By Michael Hoch, Seong Kwan Rhee

The ternary system Zr-Cr-0 was investigated at 1200°, 1500°, and 1700°C. The isotherms at these temperatures were determined by metallographic and X-ray diffraction analysis of carefully selected alloys. AS a part of a series of investigations1-4 of the ternary and quaternary phase diagrams on refractory metals and their compounds, the ternary system Zr-Cr-O was investigated at 1200°, 1500°, and 1'700°C. The binary diagrams Zr-Cr, Zr-O, and Cr-0 as reported by Hansen5 and Levin et a1.' and the existence of a ternary coompound ZrsCrsO (q-carbide structure a. = 11.96A) provided a good base for this investigation of the Zr-Cr-O phase diagram. MATERIALS The materials used and their suppliers were: Zirconium powder, 99.4 pct pure, Charles Hardy, New York; Zirconium dioxide, Fairmount Chemical Co., Newark, N.J.; Chromium powder, 99.85 pct pure, Fairmount Chemical Co., Newark, N.J.; Chromium sesquioxide, 99.86 pct pure, J. T. Baker Chemical Co., Pillipsburg, N.J. Though the materials used were not "hyperpure", the impurities present do not affect the results (lattice parameters, phase boundaries) within the experimental accuracy. EQUIPMENT AND PROCEDURE The detailed procedures and equipment used for this investigation were similar to those described elsewherel' "ith the exception that in this study an induction-heated argon-atmosphere furnace was used. The latter furnace was used to prevent the vaporization of chromium metal in samples in the higher temperature range (above 1200°C). The tungsten crucible was induct ion-heated in a vertical quartz tube filled with argon gas. The quartz tube was 1-1/2 in. in diameter and 10 in. long; it was connected at the top and bottom to water-cooled copper plates. The argon gas of a purity 99.995 pct was further purified by being passed through zirconium metal chips which were maintained at 800°C in a silica tube 1 in. in diameter and 30 in. in length. The furnace was flushed with argon gas for an hour before starting heating; during heating, a slight (3 cm oil) overpressure of argon was maintained in the system. Power was supplied by a 20-kw Ther-Monic Induction Generator. The samples rested on a tungsten-wire basket; the wire basket was connected to a tungsten wire which passed through the tungsten crucible lid, and entered the system on top through a Wilson-type seal. By pulling on the wire, the sample was removed from the crucible and dropped to the water-cooled copper base of the furnace. Because of the presence of argon gas, the cooling of the sample was even more rapid than in the vacuum furnace.' EXPERIMENTAL RESULTS AND DISCUSSION 1) Isothermal Section at 1200°C. The compositions investigated have been numbered within the phase diagram, Fig. 1, and all the pertinent information about the samples can be found in Table I. This table lists the composition of the samples, the phases present in the room-temperature diffraction patterns, the phases detectable in the microstruc-ture, and calculated lattice parameters of the a-zirconium phase. The shapes of the various phase

Jan 1, 1964

THE paper on "Cross-cuts in Coal Mining," by J. J. Rutledge (published in MINING AND METAL-LURGY, February, 1927, p. 64) was brought up for discussion at the annual meeting, where the follow-ing comments were made T. D. Thomas (Lehigh Coal & Navigation Co., Lansford, Pa.) : This question has caused me a lot of worry, not in the particular district in which I am, but throughout other districts. There are always several angles to consider. If you are in a hurry to push development work, you might increase the distance between cross-cuts from 60 to 350 ft., but if you have a 40-ft. chain pillar every 60 ft. it will cut down your entry driving a whole lot. Looking at it from the ventilation angle, I agree that too many cross-cuts in entries are bad things. You have a tremendous amount of leakage, and I have seen currents starting out with 45,000 cu. ft., and after passing about 30 or 40 cross-cuts the current has dwindled down to about 18,000 or 15;000 cu. ft. The result is that the question of putting in auxiliary fans is raised. That involves several points into which I do not want to go too far, but I am in favor of not getting in too many cross-cuts, putting them in only where they are necessary: I think the state mining laws are wrong in a number of places on that, and that when you finish with a cross-cut it should be in the room. It should be well sealed on an entry. There are several ways of tightening up the cross-cuts so as not to have the great amount of leakage and wastage of: air that we now have. 'I prefer tile stopping; other people prefer cement or brick, but there is a big fac-tor to all mines, saving the mine. I checked up on the number of fans in the anthracite region and found there are 651. That was derived from the state report of 1921, and it enabled me to compute from the power the weight of the air. In the anthracite region of Pennsylvania we put in 9 tons of air to every ton of coal we get out. Tracing that back again and taking the Government's figures which they made some time ago, I found but 20 per cent of the air got to the faces where it was actually needed. That is a tremendous big loss and shows a possibility for saving, money for the various coal companies. Chairman Rice: I think what Mr. Thomas refers to was an investigation by R. Y. Williams, of the Bureau of Mines in Illinois, where a study was made of 100 typical mines, and, speaking off-hand, my recollection is that we found as little as 15 per cent of air reached the faces in one of the mines and another was as much as 50. That seems to be a reflection on the type of stoppings and general ventilation scheme.

Jan 3, 1927

By C. E. Sims

In some experimental work conducted several years ago, it was noted that sulphur seemed to have a distinct influence on grain size of carbon steels. 111 order to check this observation, a series of S..A.E. 1040 steels was made with the normal composition held as nearly constant as possible. The steels were made with three sulphur levels, which were 0.012, 0.024 and 0.038 per cent sulphur, respectively. For each of the sulphur levels, steels were made with only silicon deoxidization and with aluminum additions of 0.1015, 0.025, 0.050 and 0.10 per cent. The melting medium was an acid-lined high-frequency induction furnace. These steels were forged and rolled and differentiall!. quenched from temperaturcs in the range of 1500O to 1800°F. After this, the A.S.T.M. grain size was determined and plotted as in Fig. I. It will be noted, first of all, that the aluminum-free steels had filler grain size with higher sulphur when heated to 1500, but that this condition was reversed at 1700°. When aluminum was added to produce fine grain size, the steels in the lowest sulphur level were fine-grained only to 1600°. and then only with an addition of one pound of aluminum per ton. The medium sulphur steels werc fine-grained to 1600' with a wider range of aluminum addition. The steels in the highest sulphur level were fine-grained at 1600° over a still wider range of aluminum additions and fine- grained at 1700° with an addition of one pound per ton. Fig. 2 shows curves of the grain-coarsening temperature for these steels and illustrates how sulphur and aluminum combine to give greater inhibition to grain growth than aluminum alone. Only the highest sulphur steels have a grain-coarsening temperaturc above 1700°.. At 1650°, the low sulphur steel is fine-grained only at its peak, while the highest sulphur steel is fine-grained over a wide range. In these tests, one pound of aluminum per ton gave the best results; this is equivalent to about 1 1/2 lb. per ton for commercial condition. IllcQuaid-Ehn tests made on these steels showed the same trend but to a lesser degree. The tests were repeated on a series of S.A.E:. 1015 steels with sulphur levels of 0.02 and 0.03j per cent. Aluminum additions were made in the range from 0.025 to 0.15 per cent. These steels were forged and rolled, normalized at 2000°F. to put them all in the same starting condition, then reheated to various temperatures from 1600" to 1800" and cooled at rates that would allow ferrite precipitation in the austenitic grain boundaries. The results of these tests arc shown in Fig. 3. It will be noted that. up to the temperature of 1650°, there is very little difference in the grain size obtained from the two levels of sulphur. .At temperatures of 1700° and 1750°, however, the lower sulphur steel was fine-grained only with an aluminum addition of 1 1/2 lb, per ton;

