By Charles Clayton

CAST-STEEL runners, while not interesting from a commercial standpoint, furnish valuable material for microscopic study. Foley1 found not only the usual ingot structure, but zones of Widmannstattian structure, which he explains as due to differential crystallization. The writer, in examining nickel-steel runners, found a type of pro-eutectoid ferrite that is unusual and most probably new. The runner in question was 8.75 cm. (3.5 in.) in diameter and analyzed at its center 2.69 per cent, nickel and 0.350 per cent. carbon and at its edge 2.62 per cent. nickel and 0.359 per cent. carbon. The macrostructure, which is the usual type, is shown in Figs. 1 and 2, which are a cross-section and the longitudinal surface, respectively. Slight segregation of ferrite can be seen near the center of the segment and at other points near the edges of polyhedral grains. Stead's reagent brings out the dendritic structure within the grains as shown in Figs. 3 and 4. This texture is what would be expected of such a steel. Figs. 5 to 10 show the peculiar swirls of pro-eutectoid ferrite, the finding of which prompted this paper. These swirls, or eddies, if such a term can be applied, occur in all parts of- the runner and in all parts of the individual grains. I he tipper left-hand figure shows this ferrite at a grain boundary; the middle left-hand figure shows the inner portion of a grain; and the lower left-hand figure shows these swirls at the edge of a grain which is also the outer edge of the runner. Straight-lined ferrite associated with swirls is found in the areas of Figs. 11 and 12. The texture of the carbon-bearing constituent of the runner is shown to- some extent in Fig. 12, the pearlite being very fine or sorbitic. Higher magnification does not bring out any new features either in the peculiar ferrite or in the pearlite. Figs. 13 and 14, at 240 diameters, show the curved and straight-lined ferrite.

Jan 3, 1920

By M. G. Corson

Until recently, the characteristics of cast copper have seldom been studied and such study as has been made has been inadequate. The prevailing idea seems to be that since pure copper is infrequently used in the cast stlate, there is no reason for trying to establish precise data regarding the properties of the metal in that condition. On the other hand, wrought copper either in the shape of sheets or wire rarely fails in service, except as a result of the action of reducing gases at the annealing temperatures, so there is little incentive to study the properties of the cast shapes —cakes, bars, ingots and billets—for the sake of tracing the causes of failures of the wrought metal to the cast stock. However, about a decade ago, wirebars of American origin often cracked badly while being hot-rolled in mills in Germany. This Icd to four investigations: by E. Seidl and E. Schieboldll by P. Siebe12 by 0. Bauer and G. Sachs,3 and by G. Welter.4 These authors came to the conclusion that failures in hot-rolling were due essentially to the presence of a wide zone of columnar crystals between t'he thin layer of fine crystal5 near the surfaces of the bars and the large but more nearly equiaxed grains of the central core. This macrostructural defect was explained in turn by the probable upward deviation in the temperature of the metal while it was being poured into the molds of the castling machine. More recently, cast shapes of copper were investigated by X. 1'. Allenh and by C. Blazey. Allen examined vertically cast wirebars and hori-zontally cast wedge cakes of electrolytic tough-pitch copper, but only for the distribution of densities; i.e., porosity. Blazey was interested mainly in the mechanism of the variations in electrical conductivity due to cold-work and anneal, but gave introductively an account of the composi-tion and average densities of the tough-pitch horizontally cast Wirebars used. As far as the present writer can tell, no investigation mas under-taken for the sake of presenting a picture of the distribution of mechanical characteristics in the wirebars of copper, or otherwise.

Jan 1, 1938

By M. G. Corson

Until recently, the characteristics of cast copper have seldom been studied and such study as has been made has been inadequate. The prevailing idea seems to be that since pure copper is infrequently used in the cast stlate, there is no reason for trying to establish precise data regarding the properties of the metal in that condition. On the other hand, wrought copper either in the shape of sheets or wire rarely fails in service, except as a result of the action of reducing gases at the annealing temperatures, so there is little incentive to study the properties of the cast shapes —cakes, bars, ingots and billets—for the sake of tracing the causes of failures of the wrought metal to the cast stock. However, about a decade ago, wirebars of American origin often cracked badly while being hot-rolled in mills in Germany. This Icd to four investigations: by E. Seidl and E. Schieboldll by P. Siebe12 by 0. Bauer and G. Sachs,3 and by G. Welter.4 These authors came to the conclusion that failures in hot-rolling were due essentially to the presence of a wide zone of columnar crystals between t'he thin layer of fine crystal5 near the surfaces of the bars and the large but more nearly equiaxed grains of the central core. This macrostructural defect was explained in turn by the probable upward deviation in the temperature of the metal while it was being poured into the molds of the castling machine. More recently, cast shapes of copper were investigated by X. 1'. Allenh and by C. Blazey. Allen examined vertically cast wirebars and hori-zontally cast wedge cakes of electrolytic tough-pitch copper, but only for the distribution of densities; i.e., porosity. Blazey was interested mainly in the mechanism of the variations in electrical conductivity due to cold-work and anneal, but gave introductively an account of the composi-tion and average densities of the tough-pitch horizontally cast Wirebars used. As far as the present writer can tell, no investigation mas under-taken for the sake of presenting a picture of the distribution of mechanical characteristics in the wirebars of copper, or otherwise.

