The Telfer Project, one of the world's newest gold mines, is located about 300 km (190 miles) northeast of the Mt. Newman iron ore project in the northern part of Western Australia. The first mineral claims were staked in 1972; and by mid-1975 ore reserves of 3. 8 million mt (4. 19 million st) of 9.6 g per mt (0. 28 oz per st) ore had been indicated. It is interesting to note that Newmont spent more than 10 years and A$10 million in Australia for extensive mineral exploration before finding the Telfer deposit, and then spent approximately A$3 million in exploration and feasibility engineering on Telfer. Including this A$3 million, a total of A$27 million was spent to complete construction of the mine, village, gold treatment plant and associated roads, airport, water and services. Over 50% of the capital cost is in the metallurgical facility, or approximately A$10, 000 per ton per day. All economically significant gold mineralization at Telfer occurs in a series of layered quartz-limonite reefs in which the former pyrite has been oxidized to limonite to a depth of 100 m (330 ft). The most important gold reef occurs at the base of the siltstone-shale horizon within the enclosing sandstone dome -like structure. At the Main Dome structure the dipping ore horizons will be mined to a vertical depth of about 60 m (200 ft) by open-cut methods. The waste-to-ore ratio is approximately 12:1. Eventually 44 million mt (48. 5 million st) of ore and waste will be mined. Mining of the waste is by contract; however, the ore and a thin layer of waste is company-mined. Dilution from mining the geological ore reserve is about 10%. The ore is completely oxidized and the gold occurs free within the reef, material as discrete particles of varying but mainly fine grain size. Most of the gold is "free milling"; that is, over 50% of the gold is coarse enough to be recoverable by gravity concentration. Two duplex mineral jigs receive the two cyclone underflows from the grinding circuit. The rougher jig concentrate is up-graded on a continuous strake from which the concentrate is tabled to produce a final free gold product. Jig tailings are returned to the ball mill and the concentrates are amalgamated. Gold amalgam is pressed, retorted, and melted into gold bars. The gravity gold recovery circuit is the same as was used in many of the gold mills in California in the 1930s.

Jan 1, 1981

By A. S. Joy

Vacuum flotation tests carried out according to the method of Schuhmann and Prakash1 have shown that the acid limiting edge of the flotation area for a Brazilian hematite, in the presence of dodecylamine, is a straight line of slope approximately unity. The flotation tests and the structure, surface ionization, and electrokinetic properties of this hematite have been fully discussed elsewhere. 2 The numbers of adsorbed H+, and OH- ions and collector molecules have been determined in the range of critical conditions defining the acid limit of the flotation area. The total amine adsorption is shown in Fig. 1 as a set of contours superimposed on the straight part of the flotation area. These were determined by spectro-photometric estimation of the complex formed between residual amine and the anionic dye Orange II.3 The ionic strength of the solutions was kept constant and at a value in sufficient excess of the amine concentration to ensure that the diffuse part of the double layer was populated predominantly by indifferent ions. Adsorption of H+ and OH- in the absence of amine was found by potentiometric acid-base titration in the presence of hematite.4 The form of the adsorption-titration curves suggested that the hematite surface behaves in an amphoteric manner, and that positively charged sites arise through loss of a hydroxyl ion, and negatively charged sites by loss of a hydrogen ion. On this basis, curves 8 and 9, shown in Fig. 2, were calculated from the titration curves. These show the variation of the numbers of positive (s +) and negative (s—) sites with pH. To distinguish between ionic and other modes of adsorption, zeta-potential determinations have also been made using the streaming potential technique. The influence of amine on the zeta-potential of the mineral over a wide pH range is shown in Fig. 3. The change in charge ?s, due to adsorption of amine ions in the Stern layer, was calculated by applying the Gouy-Chapman theory, as modified by Stem, to the results shown in Fig. 3. The validity of this treatment has been shown by Ottewill and Jaycock.5 The three full lines, Nos. (1) through (3), included in Fig. 2 show the relationship between ?s and pH at three amine concentrations. The general conclusion from the zeta-potential curves is that adsorption of amine causes a reduction in the negative charge on the surface. Comparison of the values shown in curves (1) through (3) of Fig. 2 with the - curve shows that the magnitude of the reduction is comparable with that of s - at any given

Jan 1, 1964

By B. Silliman

The experiments detailed by Dr. Hunt,* having demonstrated the fact that the copper contained in the "clay ore" of Jones's Mine, was rendered completely soluble in the bath of ferrous chloride, used in the Hunt and Douglas process, after heating in contact with carbonaceous matter in a close vessel, I set myself to devise a form of muffle furnace adapted to the treatment of large quantities of these and similar ores by a continuous process. The result is shown in the diagrams on Plate X, reduced from the working drawings, after which this furnace was built early in 1876, at Phœnixville, by the Chemical Copper Company on their works at this place. The peculiar character of this ore determined the form, dimensions, and position, with reference to charging and discharging of these muffles. The ore arrived from the mine with from 20 to 25 per cent. of moisture, and when dried at 21o F., or more slowly at lower temperature, it falls to a light incoherent powder, with occasional lumps of undecomposed rock. In this condition it is readily mingled with coal-dust or any like reducing agent, and requires no other preparation for the muffle than the use of the shovel, to mix it well with the reducing agent. As it is a remarkably good non-conductor of heat, it was obvious that the mass, to be heated through in a reasonable time, must not be too thick, while the weight of the mass must be sustained in a way to avoid undue strain upon the walls of the muffle. These walls must be as thin as practicable, to favor the more rapid transmission of heat, and must, therefore, be so constructed as to admit of being stayed on the sides at frequent intervals to resist the lateral thrust of the very mobile mass of pulverulent ore, which, for obvious reasons, must be charged at the top and drawn from the bottom of each chamber. These considerations led to the form adopted, viz., two vertical muffles, standing upon very strong bridge tiles, seen in longitudinal section, on the line E, F, and in plan in Fig. 3, on the same plane. (Plate X.) The vertical section of the muffle is seen in Fig. 4, drawn in the plane G, H, of the longitudinal section, Fig. 6, which is the key to all sections. The walls of the muffles are built of the best firebrick, very care-

