By Taner Kavas

The refractory bricks of a rotary cement furnace containing of alumina and magnesium chromite were studied in order to determine whether they could be used in the concrete production as aggregates. Three mortars were prepared by mixing 1 part cement, 3 part aggregate materials, 0.5 part water by weight and mechanical, chemical, thermomechanical and microstructural characteristics were evaluated. The compressive and bending strength of samples were determined after 2 and 28 days curing. Resistance to chemicals were established by calculating the weight gain of mortars stored in 2 % HCl solution for 1 h and 24 h. Thermomechanical characteristics were determined by measuring the compressive strength of heat treated specimens at temperatures of 400 °C, 600 °C and 800 °C. Consequently, magnesium chromite containing waste brick aggregates have given the best results.

Jan 1, 2006

By Xi Yun Yang

Ultrafine (0.1µm) spherical magnetite powder was prepared successfully by hydrothermal reaction of ferrous sulfate and sodium hydroxide with activated pyrite as reducing agent in the temperature range 120-140?. XRD and XPS analyses indicate that pH value and pyrite amount have a direct influence on the composition of the product. Stoichiometric Fe3O4 can be obtained only when pH value is 12 and the molar ratio of pyrite/ferrous sulfate is 1:1.8. The hysteresis loop of Fe3O4 shows a ferromagnetic behavior with a saturation magnetization of 75.2 emu/g and a coercivity of 152Oe.

Jan 1, 2006

By Dachun Liu, Wenlong Jiang, Baoqiang Xu, Yongnian Dai, Bin Yang

"In the traditional method for refining of indium, glycerin-KI and glycerin-NH4Cl are used as electrolytes to remove Cd and Tl by electrolytic refining, which produces In with a purity of 99.995%. Large quantities of polluted industrial waste water are the result. It is calculated that the saturated vapor pressure of Cd and Tl are between 1-200 Pa, which is much larger than the vapor pressure of In. Thus, the study of removing Cd and Tl was carried out over the temperature range between 700-950 °C and pressures between 1-15 Pa. After vacuum distillation the contents of Cd and Tl in crude indium could sharply fall below 1 ppm..IntroductionIndium is a is a pale blue and silver white metal, and has high ductility [1-2]. Pure indium is generally used as a raw material to produce semiconductor compounds, fluorescent material and ITO targets [3]. Sublimation, zone melting and electrolytic refining are major methods to produce pure indium from crude indium. Electrolytic refining is the main method to product pure indium at present. High productive efficiency, simplicity of operation and short cycle of production are major advantages. However, glycerin-KI and glycerin-NH4Cl are used to remove Cd and Tl in electrolysis method. Large quantities of polluted industrial waste water are the result[4]."

Jan 1, 2012

By Ross McClelland

This paper provides a technical overview on the installation and commissioning of the Ausmelt lead smelting, slag reduction and slag cleaning operations at the HZL Chanderiya site in India. It also discusses theoretical concepts behind the process practices currently in place at HZL.

Jan 1, 2006

By Naiyang Ma

"High oil concentration is one of the major barriers for recycling of mill scale of steel hot rolling mills. It is of vital importance to find cost-effective technologies of reducing oil concentration in mill scale in order to recycle the mill scale without causing detrimental effects on production and environment. This paper discusses in-process separation of mill scale from oil at steel hot rolling mills. Formation of mill scale and status of oily wastewater at hot rolling mills are reviewed in the first place. A mathematical model is then formulated to relate oil concentration in mill scale to physical properties of mill scale, chemical and physical properties of wastewater and interacting parameters between mill scale particles and wastewater. From this model, three approaches of in-process separation of mill scale from oil are derived: (1) avoiding contacts between mill scale particles and oily wastewater, and (2) maintaining low oil concentration in wastewater, and (3) collecting mill scale in upper streams of wastewater flows. In-process separation of mill scale from oil might have advantages of lower capital cost, lower operating cost and less additional environmental concerns, compared to other strategies of separating mill scale from oil.IntroductionHot rolling is an inevitable step in producing finished steel products. Figure 1 schematically shows a steel hot rolling process. Semi-finished steel products, slabs here, are reheated first, and then the reheated slabs are discharged from the furnaces and transported on hot rolling trains to descaling units for removing scale with pressurized water. After being descaled, the slabs are rolled by roughing mills. After treated with cropping and the second descaling, the slabs are finally rolled into finished products, coils here, by finishing mills."