Jan 1, 1945

By Richard Moldenke

Note.—At the request of the American Society for Testing Materials, this paper wau presented at the New York Meeting, February, 1923, in connection with the "A. S. T. M. Tentative Specifications for Foundry Pig Iron" and The Physics of Cast Iron and Its Bearing on All Cast-iron Products and Specifications for Cast Iron," by William R. Webster. The discussion of this paper was not published by the Institute, having been referred to the American Society for Testing Materials, as these papers were again presented for discussion at the meeting of that Society at Atlantic Cit;, June, 1923. The result of these discussions is shown in the following abstract from the Committee A3 report on cast-iron specifications: During the past year, the adaptability of the tentative specifications for pig iron for the steel and the malleable foundry, in addition to the iron foundry proper, have been studied and suitable changes and rearrangements are being made which appear to cover the situation properly. In spite of the experience of foundrymen to the contrary, there is a persistent call from consumers of castinga for defixute compositions for given lines of castings. To respond to this call for information desired by the consumer—information every modern foundryman should have and guide his procedure with—the committee has requested the Sub-committee on General Cast!rigs to take up this matter with a view of constructing tables of analyses rang? for Important lines of foundry product. These analyses ranges however, are to be given as "recommendgd practice" and not intended for actual spkcification. In this way, the consumer of the foundry product will get the information he wants; the furnace-man will be gulded in the production of his pig irons to prepare for analyses ranges which are more closely standardized and have less of "freak" requirements made by Inexperienced metallurgists; and the foundryman will not be bound by chemical requirements he knows will not work out well with his particular reglonal supphes of melting stock. Doctor Moldenke's paper is published in full as it shows clearly the good results of the Institute's work in 1895 and a comparison of the same with the present knowledge of the metallurgy of cast iron—Bradley Stoughton, Chairman, Iron and Steel Committee. In MaRch, 1895, William R. Webster contributed a carefully prepared scheme for the study of the physics of cast iron to the American Institute of Mining Engineers at its Florida meeting. This summary of the interrelation of the chemical and physical characteristics of cast iron with the operations of daily foundry practice caused a wide discussion of the then little understood though universally used material. Mr. Webster has requested the author to bring the subject up to date and, while glad to comply, he must pay that with all the knowledge that has been gained in the quarter century that has passed since the subject was brought to the attention of the Institute—and we now are pretty familiar with cast iron in all its aspects—there is practically noth-

Jan 1, 1923

By Richard Moldenke

Note.—At the request of the American Society for Testing Materials, this paper wau presented at the New York Meeting, February, 1923, in connection with the "A. S. T. M. Tentative Specifications for Foundry Pig Iron" and The Physics of Cast Iron and Its Bearing on All Cast-iron Products and Specifications for Cast Iron," by William R. Webster. The discussion of this paper was not published by the Institute, having been referred to the American Society for Testing Materials, as these papers were again presented for discussion at the meeting of that Society at Atlantic Cit;, June, 1923. The result of these discussions is shown in the following abstract from the Committee A3 report on cast-iron specifications: During the past year, the adaptability of the tentative specifications for pig iron for the steel and the malleable foundry, in addition to the iron foundry proper, have been studied and suitable changes and rearrangements are being made which appear to cover the situation properly. In spite of the experience of foundrymen to the contrary, there is a persistent call from consumers of castinga for defixute compositions for given lines of castings. To respond to this call for information desired by the consumer—information every modern foundryman should have and guide his procedure with—the committee has requested the Sub-committee on General Cast!rigs to take up this matter with a view of constructing tables of analyses rang? for Important lines of foundry product. These analyses ranges however, are to be given as "recommendgd practice" and not intended for actual spkcification. In this way, the consumer of the foundry product will get the information he wants; the furnace-man will be gulded in the production of his pig irons to prepare for analyses ranges which are more closely standardized and have less of "freak" requirements made by Inexperienced metallurgists; and the foundryman will not be bound by chemical requirements he knows will not work out well with his particular reglonal supphes of melting stock. Doctor Moldenke's paper is published in full as it shows clearly the good results of the Institute's work in 1895 and a comparison of the same with the present knowledge of the metallurgy of cast iron—Bradley Stoughton, Chairman, Iron and Steel Committee. In MaRch, 1895, William R. Webster contributed a carefully prepared scheme for the study of the physics of cast iron to the American Institute of Mining Engineers at its Florida meeting. This summary of the interrelation of the chemical and physical characteristics of cast iron with the operations of daily foundry practice caused a wide discussion of the then little understood though universally used material. Mr. Webster has requested the author to bring the subject up to date and, while glad to comply, he must pay that with all the knowledge that has been gained in the quarter century that has passed since the subject was brought to the attention of the Institute—and we now are pretty familiar with cast iron in all its aspects—there is practically noth-

