By W. M. McKewan, R. G. Olsson

In order to improve the understanding of the iron oxide reduction mechanism, the rate of equal molar diffusion of hydrogen and water vapor was measured through disks of porous iron and alumina. The measuretneizts were made at atmospheric pressure at 800°, 900- , and 1000°C. It is shown tint the reduction of dense hematite pellets with hydrogen at these temperatures and at atmospheric pressure is to a great extent limited by gaseous diffusion between the bulk-gas phase and the iron-wustile interface. THE investigation of the reduction of iron oxides with hydrogen has been the subject of numerous papers. Although the effects of temperature, pressure, and gas composition on the rate of iron oxide reduction have been studied, the actual mechanism of the reduction process has not been definitely determined. As a means of improving the understanding of the mechanism, the rate of equal molar counterdiffusion of hydrogen and water vapor was measured through porous iron and porous alumina disks at reduction temperatures. The alumina was used as a basis of compari-son because its pore structure is homogeneous and independent of temperature. The porous iron was prepared by the reduction of dense hematite disks with hydrogen at the temperature of the subsequent diffusion experiment. The hematite disks were made from pellets that were identical to those used by McKewan1,2 in his study of iron oxide reduction with hydrogen. In these investigations the weight loss and rate of movement of the various interfaces were measured as a function of the reduction temperature and gas composition. With these reduction data and the presently reported diffusion data it is possible to determine the importance of H2-H2O transport between the bulk-gas phase and the Fe/FeO interface to the reduction of dense hematite. APPARATUS AND PROCEDURE A porous iron or alumina sample was held in the base plate of a sealed canister containing porous granular wustite, as illustrated schematically in Fig. 1. The canister was suspended from an automatic recording balance in a vertical tube furnace through which flowed hydrogen and water-vapor mixtures of known composition at atmospheric pressure (0.96 atm). Hydrogen from the gas stream diffused through the porous sample, reducing the wustite in the interior of the canister. The water vapor that was formed diffused back to the gas stream. The rate of diffusion was determined from the recorded weightloss data. The furnace, automatic balance, and gas-metering equipment have been described previously.2 The main body of the canister and the tubing extension were made of stainless steel while the base plate was made of high-purity iron. The main body of the canister was % in. in diam. It held approximately 6 g of porous granular wustite that was prepared by reducing 0.1- to 0.2-cm-diam specular hematite particles at 900°C with an H2-H2O mixture of a composition near the iron-wustite equilibrium value. The upper end of the 1/8-in.-diam tubing extension was sealed with a segment of plastic tubing and a tubing clamp. The temperature at the top of the furnace was sufficiently high so that no water vapor condensed inside the extension. In the experiments with porous iron, iron oxide samples were prepared from reagent-grade hematite that was pressed and sintered in a manner previously described.' The resulting pellets had a density of 5.15 ± 0.05 g per cu cm. Each pellet was centerless-ground

Jan 1, 1967

Elected Died 1895 *ABBOTT, AI ATTHUR 1908 1882 *ABBOTT, ARTHUR V 1906 1905 * ABE, MASAYOSHI 1909 1903 * ADAMS, CHARLES C. 1905 1906 * ADAMS, JOHN C. 1913 1905 * ADAMS, WILLAMS 1909 1903 * ADAMS, W. EDWARDS 1910 1884 *ADDY, MATTHEW 1896 1906 * AFFLECK, WILLIAM A. 1911 1889 * AKERS, WILLIAMS A. 1906 1905 * ALABASTER, RUPPERT C. 1911 1899 * ALBERGER, LOUIS R. 1911 1894 *ALLEN R B 1896 1905 * ALLEN, R. SCOTT 1906 1874 * AMIOT, H. 1892 1886 *AMSLER, CARL 1894 1898 ** ANDRSON, JOHN W 1905 1895 *ÅNGSTROM, CARL 1901 1887 * ARCHBALD, JAMES 1910 1900 * ARLETT, GEORGE H 1906 1895 *ARMSTRONG, JOHN F 1898 1882 *ARNOLDS, HUGO 1886 1875 *ASHBURNER, CHARLES A 1889 1872 *ASIIBURNER, WILLIAM 1887 1883 *ATKINS, C M , JR 1885

Jan 1, 1917

By P. K. Koh

Isothermal salt bath annealing of 0.014-in. thick 3 pct Si-Fe sheet was conducted at temperatures ranging from 927" to 1260°C in order to investigate the grain-growth behavior. Within the temperature range studied normal grain growth did not take place; instead nucleated grain growth prevailed. The nucleation frequency was found to increase with the annealing temperature, with corresponding decrease in grain diameter of ultimate secondaries after long-time annealing. Large secondaries grown by low-temperature isothermal annealing are essentially of (110)[001] orientation, and the (110)[001] texture is strong. The relatively small secondaries grown by high-temperature isothermal annealing also have orientations near (110)[001] as an average but widely scattered; thus the amount of (110)[001] texture is found to decxease with isothermal annealing temperature. Grain growth and texture development at various annealing temperatures can be described by families of sigmoidal curves with the time axis. ThE cube-on-edge (110)[001] texture and predominating large secondaries in fully annealed 3 pct Si-Fe are customarily produced by a 1100°C annealing of a primary recrystallized sheet. On annealing the primary recrystallized sheet above the temperature at which secondary recrystalliza-tion starts May and turnbull' have demonstrated that secondary grains decrease in size as the temperature is increased. The phenomenon was attributed to a decrease in the (G/N) ratio where G is the growth rate of secondary grains and N is their nucleation frequency. In addition, the growth of grains in orientations rather far from (110) [0011 occurred. The present investigation is devoted to detailed rate studies of the same phenomenon. Mi-crostructure, magnetic anisotropy, and texture data were obtained on strips of 3 pct Si-Fe isothermally annealed for various lengths of time in a BaC12 salt bath at temperatures ranging from 927' to 1260°C. The texture results are reported elsewhere.2 EXPERIMENTAL PROCEDURE Commercial 0.014-in. cold-rolled silicon-iron strip (3.16 pct Si), prepared by two stages of cold rolling with an intermediate short anneal, was given a decarburizing 3-min anneal at 800°C. Metallo- graphic studies indicated complete recrystallization. In order to provide a protective atmosphere and to obtain a rapid rise to an elevated temperature, a BaC12 and NaCl fused salt bath was used to heat samples isothermally at temperatures from 927" to 1260°C for various lengths of time. Torque magnetometer measurements were made on 1-in.-diam disc specimens before and after annealing, since magnetic torque curves supply information on textures and texture changes. Surface layers of the strip samples were polished and etched to reveal the grain structure. The diameters of grains were measured from micrographs at X100. The average value of diameters of matrix grains was established. Individual grains in the micrograph were cut out separately along grain boundaries. These grains were classified either as matrix grains or growth grains. The percent weight of growth grains in the cut-out patterns was reported as percent growth. Manv of the individual grains in the annealed samples were large enough to be X-rayed with a 5-mil beam for Lauegrams. Complete (110) pole figures were obtained for the primary recrystallized structure and short-time annealed structure with CoKa radiation at 30 kv in the back-reflection range, such as (220) for (110) poles, as described recently by Newkirk and ~ruce.~ Both the X-ray optics and the technique for pole figure differed slightly from those adapted previously.4

