THE subject of steel cleanliness has always been a major one in the steel industry and much study and effort have been expended toward improving the cleanliness of steel and meeting the ever increasing demands of customers for steels that will give better performance in service and permit economies in design and efficiency of the final product. Sometimes wee may feel that-these demands are unnecessarily stringent, and probably this is true in some instances. However, the pressure for higher quality has acted as a stimulus toward improving quality and, therefore, has tended to promote progress. In this paper, the whole subject off cleanliness is covered in a general way. In the discussion' on steelmaking practices, remarks have been limited to basic electric- furnace practice in the making of alloy steels.

Jan 1, 1947

By S. Lipson, H. W. Antes, H. Rosenthal

A study was made of the effect of ingot structure on the strength and ductility of high-strength wrought-aluminum alloys. It was found that a fine-cast structure facilitated complete homogenization which, in turn, resulted in significant increases in ductility and strength. A completely homogenized 7075-T6 alloy developed tensile properties of 85,000 psi UTS, 75,000 psi YS, with 40 pct RA. Completely homogenized 7001-T6 alloy tensile properties were 102,000 psi UTS, 99,000 psi YS, with 19 pct Ra. A method was devised for making small ingots having secondary dendrite arm spacing of less than 10 u. This method involved multiple-pass arc melting of commercial rolled plate with a tungsten electvode. This material could be completely homogenized after 3 hr at 900°F; homogenization of the original plate material was not complete after 120 hv at 900°F. Degree of homogeneity was determined by use of metallographic and electron-microprobe analyses. The electron-micro-probe study also showed the preferential segregation of solutes in the microstructure. HIGH-strength aluminum alloys, such as those of the 7000 series, usually freeze by the formation and growth of dendrites. The dendrite arm spacing (DAS) depends on the rate of solidification.' Commercial ingots are usually direct chill-cast to promote more rapid solidification, but, due to the large mass of the ingot, localized solidification times are long and a large DAS results. During solidification, solute elements are rejected by the solid as it forms, causing enrichment of the liquid and ultimately solute-rich interdendritic regions. In order to attain a homogeneous ingot, the segregated solutes must diffuse across the dendrite arms. The larger the DM, the longer the time for complete homogenization. In the case of commercial ingots, the DAS is so large that the time for complete homogenization is prohibitively long and, therefore, second phases or compounds are always present. These un-dissolved phases are carried over to the wrought material during processing, resulting in an impairment of strength and ductility. In addition, the mechanical fibering of the undissolved second phases or compounds during working results in mechanical property anisotropy. If complete homogenization could be attained, higher ductility could be expected. The realization of higher ductility at current strength levels is a desirable objective; however, if higher-strength alloys were wanted, it might be possible to sacrifice some of this ductility by adding more solute elements and produce even higher-strength alloys than are currently available. Further, if complete homogenization leads to more efficient utilization of solute elements, then more dilute alloys should have relatively high strengths with very high ductility. In all instances, it would be expected that the degree of mechanical property anisotropy due to mechanical fibering would be reduced. Therefore, it was the purpose of this investigation to produce cast structures that would facilitate homogenization and to determine the effect of homogenization on the properties of high-strength, wrought-aluminum alloys. MATERIAL CLASSIFICATION Commercial Alloys. In order to illustrate the non-homogeneous condition that exists in commercial high-strength, wrought-aluminum alloys, typical micro-structures of 7001, 7075, and 7178 are shown in Fig. 1. The chemical compositional specifications of these alloys are given in Table I. It can be seen in Fig. 1 that a considerable amount of undissolved second-phase material is present in each of these alloys. The solute elements associated with the undissolved phases were identified by electron microanalyses. Back-scattered electron images and characteristic X-ray images of the three commercial alloys are shown in Figs. 2, 3, and 4. These data indicate that the second phases are regions of high copper and high iron-copper concentrations. The second-phase material also was analyzed for magnesium, zinc, manganese, chromium, and silicon, but no significant enrichment above that of the matrix was found. Therefore, the problem of homogenization resolved itself into one of dissolving the copper-rich and the iron-copper-rich second phases. In order to accomplish this objective, two approaches were made. The first was to reduce the iron as low as possible since this element has a maximum solid solubility of 0.03 pct in aluminum. The second was to produce cast structures with finer DAS to facilitate dissolving the second phases. Commercially Produced High-Purity Alloys. A special high-purity, 2000-lb ingot of 7075 alloy was made by a commercial producer. This alloy contained the following weight percentages of solutes: 5.63 Zn, 2.48 Mg, 1.49 Cu, and 0.21 Cr. All other elements combined were less than 0.02 pct by wt including iron and silicon at less than 0.01 pct each. The ingot was cast and processed into rolled plate using standard commercial techniques. Microstructures of standard commercial 7075 and the special high-purity 7075 are shown in Fig. 5. It can be seen from this figure that the high-purity alloy has less undissolved second-phase material, but a significant amount was still present. The second phase in the high-purity material did not contain iron but it was found to be enriched with copper. The slight effects of the increased purity and de-

