Search Documents

By K. Tangri, B. Swaroop

Simultaneous measurements of lattice (elastic) strain by X-ray line shift method and total strain with an electrical strain gage have been carried out on polycrystalli,ne nickel with the help of a specially designed tensometer attachment for the X-ray dif-fractometer. During the initial stages of deformation, the rate of increase in lattice strain closely follows the total strain until the plastic strain sets in. From then onwards, the two strains deviate from each other and with further increase in afiplied stress the rate of increase of lattice strain eventually decreases. Depending upon the mode of unloading, both compressive and tensile strains have been observed in nickel deformed up to 0.29 pct strain. These results have been explained on the basis of the effects of clustering of dislocations and also the production and behavior of point defects during loading and unloading, respectively. POLYCRYSTALS deformed plastically in a uniaxial tension test show residual lattice strains (hereafter referred to as RLS), which broaden the X-ray line profiles and shift their peak positions.''4 It is known that uniform straining of a crystal lattice (macrostrain) produced movement of ddfraction line peaks, whereas nonuniform straining (microstrain) causes line broadening.= Though the nature and origin of RLS in deformed metals is not yet clearly understood, these are believed to be due to the presence of some form of a locked-up stress system. Several possible detailed interpretations6'" of the stress system have been proposed by various workers and common to all these interpretations is the assumption that different parts of the aggregate have different tensile yield stresses; e.g., that a part A yields under a lower applied stress than a part B. Therefore, during the deformation process, the elastic strain in A will be less than that in B, and, after completion of deformation, B will tend to contract further than A but will be prevented from doing so by the restraining influence of A. Thus, when equilibrium is reached, A will be in compression while B is in tension. Although there is general agreement on the correctness of this argument, controversy still exists as to the exact nature of the parts A and B in a deformed metal. In an alternative approach to the creation of parts A and B, many other investigators have assumed that the RLS observed in unloaded specimens are in some way connected with the lack of proportionality between lattice strain and applied stress in the region above the yield stress." cullity13 has prepared a schematic summary of the results of previous workers, mainly Smith and Wood,2'11 which suggests that, above the elastic limit, the lattice strain may increase less rapidly with respect to strain, or may even decrease with increase in applied stress. If the applied stress is then decreased, the lattice strain would decrease along a line parallel to the loading line in the elastic region and thus produce a compressive residual lattice strain after unloading. At equilibrium, to balance these compressive stresses? there would have to be regions under tensile stress which may well be the grain boundaries or the substructure walls formed during deformation. The present investigation was undertaken to gain a better understanding of the nature and origin of RLS and also to experimentally verify the salient features of this hypothesis. EXPERIMENTAL Stress and strain determinations were made with a specially constructed tensometer attachment for the X-ray diffractometer, Fig. 1: which permits the following measurements simultaneously on a sheet specimen under uniaxial tension at various stress levels during loading and unloading: a) lattice strains, E=. in a direction perpendicular to the direction of pulling (x direction) from shifts in X-ray line peak positions; b) the total strain, ex, in the direction of pulling. with the help of an electrical strain gage affixed to the back of the specimen directly below the area irradiated by X-rays: and c) the applied stress, with the help of a load cell which consisted of a calibrated stainless-steel sample of dimensions identical to those of the specimen under investigation, and to which it was coupled. Because of its high stacking fault energy.I4 nickel

Jan 1, 1970

By A. E. Dwight

Lattice parameters were determined for eighteen equiatornic alloys of the CsCl-type structure, ten of which were previously un-reported. It was found that fomation of the CsCl-type structure in binary alloys of the transition elements is largely dependent on position of the elements in the periodic table. The relative size of the two elements was not found to be a controlling factor. A recent paper by Beck, Darby, and Arora1 corre-lates the occurrence of CsC1-type ordered structures with the position of the constituent elements in the periodic table for the first long period. It was also suggested that a definite increase in relative bond strength between unlike atoms occurred when, in binary alloys of iron-group elements, the other component is changed from a chromium-group element, to a vanadium-group element, to titanium. A later paper by Philip and Beck2 noted that the lattice contraction increased in the order CrFe, VFe, and TiFe. It was also noted by Philip and Beck2 that the lattice contractions of CsC1-type alloys decreased in the order: TiFe, TiCo, and TiNi, which is an apparent reversal of the contractions expected from the position in the periodic table. It was suggested that the increasing lattice contraction is an indication of increased stability, i.e., greater A-Bbond strength. The present investigation was carried out to determine whether the relation of the position in the periodic table to the formation of the CsC1-type structure was also correct for alloys involving the second and third long-period elements. A systematic search was made for CsC1-type structures among equiatomic alloys and for those found, the lattice contraction was determined. EXPERIMENTAL TECHNIQUE The elements Y, Gd, Ti, Zr, Hf, V, and Cb are designated the A group and the elements Mn, Re, Fe, Ru, Os, Co, Rh, Ir, Ni, Pd, Pt, Cu, Ag, and Au are designated the B group. Equiatomic alloys were prepared for 57 AB combinations. The alloys were arc melted in a multicrucible furnace3 in buttons ranging from 5 to 20 g. Chemical analyses were not made, as the charge weights agreed closely with those of the buttons after melting. The alloy buttons were homogenized at 800° to 900°C. Metal log raphic and X-ray specimens were prepared and heat treated at temperatures from 600° to 1200°C. Specimens for X-ray diffraction were usually ground to a powder in an agate mortar; however, needle-shaped solid specimens were used when the alloy was sufficiently ductile to permit their preparation. Diffraction patterns were taken with a Straumanistype Debye-Scherrer camera using filtered Cu or Co radiation. The lattice parameters were obtained in A by plotting the calculated a0 values against the cos29/sin 0 + cos2?/? function and extrapolating linearly to ?= 900. Metallographic control specimens were polished on cloth wheels with diamond paste and etched with various phosphoric and nitric acid reagents. RESULTS The eighteen equiatomic alloys listed in Table I gave evidence of a cubic structure with two atoms in the unit cell, although two of these cubic structures exist only at elevated temperatures and transform to a tetragonal structure on quenching. Nine of these eighteen alloys gave diffraction patterns with super-lattice lines showing that the structure is of the CsC1-type. The lack of superlattice lines in patterns of the other nine alloys may be attributed to the small difference in atomic scattering power of the components. Metallographic study indicates the occurrence of nine narrow single-phase fields at the AB composition. Any or all of these nine may also have a CsC1-type structure. The VFe alloy was found to have a CsCl-type structure by Philip and Beck2 through the use of CrKa radiation (for which the scattering factor of V is anomalously low), whereas the Cu radiation used

Jan 1, 1960

By L. L. Handy

The development of a theory for miscible liquid displacement requires evaluation of the variables which affect growth of the mixing zone between solvent and displaced oil. Factors which appear to be important are individual fluid viscosities, viscosity ratios, flood rate, fluid densities, flow characteristics of the porous medium and molecular diffusion coefficients of the fluid components. The primary purpose of this paper is to evaluate diffusion effects. Theoretical treatments to date have been limited to floods for which the viscosity ratio is one. Two principal theories have been proposed. Von Rosenberg adapted for porous media a theory derived for capillary tubes by G. Taylor.' ,' In this theory molecular diffusion perpendicular to the direction of flow is a primary factor in sharpening the flood front. Slow floods give sharper fronts for a given distance traveled than fast floods. An alternative theory considers miscible liquid displacement as a statistical problem.3,4,5 Diffusion is not an important factor in this theory, but it leads to the same general type of equation as von Rosenberg's. Both theories predict S-shaped concentration profiles with the same dependence on distance traveled. The statistical or "dispersion" theory predicts rate independence, however. To supplement rate studies a direct measurement of a diffusion effect would be helpful in evaluating which of the two proposed mechanisms best describes miscible liquid displacement for one-to-one viscosity ratio systems. No quantitative theory has been proposed for floods in which a low-viscosity fluid displaces a high-viscosity fluid. It might be anticipated, however, that the extensive fingering observed in floods with adverse viscosity ratios would increase opportunities for an exchange of components between displaced and displacing liquids by a diffusional process. Even if molecular diffusion were not an important mixing mechanism for one-to-one viscosity ratio systems, it could be significant in systems with adverse viscosity ratios. METHOD FOR EVALUATING DIFFUSIONAL MIXING In solvent flooding the displacing liquid can become mixed with the displaced liquid by a number of processes; in general, either mechanical or diffusional in character. To evaluate the contribution of diffusion, a method was sought that would distinguish diffusional mixing from mechanical mixing. Suppose two soluble tracers are added to the displacing liquid and that one tracer has a diffusion coefficient much greater than the other. Then, if diffusion is important during miscible liquid displacement and if diffusional transport is primarily transverse to the direction of flow, substances with high diffusion coefficients will have sharper concentration profiles than those with comparatively low molecular diffusion coefficients. In order to have material balance the profiles for the two tracers must intersect. For one-to-one viscosity ratios the intersection would occur at the 50 per cent concentration point. It is generally assumed that diffusion in the direction of flow is negligible. This assumption appears reasonable because flow velocities are ordinarily orders of magnitude greater than diffusional velocities. If this is not a valid assumption, however, the shapes of the fronts will be further degraded by longitudinal diffusion. The effects of rate and molecular diffusion coefficients are the opposite for longitudinal diffusion to those for lateral diffusion. Higher rates or lower diffusion coefficients would tend to give sharper fronts. The double tracer method offers several unique advantages in evaluating effect of molecular diffusion. First, the method gives a direct measure of the effect of diffusion on mixing zone size. Second, the effect of a difference in diffusion coefficients is determined from a single experiment. Comparison of several experiments at different rates is not required. Third, the method is applicable for any viscosity ratio. Fourth, the method is unaffected by density differences between the two fluids which might result in rate dependent gravity effects. EXPERIMENTAL PROCEDURE Suitable tracers are substances whose diffusion coefficients differ as widely as possible, but whose adsorptions on rock surfaces is negligible. The two tracers selected were methanol and sucrose in water solutions. The approximate diffusion coefficients for methanol and sucrose, as given in the International Critical Tables, are 1.3 X 10-5 and 0.3 X 10-5 m2/sec, respectively. Concentrations in the water solutions were 200 gm/liter of solution for both methanol and sucrose. These high