Jan 1, 1960

By David Cornell, Yusuf K. Sukkar

The fundamental differential equation for fluid flow has been rearranged, integrated numerically for natural gases, and the results presented in tabular and graphical form suitable for the direct calculation of vertical gas flow problems. The integration is rigorous except for the use of a constant average temperature. Both static and flowing bottom-hole pressures may be calculated by (his method without resort to trial and error procedures. INTRODUCTION Bottom-hole pressures can be determined either by direct measurement with a bottom-hole pressure gauge or by calculation. Since measurement with a bottom-hole pressure gauge is costly, calculation of bottom-hole pressures is to be preferred when possible. Calculation involves knowledge of the wellhead pressure, the properties of the gas, the depth of the well, the flow rate, the temperature of the gas, and the size of the flow line. These quantities must be combined in a suitable equation for vertical flow. Several equations have been developed for the purpose of calculating gas flow through both horizontal and vertical pipes1,2,4,5,6,7,8,9 These equations all have the basic differential equation for flow as their starting point. They differ only in the assumptions which are made in order to simplify the integration step. The bottom-hole pressures calculated using any of the better known equations are in good agreement with bottom-hole pressures calculated by a more rigorous but considerably more tedious stepwise integration method. All of these methods, however. require a trial and error solution for the calculation of flowing bottom-hole pressures. The purpose of this paper is to present a method which provides a direct solution of static and flowing bottom-hole pressures without use of a trial and error solution. At the same time the method involves fewer simplifying assumptions than any of the previous methods used, except lor the lengthy stepwise method. The derivation of any practical flow equation begins with the basic differential equation which is rigorous for almost all flow problems. The five terms in Equation 1 represent the potential energy, the potential energy of position, the kinetic energy, the shaft work done, and the energy losses due to motion of the fluid respectively. Equation 1 reduces to Bernoulli's theorem for the case of horizontal flow of an incompressible fluid, no work done, and no energy losses due to friction. In the present case, the term (v) (dv)/(g,.) can be shown to be quite negligible compared to the other terms, and is therefore neglected in the derivation. The term — dws includes work done by a pump or turbine in the system and is zero in this case. The frictional losses in the pipe are included in the term — d(lw) which is expressed in terms of the Moody friction factor as in Equation 2. (f) (v2) (dL) d(lW) = (f)(V2) (dl)/(2) (g) (d) The specific volume of a gas can be expressed in terms of the temperature, pressure, molecular weight, and compressibility factor. The velocity of the gas can be expressed in terms of the weight rate of flow, the specific volume, and the dimensions of the pipe.The reduced pressure Pr is to be used because z can be expressed as a function of Pr and Tr alone for most natural gases:

Jan 1, 1956

By W. I. Duvall

A brief review of the resonant frequency and ultrasonic pulse methods for obtaining elastic constants of rock samples shows that the equations for an iso-tropic elastic solid commonly used to calculate Young's modulus, modulus of rigidity and Poisson's ratio can result in appreciable error if the rock is even slightly anisotropic. Consideration of the equations that relate bar velocities and free medium velocities to elastic constants for orthotropic, transversely isotropic and isotropic solids shows that a combination of the two methods can be used to determine average elastic constants for a single sample of rock. The determination of elastic constants in different directions requires a large number of tests on oriented samples. The use of both the resonant frequency and ultrasonic pulse methods is recommended so that the determination of both Young's modulus and modulus of rigidity is independent of the determination of Poisson's ratio. The dynamic elastic constants of rock can be determined in the laboratory from measurements on small samples which may be in the form of right circular cylinders (diamond drill core). Either the resonant frequency6 or ultrasonic pulse method1 can be used to determine the longitudinal and shear velocities in the same specimen. The resonant frequency method provides a measure of the longitudinal bar velocity, V,, and the torsional bar velocity Vt; whereas the ultrasonic pulse method provides a measure of the free medium longitudinal velocity, Vp, and the free medium shear velocity, V, . The elastic constants (Young's modulus E, modulus of rigidity G, and Poisson's ratio v) are calculated from the density of the specimen, p, and one of the pairs of velocities by means of equations from isotropic elastic theory. For the resonant frequency method the equations are: It should be noted that Eq. 5 is derived from Eq. 4 and 6 and the relation between the elastic constants for an isotropic solid as given by the first part of Eq. 3. The in situ determination of dynamic elastic constants is accomplished by generating a complex seismic pulse in the rock and measuring the arrival times for the longitudinal and shear phases of the pulse at two distant points.5 From these travel times and the distance of the travel path both Vp and Vs are determined. The density of the rock is determined from samples in the laboratory, and Eq. 4 to 6 are used to calculate the elastic constants. These three methods involve the assumption of isotropy and perfect elasticity, and require the use of the relation v = (E/2G) - 1, which holds only if the elastic constants are the same in at least two directions. The calculation of v by means of Eq. 3 introduces considerable error, as a 1% error in V, and V, results in a 20% error in v. If frequencies for samples with a length-to-diameter ratio greater than four and a length greater than 8 in. are measured carefully, the experimental error can be kept to 1%. However, it is not unreasonable to expect that the variation in Vb and Vt with direction may exceed 1%. Thus, for even a small percentage of anisotropy the use of Eq. 3 can result in considerable error in v. The calculation of v by Eq. 5 also involves some uncertainty as a 1% error in Vs and Vp can result in a 6% error in v. By means of the pulse method both

