By F. D. Rosi, C. A. Dube, B. H. Alexander

WHEN a deformed polpcrystalline metal is heated to a sufficiently high temperature, a recrystallized structure develops which consists of small, essentially stress-free grains. This transformation is referred to as primary recrystallization. Under certain conditions, on prolonged annealing of the specimens, a type of grain coarsening occurs in which a small number of grains commence to grow at various points by devouring the neighboring finegrained primary structure, which, in itself, exhibits a marked stability toward normal grain growth. This grain coarsening process has been referred to by Burgers' as "secondary recrystallization" or "exaggerated grain growth." Although much work has been done on recrystallization and growth processes, present knowledge of the factors which determine the occurrence and growth of secondary grains is inadequate for the advancement of a theory which accounts for the observed characteristics of this recrystallization phenomenon. In this respect, it would be important to make measurements of the velocity of growth of these large secondary grains. The early work of Feitnecht2 on aluminum showed that the size of secondary grains increased with temperature and time, suggesting that such measurements would be possible. More recently, Burgers1 found that the growth velocity of these grains in aluminum was constant over a large time interval, as is generally found for the growth velocity of primary grains in a uniformly deformed test piece.3-5 It is reasonable to expect that the determination of the activation energy of the secondary growth process might lead to a better understanding of the underlying atomic mechanism. This investigation, therefore, is one of a series primarily designed to measure the growth velocity of secondary grains at various temperatures for silver, copper, and aluminum. It is hoped that these studies along with those of orientation relationships, will establish a sound basis for theorizing as to the origin and nature of the secondary transformation. Experimental Procedure The metal used in the present investigation was high-purity silver (999.9 fine), which was supplied in the form of cold-rolled plates 0.250 in. thick. These plates were annealed at 500°C for 1 hr and then straight-rolled to a thickness of 0.04 in. in three reductions of approximately 45 pct, followed in each case by an anneal at 450°C for 1/2 hr. The 0.04 in. sheets were given a final reduction of approximately 50 pct, which resulted in a thickness of 0.02 in., thereby insuring two-dimensional crystal growth. Individual specimens of this material about 1x3 cm were used for all heat treatments, unless otherwise noted. The annealing was carried out under an atmosphere of argon in an Inconel tube furnace whose temperature was controlled to within -+2°C. Metallographic examination of the secondary transformation was accomplished by mechanically polishing the specimens on one side to approximately one half their thickness through 2/0 metallographic emery paper, and then electrolytically polishing in a solution of potassium ferrocyanide and sodium cyanide. With a current density of approximately 20 amp per sq dm, the time required to obtain a satisfactory surface varied from 3 to 5 min. Standard potassium bichromate was used to etch the electrolytically polished surfaces. A heavy etch with this solution produced a sharp contrast between the secondary grains and the fine-grained primary structure, darkening the latter while leaving the large secondary grains bright. All area measurements of the secondary crystals were made with a planimeter on enlarged tracings of the grains.

Jan 1, 1953

By M. J. Marcinkowski, A. S. Sastri

A detailed compressive stress-strain analysis and transmission electron microscopy investigation has been made of the deformation behavior occurring in a 50 at. pct Ni-Ti (hypoeutectoid) alloy and a 54.5 at. pct Ni-Ti (hypereutectoid) alloy. In the case of the hypoeutectoid alloy, three stages of work hardening are observed. Stage I occurs at a very low stress and is associated with plastic deformation via martensite formation. Stage 11 is characterized by very rapid work hardening and is due to difficulties in causing further deformation in the fine martensite aggregate produced in Stage I. Stage III which occurs at very high stress levels is characterized by smaller work hardening rates and is due to the plastic deformation arising from alternate reconversions of the original martensites to martensites of varying orientation. Rapid quenching of the hypereutectoid alloy leads to very high yield strengths and is related to a fine precipitate dispersion that such treatment brings about. The present investigation represents the final phase of a three-part study directed toward an understanding of the solid-state transformations in near equi-atomic Ni-Ti alloys as well as the deformation mechanisms associated with these alloys. In the first part,"2 to be henceforth referred to as I, it was found that alternate simple shears on {112} planes and in (111) directions convert the parent B2 structure in the equiatomic NiTi alloy into two distinct close-packed monoclinic martensites. All of the marten-sites were of this type, whether they were formed by cooling or by plastic deformation, whether induced to form in bulk samples or in thin foils, or whether examined in the electron microscope at room temperature or below. On the other hand, in the second part of this investigation,3 to be reffered to as 11, it was shown that upon slow cooling to about 640°C. alloys in the neighborhood of NiTi which possess the B2 structure transform eutectoidally into their equilibrium phases Ti2Ni and TiNi3. However, preceding the formation of these equilibrium phases a series of metastable intermediate phases are formed. This paper will set as its goal the elucidation of the remarkable deformation behavior exhibited by NiTi. In particular, Buehler and Wiley4 have found equiatomic NiTi to be surprisingly soft, while Buehler et al.5 have shown this alloy to possess a memory effect: i.e., upon bending at room temperature it will revert to its original shape when heated to above about 50°C. In I it was shown that NiTi was soft in the sense that the yield stress was low; nevertheless, the alloy work-hardened at an extremely rapid rate to very high stress levels. On the other hand, the hypereutectoid alloys with somewhat higher nickel, say 54.5 at. pct (60 wt pct) have enormously increased yield strengths compared to those of the equiatomic alloys. In order to determine the atomistic processes giving rise to the above behavior, it was decided to examine samples that were wafered from bulk specimens deformed in compression to various strains using the techniques of transmission electron microscopy. EXPERIMENTAL TECHNIQUE All of the alloys used in the present investigation contained either 50 at. pct Ni (55.06 wt pct) or 54.5 at. pct Ni (60 wt pct) and were arc-melted in the form of a finger using the same techniques described in I and II. The finger was capsulated in a stainless-steel jacket and swaged at 850°C into rods. Compression specimens 0.300 in, long and 0.200 in. in diam were machined from these rods. In order to completely re-crystallize the samples and remove residual stresses, all of them were capsulated in evacuated quartz, annealed for 1/2 at 1050°C. and then furnace-cooled. Compression tests were carried out in an Instron tensile testing machine covering a range of temperatures from —196° to 200°C using procedures described previously.6'7 In all cases crosshead speed was 0.02 in. per min. Wafers 0.015 in. thick were spark-cut from the cylindrical samples at 45 deg to the compression axes after they had been deformed to the desired strain. These specimens were then spark-planed to about 0.005 in. and then electrochemically thinned for examination by transmission electron microscopy as described in I.