Jan 1, 1923

By R. D. Longyear

[Some Problems Involved in the Interpretation of Diamond-drill-hole Sampling and Surve ing (paper by J. J. Collins, Mining Tech., Jan. 1946). ............... I Geologic Interpretation of Magnetic Exploration on the Mesabi Range, Minnesota (paper by R. H. B. Jones, Mining Tech., July 1946) ................... 2] DISCUSSION R. D. LONGYEAR.*-Mr. Collins is to be commended very highly for the brief summary he has made of the currently used methods of taking diamond-drill sludge samples and the principles involved in evaluating the results. This paper should stimulate further discussion and research on this vitally important problem. It is particularly imperative that geologists and engineers know when assay results on sludge recovery can be accepted quantitatively and when they must be considered only qualitatively. In most cases where the sludge recovery is less than 95 per cent or more than 125 per cent, it is safest to consider the assays as of qualitative value only. Certain cases, however, are known where a relatively small proportion of the sludge sampling will give a reasonably accurate measure of the value of the total sample. One such case is ore in which the valuable mineral is of approximately the same specific gravity as the waste mineral, such as chalcopyrite in a massive pyrite body. The essential point is to determine the degree of accuracy of sludge sampling in any given drilling project and to weigh the results accordingly. It should be emphasized, however, that sludge sampling can be made reliable in many localities where careless practice produces unreliable results. In many instances, it is desirable to empty the core barrel in the core shack instead of at the drill, so that the engineer can examine the core as it first comes from the core barrel. It should be pointed out, however, that the drill * E. J. Longyear Co., Minneapolis, Minnesota. runner should be permitted to study the core to guide his future drilling. It is hoped that with the return of more normal conditions after the war geologists, engineers, contractors, and manufacturers will be able to carry on more research along the lines of improved core-barrel design and drilling technique with the objective of increasing core recovery so as to eliminate as far as possible the necessity of relying upon sludge samples. H. M. ROBERTS.*-Whoever in the future will have to do with the search for ore bodies and their exploration will have frequent occasion to refer to the clear and comprehensive summary on diamond-drilling methods by John Collins. His review of the experience of the last 40 years in this technique is invaluable. As Dr. L. D. Ricketts wrote in 1932, "The principles on which an art is founded are usually few and necessarily basic in nature, but he who wishes to achieve the power to select his aides and give success to important undertakings that may be intrusted to him in the future must ordinarily undergo years of drudgery in order to gain the experience that will enable him to distinguish such fundamentals through the haze of reinforcing detail that clothes and tends to disguise them."[t] Ricketts went on to say that since the beginning of the century there has been much

Jan 1, 1946

By J. C. Allen, E. V. Herring

CHILE EXPLORATION CO's. oxide plant at Chuquicamata, the largest of its kind, started in 1915 with initial operations at the rate of 10,000 tons of ore per day. Anaconda Copper Mining Co. acquired the controlling interest in 1923 and in the next few years modernized the plant and mine, extending operations to a nominal capacity of 490 million lb of electrolytic copper yearly by 1942. Plant production averaging 495.7 million lb of copper per year was maintained for the eight-year period extending from 1941 to 1948 inclusive. During the World War II production reached its highest level when in 1944 the output was 531.8 million lb. The maximum production for any one month was 49.6 million lb, achieved in May 1947. E. A. Cappelen Smith, consulting metallurgist for M. Guggenheim's Sons, worked out the first process for the treatment of Chuquicamata copper oxide ore about 1913, and directed a staff of 20 young engineers operating a pilot plant at Perth Amboy, N. J., on three shifts for an entire year. The copper is extracted from the oxide ore by a hydro-metallurgical treatment described in detail by T. A. Campbell in AIME Transactions, Vol. 106, Copper Metallurgy, 1933. The Oxide Plant is divided into five main operations as follows: (1) Crushing, (2) Leaching, including dechloridizing and sulphur dioxide treatment, (3) Tailing disposal, (4) Electrolytic precipitation, (5) Smelting and melting. Crushing The present Primary Crushing Plant has been in operation 25 years, during which time 4,342,112 cars of 70 tons net capacity have passed through the dumpers. The ore as received from the mine is frequently blocky and up to 5 feet in section. It is reduced to 9-in. size by two 60-in. gyratory crushers, and transported to the east and west ore bins by 60-in. conveyors. In the secondary crushing operation the ore is first reduced to 2 to 3-in. size by five standard 7-ft cone crushers and two No. 10 gyratories. This product is then reduced to 3/8-in. size by fifty-two 48-in. vertical Symons disc crushers and is transported by belt conveyors to the loading bridges from which it is charged° into the leaching vats. Conveyor belt No. 14 which serves the eight vats in the east section of the leaching plant has transported over 125 million tons of ore, which is a record for any type of conveyor. This 60-in. belt travels at a speed of 600 fpm and carries loads up to 5500 tons per hr. Leaching The ore is leached in 14 vats, averaging 13,500 short tons net capacity each. These vats are lined with a natural mastic which adequately resists the sulphuric acid leaching solutions. The leaching process as presently conducted comprises soaking the ore with successive volumes of leaching solution and spent electrolyte and withdrawing successive volumes of enriched solution from the vat to a total of approximately 3.2 million gal. The first 1.6 million gal of this volume withdrawn is called strong solution and contains about 35 parts of copper per 1000. The balance of 1.6 million gal subsequently withdrawn is stored in a

Jan 1, 1952

By J. P. Givry

The bath and the liquid metal in the aluw~inuw~ electrolytic cells are moving under the action of the Laplace forces. Consequently there are differences in level at the interface of the liquid. This phenomena is studied by means of a computer; the characteristics of the mathematical model used are presented with the results corresponding to two typical cases. This study gives a new and origi~zal interpretation of magnetic ej-jects; their action depends very closely on the hydraulic phenomenon which explain the sensibility of the cells to the slope and thickness of solid bath frozen around the pot. MAGNETIC effects produced in the electrolytic cells used for the production of aluminum are known to exist, a factor whose importance is well-known by producers through its influence on cell operation and output. In particular, these effects bring about movements in both the bath and metal as well as interface variations in level that are detrimental to sound electrolysis . A direct study of these effects by means of an experimental device would raise a number of problems particularly difficult not to say impossible to solve in the present state of techniques. It is for this reason that we had recourse to an electronic computer for working out the speed and pressure distribution within the liquid in the cells. We have assumed that all other possible causes for movement, such as thermal convection and evolution of gas at the anode, are acting without any connection with magnetic effects, and that consequently we may study each of these causes separately. A basic cause for magnetic effects lies in the presence of Laplace forces within the bath and metal. Electric current and magnetic field distribution have been calculated with the help of an electronic computer, and two communications about it have already been made to AIME.* 1) PRESENTATION OF THE MATHEMATICAL PATTERN In order to solve this problem, it was essential to assume a number of simplifying hypotheses with regard to both the geometry of the actual cells and the phenomena themselves. A first simplification consisted in assuming that the movements of the conducting liquid modify neither the electric currents nor the magnetic fields. In consideration of the magnitude of the values involved this assumption seemed accep-tible. 1.1) Finding the Equation of the Problem. The problem raised consisted in determining the flow of two viscous immiscible liquids with different densities subjected in a complex environment to gravity and Laplace forces. As a matter of fact, the sum of the external forces acting on the liquids is: F = JAB +pg where F = volume energy, B = magnetic field, J = current density, p = specific gravity, g = gravity. In the case of a laminar flow and assuming that the liquids are Newtonian and incompressible liquids, the equations governing movements are the following: 1) Navier Stokes' equation written in vectorial form: In fact one tries to find a steady-state solution, so aVx/at = 0; besides, one assumes that the movements are slow enough for quadratic terms such as Vy(a Vx/ay) (of round about the square of speed) to be neglected in front of the viscosity term: pAV, so

