By Y. Ono

In lightweight metal processing such as aluminum (AI) and magnesium (Mg), metal cleanliness is a crucial process parameter for refining, part manufacturing and recycling in order to obtain high quality parts and products. In this paper, techniques for cleanliness evaluation of molten AI and Mg using ultrasonic probes with clad steel buffer rods having high signal-to-noise ratio (SNR) are presented. Due to the high SNR of the ultrasonic probes used, backscattered ultrasonic signals from inclusions, which may be oxide films and/or particles, in molten Mg and those from silicon carbide particles, having an average size of 50f.Ull, added in molten AI are successfully detected with reflection configurations of pulse-echo and/or pitch-catch modes at an ultrasonic frequency of 10 MHz. In addition, relative cleanliness evaluation of molten Al and Mg is demonstrated. In order to establish the procedure and to investigate the optimum system configurations for cleanliness evaluation of molten metals, particle flow simulation system using water and polyvinyl chloride (PVC) particles has been constructed. Counting the number and measuring the size distribution of the PVC particles, having an average diameter of 128um, suspended in water with the PVC volume concentrations of 5ppm and 10ppm are performed with ultrasonic pitch-catch mode. The counted numbers of particles by the presented method and system have good agreement with the calculated results with a count error of less than 10% or two counts. Based on the results obtained with water simulation experiments, the prototype system for cleanliness evaluation of molten Mg by counting and sizing inclusions has been developed. Keywords: Ultrasound, Clad buffer rod, Molten metal, Aluminum, Magnesium, Inclusion detection, Cleanliness measurement, Counting, Sizing

Jan 1, 2003

By N. V. Gorelikova

A new type of zirconium mineralization has been recognized in the Devonian volcanic rocks from an orogenic depression in the Central Kazakhstan. The most characteristic features of this deposit are the fine-grained nature of the zirconium mineralization, an unusual texture of the zirconium ores, and a close association of zirconium with phosphorus in the ores. Zircon grains form fine globular aggregates with the features of hexagonal crystal habit. In addition to crystalline zircon, the ores contain metacolloidal zircon, similar to hydrozircon. The morphological and textural features of the zirconium ores suggest that the deposition of ore deposits took place at a low temperature from colloidal solutions. It is believed that this deposit should be considered to be a new type of zirconium mineralization that is related to low-temperature hydrothermal processes.

Jan 1, 1995

By Sutham Niyomwas

Biomorphic Cellular TiCIC ceramics were produced by vacuum-infiltrating carbon preforms with Ti02 sol and subsequent synthesis by the carbothermal reduction process. The carbon preforms used in the study were obtained by pyrolysis of parawood and neem wood. The effect of infiltration time on the composition and microstructure of the biomorphic TiCIC ceramic was analyzed by X-ray diffractometry and scanning electron microscopy. The biomorphic structure of the TiCIC ceramic is consistent with that of the biotemplate natural parawood and neem wood.

Jan 1, 2008

By A. Warczok

The heat transfer coefficient between liquid slags and solid surfaces is important for the design and operation of metallurgical reactors. An experimental technique developed for the purpose of measuring the heat transfer coefficient between liquid slags and solid metals is described. During the initial heating up of a Ni cylinder upon immersion in a liquid slag, a layer of frozen slag initially forms, then melts. The heat transfer coefficient measured during the initial rapid heat-up of the Ni cylinder, is approximately twice as high as the heat transfer coefficient measured during the final heat-up of the Ni cylinder subsequent of the liquidus temperature of the slag. The technique was tested in various melts i) NaNO3, ii) NaCl, iii) Na3AlF6 and iv) 2FeO*SiO2, giving consistent results. It was found that the heat transfer coefficient increases with increasing bath superheat and stirring. The heat transfer coefficient during the heating up following complete remelting of the frozen slag, is related to the slag superheat(AT) and the specific stirring energy(W) per kg of slag(E) as follows.