Jan 1, 1965

By W. R. Wilcox

The camphor-anthracene system was chosen as a transparent low-melting analog of the zirconium carbide -graphite system. Camphor and zirconium car -bide both grow nonfaceted, while casting of mixtures yields platelets of both anthracene and graphite. Zone melting of thin layers of organic was observed under the microscope. Irregular lamellar structures were produced at high values of the ratio of the temperature gradient G to the zoning rate V. The anthracene invariably led the camphor, indicating lower kinetic undercooling for the anthracene. The lamellar spacing was an order of magnitude greater than typical spacings for metal eutectic systems. Exact behavior depended on orientation of the anthracene. Oriented dendritic structures were produced at low values of G/V. Transient and oscillatory behavior were also observed—much of it unexpected. A.RC-CAST refractory carbide-graphite mixtures are promising thermal-shock resistant materials. Oriented structures of these materials would be superior to arc-cast materials for many applications. Mollard and Flemings1 and Cline2 have shown that aligned structures can be obtained for a wide range of Pb-Sn alloys. However, these metals both solidify in a nonfaceted manner while graphite yields platelets or flakes. In addition only small diameter samples of Pb-Sn alloys were produced because it was necessary to avoid free convection and to have high temperature gradients. The purpose of the present work was twofold: 1) To observe the solidification of a transparent low-melting analog of carbide-graphite systems and 2) to see if larger diameter samples can be produced. EXPERIMENTAL PROCEDURE When zirconium carbide-graphite mixtures are cast, the resulting structure naturally depends on composition. Carbide-rich mixtures yield metal-like nonfaceted carbide dendrites in a eutectic matrix. Graphite-rich alloys have graphite platelets in a eutectic matrix. Empirically it was found that camphor-anthracene mixtures produce similar structures with camphor being nonfaceted and anthracene forming plates. The organic eutectic melted at 116°C and was composed of 78 wt pet camphor.3 The camphor used was U.S.P. grade from Fisher Scientific Company; the anthracene was 98+ pet fro Aldrich Chemical Co. The impurity content is judged to be on the order of 1 pet. Mixtures ranging from 50 to 88 wt pet camphor were employed for the experiments. All but one of the experiments were performed on the microscope-stage zone melting apparatus described in detail elsewhere.4 The organic mixtures were contained in horizontal cells made of microscope slides or cover glasses. In most of the cells the organic was present as a very thin layer, thus giving almost two-dimensional growth behavior. The cells were moved slowly under a heated wire, which caused a molten zone to move through the solid at rates ranging from 0.01 to 5.4 cm per hr. The temperature gradient was estimated before moving the zone by measuring the distance between the line where all solid was melted (freezing point) and that where solid first began to melt (eutectic temperature). The temperature gradient was found to be 465°C per cm in the thinnest cells used, which were made by pressing together two microscope cover slips in the organic melt and then rapidly withdrawing them. RESULTS The experimental results are described in four parts: simultaneous growth, dendritic growth, irregular growth, and transients and erratic phenomena. Steady state data are summarized in Fig. 1. Except where noted all comments are for the cells containing a thin layer of organic. A) Simultaneous Growth. Simultaneous and roughly parallel growth of anthracene and camphor was obtained over the full range of compositions investi-

Jan 1, 1970

By D. L. Albright, R. W. Kraft

Solidification experiments were conducted with the objective of testing the theory of eutectic colony formation. Appropriate control of variables in tests on a series of high-purity aluminum-copper specimens of eutectic composition resulted in the observation of three types of eutectic microstructures, these being a unique structure consisting of lamellae essentially parallel to one another, a banded structure, and the colony structure. Lamellar faults, which are morphologically similar in many respects to edge dislocation models in crystals, produced a complex substructure in these specimens. SOLUTE rejection at the advancing solid-liquid interface of a unidirectionally solidified single-phase metal can cause the liquid immediately in front of the interface to become constitutionally super-cooled below the equilibrium liquidus temperature. Constitutional super-cooling occurs if the solidification rate, R, is too rapid, or if the thermal gradient in the liquid at the interface, G, is too low. 1 This constitutionally supercooled layer in turn stabilizes a cellular rather than a planar interface.&apos; A similar cellular interface has been observed when lamellar and other types of eutectics were unidirectionally solidified, and it has been shown that the cellular interface led to the formation of eutectic colonies.&apos; The lamellar structure is fan-shaped at the edges of colonies (which correspond to valleys or grooves in the cellular interface) because the lamellae grow normal to the local interface. One of the possible mechanisms which might cause the formation of the cellular interface, in the case of solidifying eutectic alloys, is constitutional supercooling of the liquid with respect to a third component rejected by both phases of the eutectic.3,4 On the basis of the analogy between the solidification of single-phase metals and binary eutectics, a eutectic alloy should solidify with a planar interface if the ratio of G/R is sufficiently high to compensate for any impurity which might be present and causing constitutional supercooling. The fan-like microstruc-ture of eutectic colonies should not occur under these conditions and the lamellae should be parallel to one another and to the solidification direction for extended distances. The experiments conducted in this investigation were designed to test these ideas. Following a resume of the experimental procedure, the various microstructures observed during the study are described, and their relationship to the growth conditions which produced them is discussed. EXPERIMENTAL PROCEDURE The eutectic between an aluminum solid solution and 0 phase (approximate composition CuA12) was chosen for this work for the following reasons: it was known that a lamellar structure forms, the eutectic temperature is low enough to facilitate experimental work, and the components can be procured commercially in a very pure form. High-purity copper (est. 99.999 pct Cu, obtained from National Research Corp.) and spectrographic aluminum rods, having impurities other than copper estimated to be Zn-15 ppm, Mg-10 ppm, Fe-3 ppm, Na-2 ppm, Cd-1 ppm, and Mn < 1 ppm, were melted in a stabilized zirconia crucible in a vacuum induction furnace at a pressure of 10 pof Hg. The melt was superheated to about 1000°C to assure mixing, cooled to 780°C and cast into an investment mold which yielded sixteen cylindrical specimen blanks 1/2 in. in diam and 5 1/2 in. long. The casting was allowed to solidify under vacuum. This master heat had an analysis of 32.6 wt pct Cu and 67.4 wt pct A1 by difference. The cylindrical specimen blanks were remelted and solidified unidirectionally in an apparatus illustrated schematically in Fig. 1. An RF induction coil heated