Jan 1, 1968

By N. Albon, J. F. Miller, R. W. Coutant

The deposition of nickel from nickel carbonyl onto amorphous substrates has been studied, with attention being paid to the specific effects of the physical and chemical nature of the substrate and to the effect of oxygen on the crystal morphology. With substrates having microscratches or etch lines, nu-cleation was observed to occur preferentially at these surface features. Flame polishing of the substrate surfaces was found to remove any regularity in preferred nucleation sites. Nucleation was observed to occur less readily on substrates having relatively low surface energies, e.g., Teflon and carbon, than on materials having relatively high surface energies such as fused silica. At low oxygen concentrations [Ni(CO)4/O2 > 54 x 1031, apparently pure and well-formed nickel crystals were observed to nucleate and grow irrespective of the presence of oxygen. At higher concentrations of oxygen, a secondary growth process, dependent upon oxygen concentration and resulting in a gradual change in crystal morphology, was observed. It is concluded that the influence of oxygen on the nucleation and growth of nickel is determined by the relative kinetics of the various possible reactions, and that under the experimental conditions employed the 0-Ni interaction occurs at some nucleation or prenuclea-tion stage. THE purpose of the research on crystal nucleation in chemical vapor deposition as described in this paper has been twofold: 1) to examine some effects arising from the use of amorphous substrates, and 2) to study the specific effects of oxygen on the nucleation and growth of nickel in a nickel carbonyl-carbon monoxide system. The nickel-nickel carbonyl system was chosen for study for several reasons: 1) nickel films are of potential interest in electronic technology, and 2) the deposition can be carried out at moderate temperatures, thus making possible detailed study of the processes occurring and the use of a variety of substrate materials (including some which melt at relatively low temperatures). Fairly well-characterized chemical kinetics and a broad background of information are available on the py-rolysis reactions and on the mechanisms of Ni-O interactions. NUCLEATION AND GROWTH THEORY The theoretical background for the analysis of nucleation and growth by vapor deposition for a one-component system (physical vapor deposition) and the problems encountered therein have been reviewed by Hirth and pound.' More recently Mande12 has indicated the difficulties of applying such theory to chemical systems. One of the major problems involved is the possible multiplicity of chemical reactions and deposition routes. For example, those reactions which are probably of significance in a discussion of the pyrolytic deposition of nickel from nickel carbonyl under the conditions of the present experimental work are illustrated in Fig. 1. As is true with most cases of chemical deposition, many of the quantitative data necessary for a complete analysis of the system are either not available or not directly measurable. However, with the present system, sufficient data are available for a discussion of nucleation and growth on a qualitative basis. Classically, the rate of nucleation of a monatomic species being deposited from a vapor phase is given by

Jan 1, 1965

By P. F. Gnirk, J. B. Cheatham

An experimental investigation has been made to study the effects of tooth angle and confining pressure on the force required for indentation of dry rock samples under confining pressure. In these experiments static single-tooth indentations were made on two standstones, a limestone, a schist and a slate under confining pressures of 5,000 to 15,000 psi. Sharp wedge-shaped teeth with included angles ranging from 30°to 105°were used. In all cases the force-displarenzent curves are approxinlately linear for rocks tested under confining pressure, as contrmted with the discontinuous curves obtained for silnilar rocks at atmospheric conditions. Photonzicrographs of thin sections through the craters indicate very little evidence of chip formation during indentation. In general the experimental data lie between calculated values for perfectly rough and perfectly smooth tooth-rock interfaces. INTRODUCTION The variables associated with ctrilling at depth are numerous and, in many instances, are not easity isolated and controlled. Also, many of these variables are interdependent; however, if the variables which are sufficiently independent of each other are held constant and are appropriately introduced, the dependent variables can be more easily studied and evaluated. It is the purpose of the present investigation to study experimentally the simplest case of bit tooth-rock interaction. In essence, the experiments have involved the static loading of sharp wedge-shaped tools on the surfaces of effectively semi-infinite dry rock samples subjected to confining pressures. During this investigation the following quantities have been maintained constant: 1. Pore pressure: atmospheric (i.e., the rock is dry). 2. permeability: although the rocks may be permeable, they are "jacketed" in such a manner that the fluid is not permitted to flow through them. 3. Temperature: 75F. 4. Rate of loading: essentially static (approximately 0.002 in./second). 5. Bit tooth: a sharp wedge-shaped tooth loaded normal to the rock surface. 6. Rock surface: smooth and flat. 7. Drilling fluid: hydraulic oil. In addition to the above conditions, the rock surface was free of a layer of cuttings. There was no indexing to previously indented surfaces, and the influence of corners of the borehole was neglected because the rock samples were effectively semi-infinite. The following quantities have been varied, and the resulting effects have been studied: 1. Rock a) Type (e.g., limestone, sandstone, etc.). b) Mechanical properties ) Necessarily dependent c) Porosity on type of rock. 2. Bit tooth (included angle of wedge-shaped tooth). 3. Depth of penetration. 4. cobfining pressure. On the basis of laboratory experiments which have shown that many rocks exhibit ductile behavior at confining pressures corresponding to depths usually reached during drilling,'.' a theory has previously been advanced which predicts the force required for penetration by a single sharp wedge tooth into a ductile* material.' The material is assumed to be isotropic, homogeneous and rigidly plastic (no elastic deformation) and to obey the Coubomb yield criterion (Figs. 1 and 2). Equations governing the force required for penelration are given for two extreme cases:** 1. A smooth, perfectly lubricated tooth-rock interface (fridionless boundary), in which the solution gives a minimum value for the penetrating force: in which F = force of the tooth, b = length of tooth edge,

