By Christopher R. Casias

A basic methodology is presented (employing both standard and theoretical assessment, analysis. and data interpretation techniques) for classifying waste containing trace levels of radionuclldes. Despite increased regulatory requirements for handling. transporting. and disposing of such waste: (I) no formal characterization methodology has yet been Implemented. and (2) no limits have been set to define the point at which a waste material is considered to be low-level and below which it Is "below regulatory concern" (BRC) or can be considered to contain no more than a diminimus level of radioactivity (i.e . is nonradioactive). 'I1le concept of diminimus limits specific to waste streams and waste forms is introduced. and a mechanism fur evaluating waste In relation to BRC and diminimus limits is outlined. This methodology can be used to perform a complete and adequate characterization of waste for classification according to its level of radioactivity.

Jan 1, 1992

By Gopalakrishna B. Prabhu, David L. Bourell

"Three mol% Yttria-Stabilized Tetragonal Zirconia (YSTZ) was prepared by a sol-gel synthesis technique using zirconium tetrachloride and hydrated yttrium chloride precursors. After drying and annealing at 823K, the particle size was in the range 10 to 20 nm. The zirconia powder was sintered using a uniaxial hot press at an applied stress of 20 to 40 MPa. One hour, isothermal sintering was performed in air after initial heating at 50K/min. Theoretical density was obtained at densification temperatures above 1498K. After sintering, grain coarsening characteristics were studied using constant heating rate anneals followed by quenching, based on a model for grain coarsening in a linear heating rate cycle. The microstructural change was studied using SEM and TEM and the phases were determined using x-ray diffraction.IntroductionThe ability to sinter nanocrystalline materials to full density several hundred degrees below the normal sintering temperatures is one reason for their current interest. [1-5] Yttria Stabilized Tetragonal Zirconia (YSTZ) of grain size of about 300 nm has exhibited superplasticity, with elongations as large as 800%.[6-7] Fine grain size is critical for superplasticity. Retention of the fine grain size during sintering of nanocrystalline powder is important if a material is to exhibit superplasticity or to exhibit physical or mechanical properties associated with the ultra fine structure. This paper investigates the sintering behavior and the grain coarsening characteristics ofnanocrystalline YSTZ.Techniques for synthesizing nanocrystalline materials have been studied in great detail earlier. [8-12] The techniques used to synthesize nanocrystalline zirconia include alkoxide synthesis [9], the chloride method [11], the peroxide method [13] and the acetone-toluene method. [13] In this paper the method used in the synthesis of zirconia is the chloride technique. With this precipitation technique, either zirconium chloride or oxychloride and a corresponding yttrium salt or even pure yttria are used."

Jan 1, 1994

By Esperidiana A. B. Moura, Célio H. Wataya, Roberta A. Lima, Rene R. Oliveira

Biodegradable starch/copolyesters/silica nanocomposite films were prepared by melt extrusion, using a twin screw extruder machine and blown extrusion process. The influence of the silica nanoparticle addition on mechanical and thermal properties of nanocomposite films was investigated by tensile tests; X-rays diffraction (XRD), differential scanning calorimetry (DSC) and Scanning electron microscopy (SEM) analysis and the correlation between properties was discussed. The results showed that incorporation of 2 % (wt %) of SiO2 nanoparticle in the blend matrix of PBAT/Starch, resulted in a gain of mechanical properties of blend.

Jan 1, 2015

By J. H. Corrigan

A series of six papers describing the Falconbridge Dominicana Ferronickel project were presented at the International Laterite Symposium held as a joint project of TMS-AIME in February 1979 at New Orleans. A review of the ore mineralogy, as well as. the processing and environmental practices as they exist today at Falcondo with emphasis on modifications put into practice since 1979 are presented in two papers: Part I.- Mineralogy and Ore Dressing E.W. Lithgow - General Superintendent ? Mines Falconbridge Dominicana, C. por A. Bonao, Dominican Republic Commercial volumes of nickeliferous laterite ores overlie part of a 90 km long belt of peridotites in central Dominican Republic. Protores are serpentinized harzburgites and dunites, with lesser serpentinite. The ore mineralogy consists mostly of goethite, serpentine-group minerals, quartz and poorly crystallized, X- ray amorphous materials. Minor constituents are hematite, gibsite, olivine and enstatite. In the Ore Dressing plant, the mine feed is subjected initially to proper sizing and blending to produce a homogenized mix. Subsequent drying and upgrading, by selective crushing and screening of rock kagments through a Barmac circuit, complete preparation of the ore for pyrometallurgical processing. Part II.- Pyrometallurgy, Fuel and Power Generation J.H. Comgan - Manager ? Production Falconbridge Dominicana, C. por A. Bonao, Dominican Republic Falcondo's energy requirements are based on oil which is refined on site to provide distillate to carry out drying and selective reduction of the nickeliferous ore in the shaft furnaces, plus bunker oil to produce electrical power for process melting, refining and ancillary use. The dryer product at 1.68% Ni is briquetted and passed counter current to hot reducing gas in 12 vertical shaft furnaces. The hot calcine discharge is melted in two high power electric furnaces at very high secondary voltage. The crude ferronickel is ladle refined and cast as 15 kg ingots or 125 gm ferrocones.

