Search Documents

By Zhao-feng Xie

A new process of recycling valuable metals containing in the slag of jamesonite smelting in the blast furnace was studied. In this process, the valuable metals such as Pb, Sb, Zn and In etc. were fumed and volatilized and enriched in the dust firstly and then the dust was leached by sulfuric acid. In the leaching procedure, Zn and In in the dust entered into the leaching solution and were separated from Pb and Sb which remained in the residue.The optimal operation conditions of the fuming procedure are as follows: the mass ratio of the blast furnace slag, coal powder and lime are 100:22:10 respectively and the fuming time are 1.5~2.5 h, the fuming temperature is not below 1200C and the volatilization rates of Pb, Sb, Zn and In are 95%, 92%, 86% and 75% respectively. The optimal conditions for the leaching procedure are also presented: the consumption of sulfuric acid is 1.15 times of the theoretical consumption, the ratio of liquid to solid is 4:1 and the leaching temperature, leaching -1time and stirring speed are 90, 1.5h and 300 r?min separately. The leaching rates of Zn and In are 98.5% and 95.2% respectively. The experimental results shows that the valuable metals in the dust can be recovered and separated effectively by this process and the?ir recovery efficiencies are as follows: Pb94%,Sb91%, Zn84% and In69%.

Jan 1, 2009

By J. Rajesh Kumar

The extraction equilibrium study of tetravalent platinum was carried out using tri-octyl/decyl amine (Alamine 336) and bis(2,4,4-trimethylpentyl) monothiophosphinic acid (Cyanex 302) in kerosene from hydrochloric acid media to investigate their extraction capacity, since they have different donor atoms, ?N? and ?S?. Their distribution equlibria were studied as a function of acid, extractant, diluents and temperature. The title metal shows the inverse behavior at higher acid concentrations. Extraction of tetravalent platinum increases with increase of extractant concentration. The plot of log D vs. log [Extractant], mol.L-1 is linear with slopes 1±0.3, indicating the association of one mole of extractant with the extracted metal species. Stripping of metal from the loaded organic (LO) with mineral acids and bases such as hydrochloric, sulphuric, nitric acids and ammonia, hydrogen peroxide, sodium hydroxide, thio- urea were studied. Regeneration and recycling capacity of Alamine 336/Cyanex 302 and extraction behavior of associated elements was also studied.

Jan 1, 2009

By Kandipati Sreenivasarao

Ion flotation is a promising separation process for continuously removing toxic metal ions from dilute process effluents. After treating the effluent with appropriate surfactant(s), the metal- bearing species adsorb onto the surface of rising gas bubbles and can be collected as foams. Suitable collectors have been identified for most of the elements of the periodic table. However, a better understanding of the thermodynamic, kinetic and engineering principles that determine the performance of ion flotation systems would facilitate commercial utilization of this technology. A model system of sodium dodecylsulfate-ethanol has been studied for the removal of Cu (11) from dilute solutions, using laboratory-scale flotation columns. This paper reports the effects of the air flow rate, solution height, foam drainage zone height and col1ector:metal ion ratio on the flotation kinetics, ultimate recovery of metal, flotation product grade, foam losses and effluent quality. Preliminary results for Pb (11) removal are also reported.

Jan 1, 1993

By Vanessa M. Torres

Cia. Vale do Rio Doce is currently developing Niquel do Vermelho Project. The laterite deposit is located at Carajas Mineral Province at less than 15 km from Sossego Copper Project, scheduled for start-up in 2004. The available infrastructure, includes paved roads, large capacity railroad and port complex owned by CVRD, power supply and good quality water. The project was evaluated in the past for ferronickel production. In the late 1990s, CVRD switched its attention to investigating the usage of pressure acid leaching. The combination of good metallurgical behaviour for pressure acid leach (PAL) process route with reasonable mineable grades, and existing infrastructure justified the start of engineering studies in 2002. The project approach at the engineering phase is based on the dual objective of minimizing risks while maximizing project profitability and value. CVRD is currently completing the Niquel do Vermelho prefeasibility study. This paper outlines the main outcomes of the study and future perspectives for the project.

Jan 1, 2004

By H. Forrest

Lead smelting at Cookson Industrial Materials was formerly carried out using a combination of Blast and Reverberatory Furnaces. In the late 70' s these furnaces were replaced by two 20 tonne capacity Rotary Furnaces. This furnace type has proved to be more flexible in the range of feedstock that can be processed, including lead drosses, battery plate and even whole batteries. High rates of production have been achieved whilst attaining a good level of environmental control. The majority of the sulphur in the feedstock can be fixed by use of appropriate fluxes.

