By S. Chama, P. Chishimba, Tina Chanda Phiri, J. Machona, S. Parirenyatwa, G. Kaluba, Y. R. S. Hara, D. M. Musowoya

The investigation focuses on leaching of copper (2 wt%), cobalt (0.5 wt%) and iron (2.4 wt%) from complex tailings material from the Democratic Republic of Congo. The highest recovery of copper and cobalt into the leach solution were 78 and 10%, respectively, under direct leaching with sulphuric acid. Higher recoveries (90% for copper and 96% for cobalt) were attained when the material was pre-reduced with coal for 1.5 h in the temperature range of 700–950 °C. The increased recoveries were due to metallisation of all the copper and cobalt which is in the silicate matrix. The effects of pre-reduction temperature and sample to carbon weight ratios were analysed and found to be important in; (i) achieving high recoveries of copper and cobalt and (ii) decreasing the amount of iron in the leach solution. The samples were characterised by atomic absorption spectroscopy and scanning electron microscopy (SEM) techniques.

Mar 1, 2017

By Jiang Feng, Zhang Libo, Peng Jinhui, Guo Zhanyong, Ju Shaohua, Lei Ting

The clean utilization of the residue containing chloride, CuCl residue, produced from zinc hydrometallurgy is very important for the recycle of valuable metals. And drying is the main process in recycling. In this study, response surface methodology was used to optimize operating conditions of the drying of CuCl residue in a convection oven and desirability function used as the methodology for the optimization. Optimization factors were air temperature (80–100°C), material thickness (10–25mm) and process time (80–120min) while investigated responses was final moisture content. The optimum conditions were found to be the temperature of 95.48°C with the material thickness of 13.47mm for the process time of 89.48 min. Under optimum conditions, the predicted moisture content of CuCl residue was 4.11% while the experimental date was 4.13%. The experimental value after process optimization was found to agree satisfactory with the predicted value. After drying, XRD was used to analyze the main phases of CuCl residue. The CuCl residue is made up of CuCl,Cu2O, ZnS and other compounds.

Jan 1, 2015

By M. R. Baren

Unpublished results obtained by Baren on thermodynamic properties of sulfur in liquid Fe. Co. Ni. Fe-Co. Fe-Ni. and Co-Ni are reevaluated. correlated. and interpreted on the basis of recent developments in thermodynamics of alloys:. Existing reliable data are reviewed and compared with the? present results. Sulfur obeys Henry's law up to 0.04 mol fraction. and in this range the standard Gibbs energy of solution of sulfur is expressed as a linear function of temperature for each pure metal. The activity coefficient of sulfur in each binary metal solvent 1s correlated with the composition of alloy.

Jan 1, 1983

By S. Chama, K. Nyirenda, J. Machona, P. W. Chishimba, S. Parirenyatwa, G. Kaluba, Y. R. S. Hara, D. M. Musowoya

Our study focuses on upgrading of copper and cobalt from the Democratic Republic of Congo tailings, containing 2 wt% Cu and 0.5 wt% Co. Cobalt is in the complex iron silicate matrix such that its recovery by direct leaching is not possible. Two concentrating methods were employed in order to obtain copper and cobalt concentrates. Copper was concentrated via flotation and, at the optimal conditions its grade in the concentrate was 31.9 wt%. Cobalt was concentrated to 8.6 wt% b ycarbothermically reducing the flotation tailings with coal in a temperature range of 800–1050 °C and followed by magnetic separation. The reaction products were analysed by atomic absorption spectrometer (AAS) and scanning electron microscopy (SEM) techniques. The best carbothermic reduction temperature was found to be 950 °C due to maximum metallisation and less sintering between gangue and metallic/alloy phases.

Mar 1, 2017

By Qian Li, Li-chen Hou, Yong-bin Yang, Tao Jiang, Jian-jun Hu, Bing Xu

Extraction of gold from refractory gold concentrates usually requires an oxidation step to remove arsenides、sulphides and carbonaceous matter. In this investigation, the gold concentrates were two-stage roasted under different atmospheres and temperatures. Results indicated that at the first stage, under neutral atmosphere, the removal rate of arsenic increases as the temperature rises. Under the oxidizing atmosphere, with the increase of temperature, arsenic content in the residued calcine increases, in addition, the volatilization of arsenic is also affected by the oxidation of carbon that generated CO, which is advantageous to the decomposition of arsenate decomposition. At the second stage of roasting, it is the higher temperature and stronger oxidizing atmosphere, the faster sulfur and carbon oxidated rate is, but at the same time, the calcine appears the phenomenon of consolidation because of the phase of silicate compounds generate.