By Karl L. Konnerth

THE rapidly increasing use of machinery for the mining of coal and operations incidental thereto has materially changed conditions from a safety standpoint. A few of the coal-producing states have recognized the need for specialized electrical equipment for use in mines and have introduced certain requirements in their State safety regulations, notably Pennsylvania. This paper discusses the principal problems involved in maintenance of such equipment. PERMISSIBLE: EQUIPMENT "Permissible" electrical equipment is equipment that has met certain prescribed standards for use in mines where hazardous conditions may occur and has been recommended by the U. S. Bureau of Mines. Such machinery is available on the market for most coal-mining operations--for instance, coal cutting, transportation, drilling, loading, working-place illumination, shot-firing and pumping. A notable exception is the trolley-reel gathering locomotive which, although its parts may be explosion-tested by the Bureau, has not been approved as permissible for the following reasons: I. The trailing cable is subjected to more severe service than on other equipment. 2. State regulations do not require that a working place be examined for methane before a locomotive enters it. 3. Even with two-conductor cable, imperfect or inadequate bonding may cause the emission of sparks at the wheels of the locomotive and at rail joints. 4. As the locomotive is equipped with a trolley pole, and as the trolley wire may be installed and used in unsafe territory in spite of rigid State regulations, a trolley-reel gathering locomotive is always a potential hazard. MAINTENANCE The proper procedure for maintenance of permissible equipment may be divided into three parts: (I) inspection, (2) actual maintenance and (3) changes or improvements to existing machines. To secure the fullest benefits through the use of permissible equipment it is necessary that all men involved understand the principles underlying the safety features of this equipment and realize the significance of defects, so that neglect and indifference in the maintenance thereof may be eliminated. Inspection From the standpoint of safety it is desirable no doubt to make a suitable inspection of permissible electrical equipment once a week, but the opening of every enclosed compartment at each inspection may do more harm than good. The openings to such compartments are closed with various types of covers very accurately machined, often made of the softer alloys to reduce weight, and fastened with a multitude of bolts, screws, washers, and other small parts. Frequent handling of these covers may cause sufficient damage to defeat their original purpose and intent.

Jan 1, 1941

By G. Thodos, E. M. Phillips

A reduced density correlation for the gaseous and liquid regions of ethane has been developed from all the experimental PVT data available in the literature for this substance. Saturated vapor and liquid densities reported for methane, propane and n-butane were utilized to establish the rectilinear-diameter line for ethane. This line was then used with the saturated-vapor data for ethane to produce the saturated envelope for this substance. Most of the saturated liquid data reported for ethane were found to be inconsistent with the saturated-liquid curve resulting from this study. The correlation covers the regions 0.65 < TR <6.0 and 0 < PR < 15. For regions for which no experimental data have been reported, the isobars of the correlation were extended by the use of the theorem of corresponding states. This correlation is presented both on rectilinear and log-log coordinates. INTRODUCTION At the present time, there is considerable interest in the exact PVT behavior of pure hydrocarbons. Matschke and Thodos12 recently have developed a comprehensive compilation of experimental vapor and liquid density data for methane. Similar studies have been conducted for other pure substances.4, 7 In the present study the density data available in the literature for gaseous and liquid ethane have been critically reviewed and utilized to develop a reduced density correlation for this substance. SATURATED LIQUID AND VAPOR DENSITIES The rectilinear-diameter rule proposed by Cailletet and Mathias5 states that the sum of the saturated liquid and vapor densities of a pure substance is a linear function of temperature which passes through the critical point. This law, although empirical, has been well established by continued verification since its conception in 1886. This rule has been applied to the saturated density data of methane,6 propane 17 and n-butane8 to produce the straight lines presented in Fig. 1 which pass through the critical point TR = 1.00, Pr = 2.00. The rectilinear-diameter relationship for ethane was established from the lines for the other substances in Fig. 1 by plotting the quantity p~, + PR against zc for different reduced temperatures. A critical analysis of the saturated vapor and liquid densities reported for ethane by Kuenen,10 Maass and McIntosh,11 and Sage, Webster and Lacey18 revealed that the values of PR1 + pr resulting from these studies were inconsistent with the rectilinear-diameter line obtained from the reliable density data of the other substances, as shown in Fig. 1. In the analysis of these data, reduced quantities were calculated using the critical con-