Jan 1, 1962

By E. S. Bumps

A series of macrographs are presented for the purpose of graphically recording the strain phenomenon that accompanies the energy transition in the Charpy impact testing of a mild steel that is susceptible to strain aging. STRAIN patterns in mild steel Charpy impact specimens were obtained in order to determine whether, on the first appearance of plastic strain during deformation, the initial fracture cracks appear in the region of plastic strain or in the elasti-cally deformed regions between. Although this attempt to locate the initiation of cleavage was not successful, the observed strain patterns illustrating various stress conditions in partially deformed Charpy specimens are presented along with a discussion of the possible dependence of transition energy on the yield phenomenon. Earlier work on the development of strain patterns in mild steel have been reported by Fry1 and later by Jevon.2 Harris, Rinebolt, and Raring3 observed characteristic strain markings on the surface of Charpy V-notch impact specimens fractured above and below the transition temperature which they presented schematically. It is intended that the strain figures presented here will add to the literature a graphic correlation of strain with transition energy in impact specimens. Samples of % in. round hot rolled, 0.20 pct C steel were machined to standard 0.394 in. sq, V-notch Charpy impact specimens. Preliminary testing involved determination of transition temperature, Fig. 1, using a Sontagg impact tester. These data were subsequently used to select temperatures above, within, and below the transition range at which specimens were partially deformed. Partial deformation was obtained by either varying the energy or the testing temperature, see Table I. Macroscopic strain figures shown in Figs. 2 to 19 were produced by several metallographic repolish-ing and etching steps. The macroetchant used was as follows:4 120 g HCl, concentrated; 100 ml water; and 90 g cupric chloride. Strain figures were obtained on the outer surface and on sections through the central portion of the impact specimens in order to determine an approximation of the volumetric strain pattern. In the tensile strain figures reported by Jevon, it was found that strain etching would not work immediately following strain unless the material was heated to 200°C. The impact strain patterns presented here were obtained without this heating, but the specimens were not etched until ten months after straining. This confirms a discussion of Jevon&apos;s paper, in which it was pointed out that strain figures can also be developed after aging for long periods of time at room temperature. Hardness of the strained and unstrained portions, revealed by the etched pattern, was explored using R, impressions converted to R, hardness values. Discussion of Results In the impact test, as in the tensile test, some parts of the specimen yield and deform plastically, while other regions are deformed only elastically. The plastic deformation bears a relation to the imposed stress pattern. In the strain figures presented here, the plastically deformed regions are the dark etching ones. The strain figures are always symmetrical because the stress state in the Charpy-type specimen under impact loading is symmetrical. The difficulties encountered to produce initial cracks are intimated in Figs. 2 and 4. At a temperature of —75ºF, the stress was not sufficient to pro-

Jan 1, 1953

By L. G. Huntley

The entire production of Colombia for 1927 was that from the Tropical Oil Co. concession. Production was approximately 14,000,000 bbl., of which 12,081,000 bbl. were exported from the Mamonal terminal of the Andian National Corp. near Cartagena. The balance represents that refined and used or marketed within Colombia. As production in 1926 was only 6,443,540 bbl., the increase has been more than 100 per cent. This is partly due to the looping of the pipe line from the concession to the coast, and the resultant increase in capacity to 50,000 bbl. per day, and also to increased domestic sales. The refinery at Barranca has been doubled in capacity, and it is understood is now handling 5000 bbl. of crude daily. This gives the producing field a potential outlet of 55,000 bbl. daily. The Tropical Oil Co. completed 82 wells in 1927, with one abandoned for drilling difficulties. The average daily initial production was 1136 bbl. per well. The largest well is reported to be No. 173 La Cira, rated as 5000 bbl. initial. Most of the wells were drilled on the Infantas and La Cira structures, the latter located en echelon to the northwest of the main Infantas anticline, and separated from it only by a low saddle. Drilling operations on the Llanos fold, also en echelon with Infantas but to the southeast, and at San Luis, bearing about the same relationship to the Umir Hills uplift, are still more or less in the exploratory stage. The four structures mentioned cover approximately 15,000 acres, on which there are at present 223 producing wells. Drilling has been better than 92 per cent. successful since starting operations on this concession. Allowing 15 acres per well, which is 50 per cent. more than good practice in the Mid-Continent fields, there is thus room for 1000 wclls, which at the recent rate is a 10-year drilling campaign. This does not take into consideration the known deeper oil zones, which have not been prospected, but which are uniformly petroliferous at their outcrops to the eastward. It is estimated that with the enlarged pipe line capacity, as well as increased domestic consumption, the production for this country will be about 20,000,000 bbl. for the current year of 1928. It is possible that