Jan 1, 1969

By D. Atkinson, C. Bodsworth, I. M. Davidson

A geometric model of interstitial solid solutions, which has been used previously as a basis for the prediction of carbon activities in Fe-C austenite, is shown to serve also for the calculation of nitrogen activities in Fe-N austenite. The model has been developed to enable predictions to be made of the activities of an interstitial element in the presence of two host atom species. The activities calculated via the model are shown to be in satisfactory agreement with the measured values in the austenite phase for carbon in Fe-C-Co, Fe-C-Cr, Fe-C-Ni, Fe-C-~n, Fe-C-Si, and Fe-C-V alloys and for nitrogen in Fe-N-Ni alloys. The effect of the second substitu-tional solute on the logarithm of the activity of the interstitial element is expressed as the product of a constant mad the atomic concentration of that solute. The constants so derived we related to the thermo-dynamic interaction coefficients which describe the effect on the activity coefficient of carbon of an added solute element. In recent years the thermodynamic activities of carbon and nitrogen in the single-phase austenite field have been determined for iron binary alloys and for several iron-base ternary alloys. In order to extend the use of these measurements, it is desirable to be able to predict with reasonable accuracy the activities of the interstitials at compositions and temperatures other than those which have been measured experimentally. In all the systems studied to date, the interstitial elements do not conform to ideal behavior. Hence, the available data cannot be extrapolated or interpolated using the simple thermodynamic concepts of solutions. Several models have, therefore, been formulated for the purpose of predicting the activity of an interstitial element in the presence of one species of host atom. These models can be divided into the geometric1"5 and energetic6-' types. The former group is based on the assumption that at low concentrations the activity of the interstitial species is determined by a composition-dependent configurational entropy term and an excess free-energy term which is temperature-dependent but independent of composition. The purpose of this paper is to show that the treatment, based on a geometric model, can be extended to enable predictions to be made of interstitial activities in the presence of two substitutional host atom species. THE CONFIGURATIONAL ENTROPY OF MIXING ICaufman5 has shown that the configurational entropy, S,, for a binary solution comprising of a host atom species, A, and an interstitial species, I, can be expressed as: where NI is the atom fraction of the interstitial species, R is the gas constant, and (2 - 1) is the number of interstitial sites excluded from occupancy by the strain field around each added interstitial atom. The number of interstitial sites per host atom, p, is unityg for the fcc austenite solutions considered here. The configurational entropy of mixing for a ternary solution comprising two substitutional atom species, A and B, and one interstitial species, I, can be derived similarly. Let the number of atoms per mole of each of these species in the solution be represented by «a, ng, and nI. From geometric considerations, it is improbable that the addition of a few atom percent of a second host atom species will change the type of sites (i.e., octahedral) in which the interstitial atom can be accommodated in the austenite lattice. At higher concentrations (determined largely by the relative atomic radii of the atomic species present and any tendency to nonrandom occupancy of the host lattice sites) other types of interstitial sites may become energetically favorable. Restricting consideration to compositions below this limit, for 1 = 1 the number of suitable interstitial sites is given by (n + nB). However, if each interstitial atom excludes from occupancy (Z - 1) additional sites, the total number of sites available for occupation is reduced to (n + ng)/Z. The number of vacant interstitial sites is given by: The total number of recognizable permutations of the atoms must include the recognizable, different configurations of the A and B atoms on the host lattice. Assuming that these arrangements are purely random, and are not affected by the presence of the interstitial species, the total number of recognizable permutations in the ternary alloy is given by: The configurational entropy is obtained by expanding, using Stirling's approximation, and collecting like items, as:

Jan 1, 1969

By G. P. Boomsliter

IN previous discussions on stresses in hoisting ropes, little has "been said concerning the effect of the elasticity of the rope itself on the stresses due to acceleration. Laschinger1 has calculated acceleration stresses. for several cases but he has ignored the elasticity of the rope as a factor, except as it compresses the drum and stretches itself as it winds thereon. He also deals with steam plants and he shows the effect of the "jerky" start of the engine. This effect would actually be reduced by the elasticity of the cable. With the advent of the motor-driven hoist, new conditions have arisen. The jerk mentioned by Laschinger has been eliminated and smoother starting made possible. But the elastic properties of the rope seem to introduce considerable periodic acceleration stresses in the rope. The following discussion of acceleration stresses is based on the assumption of a constant acceleration at the drum. To be exact, the mathematical work is based upon the assumption that the top is moving upward with a constant acceleration, and ignores the fact that the cable is shortening as it winds. However, the effect of the shortening would be inconsiderable during the first part of the acceleration period. Most hoisting engineers make the assumption of constant acceleration at the drum. Under the older method of calculating acceleration stresses, this would be true with a constant torque motor. But if stresses vary, as this paper attempts to show that they do, constant torque would not give constant acceleration, although the velocity-time curves obtained in the full size test herein described showed that they approach rather closely to this condition, at least as nearly as could be measured.

