By Kenneth P. Michalek, James E. Kelly, Jonathan A. Dantzig

"Many investigations have been reported regarding the simulation of continuous casting with emphasis on in-mold heat transfer. These analyses have been limited, however, because they require either estimation or measurement of the characteristic heat transfer between the ingot and the mold. In this paper, a self-consistent model 'is presented for calculating the heat transfer between a solidifying continuous casting and the mold, in the context of the continuous casting of steel. Using both thermal and stress analyses, the air gap formed during continuous casting is calculated and used to compute the heat transfer coefficients. Iteration between the thermal and stress analyses is used to determine a self-consistent solution. IntroductionThe continuous casting process for steel is illustrated schematically in Fig. 1. Molten steel is tapped into a tundish from which it flows at a controlled rate into the continuous casting mold. The initial shell of the casting forms in the mold by transfer of heat from the metal through the mold wall to the cooling water. The remainder of the casting is solidified by application of water sprays, and/or radiation cooling below the mold.Heat transfer in the mold portion of the process is important because it controls the formation of various defects which are deleterious to subsequent processing. Examples of defects formed in this region are surface irregularities, such as cold folding and oscillation marks, and more serious defects, such as longitudinal or transverse cracks. A more catastrophic problem which may occur is a breakout, in which the shell ruptures and molten steel is discharged in an uncontrolled way."

Jan 1, 1986

By Jorge A. S. Tenorio, Chuanwei Zhuo, Joner O. Alves, Yiannis A. Levendis

"The ever increasing number of automobiles and the consequential increase in consumption of tires have generated a pressing environmental issue, concerning the disposal of unserviceable tires. The worldwide disposed of waste tires is approximately 1 billion units per year and this amount is expected to increase by 2% each year. This work presents a microstructural characterization of nanomaterials synthesized in a catalyst system from the effluent of burning waste tire chips in a horizontal two-stage laminar-flow furnace. Controlled combustion of waste tire chips took place at temperatures of 900 or 1000 °C, and stainless steel meshes were used to synthesize the nanomaterials at 1000°C. Produced materials were analyzed by scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The catalyst meshes were covered by materials with diameters of 20 to 200 nm and lengths of about 40 µm. They possessed structures similar to those of carbon nanotubes.IntroductionThe motor vehicles on the road have been increasing annually. World motor vehicle production in 2009 approached 62 million units. Consequently, the consumption of tires has also been on the rise; about 1.4 billion units were produced around the world in 2007 [l]. The disposal of scrap tires is a serious environmental problem. The worldwide disposed of waste tires is almost 1 billion units per year with an expected increase of around 2% each year. However, less than 7% of produced waste tires are recycled (excluding reuse, retreading or incineration). The waste rubber tires are a thermoset polymer, which cannot be reprocessed like thermoplastics polymers, therefore the recycling of this material requires special techniques that demand big investments [2, 3].A solution to the disposal of waste tires is the sequential pyrolysis/combustion process. Past research showed that waste tires are an attractive potential fuel due the high heating value (29-3 7 MJ/kg), which is comparable, or even higher to those of typical bituminous coals [ 4, 5]. Pyrolysis is a process wherein the material is thermally decomposed at elevated temperatures at the absence of an oxidizing gas. Combustion is characterized by the addition of the oxidizing gases during the process. Several studies indicate that the pyrolysis and combustion processes for the tires treatment have a great energy conversion potential [4, 5, 6]."

Jan 1, 2011

By D. J. Donaldson

The PAL process for recovering nickel from laterite ore requires large volumes of thick abrasive slurry to be raised lo high temperature (245°C+) and pressure (40 atm.+). Flow diagrams of the process typically result in facilities that have serious operating and reliability problems. Most of the problems can be attributed to using multiple pump stations to raise the slurry to autoclave pressure, large amounts of flash and live injection steam to heat the slurry to autoclave temperature and several steps of flash cooling to lower the temperature and pressure of the abrasive autoclave slurry down to atmospheric conditions. It is proposed that operating and reliability problems of PAL facilities can be mitigated by using Tube-in-tube heat exchangers and "float type" positive displacement pumps. The subject paper describes an innovative application of such equipment in the facility design of the PAL process. Keywords: Nickel, Laterite, PAL, Heating, Slurry