Jan 1, 1928

By William B. Plank

ENROLMENT data given in this report of the seventh study of the schools by the Mineral Industry Education Division reveals the critical situation in the mineral engineering schools of the United States. Complete figures for the year 1942-43 show that at that time, about one year after Pearl Harbor, the enrollment of mineral engineers was 6385 or 30 per cent less than in 199441. By October 1943, however, enrollment had dropped to 2050, as reported in the Journal of Engineering Education of January 1944. This was a further reduction of 68 per cent in one year, or 77 per cent in three years. With accelerated programs in effect during the current year, with many graduations since last October, and with the military forces taking practically all the high school graduates, the present enrollment is, of course, much lower than the 2050 above given. There are no late data on the exact situation. In Canada, the same situation exists in the mineral engineering schools, only

Jan 1, 1944

By Mary Barrett, Walter Rose

INTRODUCTION The conventional way to program reservoir problems* for solution on the electric analyzer1 is one which concentrates the block units towards the inner radius of the prototype system being represented by the analog model. This is achieved by the device of considering block units of equal value radial resistance, leading to the consequences: (1) the ratio of the external to the internal radius of each block unit is a constant (i.e. r1/ri-l = constant a); (2) the external radius of the nth block unit is equal to the innermost radius of the system times the constant a raised to the nth power: (3) the capacitance of the block units increase by a factor of a2 going out radially from the innermost to the outermost boundaries of the system; (4) given n block units in the radial direction, the capacitance ratio of the outermost to the innermost block unit is a (2n-2); and (5) the vertical resistance of the block units decrease by a factor of a going out radially from the innermost to the outermost boundaries of the system, such that the ratio of the maximum to minimum vertical resistance is also given by the factor a(2n-2) PRESENT PROGRAMMING METHOD While this conventional way of programming problems is quite adequate for routine uses of the electric analyzer, it leads to difficulties in those cases where the inner radius of the prototype system (e.g., the well-bore) is small compared to the external radius (e.g.. the external reservoir boundary). To handle such a case by the conventional method would require either that a large value be selected for the constant a or that a large number n, of radial block units be chosen. In consequence, the capacitance and vertical resistance ratios become impossibly large, as will be evident from the relations given above. In any event, the size of the smallest and largest capacitors will always be limited by the size of commercially available components, and the analyzer itself will determine how many mesh points are available for radial block units. For example, it can be shown that if the maximum capacitance ratio which can be electrically handled is a factor of l04, the maximum external radius of the system which can be considered (assuming an internal wellbore radius of 0.25 ft is: It is thus seen that in direct consequence of having the inner wellbore radius small compared to the external radius, models extending beyond 30 to 40 ft are not possible when the capacitance ratio is limited to l04. (NB. A value of 10-9 farads can perhaps be taken as the minimum electrical capacitance possible if corrections for the capacitance of the lead wires are to be avoided. Values greater than 10-5 farads would require the use of unstable and inaccurate electrolytic capacitors). On the other hand, models extending out to 500 to 5,000 ft may be desired in single-well problems, and hence the need for a revised method of problem programming. * REVISED PROGRAMMING METHOD The revised method of programming is one which attempts to retain the desirable features of the conventional method (viz. concentration of block units towards the inner boundary, simplicity in computation, etc.) without having as a consequence that impossible capacitance and vertical resistance ratios will be required. Other advantages will also be achieved by the revised

Jan 1, 1957

By F. C. Schora, H. P. Meissner

Both a graphical and an analytical technique are presented for calculating stream compositions and temperatures in adiabatic staged systems in which solids travel countercurrently to a gas stream. Such a system might be a tower containing several plates, on each of which the descending solid is fluidized by the rising gas stream. Examples are presented in which chemical reactions occur, including the oxidation of SO, by a solid catalyst and the gaseous reduction of iron oxides. COUNTERCURRENT staged processes involving reactions between solid and gas streams are becoming more common. These operations are generally carried out in a series of beds of fluidized solids, with each bed or "plate" acting as a stage. Fig. 1 is a schematic diagram of such a series of stages located in a column, down through which a solids stream moves from stage to stage counter to a rising gas stream. Typical reactions carried out in such systems are the dehydration of aluminum trihydrate, the calcining of limestone, and the gaseous reduction of iron oxides. Calculation of the performance of these counter-current systems rapidly becomes more complex with increases in the number of stages and in the number of chemical reactions occurring. Calcula-tional procedures for isothermal operations of such systems have been described.4 Actual tower operations, however, are generally adiabatic, and in consequence far from isothermal. The object here is to present both graphical and analytical techniques applicable to such adiabatic towers operating continuously and in steady state. In this introductory discussion, the graphical techniques presented are of the McCabe-Thiele type, rather than of the Pon-chon type. In all the examples presented, it will be assumed that both thermal and chemical equilibrium are attained in each bed. The assumption that the gas and solid streams leaving each bed are at the same temperature as the bed is in accordance with the familiar behavior of actual fluidized solid systems. Chemical equilibrium, on the other hand, is not necessarily attained in any given stage between these two streams, even with deep beds, since reaction rates may be slow. In the last section of this paper, discussion is presented of methods suitable for use when chemical equilibrium is not attained. The adiabatic tower in Fig. 1 has "n" stages numbered from 1 to n, starting with the bottom stage as number 1. In analyzing this tower&apos;s performance, it is important to express gas flow rates in terms of a key component or element which remains completely within the gas stream throughout the tower. Similarly, solid flow is best expressed in terms of a key compound or element which remains within the solid phase throughout the tower. Thus, in burning limestone with a hot flue gas, the gas flow might be expressed as G, the pound mols of nitrogen flowing through the tower per unit time, while solid flow might be expressed as S, the pound atoms of calcium in all forms in the solid stream per unit of time. Defined in this way, both G and S are constant throughout the tower. The enthalpy of the gas and solid streams are now best expressed in terms of these key components. That is, the gas stream enthalpy H is expressed as Btu in the total gas per mol of the key component in the gas. Similarly, the solids stream enthalpy h is expressed as Btu in the total solid stream per pound mol (or pound atom) of the key component in this stream.

