By N. Acarkan

Slags usually contain some quantity of valuable metals. They are actually a secondary resource of metals, rather than an end-waste and have been utilized as a resource material in many areas. In addition, for some applications, slags have comparable or even better properties than their competitors. Leaching is a method for extraction of metals from copper slags. The extraction of metals such as copper and cobalt from the copper slag of Küre-Turkey, was investigated in the past decades. Fayalitic type of these copper slags containing 0.934 % Cu, 0.353 % Co and 50.91% Fe were subjected to the experimental study. As a result of mineralogical analysis of the slag sample, fayalitic type of slag was found to contain hercynite, magnetite, hematite, pyrite, chalcopyrite, covellite, bornite and metallic copper. Direct acid leaching methods were applied on the sample. Effects of leaching time, temperature and acid concentration on Cu and Co leaching recoveries were investigated in the direct acid leaching. The optimum leaching conditions were found as leaching time of 2 hours, solid/liquid ratio of 1/3, H2SO4 concentration of 125 g/L and temperature of 70 °C. At these conditions, 75.5 % of Cu, 95.6 % of Co and 70.9 % Fe were extracted. In the second stage of the leaching experiments, copper in the pregnant solution was precipitated by cementation to produce a Cu concentrate assaying 95.58 % Cu; cobalt was obtained by precipitation with H2S to produce a concentrate containing 62.10 % Co. As a result of this study a process flow sheet has been developed for recovering Cu and Co from these slags to demonstrate its economic and technological benefits.

Jan 1, 2014

By D. H. Xiong

Low grade oxidized iron ores are usually not economic to utilize. However, the development of SLon magnetic separators and other new technologies make the process cost lower and lower. In this paper, several low-grade oxidized iron ore process flowsheets are introduced. The key procedure is that at the early stage, SLon magnetic separators are applied to discharge as more tails as possible with very low cost, only a small portion of rough concentrate going to the cleaning stage, showing the new technologies are profitable for such iron ores.

Jan 1, 2014

By Xiaojing Li, Yueyuan Zhou, Shengyao Ma

The paper presented the acnalysis of field intensity of rare-earth permanent magnet with high BH product and the research of magnet configuration with narrow pole pitch on open magnet surface, both using ANSYS. The possibility to separate micro-disseminated feebly magnetic minerals by improving the field intensity and the capture line distribution rate on open magnet surface were verified. The research on the method to pile up magnets to increase peak value of field intensity on the open magnet to 1.0T was done through correlation analysis between shape and dimensions of magnetic material and field intensity. And the research on technology method to improve capture line distribution rate in the separating field to 1.25×105/m2 was done through optimization design of magnet configuration of the open magnet with narrow pole pitch. Laboratory tests were performed with hematite sample from ore dressing plant such as Hainan mine, Qidong iron ore, etc. The separation results acquired were at the same level as using the electromagnetic separator, verifying the possibility to separate micro-disseminated feebly magnetic minerals with open magnet. The research suggested a new idea about the development of magnetic separator with high efficiency and low costs to separate feebly magnetic minerals and non-magnetic gangues.

Jan 1, 2014

By X. O. Xia

This paper introduces a kind of flotation machine for nonferrous metal, ferrous metal and non-metal minerals. With the application and development of flotation machine, researching the designment of master parts, including tank, impeller, stator, false bottom. Through the commercial run to validate the correctness of designment, achieving satisfied technical and economic target and supplying a kind of efficient and reliable flotation machine.

