By R. C. Hubli

Copper (II) chloride has proven to be an efficient lixiviant for copper sulphide ores and secondary sources of copper such as scrap. Nickel sulphides are generally associated with copper ores and copper-nickel matte is an intermediate product of processing mixed sulphides. While the copper species in aqueous chloride media are present as chlorocomplexes, the presence of nickel as Ni++ offers effective separation between the two by solvent extraction techniques. Oxidation of millerite by cupric chloride in sodium chloride solutions has been studied as a function of rate of agitation, leaching time, temperature, acid concentration and total initial cupric concentration. The reaction has a 1/2 order of dependence on initial cupric concentration in the range of 0.0 to 0.5M. The activation energy for the temperature range 333 -363 K has been found to be 59.2 kJ/mol with chemical reaction at the unreacted mineral surface as the rate controlling step. The rate expression, according to the shrinking-core model, for initial cupric concentrations between 0.0 to O.5M, is evaluated as

Jan 1, 1996

By Huaming Yang

The vanadium-doped SnO2 nanoparticle was synthesized by the co-precipitation reaction and subsequent calcination from the vanadium(III) chloride and tin(IV) chloride. The crystal size, pore size distribution, micrograph and properties of the nanocrystalline powders were examined by differential thermal analysis (DTA), thermogravimetric analysis (TGA), X-ray diffraction (XRD), desorption isotherm (Barrett-Joyner-Halenda method) and transmission electron microscopy(TEM). Thermal treatment of the precipitate powder at 600°C led to the formation of V -SnO2 nanoparticle of -10mm in crystal size. Most of the pores in the nanoparticle are about 5~15nm in diameter. Effect of doped vanadium on the crystal size of the nanopartic1e was discussed.

Jan 1, 2003

By William E. Frazier

The presence of minute amounts of sulfur (10ppm) in nickel-base superalloys has been associated with reduced oxidation resistance and the premature spallation of protective coatings. Removal of sulfur by annealing these alloys in a hydrogen atmosphere has been successfully attempted by several researchers. This paper examines the fundamental thermodynamics and kinetics governing hydrogen desulfurization of elemental nickel. Limiting conditions for successful desulfurization are delineated. Assuming that the diffusion of sulfur is the rate limiting process of desulfurization, the effectiveness as well as time associated with hydrogen desulfurization is explored.

Jan 1, 1994

By De-qing Zhu, Jian Pan, Tie-jun Chun, Dong Chen, Yu Cui

"A study of processing pyrite cinder and metallurgical slag using “one step” technology in strand grate - rotary kiln is presented, which aims to efficiently recover the valuable metals of iron, lead, zinc and copper. The effect of chloridizing roasting parameters including roasting time and temperature on the removal rates of nonferrous metals was investigated. It is shown that copper and zinc are difficult to remove and lead is removed more easily. The preheated pellets were reduced in a rotary kiln, where zinc and lead can be removed easily and high iron grade and good metallurgical performance prereduced pellets can be obtained. Furthermore, the chlorination and the reduction mechanisms of copper, lead and zinc are discussed. It is revealed that the phases of copper, lead and zinc in slag are complex and ferrite and silicate of metals are difficult to remove.IntroductionAs two kinds of significant secondary resources, metallurgical slag and pyrite cinder contain not only abundant iron but also considerable copper, lead, zinc and so on. Several tens of millions of tons of metallurgical slag and pyrite cinder are discharged in nonferrous metal and chemical industries annually in China [1, 2]. In addition, the accumulated waste slag in storage is more than one hundred million tons, which not only occupies much land but also pollutes the environment [3]. However, because the metallurgical slag and pyrite cinder are treated by high temperature processing, the properties are distinctly different from the properties of natural ores, and iron is in close association with copper, lead and zinc. So, metallurgical slag and pyrite cinder are difficult to efficiently utilize and only a small amount is used as additives in cement, paving, brickmaking and auxiliary additives [4-7]."