Jan 1, 1938

By C. A. Rowland, R. C. Nealey

Until recently there were very few dry grinding rod mills used. The early installations performed as anticipated. In the last seven years a number of dry grinding rod mills have been made, most of which have been used for grinding iron ore. The recent installations have not operated as anticipated in accordance with practices learned from wet rod milling. The paper does not establish any definite rules for the application of dry grinding rod mills but does attempt to establish some guidelines that can be followed. The paper reviews a number of flowsheets describing the problems encountered and some of the solutions found. Completely dried compared to partially dried feed is reviewed. Problems encountered in scaling up from pilot plant to production-size mills are described. Rod sizing, effect of rod length, rod bending, rod breakage, and rod tangling are discussed. While wet grinding rod mills have been used for 50 years to grind ores and make specifications sands, dry grinding rod mills have only recently come into significant use in the mineral industries. Among the materials now being processed in dry grinding rod mills are (1) lead sinter, lead slag, and limestone; (2) iron ore; (3) silica; (4) cement clinker; and (5) coke. Because the application of wet grinding rod mills was well understood at the time that dry grinding rod mills were introduced, the criteria and guidelines for selecting the former were carried over to the selection of the latter - in some cases with the anticipated results, but in many cases not. It is the purpose of this paper to describe, through a series of flowsheets, some of the recent problems encountered with dry grinding rod mills, to point out the solutions to these problems, and to set forth some guidelines for the selection and application of these mills. When dry grinding rod mills came into use, the following facts about their wet grinding counterparts were already well established: (1) The performance of large-sized mills can be accurately predicted from the performance of rod mills 5 or 6 ft in diameter. Wet grinding mills as large as 14 ft in diameter (inside shell) by 20 ft long with rods 19.5 ft long can operate satisfactorily.

Jan 1, 1970

By Thomas M. Price

Sand production for use in hydraulic concrete is probably the most important element affecting the physical characteristics of the resulting concrete in the opinion of most engineers, aggregate producers and contractors of today, who are engaged in the effort to produce stronger concrete per unit of cement used. Their opinion is based on both laboratory and field results. In the past, proper cement production has been the object of most of the study given this subject and while it is still studied by the extensive and well equipped laboratories that are a part of every cement mill, as well as by all governmental laboratories, at the present time the object of most of these studies has been in the field of low heat and quick setting qualities rather than the effect on the strength of the concrete. It is recognized that concrete must have two important qualities; namely, workability with the least water possible, and uniformity. These qualities have been accepted as axiomatic and possible to obtain if the foreman in charge knew his business. Now, however, with concrete produced by plants that mechanically weigh and chart all the ingredients, including water, of a batch of concrete, the foreman cannot cut and fit his aggregates, cement and water to fit his own desires and the secret of the important qualities of workability and uniformity are found to lie largely in the sand, hence the attention given its production at the present time. With this condition in mind the engineers of the United States Bureau of Reclamation and the Six Companies Incorporated in designing the plant for producing the aggregates for the Boulder Canyon Project included every possible means for the production of a sand of a constant and acceptable fineness modulus as well as a constant moisture content, and for attaining these results with as few detrimental ingredients, like silt and vegetable matter, as possible. This aggregate plant (Figs. 1 and 2) is in Hemenway Wash, 7 miles north of Boulder City. It is 4 miles upstream from the low-level mixing plant. At this screening plant 8,234,000 tons of raw aggregate are being

