By R. M. Brick

The etched mierostructures of cold-worked alpha brasses, after reductions in excess of about 20 per cent, exhibit dark lines or markings, which have been termed "deformation bands," "etch bands," and "strain markings." The terms will be used synonymously in this report. The markings are similar in their general appearance to etch figures found in cold-worked iron, aluminum and other cubic metals but in certain respects may differ noticeably. At reductions of from about 20 to 50 per cent in brass, they appear as straight dark lines of irregular spacing and at random directions in different grains, but apparently intimately associated with definite crystallographic planes, usually {ill), in each crystal. At higher reductions, the markings on the rolling plane tend to appear in a direction transverse to the rolling direction in all crystals but may bend away at considerable angles, particularly near grain boundaries. Samans,1 on the basis of X-ray and micrographic studies of two single crystals of brass, rolled to a 50 per cent reduction, showed that the lines of deformation were the edges of thin mechanical twins parallel to octahedral planes. Barrett and Levenson2-4 have made comprehensive studies of the deformation of iron and of aluminum. They show that in these two metals the deformation markings originate by division of the original homogeneous crystal into banded areas differing in orientation by an amount that increases with the degree of deformation. The markings thus cannot be twin bands, and Barrett, in a review of this subject,2 attributed Samans' results on brass to an accidental choice of deformation that left the bands in approximately a twinned relationship. On the other hand, Mathewson6 has suggested that in some cases mechanical twinning offers a better rationalization of the coverage of some (111) pole figures of worked brass than the assumption of band rotation into symmetry positions. Considering next a deformed and annealed alpha brass, the most striking aspect of its microstructure is the multiplicity of twin bands.

Jan 1, 1940

By J. Bulina, J. T. Brown

SINCE the inception of vacuum cold-hearth arc melting of high-temperature alloys (about 4 years ago) it has been theoretically reasoned and qualitatively found that better mechanical properties are often obtained from alloys which have been melted by this practice. Mechanical properties are emphasized in this evaluation because of their importance in design. Vacuum-arc melting has an intrinsic advantage in that it creates an ingot grain structure which is easier to forge and thus leads to greater yields for the finished product. The greater yield naturally gives the process an economic basis when the cost per pound of alloy is rather high. However, the question stressed here is, does the process create an alloy with inherently better properties? There are several theoretical reasons for suspecting that it does. One is the vacuum refining which should permit lowering the content of harmful residuals with high vapor pressures. A second is the vacuum process which should preclude the formation of harmful distribution of oxides, nitrides, or carbo-nitrides, by keeping the amount of such constituents formed to a minimum. A third is the vacuum-arc cold-hearth method which prevents the possibility of pick-up of harmful elements from a refractory crucible since none is used. Fourth, the rapid solidification rate, induced by having a cold mold and only small amounts of molten metal at any one time, minimizes the segregation of elements like titanium, aluminum, and molybdenum from the top to the bottom of the ingot. This rapid solidification rate also decreases the tendency of the above elements to form undesirable phases by segregating locally. Another less frequently considered vacuum-arc melting advantage is the inherently finer-grained ingot structure which can be produced. Finer initial grain size leads to better forgeability, and means that after relatively small reductions to billets or final forged products a finer-grained material is obtained, which, by virtue of its finer grain size, would usually have greater stress-rupture ductility.