Jan 1, 2014

By B. Orberger

The fine fraction (< 2 mm) of the high grade Mn-ore from the world class Moanda deposit, Francevillan basin, in Gabon, contains up to 30 wt. % of manganese and about 0.4 wt. % phosphorous. A pilot study at laboratory scale integrating mineralogy and geochemistry before and after ultrasonic treatment was conducted on the fine fraction (< 2 mm) of oxidized Mn ore in order to reduce the phosphorous content and enrich this fraction in manganese. The fine fraction was dried, crushed at 2 cm and sieved at 2 mm. The two fractions (< 2 mm and 2 mm ? 2 cm) were investigated by X-ray diffraction and scanning electron microprobe ? electron dispersive spectroscopy analyses. Both fractions contain lithiophorite, cryptomelane and pyrolusite as Mn carrier, and goethite, muscovite, illite and quartz as contaminants. The Mn hydroxide nsutite was only found in the fraction 2mm ? 2 cm.The < 2 mm fraction is significantly richer in goethite, muscovite/illite, and quartz. Phosphorous carriers are mainly goethite (up to 2.8 wt. % P2O5), while the Mn minerals contain up to 0.8 wt. % P2O5. The Mn minerals are partly included in an agglomerate of goethite, muscovite/illite, and quartz. The < 2 mm fraction was treated by ultrasound for 30 s in normal water. Mineralogical and chemical analyses after ultrasound treatment showed that the Mn-minerals were largely liberated from the goethite-muscovite-illite agglomerate. Mass balance calculations show that after ultrasonic treatment the < 2 mm fraction was ? 50 % enriched in Mn and ?50 % impoverished in P.

Sep 1, 2012

By V. V. Zakopaylo, M. V. Lukyantseva, V. A. Ignatkina, V. A. Bocharov, L. C. Khachatryan, D. M. Altynamanov, A. A. Kayumov, R. H. Sharipov

"This research was aimed to explain the reasons of low floatability of tennantite from refractory pyrite ores of non-ferrous metals and to create a reagent regime for selective increasing a recovery of copper sulfide minerals from arsenic-containing copper pyrite ore. ?opper-zinc ore of the Uzelga deposit has 89% of pyrite, some part as melnikovite; copper is assayed as 3.58% of tennantite and 0.25% of chalcopyrite; there is 2.19% sphalerite. Sulfide minerals are very finely disseminated. Tennantite is genetically related to primary copper sulfides. Graphene was identified on the surface of tennantite by a transmission electron microscopy (TEM) method. The recovery of tennantite was rose up by using the collector M-TF. M-TF is the mixture of diisobutylditiophosphate (DTF) and O-isopropyl-N-methyl (ethyl) (TC) in the certain ratio. M-TF change up a kinetic of copper sulfide flotation in a slightly alkaline medium, but pyrite has slowly floatability at this moment. A depressing effect of thiosulfate ions in a liquid phase of pulp flotation tennantite from pyrite ore has been established. A copper recovery up 14.2% (from 67.7 to 82.0%) into a copper concentrate level off copper grade of 18.65% (butkx) and 18.68% (M-TF) has been increased by the new technology with M-TF compared to a standard technology with butkx. A main copper recovery up to 50 % in an inter-cycle copper concentrate assaying 19-21% Cu in case of using M-TF was gotten. A zinc concentrate with recovery of 50% and a zinc assay of 41.76% by a standard flow sheet with butyl xanthate was obtained. A zinc recovery of 70.3% with a zinc grade of 44.17% by the M-TF technology was achieved.INTRODUCTION The pyrite copper-zinc ores of the Urals region are considered refractory. The distinctive features of these ores include a high content of pyrite (90-95%), the presence of arsenopyrite and arsenical pyrite, and the simultaneous presence of chalcopyrite, bornite, tennantite with the predominance of the latter (Andreasen et al.,2008;.Dobrotsvetov, 2009; Chanturiya et al. 2016). The flotation properties of tennantite differ from those of chalcopyrite (Xumeng Chen, Yongjun Peng, Dee Bradshaw. 2014), which is the reason why a comprehensive study was under taken of the flotation activity of tennantite and a process for its recovery was developed. The proposed agent treatment and flotation process make it possible to produce salable copper and zinc concentrates."