Jan 1, 1934

By Arthur C. Green

A group of 13 cities situated in Los Angeles and Orange counties in Southern California is engaged in constructing an aqueduct to carry water from the Colorado River at a point near Parker, Arizona, to a distribution point near Riverside, California. The aqueduct will have a total length of approximately 241 miles, and is designed to deliver 1605 cu. ft. of water per second, or a little more than one billion gallons per day. The aqueduct crosses a barren, desert waste and the project includes approximately 91 miles of 16-ft. tunnel. The large amount of tunnel driving that has been done in this country in the past few years has resulted in some remarkable developments in equipment and methods. The building of the Colorado River Aqueduct,, with its 91 miles of tunnels, has called on the best engineering knowledge in the country. New and better equipment has been designed for all phases of the work, and this equipment has been coordinated and adapted to the various conditions with a high degree of efficiency. The result has been that records for tunnel driving have been set under adverse natural conditions that exceed the estimates for progress under good conditions. All of the tunnels in the main aqueduct, except the Valverde and Bernasconi at the western end, have a finished diameter, inside the concrete lining, of 16 ft. Fig. 4 shows a section of the tunnel with the concrete lining in place. Fig. 5 illustrates the finished tunnel in three typical sections. The standard tunnel grade is 3.432 ft. per mile in the 16-ft. tunnels, but the Valverde and Bernasconi tunnels have a steeper grade and a finished diameter of 15 ft. 3 in. The rough bore of the large main aqueduct tunnels averages 12.95 solid cubic yards of material per foot of advance in timbered sections and 10.76 solid cubic yards per foot in unsupported sections. Tunnel Driving While the Conway mucker has been used on tunnel work for years, a larger and more powerful Conway was designed to meet the require-

Jan 1, 1937

By Wilson T. Lundy

The history of the production of sulfur from salt domes in Louisiana and Texas originated with the operations of the Union Sulphur CO. at Sulphur, La., followed by the Freeport Sulphur Co. at Bryanmound, Tex. Including the present development of Grande Ecaille by the Free-port Sulphur Co., which constitutes the tenth dome to be equipped for the production of sulfur in the Gulf Coast, less than 10 per cent of all the known domes have proved to contain sulfur in commercial quantities. The Grande Ecaille salt dome is in the tidal marsh of the Mississippi River delta in Plaquemines Parish, Louisiana. It is 10 miles southwest of the right descending bank of the river approximately 45 miles below the city of New Orleans and is within 4 miles of the shore line of the Gulf of Mexico. Terrain Characteristic of the delta region, the terrain consists of a low, flat, uninhabited area of marsh land intersected by many shallow lakes and bayous. With the exception of salt grasses, the region is devoid of vegetation and presents, in all directions, an unobstructed path to the vagaries of the winds. The general character of this area can be best visualized from the mechanism of its formation.' Offshore bars formed enclosing long narrow lagoons between the bar and the inner shore line, the lagoons communicating with the sea by means of tidal inlets. The water in the lagoons, being comparatively quiet, favored the deposition of fine debris composed of sand carried into the lagoons by action of the waves, tides and river-borne sediments from the land surface. As this material accumulated the bottoms of the lagoons were built up and eventually salt grasses obtained a foothold. The successions of growth and decay of these grasses formed a brown fibrous mat varying in depth from a few inches to several feet. This mat of vegetation virtually floats on an ooze that is several feet thick and is composed of alluvial sediments and very fine sand, and the whole is underlain by an unctuous clay. The decayed vegetation from the upper layer when dried has a peaty appearance.

Jan 1, 1934

By Y. C. Liu, R. H. Richman

From rolling textures of polycrystalline AgCl determined as a function of temperature, changes in the amounts of the individual textural components are correlated with temperature-dependent changes in glide geometry. The preferred orientations are influenced by the slip behavior as follows: 1) pencil glide, characterized by (110) slip directions and a greater participation in the deformation the higher the temperature, leads to a(012) fiber texture; 2) low-temperature deformation, primarily on (110) (110) systems, generates the {237}-(11, 9, 7) component; and 3) slip on {111}(110), comprising a significant portion of the room-temperature deformation, generates the {135}(211) and {110}(112) components. Typical re crystallization textures are also presented and briefly discussed. SPECIFIC relations between flow mechanisms in crystals and the individual orientations or components in deformation textures are necessary for a thorough understanding of the origin of such textures. Within each ordinary class of crystal struc- tures there is insufficient variety in the observed preferred orientations to permit direct and unambiguous correlation between flow mechanism and texture. A second approach to this problem is the correlation of textural changes with some known variation in glide geometry within one substance,1 In this paper, the latter approach is applied directly to a material in which there are distinct changes in the character of glide with changes in temperature. Silver chloride, although a nonmetal, is reported to exhibit slip,2,3 fiber textures,4 and rolling textures5,6 crystallographically similar to those of the well-studied fcc metals;7,8 in addition, there is a marked temperature sensitivity of the glide planes upon which flow occurs.3 Previous investigations of textures in AgCl unfortunately did not employ methods sufficiently sensitive to define possibly important minor components in the texture, nor did they utilize the temperature dependence of the glide systems. Thus, in order to clarify the effects of changes in slip mechanism, this paper reports a survey, using semiquantitative methods, of preferred orientations in rolled AgC1. Inasmuch as the influence of prior deformation texture upon preferred orientations after annealing is also of interest, some representative annealing textures are presented.

