[RALPH ADAIR Ore Dressing Consultant Bull Mtn. Rd., Asheville, N. C. Phone 4-1893 JAMES A. BARR Consulting Engineer Mt. Pleasant, Tennessee Washington, D.C. BEHRE DOLBEAR & COMPANY Consulting Mining Engineers and Geologists 11 Broadway New York 4, N. Y. I. R. BERENT Engineering Consultants and Contractors Mineral Exploration, Mine Evaluation, Mine Designs and Mine Management ` 188, Ataturk Bulvari-Ankara, Turkey BLANDFORD C. BURGESS Registered Professional Engineer Mining Consultant Monticello, Georgia GLENVILLE A. COLLINS Mining Engineer Uranium examinations Cable "Coins" 8 Haward-Canfleld Bldg. Santa Barbara, Calif.]

Jan 1, 1952

By F. R. Hensel

The present paper describes a number of experiments with fine silver, coin silver, silver-cadmium oxide and silver-nickei-copper compacts, prepared by powder metallurgical methods. The test data are of a preliminary nature, since most of the work was exploratory. Fine Silver Eject of Compacting Pressure on Hardness and Density during Cold and Hot Pressing The cold-welding properties of silver have received considerable attention and the welding characteristics are functions of such variables as: cleanliness of metal particles (impurities and adsorbed gases), chemical nobility of particles, plasticity and hardness, particle assortment, particle shape, particle porosity, apparent density, temperature, pressure, time, recrystalliza-tion characteristics. Chemical nobility, plasticity and low temperature of recrystallization after work-hardening are responsible for the excellent low-temperature bonding properties of silver. Several series of compacts were pressed at pressures of 5, 10, 20, 30, 40, 50, 60 70 and 80 tons per square inch, at temperatures of 32°C. (room temperature), l00°, 2000, 300°, 400°, and 450°C. Silver powder of minus 325-mesh, produced by displacing silver from a nitrate solution by means of copper, was used. The density was calcuiated from accurately measured and weighed compacts. The hardness was measured on the Rockwell F scale. The investigation shows that an increase in pressure promotes a higher density and hardness regardless of pressing temperature, up to a temperature of 400° C. The pressure-density curves at various pressing temperatures are shown in Fig. I, the pressure-hardness curves at various pressing temperatures, in Fig. z. The greatest increase in both hardness and density was obtained in the pressure range of 5 to 20 tons per square inch. A compact from each series was annealed at 300°C. in air, for various lengths of time. The hardness values after annealing are shown in Table I. A minimum hardness was obtained after one hour of annealing. No change in density occurred during annealing. The maximum density was obtained at 80 tons per sq. in., and at this pressure the hardness is equal to that of hard-drawn wrought

Jan 1, 1945

By J. J. Gilman

The dependence of ortho kink-band formation on crystal orientation, on temperature, and on the conditions at the ends of a specimen is described. Load-compression curves for crystals that kink are presented. The reversibility of ortho kinking is demonstrated, and motion of kink planes through crystals is shown. Finally, a phenomenological explanation of ortho kink-band formation is given. ORTHO compressive kink bands (Fig. la) were discovered for the case of metals by Orowan,1 and they have been discussed by Jillson2 and in some detail by Hess and Barrett." However, their history in nonmetallic crystals is considerably older. It is not known when they were first observed in mineral crystals, but descriptions of them may be found as early as 1885.* They were sometimes mistaken for twins.6 Mügge seems to have been first to realize their true nature and importance. He reviewed the knowledge of them for a wide variety of crystals: anhydrite, antimonite, kyanite, vivianite, gypsum, mica, graphite, molybdenite, barium bromide, cal-cite, sodium nitrate, and barite. Also, the "twins" observed by Bridgman7 in sapphire crystals resemble kink bands more than twins. The terms ortho and para kink bands have been coined in order to distinguish between two types of kink bands which seem to represent the same geometrical configurations, but which have different origins and sizes. Ortho kink bands are the usual type that form at low loads when zinc crystals are compressed parallel to the basal plane. Para kink bands form at much higher loads in highly deformed crystals. These terms refer to compression phenomena and are not to be confused with analogous tension phenomena such as tensile kink bands and deformation bands. Mügge described the geometry of ortho kink bands quite completely for kyanite crystals, Fig. lc. The geometry observed for cadmium by Orowan1 and for zinc by Hess and Barrett3 is very similar to that described by Mügge. (See Hess and Barrett for a complete discussion.) Mügge associated kinking with bending combined with basal slip. He pointed out that the kink angles