Jan 1, 1993

By Dong Hoon Han

The sulfation rates of magnesium oxide and calcium oxide (molar ratio 7:3) contained in calcined CMA ( calcium magnesium acetate) by SO2 were measured. The experiments were carried out in the temperature range 700 to 1100 °C and under the SO2 concentrations of 0.3 to I mol % (5 % 02). In the low-temperature range below 830 °C the reaction produced CaSO4.3MgSO4 and unreacted MgO, but no MgSO4 phase. The formation of CaSO4.3MgSO4 phase has a significant implication in that it allows the utilization of MgO for SO2 removal whereas the sulfation of MgO from conventional sources is so slow that it is of no practical interest. Thus, the calcined CMA can remove SO2 at lower temperatures than conventional SO2 absorbents and at a greater capacity. Above 950 °C only CaO reacts with SO2, but at a much greater rate than the calcined Ca(OH)2, which is one of the most reactive SO2 absorbents.

Jan 1, 1998

By Shuai Wang, Gang-hua Fu, Lu Yang, Yu-feng Guo, Tao Jiang

The fluorine-bearing iron concentrate is one of the refractory raw materials for pelletization, which is mainly used in Baotou iron and steel company with lots of problems, such as narrow roasting temperature range and low compressive strength of products. According to its specific character, the effects of roasting temperature, time on the compressive strength and microstructure of pellets were researched. The results show that low melting substances formed during the roasting was the dominant reason of those problems. High melting substances were added in the roasting to investigate their effects on the roasting properties of fluorine-bearing iron concentrate pellets. Low melting substances were reduced when chromite was added. The compressive strength of products was 3100N/P when the 2% chromite was added at the roasting temperature of 1150 ºC, which was increased 700 N/P compared with the pellets without chromite, and the roasting temperature range was expanded by 170 ºC.

Jan 1, 2016

By Chang-Young Choi

Korea Zinc commenced zinc production in 1978 with a capacity of 50,000 tpa. Since then, continuous investments have been made and resulted in Korea Zinc now being the biggest zinc and lead producer in the world. In the course of increasing zinc production capacity, the company management realized that the company needed a lead smelter to prevent the solid waste disposal problems by treating the lead containing solid waste. This paper begins by briefly stating the objectives and the roles of the lead smelter at Onsan. It describes the QSL process and the TSL process, and further extends the description of the TSL process, through which harmless inert solid waste could be produced for secure final disposal. It is also mentioned that the TSL process plays an important role in the integration of zinc and lead production. Throughout the paper, a positive attitude in handling the environmental issues in the non-ferrous smelting industry is emphasized. Finally, a solution for the solid waste disposal problem in the zinc and lead industry is proposed, with which the environmental issues can be an opportunity rather than a crisis. The current operation at Onsan suggests the future direction of the non-ferrous smelting technology that all of the zinc and lead producers should pursue.

Jan 1, 2003

By Jong-Ren Tarng, Gin-Hwa Chen, Wen-ku Chang, Ke-Ming Lin, Yuan-Haun Lee

"The majority of early studies used X-ray diffraction, but this requires a model to interpret the diffraction processes. A turbostratic model has been applied by Warren, Franklin and Bacon to a wide range of materials including both soft and hard carbons. Maire and Mering applied the same methods to the interpretation of the (001) lines of a series of graphitic carbons. In our case, graphitic carbons undergone high temperature and high pressure graphitization processes have been evaluated by the same methods. It were found that most technological XRD data were obtained by a Rietveld method with the least-squares refinements could be in the simplest way since the full correction technique is very laborious. The behavior of carbon materials as it proceeds through the graphitization process is characterized by changes in the measured interlayer spacings (d) a~ a function of temperature. A series of graphitic carbons including the transformation of diamond to graphite through the process under high temperature and high pressure have been evaluated. A simple calibration equation has been established. IntroductionRecently, in battery industry, carbon materials are used as cathode in lithium ion batteries. However, graphitization of those carbon materials is concerned as if lithium ion intercalated into those carbon cathode. Both high-graphitization and low-graphitization carbon materials are suitable for this kind of application.As for graphitization, the starling materials from which carbons may be prepared vary extensively from pure chemical compounds, to mixtures containing II wide range of molecular weights, such as pitches. So its graphitizing, perhaps the most notable feature of the process, is the very wide range of temperature over which the perfection increase, unlike the more common transformations of solid state materials which occur in a narrow temperature range. The variables involved in the conversion of the initial hydrocarbon to a carbon residue, which may vary widely in final perfection, are time, temperature, stress and impurity content"