By I. S. Servi, N. W. Marr

TIN markedly increases the softening temperature of pure copper with only a moderate effect on conductivity. Smart and smith' indicated a substantial increase in softening temperature upon addition of different levels of tin up to 0.05 pct in oxygen-free copper. However, after finding no effect of tin in copper containing about 0.025 pct O, they concluded that "the presence of oxygen completely nullifies these changes in properties by precipitation of SnO2.'' Since preliminary tests on Cu-Sn-0 alloys indicated that this conclusion is not valid outside the extremely limited tin range investigated by Smart and Smith, research was primarily directed toward the partition of tin between the copper-base matrix and the oxide phases. Experimental. Material was prepared by sealing an 80 to 100-g charge consisting of oxygen-free copper, tin, and copper oxide into a y-in.-ID quartz capsule which was evacuated and back-filled with tank-grade argon to 3 atm. The sealed vials were heated to 1125ºC, kept at temperature for 30 min, occasionally agitated, and then allowed to air-cool outside the furnace ("as-cast"). The castings were cold-swaged to 0.370 in., annealed 1 hr at 600°C ("as-annealed"), and cold-swaged 16.5 pct ("as-swaged"). Cross sectional wafers were annealed for 1 hr at various temperatures and Rockwell F hardness measured. The "softening temperature" was defined as the interpolated temperature at which the hardness was 50 Rockwell F. Electrical resistance was measured by an ac poten-tiometric method on 0.040-in.-diam wires after a 1 hr anneal at 600°C. Relative accuracy was of the order of 1 pct. Chemical analyses for tin were performed by two methods, identified as "Acid flux" and "HN03 dissolution". The first consisted of fusing the sample with potassium pyrosulfate and leaching the resulting melt with 10 pct sulfuric acid. The spectrophotometric procedure which followed is described in Ref. 2. Oxygen analyses were performed by the vacuum-fusion method with a bath temperature of 1650°C. Tin content of oxides and copper phases was measured with the X-ray microprobe, using a calibration curve based on a series of oxygen-free Cu-Sn alloys. Results. In Fig. 1, the nominal tin composition for alloys containing nominally 400 ppm O was plotted vs the analyzed or the computed tin content—the latter derived from one of the following: 1) "acid flux" chemical analysis; 2) "HN03 dissolution" chemical analysis; 3) X-ray microprobe analysis of the copper matrix; 4) equivalent tin content, based on the measured increase in electrical resistivity (an increase in resistivity of 1.6 microhm-cm is approximately equivalent to 1 wt pct of sn1,3). It is evident from Fig. 1 that the results of the acid flux analysis are consistent with the nominal composition while the HNO3 dissolution method generally yields lower values, consistent with those obtained from electrical resistivity measurements and somewhat higher than those obtained by microprobe analysis. Microprobe and resistivity values are affected only by the tin in solid solution; hence the HN03 method

Jan 1, 1970

By C. S. Brooks

Several of the commonly used methods for deter-mination of effective grain densities of minerals have been evaluated for accuracy and precision, and their applicability to various types of petroleum reservoir minerals tested. Consideration was given to the effect of consolidation, swelling clay, and wettability on these grain-density determinations. Procedures with helium displacement, a modified low-pressure Boyle's law porosimeter, and liquid displacement (water, n-decane, and n-octanol) were tested. The helium-displacement procedure was used primarily as an independent reference for which the effects of fluid-solid interaction, e.g., adsorption and wettability, were negligible. The procedures with the Boyle's law porosimeter and with liquid displacement are the methods in common use. Minerals investigated included calcite, West Texas limestone core samples, California sandstone core samples, and Wyoming bentonite. The number of samples tested, while not large, was adequate to permit application of statistical methods. Grain-density measurements on calcite (Iceland spar) provided a basis of comparison for the accuracy and precision of the procedures under investigation for a material with a high degree of chemical and physical homogeneity and for which fluid-solid interactions were at a minimum. Liquid-displacement procedures (water or n-decane) provided the greatest reliability and precision for measurement of the grain densities of the limestone tested. Gas-displacement procedures (helium or Boyle's law porosimeter) provided the greatest reliability and experimental convenience, if not the greatest precision, for the measurement of the grain densities of the swell- ing clay, Wyoming bentonite, and the shah sandstones which -contained appreciable amounts of swelling, in-terstitial clays. These experiments were designed to evaluate the applicability of the grain-density procedures in common we to some of the less tractable minerals—tight limestones, shaly sandstones, and swelling clays. The results should provide a useful basis for a selection of the method most suitable for application to the various petroleum reservoir minerals encountered and especially for use in the estimation of formation porosity. INTRODUCTION These experiments were undertaken to evaluate the accuracy and precision of several commonly used methods for determination of effective grain densities of minerals, and to test their applicability to various types of petroleum reservoir minerals. Consideration was also given to the effect of consolidation, clay, and wettability on these grain-density determinations. Procedures used included measurements with helium displacement, with a modified low-pressure Boyle's law porosimeter, and with liquid displacement (water, n-decane, and n-octanol). The minerals investigated included calcite, West Texas limestone core samples, California sandstone core samples, and Wyoming bentonite. The accurate determination of the porosity of petroleum reservoir formations, in particular those of low porosity, has received much attention. Both bulk-volume and grain-volume measurements necessary in the evaluation of porosity have been examined by many investigators with the objectives of improving both the accuracy and the precision of these determinations. In this investigation statistical criteria for selection of the most reliable and suitable procedure for use with a given type of mineral are demonstrated. The grain-volume measurement procedures appear to be the most susceptible to improvement.

Jan 1, 1958

By K. A. Johnson, F. H. Ellinger, C. C. Land

The Pu-In phase diagram has been determined by thevmal, filtvation, micrographic, and X-ray diffraction methods. This alloy system is characterized by 1) limited solubility of indium (-2 at. pet) in 6 and e plutonium, 2) one eutectic, and 3) fizte intermediate phases. Of the latter, PuIn and PuIn3 melt con-gruently, and Pu31n, Pu31n5, and the high-temperatuve 7 solid solution are formed peritectically. The n phase decomposes eutectoidally into Pu3In and PuIn at 865°C. Although the 6 phase can readily be retained to room temperature, it is not thermo-dynamically stable below 300°C. The Pu-In system has been investigated at Los Alamos as part of a study of the alloys of plutonium with the group 111-B elements. Constitutional studies of the Pu-A1 and Pu-Ga systems have been reported earlier.'9' To date, published information on the constitution of Pu-In alloys covers only the identification of the intermediate phases Pu3In and PuIn3.3,4 EXPERIMENTAL The alloys were prepared from five different lots of plutonium and three different lots of indium. The principal impurities in the plutonium differed from lot to lot within the following limits (in ppm): iron, 30 to 80; nickel, 30 to 60; aluminum, 15 to 30; silicon, 20 to 145: thorium, 50 to 300; carbon, 75 to 335; and oxygen, 20 to 135. Spectroanalysis of the indium showed that two of the lots were 99.9 wt pct pure, and the third was 99.98 wt pct pure. The alloys, in the form of about 5-g buttons, were prepared by arc melting in conventional equipment. The components for each alloy were weighed to the nearest 0.1 mg. In most instances the weight losses during melting were negligible; therefore confirmatory chemical analyses were usually not made. A few results are given in Table I. Density measurements of the arc-cast buttons were made by the liquid displacement of bromoben-zene. Heat treating was done in muffle furnaces controlled to +2°C. The alloy buttons were wrapped in tantalum foil before being enclosed in evacuated clear silica capsules. As a precaution against breakage, each capsule was in turn placed in a silica tube closed with a refractory wool plug prior to being charged into the furnace. For a moderately fast quench of the alloys, the outer protection tubes containing the capsules were plunged into cold water. Differential thermal analyses (DTA) in racuo were performed at heating and cooling rates of about 1.5°C per min. Tantalum crucibles having inverted thermocouple wells were used for most of the analyses. It was found micrographically, however, that the liquid alloys containing more than about 35 at. pct In reacted with the tantalum, resulting in contamination of the surface of the alloy. A search for a more satisfactory crucible material was not successful: tungsten and yttria behaved comparably to tantalum; thoria, vitrified magnesia, and vitrified alumina severely contaminated the alloys. So as to minimize the contamination by the crucible mater-