By Earl C. Herkenhoff

Publication of the article "The Flotation Behavior of Digested Asphalt Ridge Tar Sands" by R.J. Smith and J.D. Miller has confirmed and again spotlighted a most significant and important development in the field of tar sand and heavy oil mining. This is the ability to recover 95% of the bitumen in dry tar sands by a hot water process. The initial investigation by Miller and Sepulveda in early 1978. "Separation of Bitumen from Dry Tar Sands," was the first blockbuster. It is disappointing that there has been so little scientific and industry ackowledgement that the authors laid to rest the long entrenched belief that the sand grains had to be "water wetted" for a hot water process to be applicable. Dr. Miller and his researchers at the University of Utah used slightly different mineral dressing terminology in describing their process but it is essentially the old, established technique of high &lids attrition scrubbing at elevated temperatures with a conditioner or modifier, followed by dilution and froth flotation. Similar techniques were described in detail for other nonmetallic minerals in the mid-1940s by Stuart Falconer of American Cyanamid Co. The authors used a 15-minute "scrub" period (or in their terminology "digester step") at 73% solids and 95OC (203°F) in a 0.3 m solution of sodium carbonate-about 4 kg/t (8 lb per st) of tar sand. Flotation was at 10% solids. Obviously, the scrub is an expensive step with respect to energy input but the high recovery of bitumen appears to justify it. Two basic questions then arise: What are the effects of shorter scrubbing time, lower temperature, and less sodium carbonate? Would a two-stage approach be advantageous? That is, could you get the major proportion of the bitumen with a mild scrub and apply the high power and temperature only to the refractory portion? These variables should be evaluated. Apparently, all results were only for rougher flotation. What would the grade and recovery of bitumen be if multiple cleaner flotation steps were employed? We must concede that a 60.62% grade of bitumen leaves considerable room for upgrading. Finally, it should be noted by all executives who approve funds for heavy oil recovery schemes, most of which are variations of in-situ methods, that mining can yield a 95% recovery of bitumen. That is correct, 95%. Imagine what that does to the total barrels recovered from a heavy oil resource compared with the scrawny 30-35% maximum recovery we are getting now. The conclusion-let&apos;s mine heavy oil and tar sands.

Jan 1, 1983

ROBERT PEELE, New York, N. Y. (written discussion *).-This excellent paper is one of a number of recent detailed descriptions of the, methods and plant in use at prominent mines of the country. The publication of such papers cannot be too highly praised. In the past, the interchange of inside information has often been hampered by the disinclination of some mining companies to permit publication of details of their work. These companies apparently have not realized fully that free discussion is of mutual benefit; that members of mine staffs are aided in. keeping up to date, in improving old methods and devising new ones to meet changes in conditions, and, by a wholesome feeling of rivalry, are stimulated to introduce economies and do better work. In writing this paper, Messrs. Haight and Tillson have packed a large amount of information into a relatively small space, and the numerous illustrations, chiefly reductions of working drawings, are valuable. The authors are also to be commended for their highly detailed Table of Contents, which adds to the usefulness of the, subject matter. The method of mining at Franklin does not fall readily into any of the accepted classifications. It is a combination of shrinkage stoping and mining of the pillars by a modified top-slicing method. Attention may be called to the fact that, in the wider parts of the orebody, the stopes, 17 to 18 ft. (5.2 to 5.5 m.) wide are transverse; in the narrower parts, they are longitudinal, that is, in the direction of the&apos; strike. This varia-tion is made necessary by the shape and character of the deposit, and distinguishes practice at Franklin from that in some of the western mines. The direction of the stops is changed from transverse to longitudinal when the orebody narrows sufficiently to make the length of a transverse stope approximately equal to its width. Some of the longitudinal stopes exceed 120 ft. (36 m.) in length, and when the hanging wall is bad, requiring prompt filling, three operations&apos; proceed simul-taneously in the same stope, viz., ore is broken at one end, while drawing down goes on in the middle, and filling at the other end. Each transverse stope or chamber is begun by a crosscut from foot to hanging wall, which is afterward enlarged to the stone width and to a height of 12 or 15 ft. (3.7 or 4.6 m.). This preliminary work is done only once for each stope, because the stope is carried up far enough to continue stoping

Jan 1, 1918

department, first as a practical miner, next. as rodman on the survey corps, of which he soon became chief, then draftsman and mining engineer in the company&apos;s office. In January, 1916, he was promoted to the position of district engineer in charge of mining engineering work. He became a member of this Institute in September, 1917. Captain Ba.llamy&apos;s military experience began at the same time as his engineering practice. He was a charter member of Company A, Engineers, N. G. P., which was organized ten years ago. He saw service on the Mexican border as First Lieutenant of this Company, and remained in that position until November, 1916. In July, 1917, he was again called into service and was sent to Camp Hancock, Ga., with the 103d Regiment of Engineers. Before joining this regiment he attended a school for officers at Fort Sill, Okla., where he received special training in field fortifications. In December, 1917, he was commissioned Topographical Captain on the Regimental Staff, and in April, 1918, preceded his regiment by about six weeks to France, where he again attended an officers&apos; training school. He rejoined his regiment on July 15, near Chateau Thierry and was killed near Fismes on Aug. 9, 1918. Lieutenant Martin F. Bowles Martin F. BOWleS, born Apr. 25, 1893, at Bonne Terre, Mo., and graduated from the Neodesha, Kans., High School, had finished all but one month of a four-year course in metallurgical engineering at the Missouri School of Mines, Rolla, Mo., when on May 12, 1917, he entered the first Officers&apos; Training Camp at Fort Riley, Kans. At the close of the training period, he was commissioned a Sccond Lieutenant and assigned to Co. B, 355th Infantry, 89th Division, and stationed at Camp Funston. He left this camp with his company on May 21, 1918, and sailed from an eastern port on June 4, ayriving in England on June 15, 1918. After a short stay at a rest camp there, he proceeded to France. On August 14, he wrote that he was with Battalion Headquarters as Gout Officer, 1st Battalion, 355th Infantry, 89th Division. The last letter received from him, dated September 2, was written in his dugout and contained the following: "Here it is 2.45 a. M. Sitting in a dugout waiting for some patrols to report back in, I am writing this by the light of two candles." He was killed in action on the night of Sept. 3, 1918. The letter of notifi-