Jan 1, 1955

By H. N. Egan

Faced with a severe disposal problem of their fines from a coal mine in the heart of the Appalachian Mountains of extreme eastern Kentucky, Eastern Coal Corporation has built a special plant to pelletize the fines into high quality coal pellets meeting the requirements of the metallurgical market. These low-ash, low-sulfur pellets measuring 3/4 x 3/8 in. contain less than 1.5% moisture and have the same stability as raw coal of the same size. Although Eastern Coal is mining 6000 tpd, the company had, until recently, no provision to recover the fine coal which was included with the plant effluent pumped to a 12-acre refuse pond. The pond, impounded behind the coarse refuse dump, rose 15 ft last year and obviously no pond can stand many years at this rate. Limited pond space in this rugged area of steep hills and narrow valleys dictated a revised disposal method.

Jan 11, 1967

By Y. C. Liu

Both the habit plane of martensite and the orientation relationship between the matrix and martensite platelets of different habit planes have been investigated in binary titanium alloys with molybdenum, chromium, and iron. The effect of the mode of deformation on the martensite habit plane was studied. A micrograph of an exposed mar-tensite platelet is presented. IN the study of martensitic transformation in Ti-Mn alloys,' two martensite habit planes—{334), and {344)8—were reported. The {334), habit was also observed in unalloyed titanium upon transformation,' although there is disagreement with respect to the exact indices. The other habit plane, {344),, has not been reported in martensitic transformation in any other alloys. The present investigation was made to determine whether other binary titanium alloys with P-stabil-izing elements would exhibit a crystallography of transformation similar to that of Ti-Mn alloys. Furthermore, since martensite platelets can be induced by deformation under certain conditions, it was of interest to investigate whether the mode of deformation, compressive or tensile, would influence the formation of martensite platelets on a specific plane in an alloy system which possesses two martensite habit planes. Experimental Procedure The material used for the preparation of the binary alloys of iodide titanium with molybdenum, chromium, and iron had the following purities: 99.99 pct iodide titanium, 99.9 pct molybdenum, 99.423 pct chromium, and 99.9 pct iron. The compositions of alloys listed in this paper are in nominal weight percentage. All specimens used were prepared and treated according to the procedure described in reference 1, unless stated. For the subzero temperature treat,ment the following experimental schedule was followed. After specimens had undergone the grain-growth treatment, they were quenched into an ice-water bath and were then metallographically examined. In specimens of higher alloy content, no martensitic transformation was observed. In those in which mar-tensitic transformation did occur, only specimens in which the martensite platelets existed as fine needles in localized regions were used. All specimens were reannealed 17 hr at 1200°C, quenched into ice water. and the capsule was broken. They were held in the ice water for from 5 to 10 sec, then transferred to a liquid-argon bath. This stepped quenching procedure was found to be more efficient than direct quenching into liquid argon. In the latter case, as soon as the hot specimen was immersed in the liquid argon, a protective, insulating layer of argon gas formed, and the specimen continued to glow vividly in the bath for some time. In the study of the habit behavior of martensite produced by deformation, specimens were deformed at room temperature either by compression, tension, or rolling. Martensite habit planes were determined by the two-surface analysis procedure described in reference 1. A stereographic net of 153/4 in. diam was used throughout the investigation. The method for determining the orlentation relationship between martensite and the matrix follows that used by Greninger and Troiano.' A diamond-polishing table with its auxiliaries was used in order