Jan 1, 1965

By C. D. Rubert, W. J. Parton

A flotation plant was placed in operation in 1945 at the Tamaqua colliery of the Lehigh Navigation Coal Co. Inc., to recover fine anthracite which is discharged from the cleaning plant with the washery water.‡ In addition to the recovery plant, facilities were provided for the complete clarification of the washery water, recirculation of this clarified water for breaker use, and disposal of the refuse solids in a waste impounding dam. Fig I shows a view of the settling tanks and the flotation plant. Flow Diagram The flow diagram for the complete recovery project is given in Fig 2. All the waste water from the cleaning plant is collected in a sump A outside the breaker structure, from which a 7000 gpm pump B delivers it through a 16 in. line to a 75-ft diam hydroseparator C. The hydroseparator, acting as a classifier, is set to give a separation at approximately 200-mesh. The minus 200-mesh overflow is discharged by gravity into the 180-ft thickener D for final settling of the solids. The classifier underflow sludge is pumped to the flotation plant by a 6-in. quadruplex diaphragm pump E. A 10-ft diam hydroseparator F is used to make a second classification on the sludge solids at approximately 28-mesh. The underflow from this classifier containing the coarse particles is elevated by a 6-in. diaphragm pump G and is discharged on two 4- by 6-ft vibrating screens II. These screens are dressed with approximately 28-mesh cloth. Screen oversize product flows directly to the centrifuge that dewaters the cleaned froth. The screen underflow and the overflow from the 10-ft classifier flow to the flotation circuit. The flotation feed is conditioned in a 12 by 12-ft agitator tank J at a pulp density of I:2.33 (30 pct solids). Reagents are fed to the circuit by reagent feeder I. The conditioned pulp is then diluted to a pulp density of approximately I: 5 (18 pct solids) and is fed to two banks of four 100-cu ft froth flotation cells K for primary coal recovery and cleaning. Additional reagents from reagent distributor L are added to the feed weir-box of Nos. 2, 3, and 4 cells of each bank of flotation machines. Clean coal removed from these cells flows directly to the clean-coal sump. Dilute tailings from the primary cells is re-thickened in a 30-ft diam thickener M and is then retreated in a scavenger circuit for final recovery of coal. The scavenger circuit consists of a 6- by 6-ft agitator tank N and two banks of four 24-cu ft froth flotation cells 0. Coal froth from these cells flows to the dewatering equipment and the tailings flows to a vertical refuse pump which delivers it to the 180-ft diam waste thickener D. Dewatering of the coal products is accomplished in a 54- by 72-in Bird centrifugal filter P. The cake product is dropped onto a conveyor and is loaded

Jan 1, 1949

By V. A. Phillips, M. Safdar Ali

The tensile properties of Cu-0.20 pct Al, Cu-0.45 pct Mg, Cu-0.27 pct Cr, and Cu-0.22 pct Be solid-solution alloys were studied at -196°, 18°, 2509 and 500°C on wires internally oxidized at 900°and 1000°C. Internal oxidation produced marked increases in yield strength relative to pure copper, particularly at low temperature. The yield strength decreased with increase in temperature to a much greater extent than predicted by current theories of dispersion hardening. The strengthening effect of internal oxidation persisted throughout the entire stress-strain curve, but since a marked loss of ductility occurred at all test temperatures, only modest increases in tensile strength were realized. INTERNAL oxidation involves the preferential oxidation of a baser solute in a relatively noble solvent by diffusion of oxygen into the solid. Since the process is diffusion controlled, it is expedient to carry it out at a high temperature often approaching the melting point. The amount of solute is limited and the oxidation conditions adjusted so that oxygen diffuses inwards to meet the solute causing reaction to progress inwards and form subscale instead of only sur face scale. The reaction can be made to occur throughout the thickness of thin material producing a fine dispersion of oxide inside the metal. C. S. Smith1"3 appears to have been the first to recognize the true nature of the process of internal oxidation. Although extensive kinetic and metal-lographic studies followed by Rhines and coworkers,4-5 Chaston7 andMeijering and Druyvesteyn8 working independently were the first to report hardening effects due to internal oxidation. These results prompted detailed studies of the effects of internal oxidation on the hardness, tensile, creep, and fatigue properties of a number of alloys by G. C. Smith and coworkers9-12 in England, on hardness by Gottardi13 in Italy, and on hardness and tensile properties by wood14 in the U.S.A. Publications dealing with other aspects of internal oxidation will not be reviewed here. Internal oxidation of solutes having a high affinity for oxygen provides a means of obtaining very fine dispersions stable in a suitable atmosphere at temperatures well above those at which most age harden ing precipitates coalesce. The process therefore offers a method of producing thin sheet and wire of possibly outstanding creep resistance. The size limitation might be overcome by internally oxidizing porous powder compacts made from alloy powder before final sintering. PREPARATION OF ALLOYS The alloy ingots, which were approximately 5 1/2 in. long by 1 in. diam, were made up in a high-frequency furnace, using as raw materials OFHC copper, 99.99 + pct Al, high-purity magnesium, and master alloys of Cu-4.19 pct Be and Cu-10 pct Cr. The alloys containing aluminum and magnesium were melted ii closed high-purity graphite crucibles and solidified in the crucible which was lowered partly Out of the coil to give a hot-top effect. The alloys containing beryllium and chromium were made by melting in vacuo in alumina-lined sillimanite crucibles. The magnesium, chromium, and beryllium