Jan 1, 2012

By Jian Wang, Hongyang Cao, Binxiu Wu, Junhong Li, Jimin Wang

"The enrichment and separation of scattered metal indium component in the pressure leaching solution with sulfuric acid from vacuum furnace germanium slag were studied by iron substitute and P204 extraction, which is supplied by shaoguan smelter. The experimental results show that the extracting power of P204 for indium from pressure leach solution is powerful. The optimal technological condition were the ratio of P204 and sulphonating serosene 3:7, phase ratio 1:3, solution pH 1.2, and extracting 5 minute. The enrichment indium solution of 21.7 g/L In at 95.2% recovery ratio was obtained by three-stage counter flow extraction and four- stage counter flow stripping.IntroductionScattered metals, such as Indium and germanium, were inriched as intermediate product or by-product during the metallurgy process of other non-ferrous metals, such as lead, zinc, copper and tin. For example, the indium and germanium were inriched in vacuum furnace germanium slag, which is the by-product of zinc vacuum distillation operation from hard zinc. It is difficult to recovery the indium from the vacuum furnace germanium slag, because the indium content is low, and the chemical composition and phase compositon were complex.Recovery indium from bearing indium zinc slag was researched extensively, such as pressure acid leaching, high temperature evaporation, solvent extraction method[l-7], acid leaching method has the advantages of high leaching rate, which can be separated hydrochloric acid, sulfuric acid and silicon fluoride acid systems. Solvent extraction method has the advantages of low production cost, fast reaction speed, high enrichment ratio, and simple operation."

Jan 1, 2013

By A. Dell’Era, M. Pasquali, C. Lupi

"An electrochemical cell has been designed to treat very diluted cobalt solutions, i.e. those deriving from recycling processes of lithium-ion batteries. A reticulated vitreous carbon sponge was used as cathode and a Pt-coated Ti net as anode. A controlled potential electrolysis has been carried out in a solution flowing in the cell and maintained at a constant pH of 6.5. Considering the cathode dimensions (10.0 cm * 10.0 cm * 1.25 cm), rather high volumes of solution (>1 litre) can be treated with flow rates up to 1.6 l/min. The process yield is obviously related to the solution concentration; it has been observed that, starting with a solution containing 200 ppm of Co2+, the yield is initially ~35-40%, but it decreases to ~20% when 80% of the initial cobalt content has been electrowon. The yield increases up to ~50% if the carbon electrode is coated by cobalt. The conditions allowing a fast and complete removal of cobalt are outlined. Introduction Industrial liquid effluents containing heavy metal ions arise not only during hydrometallurgical processing, but also in many sector of chemical industries utilizing metal catalysts and process reagents. These waste solutions containing low quantities of metallic ions can be treated by chemical precipitation, solvent extraction, ion exchange, etc. before final discharge. All these techniques could be efficient for complying the aqueous effluents with the severe rules related to the environmental impact, but they can not directly produce metals. Particularly the chemical precipitation presents two main drawbacks, huge amount of sludge prodction and reagent costs to produce this useless and sometime dangerous sludge that have to be considered. Electrochemical technologies can be used for the treatment of effluents polluted by metal ions, showing the following advantages in comparison with other processes: 1. recovering of the polluting substances in metallic forms, with subsequent reusing; 2. absence of process slag, which should be subsequently disposed of. In this work an electrochemical reactor with a reticulated vitreous carbon cathode and a platinated titanium net anode has been designed and utilized for removal Co from waste aqueous solutions. Porous materials have been used as electrodes for this cell, as their high specific surface area favours the treatment of these low metal content solutions (1-7). This kind of electrodic material presents very interesting chemical-physical characteristics such as: low density, low thermal expansion and high electrical and thermal conductivities; particularly the reticulated vitreous carbon (RVC) presents a very elevated void volume, rigid structure, good resistance to temperatures in non-oxidizing environments and very low resistance to fluid flow."

Jan 1, 2008

By K. Takahashi, G. Dodbiba, T. Fujita, N. Sato, S. Matsuo, K. Okaya

Different materials are used for manufacturing various parts of a cellular phone. Considering that a great number of mobile phones are being discarded every year, it is important to recover these materials and then recycle them in order to save resources. The primary objective of this work is therefore to find and suggest ways on how to recover various materials from discarded cellular phones for recycling. Much effort, for example, has been put in recovering and recycling tin oxide (ITO), a mixture of indium (III) oxide, (UI2O3) and tin(IV) oxide from the discarded liquid crystal displays (LCDs). Here we report a simple and cost-effective process, which includes a HC1 treatment process for altering the structure of the indium (III) compound into a chlorideinduced indium compound, in order to facilitate the vaporization of indium at a relatively low temperature. The experimental results indicated that 96.2 % of indium can be recovered from ITO, when the sample was heated at 973 K for 90 minutes. In addition, some thermodynamic calculations were also carried out in order to better understand the mechanism for chlorideinduced vaporization of indium.

