By Douglas J. Harvey

The surface tension of lead-tellurium alloys (in the range 0 to 6.70 at. pct Te) ad lead-arsenic alloys (in the range 0 to 10.53 at. pct As) has been examined by the maximum bubble pressure method. The surface tension of high purity lead can be expressed over a range of temperatures (M.P. to 750°C) by the relationship = 512 — 0.133t. Arsenic and lellurium were both found to be surface active in lead. The surface excess concentration at 700°C was .found to be constant at 0.74 x 10-10 moles per sq cm for tellurium. The surface excess of arsenic at 700°C varied between 0.26 x 10-10 moles per sq cm at 0.16 at. pct to 1.5 x 10-10 moles per sq cm at 8.3 at. pet. The surface tension of lead has been investigated sporadically over the last 90 years. The first recorded study was made by Quincke1 who used a rather crude application of the drop-weight method. Hogness2 obtained the first reliable value for the surface tension of lead by measuring the pressure necessary to force the liquid metal from the end of a small capillary of known radius. Hogness gives the empirical formula: ?(surface tension)= 444 - 0.077 (l-327) which describes the relationship between surface tension and temperature ("C); This work was followed by that of Bircumshaw3 who applied the two-capillar maximum bubble pressure method of Sugden.4 The values published by Bircumshaw are in good agreement with those found by Hogness. Matuyama5 examined the surface tension of lead by the drop weight method. However, the values found are somewhat higher than those previously reported. More recent investigations by Greenaway6 and by Melford and oar' have resulted in data which are not in close agreement, but which are well within the expected range at most temperature levels. The study of the surface tension of lead alloys began with Drath and sauerwald8 who examined the lead-bismuth system. They found that the surface tension values of the alloys in this system deviated only slightly from the ideal mixture rule. Matuyarna5 examined the lead-antimony system. Bircumshaw the lead-tin, and the lead-indium system was studied by Hoar and Me1ford.10 The results of these investi- gations are summarized in Fig. 1. It may be seen that the data vary only slightly from the ideal mixture rule. As none of the metals studied and reported in the literature has a very interesting effect on the surface tension of lead,*the next logical step might be to examine the effect of metals of low solubility or nonmetals having some liquid solubility. Baes, and Kellogg11 have pointed out that the elements most likely to be surface active in liquid metals are ones of limited solubility in the liquid state and possessing weak intermolecular bonding forces in the solid state. Therefore, Group V, VI and VII nonmetals are most likely to be surface active. It was decided to examine the effect of a borderline metal, arsenic, and a nonmetal tellurium. Arsenic forms a eutectic with lead having a melting point of 290°C and a composition of 6.9 at. pct As.13 Pure arsenic sublimes when heated above 610°C. Even though alloying with lead lowers the vapor pressure, fumes containing arsenic are evolved at a very noticeable rate when lead-arsenic alloys are heated above 650°C. Tellurium raises the liquidus temperature of lead sharply to 904°C,14 the melting point of PbTe (lead-telluride). The solid solubility of tellurium in lead was determined by Greenwood and worner15 to be 0.0007 at. pct at room temperature. EXPERIMENTAL METHOD Surface Tension Measurement—The two capillary maximum bubble pressure method for measuring surface tension developed by Sugden,4 and used later

Jan 1, 1962

By J. H. Yang, K. E. Gray

Results of single-blow bit-tooth impact tests on saturated rocks under elevated confining pressures and zero pore pressure were reported in a previous publication.1 This paper presents an extension of the earlier work to include a study of crater formation during tooth impact on both gas- and liquid-saturated Berea and Bandera sandstones at elevated confining and pore pressures. The basic data obtained were force-time, displacement-time, velocity-time and force-displacement curves during crater formation. Crater volume was also measured and the mode of crater formation determined. Bit tooth geometry, depth of penetration and velocity of impact were held constant. Results indicate that, with pore fluid present in the rock, failure trends from brittle to ductile as pore pressure is increased at constant confining pressure (pore pressure and borehole pressure were equal) For a given rock type, the mode of crater formation was dependent not only upon the nominal effective stress, but also upon the fluid which saturated the rock pore space. When confining pressure and pore pressure were equal (zero nominal effective stress), bit-tooth impact resulted in brittle failure for nitrogen-saturated Berea, and brittle to transitional failure for nitrogen-saturated Bandera; when saturated with liquid both rocks failed in a ductile manner at zero nominal effective stress. INTRODUCTION Dynamic wedge penetration tests have been conducted by investigators in several fields, but the failure mechanism of rock under dynamic stresses is not understood completely. The complex action of drilling bits, even considering the action of a single tooth, may be considered as a combination of drag bit and rolling cutter action. Thus, as a first step in understanding rock breakage in oil well drilling, single chisel impact and rock planing are of fundamental importance. For example, Gray 2 and Crisp3 studied drag bit cutting action at brittle stress states. Simon4 and Hartman5 studied the reaction of rocks to vertical impact by means of drop tests. The depth of penetration, crater volume and force-vs-time curves during crater formation were observed. The significance of indexing single-bit impacts has been noted.4,6-8 Gamer et al,9 reported impact tests on impermeable Leuders limestone at atmospheric and elevated confining pressures. In all cases the tests were accomplished on dry rock and pore pressure was considered to be zero. The importance of both confining pressure and pore pressure on the failure characteristics of rock was described. 10-12 It was found that the yield strength and ductility of porous rock depend on the state of stress under which the sample is tested. The importance of pore pressure on drilling rate in microbit experiments was noted by Cumingham and Eenink. l3 Robinson 12 also pointed out that in drilling the most important parameter in rock failure is the effective stress, where effective suess is defined as confining pressure pc minus pore pressure pp. The effect of pore pressure and confining pressure on rock strength was also noted by Serdengecti and Boozer 14 in strain rate tests, and by Gardner, Wyllie and Droschackl5 in elastic wave studies. Until recently all reported wedge impact studies under simulated wellbore stress states have been conducted on dry rock. Maurer 16 reported impact tests on samples saturated with deaerated water. Borehole and formation fluid pressures were equal in these tests except when mud was used in the borehole. With mud in the borehole and a high borehole-to-formation fluid pressure differential. Maurer observed "pseudoplastic" crater formation. Podio and Grayl reported impact tests on Berea and Bandera sandstone saturated with pore fluids having wide ranges in viscosities. In Podio and Gray's tests, confining pressure was elevated, but pore pressure and borehole pressure were held fixed at atmospheric pressure. The presence of