Jan 2, 1927

By J. C. Norman

Jan 1, 1985

By R. P. King

The two-phase distributed-parameter kinetic model for flotation has been wed as the basis for a digital simulation of flotation plants of arbitrary configuration. Ores that contain any number of minerals can be handled. The effects of incomplete liberation and particle-size distribution are specifically allowed for. The simulator allows the investigation of variations in throughput and in the slurry density of the feed, and of variations in stage volumes and aeration rates. It can handle cell behavior even under conditions of hindered flotation. The requirements for data preparation are completely documented so that the computer program is suitable for general-purpose use. The program is written in Fortran. The output from the simulator consists of the complete material flows in the plant, as well as the grade, recovery, and particle-size distribution in each stream.

Jan 1, 1976

By Joseph P. Lyden

In the Picher field, structure made openings for the circulation of the mineralizing solutions by flexing, shearing, and fracturing the sedimentary beds. This structure is used with the spatial and genetic relationship of the ore minerals, sphalerite and galena, and the gangue minerals, dolomite and jasperoid, in prospecting for ore bodies.

Jan 12, 1950

Jan 12, 1950

By W. A. Tiller, S. O’Hara

Grain refinement in stirred melts has previously been shown to arise from dendrite segmentation. The present work discusses experiments capable of distinguishing between remelting and mechanical effects which result from fluid motion. Nucleation of still un-dercooled Sn-1 pct Pb melts with a single-crystal seed shows that the grain size of the resulting ingots decreases as the undercooling at nucleation increases up to about 1Z0C, then increases again for larger undercoolings. Pure melts exhibit little refinement as a result of nucleation at any undercooling up to 12°C. The presence of fluid motion gives rise to grain multiplication in pure melts, but the magnitude of this effect is partly obscured by solid-state pain growth. The results indicate that two grain-multiplication pvocesses can operate, one which involves dendrite remelt ing, and another associated with fluid motion. Small ingot experiments indicated that an equiaxed transition can be caused by fluid motion. THE presence of forced convection during recales-cence of undercooled Sn-1.3 pct Pb melts has been shown to give rise to extensive grain refinement during solidification of small ingots of this alloy.''2 In Ref. 2, this refining was shown to result entirely from dendrite fragmentation and not from any nucleation mechanism. The purpose of the present work is to establish what processes lead to dendrite segmentation. Experiments were therefore carried out to determine the resulting structure of both pure tin and Sn-1 pct Pb melts, nucleated at various undercoolings by single-crystal seeds in the absence of forced or natural convection. By comparing the information obtained from these experiments with the results of Refs. 1 and 2, the effects of fluid motion on the ingot structure, and the details of the segmentation mechanisms, should become clear. The results of these experiments should also be helpful in understanding the solidification structures of larger ingots since natural convection, which is known to play an important role in determining ingot structure13 differs only in degree from the fluid-motion effects studied here. I) EXPERIMENTAL PROCEDURE The apparatus shown in Fig. 1 was constructed to permit controlled nucleation of stirred or unstirred supercooled melts using a seed oriented in the tin dendrite growth direction. Because the melts, in all cases, were capable of larger supercoolings than the one used in each experiment, the structure observed always resulted from a single nucleation event at the surface. The sequential procedure was as follows: Tin was melted under purified hydrogen and the oxide removed at a temperature of 450°C . Electromagnetic stirring was then used to clear the surface completely and during this time the guide tube was lowered underneath the melt surface. A pointed Czochralski-like crystal was then propagated from a specially prepared tin dendrite seed4 inside the guide tube while the temperature of the bulk melt was held just above the melting point, ensuring a perfectly clean seed which was epitaxial with the original dendrite. The dendrite and epitaxial seed, still in the guide tube, were withdrawn from the melt which, in turn, was undercooled to 2C° below the temperature at which the nucleation experiment was to be performed. The melt was held there for several minutes, both in stirred and in still-melt experiments. The temperature was next raised to the required value and the melt nucleated by the carrot seed inside the guide tube, the heater power being shut off just after nucleation. In experiments where quenching after nucleation was required, a high-density graphite crucible was used, but otherwise the procedure was as described above. The temperature gradient in the melt before nucleation was kept below 1C° per cm by carrying the experiment out just below the center of the heater shown in Fig. 1.