Jan 1, 2011

By Gabriel Plascencia

Copper was oxidized in the temperature range from 300 to 1000 °C under different pressures of oxygen, In the range from 300 to 500 °C, copper oxidizes following the logarithmic rate law; while in the range from 600 to 1000°C oxidation follows the parabolic rate law. Transition from logarithmic to parabolic growth occurs at about 525°C. X-ray diffraction was performed on oxide scales to account for the CuO/Cu2O ratio at different temperatures. Activation energies found in this work are in good agreement with reported values.

Jan 1, 2003

By Yasuhiro Konishi, Yoshiyuki Noda

"This paper describes a new processing of rare-earth oxide precursor, in which rare-earth carbonate powders are precipitated directly from emulsions of rare-earth loaded carboxylate solutions, using CO2 gas and water. This synthetic route of rare earth carbonate is a combined process of the stripping and precipitation stages in a conventional solvent extraction. Using this technique, lanthanum carbonate and yttrium carbonate were prepared at temperatures of 10 to 80°C and CO2 pressures of 0.1 to 3.0 MPa for 120 min. The rates of carbonate precipitation in a batch autoclave were sensitive to processing parameters such as CO2 pressure, temperature, and organic-phase composition. The particle size distributions of the carbonate powders were markedly dependent on temperature and C02 pressure.IntroductionSolvent extraction is the most appropriate commercial technology for separation and purification of rare earths. In typical commercial processes, the rare earths are stripped from loaded solvent extractants using aqueous solutions of mineral acid. After adjusting the pH of the aqueous strip solution, the rare earths are precipitated as insoluble powders of oxalates or carbonates, from which oxides can be produced by calcination. Such conventional processing can be simplified when the stripping and precipitation stages are combined by emulsifying rare-earth loaded solvent extractant with aqueous oxalic acid solution. It is likely that the single-stage precipitation stripping results in a marked decline in the consumed amounts of precipitating and neutralizing agents, thereby saving on both running and capital costs.Yoon and Doyle1) first demonstrated that oxalate powders of lanthanum and yttrium are directly precipitated from rare-earth loaded carboxylic acid solvent extractant when contacted with aqueous oxalic acid solution at ambient temperature and atmospheric pressure. Yttrium oxalate pow4ers were also prepared by precipitation stripping of di-(2 ethylhexyl) phosphoric acid. (D2EHPA) extractant using oxalic acid-hydrochloric acid solutions. 2) Moreover, neodymium oxalates were directly precipitated from organic solutions of tertiary aliphatic monocarboxylic acid and 2-ethylhexyl phosphonic acid mono-2- ethylhexyl ester using aqueous oxalic acid solutions, and powder characteristics of the resulting oxalates were compared with those of powders by the conventional solvent extraction routes. 3 • 4) Recently, attention has been directed towards the influence of processing parameters on the particle size distributions of yttrium oxalate precipitates. 5)"

Jan 1, 2000

By C. Camurri

Results from the Metallurgical Department of Universidad de Conception showed that fire-refined copper could be rolled without previous remelting for deoxidation. The goal of this work is to determine the rheology of fire-refined copper from tensile tests at different temperatures and strain rates, and Ford plane compression tests. All that in order to simulate and calculate rolling process variables. For rheology hardness coefficients, n variables between 0.28 at 600°C and 0.46 at ambient temperature are obtained. The sensibility coefficient for strain rate m varies between 0.056 at 600°C and 0.006 at ambient temperature. The activation energy for plastic flow Q in the considered temperature range is 1436 cal/mol.

Jan 1, 1999

By Zhigang Zak Fang, Michael L. Free, Jaehun Cho, Syamantak Roy, Amarchand Sathyapalan

Leaching characteristics of impurity removal from the Upgraded Titania Slag (UGS) using hydrochloric and boric acids has been investigated. Specifically, this study has focused on removal of iron oxides from the UGS that has been reduced by hydrogen gas and magnesium at 750oC for 5 hours. Reduced UGS is mainly composed of titanium hydride and impurities like iron oxides, silicon oxide, aluminum oxide, and magnesium oxide. The concentration of hydrochloric and boric acids and the leaching temperature have been chosen as the prime variables to identify the optimum conditions and leaching characteristics for removal of iron oxides. It was observed that under the constraint that 1 wt % of titanium hydride loss is the maximum amount tolerable, 0.1M HCl with 1M boric acid and 90oC are the most effective parameters for iron removal from the reduced UGS. Also, the overall rate of reaction seems to follow interfacial reaction controlled kinetics. The calculated activation energy of the reaction is 73.90kJ/mol.