By E. I. Alessandrini, A. U. Seybolt

Selective oxidation (preferential oxidation of a single alloy component) can be an important oxidation mode in the case of alloys such as Si-Fe, Al-Fe, and so on, when heat-treating in atmospheres of low oxygen potential. It was the purpose of this work to identify the oxide films formed on iron containing 31/4 pct Si at low oxygen potentials, and to make some observations on the H2O/H2 ratios required to form them. EXPERIMENTAL METHOD HYDROGEN of varying water content offers a very convenient method of establishing a wide range of oxidizing power, or oxygen potential. The method chosen to provide a desired H2O/H2 ratio was to nearly saturate hydrogen at room temperature by bubbling the gas through water at room temperature, and then to wring out the excess water by passing the wet gas through a long glass spiral immersed in a refrigerated liquid at a desired dew point. After oxidation, the samples were examined by electron diffraction in order to identify any film which might be present. PREPARATION AND TREATMENT OF SAMPLES The samples were prepared from a Si-Fe alloy made in the laboratory using electrolytic iron and 96 pct ferro-silico11, vacuum-induction melted, hot-rolled then cold-rolled to 0.015-in. thickness. After the cold-rolling the samples were annealed at 1000°C. Transmission Laue X-ray patterns showed very little evidence of preferred orientation, but it is likely that a weak texture could have escaped notice. The chemical analysis was as follows: 3.34 Si, 0.01 Al, 0.001 0, 0.006 C, 0.002 N. Before each sample was oxidized, it was polished through 4/0 emery paper, cleaned and dried using benzene, carbon tetrachloride, acetone, absolute alcohol, and ether. The method of oxidizing the samples was as follows: Samples about 1/2 by 1 by 0.015 in. were held in the upper, cool part of a vertical vacuum furnace until the desired temperature was established in the furnace, Fig. 1. The sample was then lowered into the uniform hot zone where it was heated quickly to the desired temperature, and subjected to hydrogen of controlled moisture content (dew point) as mentioned previously. Temperatures from 400" to 1000°C were used, and dew points from room temperature to —78°C were explored. In general, the runs lasted about 6 hr, but a few runs were of different duration, as will be indicated later. After the predetermined period of time had elapsed, the specimens were withdrawn by the hollow stainless steel-quartz holder to a cool zone at the top of the furnace. EXPERIMENTAL RESULTS The results are summarized in Table I. Most of the electron-diffraction patterns were obtained by glancing-angle reflection, but in a few cases it was possible to strip the oxide films from the surface by a total immersion in a 3 pct bromine-methanol solution. Some of the thinner stripped films yielded quite satisfactory transmission patterns. However, both diffraction techniques yielded the same results; the patterns while most frequently showing a (low) tridymite, also showed a (low) cristobalite in some cases. A few patterns showed evidence of both phases. Because of the known nonequilibrium behavior of silica, it is not surprising that both forms of silica could coexist on one sample. It was noted that at fairly low dew points such as —40°C, there was a tendency for diffuse diffraction rings, suggesting a very small crystallite size. Also some subsequent experiments to be reported later show that thin silica films can be amorphous.

Jan 1, 1959

By C. W. Hoffman, W. R. Hinken

Probability sizing, a fairly recent development in the field of particle separation, is now under investigation to determine its value to the mining industry. The method employed is probability sizing through a vibrating network of decreasing screen openings. While probability sizing is not new, the possibility of using it for coarse, highly abrasive ores at high tonnage rates has only recently appeared to merit practical consideration. The advantages of probability sizing vs. conventional screening methods are: (1) reduced space requirements for a high capacity unit, (2) fewer moving parts, (3) more versatile product sizing selection, (4) reduced maintenance requirements, and (5) lower power consumption. Screening is a necessary part of virtually every crushing circuit. At some stage in the process, particle separation becomes a controlling factor in the operation. The basic type of screen in use today is the vibrating unit, which usually employs a mechanical vibrator of one type or another to obtain sizing and material transportation across the screen surface. The vibrating screen has its limitations and inherent problems. Operators must live with: (1) high maintenance — worn rods, screen cloth, spacers, cross members, chutes, etc., (2) low capacity in relation to floor space requirements, (3) extreme noise levels, (4) high power consumption, and (5) structural problems in the screens and supporting steelwork. All plant operators have become tolerant of these drawbacks through the years, and little innovation has been developed in screening. The vibrating screens in use today incorporate improved metals, more efficient power sources, better lubricants, and increased manufacturing skill, but the basic machine itself remains unchanged. Screening is a relatively small part of most plants' operating expenditures and gets relatively little attention from research and development. The HiProb sizer is a new approach to the problem of particle separation on a high tonnage basis. Developed by Dr. Fredrik Mogensen (president of Fred-rik Mogensen, A. B. of Djursholn, Sweden), this unit has found its primary acceptance in the sizing of wet or dry materials in the fine ranges. Climax has been working cooperatively with Mine and Smelter Supply Company, the United States licensee, on the adaptation of the sizer to obtain consistent recovery at a high tonnage rate on a — 3/8-in. separation. This was a new application for the sizer and opened up a whole new field of problems. Dr. Mogensen's machine utilizes the control of normal probability of falling particles and is designed to eliminate some of the undesirable features of vibrating screens mentioned earlier. The machine is light, compact, consumes less power than conventional screens and has a low noise level. PRINCIPLES Probability sizing is a process designed to allow solid particles to segregate with a high ratio of the materials reporting into their respective size fractions with a minimum amount of misplaced particles. Sizing is defined in this paper as segregation of dry solid particles into fractions of comparable sizes. Probability is usually estimated as the ratio of the number of ways an event might occur vs. the total number of allowable ways. The probability process described depends upon the fact that particles falling through a network will segregate across the sizing surface even though all openings are larger than the particles. The degree of segregation is dependent upon the particle size and the trajectory applied by the sizing network to each falling particle. Specifically, the process utilizes a maze made up of screen cloth to control the path of a particle in free fall as illustrated in Fig. 1. The usefulness of this probability sizing process is dependent upon the degree of efficiency of an effective maze. Primarily, a maze must be extremely flexible to meet the multi-faceted nature of solid particles and, at the same time, the degree of control must be reproducible so that a desired separation is predictable. Dr. Fredrik Mogensen has formulated a maze that is not only flexible and easily controlled, but, mote importantly, easily adaptable to a working machine.

Jan 1, 1970

By L. H. Robinson

A proposed method of drilling utilizes sequential detonation of two types of explosive charges delivered to the hole by a conventional drilling fluid through pipe. A shaped charge first produces a long thin hole. A second charge, called a gauging charge, is pumped into the thin hole, explodes, and enlarges it to full gauge. In one suggested configuration, the explosives are contained in cylindrical capsules 4- to 5-ft long. A drilling head is positioned 2- to 3-ft off bottom. When a capsule is pumped to the bottom of the hole and stops, pressure inside the drill pipe increases and differential pressure detonates the explosive. Primacord along the length of the capsule disintegrates the capsule. The debris circulates out of the hole with the drilling fluid. The gauging-charge action was examined using 2-ft cubes of Berea sandstone. The sandstone (18 per cent porosity) was vacuum-saturated with water and surrounded by concrete. To prevent reflected tensile pulses, the acoustical impedance of the concrete matched that of the sandstone. A 750-psig pressure was applied to a drilling fluid within a shaped-charge-formed hole before detonating the gauging charge. In these tests, 190 gm of rock were removed for each gram of explosive detonated. A similar series of experiments on low-porosity (0.40 per cent) metamorphic limestone provided a more rigorous test. Extensive fracturing from the gauging-charge action prevented an estimate of the volume of the expanded hole. The diameter of the hole was irregular, ranging from about 2 to 4 in, or about fivefold larger than the hole created by the shaped charge. INTRODUCTION In the past, explosives have found a varied but somewhat limited use in the oil field. An early well stimulation technique, still in use today, in vo lves shooting ni troglycerin to en large the borehole and to increase matrix permeability near the wellbore. Bullets and jets are now the conventional method of perforating casing and tubing. Detonations are frequently used to "back off" or "shoot off" stuck pipe and, of course, seismo-graphic work has long depended on explosive-generated pulses to find attractive earth structures. Efforts to use explosives in drilling operations have received limited examinations1-3 which, in one respect, is surprising because explosives offer one way to transmit large amounts of energy directly to the bottom of the hole. Recently, Ostrovskii l described a Russian method of drilling with explosives that utilizes small capsules containing explosives which are pumped into the mud stream to the bottom of a borehole. As the capsules leave the end of the drill pipe, a detonation mechanism is armed. Impact detonates the explosive. In another configuration, two liquids (an oxidizing agent and fuel) in the capsule are separated by a frangible membrane. Separately, the liquids are nonexplosive. Near the bottom of the drill pipe, the capsule passes through a narrow constriction which ruptures the membrane. The mixing of the liquids produces an explosive. Impact is again used to detonate the explosive. About the time Ostrovskii was developing his method, Humble Oil & Refining Co. was independently doing research on another explosive drilling concept based on the sequential detonation of two types -of explosive charges. The proposed technique consisted of alternately pumping a shaped charge and then a "gauging charge" down a well. The shaped charge should drill a long, tapered hole, and the gauging charge should expand it to full gauge. This paper presents the visualized drilling concept and gives results of laboratory work which showed that sequential firing of charges can form hole at an attractive charge-to-rock removal ratio. An important finding was that increased environmental pressure, which is to be expected in wells, increases rock removal efficiency of the gauging charge.