Jan 1, 1965

By M. J. Sinnott, J. C. Tobin

A technique for collecting and analyzing the small quantities of gases desorbed on heating metal powders has been developed. The gases collected from copper powders of various types of manufacture have been analyzed and found to contain H2O, CO2, and SO2. The quantities of gas evolved vary from 0.05 to 1.0 milliliter, under standard con-ditons of temperature and pressure, per gram of powder. The source of the gas has been traced to surface films on the powder. IN the powder-metal industry it is recognized that the presence of gases in the powders affects the processing and resulting properties of the sintered product. Several sources for these gases are possible; namely, chemical reactions with the sintering atmospheres, inclusion. of gases during compacting, dissolved gases in the metal powder, and sorbed gases on the metal-,powder surfaces.1, 2, 3 Since the quantities of the gases are relatively small, no direct attempt has been made to collect and analyze them nor to isolate their source. The work that has been done has been concerned with the dimensional stability of the product., its porosity, density, or mechanical and physical properties. Conclusions are drawn on the basis of studies of this type as to the probable effect of gases on these properties. 4, 5, 0 In the present investigation an attempt has been made to obtain quantitative data on the analysis and quantities of gases associated with copper powders manufactured in different ways. Apparatus was constructed to collect gases evolved from loosely packed powder samples on heating to various temperatures under a reduced pressure of helium. The powders were outgassed thoroughly in a vacuum prior to starting the collection operation in order to eliminate mechanically entrapped gases and to prevent the possible reaction of the powder with these gases. Experimental Procedures Materials—The major portion of the investigation was carried out on a single heat of water-atomized, oxygen-free, high-conductivity copper. A relatively coarse fraction of this powder, 20 to 100 mesh, was tested as a mixed powder and as various graded size fractions. The microstructure of this powder showed equiaxed grains and was clean and free from oxides and oxide eutectic. The particle size, as determined

Jan 1, 1959

By P. W. George

This paper presents geological data regarding deposits of over 7,500,000 tons of fine-grained sulphide ore in barite gangue. A series of pyroclastics and arkoses was intruded by sills of quartz porphyry in connection with batholithic intrusions of granite 3 miles from Buchans. Gentle folding, with fracturing and shearing of tuff beds and intruded quartz porphyry, accompanied and followed the intrusion of granite and porphyry. The sulphide-barite mineralization is localized primarily in fractured and sheared tuff beds, but also in the sheared quartz porphyry. Two structures have proved particularly favorable for mineralization—one, the center of an anticline; the other, a series of weak, incompetent tuff beds intruded by thin sills of quartz porphyry and located between strong beds of arkose. During the folding the weak tuff with intruded quartz porphyry was intensely sheared and contorted and subsequently mineralized by sulphides and barite. Introduction Buchans is 5 miles north of Red Indian Lake, in Central Newfoundland, at an elevation of 900 ft. above sea level and 400 ft. above Red Indian Lake, and is reached by a 37-mile private railway from Miller-town Junction. The first ore body found at Buchans was discovered some 30 years ago in the bed of Buchans River, by Matty Mitchell, an Indian woodsman employed by the Anglo-Newfoundland Development Co. Ltd. In the years following the discovery the ore was developed by shaft-sinking and drifting, with results indicating a lenticular ore body in a shear zone, containing about 100,000 tons of extremely fine-grained sulphide ore in barite gangue averaging about 0.05 oz. Au, 4 oz. Ag, 1.5 per cent Cu, 10 per cent Pb, 18 per cent Zn. Because a profitable metallurgical treatment for the ore was not found, the mine was closed down in 1911. In 1915, Mr. H. A. Guess, Vice President of the American Smelting & Refining Co., learned of the Buchans River ore body, and after metallurgical tests had been carried on from time to time in his company's testing plant a satisfactory separation of the sulphides by selective flotation was finally effected in 1925. Prospecting for additional ore bodies was begun in 1926, utilizing geophysical methods under the direction of Hans Lund-