Jan 1, 2016

By Y. Waseda, S. V. Gnyloskurenko

"Present paper reviews the various processes for making of metallic foams. These methods are classified in accordance with the state of initial metals - liquid, powdered and ionized. Liquid metal can be foamed by direct inputting of gas into melt, using gas releasing foaming agents or producing supersaturated metal-gas solutions. This group also includes methods creating voids in the melt. Powder route is based on using powdered matrix metal with foamable precursor materials. Finally Deposition techniques allows making highly porous metallic structures using ionized metal.Experimental study presented shows importance of wettability in bubble formation at gas blowing into melt simulation liquid (water) through holes. Good wettability of injection holes by water ensures formation of bubbles with smaller sizes that effect to the final foam structure.IntroductionOne of the objectives of future production technology is to make of lightweight constructional materials while achieving improved property and good economy as well.The most perspective lightweight materials are cellular or foamed materials that are Wide8pread. in nature and have a growing interest in industry and everyday life.Even metals and metallic alloys can be produced as cellular solids or metal foams beside of the traditional engineering materials such as polymers, ceramics or glass. Recent developments in metal foams, especially aluminium, have produced a new class of lightweight materials."

Jan 1, 2000

By Na Wang, Chao Du, Hongmin Zhu, Kai Huang, Shuqiang Jiao

"Niobium aluminides were directly synthesized by a sodiothermic reduction process of NbC15 - AlCb which was dispersed into LiCl - KCl - NaCl - CaCb melts. The melt supplied a homogenous reaction medium which was substantially beneficial to the co-reduction of Nb and Al to form niobium aluminides in situ. The reduction was performed at 500°C for 4 hours. The products were analyzed by X-ray diffraction (XRD) and scanning electron microscope (SEM). The corresponding results indicated that niobium aluminides powders were successfully synthesized.1. IntroductionNiobium aluminides have received considerable attention as high-temperature structural materials, due to their high melting points, relatively low density, high strength, excellent oxidation and creep resistance [1-4]. Figure 1 shows that there are three intermetallic compounds in the Nb - Al binary [5], which includes Nb3Al (A15 structure, Cr3Si type), Nb2Al (D8b structure, cr-CrFe type) and NbAb (D022 structure, TiAb type). These niobium aluminides have been used in turbine blades or in stationary gas turbines [6-8]. However, despite their attractive features, the ir applications are still limited by the long and costly fabrication process [9, 10].Niobium aluminides were industrially fabricated by the mechanically alloyed process [11-13]. Traditionally, niobium is extracted from Nb2O 5 or K2NbF7 by a metallothermic reduction process while aluminum is produced by the Hall-Heroult process of Ah03 electrolysis. Based on the extraction of Nb and Al, respectively, niobium aluminides is synthesized by a mechanical powder alloying process. The present process for making niobium aluminides requires a set of complicated equipment, has high production cost and time consuming [14, 15].The purpose of this work is to present the simple, economic and direct synthesis of niobium aluminides powders utilizing a sodiothermic reduction from NbC15 - Al Cb dispersed into molten salts."