Jan 1, 1966

By M. R. J. Wyllie, Walter D. Rose

The use of electrical well logs for the quantitative determination of such reservoir parameters as connate water saturation, formation permeability and connate water salinity has recently been attracting the attention of a number of workers1,2,3,4,5. While the theory of the determination of connate water salinity from the self potential S.P. log has received rather detailed treatment, relatively little attention has been paid to the theoretical aspects involved in the quantitative interpretation of resistivity data. It is clear that if electrical well logs can be used for the quantitative evaluation of physical characteristics of reservoir rock, they will provide a valuable tool to supplement cheaply information obtained by more laborious core analysis. In certain cases it is conceivable that the coring program could be considerably curtailed if the electric log could be relied upon to give reasonably accurate quantitative information. It is our object in this paper to examine the theoretical basis of quantitative log interpretation as expressed in such well-established logging concepts as formation factor and cementation factor. It is also our object to investigate the physical aspects of the rela- tionship which is presumed to exist between resistivity index and brine saturation in reservoir rock. In particular, we will endeavor to draw attention to the fact that it is possible to express these logging concepts in terms of capillary pressure-saturation relationships, permeability and tortuosity, parameters which we will consider in this paper to be fundamentally indicative of rock texture. The probability of being able to obtain from log recordings alone the data theoretically essential to permit quantitative log interpretatiou will be examined, and consideration will also be given to the problem of formulating simple semi-empirical relationships for use in the field. THEORETICAL CONSIDERATIONS The concept of formation resistivity factor, or as it is now commonly called, formation factor, appears to have been introduced by G. E. Archie",". Formation resistivity factor as defined by Archie is the resistivity of a rock 100 per cent brine-saturated divided by the resistivity of the brine. This relationship had previously been used by physical chemists and the concept is, for example, implicit in an early treatment by Fricke7 of the conductivity of aqueous slurries. Archie was able to establish the fact that although the relationship between formation factor and porosity did not change too greatly for different rock textures, the relationship between formation factor and permeability was markedly dependent on rock texture. The relationship found by Archie between formation factor and porosity was expanded by H. Guyod8. Archie had suggested that the formation factor, F, could be expressed in terms of the porosity, F, as follows: F =F-m .... (11 where, F = effective porosity fraction of the sand, and, m = an exponent greater than about 1.3. Guyod introduced the term cementation factor for the exponent, m, since it may be qualitatively shown that formation factor for any given porosity tends to increase as the sand becomes more cemented. It would appear that the concept of m as an exponent representing the cementation in a sand is strictly only of qualitative value, since the quantitative estimation of m by means other than the determination of F and F has not been possible. Guyod suggests that m can be estimated from a visual examination of a sample of rock, but this method appears to be both arbitrary and unreliable. It can be said, however, that in intergranular reservoirs of practical interest, the range of m is from about 1.4 to 3.0. A possible explanation for the fact that m is found to lie between these limits will be offered below. The determination of formation factor is an essential preliminary to the

Jan 1, 1950

By S. J. Matas, R. F. Hehemann, R. H. Goodenow

The hot-stage metallographic method has been employed to determine radial growth rates of upper and lower bainite. Lower bainite appears to grow as individual plates that increase in both length and thickness while upper bainite grows as sheaves of closely spaced plates or needles. A discontinuity in the temperature dependence of the growth rate appears to be associated with the transition from upper to lower bainite and stepped quenching experiments suggest that lower bainite will not continue to grow when the temperature is raised to the upper range. Thus, a single process does not appear to control the growth of both upper and lower bainite. A tentative model based on the forces acting on a dislocation interface is proposed to account for the slow growth of bainite. It has been recognized since the early studies of Davenport and Bain that a close relationship exists between the martensite and bainite transformations in steels. However, diffusion of carbon during the transformation has lead to considerable controversy concerning the reaction mechanism.1-7 Many studies4,5,7-9 have emphasized the structura and kinetic aspects of the bainite reaction and, in particular, the difference observed between the two forms of bainite—frequently termed upper and lower bainite. A kinetic difference between the two types of bainite has been revealed in the activation energy determined from the overall reaction;4,5 however, many difficulties arise in an interpretation of these activation energies since a number of temperature dependent factors contribute to the kinetics of the overall reaction. The displacive surface relief10 accompanying the bainite reaction permits a separation of the nuclea-tion and growth contributions to the reaction and allows the kinetics of the growth process to be examined. Several investigations of this type have been conducted; however, they have been restricted to the low temperature range.3'6'11 Here, bainite plates are observed to grow slowly in both length and width. The present investigation extends such studies to include the upper bainite range. MATERIALS AND PROCEDURE Materials. The composition of the steels studied in this investigation are presented in Table I. The range of composition permitted a study of the effect of carbon content on the growth rate of upper bainite in the 9 pct Ni steels and consideration of both upper and lower bainite in the higher carbon steels. These steels were received as hot-rolled rounds and were forged to approximately 1/2 in. thick plates for preparation of metallographic specimens. In order to produce an essentially zero carbon steel, Steel A was decarburized in wet hydrogen at 1550°F for 15 days with the result tabulated as Steel AD. Experimental Procedure. In order to study the slow growth of the displacive transformation product, a commercially available Leitz hot stage was modified to permit heating of the specimen by its own resistance in a manner similar to that employed by other investigators.6 The furnace chamber was maintained at a pressure of 2 to 3 X 10-5 mm Hg prior to austenitizing at 2000° ± 12° F for 5 min. Samples could be cooled from the austenitizing to the transformation temperature in approximately 15 sec and the progress of transformation was recorded with a 9 cm by 12 cm single frame camera or a 16 mm movie camera. RESULTS AND DISCUSSION Growth Characteristics. The general growth characteristics observed in this investigation were analogous to those reported previously.3,6,11 Typical growth sequences for the high temperature and low temperature forms are illustrated in Figs. 1 to 5. In both temperature ranges, bainite plates increase in length at slow, temperature dependent rates until interrupted by a grain boundary, another plate, or

Jan 1, 1963

By J. Chipman, J. C. Fulton

Reduction of Si from slag to carbon-saturated iron is a very slow reaction. The rate is nearly independent of stirring but is accelerated markedly by increased temperature. In a slag containing 45 pct SiO2, 38 pct CaO, 17 pct Al2O3, the energy of activation is approximately 130 kcal. AT temperatures of 1450" to 1600°C occurring in the hearth of the iron blast furnace, chemical reactions are normally expected to proceed with great rapidity. Many of the reactions of iron making are indeed quite rapid and attain a condition corresponding roughly to a state of equilibrium before metal and slag are tapped from the furnace. The one conspicuous exception is the reaction by which carbon in the coke or metal reacts with silica in the slag to deliver silicon to the metal. From the practical viewpoint the slowness of this reaction is indeed fortunate, for if it were fast enough to reach equilibrium during the time of contact, it would be difficult to produce pig iron of the desired low silicon content. The one other reaction which under certain circumstances can also be very slow is the transfer of sulfur from blast-furnace metal to slag. In their laboratory exeriments on this reaction, Hatch and Chipman found that at least 5 hr were required for the attainment of equilibrium in a small crucible and that the reaction was not accelerated by increasing the rate of stirring. Subsequently it was shown2 that the presence of a reducible oxide MnO greatly inhibited sulfur removal, and finally that SiO2 itself3 under some conditions has sufficient oxidizing Dower to interfere with sulfur transfer. The kinetics of sulfur removal are now rather well understood,4 and it has been shown3,5 that when the silicon content of the metal is high enough to prevent reduction of SiO,, the desulfurizing process is rapid. Thus the observations of slow removal of sulfur are associated with the coincident slow reduction of SiO2, a process which transfers both silicon and oxygen to the metal phase. It is, of course, the oxygen which interferes with sulfur removal. An explanation of the slowness of the silica reduction reaction has not been obtained. The sulfur transfer process has been shown by the authors5 to be at least partially transport-controlled in the absence of interference by silica. Under the experimental conditions. 99 pct of the total transfer at 1600" was accomplished within an hour. Under similar conditions the reduction of silica may not proceed half-way to equilibrium6 in 8 hr. It is scarcely imaginable that silica reduction could be transport-controlled when the slag contains 44 pct SiO2 and the metal about 1.4 pct C. The experiments reported here show definitely that it is controlled by a slow step or steps in the chemical reaction. One might expect to find such a slow step in the breaking of SiO bonds or in the slow removal of oxygen by carbon at the slag-metal or metal-crucible interface or by bubble formation. EXPERIMENTAL PROCEDURE The experimental procedure used in this investigation was similar to that used in the study of the kinetics of desulfurization.5 A sketch of the graphite crucible and stirrer used in the current work is shown in Fig. 1. The quantity of metal and slag used was adjusted so that the slag-metal interface was located between the top and bottom blades on the stirrer; the top of the slag layer was above the top blade. The stirrer shaft was hollow down to the metal level and served as thermocouple well or optical pyrometer target. Stirring speeds of 0 to 500 rpm were used. A carbon monoxide atmosphere was maintained in the furnace by flushing the gas over the slag surface, except in run No. 220 when it was bubbled