Jan 1, 2018

By Ho-Seok Jeon

The separation in gravity concentrators is based on the density difference between valuable and gangue minerals. In addition to density, many auxiliary parameters like particle size, shape, feed rate, pulp density etc. plays an important role in the separation. The performance efficiency of gravity units is largely based on the interference of such auxiliary parameters during separation. Many gravity concentrators are used for the beneficiation of cassiterite ores and performance of which are varying with different feed material, particle size and required enrichment from the unit. Selection of gravity units is generally based on laboratory testing and data collected from the previous experience. In the present investigation cassiterite ore collected from Uljin deposit, South Korea has been subjected to various gravity units like jig, spiral, and Knelson concentrator with the intension to pre-concentrate the ore. Second stage concentration was carried out using shaking tables. The article mainly summarizes performance evaluation methods employed for gravity concentrators. Selection of gravity circuit for the beneficiation of cassiterite was made on the basis of the recovery-grade curve, and Tromp curve methods. Keywords: cassiterite, gravity concentration, recovery-grade curve, sink-float test, tromp curve

Sep 1, 2012

By P. Prusti

An air dense medium fluidised bed separator (ADMFBS) is the efficient process for dry beneficiation of coal. Magnetite powder is used as medium to make required pseudo-fluid density in the fluidised bed. The dynamics behavior of coal particle with reference to its position changes from ideal solution to pseudo-fluid condition in different bed densities depending on its shape, size and density. In this study, three set of projected areas of coal particles were taken. Each set contains four different shapes i.e., cubical, rectangular prism, spherical and triangular prism with different density starting from 1.3 to 1.8 gm/cc. It is observed that coal particles having density less than the bed density, floats in different positions in the dense medium fluidised bed. Higher projected area particles float in deeper height in comparison with smaller projected area. The difference in position of coal particles in the bed increases (nearly 1 to 4 cm) as the coal density approaches towards bed density irrespective of the different shapes. Different shapes of coal particles behave in different ways based on the operating parameters like bed density, coal density and projected area of coal particle. Empirical model equations are proposed to predict the position of coal particle of each shape in the air dense medium fluidised bed system. Keywords: ADMFBS, particle dynamics, projected area, shape

Sep 1, 2012

By M. L. Wu

A moderately thermophilic acidophiles strain had been isolated from the bio-heap leaching plant in Zijinshan Copper Mine, and the identification based on the PCR-16S rRNA gene sequence homology analysis with morphologic and physiologic methods was conducted by polyphasic taxono-my and phylogeny research. The results show that the strain by depurated belongs to Acidthiobacillus genus and is considered as Acidthiobacillus albertensis.

Jan 1, 2014

By Dianyin Liang, Hongxiang Ran, Xiaoming Wang, Xiaoou Xia

"This paper presents a new magnetic separator, which can be applied to increase the grade of fine magnetite ore feeding of ball mill. This innovative equipment possesses a rotating magnetic system and has a magnetic field of rapid polarity change which can strengthen the destruction of magnetic agglomerations and the dispersion of minerals to improve the quality of separation. Now this type separators have been successfully applied in several large concentrating plants such as Shuichang Iron Mine under Shouang Mining Company in China. Finally, this paper outlines practical results focused on feed grade and tailing yield, the results are showing that the quality of feeding can be improve tremendously. Hence, a new generator of rotating magnetic field has been paved. INTRODUCTION Jidong region in China is the important origin of iron ore, the characteristics of the iron ore in this region is low grade and complex, the iron mine discharges fine powder tailings reaches tens of millions of tons each year, in the wind action easy to form sand, this poses a threat to the atmosphere environment of Beijing. In order to reduce the mixing of large amount of useless ore and reduce the energy consumption of mill operation, a high efficiency pregrinding equipment is needed. Rotating magnetic field separator (RMS) is an advanced equipment, the main advantage of RMS is the significant reduction in particle entrapment and can easily break magnetic agglomeration. This reduction is so significant that RMS is capable of operating very close to theoritical limit for separator precision and can increace efficiency in selection process.Some expenrimental work on dry rotating magnetic field separation has been carried out in July 1998 in the company Ka Pty Ltd, then in 2008 BGRIMM developed industrial separation XCTG0816 in Shandong province . The wet RMS was researched in1960s in Former Soviet Union and the first industrial equipment was developed by BGRIMM in 1970s,then in 1990s wet RMS was applied in Ansteel group corporation. In 2017,6 units large wet RMS (SXCT1230)which were the largest RMS was applied in Sichuan province. No matter wet RMS and dry RMS, although they are used in differenct applications, they have some common research.in addition ,they all have good use effect."

