Search Documents

By F. Kassabji

This publication presents the main experimental and theoretical results on the recovery of aluminum scrap (dross and Used Beverage Can) without use of any addition of fluxing salts. Dross and UBC's processing experiments have been conducted in a rotary plasma furnace operating in the transferred and non-transferred mode, using different plasma gases. The investigation involved the treatment of more than 100 kg of dross and other aluminum residues using plasma torches with less than 100 kW power. The experimental work showed that this process is .far more economical and kind to the environment than the conventional route using a salt flux. An equilibrium thermodynamic calculation at elevated temperature makes possible the prediction of by-products at various temperatures for different plasma gases.

Jan 1, 1994

By Xie Zhang, Chongyang Zhao, Qingyun Huang, Bing Xie, Xiaopeng Zhen

"Extracting vanadium from vanadium containing hot metal into vanadium slag by BOF is the main vanadium production process in China. In this paper, the influence of Si content in hot metal on the quality of vanadium slag is analyzed. Synthetic vanadium slag with different SiO2 content were melted at 1673 K and then cooled to 303K at the cooling rate of 3?/min. Optical microscopy, SEM, EDS and XRD were used to analyze the mineralogical phases and crystallization behavior of vanadium slag. The results show that vanadium slag mainly contains spinel phase and silicate phase; V is enriched in the spinel phases while Si is concentrated in Fe2SiO4 CaFeSi2O6 and (Fe,Mn)2SiO4 as silicate phase. The melting point of slag increases gradually with the addition of SiO2; whereas viscosity decreases with an addition of 15~19% SiO2 and increases with an addition of 19~27% SiO2.IntroductionVanadium is an important element which is used almost exclusively in ferrous and non-ferrous alloys. The major vanadium products include FeV, V2O5, V2O3, VN and Al-V-Ti alloy. Furthermore, vanadium slags are mostly produced by oxidizing the elements in V-containing hot metal during a duplex refining process. Therefore, the process of removing vanadium from hot metal has its significance on the subsequent process[1].The extraction of vanadium is greatly affected by the mineralogical composition of vanadium slag[2], the distribution of the elements between the spinel and silicate phases and its physic-chemical properties. These characteristics of vanadium slag have been studied in some details. It has been reported that Si mainly exists mainly in the form of silicate which wraps the spinel crystals while small amount of Si stands as phosphorus quartz or diopside[2]. Chen et al.[3, 4] points out, when SiO2 content in vanadium slag increased every 1%, V2O5 decreased 1.48%. Moreover, silicate phases would embarrass the oxidation of V-containing spinels through decreasing the exposing probability[5]. Meanwhile, melting point and viscosity of vanadium slag has been greatly influenced by the SiO2 content. Therefore, this work attempts to analyze the above-mentioned questions systematically."

Jan 1, 2012

By Sabine Knott

The thermodynamic properties of four liquid ternary zinc alloys, Au-Sn-Zn, Ag-Sn-Zn, AI-Sn- Zn and Cu-In-Zn were measured with an electromotive force (emf) method at three or four cross-sections with an constant X:Sn or Cu-In ratio. At the Au-Sn-Zn and AI-Sn-Zn system calorimetric measurements were also carried out in order to compare the integral enthalpy of mixing from the direct measurements with the data of the emf measurements, which were derived by Gibbs-Duhem integration.

Jan 1, 2003

By C. Pichler, A. Ressler, D. Gregurek, A. Spanring

In order to improve the refractory lining life at one of the RHI key customer test procedures were developed within a two years collaboration project. In the first year of cooperation detailed refractory corrosion work in the rotary kiln with Ca-ferritic slag was performed. The main results of the second year of cooperation, reported in this article, involve a detailed testing work with nickel matte and pre-selected refractory brands which was performed in TBRC. A first part of this work was a complete chemical and mineralogical characterization as well as FactSage calculations carried out on provided matte samples. According to these results testing in the TBRC was realized at different process temperatures with several magnesia-chromite bricks. Based on the mineralogical investigation a high chemothermal load caused by sulfidic matte resulted in a deep reaching infiltration of the brick microstructure and partly corrosion of main brick components.