Jan 1, 1960

By L. W. Reynolds, R. F. Campbell, K. G. Carroll, S. H. Ballard

Based on metallographic and X-ray data probable equilibrium conditions from 1340" to 2400°F are presented for the composition range investigated. These are correlated with investigations of Takei and Kuo. Provision is made for existence of Mo, C and (Fe, Mo)2,C, carbides heretofore omitted in diagrams in this composition range. These carbides and (Fe, Mo),C, in equilibrium with ferrite and austenite, restrict the austenite and austenite + ferrite fields to lower carbon contents and higher temperatures than in the Fe-C system. OK groups of steel of different molybdenum content, but with approximately the same carbon variation in each group, Table I, were studied. The alloys were melted in an acid-lined 30-lb high-frequency induction furnace, and the ingots forged to l-in. rounds, which were then ground to 0.75-in. diam. To minimize chemical segregations a short length of each bar was given a high-temperature heat treatment as listed in Table I. Specimens 0.062 to 0.125-in. thick were thereafter cut from the homogenized bars for heat treatment to determine phase changes in the alloy. Heat treatments were performed in either a lead bath or muffle-type electric furnace, depending upon the temperature required. Maximum temperature variation was * 2" F in the lead bath and * 5"F up to 1900°F and +8"F above 1900°F in the electric furnace. Adequate protection of the specimen from the oxidizing atmosphere in the electric furnace was obtained by sealing the specimen in either a pyrex or a silica capsule which was evacuated or not as circumstances required. For austenitizing followed by quenching to an isothermal temperature, the specimen was placed in a closed-end refractory tube the mouth of which, extending beyond the furnace, was connected to a vacuum pump. The specimen could be withdrawn from this tube and quenched as desired. IDENTIFICATION OF PHASES The principal method of identification of phases was metallographic examination conducted on surfaces well removed from exposure to lead or atmosphere effects during heat treatment. Hardness measurements (Dph/lOkg) were also made on these surfaces. The etching reagents used and their effects are listed in Table II. Martensite and ferrite were readily recognized by their customary appearance after etching with saturated picral or 1 pct nital. The presence of liquid at high temperature was indicated by curved interfaces characteristic of boundaries between solid and melt, by intergranular pools of dendritic areas in a carbide matrix, and by a black network coincident with austenite grain boundaries. Examples of these structures are shown in Figs. l(a) and (0). The types of carbide which were attacked by the electrolytic chromic acid etch and the alkaline KMnO, etch, Table 11, were identified by X-ray analyses of extracted carbides of five alloys. Carbide residue was obtained from a metallographic specimen by etching the specimen for 24 hr in hydrochloric-picric acid in alcohol (grain-size reagent), after which the carbides, standing in relief, were scraped from the surface of the specimen and mounted on a glass slide. Diffraction patterns were obtained with a Philips spectrometer using iron-filtered cobalt radiation. Figs. 2, 3, 4, and 5 illustrate typical etching behaviors with chromic acid and alkaline KMnO,. Chromic acid attacked Mo,C as shown in Figs. 2(a) and (b)-but not (Fe, Mo),C, Fig. 3(b). Alkaline KMnO, attacked (Fe, Mo),C, Fig. 3(c), and also attacked M0,C. In accordance with these behaviors, a typical differentiation of coexisting Mo,C and (Fe, Mo),~ is shown in Figs. 4(a) and (b). The carbide (Fe, Mo),,C, could not be obtained free of other coexisting carbides for etching experiments. The behavior. however. of coexisting carbides identified by x-ray diffraction as Mo,C ind (Fe, Mo),,C, indicate that (Fe, Mo)23C6 is not etched by chromic

Jan 1, 1961

By J. M. Roberts, N. Brown

The stress-strain behavior of zinc single crystals was measured over a strain range of 10-6 to 10-2. The phenomenon of macroyielding was observed in detail and plastic strains were detected at almost zero-stress. Closed hysteresis loops were observed during loading and unloading in the strain region of about 10-5. From the hysteresis a frictional stress on the dislocation of about 6 psi was obtained. A preliminary analysis indicates that impurities are primarily responsible for the friction. Nonelastic Strains as much as 10 -4 were recovered depending on the amount of prior deformation. Part of the recovered strain occurs instantaneously upon unloading and the remainder occurs at zero stress. The time dependence of the recovered strain was measured. THIS investigation is concerned with the details of plastic deformation preceding the ordinary yield point as measured with the usual strain sensitivity of about 10-4. The approach leads to internal friction observations in the hitherto neglected frequency range below 10-1 cycles per sec. It is believed that if the phenomenon of macroscopic yielding is to be understood, then the stress-strain curve in the neighborhood of the macroyield point should be greatly magnified. It may then be possible to determine whether macroscopic yielding is a unique event or whether it is a process which begins gradually at a lower stress. In the case of low-carbon steel a unique event obviously occurs at the macroscopic yield point as indicated by a drop in the load, but copper appears to exhibit a gradual transition from the elastic to the plastic state. In zinc the yield point is rather abrupt although the data indicates that some plastic deformation precedes large scale yielding.' One of the purposes of this investigation is to determine whether there is an abrupt transition from the preyield microstrain region to the region of macroscopic deformation. Such a rapid transition would support the concept that there is a critical stress for yielding. The concept that yielding is a unique event associated with such phenomenon as activating a Frank-Read source, freeing the dislocation from solute atoms, dislocations cutting through dislocations, or dislocations moving freely by one another, has been expounded widely on theoretical grounds. It is hoped that highly sensitive measurements of strain in the neighborhood of the macroscopic yield point will shed some light on the event known as the "Yield Point". EXPERIMENTAL METHOD 1) Specimens—High-purity zinc was cast into spherical graphite moulds in air and grown into spherical single crystals by the Bridgman method under a positive pressure of Argon gas. Spectro-graphic analysis of cleaved sections from four crystals showed a purity of 99.994 pet Zn. The specimens were acid machined with an 1/8 in. gage section in a form similar to those used by Parker and co-workers.2 Bausch type grips were fastened to the specimen by Epon VI adhesive. The specimens were oriented so that only [1120] (0001) slip occurred. Fig. 1 shows two of the specimens in the grips. Prior to each test, the gage section of the specimen was given a concentrated HNO3 chemical polish followed by alcohol rinsing and air blast drying. 2) Test Method- The shear tests were performed on an Instron testing machine and the experimental set-up was made very "hard". Strain could be measured to a sensitivity of 10 -6 by means of a capacitance gage extensometer. The design and calibration of this type of extensometer to measure microstrain, as applied to pure shear and tensile tests of metals, will be the subject of a separate paper—therefore, only a brief account will be presented here. The method essentially consists of attaching a