Jan 1, 1993

By N. Choi

The distribution behavior of selenium and tellurium in nickel sulfide smelting was investigated in the temperature range of 1250-1300 °C under an inert gas atmosphere and various oxygen partial pressures. The distribution coefficients of selenium and tellurium between nickel-copper-iron matte and silica-saturated iron silicate slag were detennined in terms of matte and slag compositions, temperature, and oxygen partial pressure. The effect of slag additives such as CaO, MgO, and Ah03 on the distribution coefficients of those elements was also investigated. It was observed that the distribution coefficients of selenium and tellurium increased with increasing matte grade and temperature. The solubility of selenium and tellurium in the slag decreased with increasing the partial pressure of oxygen within the range investigated in this study. The distribution coefficients of selenium and tellurium increased with the amount of CaO and MgO. Tellurium distribution coefficients also increased by the addition of Ah03. Meanwhile, the addition of Alz03 decreased the distribution coefficients of selenium at high matte grade.

Jan 1, 1996

By H. Kaffash

Ferromanganese is a ferroalloy with high manganese content which finds many uses for example as deoxidizer in steelmaking industry. However, there is very little data on the dissolution rate of carbonaceous materials in Mn containing metals. In this paper, the kinetic analysis of carburization reactions is investigated for Mn–Fe alloys. Dissolution rate of graphite in pure iron and four different alloys with 10 wt%, 40 wt%, 60 wt% and 85 wt% manganese at 1823 K was studied. Results showed that the dissolution rate of carbon from graphite increased with increasing time for all alloys. The dissolution rate constant increased with the increasing manganese content from 6.5 × 10−3 cm/s for 0%Mn to 23.6 × 10−3 cm/s for 85%Mn.

By M. H. Erten

Most of the fourteen workable coal seams in the State of Missouri have high ash and sulfur levels and need beneficiation in order to meet customer and Environmental Protection Agency requirements. If proper ash and sulfur removal methods can be designed, more Missouri coals will be mined and used within the state. One of the main objectives of this research is to investigate the possibility of removal of sulfur of Missouri coals by conventional beneficiation methods.

Jan 1, 1982

By W. Song, C. Richards, B. Q. Li

"This paper presents a two-phase flow numerical model for spouting gas-particle flow reactors used in chemical vapor deposition processes for manufacturing heart valves and other biomedical implants. The model is developed based on the Eulerian-Eulerian formulation of gas-particle flows, with the k-e engineering model modified with the presence of particles for the description of turbulent gas flows. In parallel with the numerical model development, physical models are set up, where the particle image velocimetry is used for visualizing the particle flows and spout shapes and heights and optical probes are used to measure the particle velocities. The numerical model predictions are compared reasonably well with the experimental measurements.IntroductionVarious biomedical implant components, such as bone joints, dental components and heart valves, are coated with bio-compatible thin films by chemical vapor deposition in particle-laden chemical reactors [l-5]. In these reactors fine particles are used as packing and supporting media. During the coating operation, these packed particles are fluidized by an upward gas jet from the nozzle, reach a certain height and fall back on the top of an annulus region. These recirculating particles are mainly for levitating the implant components (usually one or two in a reactor at one time) so that every portion of them is equally exposed to the gaseous atmosphere. An equal exposure is critical for forming a uniform, mechanically strong and corrosion-resistant coating on implants. Plant experience shows that the quality of the coating is directly related to a stream of operating parameters such as temperature, particle size and loading, and gas flow rates [6]. Optimization of these operating parameters for improved reactor performance depends crucially upon our fundamental understanding of the physics governing the gas-particle flow, heat, and mass transfer phenomena taking place in these reactors."

Jan 1, 2004

By T. H. Courtney, B. R. Murphy

"Nominal room temperature mechanical alloying (MA) has been used to synthesize the high melting temperature NbC and Cu-NbC composites. Elemental powders of Cu and Nb were alloyed in the presence of either graphite or hexane to form nanocrystalline NbC or a Cu-NbC composite. Through control of hot-isostatic-pressing (H/Ping) parameters, we have been able to minimize microstructural coarsening during densijication, and have processed fully dense bulk compacts of both single phase NbC and two-phase Cu-NbC while maintaining a nanocrystalline or near-nanocrystalline structure. These materials generally exhibit high strength and low fracture toughness. However, mechanical properties vary significantly depending upon the Cu content and the method of NbC synthesis (graphite or hexane).INTRODUCTIONMechanical alloying (MA) has been recently used to synthesize a variety of inorganic solids; sulfides (1-2), nitrides (3), borides (4), and carbides (3, 5-8). One advantage of this processing route is that synthesis of fairly high melting temperature materials takes place at what is nominally room temperature. Another advantage is that the structures generated are often nanocrystalline in scale, with attendant interesting properties. The consolidation of these fine structures into near fully dense or fully dense materials while limiting microstructural coarsening is a challenge that has just recently seen limited success (5, 9). We report here on some recent studies of ours dealing with crystallite size and structural analysis of NbC and CuNbC composites consolidated to full density from mechanically alloyed powders. Bulk mechanical properties and their dependence on milling parameters are also presented."