By Paul A. Farrar, Sanford Adler

The Tz-Zr system was reinvestigated using both metallographic and X-ray diffraction techniques. It mas found that titanium and zirconium are soluble in all proportions in both the a and 0 phases. The minimum in the transformation was found at 50 at. pct and 535°C. THE Ti-Zr system has previously been the subject of several investigations.1-6 A study by Hayes et al.5 using magnesium-reduced titanium and zirconium melted in graphite crucibles indicated that the system was a continuous series of solid solutions in both a and 0 phases with a minimum at approximately 545°C and 65 pct* Zr. These conclusions were substantiated by the work of Duwez4 as well as by the limited data of Craighead et al.,3 Fast,2 and deBoer.1 However, a more recent investigation of the titanium-rich region by Ence and Margolin6 indicated that the solubility of zirconium in a, titanium at 500°C is approximately 22 pct with the a + 0 field extending to approximately 47 pct Zr. Therefore in order to resolve this discrepancy the following investigation was initiated. EXPERIMENTAL PROCEDURES The alloys used in this investigation were prepared as 20- to 30-g buttons by nonconsumable electrode melting in a helium atmosphere. The starting materials were Bureau of Mines titanium BHN 71 and Foot Mineral iodide crystal bar zirconium. The titanium was premelted before the alloys were prepared to avoid excessive weight losses in the final melting. The compositions of the alloys prepared were as follows: Ti-12.0, 22.2, 29.0, 39.6, 50.0, 58.0, 72.4, 83.5. and 90.8 pct Zr. Prior to heat treatment the alloys were cold-worked 10 to 20 pct, stopping at the first signs of cracking. Specimens for heat treatment were wrapped in molybdenum sheet and annealed in argon-filled quartz capsules for the following times and temperatures: 750°C-40 days, 675°C-61 days, 600°C—109 days, 575°C-112 days, 550°C-112 days, 525°C—127 days, and 450°C —153 days. Quenching was accomplished by breaking the capsules in an iced-brine solution. The standard techniques used for polishing the specimens involved belt grinding, grinding on emery paper, polishing electrolytically, and etching with Remington "A" etch7 or "R" etch 8 Debye-Scherrer X-ray powder photograms were obtained for a number of samples using a 114.6-mm camera and CuK, radiation. Exposure times were from 19 to 23 hr. The powder samples were obtained by filing to 270 mesh size. After filing the samples were wrapped in molybdenum foil capsuled in quartz and reannealed at the temperature of original heat treatments; following the heat treatment the samples were quenched into iced brine without breaking the capsules. RESULTS AND CONCLUSIONS On the basis of the microstructural examinations of the heat-treated samples and of the X-ray diffraction data, the Ti-Zr system shown in Fig. 1 was constructed. The data indicate that a, and 0 titanium form a complete series of solid solutions with a, and ß zirconium. The minimum was found to occur at 65 pct (50 at. pct) Zr and 535°C, in excellent agreement with the earlier investigations,1-5 see Fig. 2. Typical microstructures are shown in Figs. 3 to 7. Figs. 3, 4, and 5 show the 22.2, 39.6, and 50.0 pct Zr alloys after heat treatment at 675°C for 61 days with the 22.2 pct Zr showing equiaxed a, and the 39.6 pct Zr alloy a + transformed ß, while the 50 pct Zr alloy shows only transformed B. Figs. 6 and 7 show the 29.0 and 39.6 pct Zr alloys after heat treatment for 109 days at 600°C. The 29 pct Zr alloy has an equiaxed a structure while the 39.6 pct alloy has a partially recrystallized a+ß structure. X-ray diffraction data obtained from the 50 pct Zr alloys after heat treatment at 525° and 450°C as well as from the as-cold-rolled material showed only those lineos which couid be indexed a: a titanium, good agreement with the previously published values. 2,4,5,9 Chemical analysis* of the 50 pct Zr alloy

Jan 1, 1967

By E. M. Kalar, I. Iwasaki, J. D. Zetterstrom

Several methods of removing fatty acid coatings from iron ore flotation concentrates were tested both on a Mesabi oxidized iron ore and on a magnetic taconite concentrate, and their effects on the duplex flotation process and on pelletizing were compared. Either acid or alkali alone could not remove the coatings, but a combination of such reagents as lime and quebracho, calcium chloride and pyrophosphate, or sulfuric acid and an organic acid (oxalic, malonic, or citric acid) was quite effective. The use of activated carbon was found to be particularly promising. The removal of fatty acid coatings from iron ores is of much practical interest when a pelletizing process is being considered for a concentrate floated with a fatty acid collector or when a duplex flotation process is being considered for upgrading an oxidized iron ore. A duplex flotation process is a fatty acid flotation of iron minerals followed by an amine flotation of the siliceous gangue from the rougher iron concentrate. Such a process is being used in the Florida phosphate fields.' Although in northern Michigan mills fatty acid flotation concentrates have been pelletized successfully, at other locations fatty acid coatings on iron flotation concentrates have proved so undesirable in the agglomeration operation that other methods of concentration had to be sought.' Since fatty acid coatings cannot be removed as readily with a simple acid or alkali treatment from iron oxide surfaces as from Florida phosphates, a combination of reagents, such as lime and quebracho,3 lime and alkali phosphate,4 or sulfuric acid and oxalic acid,' has been proposed. It was also thought that activated carbon might be effective in removing fatty acid coatings due to its high adsorptive capacity. Activated carbon, with its enormous surface per unit of volume, is well known for its exceptional efficiency in removing organic pollutants from industrial effluents. This article presents the practical aspects of the above methods when they are applied to the duplex flotation process and to the pelletizing of iron flotation concentrates. The article also includes a preliminary investigation of the common parameters involved in the depressant activity of the reagents. EXPERIMENTAL WORK Initially, the experimental work was directed towards the optimization of each method for the removal of hydrophobic coatings from iron oxide surfaces floated with fatty acids. Subsequently, the methods thus optimized were tested in the duplex flotation process with an oxidized iron ore and in the pelletizing process with a magnetic taconite concentrate. Preliminary Flotation Tests: Although the three types of chemical treatment reported in the literature were briefly investigated for the purpose of comparison, major emphasis was placed during the preliminary flotation tests on the use of activated carbon because it was thought to have certain advantages over the chemical methods. LIME AND QUEBRACHO - To obtain a flotation concentrate for optimizing the lime and quebracho method of fatty acid removal, the magnetic taconite concentrate was used. The concentrate had a size consist of 90% passing 325 mesh and analyzed 64.5% iron. After a few preliminary tests the fatty acid flotation procedure with the magnetic taconite concentrate was standardized as follows. A 1200-g sample of the magnetic concentrate was pulped in a Fagergren laboratoy flotation cell to 40% solids, conditioned with 0.5 lb of soda ash per ton for 2 min, and then further conditioned with 1.0 lb of Acintol FA-2 per ton for 2 min. After 5 min of flotation, recovery was nearly complete, averaging 98.6% of the weight and 98.7% of the iron. The cell product, which amounted to 1.4% by weight and analyzed 63.2% iron, consisted mainly of relatively coarse middling particles. Since the repro-ducibility of the flotation concentrates produced by this procedure was vey high, the same procedure was used to prepare fatty acid concentrates for each of the six tests of the lime and quebracho method. To test the removal of the fatty acid from the magnetite surfaces by the lime and quebracho method, a fatty acid froth product was returned to the flotation cell, repulped by 30 sec of agitation, and then con-

