyzed chemically. A part of each annealed specimen was polished and examined metal-lographically using etching solutions, a) 0.1 to 0.5 pct oxalic acid solution in water, or b) 0.5 pct HNOs in methyl alcohol. Even though the etching solutions were quite dilute, the specimens were heavily etched and stained if the etching time exceeded more than 5 sec. Etching times found suitable were usually 1 to 3 sec. For X-ray diffraction work, a part of each annealed specimen was powdered by crushing after the exposed surface was ground off. X-ray diffraction patterns were taken with powder specimens using a 20-cm-diam asymmetrical focusing camera and Fe K radiation. These powder patterns were found quite satisfactory for the purpose of phase identification. However, X-ray diffraction patterns of single-phase alloy powder specimens were also taken using a Siemens diffractometer and filtered Cr-Ka radiation for greater resolution of the diffraction lines. Results and Discussion. In the Fe-Mn-Si system a new ternary phase was found at 1000°C between the p manganese and the MnsSi phase regions. The approximate phase relationships in this region of the 1000°C isothermal section are shown in Fig. 1. The new ternary phase, designated as the K phase, was found to occupy a narrow region about 1 at. pct in width and extending from Fee.oMn74.5Silg.5 to Fe.Mn.Silg.. At the high-iron content region, the K phase was found in equilibrium with the p manganese and the MnsSi phases but, at the low-iron content end of the K-phase region, the phases in equilibrium with the K phase were the p manganese phase, the MnsSi phase, and another new phase, designated in Fig. 1 as the v phase. The v

Jan 1, 1964

By J. T. Norton, H. Blumenthal, S. J. Sindeband

The interstitial phases formed by the transition elements with carbon, nitrogen and boron constitute a unique class of substances which are of considerable technical interest because of their well developed metallic properties and their high hardness and melting points. They are also of interest from the point of view of structure. It was pointed out by Hagg1 some years ago that the principal factor determining these structures was the relative sizes of metal and metalloid atoms. He predicted that if the ratio of the radii of metalloid to metal atoms was less than 0.59, the metal atoms would be arranged in a close-packed fashion of relatively simple type. This prediction has been amply confirmed. It appears, however, that this specification applies most generally to those structures in which the metalloid atoms occupy isolated positions in the lattice and there is no tendency for strong binding between the metalloid atoms themselves. The series of borides of the type MeB2 formed from the transition elements of the fourth (Ti, Zr) and fifth (V, Cb, Ta) groups of the periodic table provide an opportunity to investigate this situation further. If one takes as a basis the radius of 0.87 A for the boron radius and the Goldschmidt values for the metal atoms in 12 coordination, then the radius ratio varies from 0.54 for zirconium to 0.64 for vanadium, which latter is considerably greater than Hagg&apos;s limit of 0.59. It was of interest, therefore, to see if these five elements would form borides of the MeB2 type and have simple isomorphous structures. When this investigation was initiated, relatively little information had been published on the structure of this group of borides. McKenna2 reported the preparation of ZrB2 by a carbon reduction process. Its structure was hexagonal and the approximate lattice constants were given as a = 3.15 A, c = 3.53 A. Ehrlich3 reported the structure of TiB2 as being of the C 32 type with a = 3.02, c = 3.21 and c/a = 1.06 A. Recently, Kiessling4 published the results on ZrB2, showing it to be one in which the metal atoms are arranged in a simple hexagonal lattice with the boron atoms in flat sheets, midway between the layers of metal atoms. The structure is C 32 type with a = 3.169, c = 3.530 and an axial ratio =1.11 A. He also states that CbB2 and TaB2 are isomorphous with ZrB2. Preparation of Borides The borides of titanium, zirconium, columbium and tantalum were made by the electrolysis of fused salt baths after the method described by Andrieux.5 The bath, totalling about 6500 g in each case had the following general composition: Metal Oxide + B2O3 + CaO + CaF2. The actual proportions of the ingredients were determined for each individual case. Although Andrieux reports the preparation of vanadium boride by the same electrolytic method, several attempts proved unsuccessful. However, it was possible to prepare VB2 by the carbon reduction method used by McKenna to produce ZrB2. The mixture consisted of V2O5 + 6B2O3 + 11C and the reduction was carried out in an induction heated graphite crucible. This method proved satisfactory for ZrB2 and TiB2 and undoubtedly the others could be made in the same way. The borides, which were all in the form of fine gray metallic crystals from the electrolytic bath or gray powders from the reduction process, were carefully separated from other constituents and analyzed chemically for metal and boron content. The densities of the boride powders were measured using a standard 10 cc pyenometer at 18°C and ethyl benzene proved to be the most satisfactory liquid for this purpose. X Ray Technique The boride crystals, as prepared, were too small for single crystal examination so that powder techniques were employed. Patterns of the finely ground borides were prepared, using the Norelco recording X ray spectrometer. The lines on these patterns were indexed with the aid of Hull-Davy charts and the approximate dimensions