Jan 1, 1937

By George Enos

As the coating formed affects the corrosion rate, duplicate samples of eight non-ferrous alloys were placed in flowing mine water. The alloys tested were as-cast or as-rolled and machined or polished. The paper describes the tests and gives the corrosion losses and the appearance of the samples at the end of the test. AN IMPORTANT factor affecting the rate and nature of corrosion of metals and alloys is the film, or coating, formed on the surface; and this may accelerate or retard corrosive action once started. The formation of films and coatings is intimately associated with the chemical composition and physical constitution of both the metal and the corroding medium. A film or coating may be either the corrosion product resulting from oxidation; that is, an oxide or salt, or a deposition of suspended matter from the corroding media upon the surface of the metal, or a mixture of both. The coating may adhere tightly or loosely to the surface of the corroded metal. In short, a film or coating is the reaction product of the corroding medium and the metal, which adheres to the surface of the metal and with which may be intermingled material from the attacking media not concerned in the chemical reactions. As the, terms film and coating are used by different writers for very different things, distinction is made between the two, by the present writers, on the basis of thickness. Thus, a film is defined as a corrosion product or deposition, on the surface of a corroded metal, that is of such thickness that it cannot be measured by the metallurgical microscope. A coating, on the other hand, is of such thickness that it can be measured. If the resolving power of the 2 mm. (equivalent focal length) apochromatic oil immersion objective (N.A. 1.4) is taken as the limit of the microscope, the limiting resolution is two lines that are 0.0002-0.0004 mm. apart. It is thus possible to measure coatings that are greater than 0.0002-0.0004 mm. thick. This thickness is equivalent to 200,000-

Jan 7, 1924

By Orrin P. Peterson

The decision of the Supreme Court -of the United States not to review the findings of the lower courts closes an interesting chapter in the mining litigation that has arisen as a result of the extralateral feature of the mining law. The time seems opportune to record some of the important geological features, and also some of the legal features, of the controversy, in the hope that these will be permanently accessible to members of the mining profession. After many rumors of litigation, the Utah Consolidated Mining Co. sued its neighbor for the ore that had been, it was alleged, wrongfully extracted from its so-called Yampa limestone lode. This ore lay beneath Utah-Apex surface and was claimed by virtue of the extralatera1 rights conferred on the Utah Consolidated Co. through the ownership of certain specific mining claims, one of the principal claims being the Yampa. Previous to bringing suit, the Utah Consolidated Co. had strengthened its position by purchasing the Old Yampa mine and by making an agreement with the Utah Metal & Tunnel Co., which gave it clearer title to the outcrop of the Highland Boy limestone. Access to the workings of the Utah-Apex Co. was secured and reciprocal privileges gave Utah-Apex representatives the right to enter the properties of the Utah Consolidated Co. This resulted in the Utah-Apex immediately bringing countersuit for ore alleged to have been wrongfully extracted from under its surface in the Leadville country, see Fig. 4. Six cases came up for consideration: five related to the original suit and the countersuit, and one related to the Dana extralateral claims of the Utah-Apex Co. Well-known attorneys, geologists, and mining engineers were engaged by both sides, and thousands of feet of development work were done to prove or disprove ideas that would sustain the contentions of the opposing sides. Models of wood, wire, and glass were constructed to present clearly to the court the actual physical relations. These models were also of great value to the attorneys and witnesses in clarifying hazy impres-

Jan 1, 1924

By I. Cornet

INTRODUCTION WITH the greatly expanding use of magnesium during the war, it appeared necessary to the War Metallurgy Committee that the notch sensitivity of magnesium alloy extrusions be further investigated and the influence of various factors upon notch sensitivity be noted. Accordingly, the National Defense Research Committee of the Office of Scientific Research and Development placed a research contract with the University of California, supervised by the War Metallurgy Committee. The work discussed herein was done under "Restricted" Project NRC-21, reported in Dec. 1943 1; it has been released for publication by the O.S.R.D. SCOPE OF THE INVESTIGATION The notch sensitivity of various magnesium alloy extrusions was determined under axial tension, and also under several conditions of nonaxial tension. Hardness, grain size and other metallographic features were observed; stress-strain data were obtained, and the chemical compositions of the alloys were determined, in order to correlate these quantities with the notch sensitivity. Notch sensitivity under axial tensile load was determined for a few specimens which had been cold worked to various degrees by tensile prestraining. Magnesium alloy extrusions studied included Dowmetal 0, X, J, and M. For comparison, extrusions of aluminum alloy 24S-T, cast bars of aluminum alloy I22-T2, and cast bars of magnesium alloy C were also tested, The specified chemical composition of these alloys is given in Table I. All bars tested were within specification limits of composition. Investigation of the tensile notch sensitivity of various magnesium alloy extrusions, under conditions of axial and eccentric load, showed little or no correlation with stress-strain or other conventional data. Since the many uncontrolled variables present might mask significant relationships, one alloy was selected for intensive study. Magnesium 0 alloy extrusions were subjected to experimental heat treatments, and the changing hardness, tensile strength, microstructure, and notch sensitivity observed. EXPERIMENTAL TECHNIQUES AND PROCEDURES Tensile Testing Bars used for axial loading were machined with 3/8 in.- and with 1/4-in. minimum diam, and included specimens with 6o° V notches (Fig I and 2). Each V-notched specimen was roughed out carefully and then finished with a honed tool. These V-notched bars were sampled frequently, sectioned, polished, and examined at 500 X magnification to control