Jan 1, 1968

By Alan J. Strauss

The Group IV elements germanium, tin, and lead form nine 1:1 compounds with the Group VI elements sulfur, selenium, and tellurium. This paper reviews the properties of the pseudobinary solid solutions formed by these compounds, including the extent of mutual solid solubility, temperature-composition phase diagrams, transport properties, deviations from stoichiometry, optical properties, and energy band structure. Particular emphasis is placed on the Pbl-xSnxTe and Pb1-xSn,Se alloys with rocksalt structure, because of current interest in these malerials for generating and detecting infrared ,radiation. ThE Group IV elements germanium, tin, and lead form nine 1:1 compounds with the Group VI elements sulfur, selenium, and tellurium. Some of the physical and electronic properties of these compounds, including their melting points1-8 and energy gaps,4'9-12 are listed in Table I. Four compounds (SnTe, PbS, PbSe, and PbTe) have the cubic rocksalt (Bl) structure. At room temperature GeTe has a rhombohedra1 structure closely related to the B1 structure, into which it is transformed at about 400°C. Four compounds (GeS, GeSe, SnS, and SnSe) have the orthorhombic B29 structure. In samples which have not been intentionally doped with impurities, the electrical conductivity is due primarily to electrons or holes produced by the ionization of donor or acceptor lattice defects associated with deviations from stoichiometry. Undoped samples of PbS, PbSe, and PbTe may be either n type or p type, depending on whether they contain excess lead or an excess of the Group VI element, respectively, but only p-type samples of the other compounds have been reported. This paper will review the properties of the pseudo-binary solid solutions formed by the nine 1:l compounds. The topics to be considered include the extent of mutual solid solubility, temperature-composition phase diagrams, transport properties, deviations from stoichiometry, optical properties, and band structure. Particular emphasis will be placed on the Pb]-xSnxTe and Pbl-xSnxSe alloys with B1 structure, which are promising materials for generating and detecting infrared radiation in the 8 to 14 µm atmospheric window and beyond. MUTUAL SOLID SOLUBILITY The extent of mutual solid solubility in the pseudo-binary systems has been investigated for fourteen of the eighteen ternary systems (in which the two terminal compounds have a common element) and for nine of the eighteen quaternary systems. In most cases, X-ray diffraction measurements made at room temperature were used to determine the structure and lattice parameter(s) of the phase(s) present in samples of various compositions prepared by freezing from the melt. In many investigations, including the extensive studies of Krebs and co-workers,13'14 the samples were annealed at elevated temperatures before X-ray measurements were made. In some cases, metallographic examination and thermal analysis have also been employed. The results for the ternary and quaternary systems are summarized in Tables II and III, respectively. (The original references should be consulted for the annealing temperatures.) The solubility of one compound in the other is at least 5 mol pct in all cases, and is often much larger. Complete solid solubility has been observed in all systems so far investigated in which the terminal compounds have the same structure, although in the PbS-PbTe system complete solubility is limited to elevated temperatures. Thus complete solid solubility occurs in five systems where both compounds have the B1 structure (SnTe-PbTe, PbS-PbSe, PbS-PbTe at temperatures above 805°C, PbSe-PbTe, and SnTe-PbSe) and in three where both compounds have the B29 structure (GeS-SnS. GeSe-~n~e-, and SnS-SnSe), as well as in two involving GeTe and a compound with B1 structure (GeTe-SnTe and GeTe-PbTe). On the basis of thermal analysis data, complete solid solubility at sufficiently high temperatures has also been reported for the GeSe-GeTe2 and SnS- pbS22 systems. This seems unlikely, however,

Jan 1, 1969

By R. I. Jaffee, C. M. Craighead, G. A. Lenning

The a-p type alloys are subject to a loss of tensile ductility with increasing hydrogen content. No hydride phase is visible in embrittled a-B type alloys. The embrittlement encountered appeared to be of the strain-aging type. Both compositional and structural factors are shown to influence the hydrogen tolerance of a-B type alloys. IN previous papers by the authors, the effects of hydrogen on the structure and mechanical properties of high-purity and commercial-purity titanium were described. It was shown that the presence of hydrogen in these materials results in a hydride phase having low solubility at room temperature. This insoluble phase had little effect on the room temperature tensile properties, but did decrease the notch-bar toughness to a large degree. The binary Ti-H systemz indicates that hydrogen is much more soluble in £ than in a-titanium. Hence, it is not expected that the embrittling effects of hydrogen in a-fi alloys will be similar to that found in a alloys. Materials of this type studied in the present investigation included two commercial a-/3 alloys, Ti-8Mn and Ti-4A1-4Mn; three high-purity Ti-Mn alloys containing 3, 6, and 9 pct Mn; and four high-purity Ti-Mo alloys, Ti-SMo, Ti-10.9M0, Ti-13.1 M0, and Ti-20M0, of the a-B and B types. Materials and Fabrication—The high-purity base alloys, composed of iodide titanium and high-purity metals, were prepared by double arc melting under argon in a water-cooled copper crucible, using a water-cooled tungsten electrode. Radiographic examination showed homogeneous Ti-Mo alloys. The analyses of the alloys used in this investigation and their as-fabricated hydrogen content, where determined, are listed in Table I. The two commercial alloys were 1/2 and % in. diam bar stock. No analyses other than hydrogen content were made. In order to maintain the a-B relationship existing in the two commercial alloys, vacuum annealing and hydrogenation were carried out in the B field prior to final fabrication. Fabrication then was done by The three high-purity Ti-Mn alloys were forged to 3/4 in. diam rods at 1600°F, and hot swaged to 1/2 in. diam at 1380°F. Machined and degreased bar stock was vacuum annealed or hydrogenated, fabricated to 1/8 in. diam rod by hot swaging, annealed in argon for 1 hr at 1380°F !75O°C), and water quenched. The six yz lb Ti-Mo ingots were forged to Wi in. diam rods at 1600°F and then hot swaged to % in. diam. Machined and degreased specimens were vacuum annealed or hydrogenated in the /3 field, prior to fabrication, by swaging to Y4 in. rod at 1400°F. After fabrication, the 5 and 10.9 pct Mo alloys were annealed in argon for 16 hr at 1290°F and water quenched to give equiaxed a-B structures. The higher molybdenum content alloys were argon annealed 4 hr at 1470°F and water quenched to give all £ structures.