Jan 1, 2018

By N. R. Mandre

In the present work an attempt has been made to study beneficiation of low-grade iron ore associated with manganese clay by selective flocculation. The representative samples obtained for this purpose were initially subjected to chemical and mineralogical studies. The chemical analyses indicated 42.56 % Fe, 6.25% Mn, 8.72 % SiO2 and 13.60 % Al2O3 in the representative sample. The mineralogical analyses carried out under optical microscope showed that the ore mineral predominantly comprised of iron oxides and hydroxides along with manganese and silicate as gangue minerals. Prior to the beneficiation studies, the samples were subjected to settling tests. These tests were carried out by using poly acrylic acid (paa), poly acryl amide (pam) and guar gum (gg) as the flocculants. From these studies it was observed that settling rate of particles increases with increase in pH and a maximum settling rate of 0.23 cm/secwas obtained at pH 9 in presence of poly acryl amide. Further, the samples were subjected to selective flocculation studies using above-mentioned reagents. From these studies better results were obtained in the experiments carried out with poly acryl amide as the flocculant. Thus, it was possible to upgrade the iron content from 42.5 to 53%, with a recovery of 92%. However, 51% Fe with recovery of 87% and 50% Fe with recovery of 94 % was obtained using poly acrylic acid and guar gum respectively.

Sep 1, 2012

By Y. X. Yang

Porous silica was obtained by acid leaching of chrysotile. The porous silica had been characterized by chemical analysis, powder X-ray diffraction (XRD), Fourier transform infrared spectros-copy (FT-IR), and N2 adsorption-desorption techniques. It is shown in this study that the porous silica retains the nanofibrous morphology of the original chrysotile, and produces a high specific surface area (SBET) of 391. 8 m2/g and total pore volume of 1. 05 mL/g. The increase in SBET and the total pore volume of the porous silica reflect the formation of micropores of 1.2~1.5nm and meso-pores of 3.2~3.8nm in diameter inside the porous structure. The hysteresis loop of N2 adsorption-desorption curve indicates mainly slit-shaped pores. The porous silica is amorphous, but its structure is regular to some extent. The structural unit of silica from chrysotile is a SiO4 tetrahedron and six-member silicon-oxygen rings with the tetrahedral positioned alternately up and down in the six-member rings.

Jan 1, 2014

By N. Naudé

The theory on particles displacement subjected to upwards and settling movements in water, using a water pulse, is described in literature, but very little experimental data is available to verify these theoretical ideas. The aim of this research work was to visualize the displacement of solid particles in a mixture of water and solid particles created with the aid of water pulses in the Mineral Density Separator. From the literature it is known that lighter particles are subjected to higher levels of displacement than heavier particles, and when the particles then settled down, layers of material are formed ac-cording to the densities of the material. By removing the individual material layers, the materials can then be separated according to their densities. During this study the individual material layers were investigated regarding the density and size distribution in that specific density layer. It is important for this project to have a statistical prediction of the ?real? flow of the particles with different density and size distribution, inside the Mineral Density Separator. The information gathered during this study will be used to show the correlation between a two dimensional model of the particle flow and that of the real three dimensional flow inside the Mineral Density Separator.