Jan 1, 2015

By Hebi Yin

A coupled cellular automaton (CA) - finite element (FE) model was developed to calculate the growth of dendrites during the solidification of cubic and hexagonal metals. The model solves the conservation equations of mass, energy and solutes in order to calculate the temperature field, solute concentration and the growth morphology of dendrites, including the grain structure and the dendritic microstructure. Validation of the model was performed by comparing the simulation results with calculation results from previously published works, showing qualitatively good agreement in the dendritic morphology. Application to magnesium alloy AZ91 illustrates the difficulty of modeling dendrite growth in hexagonal systems, observed as deviations in growth direction caused by mesh-induced anisotropy. The model was applied to the simulation of small specimens with single- and multiple- equiaxed grain growths and columnar grain growth in directional solidification. The influence of cooling rate and some kinetics parameters on the grain morphology are also discussed.

Jan 1, 2009

By S. A. Davis

In July of 1996, the Kroll process began production again at TIMET's Henderson, NV, manufacturing facility. This, after being shut down for several years due to low market demand for titanium. Faced with limited pond capacity and increasing costs for water and wastewater disposal and storage; process changes were made to recycle water used to wash Kroll titanium sponge back into the sponge leaching process. This idea was revisited from 1992-93, when three consecutive attempts to recycle water for this application were unsuccessful due to early pump failure. Since it was uncertain why previous attempts failed, a complete understanding of the existing system was first sought. This included reviewing piping and flow diagrams; taking field measurements for all the piping, valves, and fittings; analyzing the wastewater composition; and modeling the fluid dynamics and control of the system. The fluid dynamics of the system were modeled by breaking the piping network up into nodes and applying the Bernoulli equation to each segment. The fluid flowrate control valves were modeled for this purpose also and the models were used to help specify the required processing equipment and control ranges and tolerances. Once the project was completed, an operating procedure was prepared for operation, startup, and shutdown of the washer water recycle system.

Jan 1, 1999

By Guangliang Wu, Dongchang Huang, Xinbin Liu

Oxidation Kinetics of SPHC was analyzed by TGA, and the curve of oxidation weight gain with different temperature was acquired. It is found that, when the oxidation temperature is between 500 and 600 , all the curves are linear; when the oxidation temperature is above 700 , the curves are close to parabolic. At the temperature of 900 , the oxidation weight gain increases dramatically. The TGA results indicate that the activation energy of SPHC steel is 146.19 kJ/mol at the temperature of 500 900 , and an oxidation kinetic model was set up for variable temperature. Based on the temperature change during rolling process, numerical simulation of oxide scales evolution was carried out for SPHC steel, and the simulation result agreed well with measured ones. It can provide a basis for estimating the scale growth and controlling the temperature on site.

Jan 1, 2016

By Pan Gu, Zhen Zhang, Jiang Diao, Bing Xie, Hongyi Li

Furnace refractories are in most cases chemically incompatible with smelter slag, which leads to a steady erosion in their thickness over time. Once too thin, refractory walls become mechanically unstable and catastrophic failure can result. Historically, external shell cooling was applied to generate a freeze lining of slag and thus prevent refractory erosion. Many modern high intensity smelting furnaces instead maintain their physical integrity by the use of internally cooled wall panels, plates or finger coolers. An initial refractory lining is often installed inside of the coolers, such that the furnace originally operates with a temperature (insulated) rather than a heat flux (freeze lined) boundary condition. This paper examines the change in slag-wall heat transfer coefficient and slag superheat as a function of process intensity. The implications of the changes in heat transfer on residual brick thickness are explored using analytical modelling.

Jan 1, 2016

By Xiangwen Wang

Electrochemical measurements associated with the electrowinning of lead metal from concentrated brine (NaCI) - lead chloride (PbCI,) electrolytes at temperatures in the range 328 to 353°K (55 - 80°C) were conducted. The electrodeposition of lead metal onto a lead rotating-disk electrode may be described by the electrodic reaction: {PbCl 4 2 + 2e- = Pb° + 4Cl-} The deposition-overpotential requirements are low (approximately 41mV per decade of current density - Am+), with a corresponding high exchange current (approximately 0.018 A.cm2). The diffusion coefficient of the electroactive PbC142- species in a 3.5 NaCl electrolyte at 353°K was insensitive to the total PbCI, concentration (0.01 to 0.1M), and its value was found to be (1.21*0.1)~10-5 cm2Is with a temperature-sensitivity coefficient (E,/R) of approximately 1.98x103K-1 (328OK(T<353OK).