Jan 1, 1957

By J. H. Brophy

Experimental evidence in recent years shows that nickel coated hydrogen reduced tungsten powder can be sintered to 98 pct of theoretical density at 1100°C. New data indicate that the sintering rate is the same for nickel contents ranging from 0.125 wt pct (mon-atomic layer) to 5.0 wt pct Ni coated on 0.561. tungsten powder. Nickel tungsten made by coreduction from oxides sinters in a kinetically similar way, but the rate tends to increase with higher nickel contents. The activation of sintering can be accomplished with a minimum amount of nickel if coated powder is used. Transverse rmpture strength was found to increase in specimens containing 0.25 pct Ni as density increased during the initial stage of the carrier-phase sintering process. Upon the onset of grain growth in the final stage, strength was found to decrease. With increasing nickel contents up to 4 pct, strength increased. Maximum strengths in three-point loading were observed at 73,000 psi for 0.25 pct Ni and 93,000 psi for 5 pct Ni. These were comparable to that of massive tungsten recrystal-lized in the presence of nickel and tested in the same way. The results were sensitive to the mode of powder treatment and ductility was negligible in all cases. The study and application of sintered bodies of nickel and tungsten is not new; however, the analysis of the mechanism by which small additions of nickel increase the sintering rate of tungsten promises to Contribute new information regarding sintering theory in general. Initial experimental evidence was presented by the authors showing that nickel-coated hydrogen-reduced tungsten powder may be sintered to 98 pct of theoretical density at 1100°C in 16 hr.' Simultaneously, a kinetic analysis of the process showed that it took place in two distinct stages. In the first stage, nickel evidently served as a carrier phase through which tungsten atoms could move. This stage was kinetically similar to the 'solution-precipitationo step postulated when the carrier phase is liquid3 although in the nickel tungsten case, there is no evidence of the existence of a liquid phase either in equilibrium phase relationships or in mi-crostructures at the temperatures under consideration. In the present work, new data for nickel-coated tungsten powder are offered in support of the proposed mechanism, and a more explicit study of the second stage of densification is presented. Concurrently, the sintering kinetics of these coated powders are compared to Ni-W powder made by coreduction of oxides. In this way the present work can be compared to earlier results in nickel activated sintering of tungsten in which the coreduction process was emplyed. The ultimate utility of such an activated sintering process will be determined to some extent by the mechanical and physical properties of the final prod-

Jan 1, 1962

[ ]

Jan 1, 1938

By R. I. Jaffee, C. M. Craighead, G. A. Lenning

The effects of increasing hydrogen content, introducing a notch, and changing the strain rate on properties of titanium and one of its alloys were investigated over a range of testing temperatures from —196° to 200°C. Both high purity and commercial purity A-55 titanium were used as representative a materials, while a commercial Ti-8 pct Mn alloy was used for an a-P alloy. It was found possible to analyze the data, using the ductile-to-brittle transition temperature concept. Increasing hydrogen, the presence of a notch, and increasing the testing speed raised the transition temperature for the a materials. The presence of hydrogen and notches raised the transition temperature of the a-B alloy also. However, increasing the testing speed generally decreased the transition temperature of the a-p alloy. IN previous papers, the authors have shown that hydrogen is most detrimental to the notch-bend impact toughness of a-titanium' and to the tensile ductility of a-B titanium alloys.' These general effects have been confirmed by Kessler and co-workers," and by Kotfila and Erbin." Kessler showed that the slower strain rate in notch-rupture tests was a more sensitive measure of hydrogen embrittle-ment of a-B alloys than the tensile test. In the present paper the authors cover, with tensile and notch-bend tests, the effect of testing speed, notches, and testing temperature on hydrogen em-brittlement. High purity and commercial purity titanium, examples of u materials, and a commercial a-,f3 Ti-8 pct Mn alloy were investigated. The purpose of the investigation was to correlate the factors producing embrittlement. Materials The high purity titanium for this investigation was obtained by arc-melting crystal bar from Foote Mineral Co. into 1 Ib ingots. As-cast hardnesses for these ingots ranged from 60 to 90 Brinell. The arc-melted ingots were forged to % in. diam rods at 1470°F. These rods were swaged to & in. diam at room temperature prior to machining of the specimens for hydrogenation and testing. The commercial A-55 titanium and the Ti-8 pct Mn alloy were obtained from Rem-Cru Titanium Inc., as % in. diam rod. The A-55 titanium was hot swaged to 1/4 in. diam at 1300°F prior to machining of the specimens for hydrogenation and testing. The a-p C-11OM alloy was hydrogenated prior to hot swaging to 1/4 in. roc1 at 1300°F. Hydrogenation prior to fabrication permitted testing of the a-P alloy in the equilibrated and stabilized condition. The equilibration and stabilization treatment used was an air anneal for 1 hr at 1300°F, followed by furnace cooling to 1100°F and then air cooling. Hydrogenation was done in a Sieverts apparatus described previously.' The hydrogenation treatment consisted of heating for 1/4 to 1/2 hr at 820 °C in purified hydrogen, slow cooling to 680"C, holding 1 hr for homogenization, and rapid cooling to room temperature. Intended hydrogen levels for the a-tita-nium materials were 0.05, 0.5, 1.0, 1.5, and 2.0 atomic pct—about 15 to 430 ppm. For the Ti-8 pct Mn alloy, the intended hydrogen levels were 0.05, 0.5, 1.0, 2.5, and 5.0 atomic pct—about 15 to 1100 ppm. The material for the 0.5 atomic pct level of hydrogen was vacuum annealed prior to hydrogenation to increase the accuracy of the addition. Vacuum annealing to remove hydrogen consisted of heating for 6 hr at 820°C, and resulted in a hydrogen content of about 10 to 15 ppm. When hydrogen contents were above 0.5 atomic pct—100 ppm—the hydrogen was added without prior vacuum annealing.