Jan 1, 1994

By K. Nona C. Liddell

There is a significant amount of early work that has been largely forgotten that deals with the validity of the pseudo-steady approximation for liquid-solid reactions. Much of this was originally published in the chemical engineering literature but is highly relevant to hydrometallurgical processes. The purpose of this paper is to summarize some criteria that were been developed by various authors for determining the error associated with use of shrinking core models for liquid-solid systems.

Jan 1, 2002

By S. Neven

The smelting of copper anode slimes, a material which contains mostly lead, silver, copper and selenium, has been practiced for many years with a view to recovering the silver and associated small amounts of gold. However, a theoretical understanding of the process has been lacking and this handicaps efforts to improve and intensify smelting operations. In the past few years work has been done in this area and this work will be reviewed in the paper. The underlying thermodynamics of the oxidation of silver-copper selenide mattes has been developed and used as a basis for the construction of a computational thermodynamics model which attempts to predict the composition of all condensed phases during the course of smelting. The model will be outlined and its successes in matching experimental data, as well as its current deficiencies, will be considered. Supporting work on the thermodynamics of silver solubility in slags, on activity-composition relationships in the Ag-Se system and work in progress on the oxidation state of copper in the slags will be reviewed. These projects are designed to provide further detailed data which will improve the robustness of the thermodynamic model.

Jan 1, 1999

By Felipe Daroch, Maria C. Ruiz, Rafael Padilla

Copper concentrates with high arsenic contents must be pretreated before conventional smelting to prevent environmental pollution with arsenic compounds. In this work, experimental results concerning the selective removal of arsenic and antimony from copper concentrates are presented. The process consists of an alkaline digestion using concentrated NaHS-NaOH solutions to transform the arsenic and antimony sulfides into soluble compounds. A water leaching follows the digestion to dissolve the arsenic and antimony, leaving clean copper sulfide solid residues. The laboratory scale tests were carried out using a copper–arsenic concentrate with 15.05% As and 1.42% Sb. The results showed that the most important digestion variables were temperature and concentrations of NaHS and NaOH. Over 97% of arsenic and 92% of antimony could be removed in 10 min of digestion using 8.9 M NaOH and 100% excess of NaHS at 80 °C. The subsequent water leaching was performed at 80°C for 20 min.

Jan 1, 2015

By John J. Mazza

Treatability studies were performed to determine the effectiveness of two commercially available treatment methods (solvent extraction and thermal desorption) for the removal of PCBs and PAHs from contaminated dredged riverbed sediments. The solvent extraction method evaluated was the B.E.S.T. process which extracts the contaminants with triethylamine. The thermal desorption method utilized was the ATP process which desorbs the contaminants at elevated temperature in an anaerobic atmosphere. A description of both methods and. an evaluation of the treatability study results is provided. Each treatment method was used to treat two separate samples (high and low concentration) from the site. Overall, both methods proved to be very effective with solvent extraction achieving 98% removal of both PCBs and PAHs and thermal desorption achieving better than 99% removal of both the PCBs and PAHs from the high concentration sample. Both solvent extraction and thermal desorption achieved greater than 99% removals of PCBs and PAHs from the low concentration sample. Vendor cost estimates for full scale treatment were roughly equivalent. The primary differences between the two methods lies in the realm of permitting, operational requirements, and emission concerns.

Jan 1, 1994

By Marcos Paulo Kohler Caldas, Jorge Alberto Soares Tenório, Mariana Alves de Carvalho, Denise Crocce Romano Espinosa