Jan 1, 2015

By Eric J. Grimsey

Steady state Excel models for a copper flash smelter and an iron blast furnace are used to enhance the teaching of pyrometallurgical smelting principles within a fourth year level process engineering unit delivered at the Western Australian School of Mines. A lecture/workshop approach has been adopted in which student teams undertake process simulation assignments that illustrate the multifaceted responses of process outputs to variation of inputs, the objectives being to reinforce their understanding of smelting principles. The approach has proven to be popular with students, as evidenced by the consistently high ratings the unit has received through student feedback. This paper provides an overview of the teaching approach and process models used.

Jan 1, 2014

By Philip Arthur

The ISASMELT process is making a significant contribution to the global metals industry. ISASMELT furnaces are now operating successfully in eight different countries and treating approximately 3 million tonnes of concentrates and secondary materials per year. The process is currently used in both lead and copper smelting. The most recently commissioned plants were in Germany and China, one for treating scrap copper and the other treating low-grade copper concentrates. The Copper ISASMEL T furnace ("CIF") at Mount Isa Mines Limited (UMIM") has continued to set new operational records, with throughput of more than I million tonnes of concentrate per year and very low operating costs. This paper summarises the latest operational data from the Mount Isa Copper ISASMEL T plant and outlines the successful approach to industrial R&D taken by MIM in the development of the ISASMEL T process.

Jan 1, 2003

By Sabine Knoll

The thermodynamic properties of four liquid ternary zinc alloys, Au-Sn-Zn, Ag-Sn-Zn, AI-Sn Zn and Cu-In-Zn were measured with an electromotive force (emf) method at three or four cross-sections with an constant X:Sn or Cu-In ratio. At the Au-Sn-Zn and AI-Sn-Zn system calorimetric measurements were also carried out in order to compare the integral enthalpy of mixing from the direct measurements with the data of the emf measurements, which were derived by Gibbs-Duhem integration.

Jan 1, 2003

By J. K. S. Tee

Using a novel method, zinc has been selectively removed from galvanized steel scrap on a laboratory scale. The separation is based on thermodynamic principles: during chlorination in air-chlorine (10:l) mixtures at 800 OC, zinc forms a volatile product (zinc chloride) while iron does not chlorinate as its oxides are more stable than the respective chlorides. As much as 92 % of zinc is removed from the surface of steel within 10 minutes. This process overcomes tedious and costly preparatory stages associated with leaching - electrowinning methods.

Jan 1, 1999

By Guo Chen, Xuefeng Liao, Tu Hu, Shengzhou Zhang, Hongying Xia, Jinhui Peng, Libo Zhang

Pine nut shell is as raw material for preparation of high surface area activated carbon (HSAAC) by microwave induced KOH activation. The effects of microwave power, activation duration and KOH/C mass rate (R) on the iodine adsorption capability and activated carbon yield were investigated. Additionally the surface characteristics of HSAAC were characterized by nitrogen adsorption isotherms and SEM. The operating variables were optimized utilizing the response surface methodology and were identified microwave power 738W, activation duration 17 min, and R 4, corresponding to a yield of 46.28 % and an iodine number of 2154 mg/g. The key pore structure parameters of HSAAC such as the Brunauer–Emmett–Teller (BET) surface area and total pore volume were estimated to be 3819 m2/g and 2.09 mL/g, respectively. The findings strongly support the feasibility of microwave heating for preparation of HSAAC from spent pine nut shell by microwave induced KOH activation.

Jan 1, 2016

By R. Angulo

Carbon nanotubes (CNTs) have recently emerged as materials with outstanding properties. This has promoted their consideration as reinforcements for other material systems, such as ceramics. However, one of the fundamental problems with producing CNT-reinforced ceramics is the effective dispersion of CNTs during processing. This has been successfully carried out recently using organic solvents. This paper is a preliminery investigation into the rheological behavior of aqueous CNT-alumina slips, with the objective of moving towards a more environmentally friendly aqueous tape casting process for the production of CNT-ceramic composites.