Jan 1, 1957

By Raymond L. Orr

Calorimetric measurements have been made of the heats of solution of gold axd indium in a number of liquid tin-rich alloys at a temperature of 705°K. Relative partial molar enthalpies of gold were determined as a function of dilute solute concentrations in the binary Au-Sn system and in the ternary Ag-Au-Sn and Au-In-Sn systems. Relative partial molar enthalpies of indium were determined for dilute solute concentrations in the In-Sn, Ag-In-Sn, and Au-In-Sn systems. Through application of the interaction coefficient concept introduced by Wagner and more recently extended by Lupis and Elliott, ualues have been obtained for the Au-Au, Ag-Au, Au-In, and Ag-In enthalpy interaction coefficients in liquid tin. The results are inte@reted in terms of solute atom distributions through comparisons with the predictions of dilute solution models. INTEREST in the thermodynamic behavior of dilute liquid alloys stems from two primary sources. From a practical viewpoint, it is often of importance to know or to be able to predict the effect that one solute will have on the thermodynamic properties of the other solutes in a multicomponent system. Studies of dilute solutions may also be rewarding from the theoretical point of view. Some of the difficulties arising from the more complex interactions possible in concentrated solutions are avoided, leading to easier interpretations in terms of solutibn models and bonding energies. For example, in a binary alloy the limiting values of the partial molar properties of the solute represent the case for which each solute atom is completely surrounded by atoms of the solvent, and no other interactions are possible. Solute - solute interactions in dilute solutions are conveniently treated by the interaction coefficient concept of ~agner.' Using a Taylor series expansion for the logarithm of the activity coefficient, In yi, of a component, i, in a solution consisting of dilute solutes with atomic fractions xi, xj, xk, and so forth, in a solvent, s, and neglecting the second- and higher-order terms, Wagner obtained the expression: Where Wheyz is the limiting value of yi in the pure solvent, s. The interaction coefficients, e:, e:, and so forth, are defined by: Since yi is related to the excess partial molar Gibbs energy of component i by GfS = RT In yi, E: is re- ferred to as the "Gibbs energy interaction coefficient". Lupis and Elliott~ extended Wagner's treatment to the relative partial molar enthalpy, aHi, and the excess partial molar entropy, qS. They defined the enthalpy interaction coefficient as: and the excess entropy interaction coefficient as: leading to expressions similar to Eq. [I]: The three interaction coefficients are related by? The self-interaction coefficients, E:,qf,and at, represent the effects of interactions between atoms of component i in solvent s; €3, q{, and 03 represent the effects of interactions between i and j atoms in solvent s; and so forth. From the Maxwell-type relationships between partial molar quantities, it may be shown1'2 that e{ = ej, r}\ =tj), and ai - crj. Experimental determination of the interaction coefficients requires extremely precise measurements of the appropriate properties as functions of solute concentrations in very dilute regions. Few such data exist for intermetallic alloys, even for binary systems, because of experimental difficulties. This is especially true with respect to enthalpy data for dilute alloys. Examination of the compilation of data for binary alloys by Hultgren, Orr, Anderson, and ~elle~~ reveals that determination of limiting values of &fii(Xi =0) often requires extrapolations to infinite dilution from xi = 0.05 to 0.10. Direct measurements of the enthalpy interaction coefficient, qi, for multicomponent systems are virtually nonexistent. This quantity is of course subject to direct calorimetric measurement, but its determination must be limited to cases where high experimental precision is possible. The heats of solution of gold and indium in liquid tin can be measured with relatively high precision, which makes determinations of 73 involving these metals as the measured solutes experimentally attractive. This paper presents the results of such determinations of the Au-Au, Ag-Au, Au-In, and Ag-In enthalpy interaction coefficients in liquid tin. MODELS FOR DILUTE-SOLUTION BEHAVIOR Random-Solution Behavior. In the quasi-chemical treatment of solutions, only nearest-neighbor bonds are considered, and a composition independent value