Jan 1, 1968

By Lawrence A. Shepard, Richard H. Krock

A series of ductile, two phase W-Ni-Fe composites, sintered in the presence of a liquid phase, were tested in tension. Identical room temperature stress-strain curves were obtained for specimens containing from 80 to 92 wt pct W (58 to 75 vol pct W particles). The composites exhibited a maximum elongation of 29pct at room temperature, and 10.7 pct at 77 °K. The tungsten particles in the composite elongated by the same amount at these temperatures. Single-phase alloy specimens matching the composition of the composite matrix showed about one half the flow stress of the composites. The test results demonstrated that the mechanical properties of W-Ni-Fe composites are determined by the tungsten particles alone and are independent of matrix volume fraction or mean free path over the composition range studied. A general prediction of the plastic behavior of two-phase alloys or composites from a knowledge of the properties, size, shape, and dispersion of the individual components is not, at present, possible. The excellent theoretical and experimental exposition of the dispersion-strengthening problem applies only to cases where the stronger phase is present as fine particles and in volume fractions of a few percent. Materials in which the stronger phase constitutes a significant fraction of the volume, although of broad engineering interest, have received comparatively little analytical attention. This important group of materials is the concern of the present study. The degree of deformation of each phase during the plastic working of a ductile two-phase alloy has been established by Boas and Honeycombe,1 Clare-brough,2 and Clarebrough and berger.3 These workers empirically correlated the recrystallization temperature of the individual phases with the degree of cold work sustained by each. It was shown that the deformations of both phases are equal and therefore the same as that sustained by the composite whole when the volume fraction of the stronger phase exceeds 35 pct. At yielding, however, deformation begins in the weaker phase. A direct correlation of composite strength, as a function of deformation, with the strength of the individual components cannot be made. In the presence of stronger phase particles, the flow stress of the weaker matrix phase is enhanced by an additional hydrostatic component. The development and potential magnitude of matrix strength promotion upon straining has not even been experimentally established. Quantitative work in this field has been confined to ceramic-metal composites. These materials fracture at strains considerably below 1 pct by cracking of the ceramic particles.4-6 An indication of the potential constrained matrix strength capacity is given by the observation by Nishimatsu and Gur-land4 that the maximum tensile strength of a WC-Co composite is almost double the bulk strength of the cobalt matrix. The relationship between composite strength and geometry is ordinarily expressed in terms of the mean-free matrix path (referred to subsequently as MFP) between the stronger particles.* This factor takes into account both the volume fraction of matrix phase and the average size of the particles. unke17 concluded that composite strength varied directly with the decreasing log MFP, following the Gen-samer8 relationship. However, Gurland and ~radzil~ reported a strength maximum at an MFP of the order of 1 p in WC-Co composites. A ductile two phase metallic composite was chosen for the present investigation of composite mechanical properties with the view of avoiding the difficulties and ambiguities noted above. The W-Ni-Fe heavy alloy of Green, Jones, and pitkin9 contains 80 to 94 wt pct W, and nickel and iron in a weight ratio

Jan 1, 1963

By Robert E. Cuthbertson

It is the purpose of this paper to describe in detail the laboratory development and mill application of an unusual combination of flotation reagents employed in the concentrator of the Climax Molybdenum Co., on the Continental Divide, near Leadville, Lake County, Colorado. This development originated in an ore-dressing research laboratory maintained by Climax at the experimental plant of the Colorado School of Mines, which is staffed by men directly employed by the Climax Molybdenum Co. Mill-scale testing of laboratory developments was supervised by a representative from the testing laboratory, working in close cooperation with the operating staff at the mill. General milling practice at Climax is ably described in a paper by E. J. Duggan,1 mill superintendent. Other aspects of the Climax project have been described in papers by W. J. Coulter,2 by Butler, Vanderwilt and Henderson,= by Allen Kissock,4 and by Leo H. Glanville.5 Consequently, this paper will be corfined to the metallurgical aspects of recent reagent developments, avoiding, as much as possible, repetition of material covered in these earlier publications. Brief History of Reagent Practice at Climax Prior to the year 1937, the only reagents employed at Climax for froth production and collecting action in the flotation of molybdenite were steam-distilled or destructively distilled pine oils. The only exceptions to this practice were brief periods of mill testing, when reagents of various types were tried on an experimental basis. None of these experimental runs was sufficiently encouraging to justify its continuation as regular practice. Sodium cyanide has been employed since the very early days of milling at Climax as an inhibiting agent for control of pyrite and chalcopyrite. Alkaline reagents such as lime or soda ash have been used in recent years to minimize the detrimental effect of iron salts on flotation of molybdenite. The presence of these harmful salts is attributed to the decomposition of fine metallics abraded from liners and balls in the first stage of regrinding rougher concentrate. Flint pebbles are used in subsequent regrinding, since alkaline reagents are not entirely adequate to offset the inhibiting effect of iron salts as the grind becomes progressively finer and the grade of concentrate progressively higher. Climax metallurgists were familiar at an early date with the use of petroleum products such as kerosene and gas oil as promoters of flotation of molybdenite. Charles C. Oliver6 discussed the use of pine oil and kerosene as early as 19-20, in connection with the milling practice at Dominion Molybdenite Co., Quebec. Nevertheless, the early attempts to apply this knowledge in the Climax concentrator were complete failures. In the light of recent experience, it may seem strange that the early mill tests with petroleum

Jan 1, 1947

By Robert E. Cuthbertson

It is the purpose of this paper to describe in detail the laboratory development and mill application of an unusual combination of flotation reagents employed in the concentrator of the Climax Molybdenum Co., on the Continental Divide, near Leadville, Lake County, Colorado. This development originated in an ore-dressing research laboratory maintained by Climax at the experimental plant of the Colorado School of Mines, which is staffed by men directly employed by the Climax Molybdenum Co. Mill-scale testing of laboratory developments was supervised by a representative from the testing laboratory, working in close cooperation with the operating staff at the mill. General milling practice at Climax is ably described in a paper by E. J. Duggan,1 mill superintendent. Other aspects of the Climax project have been described in papers by W. J. Coulter,2 by Butler, Vanderwilt and Henderson,= by Allen Kissock,4 and by Leo H. Glanville.5 Consequently, this paper will be corfined to the metallurgical aspects of recent reagent developments, avoiding, as much as possible, repetition of material covered in these earlier publications. Brief History of Reagent Practice at Climax Prior to the year 1937, the only reagents employed at Climax for froth production and collecting action in the flotation of molybdenite were steam-distilled or destructively distilled pine oils. The only exceptions to this practice were brief periods of mill testing, when reagents of various types were tried on an experimental basis. None of these experimental runs was sufficiently encouraging to justify its continuation as regular practice. Sodium cyanide has been employed since the very early days of milling at Climax as an inhibiting agent for control of pyrite and chalcopyrite. Alkaline reagents such as lime or soda ash have been used in recent years to minimize the detrimental effect of iron salts on flotation of molybdenite. The presence of these harmful salts is attributed to the decomposition of fine metallics abraded from liners and balls in the first stage of regrinding rougher concentrate. Flint pebbles are used in subsequent regrinding, since alkaline reagents are not entirely adequate to offset the inhibiting effect of iron salts as the grind becomes progressively finer and the grade of concentrate progressively higher. Climax metallurgists were familiar at an early date with the use of petroleum products such as kerosene and gas oil as promoters of flotation of molybdenite. Charles C. Oliver6 discussed the use of pine oil and kerosene as early as 19-20, in connection with the milling practice at Dominion Molybdenite Co., Quebec. Nevertheless, the early attempts to apply this knowledge in the Climax concentrator were complete failures. In the light of recent experience, it may seem strange that the early mill tests with petroleum