Jan 1, 1920

By C. Zener, H. Nielsen, D. Van Winkle

THE internal friction of metals has been studied frequently at elevated temperatures.1-4 In most cases it rises rapidly with increasing temperature. The notable exceptions are ferromagnetic materials, and lead.2 This paper describes an investigation of the general features of the high-temperature internal friction of 70-30 alpha brass. EXPERIMENTAL METHOD The internal friction of a metal is a measure of the rate at which it dissipates energy of vibration. The measure adopted here, I/Q, is (I/2p) times the specific damping capacity, a measure commonly used by engineers. In the measurements of this investigation, the stress level was kept so low that the observations were independent of the stress. The general method of making such measurements, and of observing the temperature of the specimen during a measurement, has been described elsewhere.5,6 The driver and detector coils were wound with wire insulated with glass thread, in order to withstand the high temperatures used. In previous work electrical eddy currents in the specimen served as the coupling between the mechanical vibration of the specimen and the electrical circuits of the driver and detector. The high values of the internal friction in the present investigation rendered this coupling insufficient. In order to increase this coupling, pole pieces cut from ordinary telephone diaphragms were attached to the specimen. A mixture of French chalk and water glass proved a satisfactory cement. All measurements were made at the fundamental frequency for transverse vibration, which lay between 600 and 900 cycles per second. SPECIMENS The measurements described herein were made upon a single cylindrical rod of brass, kindly furnished by Dr. Cyril Stanley Smith, of the American Brass Co. This rod was the specimen E of the set of alphabrass rods described in an earlier paper.6 Successively larger grain sizes were obtained by annealing at successively higher temperatures. A slice was cut off one end after each set of measurements. Grain counts were made on each slice by W. E. Lindlief, of the American Brass Co. Nine fields were viewed on each piece, located as shown in Fig. I. Results are given in Table I. The grain size is defined in the usual way; namely, Grain size = I/n ½ where n is the mean number of grains per square millimeter. EXPERIMENTAL RESULTS This paper is concerned exclusively with the part of the internal friction that becomes dominant at high temperatures. It is thus desirable to separate this part of the internal friction from the part that is

Jan 1, 1942

RICHARD A. CONKLING (communication to the Secretary*).-Mr. Hager says that his results on the correlation of well logs in the north Cushing field are the opposite to those of the author. Can he, then, explain why the structural dip of the formations increases with depth, as Dr. Ohern, in his criticism, sets forth that it does, and as all who have worked in these fields will admit, if the shales thicken on the crest of the anticline, as he says they do? We are willing to agree with Dr. Ohern that there is some evidence of a slight unconformity below the Bartlesville sand and think that we can prove, from a specimen in our office, that .this unconformity comes at the base of the Bartlesville sand in the south Cushing pool. On the Ingalls dome, in the southeast corner of Township 19 North, Range 4 East, however, we get results the same as those given by the author on Cushing. The Ballard well in the center of the Northeast Quarter of Section 33 is just 10 ft. higher, structurally, according to tile, surface contour, than the Ringold well -in the center of the Southwest Quarter of Section 34. The dip in the Bartlesville sand, between these wells, is 40 ft. and the dip on the top of the Mississippi lime is 75 ft. This also might be accounted for, partly by the unconformity, but the author used the interval between the top of the Oswego lime, which is about 420 ft. above the Bartlesville sand, and the oil horizon found in the lime in the Ballard well-just mentioned above-to find the depth at which the same oil should be found in a well in Section 5, Township 22 North, Range 3 East, 25 miles North. Using this interval below the Oswego in the former well, we predicted within 2 ft. where they would find the oil in the latter well. Of course, we know that it was accidental that we missed it only by 2 ft., but if there were much of an unconformity in this interval it would be more of an accident if we came within 100 ft. of the depth. Since it can be proven from most of the structures in this section that the clip continues to increase downward, below the Bartlesville at least, to the Mississippi lime, it does not seem necessary to the author to try to prove otherwise that the depth at which the shales will tend to thicken on top of a fold, has not been reached above the