Jan 1, 1967

Jan 1, 1908

By Joseph Jensen

FROM Aug. 31, 1937, until Apr. 30, 1939, there were 40,872,610 bbl. of oil run to storage in California; from Apr. 30, 1939, to Aug. 31 of the same year 5,512,912 bbl. were withdrawn from storage. But from Aug. 31, 1937, to Aug. 31, 1939, the number of producing wells in the state has increased from 17,706, with a potential production of 1,323,202 bbl., to 18,910, with a potential of 2,302,282 bbl. Thus, in a period of two years, during the first 20 months stocks increased over 1/3 and during the following four months stocks decreased 1/30. In the same two years the number of productive wells increased 1/15 and potential increased 3/4. Undoubtedly, the large increase in stocks created the pressure that caused the reduction in stocks that followed; yet this has come about in spite of the larger number of wells and higher potential. Cause of the change was the adoption on May 17, 1939, by the Central Committee of California Oil Producers of a uniform method of oil curtail-ment for all wells throughout the state. Acceptance of the method in the four months following adoption by practically all fields in California indicates that producers generally are convinced of its merit and fairness. True, some operators still overproduce, but the restraint practiced by the remainder of the industry has been sufficient to turn a situation headed for chaos into one of reasonable stability. Credit for this change goes to the industry itself, because it has all been accomplished under voluntary oil curtailment.

Jan 1, 1940

By Donald B. Evans, Robert D. Pehlke

The solubility of nilrogen in liquid binary alloys of iron with Litanium. zivconium, columbium, vanndiurn, and tantalum was measured for alloy composiLions up to the solalbility limils of lhe alloy nitrides. All five alloying agents were found to decrease markedly the activity coefficient of nitrogen in liquid ivon. The metal/nitvogen mole ralios in the alloy nitrides formed were generally .found to be slighlly greater than 1.0, but in no case greater than 1.5. From the experimental data, the standard free energies of fortmation of titanium and zir-conium nitrides have been calculated for the Lemperaluve range 1550° to 1750 C. The solublily Products for columbium, tantalum, and vanadium nitrides are also reported. A number of research investigations have examined the effect of refractory metals on the solubility of nitrogen in liquid iron. Although data on zirconium are not available, investigators are in agreement that titanium, vanadium, columbium, and tantalum markedly increase the solubility of nitrogen in liquid iron. This fact alone makes desirable the acquisition of thermodynamic data for these elements in liquid iron. Since refractory metals are known to be stable nitride formers, they have been suggested as steel denitrifying agents, and some of their nitrides have recently been considered as containment materials for liquid iron and iron alloys. Most available thermodynamic data for these metals relate to their dilute concentrations, but effective thermodynamic treatment of these applications requires data at concentrations near the solubility limit of the alloy nitride. Although some work has been done at relatively high alloy concentrations in liquid iron (particularly for vanadium 2,3 and titanium 2,4), the results have been somewhat contradictory. Disagreement may be partly attributed to the fact that the compositions of most refractory metal nitrides have been shown to be nonstoichiometric, and to vary 2,5-8 depending on the temperature and nitrogen gas pressure with which the solid nitride phase is in equilibrium. One purpose of this study consequently has been to determine the compositions of the refractory metal nitrides precipitated from a liquid iron solution. EXPERIMENTAL PROCEDURE Rao and Parlee2 and Evans and Pehlke 9 have discussed the technique for measuring the solubility product of an alloy nitride phase in liquid iron by finding the point of departure of the nitrogen solubility from Sieverts' law. The method consists of measuring the solubility of nitrogen in a melt of iron containing a known concentration of a second metal as a function of the nitrogen gas pressure over the melt. In this study the second metal was one of the refractory metals titanium, zirconium, columbium, vanadium, or tantalum. When the nitrogen pressure at which the refractory nitride forms is reached, a deviation of the measured solubility of nitrogen in the melt from Sieverts' law is observed in the form of a "pressure halt." The concentration of nitrogen in the melt associated with this breakpoint in the nitrogen-absorption curve is then used to calculate the nitride solubility. The Sieverts method was used to measure nitrogen solubility as a function of nitrogen pressure and temperature. The experimental equipment for this technique has been previously described in detail. 1,9 Charge materials used were vacuum-melted high-purity iron (Ferrovac-E) and the best commercial grades of the refractory metals obtainable (in all cases at least 99.8+ pct pure). Recrystallized alumina crucibles were used to hold all melts except those containing zirconium, for which zirconia crucibles were necessary. Temperatures were measured by a disappearing-filament type optical pyrometer sighted vertically downward on the melt surface through a 1/4-in.-diameter sight hole in the crucible lid. By means of a technique previously described, 9 in which the refractory-metal nitride was precipitated at one temperature then redis-solved by raising the temperature 50°C and precipitated again at a higher temperature, it was possible to obtain data over a temperature range of up to 200°C on a single melt. It was found that this technique could not be used with melts containing zir-