Jan 1, 1947

By D. G. Westlake

Polycrystalline tensile specimens of various Zr-0-H alloys have been tested at 298°, 178°, and 77°K. Solute oxygen and hydride precipitates in quenched alloys made individual contributions to the yield strength at 0.2 pct strain which combined to produce a resultant strength increment, a,., Ductility changes which were ohserved can he interpreted in terms of the various oxygen and hydrogen concentrations, testing tem -peratures, and dispositions of the hydride. ADDITIONS of oxygen in solid solution were known to increase the yield and tensile strengths of polycrystalline zirconium as early as 1951.' More recently, the critical resolved shear stress (CRSS) for prism slip in zirconium single crystals was also shown to be affected by the solute oxygen impurity.' This latter work also demonstrated that large increments of strength could be contributed by the finely dispersed zirconium hydride precipitates that are present in quenched Zr-H alloys.3 It was concluded that the combined strengthening due to alloying could be expressed by where to is the increase in the CRSS due to solute oxygen alone and TH is the increase due to finely dispersed hydride precipitates. Eq. [I] is analogous to one used to express the combined strengthening effects of work hardening and neutron radiation damage.4 Eq. [1] was verified only indirectly and for only small amounts of the impurities—up to 0.14 at. pct 0 and 0.63 at. pct H. The present investigation was undertaken to obtain a more direct verification of the validity of the form of Eq. [1] for this system and also to determine the combined effects of oxygen and finely dispersed hydride precipitates on the tensile strength and ductility of polycrystalline zirconium. EXPERIMENTAL PROCEDURE Tensile specimens were machined from the same rolled billet of Kroll zirconium used in the earlier study.' These measured 38 by 4.7 by 0.5 mm and had 10-mm gage lengths which were 2.8 by 0.5 mm. Each specimen was ß-annealed in vacuo at 1173°K for 15.5 hr and a-annealed at 1073°K for 4 hr to D. G. WESTLAKE, Member AIME, is Associate Metal l ur-gist, Metallurgy Division, Argonne National Laboratory, Argonne, III. Manuscript submitted July 17, 1964. IMD______________ give an equiaxed structure with grain diameters averaging 0.06 mm. Oxygen was added by allowing the metal to react with a known quantity of oxygen during the 0 anneal and known quantities of hydrogen were added during the a anneal. Each alloy was encapsulated in Pyrex under vacuum, annealed at 873°K for 4 hr, quenched into ice water, and polished by immersion in a solution of 46.75 vol pct H2O, 46.75 vol pct concentrated HNO3, and 6.5 vol pct HF (49 pct) at 298°K. Special heat treatments given to a few specimens are described in the results below. Tensile tests were done on an Instron machine and were begun within 20 min after the quench, except where specified otherwise. Tests at 298°K were in air, at 178°K in acetone, and at 77°K in liquid nitrogen. All tests were at a strain rate of 8x sec-1. RESULTS AND DISCUSSION Yield Stress at 298°K. The compositions of alloys and the corresponding yield stresses (0.2 pct strain) are given in Table I. A plot of the yield stresses of the oxygen alloys, A, B, C, and D, indicates that varies linearly with CO1/2, where Co is the oxygen concentration, Fig. 1. This is in accord with Fleischer's6 theory for solution strengthening if the oxygen atoms do not cluster, or the cluster size remains constant with increasing oxygen concentration. In Fig. 1, it appears that if one could prepare some oxygen-free zirconium its yield stress would be very low. Therefore, we shall assume that for the oxygen alloys is equivalent to O0, the strength increment contributed by the presence of oxygen. The relationship between0.2and Co is expressed by 0.2 = 31.3 CO1/2, when the yield stress is in kg per sq mm and the concentration is in at. pct. Each of the hydrogen alloys, Al, A2, A3, and A4, contained 0.081 at. pct 0 as an impurity. In Fig. 1, it appears that this small amount of oxygen makes a significant contribution to the strength which cannot be ignored when we evaluate the contribution of the finely dispersed hydride. Let us assume the validity of the following equation: a0.2 = (a2o+a2R)1/2 [2] which is analogous to Eq. [I] for single crystals, and calculate values of UH for the hydrogen alloys by using the experimental values of 0.2 and o (0.081 at. pct) = 8.9 kg per sq mm. For 0.36 at. pct H, oH = 6.47; for 0.72 at. pct H, OH = 11.30; for 2.16 at. pct H, OH = 19.4; and for 3.60 at. pct H,

Jan 1, 1965

By S. F. Urban, G. Derge

AT the time this investigation was initiated variations were observed in the quality of different heats of basic electric-furnace steels, although they had been made under purportedly similar conditions. This indicated that these variations were related to normally unobserved variations in the character of the bath, especially during the "refining" period. Although the slags used for this operation are commonly referred to as "reducing" slags, and are regarded as having a "deoxidizing" action on the bath, no reliable measurements of this action were available. It was decided, therefore, to study the behavior of oxygen in the metal for a large enough number of heats to learn its normal variations and to relate these variations to regularly observed conditions [f] operation. The most important general conclusion reached was that the time a heat is held under a reducing slag should be reduced to a minimum, which was about an hour and a half under the conditions studied. Beyond this time no observable beneficial effects are obtained from the reducing slags, insofar as oxygen and sulphur content of the bath are concerned. It is likely that added time may increase hydrogen content as well as heat costs. The oxygen content of the bath is never reduced below the amount in equilibrium with the carbon. Concurrently with this work, J. S. Marsh1 presented data that supplement and support many of the results of this paper. PROCEDURE The work was done in two different electric-furnace shops of the same plant. The selection of heats was made primarily with regard to the convenience of heat schedules. Companion slag and metal samples were taken just prior to slag-off and throughout the refining period for an initial set of 17 heats, and before slag-off and near tap for an additional 13 heats. Slag sampling presented no particular problem; a spoonful of slag was poured onto a metal plate and when sufficiently cool was sealed in an airtight container. Sampling the metal for oxygen presented a more complex problem. Because of the lack of previous experience in sampling electric-furnace baths, a number of methods were compared. Chilled Wedge Samples2 An unkilled metal sample is removed from tie furnace in a well-slagged carbometer spoon and poured immediately into a heavy copper mold designed to provide rapid freezing. Three different types of molds were used to determine the optimum for electric-furnace heats. The Big Wedge Mold (a) was a 4 by 4 by 4-in. split copper mold, yielding a wedge-shaped casting 1 in. wide, 1 ½ in. long, and ¼ in. maximum thickness, and was finally adopted as the most satisfactory design. The Long Wedge Mold (b) was a 2 by 2 by 5 ¼ -in. split copper mold, yielding a wedge-shaped casting 1 in. wide, 2 ¾ in. long, and ¼ in. maximum thickness. The Small Wedge Mold (c) was 2 by 2 by 4-in. split copper mold, yielding a wedge-shaped casting 1 in. wide, 1 ½ in. long, and ¼ in. maximum thickness.