Jan 1, 1960

By Zay Jeffries

This paper will include a brief discussion of Prof. Howe's paper on The Supposed Reversal of Inheritance of Ferrite Grain Size from that of Austenite.l The general subject of grain refining in steel and iron will also be treated. The conclusions reached are stated in the following hypotheses which are discussed more in detail below. 1. The ferrite grain size in pure iron, the ferrite and pearlite grain size in hypoeutectoid steel, the pearlite grain size in eutectoid steel and the cementite and pearlite grain size of hypereutectoid steel are not inherited from the grain size of the mother austenite. 2. The only structural feature that is generally inherited from the austenite of hypo- and hypereutectoid steels on cooling through their transformation ranges is the position of the excess ferrite or cementite at the austenite grain boundaries, sometimes causing complete and sometimes incomplete networks which outline the old austenite grain boundaries. Rapid cooling through the transformation range will cause the non-inheritance of this structural (network) feature. 3. The austenite grain boundaries themselves are nearly always effaced in all steels and also in pure iron during the At transformations. 4. The grain-size refining of steel and iron is brought about by the combined effect of non-inheritance of the transformation products on either heating or cooling, i.e., the austenite transformation products do cst inherit their grain size from the austenite on cooling through the transformation range nor does austenite inherit its grain size from the products which form austenite on heating. 5. In general, in both iron and carbon steel the larger the austenite grain size, the larger will be the grain size of the transformation products on cooling. This, of course, assumes all other conditions constant except the austenite grain size. An exception is found to this general rule in very pure iron such as electrolytic iron. In this instance small austenite grains may form very large ferrite grains on cooling through Arg.

Jan 1, 1918

By Maurice Ewing, J. A. Peoples, J. W. Peoples, A. P. Craby

The purpose of this paper is to present the results of the application of the earth-resistivity method of subsurface investigation to the problem of locating seams of anthracite coal beneath a mantle of soil and subsoil. Details are given of the successful use of this method in locating the outcrops of anthracite seams in actual prospecting. The presence of the outcrop of an anthracite seam is indicated at points where electrical resistivity tests showed relatively low readings. The reason for this is that in some localities the resistivity of anthracite was found to be about 0.0001 megohm-cm. compared to 1 to 200 megohm-cm. for shales and sandstones. For two reasons it is believed that the data summarized in this paper should be of particular interest. In the first place, most of the interpretations of the resistivity survey have been checked by subsequent drilling and some by the removal of the overburden and the exposing of the anthracite seams. It is infrequent that the opportunity for checking results so thoroughly is given. In the second place, the fact that recent commentatorsl,2,3 on the application of geophysical methods to mining have concluded that direct prospecting for anthracite and other types of coal is not promising makes the good results obtained more significant. So far as the authors can learn, the only previous experiment with electrical methods in the Pennsylvania anthracite field was one made by Sherwin F. Kelly in 1921, when he used the self-potential method at Wilkes-Barre4. The profile he made does not show a very marked correlation with the geologic cross section. Kelly points out that stray currents from electric motors in the mines undoubtedly affected 'his results, but the experience of the present authors with stray currents from mining machinery suggests the possibility that the potentials measured by Kelly were due almost entirely to this effect.

Jan 1, 1936

By Maurice Ewing, A. P. Craby, J. W. Peoples, J. A. Peoples

The purpose of this paper is to present the results of the application of the earth-resistivity method of subsurface investigation to the problem of locating seams of anthracite coal beneath a mantle of soil and subsoil. Details are given of the successful use of this method in locating the outcrops of anthracite seams in actual prospecting. The presence of the outcrop of an anthracite seam is indicated at points where electrical resistivity tests showed relatively low readings. The reason for this is that in some localities the resistivity of anthracite was found to be about 0.0001 megohm-cm. compared to 1 to 200 megohm-cm. for shales and sandstones. For two reasons it is believed that the data summarized in this paper should be of particular interest. In the first place, most of the interpretations of the resistivity survey have been checked by subsequent drilling and some by the removal of the overburden and the exposing of the anthracite seams. It is infrequent that the opportunity for checking results so thoroughly is given. In the second place, the fact that recent commentatorsl,2,3 on the application of geophysical methods to mining have concluded that direct prospecting for anthracite and other types of coal is not promising makes the good results obtained more significant. So far as the authors can learn, the only previous experiment with electrical methods in the Pennsylvania anthracite field was one made by Sherwin F. Kelly in 1921, when he used the self-potential method at Wilkes-Barre4. The profile he made does not show a very marked correlation with the geologic cross section. Kelly points out that stray currents from electric motors in the mines undoubtedly affected 'his results, but the experience of the present authors with stray currents from mining machinery suggests the possibility that the potentials measured by Kelly were due almost entirely to this effect.