Jan 1, 2008

By A. Patti, S. Reutzel, D. M. Herlach, L. Ratke, I. Egry

Cu-Co shows a metastable miscibility gap in the region of the undercooled melt. Undercooling of the melt below the binodal leads to separation of the melt into a Co-rich LI-phase and a Curich L2-phase. Experimentally, undercooling into the metastable miscibility gap is realised by means of electromagnetic levitation (EML), processing in drop tube (DT) and by melt flux embedding. As undercooling is large in these experiments, the velocity of the solidification front is high and the microstructure is frozen in instantaneously. Samples have been undercooled and solidified in the TEMPUS-facility (container less electromagnetic processing under weightlessness) during parabolic flight under reduced gravity conditions. Microstructures of solidified samples have been analysed and compared to those processed under gravitational conditions. The influence of convection on phase growth is much lower in reduced gravity. The microstructure shows spherical droplets of the minority phase, statistically dispersed in the majority phase.

Jan 1, 2004

By P. Schloth, H. van Swygenhoven, N. Chobaut, J-M. Drezet

"In the current trend toward thicker aluminium plates, a major concern is the stress build-up during quenching which causes distortions during machining. Indeed, cooling rates are not high enough, especially at the core of such thick plates, to prevent any precipitation and quench induced precipitates lower the hardening potential. Multi-scale modelling is required when predicting macro-scale stresses after quenching for thick heat treatable aluminium components. The reason is the instantaneous strong coupling between phase precipitation at the nano-scale and material hardening due to precipitation or softening owing to solute depletion at the microscale. For thick parts, quenching intensities decrease when going from the skin to the core of the component, thus introducing a gradient of nanostructure and consequently a gradient of mechanical properties. In addition, large thermally induced deformations lead to high macroscale residual stresses although part of them is relaxed by plastic deformation. These stresses have been measured in water quenched thick plates of 7040 and 7449 aluminium alloys using neutron diffraction and layer removal techniques and the results when compared with a thermomechanical finite element model of quenching highlight the influence of precipitation.IntroductionIn the processing route of heat-treatable aluminium alloys (AA), a critical step is quenching from the solutionizing temperature. High cooling rates are desired, as they avoid formation of coarse precipitates, which reduce mechanical properties. Fast quenching, however, cannot be achieved in the centre of thick components, where the quenching rate can be more than one order of magnitude lower than at the surface. The existence of a thermal gradient between core and surface leads to a differential thermal deformation which is accommodated by elastic and plastic deformation to comply with the compatibility of deformation. Whenever the material yields, especially at high temperature when the yield strength is low, residual stress remains after quenching due to the irreversibility of plastic deformation. After quenching, the plates are in a state of residual stress that causes unacceptable distortions during machining and may reduce service life drastically. Since stress relaxation is negligible during ageing treatments [1 ], agehardened aluminium parts are usually stress relieved prior to ageing. This is typically achieved by applying plastic deformation: stretching from 1.5 to 3 % in the rolling direction (L) can reduce the internal stresses by a factor of approximately 10 [2, 3]. However, complex geometries or thicker components like thick sheets require other approaches. Reducing the quenching rate by using boiling water for instance leads to lower residual stresses [1, 4]."

Jan 1, 2013

By Mingmei Zhu, Xin Qiu, Xiaofei Dou, Yu Wang, Tiancheng Lin, Bing Xie

In this study, the slag forming route of the single-slag steel melting when smelting medium phosphorus hot metal was investigated. The CaO-SiO2-FeO-MgO-MnO-P2O5 as hexahydric slag system was adopted in the converter. The effect of slag composition on liquidus was calculated by FactSage, the isogram of phosphorus distribution ratio was calculated by using the regular ion solution model, combining these two tasks, the theoretical slag forming route was obtained. Through experiments, the actual melting point ofthe corresponding components on theoretical slag forming route was obtained, in this way, the theoretical slag forming route was confirmed. Then, the theoretical slag forming route was applied to industrial test in a 210t BOF. After using the new slag formating route, the dephosphorization ratio was increased 3.6% while the auxiliary materials consumption was reduced, and the cost of steelmaking was reduced.