Jan 1, 1961

By C. D. Hall

This paper may be divided into two main parts: (1) analysis and data to show that Eq. 6 adequately correlates the authors' experimental data, and (2) the assertion that Eq. 20 "should permit scale-up with data taken from one pipe diameter for Newtonian, inelastic non-Newtonian, and viscoelastic fluids, such as dilute polymer fracturing fluids, which produce considerable pressure reductions." The authors might well recommend that this broad grouping of fluid types could be correlated by using Eq. 6 (requiring data from at least two pipe diameters). On the other hand, Eq. 20 is only shown to be adequate for conditions within the range of the present data set. Specifically, predictions by Eq. 20 for diameter scale-up to casing sizes would give larger deviations than implied in Table 2, and scale-up for some other fluids that give large drag reduction could be grossly in error. The description of a class of fluids "which produce a diameter family of straight parallel lines on a log (d?p/4L) vs log (8 v/d) plot. . ." defines a necessary condition for using Eq. 6; i.e., that s shall be constant for each fluid. The proposal that Eq. 20 is applicable to turbulent flow of such fluids is equivalent to saying that the spacing of these parallel lines, with A being constant, will be found to correspond to m = -1.20 for all such fluids. Table 1 shows the values of m derived from data on 16 non-Newtonian fluids. The key statement of this paper is that the diameter exponents "do not vary significantly from . . . -1.20." In statistical terms, this says that the m value for each fluid, which was obtained from all the measurements made on that fluid. has not been shown to be different from the arithmetic mean of the m values for the 16 fluids tested. This implies that the group mean, -1.20, is a more reliable value to use for an individual fluid than is the m value derived from the data on that fluid alone. No statistical test is described to support the key statement that the diameter exponents do not vary significantly from -1.20. Such a test would have to take into account that each individual m value is shown to correlate the pressure gradients for its fluid, with only about 3 percent standard deviation over the diameter range covered. That is, the m value is not the result of a single independent measurement. Thus, it would not be sufficient, or valid, to compare the deviation of one of the m values with the variance of the 16 values of m about their mean. An alternative interpretation of the key statement is that the diameter exponents do not vary appreciably from -1.20; i.e., that using -1.20 does not cause serious inaccuracy. Table 2 seems to be offered in support of such an assertion. However, such a statistical treatment (1) is unnecessary and (2) cannot lead to any valid scale-up generalization. The amount of error introduced by using a 1"wrong" value of diameter exponent — i.e., -1.20 instead of m — is determined by Eq. 6. The ratio of the pressures predicted by Eqs. 6 and 20 for scale-up from ds in small pipe to d, in casing is The pressure for 30-percent calcium carbonate slurry (m = -1.112) in 10-in. ID pipe would be predicted 30 percent higher by Eq. 6 than by Eq. 20, if based on tests in 0.5-in. ID pipe. The data set tested in Table 2 represents only a limited sample of pipe diameters (ratio of about 4:l) out of the population of diameters that would

Jan 1, 1970

By R. L. Orr, O. D. Sherby, J. E. Dorn

Creep data for pure metals at temperatures above those at which rapid recovery occurs (above about 0.45 the melting temperature) are correlatable by means of the equations and These correlations were applied successfully to data for aluminum, iron, nickel, copper, zinc, platinum, gold, and lead as well as for simple alloys. For a given metal, AH is a constant about equal to the activation energy for self-diffusion. THE early recognition that creep is stimulated by thermal activation prompted numerous investigators', ' to apply the same laws that are valid for the viscous behavior of liquids to analyses of creep data. To a good first approximation these laws are summarized by the equation were i is the creep rate; T, the absolute temperature; R, the gas constant in cal per degree per mol; T, the applied stress; AH, the activation energy in cal per mol; S', a constant dependent on the entropy of activation, the frequency of activation, and the contribution of each activation to the strain; and B', a constant dependent upon the size of the flow unit that is activated. Although Eq. 1 describes the flow of viscous fluids very accurately, its application to the creep of solids has been disappointing. Two reasons for the failure of Eq. 1 for creep are now known: First, the decelerating creep rates during primary creep demand that the internal structures of the metals are changing and that these changes might be reflected by changes in one or more of the three creep parameters S', AH, and B'. Consequently when the conventional methods of evaluating these parameters are employed by comparing the secondary creep rates at a series of temperatures and at a series of stresses, the true effects of temperature and stress are masked because of simultaneous changes in one or more of the creep parameters. Second, as will be illustrated more fully later, three distinctly different types of investigations have shown that the stress term for high temperature creep enters the analysis as and not as t/T. This rather unexpected result points sharply to a significant fundamental difference between the mechanisms for the viscous behavior of fluids and the high temperature creep of metals. More recent extensive investigations",'4 on the creep of high purity aluminum and several of its dilute a solid solutions have shown that where E is the total creep strain; temperature compensated time = for a constant temperature test; t, is the initial stress in a constant load test or the constant true stress in a constant stress test;" and t is the duration of test. • Eq. 2 is valid for either constant stress or constant load tests; but the total creep curve is difierent (i.e. the function, f, is differentl for each test. The fundamental origin of the validity of Eq. 2 is thought to arise from some equivalence of substructures in constant load creep tests at equal values of 0 or E. Both X-ray and metallographic examination revealed that practically identical lattice distortions and subgrain sizes are obtained for the same creep strain under the same load over wide ranges of test temperature.' Furthermore the room temperature tensile properties following equal creep strains at different temperatures under constant loads were also identical, illustrating that identical substructures were indeed obtained.' " A second type of correlation was obtained by differentiating Eq. 2 with respect to time, giving For the secondary creep rate, denoted by i,, But Eq. 2 reveals that 0, is a function of a, alone because the secondary creep rate in a given constant load test is always reached at a fixed value E,". Therefore where is the function that was introduced a number of years ago by Zener and Hollomon." Eq. 4 is not only valid for creep but will permit correlations between constant load creep and tensile data where e, is the rate of tensile straining and (TC is the engineering ultimate tensile strength.

Jan 1, 1955

By J. H. Scaff, H. C. Theurer, E. E. Schumacher

The microwave region of the radio spectrum was effectively utilized in radar designs during the recent war and it has become of increasing interest in the field of communications. Work in this field has led to an important use for silicon—that of the point contact rectifiers†1 in the frequency converter of microwave (radar or radio) receivers—and has stimulated considerable interest in the electrical properties and preparation of silicon and its alloys. Silicon is an electronic semiconductor. Its conductivity at room temperature results principally from the presence of certain impurities. While for metals an increase in impurity content increases the resistivity, for semiconductors such as silicon the opposite occurs and, in general, the addition of impurities lowers the resistivity. Silicon materials may be classified into one of two groups depending upon the manner in which the impurities contribute to electrical properties. These have been termed for convenience p-type or n-type. P-type silicon develops a very large positive thermal emf against metals, has a Hall coefficient of positive sign and a low resistance direction in point contact rectification with the silicon positive with respect to the point. N-type silicon, on the other hand, develops a negative thermal emf against metals, has a Hall coefficient of negative sign and a low resistance direction in rectification with the silicon negative with respect to the point. Impurities which produce n-type silicon are called donors inasmuch as these elements contribute to electrical conductivity by donating electrons to an unfilled energy band in the silicon. On the other hand, elements which produce p-type silicon are known as acceptors as these impurities contribute to the electrical conductivity by accepting electrons from a filled energy band permitting what is known as conductivity by "holes" in which the sign of the carriers appears to be positive. A general treatment of the mechanism of conduction in semiconductors from the viewpoint of modern band theory has been given recently by Pearson,2 by Becker, Green and Pearson,3 and by Torrey and Whitmer.4 In this investigation boron and aluminum have been found to be acceptors, and phosphorus, arsenic, and antimony to be donors in silicon. Data on the effect of boron and phosphorus on the electrical properties, when present singly and in combination, have been acquired. These data are discussed in the present paper. Raw Materials Used and Methods for Adding Seeond Constituents Silicon from two sources was used in this work and these will be referred to as A and B respectively. Silicon A is a material of high purity supplied by the Electro Metallurgical Co. It is prepared by chemical purification of "commercial" silicon obtained from the arc furnace reduction of SiO2. It contains 99.8 pct silicon, minimum, with small amounts of calcium, iron, aluminum, boron, and phosphorus as the principal impurities. This material was extensively employed in these studies as well as in the commercial preparation of rectifier materials. Silicon B is a material of high purity from the du-Pont Co. It is prepared by a pyrolytic reduction of Sicl4 and is free of analytically detectable amounts of boron and phosphorus. Its use permitted study of the effect of boron and phosphorus individually on the properties. This material contains, however, spec-troscopic traees of a number of metals, some of which affect electrical and rectification properties. Typical analyses for the two grades of silicon are given in Table 1. To make controlled additions of boron to the charge it was necessary to employ a low boron content master alloy since the quantity of boron to be added was usually only a few thousandths of one percent. The alloy containing nominally one percent boron was prepared by melting chemically pure boron with silicon A using the melting techniques for 320 g silicon