Jan 1, 1968

By Brahm Prakash, R. Schuhmann

Chemical conditions for flotation and nonflotation of quartz with oleic acid as collector and barium, calcium, aluminum, iron, and tin as activators were studied using a simple vacuum-flotation technique in glass-stoppered graduates. The detailed study of barium activation led to an interpretation based on ideal Langmuirian chemi-sorption. FLOTATION of quartz is of practical importance as something to be avoided in soap-floating many types of ores. Clean, unactivated quartz is not floated with fatty acids and soaps, such as oleic acid and sodium oleate, in the quantities normally used for flotation. However, data in the literature indicate that almost any multivalent cation will activate quartz if given an opportunity. Thus, a common problem is to prevent activation of quartz by the various inorganic cations inevitably present in flotation pulps. Wark and his coworkers1 have demonstrated the reversibility of the chemical reactions and adsorptions involved in the activation, depression, and collection of the common sulphide minerals. The procedure in much of their work was to bring a mineral surface to equilibrium with solutions of known pH, collector concentration, and activator concentration, and then to test the floatability of the mineral by contact-angle measurement. From the data, graphs were constructed with pH and reagent concentrations as coordinates. These graphs show fields of flotation and fields of nonflotation, separated by narrow transition regions whose locations are shown by so-called contact curves. From the shapes and locations of the contact curves, which roughly separate fields of flotation from fields of nonflotation, a quantitative understanding of the interaction of the reagents with each other and with the minerals often can be deduced. The study of quartz flotation to be described in this paper follows in broad lines the approach of Wark and coworkers. That is, pH, activator concentration, and collector concentration were varied to find equilibrium conditions of flotation and non- flotation, and the results are presented graphically by means of contact curves. However, instead of testing for floatability by measuring the contact angle on a polished surface, a simple vacuum flotation technique was developed and used. Purified oleic acid was the collector and terpineol the frother. Barium activation was studied in some detail, and exploratory studies were made of activation with calcium, aluminum, ferric iron, and stannic tin. Preparation of Materials Quartz: Large lumps of high-grade vein quartz were crushed dry in a cone crusher and rolls. The —20, +28-mesh portion was screened out and used in the subsequent steps. This material was passed through a high-intensity magnetic separator to discard iron, then leached twice with hot concentrated HCl and washed repeatedly with distilled water. The cleaned sand was then wet ground with porcelain balls in a porcelain pebble mill, deslimed repeatedly by settling and decantation to discard —800-mesh material, and again washed with hot HCl followed by distilled water. The resulting stock of quartz was stored under water. Chemical analysis gave 99.8 pct SiO2. Table I gives the size analysis of the quartz used for flotation tests. Calculations from these data, using shape factors given by Gaudin and Hukki9 indicate a specific surface of about 500 cm2 per g. Blank flotation tests in distilled water, and in water with added frother, showed the prepared quartz to be completely nonfloatable and thus indicated the absence of organic contamination. Oleic Acid: The preparation of oleic acid was based on fractional vacuum distillation of methyl oleate2,3 followed by regeneration of oleic acid, and finally fractional crystallization of oleic acid from acetone solutions at low temperatures." The pure oleic acid was stored in a refrigerator. The iodine number of the oleic acid was found to be 90.0 (theoretical 89.93). Oleic acid was used in the form of a dilute water solution of sodium oleate, after preliminary flotation tests showed no effects of form of addition and order of addition of reagents when an adequate conditioning time (that is, 30 min) was provided. Other Reagents: Sodium hydroxide solutions low in carbonate were prepared by first making 1:1

Jan 1, 1951

By Brahm Prakash, R. Schuhmann

Chemical conditions for flotation and nonflotation of quartz with oleic acid as collector and barium, calcium, aluminum, iron, and tin as activators were studied using a simple vacuum-flotation technique in glass-stoppered graduates. The detailed study of barium activation led to an interpretation based on ideal Langmuirian chemi-sorption. FLOTATION of quartz is of practical importance as something to be avoided in soap-floating many types of ores. Clean, unactivated quartz is not floated with fatty acids and soaps, such as oleic acid and sodium oleate, in the quantities normally used for flotation. However, data in the literature indicate that almost any multivalent cation will activate quartz if given an opportunity. Thus, a common problem is to prevent activation of quartz by the various inorganic cations inevitably present in flotation pulps. Wark and his coworkers1 have demonstrated the reversibility of the chemical reactions and adsorptions involved in the activation, depression, and collection of the common sulphide minerals. The procedure in much of their work was to bring a mineral surface to equilibrium with solutions of known pH, collector concentration, and activator concentration, and then to test the floatability of the mineral by contact-angle measurement. From the data, graphs were constructed with pH and reagent concentrations as coordinates. These graphs show fields of flotation and fields of nonflotation, separated by narrow transition regions whose locations are shown by so-called contact curves. From the shapes and locations of the contact curves, which roughly separate fields of flotation from fields of nonflotation, a quantitative understanding of the interaction of the reagents with each other and with the minerals often can be deduced. The study of quartz flotation to be described in this paper follows in broad lines the approach of Wark and coworkers. That is, pH, activator concentration, and collector concentration were varied to find equilibrium conditions of flotation and non- flotation, and the results are presented graphically by means of contact curves. However, instead of testing for floatability by measuring the contact angle on a polished surface, a simple vacuum flotation technique was developed and used. Purified oleic acid was the collector and terpineol the frother. Barium activation was studied in some detail, and exploratory studies were made of activation with calcium, aluminum, ferric iron, and stannic tin. Preparation of Materials Quartz: Large lumps of high-grade vein quartz were crushed dry in a cone crusher and rolls. The —20, +28-mesh portion was screened out and used in the subsequent steps. This material was passed through a high-intensity magnetic separator to discard iron, then leached twice with hot concentrated HCl and washed repeatedly with distilled water. The cleaned sand was then wet ground with porcelain balls in a porcelain pebble mill, deslimed repeatedly by settling and decantation to discard —800-mesh material, and again washed with hot HCl followed by distilled water. The resulting stock of quartz was stored under water. Chemical analysis gave 99.8 pct SiO2. Table I gives the size analysis of the quartz used for flotation tests. Calculations from these data, using shape factors given by Gaudin and Hukki9 indicate a specific surface of about 500 cm2 per g. Blank flotation tests in distilled water, and in water with added frother, showed the prepared quartz to be completely nonfloatable and thus indicated the absence of organic contamination. Oleic Acid: The preparation of oleic acid was based on fractional vacuum distillation of methyl oleate2,3 followed by regeneration of oleic acid, and finally fractional crystallization of oleic acid from acetone solutions at low temperatures." The pure oleic acid was stored in a refrigerator. The iodine number of the oleic acid was found to be 90.0 (theoretical 89.93). Oleic acid was used in the form of a dilute water solution of sodium oleate, after preliminary flotation tests showed no effects of form of addition and order of addition of reagents when an adequate conditioning time (that is, 30 min) was provided. Other Reagents: Sodium hydroxide solutions low in carbonate were prepared by first making 1:1