Jan 1, 2015

By Joni M. Barnes

A strain of Pseudomonas stutzeri isohted from selenium contaminated surface waters, was found to be effective . in reducing selenate (Se04 2) stoichiometrically to selenite (Se03 2 '), which was further reduced to elementaJ selenium (Se0 ). These reactions were concurrent with the microbial oxidation of lactate. In order to assess quantitatively the amounts of seilenate and selenitein solution, improvements to existing analytical methods (ion exchange chromatography and inductively coupled plasma atomic emission spectrophotometry technique) .were made.

Jan 1, 1991

By ZHANG Ting

In view of the high consumption and contamination of traditional vanadium extraction technology, a new process of leaching the converter vanadium slag without roasting with titanium dioxide waste was proposed. Extraction mechanism of P204 in the leaching solution had been researched and single factor experiments show that after a prereduction of Fe, and under conditions: ambient temperature，leaching solution original pH=2.5, phase ratio (A/O)=1:3, shaking time 8min, the extraction rate of V is more than 98.62% meanwhile the separation rate between V and Fe is up to 135.3 in the 20%P204-10%TBP-Sulfonated kerosene extraction system.

Jan 1, 2015

By Melinda Channel, Alan W. Weimer, Jonathan R. Scheffe

"There is a need to develop cost effective renewable energy processes for the production of clean fuels that can simultaneously mitigate the U.S. energy/global environmental security issue. If H2 can be obtained cost effectively via the splitting of water using concentrated sunlight, then it’s possible to operate a fuel cell using renewable H2 or to synthesize other fuels based on renewable H2 for generating electricity or for running internal combustion engines. For example, H2 can be reacted with sequestered carbon dioxide (CO2) to produce syngas (H2/CO) via reverse water gas shift (RWGS), i.e. H2 + CO2 ? CO + H2O. The syngas can be catalytically methanated to form synthetic natural gas (SNG) or it can be catalytically reformed to produce liquid fuels such as “green” gasoline via the MTG process (syngas? methanol ? gasoline). The desert SW United States is home to world class sunlight. Fundamental ferrite thermodynamics will be reviewed, an example of the beneficial effect of ferrite surface area on reaction kinetics will shown, and process economics will be investigated for a 100,000 kg/day facility to produce H2.Introduction and Background ThermodynamicsSpinel ferrites of the form MxFe3-xO4, where M generally represents Ni, Zn, Co, Mn, or other transition metals, have been shown to be capable of splitting water according to the two step cycle shown below:MxFe3-xO4 + solar thermal energy ? xMO + (3-x)FeO + 0.5 O2 (1)xMO + (3-x)FeO + H2O ? MxFe3-xO4 + 2H2 (2)This is an inherently clean and sustainable process, as the only net inputs are solar energy and water, and the net outputs are hydrogen and oxygen. Ferrite water splitting cycles are advantages compared to other high temperature water splitting cycles, such as the ZnO/Zn and Mn2O3/MnO cycles, because thermal reduction has been demonstrated at significantly lower temperatures[1, 2]. As a result, overall efficiency may be increased due to the fact that radiation losses increase as the fourth power of temperature, and material considerations for reactor design should be more flexible. Additionally, cycle repeatability has been demonstrated with relative ease as compared to other thermochemical cycles [3-6]. However, the amount of hydrogen per mole that is generated is significantly less than for other high temperature thermochemical cycles due to the fact that only Fe3+ is capable of being reduced at the temperatures of interest[6]. In addition, water oxidation kinetics appear to be very slow, likely due to diffusion or surface area limitations created by near surface oxidation [6, 7]."

Jan 1, 2010

By Zhang Libo, Li Wei, Peng Jinhui, Guo Shenghui, L. Jing

Partially stabilized zirconia ceramics (PSZ) were prepared by microwave sintering using natural baddeleyite which was obtained by flotation of baddeleyite ore as starting materials. Because of using natural baddeleyite as raw and the process producing no waste, it realized shorter process, energy savmg, environmentally-friendly and non-damage processing. In this work natural baddeleyite stabilized with 3.8wt.% CaO were sintered at 1300°C for 60min in a multi-mode 2.45GHz microwave furnace. Microwave sintering could fast heating and sintering. Besides that, microwave sintering could heat materials wholly, low the sintering temperature, improve the materials properties and save energy. X-ray spectrum displayed the product composed by the tetragonal phase and monoclinic phase that also showed the product was PSZ. Fine and uniform microstructures were observed in the product through scanning electron microscopy. PSZ which was with high density was confirmed by the method of the Archimedes technique.