Jan 1, 1936

By C. S. Barrett, C. T. Haller

Twinning in magnesium is known to occur profusely under certain conditions, and when it occurs in polycrystalline materials it brings about a partial or even a complete change in the preferred orientation. The amount of research on this subject, however, has not been in proportion to its importance as a mechanism of deformation and reorientation. Much of the research has been limited to twinning in single crystals. The present study1 concerns polycrystalline sheet, and is an investigation of the twinning produced by plastic deformation as a function of the following variables: 1. Direction and type of deformation. 2. Amount of deformation. 3. Speed of deformation. 4. Temperature of deformation 5. Composition and temper of the sheet. 6. Twins previously produced. 7. Twins previously produced, then annealed. By proper control of these variables it is shown that, on a laboratory scale, samples can be produced that are free from preferred orientations. The materials used were samples of commercial magnesium-alloy sheets with nominal compositions given in Table I. X-ray diffraction was used in most of this work to detect the twins and to estimate the amount of twinning. Since twinning on (102) planes causes a re-orientation of the crystal lattice by 86", it is very easy to study with X-ray diffraction patterns, particularly if one notices the diffraction ring from the basal plane— the 002 reflection. By properly directing the X-ray beam, it is possible to produce 002 reflections from twinned material at, say, the 6 and 12 o'clock positions on the 002 ring, with the untwinned material reflecting to 3 and 9 o'clock positions; and by judging the relative intensity of the arcs on the diffraction ring at these positions, it is possible to judge the amount of twinned material relative to the untwinned. This X-ray method of estimating the amount of twinning is generally superior to metallo-graphic observation, for it was found

Jan 1, 1947

By Lawrence B. Wright

The occurrence of gold, gold-silver, silver-lead-zinc ores in the post-Cambrian sediments in the Black Hills of South Dakota, and their genetic relationship to the Tertiary intrusives, is well known and accepted, but the occurrence of gold in the pre-Cambrian rocks at the Homestake mine, which underlie this Tertiary gold mineralization, has given rise to differences of opinion as to the period of major gold introduction into the older rocks. Fig. 1 illustrates the distribution of mineralization along the axis of the Tertiary uplift in both pre-Cambrian and post-Cambrian rocks. The following possibilities have been presented: 1. The Homestake gold deposit was formed in pre-Cambrian time and the deposits in the overlying Cambrian sediments formed during Tertiary time. 2. The Homestake lode existed at the beginning of Cambrian time, but was enriched by the passage of Tertiary auriferous solutions. 3. The Homestake lode was represented by pre-Cambrian quartz-chlorite sulfide mineralization, very low in gold content and the gold superimposed on the older nearly barren mineralization during the Tertiary metallogenic epoch. 4. The sulfides and sulfarsenides as well as gold were deposited in both pre-Cambrian and post-Cambrian rocks during the Tertiary period. Those favoring the first proposition feel that the question is pretty well settled, while the proponents of the second theory are more flexible in their view, feeling that the amount of gold introduced in either period is still an open question. The third and fourth theories, with some modifications, are supported by the proponents of the Tertiary theory, who feel that the evidence strongly favors that period. The following pages are intended to present the evidence and to give the reaction of various observers with my own comments and conclusions; also, the accumulated facts of observation gathered over a period of close association with the area under discussion, beginning in 1919.

Jan 1, 1937

By C. S. Barrett, C. T. Haller

Twinning in magnesium is known to occur profusely under certain conditions, and when it occurs in polycrystalline materials it brings about a partial or even a complete change in the preferred orientation. The amount of research on this subject, however, has not been in proportion to its importance as a mechanism of deformation and reorientation. Much of the research has been limited to twinning in single crystals. The present study1 concerns polycrystalline sheet, and is an investigation of the twinning produced by plastic deformation as a function of the following variables: 1. Direction and type of deformation. 2. Amount of deformation. 3. Speed of deformation. 4. Temperature of deformation 5. Composition and temper of the sheet. 6. Twins previously produced. 7. Twins previously produced, then annealed. By proper control of these variables it is shown that, on a laboratory scale, samples can be produced that are free from preferred orientations. The materials used were samples of commercial magnesium-alloy sheets with nominal compositions given in Table I. X-ray diffraction was used in most of this work to detect the twins and to estimate the amount of twinning. Since twinning on (102) planes causes a re-orientation of the crystal lattice by 86", it is very easy to study with X-ray diffraction patterns, particularly if one notices the diffraction ring from the basal plane— the 002 reflection. By properly directing the X-ray beam, it is possible to produce 002 reflections from twinned material at, say, the 6 and 12 o'clock positions on the 002 ring, with the untwinned material reflecting to 3 and 9 o'clock positions; and by judging the relative intensity of the arcs on the diffraction ring at these positions, it is possible to judge the amount of twinned material relative to the untwinned. This X-ray method of estimating the amount of twinning is generally superior to metallo-graphic observation, for it was found