Jan 1, 1990

By Tiebao Yang

In high pressure die casting processes, a die plays a critical role in removing heat from the molten metal during the cavity filling and solidification stages. Proper control of die temperature is essential for producing superior quality components and yielding high production rates. This paper proposes a local temperature control scheme for die thermal management based on a computerized intelligent real-time monitoring and control system (IRMCS). In this scheme, cooling water lines are controlled by a pump and solenoid valves. A controller is designed according to the law of die temperature fluctuations. The results obtained from the experiments carried out on a laboratory die casting process simulator indicate that the controller can limit the local die insert temperatures in a given band. Hence, the desired thermal pattern of the die insert becomes achievable.

Jan 1, 2006

By John T. Berry, Robert D. Pehlke, Michael J. Beffel

"Pattern making and metal casting organizations are currently adopting CAD/CAM systems and implementing this technology in design and production. Al though significant progress has been reported, these systems generally are based on two or two and one half dimensional analyses. Very few are based on solid geometric modelers.The present paper emphasizes the need for solid geometric modeling of the casting and rigging system and linkage with a solidification simulator. The nature of some of the technological challenges which have slowed this development are discussed, including accurate description of complex surfaces and their intersections and the bridging of computer encoded information with NC technologies and with FEM-based simulators for stress and thermal analyses. A recently prepared modular-structured FEM simulation code implemented on a micro computer is described.Construction of a solid geometric model of the casting and rigging and validation of the combination for optimum characteristics of soundness, quality and yield by solidification simulation are I inked as key elements in the foundry of the future. Data base support for this CAD/CAM system is rapidly being developed throughout the world.INTRODUCTIONThe simulation of shaped casting solidification using the digital computer, goes back to at least the early nineteen-sixties when Forsund (1) in Denmark applied the technique to the problems of casting surface quality.Prior to that time, the work of Paschkis and co-workers using the analog computer ranges back to the nineteen-forties, when work sponsored by the AFS Heat Transfer Committee at Columbia University revealed many hitherto unknown or only partly anticipated aspects of casting solidification (2).Three reviews of the various historical aspects of simulation should be referenced. Firstly, the AFS monograph by one of the present writers (RDP) and his colleagues - describing background and later work, again sponsored by the AFS Heat Transfer Committee at the University of Michigan (3). Secondly, a review prepared by Durham and Berry (4) which discusses broad aspects of casting solidification simulation. Thirdly, a review by Erickson (5) which contains an excellent bibliography to 1980. In addition to these papers, the publications lists of the CADCAST project* and the proceedings of the two Engineering Foundation Conferences of Casting and Welding Modeling, published by ASME, are also most notable (6) •"

Jan 1, 1986

By Paulo von Krüger

This paper deals with the cell design and operation of a tin electrorefining 1:5 pilot plant. The purpose of the work was the fitting of the basic parameters to be used in a full-scale tankhouse from a major Brazilian tin producer. The main specific difference was the use of permanent stainless steel cathodes instead of conventional tin starting sheets. The results of both product quality and operating parameters are discussed.

Jan 1, 2003

By Christoph Pichler

A special desulphurization slag accrues during the processing of iron ore to steel, which is needed to generate high quality steel. Sulphur removing is done by different technologies, but the most common one is the generation of a high sulphur containing slag by sulphur affine elements. Currently, this desulphurization slag is partly recycled, however, huge amounts are still dumped. To utilize this desulphurization slag for future purposes, a recycling process must be established. Therefore, first characterization of this material started some years ago at the Chair of Nonferrous Metallurgy, Montanuniversität Leoben. Subsequent trials in lab scale size were performed, also some investigations for different treatment steps were evaluated, starting with a parameter study in a hot stage microscope at various gas-atmospheres. Finally, the developed recycling process concept was verified in pilot scale trials to confirm the new recycling technology. Due to the successful treatment process, also a patent was applied.