Jan 1, 1957

By Herbert Clark Hoover, Lou Henry Hoover

SINCE the Sixth Book has described the iron tools, the vessels and the machines used in mink, this Book will describe the methods of assaying1 ores; because it is desirable to first test them in order that the material mined may be advantageously smelted, or that the dross may be purged away and the metal made pure. Although writers have mentioned such tests, yet none of them have set down the directions for performing them, wherefore it is no wonder that those who come later have written nothing on the subject. By tests of this kind miners can determine with certainty whether ores contain any metal in them or not ; or if it has already been indicated that the ore contains one or more metals, the tests show whether it is much or little ; the miners also ascertain by such tests the method by which the metal can be separated from that part of the ore devoid of it ; and further, by these tests, they determine that part in which there is much metal from that part in which there is little. Unless these tests have been carefully applied before the metals are melted out, the ore cannot be smelted without great loss to the owners, for the parts which do not easily melt in the fire carry the metals off with them or consume them. In the last case, they pass off with the fumes ; in the other case they are mixed with the slag and furnace accretions, and in such event the owners lose the labour which they have spent in preparing the furnaces and the crucibles, and further, it is necessary for them to incur fresh expenditure for fluxes and other things. Metals, when they have been melted out, are usually assayed in order that we may ascertain what pro- portion of silver is in a centumpondium of copper or lead, or what quantity of gold is in one libra of silver ; and, on the other hand, what proportion of copper or lead is contained in a centumpondium of silver, or what quantity of silver is contained in one libra of gold. And from this we can calculate whether it will be worth while to separate the precious metals from the base metals, or not. Further, a test of this kind shows whether coins are good or are debased ; and readily detects silver, if the coiners have mixed more than is lawful with the gold ; or copper, if the coiners have alloyed with the gold or silver more of it than is allowable. I will explain all these methods with the utmost care that I can.

Jan 1, 1950

By C. E. Melbye

A serious problem confronted the city of Gunnison early in 1958 in that, for a few months during each spring runoff, the water supply derived from the Gunnison River became polluted to an unsafe point. The city management had the choice of building a new filter plant to replace the old unworkable one or drilling wells to develop a ground water supply. The cost of a new filter plant was estimated at $180,000 compared to $50,000 for 6 wells, pumps, and additional water lines, hence their decision to attempt the development of sufficient ground water. Six wells at 300 gpm per well were estimated as necessary to handle the peak usage of 1800 gpm, compared to only 600 gpm winter usage. Although the water table is only about 7 feet below the surface, existing private wells drilled at random locations were producing much less than 300 gpm. The problem was to find sufficient quantities from about 6 wells. Since the presence of an ancient bedrock channel was suspected, which would be expected to localize greater quantities of water, the city of Gunnison authorized a resistivity survey to investigate bedrock topography below unconsolidated gravels. Survey results were highly satisfactory and led to the preparation of a fairly detailed bedrock contour map, Fig. 1. This map was used in selection of all well sites. The city of Gunnison is situated in a flat, broad, Quaternary gravel-filled valley (terrain dips south at 20 feet per mile) at the junction of the Gunnison River and Tomichi Creek. The valley, about 2-4 miles wide, is bordered by hills of Tertiary volcanics to the northwest, Cretaceous and Jurassic sediments to the north and northeast, and pre-Cambrian granite and gneiss to the south. One previous deep test well at the west end of the city hit pre-Cambrian granite at 496 feet, which, allowing for 40 feet of surface gravels, makes the older sedimentary section 456 feet thick. This section is probably all Jurassic Morrison formation, consisting of the Saltwash sandstone overlain by the much thicker section of Brushy Basin shales and mudstones. According to the driller's logs, each well was bottomed in what is believed to be Brushy Basin shale. FIELD PROCEDURE A standard Gish-Rooney type of resistivity apparatus was employed, which used 45-volt dry batteries as a direct-current power source. Applied voltages could be selected from 45 volts to a 270-volt maximum. Copper-coated steel stakes were employed as current electrodes and porous porcelain pots as potential electrodes to avoid possible polarization effects with direct current. The expanding Wenner electrode configuration was utilized for this investigation and measurements were made at 20 40, 60, 80, and 100-foot spacings,