Jan 1, 1947

By J. R. Campbell

It is the purpose of this paper to review somewhat in detail the literature on the subject that is extant, which ought to provoke considerable beneficial discussion. The value of 1 per cent. ash in blast-furnace practice was brought to the attention of the writer when he was connected with the U. S. Steel Corpn. Various groups of blast furnaces in the Pittsburgh district compiled a statement in which the average saving was about 6 c. per ton on pig iron for every 1 per cent. of ash reduction. Later, the same groups of furnaces, when materials had reached a higher price, compiled a statement in which there was a 30-cent saving on pig iron for every 4 per cent. ash reduction in the Pittsburgh district, which was equivalent to 7½ c. for every 1 per cent. ash reduction. In the Chicago district, on long freight hauls of coal and coke from the Pocahontas district, the set-up was 30 c. per ton of pig iron for every 2 per cent. ash reduction, or 15 c. for every 1 per cent. Some years ago, Ralph H. Sweetser, of the American Rolling Mill Co., presented a paper which provoked considerable comment.' To get the matter again before this body a résumé of his computations is given below: Comparison of Pig Iron Costs Ash in Coal. Ash in CoKe, Fixed Carbon in Coke peR Ton OB PIG Iron peN Day, Per Cent. PeR CeNt. Coke. Per Cent. PIG IRon. Lb. Tons 6.00 8.70 89.80 1800 365.0 7.00 10.15 88.35 1860 353.2 Coke with 8.70 Per Cent. Ash Ore mixture, 4144 It). = 1.85 tons @ $5.50.............................. $10.17 Coke, 1800 lb. = 0.90 ton @ $6.50..................................... 5.85 Limestone, 1000 lb. = 0.50 ton @ $1.50................................. 0.75 Labor, $365 per day on 365 tons....................................... 1.00 Supplies and service, $250 per day...................................... 0.68 Overhead, $200 per day............................................... 0.55 Reserve for relining and depreciation................................... 1.00 Total............................................................. $20.00

Jan 1, 1931

By J. J. Kanter

The choice of a nonferrous metal or alloy for a given Application is frequently predicated upon a consideration of properties other than merely the capacity to withstand stress. When ability to withstand stress is the dominant engineering requisite of the material to be used, economic considerations seldom lead to the choice of nonferrous metals and alloys. In most instances where a nonferrous metal is used it is because of some special quality of either corrosion resistance, electrical properties, thermal properties, antifriction, or fabrication advantage that commends its application. The mechanical properties, as a rule, present an incidental engineering consideration entirely secondary to the special quality deciding its use. Indeed, great ingenuity has often been exhibited by engineers and metallurgists in overcoming the mechanical shortcomings of a nonferrous base material. in order to take advantage of some outstanding property. . With this thought in mind, we might better appreciate some of the problems in stress design. encountered with nonferrous metals and alloys pertinent to a symposium on their creep characteristics. Our considerations must necessarily be far from complete because of the broad range of materials in the nonferrous category for which creep properties assume a technical interest. Creep deformation of these metals can be subject for study at temperatures ranging from ambient to incandescent, depending upon which one is under consideration. Whereas the steel metallurgist thinks of creep as an essentially high-temperature engineering consideration, the same is not necessarily true in the field at hand. The diversity of the creep problems in the nonferrous field is perhaps accountable to some extent for its virginity as a symposium subject. Each research has necessarily been sponsored by some organization or group interested either in promoting the use of a certain nonferrous base or in obtaining data toward the solution of a mechanical difficulty encountered in applying a material indispensable for its special attributes. Perhaps as many techniques of creep testing have been used as there are base metals implied under "nonferrous." Some of the creep problems that have occasioned researches are associated with steam-pressure vessels such as tubes, drums, castings, and forgings of copper-base and nickel-base alloys, cable sheathings of lead and lead-base alloys, electrical transmission lines of copper and aluminum, engine parts die-cast from alloys based on zinc, aluminum, copper— soldered and brazed joints-—as well as numerous duties at extremely high temperatures met with alloys based on cobalt, nickel, tungsten, molybdenum, platinum, and other precious or semiprecious metals. Postwar technology will have the benefit of much creep research on nonferrous metals, which for reasons of security cannot be discussed on this occasion. Suitability OF Metals As already intimated, the bulk of the constructional metal that ordinarily is

Jan 1, 1945

Arizona Bureau of Mines and College of Mines and Engineering, University of Arizona, Tucson, Ariz. Lists of the maps and bulletins available will be sent upon request to G M Butler, Director, Arizona Bureau of Mines, Tucson, Ariz Bulletin 119, A resume of the geology of Arizona, by N. H Darton, is sold for $1, postpaid Fourteen other bulletins, any five of which may be had free of charge (additional numbers may be purchased for 10 cents each) are available as follows - 106, A geological reconnaissance of the Tucson and Amole Mountains, by Olaf P Jenkins and Eldred D Wilson, 114, Fluorspar, by M A Allen and G M Butler, 120, Gold and copper deposits near Payson, Arizona, by Carl Lausen and Eldred D Wilson, 122, Quicksilver resources of Arizona, by Carl Lausen and E D. Gardner, 123, Geology and ore deposits of the Courtland?Gleeson region, Arizona, by Eldred D Wilson; 125, The mineral industries of Arizona, by J B Tenney, 126, Asbestos deposits of