Jan 1, 2004

By Qingchun Yu, Bin Yang, Yong Deng, Heng Xiong, Fei Wang, Minxiu Chen

"Metal aluminum produced by non-electrolysis process received much attention due to its lower energy consumption. In this paper, carbothermic reduction and carbothermic-chlorination of alumina in normal pressure and vacuum were studied. The products were examined by means of XRD, EDS and SEM. During the carbothermic reduction process using carbon reductant in normal pressure, no metal aluminum was found. However, when coal was used as reductant, a mixture containing metallic aluminum, A14C3, and silicon was obtained, but metallic aluminum couldn't be separated from the mixture. During the carbothermic-chlorination process in vacuum, Al404C and Al4C3 were produced by the reaction between alumina and carbon, and Al Ch gas reacted with Al404C and Al4C3 to produce Al Cl gas. Metallic aluminum was produced due to the disproportionation of A!Cl gas and condensed on the collecting plate. Meanwhile, the initial temperature of carbothermic reduction of alumina reduced in vacuum compared with that in normal pressure.IntroductionIndustrial production of primary aluminum is carried out in alumina cell by the so-called Hall- Heroult process, necessitating the use of very high currents of low voltage. The alumina from which metallic aluminum is gained must be chemically pure, otherwise impure metal results. The main drawbacks of the electrolytic production are its very high energy consumption, the release ofperfluorocarbons, and the high specific C02 emissions [1]. During the past years, there were a lot of attempts to produce metallic aluminum by carbothermic reduction of A1203 [2, 3]. Cox [4] determined the vapor pressure over the A1203-C system and performed X-ray diffraction analysis of condensed products. It was demonstrated that an increase in the carbon content in the system leaded to the sequence of transitions: A1203~Al404C~A1zoc~A14C3 ~AI [5]. In any carbothermic reduction process for aluminum, extremely high temperatures (2000 °C ) were required [6]. In spite of considerable effort, the carbothermic reduction of alumina to aluminum remains a formidable technical challenge, due to the high temperatures required, and to the formation of aluminum carbide and oxycarbide byproducts [7]."

Jan 1, 2013

By Selvin Yesilay, Munevver Caki, Canbora Bayraktar, Bekir Karasu, Rahmi Imrak

"In this study, the utilization capability of the solid wastes taken from a commercial roof tile and brick factory in Eskisehir of Turkiye has been investigated in the production of stoneware bodies which can be formed by slip casting. At the first stage, X-ray fluorescent (XRF) and X-ray difractometer (XRD) analyses of the wastes were performed. Depending upon the results, a body recipe with an optimum casting concentration was adjusted. The bodies obtained from prepared slips were fired at 1160 oC as glazed and unglazed forms. Then, they were undergone certain tests in order to determine their firing shrinkage values, water absorption levels and optical parameters. To establish what kind of phase formations occurred after firing as a result of waste incorporations into bodies XRD analysis was conducted. Additionally, effects of such a compositional modification on the microstructure of the bodies were examined by a scanning electron microscope (SEM). Consequently, it was concluded that fired roof tile and brick wastes could be evaluated in both glazed and unglazed stoneware bodies. Introduction Stoneware is the general name applied to many wares fired between 1150 and 1300 °C. It has a different and denser structure than those of ceramics produced at lower temperatures. Fired stoneware possesses a lower water absorption value. When matured at a high temperature, it gives a possibility for the use of feldspar as a main ingredient [1-2]. Colors of stoneware can be brown, red, white and most of the times beige. Firing usually takes place in oxidation atmosphere but also reduction can be rarely used. This naturally has an effect on the body colors [3]. Earth, which contains clay minerals, becomes plastic mud when mixed with water, has a capability to be easily shaped and can be hardened without cracking if fired at 900-1000 °C, is referred as one of the brick and tile raw materials [4]. Natural and aesthetic appearances of buildings obtained with brick and tile products, which make them preferable especially for construction sector, are of importance. Because clays being main raw material of that type of productions generally do not exist as pure materials in nature, their usability depends on their mineralogy and impurities they contain [5]."