Jan 1, 1951

By A. Phillips, D. H. Killpatrick, V. Kerlins

The tensile failure of two dispersion-strengthened Ni-20 Cr alloys was studied and compared to the fracture of a similar alloy with no dispersoid. The fracture characteristics were studied using electron fruc-tography and transmission electron microscopy. In all three cases, the mode of failure was found to be microvoid coalescence. The failure in the dispersion-strengthened alloys was found to have initiated at the particles. The size of the dimples in the fracto-graphs was found to be related to the spacing of the particles, but not to the total elongation before failure. The elongation before failure was found to be related only to the amount of dispersed phase. These results are compared to those predicted by a theoretical model of ductile failure. THE continually increasing strength requirements for creep-resistant materials capable of long life at service temperatures above 1600"F (875"C) have developed considerable interest in dispersion-strengthened nickel-base alloys. The high yield strength of these alloys results from the presence of a dispersion of fine particles of thoria which act to impede the normal motion of dislocations. Many theories have been presented to explain the role of the dispersion in the strengthening of these alloys. A good review of these theories is presented by Ansell.' The ultimate strength of such alloys is not only related to mechanisms raising the yield strength, but also to the amount of work-hardening which occurs. This work-hardening is determined by the work-hardening rate and the amount of plastic strain before failure. Since fracture limits the amount of plastic strain, a study was undertaken to gain a better understanding of the fracture mechanisms in these alloys. Electron fractography and transmission electron microscopy were used to study the fracture characteristics in two dispersion-strengthened alloys and one similar alloy containing no dispersoid. These results are related to the tensile properties of the dispersion-strengthened alloys at room temperature and at 2000°F (1095°C). The results are also related to a theory for ductile fracture. 1) PROCEDURE Standard tensile specimens were made from 0.020-in. (0.051-cm) sheets of three different Ni-Cr alloys. The alloys had nominal compositions of Ni-20Cr, Ni-20Cr-2Th0,, and Ni-2OCr-4Th0,. All alloys were supplied in an annealed condition. The specimens were fractured in tension at room temperature to determine the effect of the dispersed thoria on the fracture appearance. The tensile properties were determined from the average of a minimum of three ten- sile specimens for each condition tested. The fracture surface of all of the alloys was examined by electron microscopy using standard two-stage plastic-carbon replica techniques. Thin foils of the dispersion-strengthened alloys were used to investigate the size and spacings of the dispersion particles, and to investigate sections of the 2 pct thoria alloy taken from areas of the specimen adjacent to the fracture surface. The thin foils were mechanically ground to 0.010 in. (0.025 cm) and then chemically polished to approximately 0.001 in. (0.003 cm) in a solution of 29 g of ferric chloride and 10 ml hydrochloric acid in a liter of water. The polishing solution was maintained at 150"F (65°C) during the thinning operation. The final thinning of the foil was done electrolytically using a solution of 700 ml ethanol, 100 ml 2-butoxy eth-anol, 120 ml distilled water, and 78 ml perchloric acid (70 pct). The potential was maintained at 15 v and the bath temperature at -20°~ (-29°C) during the thinning operation. The final thickness of the foil was approximately l000A as determined from the width of twins boundaries observed in many of the foils. 2) RESULTS AND DISCUSSION The electron fractographs of the fracture surfaces of the alloys are shown in Figs. 1, 2, and 3. The normal interpretation of this type of fractographz is that, as a result of the difference between elastic and plastic properties of the matrix and the particles or other inhomogeneities in the alloy, microvoids are formed

Jan 1, 1969

By J. M. Uys, T. B. King

The solubility of water in silicate melts of various compositions was measured. The basicity of the silicate did not appreciably affect the water solu-bulity at low-base content (acid compositions). Near the orthosilicate composition the solubility increased with basicity for silicates in which the cation displayed a weak ion-oxygen attraction and apparently decreased for those in which the cation showed a strong ion-oxygen attraction; metasilicates of the former class dissolved more water than those of the latter. Temperature had little effect on water solubility. The experimental results are interpreted on the basis of two modes of solution, the contribution of one decreasing, and that of the other increas -ing, with increased melt basicity. In the former, solution occurs through interaction with doubly-bonded oxygen atoms and in the latter, through interaction with singly-bonded oxygen atoms, or, in very basic melts, through reaction with free oxygen ions. THE hydrogen content of a steel melt is in a large measure determined by water dissolved in the slag. In some glasses water may be a major cause of "seeds". Water vapor in the furnace atmosphere is the primary source in both instances. A knowledge of the mechanism of water solution in silicate melts should help in assessment of practical methods for its control in steelmaking and glass refining. Walsh et a1.l measured the water content, expressed as hydrogen, of 40 pct lime-20 pct alumina-40 pct silica and 62 pct manganese oxide-38 pct silica melts as a function of the steam partial pressure, in equilibrium with the melt. Tomlinson 2 and, also, Russell3 investigated this relationship for a molten 30 pct soda-70 pct silica glass. In all three investigations, the solubility of water was found to be proportional to the square root of the partial pressure of steam. Moulson and Roberts 4 confirmed this relationship for a silica glass. On the basis of the square root relationship, Tomlinson2 and Russell3 interpreted the solution reaction as "network-breaking", similar to that expected on the addition of metal oxides to silica. Walsh et al.' postulated two possible modes of solution, one the mechanism suggested by Tomlinson and Russell and the other the reaction of the water molecule with an oxygen ion to form hydroxyl ions. These two modes of solution suggest opposite effects of melt basicity on water solubility. However, little appears to be known about the effect of melt basicity on water solubility. Walsh et a1.l found, in the lime-silica system, that the water content increased slightly with increased basicity. As these authors pointed out, this does not appear to be in accord with their further observation that slags containing little or no silica dissolve very little water. Kurkjian and Russell5 measured the effect of basicity on water solubility in alkali silicates in the composition range 15 to 45 mole pct alkali oxide. They found a minimum in the water content at about 25 mole pct alkali. This was interpreted on the basis of two concurrent solution reacZions; one in which solubility was proportional to the activity of doubly-bonded oxygen and, in the other, proportional to the activity of singly-bonded oxygen. The present work was aimed at establishing the effect of basicity on water solubility in silicate melts over as wide a range of compositions as practical. APPARATUS AND EXPERIMENTAL PROCEDURE The silicate melt was equilibrated with a "carrier-gas" of accurately known water content, quenched, and analyzed for water by a vacuum fusion technique. Some pertinent details of the equilibration procedure, analysis technique, preparation, and handling of the silicates are given below. Gas-Silicate Equilibration. The apparatus used to equilibrate the melt with the gas mixture was similar to that used by Walsh et al.' but with some important modifications.6 Purification trains were provided for nitrogen and hydrogen; whenever air or oxygen was used as carrier gas the nitrogen purifiCation train was used with the copper furnace at room temperature. Gas flow rates were measured with capillary flow meters; bleeders filled with a mixture of dibromo and tribromo ethyl benzene (density about 2 g per cc) were used for convenience in controlling flow rates.

Jan 1, 1963

By W. Rostoker

Single isothermal sections were constructed for the titonium-rich corners of the systems Ti-Fe-O, Ti-Cr-O, and Ti-Ni-0 with a view to locating the shape and disposition of the ternary intermediate-phase fields for the compounds isomorphous with Fe3W3C. IN a previous note,' it was reported that a group of ternary intermediate phases existed which occurred in the general composition range Ti,X,O-Ti&O where X was one of the following elements: copper, nickel, cobalt, iron, or manganese. In two instances, binary intermediate phases occurred (Ti²Cu and Ti²Ni) which appeared to be isomorphous. The X-ray diffraction patterns of the phases could be indexed on a cubic lattice whose cell edge was of the order of 11 kX. Karlsson2 stated that the line extinctions and line intensities indicated that these phases were isomorphous with Fe³W³C and therefore belonged to the space group Oh. This author also noted that no unique phase of this type occurred at the composition Ti,Cr,O. This latter statement was accepted as true at the time the previous technical note was written.' However, work continued along these lines and that reported here has shown that a phase isomorphous with Fe³W³C does exist in the vicinity of the composition Ti³Cr³O but not at or near Ti4 Cr²O. The lattice parameter of this phase was found to be 13.01 kX. Metallographic examination of both as-cast and annealed specimens of these supposed ternary oxide phases disclosed structures which were far from single phase in many instances. It was considered a point of some interest to locate more positively the composition coordinates of the single-phase fields. To this end, single isothermal sections for the systems Ti-Fe-O (1000°C), Ti-Cr-0 (1000°C), and Ti-Ni-0 (900"C) were constructed. Phase relationships were studied by both X-ray diffraction and metallotrra~hic methods. Allovs were prepared as 10 g buttons by melting in a noncon-sumable electrode, water-cooled copper crucible arc-melting furnace using a helium atmosphere. Oxygen was introduced quantitatively by the use of weighed amounts of TiO² or TiO. Iodide titanium and the purest available alloying metals were used. All results are discussed in terms of the nominal composition of the melts. Previous experience with making oxygen-rich alloys had shown that oxygen losses were not significant if a homogeneous melt was produced. Weight-loss measurements were used to check loss in metallics during melting. Anneals were conducted in evacuated Vycor bulbs, and annealing times ranged from 24 hr at 1000 °C to 48 hr at 900°C. To achieve equilibrium in certain sluggish alloys, seven-day anneals were used. Debye-Scherrer powder patterns were taken in a 14 cm diam camera using filtered CuK radiation (K² = 1.541232 kX; K., = 1.53739 kX). Specimens were prepared by crushing and screening previously annealed buttons. In general, the X-ray diffraction results were used to identify the major phases, while the metallographic examinations were more useful in indicating the number of phases present. By the use of the combined results and general fundamental rules governing ternary equilibrium, it was possible to construct isothermal sections in good detail. In some instances where auxiliary lattice-parameter data were available, it was possible to lay down tie lines and to locate more positively corners of three-phase fields. Isothermal Section of the System Ti-Fe-O at 1000°C The binary systems Ti-O³ and Ti-Fe4 have been published. Binary phases, TiO, TiFe, and TiFe2, are likely to be encountered in the titanium-rich corner of the system. The structures are NaCl (Bl), CsCl (B2), and MgZn, (C14) types, respectively. Although preliminary X-ray diffraction studies indicated the presence of a ternary phase in the composition range Ti,Fe,O-TiJ?e,O, metallographic examination of two specimens at these compositions revealed the presence of other phases. Thirty-eight alloys were used to delineate the phase boundaries of the isothermal section illustrated in Fig. 1. The five almost single-phase ter-