Jan 1, 1965

By Ralph W. M. Lai, D. W. Fuerstenau

This paper presents the results of a study of the principles which control the distribution of ultrafine particles between an oil phase and an aqueous phase. Alkyl sulfonates were used to control the wettability of fine alumina particles and to stabilize the water-isooctane emulsion system in the extraction process. The effects of sulfonate chain length, sulfonate adsorption, pH, and oil-water ratio on the recovery of solids in the oil phase were investigated. Higher extraction was found under conditions which yield higher hydrophobicity and large interfacial area of the oil-water emulsion. Today there is considerable interest in developing methods for the recovery of fine particles from disseminated ores. One such method might be the extraction of fine particulate solids from aqueous suspensions into an oil phase, and one example of a successful industrial process based on oil-water distribution phenomena is the emulsion flotation process used in concentrating manganese ore.' The oil agglomeration process of Farnand, Smith, and Puddington has been suggested for concentrating tin ore. Patents 3-4 for oil flotation processes extend back to that of William Haynes in 1860. The basis of all these processes is directly related to the stabilization of emulsions with solid particles. The first extensive study of oil-water emulsions stabilized by finely divided solids was made by Pickering. Later, Briggs,6 weston, 7 Chessman and King,8 and Leja and Schulman9 experimentally demonstrated how solid particles control water-oil and oil-water systems. Hildebrand10 suggested that fine particles can stabilize an emulsion because the fine particles are partially wettable by both oil and water, that is, that the contact angle must be finite. Takakuwa and Takamori 11 recently applied emulsion inversion to the study of collector adsorption in flotation systems. At the Royal School of Mines, Shergold and Mellgren12 are currently carrying out a comprehensive study of the extraction of fine particles into an organic liquid phase. In the present study of the liquid extraction or oil flotation of ultrafine particles, the recovery of hydro-philic alumina particles of 0.1-µ average diameter was determined after separating an isooctane-water mixture (emulsion) into its two phases. Alkyl sulfonates of different chain lengths were used to change the wettability of the alumina and to effect emulsifi-cation of the oil-water mixture. The effects of the oil-water volume ratio, sulfonate adsorption, and pH on the recovery of the fine particles were investigated. Since the surface charge on an oxide such as alumina is determined by the adsorption or interaction of H+ and OH- with the surface, pH control is extremely important. Furthermore, since the zero point of charge (zpc) of alumina13-14 occurs at pH 9 to 9.4, major adsorption effects with anionic collectors in these systems will occur below pH 9. The results of the foregoing investigation are discussed in terms of the recovery of the fine particles, the oil-water ratio, contact angles, surface tension, the adsorption of sulfonate onto the solid surface, and the emulsifica-tion of oil. MATERIALS AND EXPERIMENTAL METHODS Materials: The particulate solid used in all the experiments was Linde "A" alumina, a high-purity, readily available form of a-alumina. The surface area of the alumina, as evaluated from measurements of stearic acid adsorption from benzene, was 14.5 sq m per gm, based on a value of 20.5 sq Å for the cross-sectional area of stearic acid.13 All aqueous solutions were prepared from triply distilled conductivity water. Other materials included high-purity crystals of sodium alkyl sulfonates, isooctane, and, for pH adjustments, reagent grade hydrochloric acid and sodium hydroxide-Because sulfonic acids are strong acids, they are

Jan 1, 1969

By C. R. Fast, George C. Howard

Laboratory and field testing of various squeeze cementing techniques and materials revealed that many improvements could be made in squeeze cementing operations. The use of a slow-pumping squeeze cementing procedure permitted the control of the quantity of cement displaced into a formation and aided in obtaining a high final squeeze pressure. Field testing indicated the desirability of obtaining high final squeeze pressures, the need for improved formation breakdown fluids, and the necessity of controlling the pressure differential during testing after a squeeze job. INTRODUCTION During the past few years, squeeze cementing operations have been investigated, both from the theoretical as well as the practical point of view, in an effort to arrive at some solution to the many and varied problems that arise with this type of operation. A review of well files indicated that in many instances, wells were being squeeze cemented four and five times before a satisfactory pressure buildup was obtained. There seemed to be considerable variation in opinion as to the proper method of squeeze cementing, as well as disagreement as to the proper breakdown agent, the quantity of cement that should be used, type retainer and length of WOC* time that was necessary. Consequently, it was deemed advisable to approach this problem theoretically, field testing each idea developed in hopes of eventually arriving at a squeeze cementing procedure that would give reasonable assurance of a successful job after one squeeze cementing operation. This investigation was. therefore, divided into two broad headings: (1) Preliminary studies, which include both theoretical and laboratory studies, and (2) Field investigations to determine the proper squeeze cementing methods. PRELIMINARY STUDIES Overburden Pressure Studies Squeeze cementing problems are so intimately related to the earth's overburden pressure that solutions to them are very difficult, if not impossible, without an understanding of the nature and magnitude of the overburden pressures encountered at the depths of producing wells. It was thus felt that the first approach to research on squeeze cementing should be made through a study of these pressures. Since there has been rather loose usage of a number of the terms related to overburden preasure by different writers, the terms to be subsequently used are defined here. Theoretical overburden pressure is the calculated pressure at any given depth exerted by the theoretical weight of overlying formations as calculated from the average rock density. Fluid displacement pressure is that pressure at which fluid can be injected into a formation after it has been broken down. It may be more or less than the theoretical overburden pressure. Formation breakdown pressure is that pressure at which a formation parts or breaks and is usually thought of as fluid displacement pressure plus rock strength. Breakdown agent is that fluid with which the formation is fractured. The first step in the study of the earth's overburden pressures involved a review of pertinent technical literature. The general opinion expressed was that the overburden pressure gradient of the earth's formations is roughly 1.0 psi per foot of depth, and that application of sufficient pressure to stratified formations. will cause them to part at or parallel to the bedding planes. The second step in the study of overburden pressures involved a study of available well data in an effort to obtain some definite information as to the actual values experienced in the field for the above mentioned terms. Data from 115 cement squeeze jobs in the Gulf Coast area and 46 cement squeeze jobs and acid jobs in the West Texas-New Mexico area were closely analyzed. The analysis of these data showed that the average formation breakdown

Jan 1, 1950