Jan 1, 1960

By Charles A. Stickels, Edward E. Hucke

The dihedral angle, formed by the intersection of three interfaces, is often determined by measuring a sample of apparent angles of intersection seen on a random plane of polish, then comparing the exerimental distribution of angles to the distribution calculated by Harker and Parker. Statistical tests show that the latter distribution does not satisfactorily describe the population from which samples are drawn. It is concluded that the major reason for this discrepancy is the presence of a range of dihedral angles in all specimens. When reasonable care is used experimentally, random measuring error is unimportant. It is shown that measurements made on dispersed second-phase inclusions are subject to a systematic error depending on inclusion size, which can be minimized by using adequate magnification. A dihedral angle, calculated from a sample of observed angles as though a unique dihedral angle were present, is termed an "effective dihedral angle". Experience has shown that "effective dihedral angles'' are reproducible quantities, useful for characterizing samples. Methods of determining an "effective dihedral angle", establishing its reliability, and making comparisons between samples are discussed. THE authors have recently reported measurements of the dihedral angle formed by liquid-lead inclusions lying in nickel grain boundaries.' Di- hedral angles were measured by the statistical method first employed by Harker and parker2 and used subsequently by many other workers.3"8 Since a relatively high degree of accuracy was necessary in the authors' experiments, the reliability of this method of dihedral-angle measurement was examined. Briefly, this method of measuring dihedral angles is usually performed as follows. A multiphase alloy is prepared, equilibrated under conditions which allow sufficient interface mobility to establish equilibrium, quenched to room temperature, then prepared for metallographic examination. A large number of observed angles, formed by the traces of grain boundaries and/or interphase boundaries on the plane of polish, are measured at high magnification. If all orientations of interfaces in the specimen are equally probable, Harker and parker2 showed that the population of observed angles is described by a distribution function containing a single parameter, the dihedral angle, 8. certain properties of the population, e.g., the mode or median, have been calculated from this distribution function in terms of the dihedral angle.3, 9 Thus, if the mode or median of a sample is identified with the corresponding property of the population, a unique value for the dihedral angle is determined. One defect in this procedure lies in identifying the properties of a sample of observed angles with the properties of the population from which they are drawn. If one were to proceed in a more rigorous fashion, it would be necessary to find a function of sample properties which is an estimator of the dihedral angle. Then by determining the distribution function for the estimator one could set limits on the value of the dihedral angle. The most apparent obstacle to this straightforward approach is the complexity of the distribution function assumed to describe the population. In analytical form, the distribution function may be written:2, 10

Jan 1, 1964

By A. H. Daane, W. J. Wunderlin, B. J. Beaudry

The solid solubility of holmium in copper, silver, and gold, determined using metallographic techniques, was found to be a maximum of 0.06, 2.4, and 3.2 wt pct, respectively, nt the eutectic temperatures. The temperatures of these eutectic horizontals, determined by differential thermal analysis, were found to be 868", 787", and 778"C, respectively. The first compound on the silver-rich side of the Ag-Ho system was found to be A&Ho2. In a study by Gold et al.,' on the effect of small amounts of soluble impurities on the electrical resistance and thermoelectrical properties of copper, traces of iron were shown to have drastic effects on the thermoelectric power due to the magnetic scattering of the conduction electrons. Since little is known about the state of the iron ion when dissolved in copper, Gold had hoped to repeat these experiments using certain rare earths as the magnetic scattering centers; because of the tightly bound 4f electrons it is not expected that their spectroscopic state would be affected by alloying. In such an experiment the sole role of the trace rare-earth impurity would be to magnetically scatter the copper conduction electrons without producing appreciable distortions in the otherwise pure copper matrix. Since holmium was chosen for such a study because of its high magnetic moment, it was necessary to establish precisely its solid solubility in copper. The study was extended to include the solvents silver and gold, so that an evaluation of the data using classical solubility parameters could be made. No previously reported work on the systems of holmium with copper, silver, or gold was found in the literature. Information on the solubility of other rare earths in these three metals is also very meager. The solubility limit of yttrium in copper was reported as less than 1 wt pct2 and the solubility of praseodymium in gold as 0.35 wt pct,3 while no references were found on solubility studies of rare earths in silver. EXPERIMENTAL Materials. The materials used in this investigation were distilled holmium prepared in this Laboratory, OFHC* copper, electrorefined silver (99.9 *OFHC = oxygen-free high conductivity. pct), and gold with the analyses given in Table I. Sample Preparation. Samples weighing 1 to 2 g were prepared by arc-melting the components together on a water-cooled copper plate under purified argon atmosphere. The samples, turned and remelted at least five times to ensure homogeneity, showed weight changes of less than 0.1 wt pct after melting. Samples containing less than 0.7 wt pct Ho were prepared by diluting 1 to 2 wt pct Ho alloys with the pure solvent, while samples with concentrations greater than 0.7 wt pct Ho were prepared directly from the metals. The samples were wrapped in tantalum foil, sealed in outgassed Vycor tubing under helium, annealed at the desired temperature for at least 24 hr, and then quenched by shattering the Vycor tube in cold water. Metallographic Methods. Standard mechanical polishing methods were used in preparing the silver and gold alloys for examination, while the copper alloys were electropolished using a 40 pct solution

Jan 1, 1963

By Nicholas J. Grant, David S. Bloom

An investigation of the Cr-Ni system has revealed that there exists a eutectoid transformation at about 1180°C. 'The transformation in chromium implied by the eutectoid reaction was detected at about 100°C below its melting point. Associated with the eutectoid transformation, a metastable transition structure has been found. THE Cr-Ni phase diagram is shown in current literature to be a simple eutectic system in which the high chromium end of the diagram is incompletely determined, Fig. 1. The last investigation of this system was undertaken in 1936.' Because of limitations in metal purity, especially of chromium, and temperature measuring techniques, the diagram should be accepted with some reservations, as was indicated by Hansen.V or examwle.-, the wresence of the compound Cr²Ni, with a tetragonal structure," remains unverified and incompatible with the simple eutectic diagram. The work reported here began because of discrepancies that appeared in experimental studies in the binary alloys Cr-Ni and in the ternary system Cr-Mo-Ni. The existing binary Cr-Ni diagram failed to provide a complete explanation of observations made by microscope, X-ray, and thermal analyses. Experimental Methods The materials employed were of a higher degree of purity than were available to previous investigators. The Mond nickel used had a nominal purity of 99.87 pct, while the electrolytic chromium analyzed 99.03 pct with the major impurity being 0.5 to 0.7 pct oxygen with some iron. All alloys were melted in a vacuum furnace to remove dissolved gases, sufficient carbon was added to the charge to combine with all the oxygen as CO. Final analysis determined the carbon as about 0.02 pct and the oxygen around 0.06 pct or slightly more. Stabilized zirconia crucibles and thermocouple protection tips were used throughout and contributed no detectable impurity to the melts, as long as the oxygen in the chromium was kept low. Heats averaged about 250 g, which permitted about 2 in. of the thermocouple protection tips to be submerged. The temperature drop across the thermocouple protection tip was determined to be about 3°C, a minor source of error. The alloys, after removal from the vacuum furnace, were placed in a furnace operating in a purified argon atmosphere for the thermal analyses. An- nealed wolfram-molybdenum thermocouples provided the primary means of temperature determination, though a Pt-Pt-10 pct Rh couple was employed for a check when possible. A sensitive, high-speed Leeds and Northrup Speedomax recording potentiometer indicated the thermocouple output. X-ray diffraction patterns were obtained primarily on a Norelco unit, which permitted diffraction angles only up to 45" (28 = 90"). In general, either rotated or stationary solid samples were used, because it later evolved that many samples were susceptible to transformation resulting from the cold working involved in pulverizing. It was also noted that rotating a sample sometimes suppressed weak lines, so, usually, samples were not rotated. Later a high temperature camera was adapted for use at temperatures up to 1400 °C on the Norelco unit utilizing both solid and powdered samples. Unless otherwise noted, all X-ray patterns were made with a chromium tube and a vanadium filter. Further-