The massive application of electrical and electronic equipments increased the production and industry development, which leads to a rising envronmental and economic problem: the increase of e-waste’s generation. The main cause to explain this problem is the combination between the diversification of electric and electronic device’s applications and programmed obsolescence, which promotes a high generation the so-called waste electrical and electronic equipments (WEEE). Printed circuit boards (PCBs) are present in almost all WEEE and their heterogenous composition have a considerable amount of metals, including some preciousones. It is necessary to think about viable alternatives for the destination of WEEE, mostly PCBs’. Recycling is an environmental friendly purpose for PCBs’ destination, combined with economic advantage from the recovery of metals. The choice of correct process to recycling depends on the composition of the PCBs, so the correct characterization is required. This work aims to characterize two different PCBs from obsolete computers: motherboard and memory board, concluding that they have 35.5 and 18.92% of metals, respectively, including precious metals as silver and gold. Also, memory board has 0.122% of these precious metals to the detriment of 0.047% from motherboard. )

Mar 1, 2018

By V. M. Mukhin

Among the methods proposed for spent activated carbon regeneration, the most acceptable is, thermal reactivation, because in this case the existing equipment for manufacture of activated carbon can be adapted for this purpose. In order to conduct the process of thermal re-activation of spent activated carbon directly at gold mills, a full-scale drum-type furnace with external electric heating has been developed, i.e. EPV-300 model with a throughput rate of 50 to 120 kg/hour. Its use ensures restoration of the adsorption properties of carbon up to the level of fresh activated carbon with an insignificant (by 0.7%) decrease in strength and with a high (95% to 97%) yield of reactivated carbon. During the recent years, activated powder carbon has been extensively used in flotation processes for treating polymetallic ores at ore treating plants to improve recoveries of main metals (copper, lead, nickel, etc.). Especially large volumes of activated powder carbon are used at the Talnakh concentrator of the Norilsk Mining and Metallurgical Complex in Russia for absorption of residual flotation reagents from recycled water in order to ensure efficient selective separation of minerals with similar physical and chemical properties.

Jan 1, 2006

By Stephan Mulch, Christian His, Patrick M. Stephan, Thibault Champion

"When fuel costs increase dramatically, waste to energy (WTE) conversion technologies become a good alternative to produce energy. The potential energy available in domestic wastes, in developed countries, could be upwards of 4% of their total energy needs. Due to low energy recovery and low level of treated domestic wastes in many countries, the energy coming from waste is generally less than 0.5% of the country needs.Domestic waste incineration can convert heat to electricity for industry and housing and allow waste volume reduction in countries where land fills are a scarce resource.There is a request to improve existing combustion technology by increasing energy recovery with better heat transfer in the boiler and also by increasing lining durability with more resistant materials and technologies.The knowledge of corrosion phenomena and material performance allows Saint-Gobain Group to develop and propose high performance refractory lining solutions.IntroductionThe interest in alternative energy has been growing dramatically in the two last decades due to several combined factors, such as global energy demand, fuels prices evolution (e.g. crude oil, Figure 1) or environmental and geopolitics factors"

Jan 1, 2008

By Guo Chang Jiang

In order to improve the IIAZ toughness of X-60 pipe steel, the intragranular ferrite plate (IFP) technology was used. The characteristics of IFP is claimed to be much fine ferrite plates appear inside the original austenite grains. By means of suitable Re, Zr, Ti additions in a bath with a higher initial oxygen potential, a good control of the peak temperature and the cooling rate during welding simulation, one can get a %IFP in volume over 50%, and the toughness gets up from 55 J to 160 J. It was found that the inclusions most effective in nucleating IFP are some deformable complex silicates which either entrap Re, Zr, Ti oxides or contain these elements. The greater the number of the evenly distributed and effectively nucleating inclusions, the more the %IFP in volume, and the finer the microstructure of the HAZ, so the better the relevant toughness. Generally, these silicates bahave as fine spheres along a line. The present authors revealed that these fine spheres result from the remelting of the shuttle- like silicates due to heating in the process of welding simulation. These silicates used to get a higher sulphur capacity, so MnS deposits might be observed on the periphery of the silicates. IFP was proved to be directly rooted in the [Mn] depleting zone which locates beside MnS deposits.

Jan 1, 1997

By Yuzhe Zhang, Xiaodi Huang, Xinli Wang, Bowen Li, Matthew Andriese, Jiann-Yang Hwang, Zhiwei Peng, Likun Li

With the development of the world, the waste tires have been a serious environmental problem. There are about 2 billion waste tires produced all over the world every year and about 500 million waste tires are produced in the United States. Most of the waste tires are land filled, which waste a lot of space. It takes hundreds of years to resolve the macromolecules of waste tire into the standard which does not pollute the environment. Microwave irradiation is a thermal processing way for waste tires decomposition. In this study, the relative dielectric loss factor of the tire at various temperatures was determined to understand the behavior of tires under microwave heating.