Jan 1, 1961

By H. F. Moore

DURING the last six years, there have been many extensive investigations of the fatigue of metals. The major work of 'these investigations has been the determination of constants for fatigue strength of wrought ferrous metals; but during the past year or two there have become available considerable test data on the fatigue strength of certain nonrferrous metals, including copper, brass, bronze, nickel, copper-nickel alloys, aluminum and aluminum alloys, magnesium and magnesium alloys. It is not proposed to give here extensive quantitative tables of test results; for such tables, reference is made to the published data of various laboratories. The following general conclusions, however, seem to be fairly well established: 1. The phenomenon known as "fatigue" of metal really a progressive fracture of metals. A minute (probably submicroscopic) crack is formed in the metal, the internat stress, is intensified at the ends' of the crack, and under successive applications of load the crack spreads like a minute hacksaw cut until there is not enough sound metal left in the cross-section of the piece to stand the load. applied, and then failure occurs suddenly. 2. For wrought ferrous metals, there is .a limiting intensity of stress (as computed by the ordinary formulas of mechanics of materials) below which, a metal is able to withstand an indefinitely large number of repetitions of stress without failure. This limiting stress is known as the "endurance limit or the fatigue limit.? For reversed flexure, the endurance limit for. wrought ferrous metals is usually not far from 50 per cent. of the ultimate tensile strength.

Jan 1, 1925

By L. F. Pease, J. H. Brophy

A phase diagram for the Ta-Zr system is presented. The system is of the minimum-melting point type with the 0-zirconium phase decomposing monotectoidally at 785°C and 95.5 at. pct Zr. The minimum solidus temperature is 1875°C and the temperature of the top of the monotectoid loop is 1775°C. Techniques employed included X-ray diffraction and fluorescmce, electron microprobe analyses, diffusion couples, metallography, and melting-point measurements. Errors due to interstitial solutes and in melting observations are particularly common in this system, and their occurrence is discussed. SEVERAL versions of the Ta-Zr phase diagram have been reported in the literature.lm7 Williams et al.' report a diagram of the minimum-melting point type with a monotectoid reaction at 800°C and 12 wt pct Ta. The minimum in the solidus occurs at 1820°C and 25 wt pct Ta, while the top of the monotectoid gap is located at 1780°C and 80 wt pct Ta. The experimental techniques employed were metallography, electrical resistance variation with temperature, dilatometry, X-ray diffraction, and direct observation of melting by the technique of Pirani and ~lterthum.' Experience in the Nb-Zr phase diagram has shown that small changes in the interstitial content can cause large shifts in the positions of the phase boundaries. Small amounts of inter -stitials can cause similar changes in the Ta-Zr system and may be responsible for the wide variations in the phase diagrams previously reported.'-' The authors15 have found that alloys containing 0.75 wt pct 0 and 1.0 wt pct Ni with tantalum contents from 19 to 85 at. pct often contain a lamellar or cellular precipitate after annealing above 1400°C. This precipitate is very similar to that reported by pollack,12 Ralls," and Donlevy17 for the Ni-Zr system. In the present investigation, a wider variety of experimental techniques and improved alloy purity were applied to the resolution of errors in diagrams for this system as they now appear in the literature. New results have been obtained in the areas of alloy homogeneity and purity. Errors in the common techniques of direct melting observation in binary alloys have been demonstrated. In the commercially important high-tantalum region, the more accurate metallographic method of solidus determination has been employed. EXPERIMENTAL PROCEDURE Nominal analyses of the materials employed are given in Table I. The zirconium was low hafnium reactor grade iodide crystal bar, and the tantalum was in the form of high-purity sheet. Powders were impossible to use because of gas content. Alloys were melted on a water-cooled copper hearth, with a thoriated tungsten-tipped nonconsumable electrode in 2/3 atm of Zr "gettered" argon. Alloys were