Jan 1, 1956

By Craig R. Barrett

The influence of the stress dependence of the dislocation density on the overall stress dependence of The steady-state creep rate is discussed. Experimental measurements of dislocation densities and creep rates jor an Fe-3.1 pct Si alloy tested over a wide range of stress are presented which indicate a close correlation between the two quantities. EXPRESSING the stress dependence of high-temperature steady-state creep rates has been the subject of numerous investigations over the past decade. From these investigations have emerged a few general equations which fit most of the available data reasonably well. Garofalo 1 has proposed that for a wide range of stress and temperature the creep rate, i, can be expressed by a relationship of the form: where A, ß, and n are temperature-dependent and is the applied stress. Eq. [I] gives a stress dependence of a at low stresses and exp(nßo) at high stresses, both consistent with experimental observation where n = 5. A number of other investigatorshave proposed a similar expression where: where m and w are in general functions of temperature. Theoretical justification for Eqs. 111 and [2J comes from two different approaches, theories based on dislocation glide3-5 and theories based on the balance between work-hardening and recovery.' Dislocation glide theories predict where p is the mobile dislocation density and V is the activation volume. In order for Eq. [3] to predict a on stress dependence at low stresses with n = 5, it is necessary for p to be a strong function of stress, about proportional to u3 or u4.436 Recovery models of creep start with the general expression:' where r is the recovery rate and h is the work-hardening rate, and then employ a detailed model to determine the stress dependencies of r and h. As example, weertman2 has described a model based on pile-up hardening which results in an expression similar to Eq. [2] with m = 2 and p = 2.5. A recent, seemingly more general approach suggested by McLean is to use Friedels dislocation network growth expression to calculate the stress dependence of r. This model predicts r = p 3,2 and, as h is taken to be a relatively weak function of stress, the stress dependence of i should be about proportional to p3, 2. Once again, it is required that p be a strong function of stress to yield i This recovery model is by no means complete as the stress dependence of network growth is calculated in the absence of an applied stress meaning that r should probably be a stronger function of stress than given by p3, 2 and also some recent work by Mitra and McLean8 suggests that the stress dependence of h may be as large as Because of the importance of the stress dependence of p in determining the overall stress dependence of the strain rate it seems reasonable to examine this relationship in some detail. Measurements made on dislocation densities present during high-temperature steady-state creep generally obey the following relationship a =o0 + aGVWp [5] where uo is usually called a friction stress, a is a numerical constant about equal to unity, G is the shear modulus, and b is the Burgers vector. Depending on the magnitude of uo, data obeying Eq. [5] can give rise to a range of stress dependencies of p. For example, if we assume that the expression where 6 is some constant, adequately represents the stress dependence of p over a range of o, then from Although Eq. [6] obviously breaks down when u 5uo for uo 6 can vary over a wide range of values. In particular, if u > a, > 0 then 6 will be greater than 2. As an example the data of Ishida and McLean are plotted in Fig. 1 showing excellent agreement with dynes per sq cm) and also showing good agreement with a p cc u3 dependence when plotted on a log-log basis. As oo increases 6 tends to increase and correspondingly the stress dependence of the predicted creep rate should also increase,* as-

Jan 1, 1968

By J. W. Downey, S. T. Zegler

A study has been made of the occurrence of Phases having the Cr30-type structure in ternary alloys having the general composition where B cept for iron and copper all the B components are known to form binary compounds having the type structure. The occurrence of the struc-ture type in the ternary alloys was investigated using optical and X-ray metallography. The results indicate that iron can replace virtually none of the cobalt in at 900°C, but substitutes for nickel in up to the approximate composition tually insoluble in V3Ni and 2) and exhibit complete solubility. At 100 nickel can be substituted for cobalt in VSCo up to the composition solubility; and 3) in the system , two solid solutions having the type structure occur. At the same temperature, 1000°C, V3Si exhibits limited solubility for V3Co but is completely mis-cible with V3Ga. Lattice parameters have been determined for all the binary and ternary phases. The solid solutions are discussed in terms of the atomic size and electronic factors which are thought to influence the occurrence of Cr30-type phases. The binary compounds V3Co and V3Ni were found to form peritectoidally from o phases and a vanadium, the former compound at a temperature between 1000" and 1050°C, the latter between 800°and 900°C. The substitutions of nickel and rhodium for cobalt in V3Co were determined not to raise the superconducting transition of VSCo to a temperature as high as 2°K. The occurrence and stability of binary intermediate phases having the Cr30- or A15-type structure (space group o;, Pm3n) have been discussed in several recent papers . Vanadium forms the struc -ture at or near V3B stoichiometry with all the mem -bers of the cobalt and nickel groups in the periodic table and also with Au, Ga, Si, Ge, Sn, P, As, and Sb. This paper describes a survey of the occurrence of the CrsO-type structure in ternary alloys having the general composition V3(B, B') where B and B' are Fe, Co, Ni, Cu, Rh, Ir, Si, and Ga. The purpose of the survey was to clarify the connection between the position of the B partner in the periodic table and its CrsO-type phase-forming tenden~y.~,~ The survey is part of a broader program concerned with the influence of B-partner substitutions on the superconducting transition temperatures of CrsO-type compounds. The transition temperatures, Tc, of some of the ternary Cr,O-type phases found in the survey are also discussed in this paper. EXPERIMENTAL PROCEDURE The alloys were prepared by arc-melting in an A-He atmosphere and were in the form of buttons, weighing approximately 3 g. The metals used in their preparation were received from commercial sources and were in all cases 99.9+ pct pure. The vanadium was spectrochemically pure except for 800 ppm of Si, 200 ppm of Fe, and 200 ppm of Al. For study of each pseudobinary system at least seven alloys were prepared having the general compositions case of alloys containing gallium, melting losses were small, usually less than 0.3 pct of the total weight of the metals charged for melting. Melting losses were somewhat greater for gallium alloys, ranging in general from 0.9 to 5.0 pct. Ternary V-Si-Ga alloys were chemically analyzed and the results are given in Table I. The analyses show most alloys to be within 2 at. pct of the intended composition. Throughout the balance of the paper the intended compositions are used in discussing the alloys. The cast buttons were annealed within evacuated quartz capsules for times ranging from 3 to 6 weeks at temperatures between 800" and 1000°C and water-quenched. The phases present in the annealed and quenched alloys were identified by optical and X-ray metallography. X-ray diffraction photograms were made with powders prepared from the bulk specimens, by the use of a 114.6-mm-diam powder camera with copper irradiation. The lattice parameter of CrsO-type phases and their standard errors

Jan 1, 1963

By Klaus Detert

Fifteen and 18 pct Ni maraging steel and several binavy and ternary alloys of the iron-rich corner of the Fe-Co-Ni system have been studied. After annealing in the austenite range, these alloys were deformed slightly by cold rolling and subsequently aged. Compavison of experimental measurements at various processing stages indicates that small degrees of deforn~ation (5 to 10 pct reduction in thickness) do not influence hardness and strength or the aging kinetics. Electrical resistivity and ductility are somewhat redu]ced and the coercive force is substantially lower when compared to identical samples which were not deformed. The results are explained in terms of retained austenite which transforms into martensite with the small amount of deformation. RECENTLY there has been increasing interest in maraging steel for applications in electric power generators requiring a high ratio of power to weight.' Fifteen pct Ni maraging steel has been investigated to evaluate its properties and performance for application as high-strength magnetic rotor steel,' and a thorough investigation of the precipitation and transformation processes in this alloy has been conducted in this laboratory.3 The influence of deformation, which preceded the aging treatment, was also studied. It was found that a small deformation in the order of 5 pct has a rather striking effect in reducing the coercive force. Other interesting effects on the properties caused by such deformation have led to the more detailed studies reported herein. EXPERIMENTAL METHOD The methods used to produce the samples from 15 pct Ni maraging steel have been described elsewhere.3 The general procedure of hot forging and cold rolling to sheet has been followed. The composition is included in Table I which also contains the composition of the 18 pct Ni maraging steel grade 250 studied. More data about the material and the processing of the 18 pct Ni maraging steel have been recently reported.4 The experimental alloys of binary and ternary Fe-Ni-Co alloys were made by levitation melting in an argon atmosphere and casting into rod-shaped ingots 7 mm thick weighing 20 g. From these ingots 25-mm-long rods were machined to study the phase transformation by a dilatometer. These rods were then cold-rolled to strips, 2.4 mm thick. Annealing for austenitizing was done in tube furnaces in an argon or helium atmosphere followed by cooling in the water-cooled portion of the tube. Aging was done in a salt bath containing a neutral blend of Alkali nitrates and nitrites. Vickers hardness was measured using a load of 50 kg for 15 sec. Tensile tests were carried out on a hard beam tensile tester at a strain rate of 5 X lo-' per sec using flat samples with a gage length of 37.5 mm and a cross section of 1.25 by 6.25 mm. Estimated sensitivity was 5 K x strain and 0.35 kg per sq mm stress. Magnetic saturation was determined on small cylindrical samples, 2.5 mm in length and diameter, by measuring the force exerted by the gradient of a magnetic field of 1000 oe per cm in a mean field of 11,500 oe. The measured values could be reproduced within *1 pct. Coercive force was measured by a precision-type magnetic field probe in a magnetic coil as described by Foerster.5 The magnetizing field was 1300 oe. The samples were 5 cm long, 1 cm wide, and 2.4 mm thick. he coercive force was measured to within +0.1 oe. Electrical resistivity was measured by using a potentiometer on flat strips with a gage length of 100 mm and a cross section of 2.5 by 0.5 mm. The accuracy of the measurement was 0.1 pct but the reproducibility of the measured specific resistivity among different samples was in the order of 1 pct. The method used to prepare the samples for electron transmission has been reported elsewhere.3 RESULTS Fig. 1 shows the influence of deformation after annealing on the resistivity, hardness, and coercivity. The samples were annealed for 30 min at 1000"C,