Jan 1, 1933

By E. J. Dulis, R. M. Fisher, K. G. Carroll

IT is well known that ferritic steels containing more than 15 pct Cr when subjected to temperatures in the range of 700" to 1000°F exhibit increasing hardness and decreasing ductility. The phenomenon has been widely termed the "885 °F embrittlement," after the temperature of most marked effect.'.' In view of the excellent review articles available in the literature3-6 only a brief account of experimentally established facts need be given here. The extent of changes in physical characteristics during embrittlement depends on chromium concentration and time at temperature, higher alloy content and longer time both promoting more rapid and extensive changes. In a 27 pct Cr steel, changes in impact strength and in angle of fracture in bending can be detected after only a 1 hr exposure at 885°F; after 50 hr this steel becomes quite brittle. Hardness increases slowly with time during thousands of hours exposure and may attain a maximum hardness number twice as large as that of the unexposed steel. Microstructural changes accompanying embrittlement have been described as an initial widening of grain boundaries followed by eventual darkening of ferrite grains. Embrittled steels etch more readily, e.g., the weight loss of a 27 pct Cr steel in acid solution may occur at a rate one hundred fold greater following exposure at 885 OF. Marked changes which accompany embrittlement have been observed in electrical resistivity, specific gravity, and magnetic coercive force. Changes in physical properties may be readily removed by heating at temperatures above the embrittling range, such as a treatment at 1100°F for 1 hr. It has frequently been noted that the 885 °F embrittlement suggests precipitation on a submicro-scopic scale of a chromium-rich constituent, the nature of which has not been revealed by X-ray diffraction. Progressive broadening of the body-centered cubic diffraction lines during embrittlement has been observed," and recent observations by Lena and Hawkes' upon single crystals have shown early asterism in X-ray photographs, disappearing within an hour at 900 °F. Many workers have ascribed8-13 the phenomenon to a precipitation of a phase (FeCr), which is known to cause embrittling effects at temperatures much higher than 885°F. Two general observations, however. suggest that a precipitation cannot be responsible for the 885°F phenomenon: 1—prior cold work greatly enhances a formation, whereas it scarcely affects the 885 °F embrittlement, and 2—the presence of an alloying element such as nickel or manganese may have an effect on the 885 °F embrittlement which is opposed to its effect upon a formation. The slight enhancement of a formation and 885°F embrittlement observed in the presence of elements with strong carbide and nitride forming tendencies' is probably a consequence of lessened chromium depletion of the matrix. The bar graph in Fig. 1 shows a typical example, taken from two 27 pct Cr steels used in this work, of the hardness after exposure for 10,000 hr at 900°, 1050°, and 1200°F. Steel A (0.03 pct C, 3.13 pct Mn) showed marked hardening at 900" and 1200°F, whereas steel B (0.12 pct C, 0.63 pct Mn) exhibited only the 900°F hardening. The cr phase was found in steel A at the higher temperatures but not in steel B. Presumably a formation is enhanced by the low-carbon and high-manganese concentrations in A," Thus there are two distinctly different hardening phenomena present which cannot both be ascribed to v precipitation without invoking a transition phase possessing remarkable properties. Materials A number of chromium steels exposed for long periods (5000 to 34,000 hr) at 900°F, as well as unexposed samples of one of the steels, were available for this investigation. Table I gives the chemical compositions and aging treatments of these steels. In addition to these steels exposed in the elevated temperature test furnaces of the National Tube Division, a number of high-chromium steels were heated for short periods in small laboratory air furnaces and lead baths. Supplementing these commercial steels, a sample of high-purity (0.018 pct C, 0.002 pct N) 28 pct Cr iron, exposed 1000 hr at 887°F. was furnished by the Union Carbide and Carbon Corp. In addition, an alloy of iron and chromium of high purity containing 46 pct Cr was used. This

Jan 1, 1954

By R. J. Hafsten, E. S. Davenport, R. A. Grange

THE influence of austenite grain size upon the hardenability of steel is now fairly well understood; for a given austenite, increasing the grain size increases the depth of hardening, and, since the latter is related to the fundamental transformation behavior of austenite, it follows that austenite decomposition must, in general, be retarded by increasing grain size. To date, very little quantitative information bearing directly on the effect of austenite grain size upon the progress and result of isothermal transformation has been published. Davenport and Bain,1 and Zimmerman, Aborn and Bain2 have shown that the transformation is definitely retarded in hypereutectoid plain carbon steels at temperatures near and above the upper region of rapid transformation (Ar') when the austenite grains are increased in size. More recently, Griffiths, Pfeil and Allen3 investigated the effect of a series of different heating (austenitizing) temperatures upon the progress of isothermal transformation at 1245°F. (675°C.) and 745°F. (395°C.) in a medium carbon, low-alloy steel; while they reported no measurements of the austenite grain size, their results suggest that increase in grain size retards austenite transformation at 1245°F. (675°C.), but has no appreciable effect at 745°F (395°C.). The present paper deals with the results of a study of the isothermal transformation of austenite in a single commercial alloy steel in which a fine-grained or a coarse-grained state was induced by appropriate selection of austenitizing temperature. The data are presented in the form of isothermal transformation diagrams, which clearly show that coarsening the grains lessens the rate of transformation of austenite to proeutectoid ferrite and pearlite-that is, at temperature levels above about 1000°F. (540°C.)-but is without significant effect at lower temperatures where the transformation product is bainite or martensite. It is to be presumed that the foregoing statement would be valid, at least in principle, for many other grades of steel; it confirms again that the mechanism of transformation to a pearlitic structure is fundamentally different from that to an acicular structure. A number of related observations were made, which seem to throw some light on the transformation process as it takes place in alloy steels, particularly at temperature levels in the vicinity of 1000°F. (540°C.), where the transition from lamellar to acicular structures occurs. These data are discussed briefly in the belief that they may lead to a clearer understanding of this aspect of the subject. MATERIAL AND EXPERIMENTAL PROCEDURE The material investigated was a commercial grade of S.A.E. 4140 steel, the composition of which was as follows: 0.37 per cent C, 0.77 per cent Mn, 0.98 per cent Cr and 0.21 per cent M0. It was hot-rolled to a 1 1/8-in. round bar and normalized by air-cooling from 1800°F. (980°C.).