Jan 1, 1963

By NONE N

Jan 1, 1963

By H. H. Wade, N. F. Schulz

The large quantities of iron-bearing materials, including taconite, semi-taconite,* and other low-grade ferruginous materials occurring in Minnesota and elsewhere, constitute an important potential source of iron. Satisfactory grade and recovery of iron ore concentrate cannot ordinarily be obtained from these ferruginous materials by simple methods of beneficiation. Iron is distinctive in that the free metal and two of its oxides [magnetite (Fe2O3) and maghemite (gamma-Fe2O3) ] are strongly ferromagnetic. The successful magnetic separation of natural magnetite from taconite has already been established on a commercial scale. The iron in semi-taconite, however, occurs largely as goethite (Fe2O3-H4O) and hematite (Fe2O3) which do not respond to ordinary magnetic separation methods. Magnetic roasting converts these iron oxides to magnetite, which can, after liberation, be magnetically concentrated. MAGNETIC ROASTING Hematite undergoes a stepwise reduction when exposed at moderately elevated temperatures to a reducing atmosphere containing hydrogen or carbon monoxide: Fe2O3? Fe3O4 ? FeO ? Fe Since the desirable product in magnetic roasting is Fe3O4, the conversion is halted after the first stage by controlling the reduction potential of the gas mixture with water vapor or carbon dioxide. The reducing gas mixture must be such that the oxygen partial pressure at the solid-gas reaction interface will be maintained intermediately between the oxygen partial pressures in equilibrium with Fe2O3 and Fe3O4 at the prevailing temperature. Because of the rapid increase in decomposition pressure of Fe3O4 with increase in temperature, the practical upper limit of useful reaction temperature is about 1400°F, above which over-reduction usually occurs in atmospheres containing hydrogen or carbon monoxide. On the other hand, useful reaction rates usually occur only above 800°F. Goethite reacts similarly except that the combined water probably has to be driven off thermally before the reduction to magnetite occurs. Iron carbonate must also be decomposed thermally to an oxide before conversion to magnetite. Iron silicates are apparently not amenable to magnetic roasting. The rate of penetration of the reaction toward the interior of a given ore fragment is dependent on the chemical composition and physical structure of the solid. Most ore fragments tested here reduced satisfactorily to 1/4-in. depth in less than 14 min at 1200°F. Some very dense fragments, however, were reduced to less than 1/32-in. depth under the same conditions. Determination of the optimum temperature, gas composition, ore fragment size, or time of exposure

Jan 1, 1961

Who's Who in Mineral Engineering - The 1978 Membership Directory of the Society of Mining Engineers of AIME

Jan 7, 1978

By Ling Yang, John Henderson

Self-diffusion coefficients of copper in molten copper have been measured by the capillary reservoir method in the temperature range 1140o to 1260°C. The results can be represented by the equation D = [(1.46 * 0.01) x 10-3) exp [(-9710 * 710)/RT] cm2/sec. The energy of activation agrees within the limit of experimental uncertainty with that for viscous flow. The relationship between the diffusivity and coefficient of viscosity is best described by the equation D = kT/4pnr cm2/sec. MEASUREMENT was made of the self-diffusion coefficient of copper in molten copper in the temperature range 1413º to 1533ºK, using the capillary reservoir technique and CU64 as the radioactive tracer.The procedures for filling the capillaries, making the diffusion run and evaluating Dcu from the counting results were the same as described previously.1,2 All experimental operations involving the melt were carried out in a purified argon atmosphere. A graphite crucible, enclosed in a McDanel tube, was used as a container for the melt because of its satisfactory nature as a refractory material and the low solubility of carbon in copper. Graphite was also used for the capillary material. A McDanel thermocouple sheath, to which graphite radiation shields were affixed, was used to hold the capillaries. By moving this sheath through a rubber seal at the top of the McDanel tube, the capillaries could be lowered into or raised out of the melt. A Globar furnace with a constant temperature zone (± 2°C) of 2 in. was used to heat the assembly. The temperature of the furnace was the equilibrium value corresponding to a given setting of the transformer. Temperature was measured with a Pt-10 pct Rh/Pt thermocouple and varied during a run

