By F. C. Langenberg

IT is the purpose of this paper to present a limited amount of experimental data obtained on the Charpy impact machine. Several concrete examples will be given showing the relation existing between the results obtained upon the Charpy impact machine and the behavior of the parts tested when in service. Although it is pointed out by G. Charpy and A. Cornu-Thenard1 that it is first necessary to determine a satisfactory working process before studying the correlation between the results of these tests and the behavior of the parts tested in service, this ideal course cannot be strictly adhered to. If a certain part repeatedly fails in service and the available tests give no indication of its cause, advantage must be taken of any possible means that will solve the problem; therefore, even though the reliability of the results obtained by the Charpy impact machine have been questioned by many, it was necessary to use this instrument without giving careful consideration to its possible sources of error. It would seem that the conclusions arrived at by Charpy and Cornu-Thénard justify the assumption that the precision obtained by this machine is comparable to that obtained by, the other more common forms of testing. The second general conclusion arrived at by them, namely, that the impact test upon notching does not offer any direct correlation to the ordinary tests, is also borne out by many hundred determinations made in the laboratories at Watertown Arsenal. This statement, however, should be qualified as follows: Other ordinary tests include the static tensile test from bars taken in a longitudinal .direction and the Brinell hardness. The author agrees that no law is yet known for the computation of the energy absorbed in the rupture of bars of the same material but of different dimensions. Although Charpy and Cornu-Thénard do not refer in their valuable article to the use of the Charpy machine in industrial practice, it should be stated that this instrument has been in constant use in the laboratory at Watertown Arsenal for several

Jan 8, 1919

By J. W. Dougherty, J. M. Douglas

THE Hollinger gold mine is in the Porcupine mining division, District of Cochrane, in the northern part of the Province of Ontario. The adjacent town of Timmins, with a population of 25,119, lies 490 miles by railway north of the city of Toronto. GEOLOGY The property is situated on the northwest limb of a major syncline, which pitches northeast at approximately 50°. The principal rocks of the Hollinger area are of pre-Cambrian age and consist of altered, schistose, Keewatin lava flows intruded by stocks of schistose, quartzfeldspar porphyry generally assigned to the Algoman period. The structure of the Keewatin series is extremely complex as a result of close folding and some faulting. The schistosity, trending north 70° east and dipping steeply to the southeast, is most highly developed along a subsidiary anticline in which the major porphyry bodies occur. The ore bodies, which exhibit three principal structures, consist of quartz veins and associated pyritized wall rock. Some lodes are composed of en echelon veins, others exhibit a main quartz body with branching stringers and a third consists of a single definite lead. Gold, in a coarse visible form, may be confined to quartz in some ore bodies but in others it is finely divided and is found not only in quartz but also associated with pyrite in the adjacent wall rock. In many veins the distribution of gold is such that there are several ore sections, separated by areas of low-grade material, in the same vein although its physical appearance remains unchanged. The veins form a very complex pattern in an ore zone which in places attains a length of 6000 ft. and a width of 4000 ft. They are most abundant in the Keewatin lavas in the neighborhood of the porphyry bodies. Few of the veins are persistent for long distances, though some

Jan 1, 1940

By H. S. Cannon, F. N. Rhines

IT. H. Hausner( Sylvunia Electric Products Inc., Bay-side, N. Y.)—The results reported by the authors are interesting because they contribute some information on the principles of sintering and also because of a certain practical value for the manufacture of powder . metallurgical parts in production. Pressed powder compacts are frequently sintered in a boat in several layers so that the lower layers are actually sintered under the weight of the upper layers and, therefore, are frequently deformed. The authors gave information on this deformation process by determining the effect of the load on the density. The experimental setup of the authors, however, has a disadvantage—that the sintering occurred in a cylindrical container so that the deformation was stopped in the direction of the diameter. The authors should have rather called this a study of hot-pressing than of sintering. I want to call the attention of the authors and others interested in sintering under load to the experimental work described by Dawihl and Rix.' These authors sintered cylindrical compacts under a lengthwise ten-sional load of 0 to 25 g and found that the shrinkage in length and diameter changes considerably with the load, but that the volume shrinkage is affected very little by the load. H. S. Cannon (authors' reply)—We wish to thank Dr. Hausner for calling attention to the experimental work of Dawihl and Rix. The fact that they found volume shrinkage little affected by varying tensional loads during sintering seems to support the contention that the forces due to loading are equivalent to and additive to the forces which cause densification. This contention is the basis of our comparison of sintering and creep.