Jan 1, 1941

DAVID THOMAS 1871 R. W. RAYMOND 1872-1874 A. L. HOLLEY 1875 ABRAM S. HEWITT 1876 T. STERRY HUNT 1877 ECKLEY B. COXE 1878-1879 WILLIAM P. SHINN 1880 WILLIAM METCALF 1881 RICHARD P. ROTHWELL 1852 ROBERT W. HUNT 1883 JAMES C. BAYLES 1884-1855 ROBERT H. RICHARDS 1886 THOMAS EGLESTON 1887 WILLIAM B. POTTER 1888 RICHARD PEARCE 1889 ABRAM S. HEWITT 1890 JOHN BIRKINBINE 1891-1892 H. D4. HOWE 1893 JOHN FRITZ 1894 J. D. WEEKS 1895 E. O. SPILSBURY 1896 THOMAS M. DROWN 1897 CHARLES KIRCHHOFF 189S

Jan 1, 1939

By John C. Sawyer

A brief review is given to show that catastrophic oxidation of stainless steel in the presence of lead oxide is similar in many respects to catastrophic oxidation as caused by MoO3 and V2O5, Experimental data are presented to show that lead oxide accelerates the normal oxidation process of stainless steel by chemically altering the normally protective oxide film formed on the base metal. Data are given to show that similar reactions occur during oxidation of stainless steel in the presence of MOO3,and V2O5. THE mechanism by which pure metals oxidize at high temperatures has been the subject of intensive research for many years and much has been accomplished towards understanding the processes involved. The mechanisms by which alloys oxidize have also been investigated, but due partly to the fewer number of investigations and partly to the complexity of the oxide systems present, available knowledge is not as extensive as with pure metals. When oxidation processes are further complicated by atmospheres contaminated with sulfide, halide, or oxide vapors, the knowledge of fundamentals becomes meager or altogether lacking. Thus, it is not surprising to find that the catastrophic oxidation of stainless steels in metal oxide vapors of MOO, and V2O5 is not a well understood phenomenon despite the fact that a number of investigations have been undertaken. The literature in dealing with the subject of catastrophic oxidation is primarily concerned with the effects of MOO3 and V2O5, but does mention that other metal oxide vapors, one of which is lead oxide, appear to promote a similar type of accelerated oxidation. While this latter effect is virtually unknown, the deleterious effect of lead oxide is of considerable commercial importance, as it is believed to be one of the fundamental reasons for exhaust-valve failure in gasoline engines. For this reason studies have been in progress for many years attempting to better understand the mechanism involved. Modern exhaust-valve alloys"2containing 20 to 25 pct Cr plus nickel and/or manganese are in effect high-grade austenitic stainless steels exhibiting ex- cellent oxidation resistance in air at exhaust valve operating temperatures of 1100° to 1700°F; yet these same alloys are prone to corrode during engine service because of the conditions attending their operation. These conditions are such that the valves become coated with deposits of complex lead compounds mainly derived from gasoline additives of tetraethyllead, ethylene dibromide, and ethylene dichloride. Literature searches3-7 and discussions with various investigators show that considerable difference of opinion exists as to the nature of the lead-bearing deposits found on the surface of exhaust valves and the atmospheres to which they are subjected; yet, all seem to generally agree that corrosion, a gradual transformation of alloy to nonmetallic products of corrosion, is a consequence of the presence of lead compounds. This majority opinion seems to be substantiated by laboratory engine tests which show that corrosion does not occur to any appreciable extent when lead-free fuels are used. The first observations of catastrophic oxidation reported in the literature were probably made by pfeil,8 but it was Leslie and Fontana9 who undertook the first detailed study of the phenomenon. Their work was chiefly centered on the acceleration of oxidation which took place when stainless steels containing more than 3 pct Mo were heated in air with restricted circulation. These investigators reported that the presence of other oxides near the surface would further accelerate the rapid oxidation which occurred. While they recognized that the effect was attributable to the presence of molybdenum, it was Rathenau and Meijering" who emphasized the fact that the presence of molybdenum in the alloy was incidental to the presence of MOO3 vapor in the atmosphere surrounding the specimens. Evans,11 as well as Cunningham and Brasunas 12 studied similar

Jan 1, 1962

By H. C. Chao, L. H. Van Vlack

Small MnS inclusions with known crystallographic orientations were placed inside powder compacts of low-carbon steel. After the metal was axially campressed with negligible end friction, the deformstions for the metal and the inclusions were compared. The MnS inclusions deformed more when the [100] direction was aligned with the compression axis than when the [111] direction was parallel to this axis. The deformations of the inclusions in the two principal radial directions were equal for each of the above orientations. Inclusions with [110] compression alignments did not deform with radial symmetry. The relative deformation of the inclusion and metal was closely dependent upon the relatiue hardness of the two phases. The relative deformation of the two phases was not sensitive to the rate of deformation. RECENT studies by the authors1.&apos; suggested that the plastic deformation of MnS in steel would probably be highly sensitive to the orientation of the inclusions and to the temperature of the metal. This paper reports an investigation of these factors upon MnS behavior within steel. Manganese sulfide (MnS) possesses an NaCl-type structure and typically has extensive (l10) {110} slip as a separate (noninclusion) crystal.&apos; A secondary slip system, ( l 10) { l l l}, has also been observed where the major slip system is restricted. In general, MnS inclusions must be rated as a highly deformable second phase.3 The amount of sulfide deformation varies, however, with several composition and processing factors. Some of these have been only partially assigned. For example, it is known that minor amounts (<0.01 pct) of silicon within free-machining steels will increase the amount of MnS deformation,4 but the mechanism of the added deformation can only be surmised at the present. Manganese sulfide and steel have sufficiently comparable deformation characteristics so that slip which is started in steel may be continued through the sulfide inclusions and back into the steel if the crystal orientations are favorable.5 A more detailed discussion of previous work on the plastic deformation of NaC1-type crystals and on the plastic deformation of inclusions within a metal is given in Chao&apos;s work.6 EXPERIMENTAL PROCEDURE The manganese sulfide which was used in this study was prepared by previously described methods.&apos; Single crystals of MnS, both as cleavage cubes and as spheres, were oriented within steel powder compacts so that the desired crystal directions were parallel to the direction of axial compression. A four-stage hydrostatic compaction procedure was used and involved the following steps. In the first stage part of the powder was placed in a metal die 1 in. in diameter with a thick (1 in. OD, 5/8 in. ID) rubber liner which had one end plugged. The steel powder was hand-rammed, making it as dense as possible before placing a carefully sized MnS crystal (either as a sphere or as a cube) near the center. The crystal was oriented with the chosen direction vertical; viz., [001], [011], or [111], with the aid of a X10 microscope. A pair of tungsten wire threads 0.020 in. in diameter was inserted along the side of this (&apos;core compact" to locate the desired plane after the compression tests. After the crystal was positioned in the center of the die, more powder was added and carefully rammed by hand. The die was then capped with a rubber plug of the same hardness and thickness as that of the liner. The whole assembly as shown in Fig. 1 was compacted by a ram load of 54,000 lb (about 70,000 psi). In the second stage a smaller, 3/4-in, rubber-lined die was used to give a stress of approximately 120,000 psi. The above process was repeated with the initial compact serving as a core for a larger compact. The final product after sintering was a cylinder 1 cm long and 1 cm in diameter, having a density of 7.54 g per cu cm. This was close to the theoretical density since the metal contained a non-metallic phase. There was no evidence of MnS deformation during the hydrostatic compaction or subsequent sintering. Elevated-temperature hardness data were obtained by procedures previously described.2 Compression tests for inclusion deformation utilized the cylinders which were described above. The critical problem in these tests was the lubri-