Jan 1, 1996

By Milton Blander

A review of concepts and theories for predicting thermodynamic solution properties of multi- component high temperature liquid solutions is reviewed. During the last 50 years the ability to predict :such properties for molten salts, silicates and metals based on the generally known properties of the lower order (often binary) systems has been developed and shown to provide predictions which are quite useful in science and technology. There are many gaps in our understanding of these high temperature solutions, especially for metals, and considerably more work is needed.

Jan 1, 1996

By Chang-Young Choi

Korea Zinc commenced zinc production in 1978 with a capacity of 50,000 tpa. Since then, continuous investments have been made and resulted in Korea Zinc now being the biggest zinc and lead producer in the world. In the course of increasing zinc production capacity, the company management realized that the company needed a lead smelter to prevent the solid waste disposal problems by treating the lead containing solid waste. This paper begins by briefly stating the objectives and the roles of the lead smelter at Onsan. It describes the QSL process and the TSL process, and further extends the description of the TSL process, through which harmless inert solid waste could be produced for secure final disposal. It is also mentioned that the TSL process plays an important role in the integration of zinc and lead production. Throughout the paper, a positive attitude in handling the environmental issues in the non-ferrous smelting industry is emphasized. Finally, a solution for the solid waste disposal problem in the zinc and lead industry is proposed, with which the environmental issues can be an opportunity rather than a crisis. The current operation at Ousan suggests the future direction of the non-ferrous smelting technology that all of the zinc and lead producers should pursue.

Jan 1, 2003

By A. F. Kaczmarek

Cerro Negro is an undeveloped ore body located at the Cerro Verde mine near Arequipa, Peru. The mineable reserve contains 70 Mt of oxide ore grading 0.532% copper. Mineralization is hosted in three distinct rock types: tourmaline breccia, crackle breccia and granodiorite. Rock type effects copper recovery and acid consumption. The paper describes Cyprus' testwork philosophy and the resulting four-phase metallurgical program used to define the commercial leaching parameters. Copper recovery and acid consumption were monitored as functions of crush size, heap height, irrigation rate and acidulation conditions. Single lift, on-off and permanent multi-lift heaps were considered. Leach cycle times were based on incremental copper extraction and acid consumption rates, with added constraints imposed by operational requirements. The optimum leach system involves an on-off pad using tertiary crushed ore acidulated with 20 kg/t acid and stacked to a height of 6.5 m. The active leach cycle is 82 days at an irrigation rate of 0.26 l/min/m2. Under these conditions copper recovery is expected to average 81% over the life of the mine.

Jan 1, 1999

By P. J. Uggowitzer, H. Kaufmann

"New Rheocasting is a novel route of semi-solid casting, in which the globular semi-solid precursor material is produced by controlled cooling of only slightly superheated melts in conventional steel crucibles. The resulting semi-solid slugs are placed into the sleeve of a vertical Squeeze Casting Machine and then filled into steel dies. Solidification occurs under hydraulic pressures up to 100 MPa Due to the reduced cost of precursor material, reduced investment cost and easier recycling, the New Rheocasting process offers cost reductions of up to 25% over conventional semi-solid casting · routes. The New Rheocast products are pore free, pressure tight, weldable and heat treatable castings.In the present work the New Rheocasting Process is introduced and the influence of heat treatment on mechanical properties of the New Rheocast alloy A356 is discussed.The alloy A356 is cast under ideal New Rheocasting conditions into a step die on an UBE HVSC 350 Squeeze Casting machine. As-east, TS and T6 heat treatment conditions with variations in solutionizing and aging time/temperature parameters are applied and the samples are tested by tensile testing. Alternatively, the same heat treatment conditions are applied to conventional Squeeze Casting parts and compared with New Rheocasting.Questions of potential cost savings due to modified heat treatment conditions are also addressed in this paper."