Jan 1, 1962

By C. S. Smith, L. H. Beck

KNOWLEDGE of the Cu-Zn constitution diagram was critically examined in 1944 by G. V. Ray-nor,1 who suggested the diagram reproduced in Fig. 1 as the best evaluation of available data. No pertinent work on the constitution has been published since that time, although a number of authors have discussed transformation kinetics and theory. Despite the large amount of work that has been done on the constitution of these industrially important and scientifically interesting alloys, minor uncertainties still exist. For example, it is still not possible to say definitely whether a two-phase region exists between the ordered and disordered forms of the 8 phase. A careful re-examination of the phase boundaries in this part of the diagram was therefore undertaken. Two methods were selected for the new investigation—quantitative metallography for the higher temperatures and precision lattice parameter measurement for lower temperatures. Because of the relatively narrow two-phase regions flanking the ß phase in these alloys, quantitative metallography is particularly suited for their examination, since the relative amounts of the two phases are very sensitive to their compositions. The method, however, is useless below about 350°C because of the inadequate resolution of the two constituents. Below 400°, however, the X-ray diffraction method is applicable, although it is of somewhat lower sensitivity in this system. The changes of composition that occur during quenching from above about 500°C entirely vitiate X-ray measurements at room temperature though they do not affect metallographic area measurements. The two methods overlap and supplement each other admirably. Both methods depend on the attainment of equilibrium composition of the two phases in a more or less intimate mixture and thus avoid the difficult problems of nucleation and long range diffusion involved in the conventional metallographic bracketing method. The alloys were melted from a master alloy made from re-electrolyzed cathode copper and Horsehead 99.99 pct Zn. Melting was done under a cover of either borax or charcoal and the alloys cast into a 7/8 in. sq graphite mold for the a-ß alloys or a 3/8 in. diam cylindrical graphite mold for the ß-? alloys. The a-ß alloys were rolled at 750°C to 5/8 in. sq; annealed for 24 hr at 800°C and quenched; then rolled and swaged at 200°C to 3/8 in. diam rods, annealed 24 hr at 200°C, quenched and cold rolled 2 pct reduction. This treatment was intended to obtain a small grain size and to produce many nuclei of the minor phase for growth on subsequent heat treatment. The unworkable ß-? alloys were given preliminary treatment by sealing in Vycor tubes in vacuum and annealing for 4 hr at 800°C followed by cooling in air. Samples of homogenized alloys were checked spectrographically for impurities, but the principal components were determined on samples subsequent to heat treatment. The impurities analyzed averaged approximately as follows: Ag, 0.0002 pct; Fe, 0.004; Si, 0.0008; Cd, 0.005; Mg, 0.0002; and Pb, 0.002. For metallography, samples of appropriate composition were cut into rods 5/8 in. long, sealed in pyrex tubes in vacuum and annealed for eight weeks at temperatures of 470°C and below, two weeks at 480°, 500°, and 600°C, and 4 hr at 700°C, followed by quenching in cold water. Temperatures were accurate to ±2°C. The cylinders were then machined to 8.7 mm diam and a slice weighing 1.5 g cut with a thin saw transversely from the center of each. This

Jan 1, 1953

By S. S. Shen, M. J. Pool, P. J. Spencer, J. R. Guadagno

VERY few thermodynamic data are available for rare-earth alloys, partly because of the difficulties of obtaining the metals in sufficiently pure form and also because of their comparative scarcity up to the present time. The rare earths form a very interesting series in the periodic table in view of the progressive filling of their 4f subvalence electron shell and would be expected to provide useful information with regard to alloying characteristics of transition elements. It has been found in recent calorimetric investigations that the heats of solution of a number of the rare-earth metals in liquid tin are highly exothermic.1-4 Exceptionally strong bonding between rare-earth and tin atoms is clearly indicated in the liquid solutions. Continued thermodynamic studies of the behavior of rare earths in solution could thus contribute a great deal to present theoretical knowledge of alloying behavior and would yield an insight into bonding of a strength hitherto unencountered in liquid alloys. The determination of the heats of solution of the pure components in liquid tin is an essential preliminary to calorimetric work of this nature. Heats of solution of praseodymium, neodymium, and samarium in liquid tin at 750" &apos; and the heats of mixing of Pr-Nd solid solutions&apos; have already been determined in this laboratory. The present investigations with lanthanum continue the study of rare-earth elements. Details of the construction and operation of the liquid metal solution calorimeter used in this work have been published previously by Pool and Peluso and no further description will be given here. The lanthanum used in heat of solution determinations was supplied by Lunex who quoted the purity as 99.9 pct. Their detailed analysis of the material is given in Table I. Samples of 0.0003 to 0.0005 g-atom were used for each run and great care was taken to remove all surface oxide prior to weighing. The samples were stored at all other times in a beaker of oil to prevent their otherwise rapid oxidation. The compounds LaSn (Cudu, L1P type structure) and La&, (structure not classified) were prepared from the appropriate quantities of the two pure components by arc melting under a purified argon atmosphere and once again great precautions were taken to avoid any subsequent oxidation of the specimens. Although no structural examination of the compounds was made, the consistency of thermodynarnic measurements carried out on twenty or so individual samples of each indicates that the compounds were in fact homogeneous, single phase alloys. Samples of the compounds consisting of 0.0003 to 0.002 moles were used in the calorimetric measurements. A solvent bath consisting of approximately 80 g of 99.9 pct pure Sn was used for each series of runs and its heat capacity was determined at regular intervals throughout the experiments using pure tin or tungsten calibration samples. Measurements were made of the heat of solution of lanthanum in liquid tin at 725", 750C, and 775°K and at compositions up to 2.21, 4.76, and 5.25 at. pct La at the three temperatures respectively. In every case, the heat of solution of lanthanum remained constant at its limiting value, within experimental limits, up to the highest lanthanum concentration investigated. Since no change in was observed, it was concluded that the liquid/liquid + LaSn, phase boundary had not been