Jan 1, 1965

By J. E. Walstrom

While intensive research continues to promote a more complete understanding of the potential and resistivity measurements that comprise the electric log, it is believed that consideration should also be given to translating these numerous and often widely separated findings into a coordinated and readable body of fundamental facts designed specifically for the petroleum engineer and geologist. Although provision is made through publication for a ready exchange of new theoretical concepts. it is also desirable to provide reviews and appraisals of the more established techniques and methods from the operating standpoint so that an economic and practical application may be realized concurrently with the theoretical progress. With these basic premises as a guide the author reviews the presnt state of electric log interpretation. The paper is directed not so much to the logging or research specialist as to the petroleum engineer and geologist to whom the electric log is only one of the many tools which he employs. Frequently, these persons do not have the time to follow in detail the many specialized contributions that appear and, as a consequence. are not in a position to place these contributions in proper relation to each other, or to the art as a whole. The paper reviews the basic steps in making quantitative determinations from the electric log of the amount of oil or gas present in subsurface formations and also discusses the degree of reliability of these determinations under various conditions. The paper also indicates the trend of future developments in electric logging systems and methods of interpretation. INTRODUCTION The electric log has been used about 20 years as a means for studying the formations penetrated by a well bore. The first half of this period is characterized by the development of suitable logging techniques and equipment. Although progress in this direction is continuing at a satisfactory rate, the last ten years are characterized more by an increasing interest in methods of electric log interpretation. During this period, a large number of fundamental papers have been published, expounding various logging techniques and particular phases of the interpretation problem. Many of these papers represent important contributions, and a few are classic. This paper is an effort to outline as concisely as possible and in simple terms the main course of progress in electric log interpretation. More specifically, it is the purpose of the paper to review the necessary elements and basic steps used in making quantitative determinations of water saturation from the electric log; and to point out the degree of reliability of these determinations under different conditions. It is strongly advised that the operating staffs of the drilling and exploration departments of oil companies cooperate wholeheartedly with both the electric logging service companies and research organizations in the testing and development of new logging systems and interpretation methods. One purpose of the paper is. however, to indicate the degree of caution which must be exercised in placing confidence in new techniques and interpretation methods that have not been thoroughly tested in the field. It is entirely possible to be cooperative in trying new methods and yet reluctant to believe in the results until the methods are firmly established. It is important to define the meaning of quantitative electric log interpretation. In the most general sense, an interpretation of the log has been made when the electrical characteristics of the formations, as portrayed on the log, have been translated into terms describing the formation geometry, rock type, or any other physical characteristics of the formations. The determination that the top of a sand is at a certain depth is an interpretation of the log. Structural determinations made by correlating electric logs from a given area are also interpretations of the logs. The term quantitative interpretation, however, will be used in this paper in the restricted sense to indicate the determination of the water saturation of a formation. This determination defines the fluid content of an oil and gas productive formation only if the porosity is known, and it assumes that the remainder of the pore space contains hydrocarbons. This assumption is believed to be true for most oil and gas productive formations. The quantitative electric log interpretation may he said to be a determination of the fluid content only to the extent which the water saturation, under the conditions given above. defines it. THE BASIC STEPS The fundamental steps in calculating water saturation from the electric log are: 1. Determination of the true resistivity of the formations from the apparent resistivities as recorded on the electric log.

Jan 1, 1952

Discussion of the paper of EZEQUIEL ORDOÑEZ, presented at the Pittsburgh meeting, October, 19.14, and printed in Bulletin No. 94, October, 1914, pp. 2531 to 2536. DAVID T. DAY, Washington, D. C.-Dr. Ordoñez is really the pioneer in the study of the occurrence of Mexican oil. His studies came at such an early time as to prove really prophetic. He was successful in pointing out the relationship of these oil deposits to the volcanic teeth which are so very characteristic as a geological feature in the coastal plain of Mexico. At that time only the first wells around Ebano had been drilled, and drilled under the direction of Dr. Ordoñez himself. Only these Ebano wells were available for a real study of the condition of the occurrence of oil, the other large gushers not then being known. From that time on, the study of the geology of the country has, in large measure, been able to keep up with the oil development. As usual, a great deal of haphazard work in the exploration of the oil fields has been carried on. The results have been good, bad, and indifferent. We know a great deal more about the distribution of oil in Mexico than we do about the geology of it. Two ideas have become prevalent in regard to the Mexican oil, due to the peculiar development there: (1) That oil is omnipresent over a tremendous area bounded by De Soto La Marina, in the province of Tamaulipas, on the north, to south of Tuxpam in Veracruz; and (2) that there are very few spots in all this region which have rich gushers. The truth is somewhere between the two. The amount of land taken up, chiefly by three or four large companies, is extremely great, and covers all the possible chances. The idea that oil is going to be discovered in a large percentage of the land taken up by the oil companies, seems to me entirely unjustified. The amount of oil that will be produced from comparatively small spots here and there over that territory and other territory, undoubtedly will be very great. I do not think there is any hope of multiplying the capacity of these large gushers by the area of that part of Mexico in which they are contained, as a, large number of promoters are inclined to do.