Jan 1, 1947

By J. E. Burke, C. S. Barrett

THE fine lines shown in Fig 1 are typical of markings that may be detected after polishing and etching deformed specimens of alpha brass and other alloys. Although they have long been the subject of discussion by metallurgists their nature is still uncertain and the names that have been applied to them, such as deformation lines or strain markings, indicate this uncertainty. In this paper which reports the results of a further investigation of their nature, they will be called strain markings. INTRODUCTION Matthewson and Phillips1 in 1916 concluded that strain markings appeared only after deformations that exceeded 20 pct. They objected to the markings being called slip lines believing this term should be reserved for surface markings produced by plastic deformation. In 1921, Vogel2 described similar striations which appeared after polishing and etching the roughly ground surface of numerous alloys. He reported that the markings were crystallographic in nature, and since they resemble Neumann bands in iron, at least superficially, he assumed them to be mechanical twins. In 1928, Matthewson3 reported work by Phillips which indicated that the lines were more readily produced by impact than by slow deformation and that in many cases the twins inside recrystallized grains were parallel to strain markings in the original deformed grains. This was taken as evidence that the markings coalesce into annealing twins, and hence that they themselves are mechanical twins. Many attempts have been made to [ ] demonstrate directly that the markings are mechanical twins. In 1934, Samans4 described the results of X ray studies of two deformed crystals of alpha brass. Evidence was obtained which could be interpreted to indicate that the strain markings are mechanical twins, and this remains the only direct evidence to this effect. Several other attempts to obtain similar evidence by X ray diffraction have failed5,6,7 although in no case was the original method of Samans employed. An

Jan 1, 1948

By Ralph W. Smith

DEVELOPMENT of the lime industry- in Ste. Genevieve County began in a crude way in 1840. According to information furnished by the Missouri Bureau of Geology, in the early days small vertical kilns built of stone were used, and wood was the fuel. Modern development began in 1904 when one company introduced steel shells lined with firebrick. Within a few years two more companies erected similar plants, and in 1925 a fourth company began operations. Thus there are today four lime companies at Ste. Genevieve, all operating at high capacity and with a gradually increasing production. GEOLOGY The limestone of Ste. Genevieve County, which has the chemical composition and purity required for lime burning, is the upper 80 or 90 ft. of Spergen formation. The Missouri Bureau of Geology, in its geological map of Ste. Genevieve County, gives the Spergen formation a total thickness of 160 ft., but only the upper portion is pure enough for lime burning, with an average raw-stone analysis of 98.7 per cent CaC03; 0.35 Si02; 0.3 R203; 0.35 MgCO3; 0.3 S03. The Spergen, one member of the Meramac group, Iowa series, of the Mississippian system, underlies an area approximately 12 miles long north and south, by 5 miles wide east and west (Fig. 1) in Ste. Genevieve County. The entire eastern two-thirds of Ste. Genevieve County is sedimentary, the formations dipping gently toward the east on an average grade of about 4 per cent, or 2 ½ º. Thus the outcrops of the various sedimentaries run approximately north and south. A line running west from Ste. Genevieve crosses the outcrops of the sedimentaries, ranging from the top of the Mississippian to the Ozarkian geological system in a space of 12 miles. Thus with the gentle dip of 2 ½ º the 160-ft. thickness of the Spergen formation stretches out in its outcrop so that it is approximately one mile