Jan 1, 1969

By W. W. Krysko

In order to calculate the critical particle size of lead oxide entrapped in lead, Stoke&apos;s Formula may be applied. All data were available except figures for the density of lead oxide at elevated temperatwes. The density of lead oxide was determined by means of dilatometmetrc and volumetric methods up to 1010°C. Graphs of the density of lead and lead oxide as well as the viscosity of lead are given and discussed, with the conclusion that the most unfavorable region for the separation of lead oxide from molten lead lies just above the melting point of lead. DURING previous investigations, particularly on the dedrossing of lead with aluminum1 and the oxygen solubility in lead,&apos; the critical particle size of lead oxide which could be entrapped in solidifying lead was estimated by calculation, and it was shown that high values found for the oxygen content of lead may be due to the method of sampling and the entrapped particles of dross. Unfortunately, due to lack of data, an exact mathematical solution was not possible. The particle size which will separate under a given condition can be estimated from Stoke&apos;s Law, which states that where: d = diameter of the critical particle size ¦q = viscosity of lead in Poise V = constant velocity in cm sec-I g = 981 cm sec-2 61= specific gravity of lead 62= specific gravity of lead oxide The depth of the lead bath and the time before solidifying define the velocity. The viscosity of molten lead is known from earlier work by Krysko and is given in Table I. The specific gravity of lead is also known, see Table II. These values are according to Hofmann. A careful survey of literature revealed no values for the density of lead oxide at elevated temperatures. The present investigation was therefore conducted to provide this information. RESEARCH INVESTIGATIONS The density of lead oxide was determined from the following experiments: 1) Determination of the density of lead oxide at room temperature. 2) Dilatometric investigations on the same samples. 3) Determination of the shrinkage at the liquid-solid trans£ormation. 4) Density determinations on liquid lead oxide. 5) Time temperature curves during cooling. 1) The samples for the determination of the density of lead oxide in the solid state were prepared in the following manner. Molten lead oxide was cast into I hot mold which could be opened along the longitudinal (vertical) axis. The cast samples were cylinders of approximately 10 mm diam and approximately 80 mm length. The cylindrical hot mold was open at both ends and was placed on a large copper chill plate shortly before casting. The solidification of the lead oxides proceeded upwards without any formation of internal cavities. The sample was carefully checked with respect to density and crystalline appearance, and only the lower portions which were crystalline and free from porosity were used. The density was determined in a specially made pyknometer-like container, where the surplus liquid was squeezed out through an orifice approximately 1/10 mm in diameter. Mercury or water was used as the liquid. The densities of the samples were calculated from the weight, volume, and mean specific gravity of eight samples was 9.62 * 0.05 g cm"3 at 22"~. 2) The samples were machined to approximately 1 1/2 in. in length and fitted into a dilatometer. A

Jan 1, 1962

By M. D. Arnold, P. B. Crawford, P. C. Hall

An experimental study has been made to determine the optimum flooding pressures for four different oils. The oil formation volume factors ranged from 1.08 to 2.13, and solution gas-oil ratios ranged from about 200 cu ft/bbl to 2,250 cu ft/bbl. Viscosities ranged from 0.38 to 0.95 cp at the respective bubble points of the fluids and from 0.7 to 20 cp at atmospheric pressure. Water floods were conducted at various pressure levels from run to run. The recovery as a function of flooding pressure was found to be different for each fluid, with optimum gas saturations ranging from 7 up to 35 per cent. The data indicate that substantially higher recoveries may be obtained if water floods are conducted at an optimum pressure and that this optimum pressure is a function of fluid properties. The same core was used for all tests, and the reproduction of saturations for various runs indicates that wettability in the predominantly water-wet core did not change. INTRODUCTION A paper was presented by Bass and Crawford&apos; which described an experimental study of the effects of flooding pressure and rate on oil recovery by water flooding. This work was conducted using high-pressure models operated in a manner similar to that of an actual reservoir, with gas saturations being obtained by a solution-gas-drive mechanism. They found that the greatest oil recovery was obtained for the system studied by flooding in the presence of a 5 to 7 per cent gas saturation. Another experimental study simulating field conditions was presented by Richardson and Perkins.&apos; They used an unconsolidated sand pack containing kerosene-natural gas fluid and interstitial water. They flooded at various pressures and flooding rates. For their system it was found that the recovery was independent of the pressure level at which the water flood was performed. Kyte, et al," found that oil recovery by water flooding was increased as the free gas saturation at waterflood initiation was increased. However, after the initial gas saturation was increased above 15 per cent, the increase in oil recovery tended to level off. All of their runs were made at the same pressure using a light oil saturated with helium. The desired gas saturation was obtained by injecting helium into the core. Dyes&apos; made calculations which showed that an optimum gas saturation of 12 to 14 per cent may result in an increase in oil recovery of 7 to 12 per cent over that obtained by flooding at the bubble-point pressure. Others have also found that the presence of a free gas saturation may increase the waterflood oil recovery. In each case shrinkage was small and changes in fluid properties with respect to pressure were small. A careful review of the literature reveals that at the present time there is a wide difference of opinion on the factors affecting waterflood recoveries. This diversity of opinion is probably due to the fact that very little research has been done which has taken into account the many variables existing in an actual field being water flooded. Since the literature contains little information on high-pressure waterflooding studies using various types of reservoir fluids, it was believed appropriate that such a study should be made. EQUIPMENT AND PROCEDURE All tests were made using the same consolidated sandstone core. Torpedo sandstone was used to turn a cylindrical core 13.5-in. long and with a 2.92-in. average diameter. The core had a porosity of 28 per cent and a permeability to brine of 146 md. This brine was made up by adding 20,000-ppm sodium chloride and 30,000-ppm sodium nitrite to distilled water. This was used as connate water and flooding water. No fresh water was ever brought in contact with the core, as tests showed the sandstone contained argillaceous material which swelled in the presence of fresh water and plugged the stone. The core was sealed in a section of 6-in. N-80 tubing with Woods metal filling the annulus. The core was mounted horizontally; an injection well was placed in the center of one end and a production well in the center of the other. Pressure control was maintained by placing a back-pressure regulator (upstream control) on the producing well. The "live" oil was stored in a separate bottle and water was injected into this bottle to displace the oil for saturating the core using a two-cylinder standard-proportioning pump. This same pump was used for water flooding the core at a constant rate. This system was enclosed in water jackets and the temperature was automatically main-