Jan 1, 2016

By Toshiaki Tsuru, Takeshi Ohgai, Hisaaki Fukushima, Shigeo Kobayashi, Tetsuya Akiyama

"Electrodeposition behavior of Zn-Cr alloys from the methanol baths was investigated. In the methanol baths of low Cr3+ concentration, Cr (III) compound was incorporated in the deposits and no lusfrous Zn-Cr alloys was deposited. However, Cr was existed as metallic state in the deposits obtained from the baths of higher Cr3+ concentration. With an increase in water content in the baths, the chemical state of Cr in the deposits changed from metallic to trivalent state. Under the condition that metallic Cr can be electrodeposited, Zn deposition was significantly polarized to the potential of Cr deposition.INTRODUCTIONAn attention has been paid to Zn-Cr alloy plated steel sheet because of its excellent properties for body panels of automobile and electrical appliances [1]-[4]. This plating process can be operated using the sulfate solutions containing Cr3+ ion [1] - [6].In decorative single Cr plating, on the other hand, many attempts have been made to electroplate Cr from trivalent electrolytes, which is motived by environmental deficiencies of the presently used hexavalent process [7]. [8]. However, it has been reported that in the aqueous solutions the behavior of the electroreduction of 0 3+ is atypical due to the complicated nature of the chemistry and electrochemistry of cr3+ species [9]-[11]. Even in Zn-Cr alloy plating, it is difficult to codeposit metallic Cr with Zn in simple sulfate electrolytes [l]-[4], [12]. Therefore, it can be expected that the electrodeposition behaviors of Zn-Cr alloys as well as Cr are significantly changed when the electrodeposition is conducted in non-aqueous plating solutions.In this study, the electrodeposition of Zn-Cr alloy was conducted from methanol solutions to clarify the electroreduction mechanism of Cr3·-Cr0 in the alloy deposition process."

Jan 1, 2000

By Sevinc Yildirim, Cigdem Oruclus

"Metal-Porous Silicon (PS) based structures dipped in water show the direct hydrogen fuel cell behavior. The effect of the thickness of the cupper (Cu) film on the electrical properties of direct hydrogen fuel cell is studied by fabricating Cu/Porous Silicon/n-Silicon/Indium structures. PS samples were produced electrochemical etching of n-type single crystalline silicon with a resistivity of 1,25 Ocm and (111) orientation. The thin films of Cu with different thickness between 200 and 600 nm were deposited on PS surface by electron-beam technique. Investigation of the effect of Cu layer on the performance of the structure indicates that the performance parameters such as open circuit voltage (Voc) and short circuit current (Isc) strongly depend on the Cu layer thickness. It was observed that the divice with an 350 nm Cu layer exhibits the highest open circuit voltage (0,5 V), short circuit current (0,01 mA) and power density (10 W.m-2).IntroductionHydrogen is the most attractive and ultimate candidate for a future fuel and an energy carrier. Hydrogen is recognized as the environmentally desirable clean fuel of the future since it can be used directly in different types of hydrogen fuel cells [1]. In the past years, the rise in portable electronics requires the development of miniature fuel cells compatible with standard silicon micro fabrication technology. Most silicon micro-fuel cells have used the polyperfluo-rosulfonic acid membranes (Nafion R) as a proton exchange membranes (PEM) that is not really integrated with standard micro fabrication techniques [2-5]. The composite materials such as inorganicorganic hybrid materials (Nafion-silica, Nafion-borosiloxane etc) are next generation of proton conducting membrane [4-8]. But, fuel cells run on pure hydrogen gas, which can be produced with other energy resources. Hydrogen smallest atom and thus the H2 gas can leak easiliy. The application of hydrogen for power sources has been greatly restrained due to the lack of safe and convenient generation and storage methods.A kind of hydrogen fuel cells Metal-PS-Si structures used as an energy water directly. There is no need pure hydrogen. Cu-PS-Si Schottky-type fuel cells with as proton-conducting membrane and the thin-film cupper catalist and water as fuel, which are interesting for fabrication of lowcost miniature fuel cells. Generation of the open-circuit voltage and short-circuit current has been observed by Cu-PS-Si structure dipping in different hydrogen-containing solution."

Jan 1, 2014