Jan 1, 1950

By G. L. F. Powell, L. M. Hogan

Large degrees of undercooling have been produced in bulk samples, 400 g, of copper and Cu-O alloys by melting in a slag of commercial soda-lime glass. The maximum degrees of undercooling obtained for copper, hypoeutectic and hypereutectic Cu-O alloy samples were 208°, 218°, and 97°C, respectively. No grain refinement as a function of undercooling was observed for the pure copper samples although in Cu-O alloys there was a marked decrease in grain size at degrees of undercooling greater than 150°C. The grain size change is the result of recrystallization during or immediately following the freezing process. THE first report of a large degree of undercooling in a bulk sample of metal was that by Bardenheuer and Bleckmann1 who produced 258°C undercooling in a 150-g sample of iron by melting in a glass slag. Garbeck2 extended this technique to nickel, cobalt, and copper and reported maximum undercoolings of 220°, 230°, and 60°C, respectively, while Fehling and schei13 undercooled a large number of metals as 2 to 20-g samples slagged in glass. Subsequently, one of the authors4 applied the glass slag technique to bulk samples, -500 g, of silver and obtained a maximum undercooling of 250°C. It was concluded that impurities which normally catalyze nucleation at small degrees of undercooling could be removed by oxidation and solution in a glass slag. Large undercooling of bulk samples of iron, nickel, cobalt, and their alloys has also been reported by other authors.8'10'11 Of the five metals mentioned above, copper was the only one which had not been undercooled by at least 200°C in the form of a large bulk sample. Since copper exhibits high liquid solubility for oxygen, as do iron, nickel, cobalt, and silver, it was considered that a much larger degree of undercooling than that observed by Garbeck for copper should be possible. This was obtained by modification of the technique applied previously to silver and the results of undercooling experiments with 400-g samples of copper form part of this paper. The undercooling behavior of Cu-O alloys was also studied, and the influence of a small oxygen content on the grain structure of undercooled copper was observed metallographically. 1) EXPERIMENTAL The copper was obtained as oxygen-free high-conductivity copper, the major impurities of which were Fe 0.01 pct, Zn 0.015 pct, and Si 0.02 pct. Melting was carried out in an open-ended vertical cylindrical fur- nace wound with Kanthal wire. A schematic diagram of the experimental setup is shown in Fig. 1. The undercooling technique previously used for silver4 involved preoxidation of the samples by melting the silver in contact with the atmosphere. The oxygen content was subsequently reduced by freezing the samples under a glass slag, whereby the oxygen was evolved as gas and the continuous glass cover over the surface prevented re-solution of oxygen when the sample was remelted. Since oxygen is not released as gas when a Cu-O alloy is frozen. the technique had to be modified for use with copper. Also, copper is oxidized during fire refining so that an in situ preoxidation treatment of the samples was not considered to be a prerequisite to large undercooling. Experimentation proved that this supposition was correct. Instead, it was found that care was necessary during melting of the copper under glass to minimize oxygen pickup. Samples of copper weighing 400 g were prepared by adding 50-g pieces of copper to a vitreous silica crucible partly filled with soda lime glass at a temperature of approximately 1000°C. Each piece was quickly immersed in the glass slag and held at this temperature until the oxide coating on the surface decomposed. This change was easily observed and coincided with the formation of gas bubbles in the glass

Jan 1, 1969

By A. E. Dwight, A. F. Berndt

Binary and ternary alloys of uranium with transition metals were prepared with U2X stoichiometry. The compounds U2Tc, U2Rh, U2Os, and U2lr were formed by peritectic or peritectoid transformations, and were shown to be isostructural with U2Ru. The lattice constants are presented. Miscibility relationships obtained from the study of ternary alloys are graphically summarized in terms of an area-of-stability plot. The compound U2Re is not isostructural with either U2Ru or U2Mo. A series of compounds with stoichiometry U2X has been prepared in which X is technetium, rhodium, rhenium, osmium, or iridium. The only other U2X compounds, for which X is related to the above transition metals by proximity in the periodic table, are U2Mo and U2Ru. The structure of U2Mo is the tetragonal C11b type (MoSi2 type)1 and U2Ru is monoclinic, with a new structure type.' This investigation was undertaken to determine if any of the above compounds are isostructural with either U2Ru or U2Mo and to find the range of occurrence of these phases. EXPERIMENTAL Alloys were prepared from stoichiometric amounts of electrolytic uranium (99.99 pet pure) and transition metals of 99.5 pet purity (98+ pet pure Tc), by arc melting on a water-cooled copper hearth under an Ar-He atmosphere. Weight losses were negligible. The buttons were homogenized at temperatures between 700o and 800°C (900°C for U2Tc) in evacuated capsules and air-cooled. The X-ray powder specimens were annealed briefly at the temperature of homogenization. Except in the case of the technetium alloy, metallographic examination was used to determine the number of phases present. The radiation hazard involved in handling technetium precluded the use of metallography to examine U2Tc. The temperature and mode of formation of the U2X phases were determined by heating the metallographic specimens to successively higher temperatures, until examination indicated the presence of chilled liquid or a peritectoid transformation. RESULTS The U2X compounds investigated were found to be formed under the following conditions: UzTc unknown U2Ru peritectic 897o ± 3°C U2Rh peritectoid 755o ± 5°C U2Re peritectoid3 below 750°C Uas peritectic4 920°C U2Ir peritectoid 775o ± 5oC Debye-Scherrer patterns for the above U2X phases were made with CuKa radiation (nickel filter). The similarities in the positions and intensities of the strongest lines in the front-reflection region strongly suggested that U2Tc, U2Ru, U2Rh, U2Os, and U21r are isostructural with only minor differences in the unit-cell dimensions. The known lattice constants and intensities of the Debye-Scherrer rings for U2RU2 were used as a guide in order to index the low-angle X-ray reflections of the U2TC, U2Rh, U2Os, and U2Ir powder patterns. Approximate lattice constants for these compounds were thus obtained and were used along with the intensities observed for U2Ru to index the strongest lines in the back-reflection regions. A sin2 2? correction term was included and the lattice constants were refined and standard deviations estimated by least squares. Comparison of observed and calculated values of Q(= 4 sin2?/?2) used in these calculations are given in Table I. In each case when the positions of lines could not be resolved on the films they were not measured. The final lattice constants, with their standard deviations, are given in Table 11, along with the unit-cell volume and X-ray density. The values of the atomic volume5 of the transition ele-