Jan 1, 2011

By H. Kurokawa

Sumitomo Metal Mining decided to expand copper production capacity of Toyo Smelter and Refinery to cope with the recent copper demand growth in Asia, and to survive by reducing cost. The expansion plan is promoted to increase electrorefined copper production capacity from 270,000 metric tons in 2001 to 450,000 metric tons in 2007. The major changes in smelting section are introduction of the rotary steam dryer, renewal of the feeding system for flash furnace, improvement of the concentrate burner, modification of the flash furnace cooling materials, renewal of the slag cleaning furnace, modification of the flash furnace waste heat boiler, installment of a new converter furnace, enlargement of two anode furnaces. In addition, the gas cleaning system was upgraded and the second acid plant was installed. In the refinery section, the existing tank houses have been operated at high current density of 300A/m2 using the conventional starting sheet cathode technology and moreover a new tank house utilizing the permanent cathode technology was constructed. Although the copper production capacity has been increased, SO2 emission has been kept the lowest in the world through consideration of influence on the environment by expansion project.

Jan 1, 2006

By Hideki Yamamoto

A new technology to convert fluoride gas (C2H2F4 ; R-134a) contained in the exhaust gases from semiconductor manufacturing plants and refrigerators directly into a harmless substance have been established, thus, presenting a new concept for the disposal of fluoride gases such as CFCs that are associated with the global warming. Experimental results verify that chemical reactions with metal compounds can take place at substantially lower temperatures of 700- 800K as compared with combustion. treatment temperatures of 1200-1500K. The reaction product is mainly metal fluoride, which chemically is a harmless material. Furthermore, this process is compact, easily controlled, safe and has low running costs. This paper deals with a new chemical reaction method for the harmless disposal of gases effecting the global warming.

Jan 1, 2003

By G.A Subagyo

The condition of slag in a pyrometallurgical reactor is vital to ensuring control of the process. A new technique based on multivariate image analysis (MIA) of digital images has been developed to provide an online measurement of important slag characteristics, such as the presence of exposed metal, the presence of solid phases, and temperature. This paper shall describe the technique and provide some results from analysis using industrial plant data.

Jan 1, 2003

By Yu. A. Grinin, Yu. A. Sannikov, M. A. Lyamina, V. A. Shumskij, L. V. Slobodkin, N. N. Ushakov

This manuscript describes the Kivcet treatment of lead-bearing materials having high contents of copper and zinc. The tests were carried out on bulk concentrates from the Zyrianovsk Mining and Concentrating complex, "Kazzinc" JSC (Kazakhstan) with the following composition: Pb 37.6%, Cu 10.4% and Zn 6.8%. Two properties of the concentrate were under investigation: their calorific value and their desulphurization rate. By adding flux, the charge properties were brought close to the properties of high-grade lead sulphide concentrate. The charge was melted with high productivity. To ensure high copper recovery, Waelz residue was added to the charge. The residue contained more than 20% carbon and about 30% iron metal. The residue was partially replaced by coke that facilitates high copper recovery into the matte. The smelting achieved a production rate of 20 t/h with one burner. Lead recovery into the lead bullion was 88.8%; copper recovery into matte was 92.3%; zinc recovery into slag was 75.5%; and zinc recovery into the fume was 5.1%.

Jan 1, 2000

By Nobuaki Sato

The electrical conductivity, k, of pure and sodium doped sulfur melts was measured with and without ultrasonic waves at temperatures ranging from 140 to 340'C by the two probe method using an ultra high resistance meter. The k value of the pure sulfur melt with irradiation jumped at around 170°C by an order of 102 after which it mouutuniocally increased from 10-5 to10-4 A' 1 cm-1 with an increase of the temperature. The addition of the sodium metal to the sulfur melt was found to cause a larger jumping in the K value. The k value increased with the increase of Na proportion in the melt. For a 10mol% Na doped sulfur melt it was as high as max ~30 A 1cm -1 above 180 C under the irradiation of of ultrasconics.