Jan 1, 2000

By W. Dresler

Design details of a 100 kVA DC electric-arc reduction furnace are described. The furnace is equipped with a 610 mm (24 inch) diameter graphite crucible hearth. A 76 mm (3 inch) diameter top graphite electrode is used as a cathode. The current passes through the bottom of the crucible and is carried to a bottom plate (the anode) by conductive magnesia carbon bricks. The furnace can be operated up to a maximum of 120 V, 1800 A, and presently 100 kW. The start-up operating experiences and metallurgical results of one reduction test with a Montana chromite containing 38% Cr2O3 are discussed.

Jan 1, 1994

By Valerio Viti

In High Pressure Die Casting a molten metal is injected through a thin gate into the cast cavity. High injection pressures and high gate velocities create atomization phenomena which can negatively affect the final quality of the cast. In order to control atomization process it is essential to understand the atomization patterns and the two-phase flowfield that exist at the gate exit. In the present work, 2D numerical simulations of the flow of molten Magnesium through a high aspect-ratio rectangular gate are performed using a water analogue for an open and closed cavity. The numerical simulations made use of VOF-type (Eulerian) physical models and Lagrangian models. Further, a sub-grid scale model was implemented that, in conjunction with VOF-type equations can efficiently predict the general atomization pattern without the need for high-resolution grids. The numerical results were compared to experimental data for validation.

Jan 1, 2006

By Veena Sahajwalla

The cupola furnace is a coke-fueled shaft furnace used as a primary melting unit in iron foundries. Control of chemical composition of the iron tapped from the cupola is a key factor in productivity and quality control. In an effort to develop a control model for the cupola, a fundamental approach based on physical and chemical principles has been taken to describe the melting process. The behavior of oxidation of the solid charge in the stack of the cupola has been studied. Sulfidation of the charge materials by sulfur-bearing components released to the furnace gases from the coke has been described. Carburization of metal droplets of iron and of steel in separate molten streams has been characterized. Finally, reactions with alloying elements in the hearth (well) of the furnace have been defined. These reactions have been described in a computer-implemented model developed to predict the composition of the iron tapped from the cupola. The model has utilized the thermodynamics and kinetics of the oxidation, sulfidation, and carburization reactions, including temperature and physical aspects, in the various zones of the melting unit. The model predictions have been compared favorably with operating results.

Jan 1, 1992

By Vinod K. Sikka, René Cooper

"Cohoes, New York 12047 Intermetallics are an attractive class of advanced materials. The aluminide intermetallics offer advantages including: (1) lower density, (2) oxidation resistance, (3) carburization resistance, and (4) interesting mechanical properties because of their ordered crystal structure. Even though the attractive properties of the aluminides and other intermetallics have been known for nearly four decades, their practical applications have not been developed for two reasons: (1) the poor ductility (in some cases, both ambient and high temperatures) and (2) the lack of processability into meaningful components. Recent advances such as ductilization of Ni3Al by small additions of boron and the knowledge that environmental effects are the major cause of poor ductility in Fe3Al and FeAl systems have brought the intelmetallics into the forefront of research and their commercial applications. This paper has described a method for melting Ni3AI-based alloys that successfully utilize the exotherrn for the formation of NiAl from the elemental materials. The reaction-synthesis method has also been utilized for the production of NiAI and NiAI-based alloy powders from the elemental powders. The reaction-synthesized powders of NiAI and NiAI-based alloys were consolidated by hot extrusion and evaluated for tensile properties over a temperature range from room temperature to 1050ºC. The powder-processing conditions have been found to have more influence on the ductile-to-brittle transition temperature of NiAI than the powder-production method.IntroductionIntermetallics are an attractive class of advanced materials [1-11]. The alum in ide interrnetallics offer advantages including: (1) lower density, (2) oxidation resistance, (3) carburization resistance, and (4) interesting mechanical properties because of their ordered crystal structure. Even though the attractive properties of the aluminides and other interrnetallics have been known for nearly four decades, their practical applications have not been developed for two reasons: (I) the poor ductility (in some cases, both ambient and high temperatures) and (2) the lack of processability into meaningful components. Recent advances such as ductilization of Ni3Al by small additions of boron and the knowledge that environmental effects are the major cause of poor ductility in Fe3Al and FeAl systems have brought the intermetallics into the forefront of research and their commercial applications. The paper will briefly review the processing techniques being pursued for the commercial applications of Ni3Al-based intermetallics. The major emphasis of the paper will deal with synthesis of Ni3Al and NiAI intelmetallics."