Jan 1, 1938

By David Scott

THE MOGOLLON mining district, New Mexico, has received little public attention, although for 15 years it has been the leading silver producer of the state; it is situated in a region remote from the principal lines of travel, and its activities have usually been limited to the operations of two or three companies. The value of the total production of the district in the 44 years of its history has been estimated at $15,000,000. For the years 1904 to 1917, inclusive, the output was: gold, $4,370,000; silver, 10,042,000 oz.; copper, 874,862 lb.; total value, approximately. $10,500,000. In 1913 the district contributed 80 per cent. of the total silver production of New Mexico, but in 1917 only 41 per cent., due to serious interruption in the operations of the leading producer. Since 1914 the silver output has diminished one-half, and the present high value of silver is nearly offset by the increase in cost of production. The output of gold has rarely exceeded 35 per cent, of the total for New Mexico. The ratio of silver to gold, by weight, has averaged 46:1 based on the whole output of the district. LOCATION AND TOPOGRAPHY The town of Mogollon is 75 mi. (121 km.) by a poorly located highway from the nearest railroad terminals, at Silver City and Tyrone. All supplies are transported by motor trucks and teams. The area, sometimes called the Cooney Mining District, lies on the western flank of the Mogollon Mountains, which occupy the western part of Socorro County. The elevations drop steeply on the west to the valley of the San Francisco River, adjacent to the Arizona boundary. The topography is very rugged, the whole area being sharply dissected; deep canyons with steep gradients and rugged walls are characteristic of the whole western-slope of the Mogollon Range. The main canyons run east and west, and usually maintain a flow of water during the entire year. As would be expected in a region of such deep dissection, the

Jan 2, 1920

By Peter T. Luckie, Harold L. Lovell, E. R. Palowitch, A. W. Deurbrouck, James K. Kindig

PART 1: DENSE MEDIUM SEPARATION by E. R. PALOWITCH and A. W. DEURBROUK INTRODUCTION During 1965, 64.9 percent of the 512 million tons of bituminous coal and lignite produced was cleaned mechanically, of which 95 million tons was cleaned by dense medium processes.l The percentage of bituminous coal and lignite cleaned mechanically by dense medium processes rose from 7.0 to 28.5 percent from 1938 to 1965. Dense medium separations include those coal preparation processes which clean raw coal by immersing it in a fluid having a density intermediate between clean coal and reject. As there is a general correlation between ash content and specific gravity, it is possible to achieve the required degree of removal of ash-forming impurities from a raw coal by regulating the specific gravity of the separating fluid. Dense medium processes offer the following advantages over other coal cleaning processes : 1. Ability to make sharp separations at any specific gravity within the range normally required even in the presence of high percentages of the feed in the range of e 0.1 specific gravity units. 2. Ability to maintain a separating gravity that can be controlled with ±0.005 specific gravity units. 3. Ability to handle a wide range of sizes (up to 14 inches). 4. Relatively low capital and operating costs when considered in terms of high capacity and small space requirements. 5. Ability to change specific gravity of separation to meet varying market requirements. 6. Ability to handle fluctuations in feed both in terms of quantity and quality. HISTORY Sir Henry Bessemer patented the first dense medium process in 1858. Solutions of the chlorides of iron, manganese, barium and calcium were proposed as separating liquids; the separation was made in a cone-shaped separator. One large-scale plant using calcium chloride was erected in Germany but soon was abandoned. The Chance process, using a mixture of sand and water, was first