Jan 6, 1917

By Irving Cadoff, Jack Medoff

THE linear thermal expansions of oriented single crystals of zinc were measured in the range from 20" to 416°C using a Leitz HTV optical lever differential dilatometer. The single crystals, supplied by Dr. J. J. Gilman, General Electric Research Laboratory, Schenectady, N.Y., were prepared from 99.999 pct-purity zinc, and were in the form of rods approximately 2 in. long by 0.15 in. in diameter having the following orientations: x = 1.5, 12, 20, 30, 37.5, 49, 60, 73, and 82 deg where x is the angle between the specimen axis and the (0001) plane of the crystal. From the family of expansion vs temperature curves, the instantaneous expansion coefficients were calculated at 100°C intervals, and Fig. 1 shows a plot of these derived coefficients for each orientation. Coefficients were obtained from the raw data using the chord-slope method. The curves in Fig. 1 indicate a positive temperature coefficient for low x, a negative temperature coefficient for high X, and an expansion coefficient invariant with temperature, amounting to about 43 x 106, for a crystal orientation of approximately 52 deg. From the available data, it is possible to arrive at the values for the axial thermal-expansion coef- ficients a, and a, by extrapolating the curve of the expansion coefficient vs orientation to zero and 90 deg orientations. More precise values for a, and a, are obtained if the instantaneous coefficients are plotted against the square of the cosine of the orientation angle, as shown in Fig. 2. The extrapolated terminal points of the best straight line through the data points of such a plot define the axial coefficients at that temperature. The theoretical justification for the linearity of this curve comes from inspection of a rearranged form of the general anisotropic equation for expansion: ax=a, + (a, -a,)cosZx [1I in which a, is the expansion coefficient in the "c" or [0001] direction and a, the expansion coefficient in the "a" or [ll50] direction. From Fig. 2, the axial coefficients at 100°C, for example, were found to be a, = 13.9 x 10&apos;6 and a, = 62.4 x 10"6 per "C. In the same way, the coefficients were determined for 20", 200°, 300°, and 400°C. This data is summarized in Fig. 3. It is of interest to observe the common intersection of the curves in Fig. 3, which seems to bear out the earlier observation, from Fig. 1, of a

Jan 1, 1964

By Pol Duwez, Paul Pietrokowsky

The crystal structure of the compound TisGeS has been determined from X-ray powder diffraction data. Related silicon and tin compounds have been found to be isomorphous. Unit cell dimensions, axial ratios, and parameters for equivalent atomic positions are given. THERE is, at present, only meager information pertaining to the solid state reactions of titanium with the elements in group 4B of the periodic table (silicon, germanium, tin, and lead). The only two compounds whose crystal structure has been established are TiSi² and TiGe² (references 1 and 2 respectively). These two compounds are isomor-phous and have an orthorhombic symmetry D242h— Fddd. The titanium-rich regions of the constitution diagrams of titanium-silicon, titanium-tin, and titanium-lead have been investigated by Craighead et al.³ While valuable information concerning the alpha solid solubility of these three elements in titanium was obtained, no light was shed on the existence or nature of the titanium-rich compound in these systems. The present study is concerned with the crystal structure of the intermediate phases Ti5Si ?, Ti³Ge³, and Ti5Sn³, which were found to be isostructural. The alloys were prepared by mixing the pure metal powders in the desired proportions, pressing the mixture into pellets, and melting them in an electric arc furnace in the presence of a helium atmosphere.& After melting, the specimens, weighing approximately 5 g, were sealed in evacuated quartz vials, homogenized at 1038°C for three days, and quenched from that temperature. Powder diffraction patterns were made with a 143.2 mm diam Debye-Scherrer X-ray camera in which the Ievins and Straumanis film arrangement was utilized. Filtered copper radiation was used throughout the entire investigation. A study of the powder patterns of a series of alloys of various compositions indicated the presence of a compound around a composition corresponding approximately to a ratio of 3 titanium to 2 silicon, germanium, or tin. From a visual examination of the diffraction patterns, it was evident that the silicon and germanium alloys were iso- morphous. For small angle reflections, the powder pattern of the tin compound was analogous to that of the silicon and germanium compounds, but after the first ten reflections, the similarity was no longer clear. The powder pattern of the germanium compound was selected for indexing, since it exhibited a weak small angle reflection and clearly resolved doublets in the back-reflection range. Good agreement between observed and calculated values of (1/d)² was found by indexing the pattern on the basis of hexagonal symmetry. For the hexagonal system:

Jan 1, 1952

By James Norman, O. C. Ralston, John Dasher

MOST mineral products are used in the finely divided state, but some are sold in larger sizes. Coal, gravel, metallurgical fluorspar, phosphate rock, hematite, chromite, and other products are sold in sizes coarser than can be treated by many mineral-dressing methods. Gravity separation of coarser sizes by log washing and jigging is probably as ancient as any process now in use. The performance of jigs on a feed with sufficient difference in density of the minerals is excellent, but many families of minerals are too similar in density to be separated effectively by this method. The use of heavy suspensions of fine solids to separate coarse coal from bone and slate has been in use for some years. This separation by sink-and-float was limited until recently to light minerals. Development of galena and ferrosilicon as suspension media, by Minerals Beneficiation, Inc., at Mascot, Tenn., Pitcher, Okla., and Crosby, Minn., under patents granted during and since 1938, has permitted excellent results to be obtained on minerals of very similar densities up to 3.3. This process has been put in the hands of American Cyanamid Co. for exploitation, and further research now in progress may increase the density of suspension obtainable so that separations at a density of 4.0 may be practicable before this is published. The Huntington-Heberlein dense-medium process, developed in England, is also being commercialized in the United States by Sink and Float Corporation. Du Pont has developed a sink-and-float separation using halogenated hydrocarbons as parting liquids; at this writing, the method is used commercially only on coal but has been successful in the pilot plant on many other minerals using tetrabromethane at densities up to 2.95. While these processes were being developed to extend the range of separation by difference in density to the coarser sizes, the Bureau of Mines was engaged in developing a process that will extend the range of separation by difference in wettability up to 2-in. size. War work has pushed aside its further development indefinitely. The results are published here with the hope that some use may be suggested that will justify post-war development, and so that readers that may be able to make immediate use of the scheme may have the information. EARLIER WORK It has been known since the time of Herodotus (B.C. 484(?)-425) that water-repellent particles will adhere to sticky surfaces. That early historian reports the