Jan 1, 1952

By F. E. Rizzo, L. R. Bidwell, D. F. Frank

THE poor high-temperature oxidation resistance of the refractory metals becomes an important problem as higher operating temperatures are sought. A meaningful analysis of their oxidation behavior requires a knowledge of the phases that can appear during oxidation as well as their relative stability. Although several extensive investigations have been carried out to obtain this information for the W-0 system,1-10 serious inconsistencies still remain. First, the standard free energies of formation (AG°) determined in recent studies which used the solid electrolyte galvanic cell technique6,7,9 differ significantly from those obtained primarily from gas equilibration measurements.1,3,4,10 The disagreement is especially large for the highest oxides. These data have been used to predict the decomposition temperatures of WO2. 72 and WO2.90.1 A considerable extrapolation is required, resulting in a large uncertainty in the decomposition temperatures. Second, Bousquet and perachon3 have presented convincing evidence, ob- tained by gas equilibration measurements, in support of the long-contested existence of W30. Phillips and chang,ll on the other hand, were not able to observe this phase under similar experimental conditions. The purposes of this work, which is part of a continuing investigation of the W-Mo system, were to resolve the discrepancies between the AGO measured by gas equilibration and solid electrolyte galvanic cell techniques, to extend the latter measurements to lower temperatures, to redetermine the WO2.72 and WO2.90 decomposition temperatures, and to apply the more sensitive electromotive-force method to the question of the existence of W3O. I) EXPERIMENTAL PROCEDURE The measurement of ?G° of reaction by the use of calcia-stabilized zirconia solid electrolyte galvanic cells has been described previously.12 The method is based on the measurement of the difference in chemical potential of oxygen between an electrode containing the two oxides of interest and a reference electrode of known oxygen activity. Two different types of cell holders were used in this study. The first type of apparatus has been described earlier." It consisted of two solid electrodes separated by a disc of electrolyte. Both electrodes were exposed to the same stream of purified helium. With this design a gaseous transport of oxygen between the two electrodes is possible. The second type of apparatus, which has also been described earlier,14 effectively separated the two electrode atmospheres. It utilized a closed-end impervious, calcia-stabilized zirconia tube that was open to the atmosphere. The tube served as an electrolyte for the cell and provided a means for separating the anode compartment, which was held under a static vacuum, from an air reference cathode. The cells and reactions of interest are described in Table I. High-purity tungsten metal was obtained from the Fansteel Metallurgical Corp. and the Allied Chemical Corp. Table II contains an analysis of each material. WO3 was prepared by oxidizing the metal in air at approximately 600°C in high-purity recrystallized alumina boats and by the dehydration of reagent-grade tungstic acid in alundum boats. The two methods of preparing WO3 resulted in slightly different purities.

Jan 1, 1968

By H. Kosmider, P. Coheur

New processes of blowing with an oxygen-enriched air or gas mixtures of oxygen and steam allow the steelmaker to produce, in a basic converter, a rimmed steel low in nitrogen (0.0020 pct), phosphorous (0.020 pct), and sulphur (0.020 pct). The physical properties (ductility) of the new steels are excellent. Furthermore, from the point of view of economy, these new methods of blowing offer outstanding possibilities. THE natural occurrence of geological deposits of iron ore and local economic circumstances led European blast furnace men to work large quantities of lean iron ore with a phosphorus content as high as 0.5 pct. The iron obtained from these ores generally contains 1.5 to 2.1 pct phosphorus, 3.6 to 3.9 pct carbon, 0.3 to 0.6 pct silicon, 0.04 to 0.08 pct sulphur, and 0.3 to 1.2 pct manganese. To produce steel from this pig iron, the steelmaker has at his disposal several processes. One of the simplest and most economical is the pneumatic process developed by S. G. Thomas in 1879. This process of steelmaking, called the Thomas process, consists of blowing through the bottom of a basic bessemer converter and is used widely in Western Europe, as shown in Table I. Due to the development of tonnage oxygen plants, this process has become more important because the use of oxygen offers new possibilities of steel manufacture. Not only may the quality of the steel be improved, but liquid pig iron also may be used, the composition of which does not meet the heat requirements of the blow with atmospheric air. It is not intended to present here a detailed scientific discussion of the basic bessemer process but rather to discuss briefly its industrial possibilities in the case of rimmed steel and when blowing with atmospheric air, oxygen-enriched air, or gas mixtures of oxygen and steam. This paper is based on the current practice at Klockner-Hüttenwerk Haspe's steel division, and at six Belgian and Luxemburg steel works. The latter are members of the Liege section of the C.N.R.M. (National Institute for Metallurgical Research) and are: ARBED, John Cocker-ill, Esperance-Longdoz, HADIR, Miniere et Metal-lurgique de Rodange, and Ougree-Marihaye, most of which are working with tonnage oxygen plants.' In order to avoid any misunderstanding, it should be noted that most of the techniques to be men- tioned, or similar ones, are used currently at many steel plants in Western Europe. Background The basic converters used in Europe have a capacity of 17 to 65 tons of steel, and are similar in shape to the one in Fig. 1. The lining is brick or rammed dolomite and has a life of 250 to 500 blows. The bottom is rammed dolomite and has a life of 40 to 80 blows. As far as we know, the type of blast used does not appear to have any influence on the life of the lining. Bottom life, on the contrary, depends very much upon the composition of the blast. It is only when

Jan 1, 1955