Jan 1, 1968

By Cyril Wells, Robert F. Mehl

The diffusion of carbon in gamma iron plays an essential role in many metallurgical processes. In carburizing, in graphitizing, in homogenizing, in the formation of pearlite from austenite, and in other processes, migration of carbon in gamma iron occurs.1'2 A full understanding of the rate at which these processes occur obviously requires a knowledge of the rate of diffusion of carbon. In carburizing, for example, the depth of carbon pentration is determined by the carbon concentration in solid solution at the surface, and by the rate of diffusion inward of the carbon. Until reliable data on the rates of diffusion of carbon are available it is unlikely that a full quantitative description of this process will be obtained. In the formation of pearlite from austenite, the segregation of carbon and alpha iron from the austenite obviously requires the diffusion of carbon; the rate at which pearlite nodules grow is evidently controlled at least in part by the rate of diffusion of carbon; it is unlikely that we shall understand the factors that determine the rate of growth unless data on rates of diffusion of carbon, and the variation of these with composition, grain size, and temperature are available. Accordingly it was decided: (1) to determine, more accurately than hitherto, the diffusion coefficients of carbon in austenite over a wide temperature and a wide concentration range, (2) to study the influence of grain size and impurities on this diffusion coefficient, and (3) to study the effect of manganese and nickel on the rate of diffusion of carbon in the austenite of manganese and nickel steels, respectively; the influence of carbon on the rate of diffusion of manganese and of nickel will be made the subject of later papers. The rate of diffusion of carbon in gamma iron has been studied by Runge3 by Tammann and Schonert4, by Bramley and co-authors,5-14 and

Jan 1, 1940

By Cyril Wells, Robert F. Mehl

The diffusion of carbon in gamma iron plays an essential role in many metallurgical processes. In carburizing, in graphitizing, in homogenizing, in the formation of pearlite from austenite, and in other processes, migration of carbon in gamma iron occurs.1'2 A full understanding of the rate at which these processes occur obviously requires a knowledge of the rate of diffusion of carbon. In carburizing, for example, the depth of carbon pentration is determined by the carbon concentration in solid solution at the surface, and by the rate of diffusion inward of the carbon. Until reliable data on the rates of diffusion of carbon are available it is unlikely that a full quantitative description of this process will be obtained. In the formation of pearlite from austenite, the segregation of carbon and alpha iron from the austenite obviously requires the diffusion of carbon; the rate at which pearlite nodules grow is evidently controlled at least in part by the rate of diffusion of carbon; it is unlikely that we shall understand the factors that determine the rate of growth unless data on rates of diffusion of carbon, and the variation of these with composition, grain size, and temperature are available. Accordingly it was decided: (1) to determine, more accurately than hitherto, the diffusion coefficients of carbon in austenite over a wide temperature and a wide concentration range, (2) to study the influence of grain size and impurities on this diffusion coefficient, and (3) to study the effect of manganese and nickel on the rate of diffusion of carbon in the austenite of manganese and nickel steels, respectively; the influence of carbon on the rate of diffusion of manganese and of nickel will be made the subject of later papers. The rate of diffusion of carbon in gamma iron has been studied by Runge3 by Tammann and Schonert4, by Bramley and co-authors,5-14 and

Jan 1, 1940

By F. L. Bosqui

The history of the development of gold metallurgy in South Africa is divisible into two periods: That preceding the introduction of the cyanide process on a commercial scale in 1890; and the 24 years intervening between that important event and the present time. The period between the discovery of the banket reefs of the Witwaters-rand and the year 1890 was one of phenomenally rapid progress in mining development, but of no special interest to the metallurgist, There were no strikingly original or distinctly local advances in the treatment of gold ores. Californian practice in stamp milling and amalgamation prevailed, in mills ranging in equipment between 5 and 50 stamps, operating within a wide range of efficiency, and under the trying conditions usually encountered in a new and isolated field. The somewhat incomplete records of gold output of that period show that in December, 1887, there were 20 producing companies in the Witwatersrand district, of which 10 had mills, the largest being of 20 stamps. The only official record of returns for May, 1887, was that of the Wemmer mine, whose modest achievement with a 5-stamp mill was 100 tons crushed, producing 887 oz. 3 dwt. of gold. This is interesting in view of the present-day output of this field, which in 1913 reached 8,430,998 oz. The rapid increase of production during this first period (May, 1887, to January 1891) is shown by the following summary for the year 1890:1 Total tone crushed.................................. 702,828 Number of stamps in operation....................... 1,046 Average number of tons crushed per stamp per day..... 2.36 Yield of gold, ounces................................ 494,817 Yield per ton, pennyweights.......................... 13.36 The stamp duty ranged between 11/2 and 4 tons per day, according to weight of stamp, fineness of screen, and operating skill available. The prevailing weight of stamp was about 900 lb., and the screen, 900 meshes to the square inch.