Jan 1, 1962

By O. M. McRae

The Courtland-Gleeson area is in Cochise County about 15 miles east of Tombstone in southeastern Arizona. Rocks exposed in the area range in age from Pre-cambrian to Quaternary. The Precambrian is repre-sented by the Pinal schist. Paleozoic rocks include the Cambrian Bolsa quartzite and Abrigo limestone, Mississippian Escabrosa limestone, and the Permo-Carboniferous Naco Group limestones. Rocks believed to be of Triassic and/or Jurassic age include the Copper Belle monzonite porphyry, Turquoise granite, and Gleeson quartz monzonite. The Cretaceous is represented by andesitic volcanics and various sedimentary rocks. Tertiary rocks include the intrusive and extrusive Sugarloaf quartz latite porphyry and numerous dikes of various rock types. Quaternary conglomerates cover the northern and eastern part of the area. The geologic structure is extremely complex. All rocks as old as early Tertiary have been involved in either tilting, normal faulting, high angle reverse faulting, imbricate thrusting or folding and overfold-ing. Major deformation was initiated during the first half of the Tertiary. Northeast-southwest compres-sional forces caused thrust plates containing lower Paleozoic rocks to override Cretaceous rocks. Subsequently, two large slide blocks of lower Paleozoic rocks, acting under the influence of gravity, moved eastward. The imbricate structure and the gravity slide blocks were then broken by late Tertiary normal faults. INTRODUCTION The Courtland-Gleeson area, or Turquoise Mining District, has long been recognized as an area of extreme structural complexity. Gilluly 2 referred to the entire district as a "gigantic thrust breccia". In 1962, Bear Creek Mining Company completed a two year program of detailed geologic mapping supported by exploration drilling. The purpose of this paper is to present some of the results of this investigation and to provide a structural interpretation based on these results. The geologic map that accompanies this report is generalized and shows only the major and significant features. The area was initially mapped on aerial photographs on a scale of 1 in. equals approximately 500 ft. These data were transferred to a planimetric base using a vertical sketch master. LOCATION The Courtland-Gleeson area is in central Cochise County, about fifteen miles east of Tombstone, and about twenty-two miles northeast of Bisbee in southeastern Arizona (Fig. 1). The area is readily accessible over graded gravel roads from both Tombstone and Elfrida. GENERAL GEOLOGY Rocks exposed in the area range in age from Pre-cambrian to Quaternary. wilson3 and Gilluly2 have published very detailed descriptions of the principal rock units exposed in the area. Only a summary description is provided in Table I. A great number of previously unmapped narrow Tertiary dikes and small irregular masses of hornblende andesite porphyry, lamprophyre, and aplite intrude the Gleeson quartz monzonite in the western part of the map area. The scale of the map prohibits showing them. The aplite dikes are related to, and bear the same structural relationships as, the Sugarloaf quartz latite dikes found in this area. For that reason, and because both the hornblende andesite porphyry and the lamprophyre are post-mineral and post-thrusting, their omission from the map is not considered significant. Because so many of the contacts in the district are fault contacts, because bedding faults appear to be prevalent but are difficult to recognize and map, and because igneous intrusions are so common throughout the sedimentary section, it is virtually impossible to measure an exact total thickness of any of the sedimentary rock units. Nevertheless, neither the field mapping program nor the diamond drilling provided any basis for suspecting that the thicknesses of the sedimentary units are significantly greater or less than what might be inferred from surrounding districts.

Jan 1, 1967

By Herbert Hoover

DURING the year, the' Institute has made the most remarkable growth in its history. Our actual increase in membership was 1816 and therefore was 80 per cent. larger than any previous year. Even without expectation of any abnormal growth, we should pass in the year 1921 the 10;000 mark. The causes of this increased growth are not far to seek.. They lie in the widening vision of the Institute's work, not only in its relation to' the profession but as an avenue of service to the nation as a whole. The Institute is today in the first rank of influence among public institutions in the country. During this year we have, for the first time in many years, had a ?deficit of some $3000 in our finances. The sum is not important, but it- does indicate the tendency of the times, and that is the high cost of living:' The increase in our expenses lay, to the largest degree, on the publishing side of the Institute's work. If we compare the year 1918, as a fairly repre¬sentative year, with that of 1920, we find that the costs of issuing the' Institute's publications, after deducting the income received from these publications, shows a .net increase of about $33,000. for the year. This has been to some degree due to the enlarged membership but to a large degree due to the cost of the paper and printing.