Jan 1, 1994

By Zhang Libo, Li Wei, Peng Jinhui, Guo Shenghui, L. Jing

Partially stabilized zirconia ceramics (PSZ) were prepared by microwave sintering using natural baddeleyite which was obtained by flotation of baddeleyite ore as starting materials. Because of using natural baddeleyite as raw and the process producing no waste, it realized shorter process, energy savmg, environmentally-friendly and non-damage processing. In this work natural baddeleyite stabilized with 3.8wt.% CaO were sintered at 1300°C for 60min in a multi-mode 2.45GHz microwave furnace. Microwave sintering could fast heating and sintering. Besides that, microwave sintering could heat materials wholly, low the sintering temperature, improve the materials properties and save energy. X-ray spectrum displayed the product composed by the tetragonal phase and monoclinic phase that also showed the product was PSZ. Fine and uniform microstructures were observed in the product through scanning electron microscopy. PSZ which was with high density was confirmed by the method of the Archimedes technique.

Jan 1, 2011

By George H. Edwards

Most cullets consumed in large-volume glass manufacturing processes receive little processing beyond crushing. But lead-glass cullets for specialty glasses such as industrial lighting refractors or cathode-ray tubes are combined with metals and various coatings that prohibit their direct recycling into the glass-melting processes that created them. In many cases, the contained lead renders these cullets hazardous. At present, virtually all industrial processes to separate one cullet from another depend on hand sorting, and thus are necessarily costly per unit weight. Lead-glass cullets of differing lead content are of interest because they offer the possibility of separating one glass composition from another by high-speed, automated processes at low cost. A potential process for comminution, cleaning, and separation of lead-glass cullets would involve primary and secondary crushing, magnetic and other metals separation, attrition scrubbing in water, separation of glass types by gravity techniques, drying if necessary, sampling, and preparation for transport to the point of use. Process water would be filtered to remove finely divided coating materials and glass, and reused. If carried out on a scale similar to a specialty industrial mineral processing plant, the cost per unit weight of such processing should be substantially less than the raw material value of the cullet in specialty glass production. The added value of avoiding waste disposal costs makes this process economically attractive.

Jan 1, 1994

By T. P. R. de Jong

Dual energy X-ray transmission imaging is extensively applied for safety luggage inspection. Its advantages are its rapid scanning rate (25 to 100 cm/sec) at approximately I mm resolution and simultaneous thickness independent metal identification. This is especially advantageous for secondary scrap metal inspection and automatic sorting. Other applications include metal product inspection, bale control, and waste processing. Recent progress in development of an automatic on-line sorter for bulk solids is presented and discussed. Besides various non-metal applications (solid fuels, wastes etc.) it appeared particularly effective in light metal sorting. As inspection tool better control of difficult to monitor solid bulk streams, batteries, bales and other related metals becomes possible.

Jan 1, 2003

By Jesse White, Arlin Olson

"An Engineering Scale Technology Demonstration (ESTD) unit utilizing the THOR fluidized bed steam reforming technology was built and operated by Hazen Research, Inc. for the purpose of denitrating and solidifying various Department of Energy (DOE) radioactive tank waste surrogates into granular products. The ESTD offered the opportunity to investigate the operational characteristics of two fluidized beds in series to test process system designs such as those for fluidization, feeding, and product collection. Operational characteristics that were evaluated included bed attrition rate, particle growth, and elutriation; and the effects that variations in process parameters (e.g., fluidizing gas flow rate, feed composition, feed injection method, and gas distributor design) had upon these characteristics were observed. Testing of the process systems on this scale allowed for design changes to be made where the cost in time and money were significantly less by comparison to those same modifications being made on the commercial scale.IntroductionFluidized bed steam reforming (FBSR) offers a moderate temperature (620-750°C) continuous method by which various liquid wastes can be processed irrespective of whether they contain organics, nitrates, sulfates/sulfides, chlorides, fluorides, volatile radionuclides or other aqueous components. The FBSR technology has exhibited the potential to process these wastes into either a carbonate or crystalline ceramic (mineral) granular product.Pilot scale testing was performed using the THOR Treatment Technologies, LLC (ITT) FBSR process, as it offered the opportunity to evaluate multiple aspects in an environment more conducive to experimentation. Process changes and system modifications could be made faster and with less cost impact as compared with changes to an assembled commercial plant. These aspects include verification of process chemistry and kinetics, evaluation of materials of construction, equipment sizing and design, and the interactions of the systems. Evaluation of process chemistry allowed for the verification of thermodynamic and kinetic models, and was used in conjunction with these models to improve the database and modeling assumptions. It also allowed for the reevaluation of data from earlier bench scale testing with the opportunity for long-term operations. These long-term effects may include the buildup of one or more elements that results in the formation of eutectics leading to the destabilization of a fluidized bed, or the shift in particle size as a result of attrition or agglomeration. The pilot plant also provided an environment to evaluate materials of construction."

Jan 1, 2014