Jan 1, 1952

By Janshi Sen

VERTICAL-INTENSITY magnetometers, such as the Hotchkiss Superdip and the Askania vertical field balance, are now [ ] widely used, because vertical-intensity charts give definite information for the location of upper pole, dip and strike, and approximate shape of the deposit. Again, a slow and steady increase of dip over a large area indicates a large deep-lying deposit, while a large dip limited to a small area and falling away rapidly suggests a small and shallow one. The complication comes more from the richness of the ore. A large body of lean ore near the surface might produce the same vertical-intensity chart as a rich ore at depth. This paper presents a method for calculating the maximum depth of a single-pole deposit and another for a two-pole mineral body, by utilizing data of both vertical and horizontal intensities as obtained by a Thalen-Tiberg magnetometer. As shown on the left side of Fig. 1, lean ore, rich ore and a single pole produce the same magnetic field. The depth of the pole, [ ] h, can be calculated from the following relation: [h=a=tan¢=G-F h=aXFy] where G is the vertical intensity at point A due to the pole; F, the horizontal intensity of the same; and a, the distance from the point of maximum vertical intensity or the vertical projection of the pole on the surface to the point of observation A. If an entirely covered deposit is indicated by magnetic measurements and boring cost estimated from the calculated depth is so reasonable as to encourage drilling, the ore should be struck somewhere within the limit of the calculated depth by the borehole. A number of such points as A should be taken for calculation, erratic results should be rejected and the average figure used for cost estimation.

Jan 1, 1944

By John Suman

DURING the past few years the taking of cores in drilling with rotary equipment has been perfected to a remarkable degree in the Gulf Coast fields of Texas and Louisiana. Taking of cores is becoming quite a common thing, especially in the newer fields, and drillers are becoming expert in this work. The writer has seen cores 5 to 8 ft. long taken with great ease in wells as deep as 4500 ft. Coring is doing much to remove the prejudice which so many petroleum engineers seem to have against .the use of rotary drilling equipment for exploratory work. Some operators .are now claiming that when used with a reasonable amount of coring the rotary system is even more satis-factory than cable tools for exploring in certain territory. A case has recently been pointed out in the South Electra field of North Texas, where producing oil sands, passed over by cable-tool drillers, are being brought in with rotary equipment. It seems that in this particular territory the sands are rather thin. Cable-tool drilling was carried on for the most part in a wet hole and the red mud encountered in drilling caved into the hole very badly, so that the cuttings showed mostly red mud and the driller, thinking that the sand did not amount to anything, carried his water string through the sand. The later .operators, drilling into the sand with rotary equipment and coring it, found that it was well worth testing.

Jan 10, 1922

By R. L. Templin, D. A. Paul

The modulus of elasticity is defined as the ratio of stress within the proportional limit to corresponding strain. This property, as thus defined, is a constant for each kind of material; and in tension or compression is usually designated by the symbol E. The modulus of elasticity serves as an index of the stiffness of a material or a measure of its ability to resist change of shape under stresses not higher than the proportional limit. In view of the frequency with which the modulus of elasticity is used in engineering calculations, it is surprising to note the uncertainty that exists as to authentic values, and the marked lack of published information relating to the variation of the constant E within individual alloy systems. A value of 10,000,000 Ib. per sq. in. has been quoted as representative of aluminum and its alloys. This value has been found to be approximately corrcct for pure aluminum and aluminum alloys in which the total percentage of the alloying elements is low, but seriously in error in the case of alloys that contain relatively large amounts of the alloying elements. a National Metals Handbook. b Intcrnatiunal Critical Tables. '' Aluminum Co. of America. " Based on density of alurminum (2.70). c Smithsonian Pliysical Tables.