Jan 1, 1950

By J. W. Spretnak, V. Kandarpa, G. W. Powell, R. A. Erickson

Neutron-diffraction pattens were obtained at room temperature from two austenitic manganese steels, oxc wth n carbon content of 1.23 zct PC/ and the olher 0.63 wt pct. Analysis of the data showed that the curOan atols (ions) occupy tile octaheadral site. any of the cavbon is in the tetahedral site, tile concentration is too strzall lo be detecled by tzeulr-on d$facton. AS part of a long-range investigation of eutectoid decomposition, a study of the structure of austenite has been undertaken in order to characterize as best as possible the parent phase in the Fe-C system. Austenite is a solid solution of carbon atoms in fcc iron, the carbon atoms being located in interstitial positions. Of the two kinds of interstitial sites, octahedral (0, +, +) and tetrahedral (4, a, $), in this lattice, the larger octahedral sites are usually considered as the probable position of carbon. The strain energy involved in pytting a neutral carbon atom (covalent di; ameter 1.54)&apos; into a tetrahedral site (diameter 0.56A) is considerably greater than that associated with p2tting carbon into the octahedral site (diameter 1.08A). Dayal and arkeen&apos; observed the migration of carbon in iron under the influence of an electric field indicating tha tye carbon is ionized. pe ionic radius of C&apos;4 is 0.15A and that of C" is 0.29. Consequently, it is conceivable that carbon ions could occupy the tetrahedral sites if one considers only the strain energy. Size considerations alone do not provide a complete explanation for the formation of the interstitial solid solutions, however. because metals such as copper, zinc, and cadmium do not appear to form interstitial solid solutions in spite of their large interstitial sites. Evidence which suggests partial ioni-zation of the carbon in austenite has also been obtained by Speiser, Spretnak, and alor who derived formu- lae relating the observed change in lattice parameter to the effective diameter of the solute atom. Assuming the carbon occupies the octahedral site. they computed the effective diameter of carbon to be 1.33A whereas the covalent diameter is 1.54A. petch5 concluded from powder X-ray diffraction experiments that carbon atoms occupy the octahedral sites. His conclusion was based on the general trend observed in the intensity of the diffraction lines as the carbon content of the austenite was increased. However, the major difficulty associated with application of X-ray diffraction to this particular problem is the relatively poor scattering power of carbon. Williamson and smallman&apos; utilized X-ray diffraction to study the line broadening caused by the strain field about carbon atoms inferrite: these investigators concluded that at least 85 pct of the carbon in ferrite occupies the octahedral (0: 3, B) site rather than the larger