Jan 1, 2011

By Eric Pirard

Theoretical studies carried out on shape analysis supply mathematical tools to analyze the influence of grain shapes on ore beneficiation. In the case of statistic images like those encountered in applied mineralogy parametrical and harmonical analysis methods are used. It is important that the shape parameters are adapted to the specific processes involved in ore beneficiation, while remaining easy to manipulate. The inertia parameters are considered in the scope of granulometric and gravimetric processes It appears that they are able to distinguish between the resulting products where very popular shape parameters are not. The measured statistics are analyzed through discriminant analysis procedures in order to estimate the importance of morphological differentiation and the aptitude of shape parameters to account for this.

Jan 1, 1989

By Norihiko Fukatsu

In order to use effectively the previously reported new sensing system for hydrogen and oxygen potentials in molten copper, the criteria of the potentials for getting sound castings have been determined in the laboratory experiment. The copper melt equilibrated with a given hydrogen and an oxygen potential was rapidly quenched in the crucible. The relations between the holding potentials and the gas porosity in the solidified sample were investigated by measuring the density of the sample and microscopic observations. It was found that the defects of the gas porosity became the maximum at the potentials where the dissolved amount of hydrogen and oxygen was in the mole ratio 2:1. The samples having the density more than 99% of the theoretieal value were obtained in the higher oxygen and lower hydrogen potential region or in the lower oxygen and higher hydrogen potential region. The criteria thus determined were examined by comparing with the measured potentials in the practical casting machine. In tough-pitch copper casting, the problem due to gas porosity was found to be serious when the hydrogen potential increased. In the. oxygen-free copper casting, the evolution of hydrogen was found not avoided. The gas porosity in the casting, however, was found eliminated when the oxygen potential was kept at a low value.

Jan 1, 2003

By Adriana de Aquino Soeiro da Silva, Joao Alves Sampaioa, Luiz Carlos Bertolino, Francisco Manoel Garrido, Marta Eloisa Medeiros

"Brazil has a large agricultural potential and its production success is related to the chemicaland physical soil characteristics. Therefore, the demand in the use of a great quantity offertilizers to compensate the low amount of nutrients in the soil includes about 40% of foodproduction costs. In order to develop economical alternatives to traditional fertilizers, rockswith potential use in agriculture will be studied. In this work the potassium rock, a greensandslate, will be chemically and structurally characterized for the development of a potassiumthermophosphate. This alternative fertilizer will be obtained based on a fusion of a ponderedmixture of potassium, magnesium and phosphate rocks to be applied in the Brazilianagriculture. Preliminary characterization results indicate that the greensand slate presents ahigh percentage of glauconite, quartz and micas.Keywords: Potassium thermophosphate, alternative fertilizers, greensand slate.IntroductionBrazil has a great agricultural potential and its production success is closely related to thesoil's chemical and physical characteristics. However, the country's soils present lownutrients content and high acidity due to weather conditions. Thus, the use of a high amountof fertilizers makes up for the soils' lack of nutrients and accounts for 40% of food productioncosts. Therefore, research on obtaining new alternative fertilizers is a constant worry due tothe increase on food demand [ 1].The lack of raw material for the preparation of NPK fertilizers in Brazil is a concern and theissue of potassium fertilizers a priority. Such a fact is because in 2008 only 608.000 tons ofKCl were produced, corresponding to just 10% of the Brazilian necessity. Thus, the use ofrocks as agricultural nutrients can contribute to reduce the need for industrial fertilizers.This way, the development of a new agricultural raw material originated from a rock thatalready exists in the country's soil is of great importance for the mineral and agriculturalsectors."

Jan 1, 2011