Jan 1, 1931

By Earl R. Hoskins, James E. Russell

The electrical resistivity of rocks has been studied quite extensively, in particular, the effects of temperature and confining pressure on resistivity. References 1 through 6 at the end of this chapter pertain to electrical resistivity of rock and contain further references on the same topic. The present study is motivated by an interest in determining the in-situ properties of rock as well as the stress state of the rock and how these quantities are changing with time. Most of the previous work on the electrical resistivity of rocks has been directed toward saturated rocks at relatively high confining pressures and temperatures. The present study was oriented towards air-dry surface rock that might occur in mine pillars. The mean stress and temperature under such conditions are comparatively low. It has been demonstrated that the resistivity of rock is highly dependent upon the porosity. In fact, for saturated rocks, a relationship referred to as Archie's law has been established between porosity and electrical resistivity. In the case of saturated rock, the property that is actually being measured is the resistivity of the solid/fluid system. Since the resistivity of the fluid alone is usually much lower than that of the dry rock, it is understandable that the resistivity of a saturated rock is in general several orders of magnitude lower than the resistivity of a relatively dry rocli. For dry rock, it seems reasonable that the electrical resistivity should increase as microcracks open within the material. Since microcracks open as material is stressed closer and closer to its failure point, it appears that there should be a correlation between electrical resistivity

Jan 1, 1970

By T. J. Woods

This paper deals with the origin, definition and prevention of scabs on semifinished rolled-steel product. Mold coatings, which are considered essential in scab prevention, were found to be effective only in relation to the ingot surface of semikilled and killed steels and not necessary for the rolled product. That is to say, the scabs on ingots caused by having been cast in uncoated molds are eliminated in the soaking and rolling operations, therefore are not present on the rolled product. This fact, which is contrary to the average opinion, was established after extensive and thorough experiments had proved the ordinary conception of the origin of scabs to be incorrect. This subject may be of little or no concern to steel plants producing small ingots for the manufacture of small billets and bars, except as it may be of interest in showing why their surface troubles with scabs do not exist on the product of heats with normal pouring practice. But to the producer of large ingots to be rolled into slabs for large plates used in shipbuilding, it is a very important subject. Definition of a Scab The generally accepted opinion is that the individual scabs present on rolled products (as shown by Fig. I) are considered to have been individual splashes on the ingot surface. This opinion was found to be incorrect. Experiments showed that there were no individual scabs on the product that had appeared as individuals on the ingot surface. The single scabs seen are either pieces of a shell that is present near the bottom of all top-cast ingots, or a veneer that may be present on any part of an ingot improperly poured, as when the stream strikes the mold wall. This definition is based on a detailed study of scabs and their characteristics in which the following have been found true: Location.—On the product of heats poured without trouble, scabs, if present, are always on the product that corresponds to the bottom end of the ingot, and usually occur in clusters. This is true whether molds are coated or not. Shape.—There is no regularity as to shape, size or thickness. It is sometimes possible to separate a few pieces and place them together, like pieces of a jigsaw puzzle, indicating that at one time they had been united as one piece. If individual splashes were the origin of scabs, the foregoing would not be true. Instead, the splashes, which occur throughout the pouring of the ingots, would be present uniformly over the entire product and there would be considerable similarity in the shape and thickness of the scabs. Experimental Work Our experimental work was conducted on 200-ton heats of semikilled plate steel tapped into an oval ladle 15 ft. high. All ingots were top-cast direct into 24 by 54 by 82-in. molds, straight-sided, set on flat stools. Two separate studies were made about one year apart, each study extending