Jan 1, 2014

By F. Karakas

In this investigation, one of the most energy consuming stage of the cement manufacturing process, grinding stage, was studied. The aim of the study is to reduce the energy consumption. Optimum operating parameters were determined. Experimental studies were performed at three differ-ent stages. Grinding of limestone, clay and marl which are the main components of the cement, to approximately below 90 microns, was the first stage of the cement grinding. At this stage, effect of feed size and ball charge were investigated. At the second stage, the Bond work index of clinker and additives (slag, trass, limestone and gypsum) was found separately. After forming composite cement with clinker and additives, the Bond work index of this mixture was also determined, thus the results of separate grinding and grinding of mixture were compared. The Bond work index of mixture was found as 13.59 kWh/t, while the arithmetic mean of the Bond work index values of components was 14.90 kWh/t. Finally, clinker and additives (slag, trass, limestone and gypsum) were ground under the same conditions. At this stage, laboratory type of ball mill was used in order to understand grinding characteristics of the cement components. As a result of the experiments, it was found that energy consumption for the grinding will be lowered if the mills with 38 % ~ 40 % ball charge are used in the cement grinding. Moreover, grinding with mixture of clinker and additives gave better results than separate grinding of these components in terms of energy consumption.

Jan 1, 2014

By Mohammad Mainul Hoque, Linhan Ge, Ai Wang, Geoffrey Evans, Subhasish Mitra

"Dispersed phase interactions involving bubbles and particles in the turbulent environment play a significant role in the flotation process. The conventional collision models only account for the deterministic rather than the stochastic behavior of turbulenct flow. What the bubble-particle collisions would be like remains an open problem due to the complex nature of turbulent flow. To address this research question, the present study aims to quantify the bubble-particle collision efficiency incorporating turbulence using the computational method. Multiple solid particles were released to interact with a single stationary rigid bubble (non-deformable interface). Effect of particles Stokes number, turbulent intensity (TI) and integral length scale on the bubble-particle collision efficiency (Pc) was examined. Large Eddy Simulation method (LES) was used to compute the continuous phase. Fluctuating velocity required at the inlet boundary condition was derived from Gaussian energy spectrum to generate the upstream turbulence. Discrete Phase Model (DPM) is used to simulate particle trajectory. The characteristics of turbulent flow were analyzed through Energy spectrum and energy dissipation rate. The critical initial releasing radius of the annulus, where Pc equals zero, reaches up to 1.5(Rb+Rp) under high turbulent intensity (TI) 20.48% compared to 0.23(Rb+Rp) calculated from the traditional Pc model. Pc decreases as the distance of initial releasing annulus between bubble centre increases. Pc increases as particle Stokes number increase up to 0.66. The collision efficiency for particles of St less than 0.38 is higher under TI 11.78% compared to TI 4%.INTRODUCTION To increase mineral recovery, interactions between bubbles and particles are essential. All flotation devices achieve it through introducing some level of turbulence into the system by increasing specific energy dissipation rate. Figure 1 shows three different flotation equipment, traditional floatation cell, Concorde cell and cyclonic-static micro-bubble flotation column (FCSMC), with different turbulence generation mechanisms – impeller, down-flow liquid jet and pump recirculation, respectively."

Jan 1, 2018

By J. Quinteros-Riquelme

Despite increasing demand, the supply of silver is limited by its inadequate recovery from ores. Due to its scarcity in nature, its high ore variability and complex mineralogy of current silver deposits, its recovery by mineral froth flotation presents a real challenge for process engineers. A silver ore often contains significant amounts of five to ten different silver minerals and knowledge of the mineralogy is a necessary precursor to flotation testing. In this work, a complex silver ore was treated by using batch laboratory flotation, in an effort to find the best experimental conditions to obtain the optimal silver recovery. Mineralogical characterization of feed samples was conducted using a combination of tools, namely the mineral liberation analyzer (MLA) and inductively-coupled plasma mass spectrometry (LA-ICP-MS), which indicated that most of the silver occurred as ?invisible? silver in pyrite. The pyrite assay of the ore was approximately 4%. The ore was processed in two flotation stages. The first stage, sulphide flotation, aimed to collect a sulphide mineral rich concentrate; then a non-sulphide flotation stage was performed by adding sodium sulphide and collectors to the remaining material in the cell, with the objective of obtaining a pyrite rich concentrate. To reach the target recovery of silver from this ore, various variables were altered. In the first stage: mixed collectors, activators, dispersants, and mainstream inert grinding were assessed. In the second stage, the conditions for sulphidization and subsequent flotation were both investigated. From the grade recovery curves for silver and sulphur it was possible to observe a similar metallurgical behavior for both elements, supporting the results given by the mineralogical characterization. Keywords: silver oxide, froth flotation, sulphidization, mig