Jan 1, 1942

By W. A. Bates, R. J. Miller

Although cresylic acids have been standard frothers in flotation for many years, there has been little discussion of their nature in the metallurgical literature. Aside from references in the patent literature, the paper by Landolt, Hill, and Lowyl in 1930, which resented a study of the frothing and collecting properties of some of the constituents of crude cresylic acids, represents the only contribution of this type. The close froth control required in the delicate selective separations of present-day flotation operations have required the flotation metallurgist to choose his frothers with care, and have caused him to require of the manufacturer a closely controlled, uniform product. A background of knowledge of the chemical composition and physical and chemical properties of the frothers, by which their action may be correlated, should aid in selecting frothers for particular flotation requirements. Further, the recent almost complete replacement in flotation of coal-tar cresylic acids by those derived from petroleum makes it especially desirable to review the flotation behavior of the acids from the old and the new sources. In view of these facts the Milling Methods Committee of the A.I.M.E. suggested to the Oronite Chemical Co. of San Francisco the preparation of a paper on the subject, and this paper has accordingly been prepared as a contribution by the California Research Corporation, the research affiliate of the Oronite Chemical Co. The discussion is from the following aspects: (I) constitution and properties; (2) sources; (3) comparison of coal-tar and petroleum cresylic acids; (4) characteristics as frothers, with particular reference to the effect of the substitution of petroleum acids for coal-tar acids. Constitution and Properties Cresylic acids are commonly regarded as mixtures of orthocresol, metacresol and paracresol. This was, indeed, the former meaning of the term, but in recent years it has been loosely applied to any mixture of alkyl phenols boiling above 190°C.; that is, excluding only phenol itself. This means that cresylic acids, as they are known today, may consist of mixtures, not only of the three isomeric cresols, but of six xylenols and of a variety of higher boiling homologues. Generically the constituents of cresylic acids are alkyl phenols, and they are often so designated in the literature to avoid the more indefinite term, "cresylic acids." They form an homologous series starting with phenol, which has the familiar benzene ring, with an hydroxyl group in place of one of the hydrogen atoms. The series of alkyl phenols is formed by the substitution of alkyl side chains, such as methyl, ethyl, propyl, butyl, etc., for hydrogen atoms of the benzene ring of phenol. Some

Jan 1, 1947

By G. M. Ritcey, A. W. Ashbrook, E. G. Joe

Solvent-in-pulp extraction of uranium from acid leach slurries of flotation concentrates is described. Solvent extraction was carried out in a 10 in. diam pulsed-plate column. The extractant was a 0.1 M tertiary amine (General Mills Alamine 336) in a kerosene diluent containing isodecanol as an emulsion suppressor and third phase inhibitor. In pilot plant operation at the Beaverlodge mill of Eldorado Mining and Refining, Ltd., slurry feeds containing up to 35% solids were processed at a throughput rate of 13.5 tpd of dry feed. Uranium extraction obtained was as high as 98%. Amine losses to the raffinate were approximately 0.07 lb amine per ton of original dry feed. The Beaverlodge Mill of Eldorado Mining and Refining employs a carbonate leach for the extraction of uranium from the ore.&apos;,&apos; Prior to carbonate leaching sulphides are removed by flotation to reduce reagent consumption. This flotation concentrate containing some uranium is then leached with sulfuric acid, filtered, and the uranium precipitated with magnesium hydroxide. The precipitate is then returned to the carbonate leach circuit. Although the tonnage of flotation concentrate treated by acid leaching is low, reagent costs are relatively high. Also maintenance costs on the acid leach filtration circuit were beginning to show significant increases. The choice of solvent extraction-in-pulp as an alternative to the present circuit was influenced by the following factors: 1) elimination of acid pulp filtration, 2) increase in overall recovery because of soluble loss elimination, 3) reduction of reagent cost (mill sodium carbonate solutions are used as strip), and 4) production of higher purity precipitate at the mill site. Because a solvent-in-pulp process would be difficult to test on a bench-scale, the Eldorado experience in the use of pulse columns,3-5 mixer-settlers,6 and solvent-in-pulp operations in particular7 was applied directly to the initial pilot plant carried out during the summer of 1965 and followed by the second pilot plant in 1966. The latter work, which is presented in this paper, determined the following factors for anticipated scale-up to plant production: 1) overall uranium recovery by this process, 2) tonnage throughput expected, and 3) solvent losses anticipated for the full-scale plant. The equipment used consisted of a 10 in. diam extraction pulse column and three mixer-settlers for scrubbing, stripping, and acid equilibration. All equipment was designed by Eldorado and much of the pilot plant was built at the mill site. PROCESS CHEMISTRY Feed to the acid leach plant consists of a sulphide flotation1,2 concentrate containing mainly pyrite, uranium and graphite, with a particle size of 90%