Jan 1, 1943

GENERAL GEOLOGICAL DESCRIPTION The uranium mineral appraisal herein described was made for an ore deposit in New Mexico. The uranium mineralization occurs as roughly tabular to lens-shaped deposits of varying thickness within the sandstone of the Jackpile formation of Jurassic age. The mineralization occurs at several horizons within the Jackpile formation, but is not always confined to specific beds. It often transgresses across stratigraphic layers, as demonstrated when attempting correlation of uranium gamma anomalies between adjacent drill holes. Preferred mineral trends have been established in some parts of the deposit, but are not always predictable when attempting to extrapolate beyond the zones defined by drill hole sampling. MANAGEMENT OF DRILL HOLE SAMPLE DATA All of the drill hole sample data used in the appraisal were obtained from interpretation of gamma-ray logs. A brief description of gamma-ray log sampling is given in Chapter 2. Two preliminary steps are involved in preparing gamma-ray logs into sample data normally acceptable for computer manipulation. 1) The gamma analog trace produced by the downhole probe must be digitized, i.e., counts-per-second (CPS) are recorded for each 0.15 m (1/2-ft) interval across the gamma-ray anomaly. The work is usually done on a "digitizer" while following the analog trace with an electronic stylus on a special tablet or table. The other alternative is to do the work manually. Some of the newest downhole logging equipment produces a magnetic tape output which can be read by a computer. 2) The gamma-ray CPS values must then be converted to equivalent U308 assay values, taking into consideration all appropriate correction factors. The US Atomic Energy Commission, now part of the Department of Energy, developed the theory and algorithm for this conversion in the 1960's, and though the work can be done manually, it is best done with the GAMRED (gamma-reduction) computer program. Fig. 14-1 illustrates a typical analog trace produced by the probe instrumentation, including gamma-ray trace (left), self-potential electric log (center), and resistivity log (right). Fig. 14-2 shows a form of the computer output after the analog data has been digitized to 0.15-m (1h-ft) intervals and converted to percentage U308 values for the same hole. The U308 grade bar graph on the right permits rapid visual inspection of anomalous values by depth and elevation. The converted U308 sample data were next processed by the SURVEY program that assigned to each assay interval [0. 15-m (1h-ft)] an X Y Z coordinate, taking into account all deviations indicated from downhole survey information. The output file of the SURVEY program was listed on the line printer for examination by project geologists, and also became the main input file for the URAN/ COMP compositing program, which is designed to group individual 0.15-m (/-ft) U308 sample values into larger intervals representing discrete anomalous zones according to a series of specified parameters entered into the program by the user. Composite U308 intervals were computed by the URAN/COMP computer program, the logic of which may be briefly described as follows: Step 1 The program searches for the highest U308 value in the hole and builds a composite by adding the highest grade interval on either side so long as the added value is greater than a minimum acceptable grade, and the total composite, after addition, meets minimum GT (grade times thickness) constraints. Step 2 The program loops back to find the next highest assay value in the hole not already included into a composite, until all anomalies above minimum cutoff grade are composited. Step 3 Individual composites are combined if they are closer than a specified minimum waste thickness, and the resultant composite grade still meets GT minimums.