Jan 1, 2011

By Jiechao Liu, Lijian Luo, Yubao Ma, Bo Zhang, Yanfeng Yang, Xin Hong, Luming Liu, Jienan Liu

Reduction kinetics of stainless steel slag in iron bath smelting reduction was studied at the temperature of 1500℃ ~ 1650℃. It was concluded that the reduction process consisted of two parts. That is to say smelting reduction was controlled by stainless steel slag melting initially and by interface reaction later. In order to increase smelting reaction rate, the melting point of slag should be decreased at the first stage and adjust the liquidity of slag at later stage. Smelting reaction rate will be accelerated by means of optimize the slag content. The optimal reduction result that all most all of the chromium in slag been recovered was obtained in temperature was 1500℃, basicity of slag was 1.0~1.2, the value of Al2O3+MgO was 25%.

Jan 1, 2015

By Jenq-Gong Duh, Jyh-Wei Lee

"Hard chromizing process is a method for developing a surface modified coating providing wear, corrosion resistance and high temperature surface protection. Two carbon steels with 0.45 wt% and 0.95 wt% carbon contents, respectively, were chromized with pack cementation process at 950'C for 4 and 9 hours, respectively. The phase transformation and microstructure phenomena of chromized coating layer and matrix of two steels were studied with X-ray diffractometer and electron probe microanalyzer. (Cr,Fe)23C6 and (Cr,Fe)7C3 carbides and (Cr,Fe)2N1-x nitride phases were observed on the chromized surfaces. The thickness of chromized layers obeyed the parabolic rate law. The mechanism and diffusional kinetics of the chromizing process were proposed. The diffusivity of chromium in the (Cr,Fe)7C3 carbide phase was calculated using the moving boundary method.IntroductionChromizing process is one of the surface treatment technologies that can produce a chromium contained surface layer with sufficient corrosion and wear resistance on the steel matrix [1-7]. The relatively low cost and no ""line-of-sight"" restrictions are main advantages of chromizing. Adequate bonding strength of these coatings to the substrate was reported [7]. Chromizing process can be classified into soft chromizing and hard chromizing [2]. Soft chromizing is applied to steels containing less than 0.1wt% carbon through which chromium will be diffused. High temperature oxidation resistance improvement is the main purpose of soft chromizing process. On the contrary, the hard chromizing can be applied to steel containing more than 0.3wt% carbon, and very hard chromium nitride and carbide layers will be formed on the surface, which are very resistant to wear, corrosion and temperature [5-7]. In the previous studies on the Fe-Mn-Al-Cr alloy [5,7] and carbon steels [6], the thickness (X) of chromizing layers was analyzed and found the parabolic rate Jaw prevailed:"

Jan 1, 2004

By C. Liliane Carvalho

In the current study, bio-oxidation tests were carried out in shaking flasks with a flotation concentrate containing the sulphides pyrite, arsenopyrite and gudmidite. The tests were performed with mesophilic microorganisms (At. ferrooxidans) at 30 °C and also with the moderate thermophile S. thermosulfidooxidans, at 50 °C. The effects of (i) previous adaptation of the microorganisms to the concentrate, (ii) ferrous iron concentration and (iii) pulp density (2%, 4% and 6% (w/v)) on the dissolution of the sulphide were studied through arsenic extractions. S. thermosulfidooxidans was more sensitive to the pulp density in comparison to At. ferrooxidans as a reduction in sulphide oxidation was observed with the increase in the solid content to 6%. Therefore, the mesophilic strain was selected for further work, which comprised a rolling bottle experiment at 10% solids. After 40 days of bio-oxidation, the solid material was subjected to cyanidation, which revealed 85% gold extraction as compared to 21% from the original concentrate. The antimony sulphide grains in the bio-oxidized product showed similarity to what was observed in the original sample, suggesting such particles were not susceptible to the bio-oxidation process.