Jan 1, 2008

By Ennio Bonetti

The technological applications of MgH2 hydrides for hydrogen storage demand the overcoming of some critical issues: an improvement of the reaction kinetics and a reduction of the desorption temperature. The synthesis of nanocrystalline MgH2 by reactive milling and inert gas condensation and a proper metal catalyst addition, constitute recently employed strategies. In the investigation of the hydrogen short and long-range dynamics, sorption kinetics and nanostructure stability, the mechanical spectroscopy offers some specific advantages. In the present research this technique was employed with other experimental approaches (XRD DSC) to investigate relaxational and structural damping processes in nanocrystalline MgH2 with added catalysts (Fe). Time/temperature variation of the dynamic elasticity moduli and mechanical quality factor are correlated to hydrogen anelastic relaxation processes and concomitant structural transformation of MgH2 to Mg associated to long range H diffusion. Results are discussed with reference to microstructural modification strategies able to assist hydrogen release.

Jan 1, 2006

By Yun Soon Han, Joo Hyun Park

Indium (In) solubility in the FeO-SiO2-Al2O3-5%CaO slag was measured under p(O2)=10¯¹¹ atm at 1573 K to clarify the dissolution mechanism of In in FeO-bearing metallurgical slag. The In solubility increased with increasing oxygen partial pressure, whereas it decreased by increasing the activity of basic oxide, viz. FeO. Thus, a dissolution mechanism of In in the FeO-SiO2- Al2O3-5%CaO slag was described by the following equation. In(s)+1/4O2(g)=(In+)+1/2(o2-) The enthalpy change of the In dissolution reaction was negative, indicating that the dissolution reaction was an exothermic reaction. This is consistent with the above reaction mechanism.

Jan 1, 2014

By Allan J. MacRae

A copper alloy to be used for coils in cast copper cooling blocks has been identified and samples prepared for metallurgical examination and destructive testing to compare with cast cooling blocks manufactured from copper and nickel-copper alloy pipes. The copper alloy allows for the formation of a metallurgical bond between the pipe and the cast copper during the casting process, which does not normally occur with pure copper or nickel-copper alloy pipes. The alloy's coefficient of thermal expansion is also much closer to that of pure copper compared with nickel-copper alloys, so there is less strain induced at the pipe-cast copper interface due to differential thermal expansion. It is expected that this new pipe coil alloy and associated casting techniques will allow for the production of cast copper cooling blocks that have greatly enhanced service life in high heat load applications compared to existing technologies.

Jan 1, 2002

By A. Mezei

Samples of cobalt and bismuth concentrates produced from the NICO deposit in Northwest Territories were subjected to a comprehensive metallurgical testwork consisting of: pressure oxidation, ferric chloride leach and carbon in leach, to recover the cobalt, bismuth and gold, respectively. A specific testwork program was designed to allow for the optimization of process parameters under multiple restrictive criteria. The overall objective was to establish leaching sequences that could produce acceptable recoveries while generating environmentally disposable residues as well as solutions suitable for further processing. The recoveries for the leaching stage, under the optimum conditions, were 97% for cobalt and 95% for gold, in the case of the cobalt concentrate. The bismuth concentrate produced recoveries of 99% for bismuth, 99% for cobalt and 97% for gold, respectively

Jan 1, 1999

By Milton Manrique

The thermal decomposition of zircon concentrates in a non-transferred arc thermal plasma flow reactor was investigated. The plasma torch was operated using argon-helium and argon-nitrogen mixtures as plasma gases. The effect of power, feed rate and zircon particle size was studied. Products were characterized by XRD, SEM, TEM and chemical analytical techniques. The average size of the product was in the submicron range. Free energy minimization plots were used to predict the behavior of the system under different operating conditions. A kinetic model to describe the different stages of the thermal decomposition process is proposed. The results of this investigation showed a significant segregation process where the zirconia-rich product is collected in the reactor while the silica-rich product is collected in the filter. TEM analysis indicated that silica vapor is condensed on the surface of the zirconia particles.