By M. C. Fuerstenau, A. M. Gaudin

A homogeneous suspension is viewed by X-rays. The radiation density seen, affords a measure of the extra absorption due to the solids contained. This radiation density, at a predetermined depth, varies with time. The chart of this relationship gives the desired determination. s it is frequently necessary to know the distribu-rt tion of particle sizes in various products used in industrial applications, a number of means have been devised for these determinations. Some of them include direct microscopic measurement, screening of product, extraction of samples from a settling slurry, air and liquid elutriation, adsorption of gases and liquids, and light absorption. The absorption of light as a means for particle size analysis has been known and employed for some time. X-ray absorption has not received the attention that light has enjoyed primarily because of the complex and costly instrumentation involved with X-rays. In 1954, Brown and Skrebowskil suggested the use of X-rays for this type of determination but did not supplement their suggestion with experiment. In 1958, the authors conducted size analysis experiments on suspensions of quartz with the Trans-viewer: an X-ray unit specifically adapted for sedimentation research, and Rossa conducted experiments in a similar manner in 1959 with a stable gamma emitter, AmZ4l, on suspensions of uranium oxide. To illustrate the applicability of X-ray absorption for analyzing particle size distributions, an essentially mono-energetic and well collimated X-ray beam was used as a source. The beam was made mono-energetic by placing a zirconium filter before the counting window together with feeding the pulses from the proportional counter into a reverter, a device capable of discriminating against pulses of various heights. The sketch in Fig. 1 shows the collimation arrangement in more detail. As shown, the X-ray beam was collimated by inserting a 3/8-in. ID pipe into one of the ports of the X-ray tube and further by two small steel plates with slits 3/32-in. wide and 1/2-in. long placed in front of the window of the Geiger-Mueller (G-M) tube. One of the plates was located 1/2 in. and the other 2 1/2 in. from the window of the counter; both plates were contained in an aluminum holder mounted on the box containing the G-M tube. This type and degree of collimation should eliminate any intensity due to scattered radiation; the transmitted intensity would then be solely a functior. of the absorption by the suspension at that level. Experimentally, homogeneous suspensions of finely ground quartz were prepared, Daxad (a sulfo-nated compound made from wood) was added as dis-persant, and the transmitted X-ray intensity measured as a function of time at a fixed depth in the suspension. In more detail, the experimental procedure involved the following: 1) measuring the transmitted X-ray intensity through the Daxad solution at a predetermined position or settling depth in the absence of solids, 2) placing a known amount of dry solids into the vessel and agitating thoroughly, 3) measuring the transmitted X-ray intensity at time zero (i.e., immediately upon cessation of stirring), and 4) measuring the transmitted X-ray intensity as a function of time (a 10-sec counting interval being chosen and counting being started 5 sec before the desired time). Since a linear relationship exists between percentage solid in a slurry and the logarithm of transmitted intensity for a homogeneous material, the cumu-

Jan 1, 1961

By James E. Lawver, James L. Wright

This paper discusses the design and calibration of a Faraday pail for measuring electric charge. The paper also shows that at least for two minerals, quartz and calcite, the phenomenon that Johnson termed "reversibility" can be explained in terms of the contact electrification between the minerals and the metal rotor of an electrostatic machine. Each year the free world produces about 13 million tons of mineral concentrates by electrical separation. However, despite the rather general acceptance of electrical concentration as an industrial process, research in this area has lagged far behind the efforts devoted to competitive processes such as froth flotation. The purpose of this paper is to describe the design and calibration of a Faraday ice pail for measuring charge density on mineral grains and to show some of its applications in the area of electrostatic and electrodynamic research. THE DESIGN AND CALIBRATION OF FARADAY PAILS FOR ABSOLUTE CHARGE MEASUREMENT The electric charge on mineral grains at a given time during an electrical concentration process is de- pendent on many factors and cannot, in general, be accurately calculated a priori. It is thus important to devise a method of measuring absolute charge. One method of measuring electric charge is to note the potential rise of an electrometer when charged particles drop into a Faraday pail. Two types of Faraday pail have been constructed and calibrated. The first type, Faraday Pail I (Fig. 1), is a vertical pail originally designed to measure the charge due to contact electrification between mineral grains and a metal rotor or due to conductive induction when mineral grains are passed over a rotating cylinder in the presence of an electric field. The second type, labeled Faraday Pail II (Fig. 2), is a horizontal pail designed to determine the charge distribution of mineral grains after they pass through the separating zone of the electrical concentrator shown in Fig. 4. The main advantage of the horizontal pail is its low head-room requirement and the long opening which enables the experimenter to sample the entire width of the stream of minerals being separated. The Faraday pails were calibrated in the following manner: A calibration head was constructed in the form of a hollow brass sphere that could be held in an insulated metal cylinder by vacuum (Fig. 1). The capacitance of the sphere was calculated by measuring the capacitance of the sphere and cylinder combined and that of the cylinder alone and subtracting the latter measurement from the former. The sphere was then charged to a known potential (V) and allowed to drop into the Faraday pail which was attached to a Keithley Model 610A electrometer. This instrument has an accuracy of 2% full scale and has

Jan 1, 1969

By Clyde E. Williams

MUCH has been said recently concerning the depletion of the Lake Superior iron ore re- serves. Estimates given indicate a total life of the present known reserves of twenty to thirty years. Some argue that there is no need to concern ourselves about the possible depletion of the Lake Superior iron ore supply because foreign ores can be brought in to this country at a lower price than rich agglomerated ore can be produced from the lean domestic ores. Some fear, as a result of this, a displacement of the steel business from present districts to the Atlantic seaboard. Others show that foreign ores will be brought to interior points via the projected Great Lakes-St. Lawrence waterway. Others believe that the South, given better freight rates, will extend its iron and steel market into northern territory.

Jan 1, 1931