By Hector M. Henao

There is an increasing trend in the copper smelters to recycle electronic materials, which contain relatively high concentration of precious metals. As a consequence, the amount of precious metals lost in the slag phase is increasing. To determine the portion of the precious metals chemically dissolved and that associated with the mechanically trapped matte in the slag will be a key factor to improve the recovery of those metals. Thus, an experimental study was carried out to determine the distribution of precious metals (Au, Pt, Pd, Rh, Ru) between the equilibrated copper matte and iron-silicate slag phases. The experiments were made in a magnesia crucible at 1573 K and a fixed partial pressure of SO2 of 0.1 atm for the matte grades between 40 and 70 mass% of copper. It was found that the distribution ratios (defined as mass% X in slag/mass% X in matte, where X represents the precious metal) are around 10-2 for Ru, 10-3 for Au, Pt and Pd and 10-4 for Rh. The distribution ratios show a tendency to increase when the grade of matte is increased.

Jan 1, 2006

By Jian-Xun Fu, Hong-Qiang Liu, Si-Yu Liu

The production of zinc-bearing solid dust is up to 4%~8% of total crude steel in steel plant, which is difficult to be recycled in traditional methods. To fully utilize the resources and reduce environmental pollutions, Chinese steel plants are using rotary hearth furnace (RHF) process to recycle solid dust. A consequential life-cycle inventory was carried out to assess the impact of dust recovery on greenhouse gas emissions based on the local production status. In the study system, the selected steel plant named which have 10.5 million tons of Crude steel productivity and 0.48 million tons solid dust come out meanwhile. To research, a RHF production line of 0.3 million tons directly reduced iron (DRI) a year was established to recycle the solid dust. The DRI will be obtained from RHF and sent to the blast furnace as raw materials to reduce the demand for iron ore and coke in steelmaking processes. By researching on the life-cycle inventory in the system, the steelmaking process with RHF was 2299.3kgCO2/ton steel. It’s a little higher while compared with the process without RHF, which data is 2297.0 kgCO2/ton steel. The small production of DRI make a small difference to reduce the carbon footprint of steelmaking process, the added carbon footprint of RHF process is more than BF and other steelmaking processes reduced. It is concluded that dust recovery has no contribution to the greenhouse gas emission reductions in the technic condition of Chinese steel plants currently.

Jan 1, 2016

By Leonard J. Friedman

Modern smelting systems using continuous, flash and/or oxygen smelting processes have a significant effect on the choice of sulfur dioxide control processes and system arrangements. Based on gases from an enriched air or oxygen smelting furnace and copper converters the paper reviews and analyzes alternate processes and system arrangements for recovery of sulfur dioxide. The work indicates the choice system to include a conventional sulfuric acid plant for converter gas and a liquid SO2 plant to handle the high strength smelting fur¬nace gas. The liquid SO2 plant would be used as a fly-wheel to damper the flow and SO2 concentration variations of the con-verter acid plant. Potential energy recovery alternates and product flexibility are also reviewed.

Jan 1, 1983

By Yeliz Demiraya, Onuralp Yucelb

"Production of strontium metal from its oxide was studied under the pressure of 1-5 mbar by methalothermic process. SrO with 99 % purity was used in the experiments. Effects of Al powder addition (100, 200, 300 % of stoichiometric ratio) and time were investigated on recovering of metallic strontium. Effects of BaO addition (100 %, 200 %, 300 %) was also investigated. The final residues were examined for their chemical composition. XRD, AAS and Flame Photometer were used for chemical analysis. More than 96 % of strontium metal recovery can be obtained.IntroductionStrontium is an element which is used in many advanced technology applications. Barium strontium titanat, strontium bismuth titanat, and strontium bismuth tantalat thin films are promising materials in ferroelectric and Schottky-based microelectronics technologies, especially for memory applications. Physical vapor deposition (PVD) techniques as magnetron sputtering, thermal evaporation and molecular beam epitaxy (MBE) are the most widely used methods for growth of these thin films [1-3]. In these techniques high-purity of Sr metal is used as evaporation sources and sputtering targets. Furthermore, metallic strontium is used as a ""getter"" in electron tubes, and as an alloying elements in aluminum alloys [4].The most used Sr compound is SrCO3 and widespread process used in production of SrCO3 is the hydrometallurgical carbonation of celestite. Although there are considerable amount of Selestite reserves, SrCO3 and strontinum metal are not being produced in Turkey, yet [5].Concentrated celestite (SrSO4) is conversed to SrCO3 in carbonate media. Black ash and direct conversion processes are currently used methods. There are many satisfactory studies about hydrometallurgical carbonation of celestite and decomposition of SrCO3 [6, 7]. Since strontium metal is produced from it’s oxide (SrO), SrCO3 needs to be decomposed to SrO."