By M. K. Patel, K. A. Pericleous, M. Molaei

"The future trading of carbon credits and increased financial cost necessitates substantial cuts in incidental C02 emissions in the production of metals (iron, steel, aluminum, zinc, lead). Although greener methods of production are being developed, in the short term the use of point-source C02 extraction using existing technology remains attractive. Accelerated natural carbonation, in a fluidized bed is a feasible technological route investigated in this research. CFD modelling has been used to study the efficiency of C02 capture in a fluidized bed reactor containing a CaO solid sorbent. A Lagrangian/Eulerian scheme describes describe CaO particle trajectories and exchange of mass, momentum and energy with the carrier gas, with a typical off-gas composition. Different reactor geometries are considered (with uniform, stepped and gradually expanding cross-section), to maximize conversion for a given particle loading and size distribution (100-200 microns). Removal efficiencies of up to 80% are demonstrated, making this a viable process.IntroductionBased on Intergovernmental Panel on Climate Change (IPCC) reports, the major cause of climate change and global warming is due to a high level of C02 concentration in the atmosphere resulting from fossil fuel combustion, particularly in coal-fired power plants [1]. Carbon capture and storage is therefore the most important action proposed to reduce C02 from combustion flue gases. In this process, carbon dioxide is captured and may then be regenerated as pure C02 and conducted to a permanent storage, or simply stored as a solid carbonate [2]. Capture and storage of C02 has an economic penalty and the main cost of this penalty is associated with the capture plant. Capturing C02 with a lime-based solid sorbent (CaO) is a very promising technique, due to the low cost and the wide availability of the reactant. In this process, the CaO reacts with C02 based on the following reaction in a reactor called a Carbonator:"

Jan 1, 2012

By P. Louis

Gécamines is the world largest cobalt producer with about 60 % of the Western World production. During the last ten years, its annual production varied from 5,400 to 14,600 t/year. The actual cobalt production capacity of Gécarnines is 18,000 t/year and could be increased in the near future if necessary. Cobalt is presently produced at the Shituru plant by an old in-pulp electrolysis process and in Luilu, by electrolysis of a clear weakly acidic solution. The Shituru Cobalt quality is lower than the Luilu one. For that reason, part of the Shituru Cobalt is fire refined and cast into granules. Large efforts have been succesfully accomplished to improve the cobalt quality. This has been made possible by a better knowledge of the purification processes and of the electrolysis parameters.

Jan 1, 1988

By Xiangru Chen, Honggang Zhong, Qijie Zhai, Qingqing Sun

"A horizontal directional solidification equipment, with an in-situ pouring system, was employed to physically simulate the solidification behavior of continuous casting. In this paper, the 2304 duplex stainless steel (DSS 2304) was investigated using this equipment due to its microstructure produced by continuous casting process was usually not satisfied. The grain size combined with the position of columnar to equiaxed transition (CET) of DSS 2304 were observed and the results showed these microstructure characteristics were very close to those of the continuous casting slabs. In addition, the influences of pouring temperatures and cooling conditions on the CET behavior were investigated. The results revealed that the length of the columnar grains decreased with decreasing the pouring temperatures and flow rates of the cooling water. Besides, the content of austenite decreases with increasing the distance from the chilled sidewall.IntroductionDuplex Stainless Steels (DSSs) have been widely used in industry for their excellent mechanical strength and superior corrosion resistance in Cl- environments when compared with other stainless steels [1,2]. Their good performances are mostly on account of the duplex phase structure-ferrite (d) and austenite (?) and the high proportion of alloying elements. Although, DSSs have good ductility, but worse formability compared to the austenitics, and this is the key to restrict DSSs application [3]. This is due to the differences properties between the two phases. The hot workability of ferrite (d) is better than austenite (?) and exhibits a lower flow stress during hot rolling processing [4]. The early workers had revealed that coalescent force of phase interface, microstructure, difference of mechanical property between two phases and the precipitations are the main factors affecting the formability of DSSs [5,6]. Another important reason that affects the alloy’s mechanical properties is columnar to equiaxed transition (CET) [7]. It often occurs during continuous casting solidification process and induces inhomogeneous mechanical properties and the microstructure varies with different processing parameters, such as pouring temperatures, cooling conditions (water flow rates in the cooling zones) and casting speed [8]."

Jan 1, 2012

By Shengqin Zhang, Yousef Mohassab, Feng Chen, Hong Yong Sohn, Mohamed Elzohiery, Amr Abdelghany

The kinetics of hematite concentrate reduction by mixtures of hydrogen and CO of various compositions has been investigated as part of the development of a flash ironmaking process at the University of Utah. This process produces iron directly from iron oxides concentrates by the gas-solid flash reaction based on the partial oxidation of natural gas, resulting in a significant reduction in energy consumption and greenhouse gas emission. The reduction kinetics of hematite concentrate of an average particle size 21.3 μm by the above mentioned gases in the temperature range 1423 to 1623 K (1150 to 1350 ºC) was investigated. Hematite concentrate particles can be reduced to > 90% by any of these reductants in several seconds of residence time typically available in a flash reactor. The activation energy ranged from 214 kJ/mol for hydrogen to 231 kJ/mol for CO.