Jan 1, 1993

By H. Ikeda

The new Onahama N0.3 tankhouse was put into operation early in 1973. This new tankhouse, which has a capacity of 90,000 metric ton cathode per year, is distinct in many important respects from conventional tankhouses. The major objectives in design were to simplify the construction and ope- ration for reduction of the costs for labor, interest and depreciation and also to reduce the copper inventory in the tankhouse by the use of conti- nuously-cast anodes. As a result, the investment cost was decreased by approximately 30% and the inventory cost by approximately 600, while the production per unit area of the tankhouse was increased by 80 - 100% as compared with the existing conventional-type tankhouses at Onahama. By abolition of cell inspection and maximum mechanization of materials handling the labor cost was decreased by as much as 80%. On the other hand, the new system has some disadvantages, such as increase in anode scrap ratio and increased cost of anode casting. The No.3 tankhouse system is, however, still at its starting point, while conventional methods have been continuously improved over the past years of operation. It is expected that the innovational ideas behind this system will serve as bases for a more efficient electrolytic refining system in future.

Jan 1, 1976

By Run Huang, Xuewei Lv, Lei Lei, Guibao Qiu, Chenguang Bai

"The TiO2-rich slag and pig iron can be produced from ilmenite concentrate by the electric furnace process. In this study, ilmenite concentrate was reduced in a vertical furnace equipped with a weighting data acquisition system. The effects of reducing agent (carbon) amount on the iron reduction were studied. The phase transformation, morphology and chemical compositions of reduced samples were investigated by X-ray diffractometry (XRD), scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS), respectively. It was found that the reductive degree of ilmenite concentrate increased with the increase of reducing time. The phases of reduced samples were mostly iron, rutile, Ti3O5 and Fe2TiO5. The mass loss percentage increased with increasing the carbon amount from 8% to 12%. When the carbon amount exceeded 12%, the mass loss percentage decreased with the increasing of carbon amount.IntroductionIlmenite and rutile are the main raw materials for producing titania pigment and titanium metal. With the development of the titanium industry, huge amounts of titanium resources are needed. As sources of high-grade titania mineral decrease worldwide, more attention should be paid to the processes involving low grade mineral such as ilmenite ore. In ilmenite, MgO and CaO are the gangue parts. Therefore, the ilmenite refining becomes more and more popular. In the previous studies, the methods of ilmenite refining are electric furnace smelting, direct acid leaching, selective chlorination and thermal reduction [1]. Electric furnace smelting method is widely used in the titanium industry, however, which consumes a great deal of energies and has a high CO2 emission. Its essence is to remove iron oxides and obtain a high titania slag. So the thermal reduction of ilmenite concentrate is an important step in titanium industry, which can decrease carbon reagent consumption and save energy.Over the past several decades, many studies have been carried out on the mechanism and kinetics of the reduction of different ilmenite ores, which are as follows: The carbothermal reduction of Panzhihua ilmenite initiated at about 860 oC. In the temperatures ranging from 900 oC to 1400 oC, the reaction rate was changed like a shape of “M”. That was to say that the reaction rate increased with the growth of temperature at first, then decreased, afterward increased again and at last the reaction was arrested [2]. The Mohammad A.R group [3, 4] showed that the carbothermal reduction of primary ilmenite concentrate was faster in hydrogen and initiated at a lower reduced temperature than in argon and helium. The reduction in argon and helium had about the same rate and extent. Titanium oxycarbide started at 1000°C in hydrogen. The conversion of primary ilmenite concentrate to metallic iron and titanium oxycarbide at 1200 °C was completed in 300 minutes. Monoxide as the reductant to reduce ilmenite had been studied intensively by a few research groups [5, 6]. The rate and the degree of reduction depended on the formation of a metallic shell of iron which inhibited the transfer of CO to the reaction zones; titanium had a strong effect on the mechanism and rate of reduction of iron oxides. Wang and Yuan [7] studied the reductive kinetics of the reaction between a natural ilmenite and carbon. At temperature below 1100°C, chemical reaction was the rate controlling step, at 1100 to 1250°C mixed controlling was rate controlling step, above 1250°C diffusion through the product layer controlled the reaction. Zhang [8] investigated the reduction of natural, sintered and preoxidized ilmenite concentrates in hydrogen methane mixtures. Preoxidation and sintering of ilmenite concentrates changed their phase composition and caused a sharp decrease in specific surface area of raw materials and an increase in carburization temperature. Sintering also increased the metallization temperature of iron."