Jan 1, 2011

By Thenepalli Thriveni, Ch. Ramakrishna, Yujin Jegal, Ji Whan Ahn, Jyothi Rajesh Kumar

In alumina production or alumina refining, bauxite is converted to alumina (aluminium oxide) The rare-earth elements (REEs) are a group of 17 chemically similar metallic elements (15 lanthanides, including scandium and yttrium). Rare earth elements play a key role in many industrial applications, petroleum refining, clean energy, automobile, electronics, and defense applications. These rare earths are essential to the success of green technologies. China today controls more than 95 percent of the rare-earth supplies and nearly all rare-earth refining and after 2009 year rare earths crisis raises due to China’s export restrictions and growing internal demand for rare earth elements. The extraction of gallium and yttrium from Korean red mud (KC red mud) by selective acid leaching was explored. The recovery of gallium and yttrium from a leach solution of the Korean red mud using solvent extraction was studied. A number of extractants were investigated for the extraction of those mentioned two rare earth elements and also we proposed a flow sheet of rare earth elements respectively. The toxic heavy metals presented in KC red mud were removed by CO2 stabilization.

Jan 1, 2015

By M. Mujahid, A. Maqsood, M. H. Asghar, K Iqbal

"Thin film multilayer anti-reflection coatings (Si02/Si/Si02) having thicknesses 286/571/143nm were deposited by RF magnetron sputtering deposition technique on 0.5mm thick Si(100)-substrates. Post-deposition annealing is also carried out in the temperature range 150-650°C for 4hr at the rate of 10°C /min. Si Optical window was designed at 4.21lm wavelengths and correlated with modeling software. The films are transparent in the 3-51lffi band of the electromagnetic spectrum, firmly adhered to the substrate. The prepared multilayer thin films are characterized optically and structurally using a spectrophotometer, an atomic force microscope, x-ray diffraction and a scanning electron microscope. Optical and structural characterizations show that the %transmittance is between 60% and 75%, no appreciable change in crystal structure and roughness of coatings vary between 9 and 25 nm when annealed in the temperature range of 150-650oC. Local elemental characterization on the surface of the thin film was carried out using energy dispersive spectroscopy. The quantitative result of energy dispersive spectroscopy has also shown that the ratio of Si to 0 on the film is 0.67: 1.IntroductionSi02 thin films have unique properties in the interfaces with Si and most studied materials in the field of microelectronics and optical devices [1]. Multilayer thin films are using nowadays in the design and fabrication of the shrinking systems with a variety of fields such as optoelectronic devices. The physical properties and parameters can be controlled at scales of microns down to nanometers by using RF magnetron sputtering system [2].Silicon and Silicon dioxide are used as coating materials [3]. These thin films are laid on top of each other in SiO2/Si/Si02 order by RF magnetron sputtering on top of a substrate as given in Table 1."

Jan 1, 2012

By Carlos Eduardo Gomes de Souza, Luis G. S. Sobral, Paulo A. Medeiros da Silva, Selma G. F. Leite, Renata de B. Lima

"The use of mixed cultures of acidophilus microorganisms that act in different temperature ranges, aims at speeding up the digestion of chalcopyrite, highly refractory sulphide mineral, the major mineral in the flotation concentrate of Caraíba Mining Co., with an attractive processing cost. The concentrate under consideration contains mainly chalcopyrite (CuFeS2) and bornite (Cu5FeS4) with contents of, approximately, 70 and 30%, respectively. It was observed in this study, the performance of consortium of mesophiles, moderate and extreme thermophile microorganisms, in the oxidation of the aforementioned sulphides minerals, evaluating operational parameters such as pH of the leaching solution, the reaction temperature and redox potential, with consequent extraction of 80% of the concentrate copper content within 60 days of bioleaching. Such high copper extraction was achieved in column bioleaching tests.INTRODUCTIONThe solubilization of metals by the application of microorganisms from the mineral ores and the subsequent recovery of metals from solution are referred to as bioleaching (Rohwerder, T et al, 2003). This is an economical method for the recovery of metals from minerals; especially lowgrade ores, overburden, and waste from current mining operations which requires moderate capital investment with operating cost (Watling, 2006).Furthermore, bioleaching is generally more environmentally friendly than conventional metal recovery processes such as concentration and smelting. Those physicochemical metal extraction processes generate sulphur dioxide, a toxic emission that is increasingly the target of regulatory legislation (Stott et al., 2000; Olson et al., 2003). Bioleaching of chalcopyrite is the key industry target. The main problem hindering commercial application of chalcopyrite bioleaching is the slow dissolution rate (Fu et al, 2008).Dissolution of acid-soluble sulphide minerals such as sphalerite, and to a lesser extent chalcopyrite, occurs by a combination of ferric iron and proton attack via the polysulphide pathway (Rohwerder et al., 2003)."