Jan 1, 2003

By John Frederick Colloghon, O&apos

Bulong remains the only hydrometallurgical process plant in the world that recovers nickel and cobalt directly from high pressure acid leach (HPAL) laterite leach liquors without need for precipitation of an intermediate product (e.g. sulphide, hydroxide or carbonate). Direct solvent extraction (DSX) of both nickel and cobalt in combination with electrowinning of nickel has been operation at Bulong since early 1999. Focus in the first years has been on ramp-up and resolution of commissioning problems. More recently the focus has been on de-bottlenecking and process optimisation. A number of significant process problems have been resolved, the most difficult being the formation of gypsum in the nickel solvent extraction circuit. Sound control of process chemistry is essential to ensure the production of high quality nickel and cobalt products at the lowest possible cost. This paper describes the numerous changes and enhancements to the process chemistry and plant equipment at Bulong and discusses the importance of ore leach chemistry on downstream impurity metal removal. Potential additional enhancements to further reduce unit costs are also presented.

Jan 1, 2004

TiO2 and Ti/TiO2 thin films were deposited on a quartz substrate by laser ablation of Ti02 and Ti targets using Nd:YAG pulsed laser. After sulfurization of the Ti02 film in H2S or CS2 gas at 1273 K for 1 hour, the surface atomic structure was changed. Furthermore, the Ti/TiO2 film was successfully prepared by the subsequent ablation of Ti and TiO2 targets. The morphology and structure of the films were characterized by XRD, XPS and AFM analyses.

Jan 1, 2003

By J. -C. Tedenac, C. Colinet, X. Tao, P. Jund, R. Viennois

"We report an ab-initio study of the stability and electronic properties of transition metal silicides in order to study their potential for high temperature thermoelectric applications. We focus on the family M5Si3 (M = Ta, W) which is stable up to about 2000 °C. We first investigate the structural stability of the two compounds and then determine the thermopower of the equilibrium structure using the electronic density of states and Mott’s law. We find that W5Si3 has a relatively large thermopower but probably not sufficient enough for thermoelectric applications.IntroductionIn the search of new sustainable energies, thermogeneration of electricity is one of the promising ways, notably because it is able to produce electricity from different kinds of heat wastes and to its portability. However, despite recent progress in the field, the state-of-the art materials have specificities making their mass-production difficult or even impossible: toxicity (thallium, chalcogen or/and pnictogen based alloys), weak abundance (tellurium based alloys) or cost (germanium or rare-earth based alloys). For all these reasons, finding thermoelectric materials without these drawbacks is vital if we wish to use high temperature thermoelectricity for generating electricity in the near future. Due to their abundance, low cost and low toxicity, transition metal silicides are candidate materials of primary interest and the slightest advance in this field would immediately find an application for the thermogeneration of electricity."

Jan 1, 2011

By In-Ho Chi

In copper metallization, resistivity of copper seed layer is very important since the thickness of seed layer is less than 200iun. Conventionally MOCVD has been used for this purpose however electroless copper plating is simple process and the resistivity of copper deposit is less than that of copper prepared by MOCVD. In this study eIectroless depositions of copper were conducted on different substrate to find optimum conditions of electroless copper plating for electronic applications. To find optimum conditions, the effects and selectivity of activation method on several substrates were investigated. The effects of copper bath composition on morphology were investigated. The effects of pH and stabilizer on deposition rate was investigated. The resistivity of copper with thickness was also measured.

Jan 1, 2001

By T. Xin

A vertical grain boundary intercepting a horizontal free surface forms a groove to reduce the combined surface energy of the system. We study grooving by surface diffusion with anisotropic surface energy. A recently developed delta-function model of facets is used to describe the surface energy with three or four fold symmetry. It is found that the groove grows following a similarity law. The self-similar groove profile is solved numerically by a shooting method. Even with strong anisotropy, the groove profile can be smooth if the exposed surface orientations do not include a facet orientation. The smooth self-similar groove shape is the same as an isotropic groove, but the size is reduced by a factor that depends on the degree of anisotropy. This induces a large error on the value of surface diffusivity if the isotropic model is used for an anisotropic system. In this talk. we will describe how to correct for this error.1 I Xin, T. and H. Wong, "Grain-Boundary Grooving by Surface Diffusion with Strong Surface Energy Anisotropy," Acta Materialia 51, 2305-2317 (2003). Keynotes: Grain growth, Surface Diffusion, Surface energy, Anisotropy

Jan 1, 2003