Jan 1, 1968

By Oscar T. Marzke

Four alloys that precipitate the alpha phase from the beta of the copper-zinc system were heat-treated in various ways to develop as many forms of the segregate as possible. It was found that the precipitate may have the form either of plates or of needles. Plates usually result when precipitation occurs at low temperatures and needles when precipitation takes place at high temperatures. The needles tend to align themselves along certain planes in the matrix and to coalesce into plnte-like structures. The two phases were found to be related so that a (111) plane and [Oil] direction of the precipitate are parallel to a 10111 plane and 11111 direction of the matrix. DISCUSSION (E. A. Anderson presiding) D. W. Smith, Pittsburgh, Pa. (Written discussion).—Tllis report by Dr. Marzke covers completely all possible heat treatinents over a considerable range of compositiol~s in which a1pha precipitates from beta brass, and may be said to complete the Inctallographic part of this problern The lining up of ncedles of segregate to form plates, espeeially as shown in Fig. 5, appears to he regular, although the author&apos;s frequency plot in Fig. 11 makes it appear rather irregular. Has the author attempted anY correlation between some of the major dircetions and the oricntntaion of the parent grain as determined by X-ray analysis? Also, in Figs. 4, 5 and 6 the cross-sections of the needles appear to be straightsided and regular. Have these directions been correlated with the matrix latttice? Dr. Mnrzkr &apos;s method of interpretation of the orientation rclationships between the alpha. and beta phases is a bit uncertain and seems to wed more explanation. If this relationship, as staited is such that :L (1111 plane and a [I 10] direction of that plane in the precipitate is parallel to a. {110} p1ane and a [111] direction of that, plane in the matrix, there mill be a maximum of 24 possible orientations of the alpha phase within a. single grain of the beta phasc. This relationship is expressed strercographical1y in Fig. 13, ill which the locations of a11 of the alpha {111} poles for the 24 orientations of alpha me given. Fig. 12 chccks fairly closely with this thcoretical plot,. with a few exeeptions which may be due to the inaceuracy inherent in the method used by the anthor in determining the orientations of the segregates. The method might have been refined somewhat had corrections been made for the displacement of the slip p1ancs upon deformation.

Jan 1, 1933

By R. D. Reiswig

An increasing amount of high-temperature metall~?~gical research is carried out in resistively heated tube furnaces in which a bare specimen is suspended by a fine wire at the midpoint of the tube. It is shown that the assumption of near-blackbody conditions on the surface of the sample may give rise to errors in optical pyrometry of 50°C or more. A number of papers published in the metallurgical literature in recent years have described the use of high-temperature tube furnaces for heat treatments, melting-point determinations, and other work. Typically, the tube is of a refractory metal with open ends, is heated by the passage of an electric current, and has concentric cylindrical radiation shields outside it. In at least one of these,&apos; the specimen is contained within a crucible having a small hole in its lid through which optical-pyrometer measurements are made under essentially blackbody conditions. In another design,* the specimen is inside a muffle which is concentric with the heater tube and which contains a number of washerlike longitudinal radi- ation shields to reduce axial temperature gradients and to give conditions near the specimen closer to those of a black cavity. Yet another design3 employs a wire specimen coaxial with the heater tube. Blackbody conditions are simulated by passing current from a separate supply through the wire until it "disappears" against the background (the inside of the heater tube) as seen through a radial spy hole in the tube. Good agreement with known melting points is achieved when an optical pyrometer is used under such disappearance conditions as the melting point is approached. That this latter method works so well is due, evidently, to considerations such as those mentioned by Dike4 and others.5-8 A more common method than the above, however, has been the suspension of an uncovered specimen by a fine wire in a resistively heated tube with open ends. A radial spy hole about midway between the ends of the tube permits optical-pyrometer observations on the specimen, the inside of the tube, or both. So observed, the specimen typically appears to differ but little in brightness temperature from the inside of the tube. According to De vos9 the radiation from such a spy hole in an empty tube of reasonable 1ength:diameter ratio (e.g., 10 or greater) should be essentially blackbody radiation. For these reasons, apparently, descriptions of work carried out in such furnaces usually include a statement to the effect that conditions surrounding