Jan 1, 2008

By Laurence G. Dyer, David G. Dixon, John Rumball, Maziar Eghbalnia, Edouard Asselin

"Linear scan voltarnmetry was used to determine the reactions that occur during the cyanidation of petzite (Ag3AuTe2). Gold oxidation in petzite requires more oxidising conditions than are required for pure gold, it also does not achieve the same current (related to reaction rate). Tellurium oxidation occurs at a similar potential in water and cyanide, but as a component of petzite is impeded somewhat in water, likely due to the stability of the precious metals. Pre-treatment of petzite to oxidise tellurium in the absence of cyanide prior to gold recovery appears to be at least moderately successful.IntroductionWhile gold occurs most prevalently in its native form, many other gold bearing phases appear throughout natural systems [I]. Tellurides are a common group of such minerals, many of which also contain silver, often existing in association with native gold deposits. The six major gold-bearing tellurides are calaverite (AuTe2), sylvanite [(Au, Ag)2Te4], montbrayite [(AuSb)zTe3], krennerite [(Au1-x, Ag,)Te2], petzite (Ag3AuTe2) and muthmannite (AuAgTe2) [2]. While several other phases exist they are much more complex (i .e. buckhornite), which dilutes and confuses the influence of each specific component. Studies of gold tellurides have predominantly focussed on calaverite as it is the simplest and most common phase, however petzite, commonly found in Australia and North America, is the focus of this investigation.Gold processing via cyanidation has been operated for more than a century and is a highly effective hydrometallurgical treatment of native gold deposits. However, some gold alloys such as tellurides have proven to be somewhat less responsive under the same conditions. Several groups have shown that gold/silver tellurides are amenable to cyanidation, but are significantly more refractory than native gold [3]. Pre-oxidation steps have been tested to remove constituents that would consume cyanide such as sulfides. Such species are also linked to the precipitation of oxidised telluriwn, forming a passive layer, further inhibiting gold recovery [2]. It is uncertain to the definite reasons underpinning the refractory nature of precious metal tellurides in conventional cyanidation."

Jan 1, 2012

By Kouji Mimura, Tamas Kekesi, Yongfu Zhu, Masahito Uchikoshi, Minoru Isshiki

"The formation and anion exchange sorption of chloro complex ions can offer a great potential to be utilized for the separation and purification of metals in aqueous solutions. Available stability data were primarily used to estimate the predominance of chloro complex species, indicating the feasibility of such separations. Anion-exchange sorption functions, describing the equilibrium distribution of a number of important elements have been determined by the batch equilibrating method in the practical HC1 concentration range. Various oxidation states were stabilized by the addition of appropriate agents. Tendencies in oxidation, complex formation and anion exchange sorption were confirmed by spectrophotometric investigations. Based on the fundamental results, anion exchange processes have been developed for the purification of iron, cobalt, copper and zinc. The efficiency of separation was assessed and the procedure optimized by the analysis of experimental elution curves. Results have demonstrated that by properly controlling the oxidation states and HC1 concentrations, practically all the impurities can be eliminated. Computer programs have been developed to estimate complex formation and redox equilibria, to screen and correct analytical data, to determine distribution coefficients and to evaluate efficiencies of separation.IntroductionBase transition metals have long been used as the staple materials in various fields of industry. In general, there has been an increasing tendency in purity requirements but recent advances have created a rapidly increasing demand for ultra-high purity metals. To give a few examples, ultra high purity copper can be used as bonding wire and interconnection in integrated circuits, or as material for superconductor stabilizing, high-field magnets, beside its use in cryogenics and ultra high vacuum technology [1]. Iron holds promises as a constituent element in the ß-FeSi2 material to be applied in new opto-electronic devices [2] and it is currently used, together with chromium and manganese, in the production of special magneto-optical materials for digital recording. The use of ultra high purity manganese and chromium in semiconductor technology is evolving. Although not considered a transition metal, zinc is also treated here because of the major significance in compound ZnSe semiconductors [3], and the possibility to purify it by the anion exchange method."

Jan 1, 2000