Jan 1, 1968

By F. D. Rosi

The plastic properties of extended silver and copper crystals of varying purity were studied as a function of crystal orientation in the early stages of flow. Variations in the gross shape of the shear stress-shear diagram and in the properties of critical Variationsshear stress and shear-hardening coefficient were correlated with changes in slip-band developments. The phenomenon of work hardening is discussed in terms of the existing dislocation theory. IT appears certain from the early studies on the deformation characteristics in metal crystals1-3 that plastic flow takes place in a preferred crystallo-graphic slip system which is determined by the geometry of the crystal (law of maximum shear stress), and that the value of shear stress for this system is independent of crystal orientation (law of critical shear stress). Experimentally, it has been demonstrated further that the law of critical shear stress can be extended to include extensive plastic flow.&apos; Thus, the shear-hardening coefficient, which is defined as the slope of the shear stress-shear curve, also is considered to be independent of orientation. It is noteworthy that deviations from this empirical shear-hardening law have been reported in cubic crystals whose initial orientation favors slip on more than two systems.&apos; Moreover, this law appears to have been derived from stress-strain data relating to relatively high values of shear strain (0.5 to 4), where widespread slip and complex distortions can be expected, regardless of crystal orientation. Since existing data indicate that the strain inhomogeneity in a crystal is manifested particularly in the early stages of flow, it would appear that a more exacting test as to the fundamental nature of the shear-hardening law would be to investigate systematically the shape of the stress-strain curve as a function of crystal orientation in the earlier stages of deformation. With regard to the general form of the shear stress-shear curve for cubic crystals, early studies show a parabolic hardening law, where the shear 1 stress is proportional to the square root of the shear-strain. Since this law was predicted theoretically by Taylor" in his original dislocation model for hard- ening, it has been accepted widely as a fundamental flow characteristic of cubic metals. However, it was recently pointed out by Masing6 hat the parabolic law is not the elementary form of hardening in cubic crystals, but instead is a consequence of complexities in the flow process (e. g., deformation bands and unpredicted secondary slip). Thus, in the very early stages of deformation (< 2 pct extension) where the occurrence of such complexities is unlikely, a different strain-hardening behavior might be anticipated. This view is supported by the recent work of Rosi and Mathewson7 on high purity aluminum where a linear law was obtained for extensions up to 2 pct. A linear hardening over a wider range of deformation also was reported by Rohm and Kochendorfer8 ho deformed aluminum crystals under conditions approximating pure shear. Even more pertinent is the recent evidence of Masing and Raffelsieper9 on high purity aluminum crystals. It was found that for crystals having initial orientations near a <l00> or <1ll> axis, a high hardening was obtained, whereas crystals with a <110> orientation exhibited a low and linear hardening curve followed by a region of more rapid hardening. Since much still remains obscure concerning the details of strain hardening as well as slip-band formation in face-centered-cubic crystals in the early stages of deformation, the present study was undertaken to evaluate the effect of crystal orientation on these two important manifestations of glide. It is important to note here that at the time of this study, Lucke and Lange11 presented information on the orientation-dependence of the shape of the strain-hardening curve in aluminum of various purities. Their work, which essentially represents an extension of that of Masing and Raffelsieper, in many respects is parallel to that of the present study. Experimental Procedure Production of Single Crystals: Single crystals of silver and copper of varying purity were used in

Jan 1, 1955

By Shiro Ban-ya, John Chipman

The effects of many alloying eletnents on the acticity coefficient of sulfur in liquid iron have-been studied by the equilibriutn in the reaction Sfin Fe) + Hz = HzS at 1550°C&apos;. Results are expressed in terms of a concentration variable for a nonmetallic or for a substitutional metallic solute. Activity coefficient of sulfur, defined as increased by B, Al, C, Si, Ge, Sn, P, As, Sb, Mo, W, Co, and PI. It is decreased by Cu,Au, Ti. Zr, V, h&apos;b, Ta, Cr, ,23n, and Ni. Irulues oj. the interaction coejficient 0i = 6 In are labulated. The same interactions are expressed also in terms of atom fraction and of weight percent. The thermodynamic properties of sulfur in liquid iron have been fairly well established. Our recent paper1 reported new determinations of activity coefficient up an atom fraction of 0.12 and equations based on a careful review of all published data. The effects of alloying elements on the activity of sulfur have been studied by several investigators,2"11 especially by Morris and Williams for silicon,&apos; by Morris and Buehl for carbon,~ and by Sherman and Chipman for manganese. phosphorus, and al~minum.~ However, the effects of some important alloying elements remain to be determined. The purpose of this investigation was to determine the effects of many alloying elements on the activity of sulfur in Fe-S-j ternary systems. EXPERIMENTAL METHOD This study was based on experimental determination of equilibrium in the reaction at 1550°C: The same apparatus and procedure as described in our previous paper have been retained, and the same corrections were applied for dissociation of H2S. The alumina crucibles used in the experiments consisted of four separate compartments. In a given experimental run. kach of three alumina crucibles held four different samples of about 3 g each which reached equilibrium in the same gas atmosphere and temperature. The charges were made up of electrolytic iron, pure iron sulfide, and desired alloying elements, which were pure metal or master alloys made in the laboratory. The weighed samples were held for 4 to 12 hr in the prepared atmosphere at 1550°C. They were then low- ered to be cooled as quickly as possible. The quenched metal beads were crushed to avoid the errors of segregation in the ingot. The sulfur content was determined gravimetrically and alloy content by appropriate chemical analysis. CALCULATIONS The apparent equilibrium constants of Eq. [I] are expressed as follows from the corrected gas ratios and sulfur concentrations: The term K" is the observed equilibrium constant in any given ternary solution, K&apos; is the value for the Fe-S binary solution. and the limiting value of K&apos; in the infinitely dilute solution is designated by K, which is the true equilibrium constant in Eq. [I]. In the thermodynamic treatment of nonmetallic elements in a metallic solution, it has been suggested1&apos; that the lattice ratio has certain advantages over other variables to express the concentration of solute. In interstitial solid solutions the lattice ratio zj is proportional to the ratio of filled interstitial sites to those which remain unfilled. The equations derived for the activity of the solute using zj as the concentration variable are found also to be applicable to liquid solutions containing nonmetallic solutes when the nonmetal is treated as if it were interstitial. For this purpose we adopt the following definitions: The quantity vj which is negative for interstitial solutes is taken as -1 for nonmetallic and +1 for metallic solutes. For purposes of calculation however ; j may be assigned a value which results in a linear relation such as shown in Figs. 1 to 15. The activity coefficient of sulfur, Qs, and equilibrium constant. K(z). are defined as follows: According to a Taylor series expansion. the logarithm of the activity coefficient of sulfur in Fe-S-j ternary system is: However, the value of 6 In */6zi remains constant through a broad range of dilute solutions and the terms of higher order are negligibly small. As a consequence, Eq. [6] is simplified as follows:

Jan 1, 1970

By G. C. Rauch, T. H. Courtney, J. Wulff

The superconducting behavior of Nb-Ti alloys containing 40 and higher wt pct of Nb and variable oxygen content was studied as a function of thermomechanical processing. Critical current density (Jc) us applied transverse magnetic field (H) data were obtained for 0.010 in. diam wires at 4.2° Kin steady fields up to 120 kOe. The precipitate responsible for increase in Jc in each of the alloys studied was related to niobium and oxygen content. In alloys containing 40 to 60 wt pct Nb with less than about 1600 ppm of oxygen, w precipitation in the range 350° to 450°C appears to be responsible for the maximum value of Jc observed. In alloys of higher oxygen content (-2500 ppm), the oxygen-enriched a phase which precipitates in the temperature range 450° to 550°C is a more effective fluxoid pinner. Maximum Jc in low oxygen (350 ppm) 80 wt pct Nb alloys was achieved by 600°C aging heat treatments. Measurements of resistive critical field also reflect the changes in composition accompanying precipitation in these alloys. It is well known that the superconducting critical current density, Jc, of solid solution superconducting alloys can be increased by precipitation heat treatments.1-4 The precipitate, to serve as an effective superconzlucting fluxoid pinner and increase Jc, must be of proper size and spacing.&apos; Its electronic properties must also be different from those of the matrix.6 As in age-hardenable systems, optimum temperature and time of aging are dictated by the composition and history of the particular solid-solution alloy under consideration. The alloy diagram of Ti-Nb7-9 shown in Fig. 1 is typical of ß-stabilized Ti alloys. Precipitation to achieve high Jc in Ti-Nb and Ti-Ta alloys is usually carried out in what is believed to be a two-phase a + ß region.1,2,4,10 Previous work on Ti-Nb4,11 and on other ß-stabilized systems such as Ti-V, Ti-Mo,12-14 has shown, however, that the first precipitate to appear is not necessarily (Y. Under specific conditions the meta-stable w phase is precipitated instead. A further complication arises in such alloys from the strong influence of contained oxygen on the phase stability and on the kinetics of precipitation.15,16 The superconducting critical current density of Nb-Ti alloy containing less than 36 wt pct Nb has been studied by Vetrano and Boom1 and Kramer and Rhodes.4 The most effective aging temperature was found to be about 425°C; fluxoid pinning was attributed to the precipita- tion of a by Vetrano and Boom and of w by Kramer and Rhodes. Although the latter workers used recrystal-lized material and the former cold-worked, studies carried out in our laboratory lead us to believe that the type of precipitate responsible for increased Jc is unaffected by prior cold-work.17 That other types of precipitates may also be effective, especially in higher oxygen-containing alloys, has been demonstrated by Reuter, et al.2 in this laboratory with the aid of electron microscopy. Reuter et al. found that at an aging temperature of 600°C, fee-TiO is precipitated, resulting in high values of Jc. Even higher values of Jc were observed after heat treatment at 500°C, but the precipitate could not be indexed as fee-TiO. Whether the precipitate was oxygen-rich w or a could not be clearly distinguished. The work nevertheless indicates that appreciable amounts of oxygen alter the nature of the phases precipitated at different temperatures, at least in alloys containing more than 36 wt pct Nb. Since such compositions are more readily worked into suitable wire than lesser niobium content alloys, it was decided to study the response to aging of the alloy compositions reported in the present paper with the hope of clarifying the effect of composition on the precipitation processes responsible for high values of Jc. I. EXPERIMENTAL Nb-Ti alloys containing 40, 50, 60, and 80 wt pct Nb were prepared by are-melting 35 g ingots of iodide crystal bar titanium and electron-beam melted niobium.

Jan 1, 1969

By Leo Horvitz

Microanalysis of near-surface soils for hydrocarbons is the basis of a method for locating gas and oil deposits. To substantiate this technique, evidence of vertical migration of hydrocarbons from petroleum accumulations is presented. Tabulated data relevant to hydrocarbon surveys conducted in several petroleum provinces are included. PEROLEUM and natural gas are composed principally of the saturated hydrocarbons ranging from methane, the lightest, to nonvolatile liquids and solids containing approximately thirty-five carbon atoms. A technique for locating buried accumulations of these hydrocarbons before drilling obviously requires that some of the hydrocarbons leave the deposit and migrate toward the surface of the earth where they may be detected in their original form. Earliest attempts to link near surface hydrocarbons to petroleum at depth were apparently made by Laubmeyer&apos; in Germany and by Sokolov in Russia. These investigators collected samples of soil air from boreholes one to two meters deep and analyzed them for traces of hydrocarbons. They found that soil air over producing areas is richer in these constituents than is soil air over barren areas. Since 1936 work on petroleum exploration techniques of this type has been going on in this country. However, instead of determining hydrocarbon content of soil air collected in the field, investigators analyze samples of the soil itself for adsorbed and occluded hydrocarbons, which are released by suitable treatment and found in larger amounts than are the quantities reported for soil air. Difficulties often encountered in collecting gas samples in the field, moreover, are eliminated when soil is used as the sampling medium. Field Procedure: Sample locations are first surveyed over the area to be investigated. Care is taken to locate the stations at considerable distances from roads, pipelines, drilling wells, and other sources of contamination. The borehole pay be dug with a bucket-type hand auger or with mechanical drilling equipment. Lubricants are avoided in either case. When the desired depth is reached, a sample is brought to the surface, placed in a pint glass jar or can, and securely sealed. Sample containers are carefully labeled and delivered to the analytical laboratory. Generally a satisfactory sampling depth range is 8 to 12 ft. In some regions, however, satisfactory data are obtained from samples collected at much shallower depths. Such is the case, for example, in areas of west Texas where the limestone and caliche near the surface occlude hydrocarbons and prevent their rapid escape to the atmosphere. In carrying out broad reconnaissance surveys in search of large features, considerable time is saved by first taking samples one-fourth to one-half mile apart along profiles about one mile apart. If the analytical data indicate a hydrocarbon anomaly of interest, additional samples are taken to produce a more dense and uniform sampling pattern within the interesting area. This sampling program is particularly adaptable to areas that are sectionized. In areas covered with a network of roads, sampling along these roads facilitates the reconnaissance survey. Actual sampling density used depends upon areal extent of features expected. When flanks of piercement-type domes where accumulations may be only several hundred feet wide are sampled, stations are often no more than 200 ft apart. Analytical Technique: Of the hydrocarbons composing petroleum, only the more volatile would be expected to reach the surface of the earth. The analytical technique, therefore, was developed to determine only those constituents that exert a vapor pressure at room temperature. Actually, in near-surface soils, only a very small part of the hydrocarbons are heavier than pentane. Details of the analytical technique have previously been reported. Only a brief description of the methods will be presented here. A weighed portion of the sample, about 100 g, is first treated with an aqueous solution of copper sulphate and then with phosphoric acid in a partial vacuum. The copper sulphate prevents the reaction of the acid with carbides that may be present because the sample has been contaminated by auger particles. Such a reaction may produce spurious methane. The role of the acid is to decompose any carbonates present, thereby helping to release the hydrocarbons. The carbon dioxide is removed with potassium hydroxide and the flask containing the