Jan 4, 1915

By Richard J. Borg

The vapor pressure of Cd in equilibrium with CdSb in the presence of excess Sb has been measured using the Knudsen effusion method over the temperature range 276° to 379°C. The free energy of formation of CdSb is given by AF° = -1.58 + 1.53 x l0-4 T, kcal per mole. The enthalpy and entropy are obtained from the temperature coefficient of the .free energy. CADMIUM and antimony have almost imperceptible mutual solid solubility but form a single stable intermediate phase, CdSb. This phase, according to Han-sen,l extends from about 49.5 at. pct to 50 at. pct Cd at 300°C and has the orthorhombic structure. The free energy of formation of CdSb can be calculated from the vapor pressure of Cd for compositions which contain less than 49 at. pct Cd. The appropriate reaction and formulae are given by Eqs. [I] and [2]- CdSb(s, ~ Cd(g)-, +Sb(s) [1] Since Sb is in its standard state, Af - N,,AF&apos;-,, = NcdRT In a,, = NcdRT InP/PO [2] In Eq. [2], P, is the vapor pressure of Cd in equilibrium with the alloy, and Po is the vapor pressure in equilibrium with pure solid Cd. It is implicit in this calculation that the free energy only slightly changes within the narrow limits of the single phase field. Thus, the value obtained from the antimony-rich boundary is truly representative of the stoi-chiometric compound. The results reported herein are obtained from a mixture near the eutectic composition, i.e. 59 at. pct Sb. Only two previous investigations" of the free energy of formation of CdSb have been made. Both relied upon the electromotive force method, and measurements were made over relatively narrow temperature ranges which strongly influences the reliability of the values of AH and aS. EXPERIMENTAL The eutectic composition is prepared by fusing reagent grade Cd and Sb by induction heating in vacuo with the starting materials held in a graphite crucible having a threaded lid. The material obtained from the initial melt is pulverized, sealed under high vacuum in a pyrex capsule, and annealed at 420°C for two weeks. X-ray analysis"gives the following lattize parameters: a = 6.436A, b = 8.230& and c = 8.498A using Cu Ka radiation with A = 1.54056. These values are in fair agreement with the result? previously reported by Al~in:4 i.e. a = 6.471A, b = 8.253A, and c = 8.526A. Vapor pressures are measured using an apparatus which has been described elsewhere,= however, with a single important modification. Knudsen effusion cells are made of pyrex with knife-edged orifices made by grinding the convex surface of the lid on #600 emery paper. Photographs taken at known magnifications using a Leitz metallograph enable the determination of the orifice area. Numerous calibration measurements of the vapor pressure of pure Cd give close agreement with values previously reported5,= thus indicating that no significant error can be ascribed to the substitution of glass cells for metal cells used in previous work. Because the vapor pressure of Cd is reliably established and because it is difficult to obtain Clausing factors for the glass cells, the final values used for the orifice areas are calculated from the calibration measurements of the vapor pressure of pure Cd. Effusion runs are started in an atmosphere of purified helium which is quickly evacuated as soon as the cell attains thermal equilibrium. Less than one minute is necessary to obtain high vacuum after evacuation begins, and the temperature seldom varies by more than 0.5oC from the value obtained prior to pumping out the helium. RESULTS The results of this investigation along with other pertinent data are tabulated in Table I. Fig. 2 is the familiar graph of log P against T-10 K. At least mean squares analysis of the data presented in Table I yields the following equation: log1DJP = 8.790 - 6472 x T"1 [3] The deviations of the individual measurements from the values calculated with Eq. 131 are given in column six of Table I; the average deviation is 4.0% of the calculated value. Although the partial molal properties change significantly with composition within the single phase region, the integral thermodynamic value should remain relatively constant. Hence the results of the following calculations, which use the data obtained for the eutectic composition, are probably representative of the equi-atomic compound. Eq. [4] describes the vapor pressure of pure Cd as a function of temperature and may be combined with Eq. [3] to

Jan 1, 1962

By E. H. Bronson

PROPERTY of Malartic Gold Fields Ltd. is situa-ated in the great clay belt in the northern part of the Province of Quebec. This belt represents the floor of the glacial lake Barlow-Ojibway. The clay blanket has a gently rolling, almost flat surface, with here and there projecting knobs and ridges that outline the large irregularities of the surface on which the clay was deposited. At irregular intervals glacial eskers dominate the landscape. The ore-bearing country rock is covered by strata of clay, sand, and silt to a depth varying to 40 ft. There are serious structural problems when it is necessary to place loads of unequal intensities on this surface to support buildings and machinery for a modern mining plant. Earlier mining companies and their engineers paid little attention to the science of soil mechanics, partly because they believed it unnecessary and partly because they knew little of the subject. The results are evident in some of the tottering structures in older camps. Careful analysis of soil problems is well worth-while, since cost of foundations may vary from 20 to 50 pct of the final cost of a structure. Low operating and maintenance costs can be achieved only in this way. If it is definitely established that a plant will be in operation for only a few months, this limited time factor will probably influence the design of the foundation, and rightly so. If sensitive and complickted equipment is to be mounted on these foundations and the plant is to operate for several years, there should be a thorough study of foundations and a very careful design. A familiar problem is presented by the difficulty of operating a permanent plant originally designed for a few months&apos; work. The engineer must beware of these hazards and disassociate himself from them if he cannot prevail on the promoter to spend the proper amount for a thorough foundation study. Laws of certain provinces and states hold the engineer equally responsible with the contractor for any &apos;damage that may be caused to building through inadequate study-ignordnce of the facts is no excuse in the eyes of the law. Types of Soil: The engineer should be familiar with such terms as silt, clay, peat, and varved clay, as well as perpafrost, especially if he is to work in the far northern reaches of the country. He should also be familiar with soil attributes such as porosity, texture, consistency, permeability, compressibility, consolidation, and shearing resistance. The design of any foundation requires an accurate knowledge of the physical properties and location of the soils involved. Older textbooks on the subject outline various empirical methods to determine the carrying power of soil. Tables are given in reference books. The modern ehgineer should be wary of these modes of thinking. He should analyze his problem carefully, calculate to what depth of soil the loads may be transmitted, and then check the bearing value of all soils to that or greater depths. If the strata are water-carrying, he must determine the possibility of this water being accidentally re-

Jan 1, 1958

By H. L. Hazen

THIS is the story of the recent operations of the Standard Cyaniding Co., which owns the Standard mine, a low-grade gold property in sight of Highway 40 about thirty miles from Lovelock toward Winnemucca, Nev. The ore is mined by power shovel and cyanided after grinding to only 3/S in. A total direct cost of $1.24 was attained in 1941 on 600 tons a day. Mining operations ceased, under Government edict, in 1942, and only in recent months have been resumed. The operating difficulties of today are: (1) the high cost of supplies; (2) labor problems; and (3) Federal laws as interpreted and enforced by executive bureaus of the Government. Of these, the increased cost of supplies is the least important.

Jan 1, 1947