Jan 1, 2011

By Gus Van Weert

The cost of oxygen is a major and common factor in the hydrometallurgical processes developed or proposed tor the oxidation of refractory pyrites. This cost involves charges for the generation and the transfer of the 02 to the mineral slurry. Bio-oxidation faces considerable design demands which require large scale equipment to be resolved. Nitric acid assisted oxidation offers low cost oxygen units; this method of pyrite oxidation deserves a closer look for large scale plants treating pyritic gold ores and concentrates.

Jan 1, 1990

By Guohua Bai, Yuanbo Zhang, Guihong Han, Zijian Su, Daoyuan Zhang

"Specularite ores have poor hydrophilicity and ballability as well as inferior high-temperature reactivity, which restrict the large-scale application of them in the pelletizing and sintering production. Modified humic acid (MHA) organic binders are firstly used for pellet preparation from specularite in this paper. The results show that the drop strength of green pellets is 3.7 times/0.5m and compression strength is 12.5 N/P by using 1.0 wt% MHA as binder. Under the optimal experimental conditions of preheating temperature 980 °C, preheating time 12 min, roasting temperature 1280 °C and roasting time 10 min, the preheated pellets have the compression strength more than 400 N/P, and that of roasted pellets is 2747 N/P. The strength of finished pellets meets the requirements of blast furnace iron-making. MHA is a kind of more effective organic binder for specularite pellets compared with the inorganic bentonite.IntroductionAcid Pellets have advantages of good strength, uniformity particle size, high iron grade and good reducibility, which can be used as high-quality burdens for blast furnaces [1]. With fast development of Chinese iron and steel industry domestic magnetite concentrates with high grade of iron and good firing performances become shortage.Imported specularite ores have advantages of low price and high grade of iron (generally above 67 wt%), so the application of them in pellets is an effective way for sustainable development of pellet industry in China. However, the specularites have not been utilized in pelletizing and sintering at present because of the poor ballability and high-temperature reactivity [2, 3]. Most of the pellet plants use bentonite as binders, the amount of which is about 2~3 wt%. The pellet production practice shows that 90 wt% bentonite is still residual in finished pellets and reduces the iron grade [3]. Developing a new organic binder instead of bentonite is very important to the high-quality pellet production. On one hand, the consumption of bentonite is obviously reduced, resulting in decreasing the ironmaking coke ratio and slag discharge; On the other hand, the iron grade of finished pellets are improved, which brings the benefit for the ironmaking production."

Jan 1, 2011

By Mohamed Y. Bakr, Aly M. Abdel-Rehim

The present work is related with mechanical activation of processing of Egyptian wolframite by simultaneous ball-milling and pressure alkaline leaching, to improve the recovery of tungsten from wolframite. The results show a total recovery of tungsten from wolframite (97.8- 98.7%) by simultaneous ball–milling and alkaline leaching at temperature 175-200oC. It is concluded that processing of wolframite by simultaneous ball- milling and leaching is mechanically activated and accelerated as a result of the grinding action of steel balls that caused the immediate rupture by continuous removing the product layer of the reaction ( sodium tungstate and iron and manganese hydroxides ) from reacting particle surfaces. This leads to the exposing of fresh and activated wolframite particle surfaces to alkaline leach solution and consequently the acceleration of the reaction of wolframite leaching .The results of the kinetic study 0f alkaline processing of wolframite and its mechanical activation show that the system is under kinetic control.

Jan 1, 2015

By Bowen Li, Canhua Li, Mingsheng He

Steelmaking slag is a by-product in considerable volume and a valuable material for various applications. In general, steelmaking slag is an alkaline compound of CaO, Fe2O3, and SiO2. However, its characteristics varies depending on the feedstocks, steelmaking process and cooling method of the slag. To utilize this by-product effectively, this study investigated the characteristics of steelmaking slags taken from Wuhan Iron & Steel Co. Ltd. The results showed that the slags mainly consist of the oxides of calcium, iron, and silicon, with low contents of magnesia, alumina, and manganese oxide with a feature of high alkalinity and lime saturation factor. The major mineral phases include belite, calcium ferrite, calcium hydroxide, wustite, quartz, and small amount of elite. Thermogravimetric analysis indicated the weight loss from ambient temperature to 800 °C is 8% in total. Melting test showed the glass transition temperature is between 1300 and 1350 °C, flow temperature is about 1400 °C. The slag samples investigated in this study can be considered as a typical glass-ceramic composite.