Jan 1, 1967

By C. L. Magee, H. W. Paxton

PREVIOUS workersl&apos;% ave found that as-quenched ferrous martensites can be plastically deformed at low stresses. They have also found that the stress to obtain small strains can be significantly increased by aging at temperatures up to 150°C. This behavior has been interpreted in two ways: 1) that the deformation at low applied stress is due to internal stresses and thus the aging phenomenon is due to relaxation of the internal stresses;&apos; 2) that the microdeformation arises through the motion of unpinned dislocations and the aging process is the diffusion of carbon to the dislocations to pin them.293 In a recent paper,4 we have shown that under certain conditions the dominant microdeformation mechanism of as-quenched Fe-31Ni marten-site-austenite aggregates is the transformation of retained austenite. Our results on resistance changes during deformation and temperature dependence of the deformation also established that, at temperatures above 300° K, the microdeformation was not due to this transformation. The purpose of this note is to report results of experiments which indicate that explanation 1 is appropriate for this deformation. All results presented here are from conditions where transformation does not make a measurable contribution to the microplastic deformation, in Fe-31Ni-0.002C, or in Fe-29Ni-0.02C-0.25Ti. The experimental techniques that were used for measurement of the plastic deformation are described4 and analyzed5 elsewhere. Fig. 1 shows the microplastic response of 100 pct austenite at 300" and 350° K. The microplastic response of an austenite-martensite aggregate is also given in Fig. 1 and it is seen that, after formation of martensite, the initial plastic deformation occurs at lower stresses. Thus, the softness is not entirely due to retained austenite—the quenched structure can be deformed at lower stresses despite the fact that the macroscopic strength is significantly higher. A result which allows a distinction to be drawn between the alternative explanations for this behavior is derived from aging experiments on the low-carbon alloy containing titanium. We have previously shown4 that the presence of titanium in this alloy reduced the free carbon to a sufficiently low level that thermal stabilization of the austenite-martensite transformation was not detected. Despite this, Fig. 2 shows that the microplastic response is decreased by aging treatments. A similar aging effect in Fe-ZONi, with some titanium, has previously been reported by . Thus, carbon is not necessary for the aging process and explanation 2 is at best incomplete. Since internal stress relief can occur independently of carbon (any temperature dependence of the flow stress can result in decreased internal

Jan 1, 1969

By T. E. Leontis

Several publications1-7 during the past few years have demonstrated the markedly greater effect of cerium, as compared to all other alloying elements, in enhancing the strength and creep resistance of magnesium at elevated temperature either with or without the presence of other elements. In the work reported in Ref. 1-6, the cerium was added in the form of Mischmetal, which contains all the rare earth elements in essentially the same proportions as they occur in monazite sand, the principal ore of these metals. Mellor and Ridley7 have presented the creep characteristics at 200°C of magnesium alloys prepared both with pure cerium and with Mischmetal. Up to the present time, however, no comprehensive study of the effect of the various component elements of Mischmetal on the properties of sand-cast magnesium has been made. This hiatus in magnesium technology undoubtedly is associated with the difficulty in obtaining the rare earth metals separately. This investigation provides such a survey, the object of which was to determine which of the elements present in Mischmetal contributes the greatest effect in developing high strength and high resistance to creep at elevated temperatures. Toward this end the compositional variation of these properties has been determined as a function of temperature in the following alloy systems: 1. Magnesium-Mischmetal 2. Magnesium-cerium-free Misch- metal 3. Magnesium-didymiuin 4. Magnesium-praseodymium- lanthanum 5. Magnesium-cerium 6. Magnesium-lanthanum This designation, based on the names of the metals as furnished by the producer, is used throughout the paper in order to avoid the complicated system of listing all the elements present in the more complex alloys. The composition of the metals and the alloys is discussed in detail below. Preparation of Alloys ALLOYING INGREDIENTS The chemical composition of each of the six alloying ingredients used to prepare the alloys reported in this paper is given in Table 1. In each case, the percent total rare earths, percent cerium, percent neodymium, percent praseodymium, and percent thorium were determined in addition to the listed impurities. The percent lanthanum was determined by difference from the total rare earth content and consequently includes the other elements (samarium, terbium, yttrium, etc.) present in Mischmetal. These additional elements, however, seldom amount to more than 1 to 2 pet of the total rare earth content of Mischmetal. The iron content of the Mischmetal is considerably lower than that of the other metals. This grade of Mischmetal is now readily available. The metals are listed in the order of decreasing complexity. Elimination of the cerium from Mischmetal results in what the trade calls "Cerium-free Mischmetal." Carrying the separation a step further by eliminating the lantha-

Jan 1, 1950

By G. Sachs

X-RAY analysis and single-crystal study have been utilized in recent years as a new means of following constitutional changes in alloys. If such transformations can be suppressed by rapid cooling, they can be followed at room temperature in a particularly convenient manner. In the following we shall consider changes in solubility and polymorphic transformations with particular reference to phenomena of the age-hardening type. Finally a thermodynamic viewpoint is developed for examining such transformations.

Jan 1, 1931