Jan 1, 1964

By G. R. Frank, R. E. Willett, E. H. Hollingsworth

The most generally accepted equilibrium diagram for A1-Fe alloys has a eutectic system on the aluminum side with an essentially insoluble constituent of the formula, FeAl,, as the second phase. In 1938, Bradley and Taylor1 did report a phase change of FeAl,, but this change has never been confirmed. According to them, FeA1, is the stable phase only at higher temperatures; at lower temperatures, it is converted into Fe2Al7 and aluminum. It has now been found that there is, in fact, a phase change of the Al-Fe constituent on the aluminum side of the equilibrium diagram. This change, however, is not the one reported by Bradley and Taylor. The alloys used were cast by continuous processes and had these analyses: Fe - 1.98 to 2.02 pct, Cu-0.01 pct, Si - 0.01 pct, Mn - 0.01 pct, Mg - 0.00 pct, Zn - 0.00 to 0.01 pct, Cr - 0.00 pet, Ti - 0.00 to 0.04 pct. The constituent in these alloys was identified by X-ray analysis with a Guinier camera and by chemical and X-ray powder diffraction analyses. Two procedures were used to separate constituent for the last two analyses. In one procedure, it was separated by treating a sample with a solution of methanol saturated with iodine. And in the other procedure, it was separated by first applying, at 12 amp per sq ft in 15 pct sulfuric acid at 70°F, an oxide coating to a sample, and then dissolving this coating in a solution of 35 ml of 85 pct H3PO4 and 20 g of CrO3 per liter. Several observations directed attention to a phase change of the A1-Fe constituent. Differences that appeared too great to be accounted for by micro-structure alone were found in the voltages required to apply the same thickness of an oxide coating to products from rapidly and slowly chilled ingot. Even more striking was the difference in appearance of the coatings themselves. One applied to a product from a rapidly chilled ingot was dark gray in appearance, in fact, almost black, while one applied to a product from a slowly chilled ingot was essentially white. Also, even a short period of thermal treatment at an elevated temperature of products from rapidly chilled ingot led to the same anodizing behavior as that of products from slowly chilled in-

Jan 1, 1962

By K. C. Mills, E. T. Turkdogan

The results on the rates of vaporization of Fe-Ni alloys, levitated by an electromagnetic field in a stagnant atmosphere of helium, are shown to be in close agreement with those predicted theoretically. AS shown in Part I of this series of papers, the rates of vaporization of metals enhanced by convection currents are increased further by the process of condensation of metal vapor when there is a steep temperature gradient in the boundary layer. At the time this theoretical work was completed one of the authors (K. C. Mills) had already carried out some experimental work on the rates of vaporization of molten Fe-Ni alloys. The experimental work was done under conditions which make it possible to compare the experimental rate data with those predicted on theoretical grounds. EXPERIMENTAL The object of the experiments was to evaluate the activities in a number of binary metal systems. The details of the experimental technique are given in another paper by Mills, Kinoshita, and Grieveson,2 and, for the present purpose, a brief mention of the relevant features of the experimental method will be adequate. Using an induction coil, the metal weighing about 1 to 1.5 g was levitated by the electromagnetic field in a stagnant atmosphere of pure helium. The helium was freed from oxygen and water vapor in the usual manner, and its pressure in the vaporization chamber was maintained at 1 atm through a bleeder device. The vaporization chamber consisted of a pyrex tube, 2.8 cm diam, with a side arm connected to the helium bleeder. The bottom of the tube, shaped conical, was surrounded by the induction coil, and the top was sealed with an optical flat for the purpose of measuring the melt temperature with a two-color optical pyrometer. By suitable adjustment of the high-frequency power input, the metal was brought to the desired temperature in about 30 sec of levitation. After a specified vaporization time, e.g., 3 to 4 min, the alloy was quenched by switching off the power. The amount of metal vaporized was determined from the difference between the initial and final weights of the sample. During the vaporization time, temperature fluctuations of about ±10°C were observed. COMPARISON OF EXPERIMENTAL DATA WITH THEORETICAL VALUES The experimental results are given in Table I. As already mentioned, the attainment of the vaporization temperature took about 30 sec from the moment of levitation. Therefore, the times recorded in Table I are 30 sec less than the total time; this is considered to be a reasonable estimate of actual vaporization times.

Jan 1, 1964

By R. W. Gurry, L. S. Darken

The solubility of cementite in austenite is computed by thermodynamic methods from the observed solubility of graphite. It is found that the solubility of cementite is greater than that of graphite in the entire austenite temperature range. Thus the prior discrepancy between this portion of the phase diagram and the observed metastability of cementite is partially resolved. FOR several years it has been apparent that a serious discrepancy exists in certain observations pertaining to the Fe-C system. Direct experimental data indicate: 1-That the curve representing the solubility of graphite in austenite&apos;" crosses that for cementite4 at about 945°C as shown in Fig. 1. 2— That graphite and austenite saturated therewith are stable1 relative to cementite at all temperatures between the eutectoid, about 723°C, and the eutectic, about 1153°C. These observations are mutually incompatible in view of a well-known consequence of the second law of thermodynamics, namely, that the stable phase (presumably graphite at all temperatures) has a lower solubility than the metastable phase (presumably cementite). Hence either 1 or 2 above must be in error; either the measured solubility of graphite or of cementite, or the observation as to the stability of graphite, is in error. Our present purposes are: 1—To collate the available data on cementite and prepare a table of HO — HO° and of (Fa— HO°)/T. This tabular method seems the best and most convenient way to represent the heat and free energy of formation. 2—To determine whether the measured solubilities of cementite and graphite in austenite are in accord with the above table and the measured thermodynamic properties of austenite, in order to resolve, if possible, the existing paradox of these two solubilities. Enthalpy of Cementite The enthalpy of cementite at 273 °K, H279 — HOcem, was computed by integration of the low temperature heat capacity as measured by Seltz, McDonald, and Wells" 68" to 298 °K) and as given by the Debye functions recommended by them (0" to 68°K); the result is included in Table I. At higher temperature HCem — H,,"" is given by Kelley who used the data of Naeser7 (298" to 1037°K) and of Umino8,9 (273° to 1923°K). We have recalculated Hcem — H273 cem from the data of UminoO in the following way. In the equilibrated alloy at temperature the weight fraction of cementite Pct c -Pct cr is PctC -PctCr designated f(C), and the

Jan 1, 1952