Sep 1, 2012

By V. V. Lvov, L. S. Chitalov

"The purpose of the research is intensification of physico-mechanical ore properties determination for ball grinding processes in comminution circuits. The research presents comparative studies aimed at intensification of Bond Ball Mill Work Index (BWi) determination, such as testing technique of Ahmadi and Shahsavari, Berry and Bruse, Gharehgheshlagh, Horst and Bassarear, Kapur, Magdalinovich. The subject of the research is a test procedure of apatite-nepheline, copper-nickel, gold-sulfide and iron ores for the Bond ball mill index. The Bond Ball Mill Work Index for the material firstly was determined by standard Bond test methodology. Two the most promising testing techniques - Ahmadi and Kapur testing techniques - were modified. For the Ahmadi technique it was proposed to pay attention to the circulating load, which should be stabilized on the value of 250% as fast as possible. Two methods were put forward to quicker stabilize the circulating load. For the Kapur technique it was proposed to use empirical coefficients, which is determined especially for the apatite-nepheline, copper-nickel, gold-sulfide and ores. The modified Ahmadi and Kapur techniques require no more than two cycles of ball grinding to determine BWi (while normally 6-8 cycles are required) and less than 5 kg of initial feed. The suggested modified Ahmadi and Kapur techniques allow to intensify the physico-mechanical ore properties determination for ball grinding processes and BWi test costs considerably, which makes them useful for mass sampling and monitoring strength properties of ores entering a concentrating mill. INTRODUCTION When designing concentrating mills, the choice of the technological scheme for ore pretreatment, particularly the type, quantity and size of the main process environment, the determination of optimal grinding conditions and the calculation of equipment load are carried out by preliminary studies of grinding in semi-industrial or laboratory-scale plants. Semi-industrial tests on full-scale plants provide the most reliable information for calculating specific loads for equipment. However, this requires a significant amount of ore samples, a high labor costs and the pilot plants. Thence the most researchers performed grinding tests with small laboratory equipment using small ore samples."

Jan 1, 2018

By R. Singh

The present paper deals with the development of flotation based process for enrichment of a lead-zinc sulphide ore from Ganesh-Himal region of Nepal. Detailed characterisation and flotation studies were carried out under varying process conditions. The sample assayed 2.47% Pb with 13.6% Zn. The ore was predominantly made up of spahlerite and pyrite in association with subordinate amounts of galena, minor amounts of pyrrhotite and chalcopyrite. Dolomite was the main gangue. The modal analysis showed the probability of fair liberation of sulphides from gangues around 210 microns but the locking of galena with sphalerite and other sulphides continued to finer sizes. Under the optimum process conditions the rougher lead and zinc recoveries were 96.3% and 90% respectively. Multistage cleanings of rougher products proved helpful in improving the concentrate grade, meeting the required specification. Based on the studies undertake a process flow-sheet for the concentration of the ore to individual lead and zinc concentrates was developed.

Jan 1, 2014

By Z. H. Liu

We experimented with slurry which from one of coal preparation plant in Guizhou province and made researches on double hump gradation, one of critical factor of gradation technology, which can influence pulping character in the process of making coal water mixture (CWM). The purpose for it is to find the best particle gradation which can meet the requirements in concentration, viscosity, and stability for CWM. The final result is that the concentration, viscosity, stability of CWM can meet the requirement for industrial use while the rate of fine particle in the slurry is 70%~75% and the maximum concentration of 62%.

Jan 1, 2014

By F. H. Wang

The Yinmao Lead-Zinc Mine Co. Ltd. has got 50 years of mining history. In recent years, the manganese grade in the flotation tailings has been continuously increasing. In order to make fuller use of the existing resources, as well as to increase the company?s economic efficiency, our company adopted the technique ?magnetic separation? and ?iron removal? to effectively recycle the manganese concentrate resources.

Jan 1, 2014