Jan 1, 1948

By J. P. Pritchard, J. T. Pierce, O. G. Slay

This paper discusses the results of a technology-evaluation program to ascertain the feasibility of a piotornask-photoresist technology developed for fabrication of multiple-layer thin-film superconductive circuitry. The uehicle selected for this evaluation was a 120-bil associative data processor requiring a set of nine photomasks to define a similar number of patterned material layers of lead, tin, and polymer insulation. A total circuit area of 4 sq in. involved 2500 actitle and 12,000 passive crossings. Several short-free, electrically continuous specimens were satisfactorily completed under this program. Problems encountered in the preparation and use of the requi-ed set of Photomasks are discussed, as also are the problets of providing suitable external connections. A major retarding factor in the development of the superconducting thin-film cryotron technology for many years was the absence of batch fabrication means yielding necessary device density and count per substrate for practical applications. Early workers in the field desired only limited numbers of devices to permit careful study of discrete devices and representative circuitry integrating logic and memory capabilities. For these purposes mask stencils could be formed to selectively control the placement of materials, sequentially vapor-deposited in vacuum, to form the multilayer structure. In general a distinct pattern was required for each material layer; therefore, mechanical provisions were required to change not only the material source, but the patterning mask as well, before each deposition. All deposition steps were preferably performed in a single evacuation of the deposition chamber. Thus the means for storing, transporting, and registering masks and sources with respect to the substrate existed and were operated within the vacuum environment. In the authors' experience, the approach was and remains serviceable for preliminary device study, but was not extensible to an economical manufacturing method by virtue of the difficulties inherent in mask stencil preparation and use, and the capital investment implicit in the mechanization requirements. Since the commercial attraction of the cryotron technology stems principally from its potential for economical batch fabrication, the authors' program has placed major emphasis on fabrication methods. A highly useful method has evolved through adaptation

Jan 1, 1967

By C. Hays, R. E. Swift, E. G. Kendall

Investigations of the Zr-Pt system, by metallography, incipient melting, and X-ray diffraction, determined the phase relationshifis from 0 to 50 at. pct Pt. Phase fields in the Pt-~ich region were outlined, and three intermetallics (ZrPt, Zr2Pt, and ZrPtd were located. A eutectic between Zr and Zr2Pt, and a eutectoid veaction between Zr and a Zr + Zr2Pt, were established. The maximum solubility of Pt in P Zr was approximately 13.5 wt pct, as opposed to less than 1 wt pct solubility in a Zr. EARLIER work on the Zr-Pt system was limited to an X-ray study on the intermetallic compound, ZrPt3, by H. J. Wallbaum,1 It was reported that ZrPt3 existed at 86.52 wt pct Pt, and had a hexagonal structure, isomorphous with TiNi3. Wallbaum's data revealed the following structural particulars: a = 5.633A, c = 9.21A, and c/a = 1.635A. Other studies allied to Zr-Pt alloys concerned only 1) Pt-rich alloys (0.05 to 5.0 pct Zr) for corrosion resistance,2 2) a Zr-base alloy with 5 pct Pt and 0.124 pct C for oxidation resistance,3 and 3) electroclad-ding of Zr with Pt for in-pile corrosion resistance of Zr to uranyl sulphate. 4 Metallographic, incipient melting, and X-ray diffraction techniques were applied to accurately resolve the phase relationships in the 0 to 50 at. pct (68.2 wt pct) Pt region, and to outline the phase fields in the Pt-rich area. Three intermediate phases: Zr2Pt, ZrPt, and ZrPt3, were also established by the same methods. PROCEDURE Melting stock for this program was of the highest purity obtainable. The Zr was iodide crystal bar with a low hafnium content of about 0.05 wt pct (Westinghouse "Grade 3"). The as-received Zr was treated to remove the surface film of corrosion product that resulted from a standard autoclave grade designation test. Next, the bars were processed to yield material suitable for arc melting and free of contaminants. Sheet platinum metal (Baker and Co. "Grade 2") was used for alloying additions. This material con-