Jan 1, 1965

By J. A. Roberson, A. M. Adair

A plate of an 18 pct Ni (250 grade) maraging steel was homogenized, cold rolled, and re crystallized to produce a fine grained, homogeneous structure. The strength properties were then measured as a function of cold rollinq prior to aging. Material in the solution heat treated condition exhibited substantial strengthening from cold rolling. The strength increase and the rate of strengthening were proportional to the amount of cold work. This benefit, of up to 50 ksi, was retained during aging for 3 hr at 900°F. The structures produced by cold rolling and aging have been systematically investigated by transmission electron microscopy. The dislocation debris produced by cold work influences the morphology and distribution of precipitate particles as well as the rate of precipitation. An essential feature of the high nickel maraging steels is a martensitic transformation from y to a with the resultant production of a supersaturated bcc solid solution. This solution decomposes to form precipitates during a subsequent aging treatment.' The martensitic transformation in low carbon Fe-Ni alloys and the mechanical properties of these alloys have been studied extensively.2"4 The carbon content of maraging steel is kept very low to avoid the embrittling Fe3C phase and to minimize the acicular, or twinned martensite common to high carbon steels. Maraging steels are usually strengthened only by heat treatment, but cold working is also quite effective in this respect as was shown by Decker, Eash, and Goldman,' Kula and Hickey,5 and the present work. There is, however, some disagreement between the present results and those of Kula and Hickey. Because of their unusual combination of strength and toughness, the maraging steels are suitable for applications where reliability at high stress levels is required. The strength level is achieved through a combination of solid solution hardening,' substructure hardening,3 and precipitation hardening,6 of which the last is the most important. The toughness of these steels has been reported to be a result of the absence of brittle grain boundary precipitates,7 and the fact that the matrix is a massive martensite rather than a twinned martensite.' One of the problems in the manufacture and use of maraging steel has been its tendency to develop laminations in sheets parallel to the rolling plane.9,10 The present investigation was intended to determine whether or not an improvement in the microstructure of this steel by thermomechani-cal processing would improve mechanical properties. I) EXPERIMENTAL PROCEDURES A plate ($ in. thick) of an 18 pct Ni-250 grade maraging steel* was obtained and examined metallo- "Analysis, wt pct: 18.1 Ni, 8.6 Co, 5.3 Mo, 0.4 Ti, 0.07 Mn, 0.05 Cr, 0.05 Si, 0.002B. 0.1 Cu. 0.05 Al. 0.002 Zr, 0.016 C, balance Fe. graphically. It was found to contain laminations as described by previous investigators. This plate was then annealed at 2100°F for 24 hr to promote homogeneity. Pilot studies on small coupons had shown that this was the minimum temperature required to accomplish homogenization in 24 hr. Since this treatment caused excessive grain growth, the steel was subsequently cold rolled and recrystallized. Cold rolling was accomplished at about 5 pct per pass to a total reduction of 66 pct. The standard solution annealing treatment (1 hr at 1500°F) was adequate to cause recrystallization of the cold worked steel. The recrystallized steel was then cold rolled and ground by various amounts to produce specimens with uniform thickness and selected amounts of cold rolling. All tensile specimens with less than 90 pct cold reduction were ground to a thickness of 0.050 in. Specimens with 90 pct cold reduction were 0.025 in. thick. All

Jan 1, 1970

By A. E. Deruyttere, J. Van der Planken, M. Laurent, Van den Bergen

FahRENHORST and schmid1 observed that zinc single crystals work hardened less rapidly when strained in liquid air (- 185°C)than in a bath at -82°C, whereas at higher temperatures the rate of work hardening decreased with increasing temperature, as would be expected. Cadmium and magnesium showed no such decrease at -185°C. At that time the observed anomaly for zinc at liquid air temperature probably seemed insignificant. However it later was confirmed2 by experiments in liquid nitrogen (-196°C) and in the mixture solid carbon dioxide-acetone (-77"C) and therefore appeared to be real. seeger3 then suggested that the anomaly might be due to the different wetting of the zinc crystals by the cooling media. Recently a new confirmation was obtained,4 however the cooling media again were different: the rate of strain hardening was found to be lower in liquid nitrogen and liquid oxygen than in pentane cooled to various temperatures down to -126°C. Ekperiments will now be reported in which the medium surrounding the specimen at the different temperatures was the same, namely gaseous air. The single crystals were made from "Overcor 99.99" zinc. They were grown in a vertical traveling furnace on seeds of nearly the same orientations. The diameter of the crystals was 5 mm and the length between shoulders 140 mm. The brass shoulders were stuck to the crystals by means of araldite. A thin steel wire was fixed to each shoulder and served to fasten the specimen to a Houns-field tensile testing machine. The crystals with the shoulders and part of the wires were surrounded by two concentric cylindrical containers. The coolant. either liquid air or ground solid carbon dioxide, was poured into the outer container only. During cooling the containers rested on a support which was removed when the straining was started. In order to check the temperature which the crystals would attain inside the inner container, a hollow bar of zinc in which a thermocouple was fitted was first mounted in the apparatus as a substitute for a crystal. It appeared that a constant temperature, respectively - 183° and -72°C, was attained inside the bar, if a soaking time of the order of 1 hr was allowed and if the outer container was constantly kept filled. Accordingly, this procedure was adopted for every tensile test. To take account of the large scatter, fourteen tensile tests were performed with liquid air and seven with solid carbon dioxide. The orientation of the crystals and the results are presented in the table, in which the symbols have the following meaning: 1 : temperature x : initial angle between basal plane and specimen axis : initial angle between slip direction and specimen axis a : shear strain at fracture 0: average rate of strain hardening = —-——- 100 t0 and Te representing respectively the critical shear stress and the shear stress at fracture. Despite the scatter of the a- and 8— values which is of the same order of magnitude as in the work reported by Seeger and Trzuble,4 it is evident that the strain hardening rate is significantly lower at -183°C thanat-72°C. The table also contains the average values calculated from Seeger and Trauble's results at the corresponding temperatures: z.e., four results at -183oC and two at-70°, -71°C. These authors calculated 9 in a slightly different way, but this is unimportant. The agreement between the a-values shows that both sets of experiments are comparable despite the differences in experimental techniques. The rates of strain hardening also agree and it may therefore be concluded that the anomaly is not