Jan 1, 2016

By Zhihong Liu

Monodisperse micron size nickel oxalate particles with rhombohedron morphology were prepared from condensed Ni(OH)2 suspension by a novel gel-sol process proposed by one of the authors. Firstly, condensed nickel hydroxide gel was formed by fast adding 1 mol dm-3 NaOH solution into 0.2 mol dm-3 nickel chloride solution, and then oxalic acid solution with a concentration of 0.25 mol dm-3 was dropped into the gel drop wise through a pump equiped with a pH controller under preset pH value, and in this process, Ni(OH)2 gel was converted gradually into monodisperse nickel oxalate sol. The formation of the nickel oxalate particles was found to proceed through a dissolution-recrystallization mechanism from the nickel hydroxide gel. The product particles exhibited rhombohedron like shape with micron size long axis and sub-micron size short axis. The effects of such factors, as temperature, surfactants, et al, were evaluated experimentally on the particles sizes and morphologies.

Jan 1, 2006

By Kun Wang, Xinhui Li, Huaqing Xie, Qingbo Yu, Qin Qin

"Three typical model compounds of bio-oil (ethanol, acetone and phenol) were studied in the steam reforming process for hydrogen production. In the thermodynamic analysis, the three componds showed the similar trends. The hydrogen yields increased with the increase of steam/carbon (S/C) ratios, and the temperatures of the maximum hydrogen yields moved afterward to low temperature zone. However, the hydrogen contents were just about 70%. For improving hydrogen yield, a new system for steam reforming of bio-oil with site CO2 capture was put forward. This system required the catalst with the larger granularity having greater mechanical strength and higher abrasion resistance. So, six Ni-base catalysts loaded on Al2O3 particles prepared were used and among them, Mg-Ni/Co catalyst showed the best catalytic performance. For the simulated bio-oil (the mixture of the compounds), the hydrogen yield can attain 63% with Mg-Ni/Co catalyst with the good stability and regeneration ability.IntroductionCurrently the interest in the use of hydrogen as a clean energy carrier is increasing, and the main way for producing hydrogen is steam reforming of fossil fuels, containing steam reforming of nature gas, naphtha and coal. But this way caused substantial amounts of CO2 emitted, and these sources of hydrogen which are non-renewable energy will eventually be used up [1, 2]. As a kind of renewable energy, biomass is recognized as an attractive alternative to fossil fuels, because of its neutral CO2 emissions [3]. There are mainly two thermochemical processes using biomass to produce hydrogen, gasification and flash pyrolysis followed by steam reforming (SR) of the biooil produced in the flash pryolysis process [4]. The latter was known as one of the most promising and economically viable methods for hydrogen production [5]. In the last decades, the biomass flash pyrolysis technology was adequately developed and fairly mature [6]. But the steam reforming of bio-oil is still at the research stage and yet has been leading to more and more concerns by the researchers. In their research, the catalysts were widely studied and yet mainly were powdery[7-10], and the reactors manily were fixed bed reactors[11-13], readly causing the carbon deposition and the catalyst deactivation, against the continuous running. In this paper, a new systerm was put forward and could realize continuous production of hydrogen, yet needed catalysts with the larger granularity having greater mechanical strength and higher abrasion resistance, as well as powdery CO2 sorbents which mainly calcium oxide based ones.In this paper, the thermodynamic analysis of the steam reforming processes of three typical bio-oil model compounds (ethanol, acetone, phenol) was performed, and the effect of S/C ratio and temperature on the hydrogen yield and the compositions of gaseous products were investigated. Then, a new systerm for steam reforming of bio-oil with site CO2 capture was put forward, and the catalysts with a certain granularity were prepared and studied."

Jan 1, 2014

By Sang-Su Lee

This paper shows the application of the porous plug system in the Mitsubishi continuous copper smelting and converting process. This system has already been adopted and utilized in the steel industry to enhance productivity. Recently, some copper smelters have adopted this system but the results have not been satisfactory. The porous plug system was installed at the anode furnace in December 2001 to reduce the oxidation time and decrease the oil consumption. A good effect was that the nitrogen stirring of the melt through porous plugs improved the melt heat transfer. As the result of the enhancing heat transfer the oil consumption and the build-up inside the furnace were actually decreased. But until now the oxidation time has not been sufficiently reduced. In the future, further research and tests are needed in order to increase the productivity and save costs.