Jan 1, 1916

By R. M. Brick

THE etched microstructures of cold-worked alpha brasses, after reduc-tions in excess of about 20 per cent, exhibit dark lines or markings, which have been termed "deformation bands," "etch bands," and "strain markings." The terms will be used synonomously in this report. The markings are similar in their general appearance to etch figures found in cold-worked iron, aluminum and other cubic metals but in certain respects may differ noticeably. At reductions of from about 20 to 50 per cent in brass, they appear as straight dark lines of irregular spacing and at random directions in different grains, but apparently intimately associated with definite crystallographic planes, usually {111}, in each crystal. At higher reductions, the markings on the rolling plane tend to appear in a direction transverse to the rolling direction in all crystals but may bend away at considerable angles, particularly near grain boundaries. Samans,1 on the basis of X-ray and micrographic studies of two single crystals of brass, rolled to a 50 per cent reduction, showed that the lines of deformation were the edges of thin mechanical twins parallel to octahedral planes. Barrett and Levenson2-4 have made comprehensive studies of the deformation of iron and of aluminum. They show that in these two metals the deformation markings originate by division of the original homogeneous crystal into banded areas differing in orientation by an amount that increases with the degree of deformation. The markings thus cannot be twin bands, and Barrett, in a review of this subject,2 attributed Samans' results on brass to an accidental choice of deformation that left the bands in approximately a twinned relationship. On the other hand, Mathewson5 has suggested that in some cases mechanical twinning offers a better rationalization of the coverage of some (111) pole figures of worked brass than the assumption of band rotation into sym-metry positions. Considering next a deformed and annealed alpha brass, the most striking aspect of its microstructure is the multiplicity of twin bands.

Jan 1, 1940

By D. I. Bardos

The occurrence of Laves phases (AB,) in various binary alloy systems has been reviewed in recent papers.13 Iron forms Laves phases with Sc-, Ti-, V- and Cr-group elements. However, two of the corresponding Laves phases with cobalt, namely MoCo, and WCo,, are missing. Nickel forms binary Laves phases with Sc and Y, but not with any Ti-, V-, or Cr-group element. These conditions are schematically illustrated in Table I. That electron concentration is a significant factor in determining which type of Laves phase is formed in a given case was recognized long ago by Laves and Witte,4 This concept has been more recently applied to Laves phases formed by transition ele-ments. It now appears that the average electron concentration (average number of electrons per atom outside of the closed shells of the component atoms) may be an important factor also in determining whether or not a Laves phase can occur at all in a given system. As shown in Table I, in the transition element systems considered Laves phases are absent at electron concentrations of 8, or larger (to the right and below the double line in Table I). These absences clearly cannot be accounted for on atomic size considerations, as evidenced by the many inconsistencies apparent in Table 11. While the ideal radius ratio for Laves phases is 1.222, in the systems which do have Laves phases the ratios of CN 12 radii range from 1.10 to 1.46. The consistent absence of Laves phases at RA/RB< 1.10 might be attributed to the low values of these radius ratios. However, Table II shows that absences also occur irregularly throughout the radius ratio range covered. In a previous paper7 it was concluded that, in transition element systems forming u-phases, silicon may act as an acceptor of electrons, thus stabilizing the u-phase at electron concentrations higher than