Jan 1, 1962

By R. J. Lloyd

INTRODUCTION The Mount Isa Mine is a large modern underground mine located in North-Western Queensland, Australia. Two ore types are mined and treated separately. Currently silver-lead-zinc ore is mined at the rate of 2.6 million tonnes per annum and copper ore at the rate of 4.6 million tonnes per annum. The silver-lead-zinc orebodies are mined by sub level open stoping and cut and fill methods whilst all copper ore is extracted by various forms of sub level open stoping. The mining operations are highly mechanised and utilise diesel powered load-haul-dump units of various sizes, two and three boom face drilling jumbos, electric-hydraulic rotary-percussive ring drills, in-the-hole hammer drills, rotary blasthole drills, raiseborers, battery/trolley locomotives, a large fleet of rubber tyred service and supply vehicles plus light rockdrills mounted on airlegs, rail mounted overshot shovels and battery and diesel powered locomotives. All stoping production ore is extracted with diesel powered load-haul-dump units. The ore is tipped into orepasses which connect to the main rail haulage levels. On the haulage levels electric battery/trolley locomotives are used to pull rakes of bottom dump or side dump trucks which feed the ore into primary crushers. Following two stage crushing the ore is conveyed to the shaft and hoistod to surface in bottom dump skips. Each ore stream has its own rail transport system, crushing stations and hoisting shaft feeding separate concentrators. This paper will consider some aspects of the role of equipment and machinery in the growth of the mine, will discuss in some detail the machinery and equipment in use today and will conclude with a look at some possible developments in mining equipment for the future, with particular reference to the Mount Isa Mine. A summary of mining equipment in use at Mount Isa is given in the Appendix. THE PAST Silver-lead-zinc ore was discovered at Mount Isa in 1923 and within a very short time many small mines were being developed. However the rich surface ore traces did not continue and by 1928 Mount Isa Mines Limited had acquired sufficient leases to plan for a large scale mine to exploit the low grade orebodies. At this early stage it was recognised that the mine would need to adopt the most mechanised mining techniques then available in order to overcome its twin disadvantages of low graaes and extreme remoteness. The Company introduced bar mounted drifters and overshot shovels to replace hammer and tap and hand shovelling in development work and by 1930 headings were advancing at the rate of 30 metres per week. In keeping with the concept of mechanisation the early engineers designed the Man and Supply shaft with a very large, for those days, cage compartment measuring 3.8 m x 3.4 m. This shaft was the main means of access into the mine for 36 years until the K57 shaft (now R62 shaft) was commissioned in 1966. Man and Supply is still in regular use. Production commenced in 1931 at an annual rate of approximately 660 000 tonnes of silver-lead-zinc ore. The mine was mechanised to an extent which was previously unknown in Australia; whilst the concentrator, smelter and power house utilised the most modern and efficient equipment available. Even so, the mine was very near to closure on several occasions and did not return a dividend to its shareholders for many years. Production levels remained at or slightly below 660 000 tonnes until a separate copper ore streani and mill was commissioned in 1953, doubling the existing production levels. The first underground crushers were installed at this time. Production rates expanded in the years between 1953 and 1973. By 1960 production reached 2740 000 tonnes of ore. In 1965-66 total production was 3650 000 tonnes and in 1973 the production rate plateaued at the current level.

Jan 1, 1981

By Robert D. Pehlke, Weldon L. Daines

The reduction of manganese oxide from a basic slag by silicon dissolved in liquid iron at steelmaking temperatures was studied to determine the rate-controlling step for the process. The experiments were carried out under an argon atmosphere in a resistance-heated vertical-tube furnace. The two liquid phases, slag and metal, were held in zirconia crucibles. Sampling and chemical analysis of the slag phase led to time-concentration curves for the system. Results obtained by varying parameters such as temperature, stirring rate, concentration, and melt geometry defined the limiting reaction mechanism. The reduction of manganese oxide by silicon is a fast reaction and reached equilibrium within 90 min. The rate of stirring has a marked effect on the reaction rate, while, on the other hand, the effect of temperature is very small. This identifies the rate-controlling step as diffusion rather than interfaciul chemical reaction. The variation of other parameters revealed that a) diffusion of manganese in the iron phase is the slow step, b) the value of D/6 for manganese in iron at 1550°C is 7x 10-4 cm per sec, c) the energy of activation for the apparent rate constant is 7 kcal per mole, and d) increasing the amount of silicon in the iron decreases the diffusion coefficient of manganese. THE equilibrium relations pertinent to the reduction of manganese oxide from a steelmaking slag by silicon dissolved in liquid iron have been studied, but little is known about the mechanisms that control the rate of the process. The purpose of the present investigation was to study the rate of reduction by silicon and to determine the rate-limiting step. The effects of stirring rate, temperature, composition, and melt geometry were investigated as a means of identifying the controlling step. On the laboratory scale, relatively little work has been done in the area of slag-metal kinetics, primarily because of the problems confronted in attempting to contain liquid slags and metals in laboratory crucibles at steelmaking temperatures. Since graphite is an ideal material for a crucible, several investigations have been carried out on the reduction of various oxides from a slag by carbon in graphite-saturated iron and on the transfer of sulfur between a slag and graphite-saturated iron. Most of this work has been performed in induction furnaces. Studies where the container was not graphite are extremely limited. A single kinetic study of manganese transfer between molten iron and basic slags was carried out by Sano, Shiomi, and Matsushita.' These investigators prepared calcium oxide and titanium oxide crucibles to contain the two-phase system. Only a few experiments were carried out and the results had to be treated qualitatively. Despite the paucity of kinetic data, a large quantity of information is available in the literature concerning the thermodynamics2-12 and physical properties'3-21 of the slags containing manganese oxide and the dilute liquid iron alloys containing manganese and silicon which were involved in this research program. EXPERIMENTAL METHOD A vertical-tube resistance-heated furnace was used in this investigation to study the slag-metal reaction Although most previous slag-metal studies were carried out in induction furnaces, a resistance furnace has several advantages including better control of temperature and stirring rate. Hence, a resistance furnace was selected for this study, and its design is shown schematically in Fig. 1. Slip-cast, fine-grained, low-porosity, lime-stabilized cubic zirconia crucibles were used for the kinetic experiments. The crucibles were 4 1/2 in. high and 2 1/8 in. OD with a 1/16-in. wall. The crucibles were only slightly

Jan 1, 1969

By B. F. Decker, D. Harker

The recrystallization reaction in OFHC and spectroscopically pure copper has been followed by X ray diffraction determinations of the amount of material with the cold-worked and recrystallized textures in specimens which had been given various heat treatments. The heats of activation for recrystallization are found to be: 29.9 kcal per rnol for OFHC copper and 22.4 kcal per rnol for spectroscopic copper. A reliable and speedy method for measuring the amount of recrystallized material in a piece of rolled metal, together with a new scheme for low temperature heat treatment, have made possible a determination of the activation energy for recrystallization in rolled copper. This method for studying recrystallization rates is different from others reported in the literature.' Oxygen free, high conductivity copper—OFHC copper—of purity 99.98 pct gave an activation energy for recrystallization of 29.9 kcal per mol with recrystallization data taken in the temperature range 208-245°C. Copper of purity 99.999 pct from the American Smelting & Refining Co. gave an activation energy for recrystallization of 22.4 kcal per mol with recrystallization data taken in the temperature range 43-135°C. The great change in activation energy for recrystallization as the small amount of impurity in the metal is decreased suggests that the motion of grain boundaries is conditioned by the impurities which must be concentrated in them. Thus the OFHC copper recrystallizes with an activation energy of the order of magnitude to be expected for the diffusion of the kind of impurities likely to be present. The high purity copper, on the other hand, recrystallizes with a much lower activation energy, in accord with the notion that the grain boundaries need not wait for the impurities to diffuse with them. Copper when strongly cold-rolled has a well-defined crystallite texture which can be described by saying that the [111] direction of the face- centered cubic crystals is aligned approximately in the cross-rolling direction and that faces of the form {110} lie approximately in the rolling plane. When such rolled copper is completely annealed the crystallite texture is quite different: the [loo] direction is in the cross-rolling direction and faces of the form (100) are in the rolling plane. At intermediate stages of annealing, the copper contains both textures. If a Geiger counter X ray diffraction spectrometer is set up so as to measure the intensity of the (200) Bragg reflection from the rolled surface of a piece of copper strip, this intensity increases from a very small value in the cold-worked state to a maximum as the specimen is annealed. The same would be true for (200) reflections from planes normal to the rolling or cross-rolling directions. In view of this fact, the amount of material in the copper which has recrystallized can be measured by comparing the intensities of one of these reflections just mentioned with the intensity from a similar specimen after complete annealing. In much the same way the intensity of (111) reflections from planes normal to the cross-rolling direction could be used to measure the amount of unrecrystallized material in the specimen. In the work to be described here the amounts of recrystallized and unrecrystallized material in partly annealed rolled copper specimens were determined in this way. Experimental Procedure Samples of oxygen free high conductivity (OFHC) copper, cold-rolled 99.7 pct to 0.002 in. thickness, were subjected to heat treatments for various chosen times at four different temperatures, and high purity copper samples, cold-rolled 98.0 pct to 0.0015 in. thickness, at six different temperatures. Each sample, after treatment, was placed in an orientation sample holder for use with a Geiger counter X ray spectrometer and a reading was taken of the intensity of the (200) reflection from planes perpendicular to

Jan 1, 1951