Mar 1, 2018

A simulation of a capper concentrate smelter was built with a capacity of 450,000 tons per year. The system&apos;s components to simulate were three : a Reverbetory furnace, a Wiente &apos; s modified converter ( TMC ) and two cranes. The system was classified as dynamic, stochastic and discrete. In the simulation language choice it was concluded that the most advantageous one was GPSS/H. The model verification was done through the interactive Debugger that the language has and the statistical validation was done through the result variables of sane activities, that as a whole characterize the system (charged matte and charged concentrate to the TMC, skimming white metal and skimning slag). The validation was done comparing the simulation results of these variables with the ones obtained for those variables in a specific month in the smelter. The comparison consisted in a difference of means test and in all cases the equality was accepted with a 95% of confidence. The animation tool was PROOF, a general purpose animator, that is used after processing the simulation.

Jan 1, 1994

By Yuanbo Zhang, Mingjun Rao, Guanghui Li, Chongzhong Ouyang, Shuhui Zhang

Oolitic hematite ore with high-phosphorus content is currently recognized as one of the most refractory iron ore resources in the world. The high-phosphorus content and unique structure of the oolitic hematite ore make it difficult to be beneficiated. The process of direct reduction followed by magnetic separation has significance to the utilization of oolitic hematite ore, and sodium salts can improve the dephosphorization. However, the behavior of phosphorus during reduction roasting, and the intensified dephosphorization mechanism of sodium salts are not clear. In this study, by using chemical analysis, chemical phase analysis, XRD analysis, optical microscopy, and scanning electron microscopy analyses, the behavior of phosphorus during reduction roasting of high-phosphorus content oolitic hematite ore and the effect of sodium salts on behavior of phosphorus were studied.

Jan 1, 2015

By Caisa Samuelsson, Taishi Matsushita, Hannes Holmgren, Sina Mostaghel

"Rönnskär Smelter of Boliden Mineral AB, Sweden, is a large end-processor of secondary raw materials and waste, including electronic scrap. Electronic scrap may introduce various impurities to the smelter's flow-sheet, among which alumina is a common and significant one. This article summarizes the results of an ongoing research at Luleä University of Technology, Sweden, to study the influences of alumina on different properties of slag from the zinc fuming process at Rönnskär smelter. A combination of different experimental techniques and thermodynamic calculations have been used to investigate properties such as density, surface tension, effective thermal diffusivity, viscosity, and melting/leaching behaviors. Results show that the addition of alumina to this slag increases the degree of polymerization of the melt, and physical properties vary correspondingly. Mineralogy of the semi-rapidly solidified samples is also changed due to alumina addition. A correlation between mineralogy and leaching behavior can be observed.IntroductionBoliden's Rönnskär Smelter is a base- and precious-metals producer located in north of Sweden. Its main products are copper, zinc clinker, lead, gold, and silver. Sulphuric acid, liquid sulphuric dioxide and iron sand (granulated slag) are some of its main by-products. In order to optimize the overall outcome of the process, different refining units are integrated in the smelter's flow-sheet (Figure 1). Copper concentrates and fluxing materials (mainly silica sand) are charged to the process. The produced matte is sent to the converter and the generated slag is charged to the fuming furnace, where it is treated by reducing gases to produce zinc clinker. The converter's slag is charged to the electric furnace, while the fumed slag is tapped into the settling furnace for further cleaning, where matte, slag and speiss (residual metals) are separated. The matte from the settling furnace is also sent to the converters; its speiss is sold to external customers; and its slag is water granulated and sold as construction material, which is known as iron sand."

Jan 1, 2012

By Onuralp Yucel, Osman Halil Celik, Hakan Morcali

In this study, some experiments were performed for the dimensional control, pre-treatment, getting salt, metallic aluminum and aluminum oxide into the solution of 15 kg aluminum black dross obtained from a private company which recycles aluminium drosses. Water leaching experiments are done for removing salts and aluminum nitride. Temperature stirring speed, solid-liquid rate are investigated while water leaching experiments. Removing of AlN is provided at 25 °C at a rate of 42.48%, at 80 °C at a rate of 86.4%. Leaching experiments performed with NaOH. NaOH concentration and time was analyzed. Efficiency of including metallic aluminum into the solution is determined to be 98% approximately. Melting (fusion) experiments were performed with NaOH at high temperatures to include aluminum oxide in the structure of the remaining after dissolving process into the solution and after dissolving the resulting structures in water, efficiency of including aluminum into the solution is determined to be 85%.

Mar 1, 2018