Jan 1, 1996

By W. G. Davenport

The Cu content of industrial flash furnace concentrates varies considerably. It is usually around 30% Cu (Tables 2.1, 3.1) but it may be as high as 55% Cu and as low as 20% Cu. The mineralogy of flash furnace concentrates also varies. The most common Cu mineral is chalcopyrite (CuFeSz), but many concentrates contain bornite (CuSFeS4), chalcocite (CU2S), covellite (CuS) and even native copper (CUO). Pyrite (FeSz) :is also present in many concentrates. This chapter examines how concentrate composition affects flash smelting -with specific reference to 'low-Cu-grade' FeS2-CuFeSz concentrates. Chapter 14 does the same with 'high-Cu-grade' CuzS-CuFeSz?concentrates.

Jan 1, 2001

By J. E. Dutrizac

A mineralogical study of a weak acid leach residue from the Clarksville zinc plant of Savage Zinc Inc. was carried out. The study focused on Pb and Cd as these elements most significantly impact on the environmentally acceptable disposal of the residue. The residue consists of major amounts of bassanite, zinc ferrite and various Zn-Pb-Fe-Cd silicate species. Also present are lesser quantities of PbSO4, sphalerite, Fe2O3 quartz, Mn-Pb-Fe oxides, SrS04, (Pb,Sr)SO4 iron gel-silica gel, jarosite and Ti oxide. The principal Cd carriers are the zinc ferrite, which contains up to 9.00% Cd and likely accounts for -45% of the total Cd content of the residue, and the various silicate species which contain up to 6.97% Cd and account for about 45 % of the total Cd. The sphalerite is a minor Cd carrier containing an average of 0.35 % Cd and accounting for -5 % of the total Cd; the other carriers contribute only trace amounts to the total Cd content. The major Pb carriers are PbS04, Pb-bearing silicates and Mn-Pb-Fe oxides. Minor proportions of the total 1.09% Pb content of the residue are carried by SrS04 and (pb,Sr)S04' Trace Ph carriers include the iron gel-silica gel, Fe-Zn-AI oxide and bassanite. The residue after the toxicity characteristic leaching procedure (TCLP) is mineralogically very similar to the initial weak acid leach residue; the amounts of calcium sulphate are approximately the same in the two products. The principal Cd and Pb carriers are also the same as those noted in the initial residue, except that some dissolution and reprecipitation of Pb-Sr sulphate takes place. That the residue fails the TCLP test is likely a consequence of the superficial dissolution of Pb and Cd from species such as PbS04 or Zn-Pb-Fe-Cd silicate.

Jan 1, 1995

By Yuanbo Zhang, Xiaoming Mao, Zhixiong You, Zhenyu Fan, Tao Jiang

"It is generally known that the formation of calcium ferrite is favorable during the iron ore sintering, which dominatingly contributes to the improvement of strength and reducibility of the finished sinters. In this study, effects of roasting temperature and 02 content of inlet gas on the sintering mineralization properties of typical iron ores, including hematite, limonite, specularite and magnetite, were investigated. The results showed the amount of calcium ferrite initially increased then decreased with the increase of the roasting temperature. The temperature of maximum calcium ferrite generation amount for different iron ores was determined as follows: hematite and limonite was 1275 °C, whereas specularite and magnetite was 1250 °C. Increasing 02 content of inlet gas was advantageous to the generation of calcium ferrite during the sintering. The sequence of 02 content affecting the mineralization properties of different iron ores was determined as follows: magnetite > hematite > specularite > limonite.IntroductionThe mineralization property of iron ore plays a significant role in the mineral composition and microstructure of finished sinters, which determine the quality and output of the sinters [1-2]. The mineralization process of sinters is composed of solid-phase reaction, formation of liquid-phase and crystallization. The formation and crystallization of liquid-phase is the foundation to the mineralization as the quality of the sinter is poor when concreted by solid-phase consolidation [3-4]. With respect to the iron ore sintering, liquid-phase regarded as bonding phase is generated between the iron ores and fluxes at high temperature [5]. Calcium ferrite is the most favorable liquid-phase among the bonding phases which dominatingly contributes to the improvement of strength and reducibility of the finished sinters [6-8]. Especially for high iron-low silicon sintering and high basicity sintering, making sure sufficient calcium ferrite quantity and reasonable distribution is crucial to the sinters [9-10]. Therefore, carrying out the researches on the high temperature reaction properties of iron ores is of great significance [11]."