Jan 1, 1955

By J. J. Frawley, W. J. Childs

Experiments were carried out to induce grain refinement during solidification by applying vibrational energy (freq 20 kc) to small specimens of bismuth, tin, and bismuth-tin alloys. The results show that if the intensity of the applied sound -field is not great enough to fragment the growing dendrites of a pure metal, no grain refinement is observed and the pain size of the dynamically nucleated specimens is the same as the grain size of a specimen statically supercooled the same amount. Bismuth specimens did not show any grain refinement; whereas, the tin specimens did show grain refinement. This phenomenon is the result of the difference in growth habit between the bismuth and tin dendrites. The bismuth-tin alloys showed grain refinement and, in addition, the segregation pattern was changed. THE solidification process is a change in phase requiring the nucleation of the solid phase from the liquid and the growth of this solid phase at the expense of the liquid phase. Since many physical properties and also the integrity of a casting are dependent on the solidification process, understanding and controlling this process are very important.&apos; A good example in the controlling of a cast structure using heterogeneous nucleation theory is the reduction of grain size in aluminum castings by nucleation catalysis.2 This mechanism of nucleation catalysis has been explained by Turnbull.3 Another technique for grain refinement, which has received much attention but the mechanism has not been fully understood, is to vibrate the solidifying melt. Vibrations can be applied to the melt either by vibrating the mold directly or by introducing a vibrating rod into the melt.4-13 Three mechanisms have been proposed to explain this phenomenon: 1) The mechanical fragmentation of the original dendrites that grew into the melt. These crystals or fragmented dendrites act as new growth sites. 2) The nucleation of new grains in the liquid by the generation of very high pressure pulses caused by cavitation in the liquid. 3) The remelting of the dendrite arms during the solidification process. This mechanism is operative only in alloy systems and would be enhanced by stirring or mechanical vibration. The purpose of this investigation was to determine the mechanism that will increase the number of grains when mechanical energy is introduced into a solidifying melt. APPARATUS The unit used to generate the ultrasonic vibrations was manufactured by the Redford Co., and is similar to the one used in ultrasonic soldering. Fig. 1 is a sketch of the major components used for generating ultrasonic vibrations. The crystal transducer assembly consisted of four lead zirconate ti-tanate piezoelectric crystals in an aluminum holder. An acoustical horn, which was fabricated from stainless steel, was attached to the holder by a set screw. The resonant frequency of this unit was 20,000 cycles per sec. A Pyrex crucible, 4 in. in diam and 4 in. high, was contained in a hole in the top of the horn. The piezoelectric crystals changed volume when excited by an electric signal, thereby generating a sound signal which passed through the horn. The crucible was coupled to the horn by a liquid silicone oil. The purpose of the couplant was to transmit the soundwaves from the horn to the crucible. Without the couplant, much of the sound energy would be lost. The energy transmitted was sufficient at the resonant frequency used, so that acoustical cavitation always occurred in the molten metal. The presence of acoustical cavitation was detected by the characteristic hissing sound emitted from the liquid. EXPERIMENTAL PROCEDURE The influence of ultrasonic vibration on the grain refinement of bismuth, tin, and bismuth-tin alloys was studied. These metals were chosen because of their low melting temperature and the relative ease with which they can be thermally supercooled. The following procedure was used for obtaining large amounts of supercooling. Pure bismuth (99.999+), which was received in bar form, was mechanically broken into pieces small enough to be accommodated in a 50 ml beaker. About 200 to 300 g of bismuth and a few grams of SnCl2 as a flux were placed in the 50 ml beaker and melted by induction heating. The melt was held for 20 min at

Jan 1, 1970

By G. Gutierrez, D. A. Elgillani, M. C. Fuerstenau

The zero-points-of-charge of apatite, calcite, and fluorite are pH 6.4, 10.8, and 10.0, respectively. Scheelite is negatively charged above at least pH 3. In this article, the flotation responses of these minerals in the presence of potassium oleate and sodium silicate are described and compared with electrokinetic data. Colloidal silica appears to be the species principally responsible for calcite depression, while silicate anion is the species responsible for fluorite depression. Additions as high as 1 x 10-3 mole/liter silicate have no effect on the flotation responses of apatite and scheelite. Selective flotation of nonmetallic minerals is difficult to achieve with fatty acids or soaps by themselves. As a result, specific reagents are added to aid these separations, and one of the reagents commonly employed for this purpose is sodium silicate. Flotation separations of various calcium-bearing minerals such as fluorite from calcite1-3 and scheelite from calcite2,4 and apatite,2,5 for example, almost always involve the use of sodium silicate. The mechanisms by which sodium silicate functions as a depressant are still not understood, probably for a number of reasons. For one thing, the dissolution process of sodium silicate is complex, giving rise to a number of ionic and colloidal species.&apos; Moreover, the type and concentration of these species depend on the ratio of Na2O to SiO2, the concentration of sodium silicate, and the pH of the system.&apos; At the present time, it is not known which species, colloidal silica or silicate anion, is responsible for depression. If colloidal silica is the species that is adsorbing, then adsorption must occur by electrostatic attraction between the colloid and the mineral surface. Silicate anion, on the other hand, may adsorb either physically or chemically. The objective of this paper is to determine first the active species of sodium silicate and then the conditions under which this species will adsorb and function as a depressant. EXPERIMENTAL MATERIALS AND METHODS Pure samples of apatite (Durango), calcite (Iceland-spar), fluorite, and scheelite were used in this investigation. Pure potassium oleate was used as collector, while reagent-grade HC1 and KOH were employed for pH adjustment. The sodium silicates used were samples obtained from the Philadelphia Quartz Co. In one series of experiments, various sodium silicates containing different ratios of SiO2 to Na2O were added to calcite systems. These sodium silicates contained SiO2-to-Na2O ratios of 3.75 to 1, 3.22 to 1, 2.40 to 1, and 1.60 to 1. All other experiments were conducted with the sodium silicate containing the ratio of 3.22 to 1, which is the one that is normally used in industry. Flotation experiments were conducted with 21/2-g charges of 48 x 150-mesh material in conductivity water with an apparatus and technique described previously. Electrokinetic experiments were conducted with both a Zeta Meter and streaming potential apparatus. Particle size was 48 x 65 mesh for the streaming potential experiments. EXPERIMENTAL RESULTS The first series of experiments involved flotation of scheelite in the absence and presence of sodium silicate. As shown in Fig. 1, flotation response was not affected with even the relatively high addition of 1 x 10-3 mole per liter sodium silicate. Interestingly though, no flotation was effected below pH 6 with this collector addition. The responses of apatite to flotation under these same conditions are given in Fig. 2. Similarly, no depression was obtained in basic media under these conditions. Similar experiments were conducted with fluorite, and in this case, depression was noted above about pH 11 with 1 x 10-3 mole per liter sodium silicate (Fig. 3). When calcite was floated with these same levels of addition of sodium silicate, essentially no flotation was possible above pH 7 (Fig. 4). The effect of collector addition with a constant addition of sodium

Jan 1, 1969

By Marston G. Fleming

E. C. Peterson (Anaconda Copper Mining CO., Darwin, Calif.)—A study of this quite comprehensible and interesting paper by Dr. Fleming brings to mind several observations in the practical application of alkalinity and related factors to the actual practice of lead mineral flotation. Soda ash has long been a widely used and a very helpful alkaline conditioning agent in the flotation of galena from the usual run of lead-zinc ores. Soda ash is one of the common "standard" conditioning agents tried in any laboratory investigation of lead-zinc ores because it has so often proved helpful to galena flotation. However, the use of soda ash in the actual flotation of oxidized lead ores is certainly not widespread. In the flotation of certain lead-zinc ores from the Park City district of Utah, it was found in the usual cyanide-zinc sulphate-xanthate circuit that soda ash had an effect of producing a very condensed and flat froth regardless of the many frothers tried and that substitution of lime for soda ash to produce the same pH (8.0 to 8.4) improved the froth condition. However, the flotation of coarse particles of galena became so critical that some would pass through into the tailing, but caustic soda as a substitute for either soda ash or lime produced a very desirable froth condition in the same pH range and greatly improved the metallurgical outcome. Milling was carried out in typically "hard water" from watersheds of limestone and other calcareous rocks and the ore also apparently contributed magnesium and calcium salts to the pulp. Certain lead-zinc ores of Mexico have shown their greatest flotation response in circuits conditioned with sodium bicarbonate, and such actual mill use was also believed to be related to the water necessarily used in milling. On other lead-zinc ores the optimum has been obtained in actual milling treatment by use of caustic soda in both circuits of the operation. In flotation of oxidized lead ores in which sulphidi-zation is employed by addition of sodium sulphide, very high pH&apos;s exist in the flotation circuit. With the usual oxide lead ores, demanding 5 to 15 lb of sodium sulphide per ton of ore, pH&apos;s in the circuit (closed and open water-circuits) may range from 9.5 to 12, and for ores that contain much anglesite or a high percentage of iron oxide minerals, sodium sulphide consumption may reach as much as 30 lb per ton of ore and the resultant pH will be correspondingly higher. Yet in such flotation treatment employing either xanthate or oil (high-sulphur crude oil or diesel oils) as the collector, satisfactory to excellent grades of concentrate and lead recovery are obtained. Although there have been great studies and accomplishments in the investigations of flotation fundamentals and flotation theory, and although an investigation to determine the effect of all factors entering into the actual plant flotation of sulphide and oxide ores must become very complicated, as Mr. Fleming has mentioned in his caution regarding the drawing of general conclusions for other ores, it seems that it would be of greater interest if the techniques and investigations could, with time, approach the conditions of actual practice and lead the way to improved and more efficient flotation plant performance. Marston G. Fleming (author&apos;s reply)—The gulf between fundamental flotation research and plant operation is, perhaps, less wide than Mr. Peterson suggests. For example, the work described in my paper developed from an extensive investigation of a complex lead-vanadium ore from southwest Africa. This investigation started as a standard ore-testing problem but, at almost every stage, results were obtained which could not be interpreted in terms of previous experience. A program of fundamental research was therefore undertaken and was closely interlocked with the ore testing. This coordinated investigation resulted in a flotation process which has now been proved by two years of successful plant operation, and although the grade and mineralogical constitution of ore as well as smelter requirements have altered more than could have been anticipated, our knowledge of the fundamental character of the problem has made it possible to meet each change in conditions with much more confidence than would have been the case had we neglected this aspect of the investigation.

Jan 1, 1954