Jan 1, 1962

By Charles Y. Clayton

Cast-steel runners, while not interesting from a commercial standpoint, furnish valuable material for microscopic study. Folcyl found not only the usual ingot structure, but zones of Widmannstättian structure, which he explains as due to differential crystallization. The writer, in examining nickel-steel runners, found a type of pro-eutectoid ferrite that is unusual and most probably new. The runner in question was 8.75 cm. (3.5 in.) in diameter and analyzed at its center 2.69 per cent. nickel and 0.350 per cent. carbe a and at its edge 2.62 per cent. nickel and 0.359 per cent. carbon. Th macrostruc-ture, which is the usual type, is shown in Figs. 1 and 2, which are a cross-section and the longitudinal surface, respectively. Slight segregat'ion of ferrite can be seen near the center of the segment and at other points near the edges of polyhedral grains. Stead's reagent brings out the dendritic structure within the grains as shown in Figs. 3 and 4. This texture is what would be expected of such a steel. Figs. 5 to 10 show the peculiar swirls of pro-eutectoid ferrite, the finding of which prompted this paper. These swirls, or eddies, if such a term can be applied, occur in all parts of the runner and in all parts of the individual grains. The upper left-hand figure shows this ferrite at a grain boundary; the middle left-hand figure shows the inner portion of a grain; and the lower left-hand figure shows these swirls at the edge of a grain which is also the outer edge of the runner. Straight-lined ferrite associated with swirls is found in the areas of Figs. 11 and 12. The texture of the carbon-bearing constituent of the runner is shown to some extent in Fig. 12, the pearlite being very fine or sorbitic. Higher magnification does not bring out any new features either in the peculiar ferrite or in the pearlite. Figs. 13 and 14, at 240 diameters, show the curved and straight-lined ferrite.

Jan 1, 1922

By Charles Y. Clayton

Cast-steel runners, while not interesting from a commercial standpoint, furnish valuable material for microscopic study. Folcyl found not only the usual ingot structure, but zones of Widmannstättian structure, which he explains as due to differential crystallization. The writer, in examining nickel-steel runners, found a type of pro-eutectoid ferrite that is unusual and most probably new. The runner in question was 8.75 cm. (3.5 in.) in diameter and analyzed at its center 2.69 per cent. nickel and 0.350 per cent. carbe a and at its edge 2.62 per cent. nickel and 0.359 per cent. carbon. Th macrostruc-ture, which is the usual type, is shown in Figs. 1 and 2, which are a cross-section and the longitudinal surface, respectively. Slight segregat'ion of ferrite can be seen near the center of the segment and at other points near the edges of polyhedral grains. Stead's reagent brings out the dendritic structure within the grains as shown in Figs. 3 and 4. This texture is what would be expected of such a steel. Figs. 5 to 10 show the peculiar swirls of pro-eutectoid ferrite, the finding of which prompted this paper. These swirls, or eddies, if such a term can be applied, occur in all parts of the runner and in all parts of the individual grains. The upper left-hand figure shows this ferrite at a grain boundary; the middle left-hand figure shows the inner portion of a grain; and the lower left-hand figure shows these swirls at the edge of a grain which is also the outer edge of the runner. Straight-lined ferrite associated with swirls is found in the areas of Figs. 11 and 12. The texture of the carbon-bearing constituent of the runner is shown to some extent in Fig. 12, the pearlite being very fine or sorbitic. Higher magnification does not bring out any new features either in the peculiar ferrite or in the pearlite. Figs. 13 and 14, at 240 diameters, show the curved and straight-lined ferrite.