Jan 1, 2013

By James A. Voigt

"The efficient separation of metal species from aqueous streams by precipitation techniques requires a fundamental understanding of the various processes that occur during precipitation. These processes include particle nucleation, particle growth by solute deposition, agglomerate formation, and agglomerate break-up. The application of the population balance approach has been used to develop a kinetic model that accounts for these competing kinetic processes. The usefulness of the model is illustrated through its application to the precipitation of yttrium hydroxynitrate, YHN. The kinetic parameters calculated from the model equations and system specific solution chemistry are used to describe several aspects of the effect of pH on the precipitation of the YHN. Implications with respect to the simultaneous precipitation of more than one cation type are also discussed through use of example systems. The effects of solution chemistry, precipitator design, and solvent choice are considered.IntroductionThe application of precipitation technologies to the separation of metals from solution is widely used. Regardless of its application, be it in such diverse areas as the preparation of metal oxide powders for use in commercial products or as a unit operation in the removal of trace metals during wastewater clean up, the fundamental processes involved are the same. These processes include: nucleation from solution, either homogeneous or heterogeneous; growth from solution with chemical reaction either in solution or at the precipitate/solution interface; growth by particle agglomeration; and particle break-up by collisional or shear forces. The effectiveness of the operation and the properties of the precipitate formed, or ""quality"" of the product, are determined by the competing kinetics of the different processes. The kinetics of the processes, in tum, are determined by system-specific solution chemistries and the conditions used to carry out the precipitation operation. For example, generally, when system conditions are such that the supersaturation driving force for precipitation is very high, growth species normally do not have the time to organize themselves with a high degree of crystallographic order and the precipitate is amorphous. In this case nucleation rates are invariably extremely high and the primary mechanism for growth is the agglomeration of nuclei. Conversely, when the supersaturation levels for the same system are reduced, the kinetics of the nucleation and growth processes also are greatly reduced, and a crystalline precipitate can be formed, since the growth species have time to order on particle surfaces."

Jan 1, 1996

By Robert G. Robins

Precipitation of ferric arsenate is an effective method for removing arsenic(v) from hydrometallurgical process solutions. The solubility and stability of this compound. FeAs04.2H20, has received some attention in recent years and the reported solubilities of amorphous and crystalline material have varied considerably. This paper reviews previous studies and reports some recent work with a consistent model to explain the variable results. Free energy data for ferric arsenate and its associated dissolved complexes are presented.

Jan 1, 1990

By Liyuan Chai, Bing Peng, Ji Peng, Di Yu

"Electric arc furnace (EAF) stainless steel dust has been classified as a hazardous waste by various government regulatory agencies as it releases heavy metals to environment. The solidification of EAF dust is to stabilize the hazardous components to the amorphous silica-alumina-based clays. The process of solidification is investigated and the softening temperatures of dust and additive clay mixtures are measured for economical thermal treatment. The results indicate that the mixture of dust and local clay with the ratio of 1:1 has the lowest softening temperature 1100 °C and it could pass the toxicity characteristics leaching procedure (TCLP) test for the environmental regulatory limits after thermally treated at softening temperature for 15 min. Major phases of thermal solidification product clinker are CaAl2Si2O8, (Fe, Cr)2O3, (Fe, Mg)(Cr, Al)2O4 and Al6Si2O13.IntroductionThe yield of stainless steels in China arrived to 10 million tons in 2006 and more than 0.2 million tons of stainless steel dust are produced annually. Approximately 1-2 wt.% of scrap charged to an electric arc furnace (EAF) enters the off-gases and then is converted into the dust and reported to the bag-house. The disposal or landfill of the dust becomes a serious environmental problem in China due to the increased production of stainless steels in recent years. The dust contains elements such as chromium (Cr), nickel (Ni), lead (Pb), zinc (Zn), cadmium (Cd) and their solubility in leaching media exceeds the environmental regulatory limits [1]. Even though easily feasible for low-grade MgO, it is not appropriate to stabilize the heavy metals from the heavily contaminated soils after the dust landfill [2]. Several dust treatment technologies have been developed and they can be divided into two types. One is to recover the metals from the dust [3, 4] and another is to stabilize hazardous components present in the dust [5, 6]. Recycling of the dust generated in EAF is a remediation option for cleaner production. Direct recycling of EAF stainless steel dust was developed to recover the metal value from the dust and protect the environment [7], but it was only suitable for the dust with high contents of Ni, Cr and Fe. As for the dust with low valuable metal content, thermal solidification is an appropriate choice for the dust treatment."