Jan 1, 1962

By Paul M. Tyler

Mineral raw materials, because they are essential to our industrial prosperity and military strength, must be made available in substantial quantities. regardless of cost. Variations in the cost of procuring minerals, as compared with the cost of obtaining other commodities, and changes in the cost of production of different minerals relative to one another, will naturally influence the quantities of a given mineral item that can be marketed readily. However, in the last analysis, the cost of winning minerals from the ground usually constitutes only a small fraction of the value of the end-use products and services derived from them. The miner&apos;s share of the cost of a typewriter, telephone circuit, or even a modem office building, is almost insignificant. Far more important to the ultimate consumer, therefore, than any minor saving in cost is the assurance of ample supplies of the minerals needed to aliment our expanding economy. To create a successful metal mining operation involves ( 1 ) the discovery and systematic development of a mineral deposit, (2) extraction of the ore, (3) the mechanical and metallurgical processing to eliminate worth- less or harmful impurities, and (4) the profitable disposal of the product. The first step of the technological process belongs chiefly in the realm of the geologist, the second is a mining engineer&apos;s job, the third is mainly up to the millmen and extractive metallurgists; whereas the fourth and equally important step poses a commercial problem that has aspects in common with the marketing of other products. Ore finding is far from being an exact science. There is no mathematical criterion for evaluating the efficiency of prospecting and exploration. Lady Luck shares the honors or assumes part of the blame along with the prospector and geologist. Marketing like- wise involves factors that seemingly defy engineering analysis. Although the other steps can be measured with some degree of mathematical accuracy, even they tend to vary so widely in basic principle, as well as in

Jan 1, 1959

By G. S. Rice, J. A. Davis

The Péchelbronn oil field is located in the province of Alsace, in the Rhine Valley, about 30 miles north of Strasbourg. It is approximately 4 miles wide and 12 miles long, extending from the villages of Lobsann on the north to Wintershausen and Ohlungen near Haguenau on the south. (See Fig. 1.) The productive area includes about 44,000 hectares (107,680 acres). The name Péchelbronn signifies "pitch-spring" or "pitch-fountain." The first exploratory galleries were driven in from the hillside in 1735; and in 1745 the first official concession was granted by the French government and the first pit sunk to a depth of about 30 ft. Extraction by drilled wells was begun in 1879, supplementing the mining operations, and during the next 10 years 200 wells were drilled to an average depth of 172 m. (568 ft.). The bringing in of two "gusher" wells, in 1882 and 1888, respectively, was followed by the abandonment of all underground work. Underground mining, with a view to increasing the production of petroleum by recovering the oil left in the sands after drilling wells, was resumed in 1916. This mining operation started by sinking shaft No. 1 to a depth of 150 m. (495 ft.). The underground developments were pushed during 1917 and 1918 and the annual production of the Péchel-bronn field was increased to about 50,000 metric tons or 350,000 bbl. On the signing of the Versailles Treaty the province of Alsace, which had been taken by Germany as the result of the war of 1870, was returned to France, and the proprietary rights were taken over by the French Government. Concessions or leases, which embraced all the known oil-bearing territory of the field, were granted to the present operating company, Mines de Péchelbronn. This company followed both the drilling and the mining methods of the previous company.

Jan 1, 1927

By D. K. Crampton

Internal stress and season cracking in brass have been studied for many years and the technical literature contains many data on various phases of the subject. A resume of the literature shows certain fairly well established points upon which various authors are mostly agreed: 1. Season cracking is primarily caused by the presence of relatively high internal stresses, or possibly in some cases by external stresses, or both. 2. A specific corrosion is also essential to season cracking. Certain agents, particularly mercurous salts, mercuric salts and ammonia salts, have such a specific corrosive effect. 3. The tendency to season crack under given conditions increases with increasing zinc content, brass containing less than 20 per cent. zinc being relatively immune. 4. In alpha brass the season cracks are intercrystalline; in alpha-beta brass they lie between the two constituents; and in beta brass they are transcrystalline. 5. The ordinary impurities or added elements in special brasses have little or no effect on the tendency to season crack. 6. Internal stresses can be eliminated, or at least reduced to a safe limit by annealing treatments at temperatures that do not produce visible microstructural changes or appreciable softening of the worked brasses. There are, however, some points in connection with the phenomenon of season cracking which have not been thoroughly investigated, or wherein different authors and investigators are not entirely in agreement. The investigations described in this paper were undertaken to determine: 1. The correlation between mercurous nitrate tests and actual season cracking on long-time atmospheric exposure. 2. The quantitative effect of type and degree of drawing operations on the intensity of internal stress and on the tendency to season crack in brass tubes. 3. The possibility of drawing high-brass tubes in such a manner as to prevent the occurrence of harmful stresses rather than to find a remedy for such stresses once having obtained them.

Jan 1, 1930