Jan 1, 1921

Jan 1, 1959

By H. H. Bein

Most western industrial sands are feldspathic and contain feldspars in variahle amounts. A few deposits will show alumina contents of less than one per cent while others will contain over twelve per cent alumina. Some industries are not especially concerned with the amount of contained feldspar but are interested only in color and in size gradations. Other industries, however, are very much interested in alumina content and set up quite rigid specifications as to this content. Several western plants are beneficiating crude sands both to reduce the iron content and to control the feldspar content. At present, most of these plants are using flotation processes for both controls although a few plants do use magnetic separators for the reduction of iron content. Some work has also been done with electrostatic separators for the feldspar-quartz splits. The Sand Division of Del Monte Properties Company, Pebble Beach, California, has been operating a flotation plant for iron removal and the separation of quartz and feldspar since 1950. As mentioned before, control of alumina, especially in the quartz product, is very important. Some users require an alumina content of less than two per cent and others will demand a product of less than one per cent Al2,O3,. The standard Quinolate method for determining alumina is lengthy and time consuming. The HF —H2SO4 evaporation step is especially critical and, if forced, spattering is apt to occur with a resulting loss of sample. Standard procedure is to evaporate to dry ness overnight at a low temperature. Even with forcing under optimum conditions the procerlnre will take two or three hours to complete. A new method has been developed which allows an alumina determination to be made, in 10 or 15 minutes, on a sample of the quartz product as it is being produced. This pocedure, although simply an approximation, has been most helpful in showing whether or not the product being formed is meeting specifications. This procedure has also allowed a great reduction in samples formerly taken and analysed by the orthodox method. Whether a sample assays 1.75% A12O3, or 1.95% .41,0, is not so important as the fact that it is below the allowable maximum of 2.00%. Similar thinking would apply to products required to contain less than 1.00% A1,0,. The step by step procedures for the method are as follows: 1. Collect sample, drain or filter, and dry. 2. Split sample through standard Jones sample cutter to quarter or eighth sample, depending on size of original sample taken, then split down to about 5 grams through Sepor micro-splitter. 3. Screen through 50 mesh sieve (U.S. Series) and reject undersize. 4. Weigh out 2 grams and place in platinum crucible. 5. Etch with 3-5 mls 38.40% HF for 1 minute at room temp. 6. Decant and wash. 7. Stain for two minutes in same crucible with a 1% water solution of Nigrosene dye. 8. Decant and wash well. 9. Dry.