Jan 1, 2012

By David Langberg

Recovery of dissolved copper from discard slags is a critical consideration affecting the economics of copper smelting. Slag cleaning is frequently carried out in electric furnaces, however reduction by injection of natural gas in a holding furnace may offer a lower cost alternative in some circumstances. As the residence time of the injected gas is short, the factors controlling the rate of reduction need to be clarified in order to optimise the design of the slag cleaning furnace. A series of medium scale (200 kg) reduction tests to investigate the rate of reduction of copper-containing slags by injection of natural gas-nitrogen mixtures between 1150-1250C was carried out by CSIRO Minerals. The composition of the gas in the top-space of the reactor was found to be significantly more reducing than the slag, indicating that thermodynamic equilibrium was not established between the slag and the gas in the bubble plume. An apparent first order rate law was observed between the rate of oxygen elimination from the bath and the magnetite concentration of the bath. The dissolved copper concentration was closely correlated with the oxygen potential of the slag, suggesting a partial equilibrium between the dissolved components of the slag. The utilisation efficiency of the natural gas decreased as the natural gas flow rate was increased. The results of the tests tend to indicate that the rate is controlled by a mixed reaction kinetics/ mass transport mechanism. The work was supported by Xstrata Copper ? Mt Isa Mines.

Jan 1, 2006

By Edilson Marques Magalhães, Danielly Da Silva Quaresma, José Antônio da Silva Souza, João Nazareno Nonato Quaresma, Emanuel Negrão Macêdo

"The production of alumina from bauxite using the Bayer process generates the residue known by red mud. This material can be used as a source for concentration and recovery of valuable metals such as titanium. The greatest difficulty of concentrating titanium compounds is the large amount of iron oxide present in red mud > 30% by weight. This paper shows the extraction of the iron oxide, increasing the concentration of the titanium compounds. The red mud is leached with H2SO4 at 30% concentration and temperature range of 60°C, 80°C and 90°C. Analysis of the leached and concentrated was made to verify the effectiveness of the iron oxide extracting process and the titanium compounds concentration viability.2- IntroductionIn the state of Para is located the Industrial Unit Alumina of North of the Brazil S/A (Alunorte), created to produce and commercialize alumina, aluminum oxide, Al2O3. The ALUNORTE with Aluminum Brasileiro S/A (Albras) and Mining Rio do Norte S/A (MRN) complete the production cycle of aluminum in the state. Although the production of alumina has a importance great for the socio-economic status, as in any area other, generates a amount large of waste, thus causing environmental impacts. Pará State has produced 25 million tons of bauxite (Pinto, 2010), of which 60% were transformed into alumina plant in Pará and Maranhão by ALUNORTE by ALCOA, generating approximately 9,000,000 tons of waste known as Red Mud (RM). Due to the high reactivity this material is considered dangerous, and currently there is no operating process capable of reuse all the material produced at any refinery. The search for industrial processes in order to reuse these wastes can contribute to reducing the overall impact of the production process of alumina. In this context, this paper estudied, within the research line of Solid Waste valorization the mining industry and metallurgy, a process that makes possible the red mud as a source of raw material, in other words, seeks to maximize the use of red mud as raw material for concentration and or recovery of titanium compounds in both the crystalline form of anatase, rutile and ilmenite, avoiding the predatory extraction of natural resources of these materials. Applying definitely the concept of self-sustainability of the mining industry and metallurgy."