Jan 1, 2003

By Sang-Su Lee

This paper shows the application of the porous plug system in the Mitsubishi continuous copper smelting and converting process. This system has already been adopted and utilized in the steel industry to enhance productivity. Recently, some copper smelters have adopted this system but the results have not been satisfactory. The porous plug system was installed at the anode furnace in December 2001 to reduce the oxidation time and decrease the oil consumption. A good effect was that the nitrogen stirring of the melt through porous plugs improved the melt heat transfer. As the result of the enhancing heat transfer the oil consumption and the build up inside the furnace were actually decreased. But until now the oxidation time has not been sufficiently reduced. In the future, further research and tests are needed in order to increase the productivity and save costs.

Jan 1, 2003

By Yutaka Yasuda

The particle dispersion phenomena in a turbulent gas jet of the flash smelting process has been investigated. The particle number density in a non- reacting jet was measured experimentally by taking photographs of the particles in flight and counting them using the image analysis. Numerical computations were also performed using a mathematical model for a turbulent particle laden gas jet The experimental particle number density data were then compared with the predicted results of the model. Good agreement was obtained between the experimental and predicted data. The effects of the parameters such as the injector design, particle loading and air flow rate are discussed. Optimization of the concentrate burner design can be achieved with the help of experimental and theoretical simulation as performed in this work.

Jan 1, 1994

By Philip Nash, Jie Zhou, Joshua Blackketter

"Large ingots tend to have internal defects such as shrinkage cavities and porosities, which have to be closed during the cogging stage to ensure sound internal quality of forged parts. In this work, finite element methods were used to simulate open die forging passes, with varying parameters that affect the void closure behavior profoundly. Numerical models ware constructed in ABAQUS, DEFORM and FORGE using data taken from footage of the forging process and material mechanical data obtained from the Gleeble compression tests. Forging variables such as pass rotation, reduction per pass, and feed ratio were studied with intense attention paid on the special properties of H13 steel, so that this study can be applied to solve real world problem.IntroductionCenterline defect closure is a frequently studied but still challenging topic in open die forging industry. In practice, open die forging is employed as an effective hot forming process to make desired shape of metal products as well as to ensure center consolidation of internal defects which result from the casting process. Nowadays, remarkable large forgings have been more and more required to meet industries demand. However, the increase in ingot size has tended to result in considerable macrosegregations and shrinkage cavities or voids, which need to be worked thoroughly during the forging process; but the size of the products and limitations of manufacturing capacity, such as the press load, make it difficult to achieve adequate local deformation to close those defects. Therefore, choosing optimal forging parameters under given work condition to ensure good internal quality of forged products is critically important."

Jan 1, 2012

By Blas Melissari, Stavros A. Argyropoulos

"In this paper a computational approach was employed to estimate the melting of solid spheres immersed in different liquid metals and under different convective conditions. The spheres are made from the same material as the liquid metal. The SIMPLER algorithm was implemented using a three-dimensional system in Cartesian co-ordinates. Experimental validation of the dimensionless correlation was carried out in two fluids with vastly different Prandtl numbers. The dimensionless heat transfer coefficient (Nusselt number) is obtained as a function. of the Reynolds and Prandtl number.IntroductionThere is a paucity of dimensionless convective heat transfer correlations applicable to fluids like liquid metals. The existing correlations cover single Prandtl number metals [l] or at most two different Prandtl number metals [2]. A knowledge of heat transfer rates from particles at high flux levels has become increasingly important to the design of energy transfer systems. Melting of solid particles has been studied extensively as it relates to many engineering and environmental applications, such as materials processing, space applications, water resource and energy conversion. When objects are immersed in a fluid with a temperature higher than their melting point, they melt and produce molten material that then mixes with the surrounding fluid. These objects experience not only size variation but also changes in their shape. This observation is more pronounced when the melting occurs in a forced convective flow.Yuge performed pioneering experimental work on the heat transfer from a sphere to air under mixed convection [3]. He suggested procedures for predicting the Nusselt number. Hieber et al [4] studied the spherical system analytically, but their study was limited to flow with small Reynolds numbers. Many researchers studied the melting dynamics of ice spheres in water at different convective regimes. Aziz et al [5] and Hao et al [6] performed measurements of the heat transfer coefficient in the water system by measuring the melting time of ice spheres in forced convection. Hao et al [7] performed visualization studies of ice spheres melting in water under mixed convection regime. All of this groundbreaking work, however, did not involve the use of liquid metals"

Jan 1, 2004