Jan 1, 1961

By J. Gurland

A method of measuring the degree of contact between grains of 1 phase in multiphase alloys is derived. It is shown that the number and the areas of contacts between grains can be determined by metallographic analysis. Relations between the area of contact, the dihedral angle, and the mean free path of spherical grains are developed. It is often desirable to interpret the mechanical behavior of alloys in terms of structural features observed under the microscope. A quantitative description of microstructures of multi-phase alloys requires consideration of geometrical and topological factors such as the amount, size, and shape of grains and the continuity of the constituent phases. The number and dimensions of grains may be metallographically determined by applying the methods described by Smith and Guttman1 and by Fullman2 in their papers on the measurement of particle size and internal boundaries in opaque bodies. The present work intends to show that the same methods can be used to evaluate some of the parameters of phase continuity; namely, contiguity, number of contacts, and areas of contact of grains of 1 phase. Application of these concepts may be found in such problems as the calculation of electrical conductivity of 2-phase alloys, or the evaluation of the length of fracture path through grains of a brittle phase more or less dispersed in a matrix. I. DEFINITION The following definitions and derivations are based on 2-phase alloys, of which the units of the microstructure are grains. Contiguity is defined as the average fraction of surface area shared by 1 grain of a phase with all neighboring grains of the same phase. In a 2-phase alloy of constituents A and B, the contiguity of phase B is given by: where Cb is the contiguity of phase B aBß is the average area of contact between a grain of phase B and adjacent grains of phase B, aAB is the average area of contact between a grain of phase B and adjacent grains of phase A. The contiguity is a measure of the average degree of contact between grains of phase B in the 2-phase mixture. The ratio varies from 0 to 1 as the distribution of phase B changes from a completely dispersed to a fully agglomerated structure. Smith and Guttman1 have shown that the relative areas of 2 kinds of interfaces in a volume are directly proportional to the number of interfaces of each type intersected by a random line. The lines can be drawn on metallographically prepared surfaces as long as these are random sections through the sample. The contiguity ratio of phase B then becomes: Cb = 2NBB/NAB + 2N BB [2] where: NBB is the number of interfaces between grains of phase B intersected per unit length of random line. Nab is the number of interfaces between grains of phase B and grains of phase A intersected per unit length of random line. The factor 2 arises in Eq. [2] because each interface B-B is associated with 2 grains of B-phase, whereas the interface A-B involves only 1 grain of B-phase. The calculations of contiguity do not require any assumption as to volume fraction, particle size, or particle shape. Fullman2 gives an expression for the determination of the mean free path between particles. The mean free path PB between grains of phase A, i.e., through grains or agglomerates of phase B, may be found from the relationship: PB =2fB/NAB [3] where fB is the volume fraction of phase B. The calculation of the mean free path is independent of grain shape and grain size distribution. The calculation of the number of contacts and of contact area requires assumptions of grain shape, grain size, and contact shape. In the case of uni-

Jan 1, 1959

By L. W. Bahney

MANY methods for the determination of gold or silver, or both, in cyanide solutions have been published, which with care in manipulation, and modification in some cases, will give results that are satisfactory. It is possible to classify or group these methods as follows: 1. Evaporating the solution in a porcelain or agate-ware dish containing litharge,1 or in a "boat" made of lead foil. 2. Forming a lead sponge containing the precious metals by means of zinc shavings,2 zinc dust,3 or a piece of aluminum.4 3. Decomposing the cyanide solution with an acid and precipitating the precious metals by the use of one or a combination of some of the following: Copper sulphate,5 sodium sulphite,6 hydrogen sulphide,7 cement copper.8 4. Precipitating the silver by zinc dust held in a Hooch crucible and determination with a standard solution of sulphocyanate.9 5. Electrolysis.10 6. Colorimetry.11

Jan 2, 1915

By R. J. Wensley

THE use of small substations for the supplying of 275-volt energy to the locomotive and cutting machines in coal mines is a well-established practice. A few years ago, when labor costs were lower, these substations were located as near to the load as possible, and an operator was provided for each station. This practice has now become so expensive that substations are being located with reference to other mining machinery, such as hoists or pumps, so that one operator can look after both. Some-times the substation is operated by one whose duties make him traverse quite a large area. In such cases the interruption of alternating-current supply may produce a long interruption in the direct current, as the station cannot resume service until this man reaches it. Such interruptions interfere seriously with production and may easily counterbalance the supposed saving gained by such operating methods. The grouping of substations for convenience in operating may also result in excessive copper loss and consequently poor trolley voltage, with its attendant evils of low locomotive speeds and increased locomotive motor maintenance. The speed of the coal-cutting machines will also be reduced. By relieving the substation of its, burden of the operating labor cost, the most economical location, from an electrical standpoint, may be chosen. The matter of machine insurance should also be considered. If an attendant is caring for several kinds of equipment, he cannot watch the machine continually for signs of trouble; therefore, continued overload, phase failure, low alternating-current voltage, bearing trouble, etc. may result. Some partly automatic equipments have been installed; these have protection against low voltage, reverse current, and bearing trouble and are provided with automatic reclosing circuit breakers. This is a step in the right direction but it does not go far enough to give first-class machine insurance.

Jan 9, 1921