Jan 1, 2012

By P. Hanniala

In the day-to-day life the copper business of today is influenced directly by the ever-increasing general concern about the environment. In addition to that the inherent shortcomings of the copper smelting business, have since many years been the falling real price level of the metals and the relatively high initial capital investments required for the production units. These shortcomings have been compensated for by high productivity, low specific operating costs, low metal inventory and unbeatable technological superiority. Thus today more than 50 % of the world primary copper is today produced by utilizing Outokumpu Flash Smelting Technology. This figure is expected to grow at an increasing speed in the near future. Characteristic for the Outokumpu Flash Smelting technology is high flexibility for a wide grade of concentrates and the highest sulfur capture owing to at the same time competitive investment and operational costs. The Flash Converting technology offers new options for copper production and optimization of the mine- concentrator-smelter production chain. In the following years it is expected that the trend in copper making is that higher grade concentrates are produced at the mines. Thus increasing amount of high grade concentrate will be available for direct-to- blister Flash Smelting causing an overall cost reduction in copper smelting i.e. both in capital and operational costs. In the '90s new technologies based on Outokumpu Flash Smelting technology have been taken into operation, thus eliminating the non-continuous Peirce-Smith converting process step. New innovative solutions have been used in the latest projects, as in Kennecott Utah Copper, where the new Kennecott-Outokumpu Flash Converting process was started up in 1995. Also, in 1995 the new DON process was started at Outokumpu Harjavalta nickel smelter followed by the Fortaleza nickel smelter in Brazil in 1997. The aim of the continuous development work at Outokumpu has been the expansion of the direct-to-blister process towards lower grade concentrates. The most recent example of this is the start-up at the Olympic Dam smelter in Australia, where the existing direct-to-blister Flash Smelting furnace was replaced with a new one having a capacity of 200 000 t blister copper per annum in just one smelting step.

Jan 1, 1999

By Leonardo Mota, Lucas L. da Costa, Milton B. Filho, Sergio N. Monteiro, Helion Vargas, Tammy G. R. Portela da Silva

"A natural biofoam extracted from the buriti palm tree has shown characteristics for potential substitution of synthetic foams. In the present work, a photoacoustic thermal characterization was performed on buriti biofoam samples. An open photoacoustic cell technique and a photothermal rise method performed under continuous laser illumination were employed in order to determine the thermal diffusivity and the specific heat capacity of such material. In addition to their intrinsic values (finger print), these physical parameters represent the light-into-heat conversion efficiency and the amount of heat stored per unit volume, respectively. The results showed that the buriti biofoam presents thermal properties that permit its use as an effective insulation material.IntroductionSolid foams are very light materials with increasing engineering applications [1]. A natural biofoam obtained from the petiole of the buriti palm tree (Mauritia flexuosa) has been recently investigated [2-4]. The evaluation of the buriti biofoam properties and the characterization of its microstructural aspects have shown that this biofoam has a potential as a new engineering material with very low density. Additionally, its reduced open porosity and low absorbed humidity revealed a promising material for packing and floating applications. In fact, this buriti biofoam, extracted from the palm tree natural of the north region of Brazil, is being used by the low income population as a modest substitute for Styrofoam® [1].As a potential insulating material, the buriti foam needs to be characterized in terms of its thermal and acoustic properties. A preliminary investigation [3] on the thermal behavior of this natural biofoam by thermogravimetric analysis, TGA, and its derivative, DTG, as well as differential scanning calorimetry, DSC, revealed parametric conditions associated with water loss and structural decomposition. Both the surface humidity and the release of hydration water were determined. Different decomposition events were attributed to both, more rigid as well as to more flexible molecular segments. Table 1 depicts technical data obtained so far for the buriti biofoam. These data are compared to those corresponding to Styrofoam®."

Jan 1, 2011