Jan 1, 1922

By Harry V. Welch

Early in the development of the art of metallurgy, it was noted that a distinct difference existed in the character, collection possibility and health hazard of the "smoke" from lead furnaces and those from copper plants. Zinc-plant fumes, although not so detrimental to health, were closely allied in nature to those of the lead works. In Cottrell plants, there are sufficiently distinct differences in operation and amount of construction between those for lead and copper to justify their consideration under separate headings; therefore, while the application of the process at copper-reduction works was covered by the writer some two years ago in the Transactions1,† this discussion will confine itself more distinctly to "fume" collection. General information on the process has been presented in numerous articles and by many authors: Cottre112, Schmidt3, Bradley4, Anderson6, Labbe6, Shiga7, Rathbun8. "Fume" may be defined as material, metal or nonmetal, elemental or compound, evolved as a vapor from a furnacing or chemical reaction and condensing, chilling or reacting within the gas stream to yield a solid form, and in this definition liquid particles are solids in a sense as distinguished from gases or vapors. Such condensed particles are of minute form, on the order of "smoke," and, for example, on the order of a few hundredths of 1 micron (1 micron = 1/25,000 in.) to perhaps 3 microns, with agglomerates, in relatively small proportions of many particles. Metallurgically typical fume products are lead compounds, oxides, carbonates and sulphates; elemental zinc, more commonly encountered as a fume particle of zinc metal with a surrounding "skin" of zinc oxide; arsenic, both metal and oxide and some of its more complex salts such as added sulphates as found in flue dusts; antimony, more particularly its oxide forms; and elemental sulphur, sometimes a troublesome product, in Dwight-Lloyd sintering-plant fumes. These products, particularly the elemental or lower oxide forms, have relatively appreciable vapor pressures at the existing operating temperatures as reported by Welch and Duschak9, Ingold10, Johnstonll, Millar12,13.

Jan 1, 1937

By R. Kossowsky

USING etch-pit techniques, Johnston and Gilman' have shown that the stress dependence of dislocation velocity can be represented by the expression where r, is the dislocation velocity, a is the applied stress, and oa, is the stress to produce a unit velocity. Noble and Hul12 showed that the exponent m is strain-dependent and increases rapidly in the work-hardening region. This was explained by arguing that in the work-hardened material the applied stress required for any given velocity will be greater than in the annealed material by an amount equal to a back stress due to work hardening. schadler3 has stressed the importance of substructure as a possible source of error in dislocation velocity measurements, and took care to make velocity measurements in which dislocations moved such short distances that interactions with boundaries were avoided. schadler3 also pointed out that, if standard testing equipment is used, measurements of m from flow stress data could be seriously in error in materials with a high initial work-hardening rate. Noble and Hu112 have further argued that, due to the strain dependence of m , the extrapolation to zero strain4 to obtain the true value of m can be justified only in the preyield region. Microstrain experiments in high-purity iron5,6 have led to the conclusion that aiA (Ref. 5) (defined as the stress to first produce a permanent set of 10-6 in. per in.) and oflow are not controlled by the same deformation mechanism. It has been proposed5,6 that aA is governed by the lattice resistance to the motion of screw dislocations in a given slip plane and that oflow is controlled by the lattice resistance to a full-scale cross slip. The purpose of this note is to extend Noble and Hull's argument further and to show that measurements of m from flow stress data can be in error due to the rapid increase in stress in the microstrain region6 when stress is increased beyond aA. Double z-one-refined single crystals of molybdenum (with the (101)[ 111] slip system operating and a Schmidt factor of 0.475) were used in an experimen-

Jan 1, 1968

By R. F. Mehl, M. Gensamer

Although a large number of X-ray photograms of cold-rolled steel have been published, two circumstances have led to the experimental work reported in this paper. The first is that no complete study, making use of the pole-figure method of Weverl, has been made of cold-rolled low-carbon steel. Wever has published pole figures of mild steel subjected to plane parallel deformation1, 2 and undoubtedly he has applied the method to cold-rolled mild steel, but the authors have not found these data published. Kurdjumow and Sachs3 have applied the method to the study of rolling and recrystallization textures in electrolytic iron; their results will be referred to later. The reason for this dearth of papers using the pole-figure method is obvious; a greater number of photograms and more analytical work (although this work is quite simple and straightforward) are required to construct a pole figure than most investigators have felt worth while, despite the fact that no other method of which the authors are aware will satisfactorily depict the orientations of the crystallites in a polycrystalline aggregate. The second circumstance that led to the work reported in this paper was the appearance of a paper by Wayne A. Sisson4 on the same subject. In his valuable study of the factors influencing the development of preferred orientations in cold-rolled mild steel, Sisson made one observation that required confirmation; that is, that at some stage of the rolling process the type of preferred orientation changed from the type that gives a photogram characterized as a "six-point" X-ray pattern to that known as a "four-point" pattern. A similar observation had been made by Tam-mann and Heinzel5, who studied the orientations developed in the rolling of steel by the specular reflection of light from the etched surface of rolled samples. These workers also found that the type of preferred orientation changed during the rolling process. The authors had some difficulty in seeing how this behavior could be consistent with modern views on the genesis of preferred orientations, particularly with those of Wever2

Jan 1, 1936