Jan 1, 1980

By G. W. P. Rengstorff, R. B. Fischer

A study was made of the effect of impurities on the bend ductility of cast molybdenum. High purity molybdenum was repared by re-melting under high vacuum. The ductility of "transverse-grain" specimens indicated that intergranular brittleness decreased with an increase in purity of the metal. THE production of as-cast molybdenum with high ductility at room temperature would make working of the metal easier and increase the usefulness of the as-cast metal. Furthermore, a .knowledge of the factors that influence the ductility of as-cast molybdenum might be applied to the problem of making fusion weldments having satisfactory room-temperature ductility. Individual grains of commercial as-cast molybdenum are slightly ductile at room temperature. However, the presence of carbides at the grain boundaries may cause the metal to fracture in a brittle manner. This behavior has been discussed.' The amount and distribution of the impurities in as-cast molybdenum would be expected, from previous research on the metal, to have considerable influence on its ductility. Some effects of oxygen and carbon on the mechanical behavior of the metal were discussed by Parke and Ham,2 Woodside,3 and Zappfe. Landgraf, and Worden.4 Parke and Ham2 found that, if a sufficient number of molybdenum oxide particles were present at the grain boundaries, the intergranular cohesion was reduced to the extent that arc-melted molybdenum would rupture intergranularly during hot forging. They also found that if the oxygen content was less than 0.003 pct, the cast molybdenum was hot forgeable. It is suspected, however, that forgeable molybdenum may contain a small amount of oxide that could reduce the ductility of the as-cast metal at room temperature. Also, there is the possibility of the unfavorable distribution of other impurities having a detrimental effect on the ductility of cast molybdenum. The results of a study of the influence of purity on the room-temperature ductility of cast molybdenum are presented here. Vacuum Arc-Melting to Produce High Purity Mo One way of determining the effect of impurities on the ductility of molybdenum is to prepare and test metal as free of all impurities as possible. Accordingly, the present investigation was undertaken with this in view. Arc melting in high vacuum (less than 0.1 micron of mercury) was chosen as the method for reducing the impurities below the concentrations occurring in commercial molybdenum. Commercial arc melting of molybdenum is carried out at about 50 microns pressure. During the arc melting, carbon and oxygen in the metal react to form carbon monoxide. By virtue of the vacuum process, the partial pressure of carbon monoxide is maintained at such a low value that the reaction greatly lowers oxygen and carbon contents. An excess of at least 0.03 pct C is used in commercial arc melting to insure that the oxygen content will be below 0.003 pct. The excess carbon remaining after the deoxidation step forms carbides on freezing. Some of the carbides precipitate at the grain boundaries and, as will be shown, have an unfavorable effect on the room-temperature ductility. In the present work, only the small amount of carbon (0.003 pct) contained in the commercial powder-metallurgy molybdenum used for melting stock was present. Partial removal of oxygen from the melt probably occurred as the result of the volatilization of molybdenum oxides, or by distillation of oxygen at the high melting tem-

Jan 1, 1953

By J. L. Wyatt

THE smelting of ilmenite to produce a slag rich in titanium, with pig-iron as a byproduct, introduces new concepts in electric smelting metallurgy. Titanium slags are characterized by low electrical resistance, thereby requiring a different type of electric furnace operation, and power supply sources substantially different from those encountered in normal steel melting and siliceous ore smelting furnaces. This paper describes special apparatus for determining specific electrical resistivity of titanium slags, and reports the values obtained on slags encountered in the process of smelting ilmenite ores. In an induction furnace under conditions approximating normal furnacing operation, 25 general heats and 6 special standardization and comparison heats were run. Results indicate relatively low resistivity. Resistivity depends primarily on slag composition, and, to a lesser degree, on temperature. During the summer of 1947 a cooperative project between the National Lead Co. and the Bureau of Mines was conducted at Boulder City, Nevada, in the Electrometallurgical Laboratories of the Bureau. The project involved smelting of ilmenite ores in electric furnaces, and has been reported in detail.' The author participated as a member of the staff of the National Lead Co. during the entire campaign. One outstanding characteristic of the titaniferous slags, their apparently excellent and variable electrical conductivity, was considered sufficiently important to warrant further study. Although little electric smelting of iron ores has been done in the United States, a certain amount of information is available for comparative purposes. Personal experience in smelting siliceous iron ores in electric furnaces furnished further information for comparison. In general, silicate slags are relatively poor conductors of electricity. Current flow during smelting operations may be maintained through a floating layer of coke on top of the slag bath, or through a bath of molten iron, beneath the slag. Silicate slags are not sufficiently conductive to furnish a path for current passage when normal furnace voltages are used. Experimental smelting of a silicate iron ore was undertaken for comparative purposes. A fluid melt was not obtained until the FeO content was reduced to 15 pct. The resistivity increased as the FeO content decreased, FeO compounds being the most conductive of the various oxides in such a normal slag system. The converse appears to be true in slags containing large percentages of TiO2. It has been found that titanium slags become molten with FeO percentages in excess of 30 pct, and that the conductivity becomes generally better as the FeO con-tent of the slag diminishes. This phenomenon was demonstrated in the furnacing operations at Boulder City. During the initial smelting period furnace electrodes could be held immersed several inches in the slag, with tap selectors set for a no-load voltage of 70 v. As the FeO content decreased, the furnace electrodes would "walk up," until at one point in the process the tips would break the surface and arc on top of the slag. This was undesirable since direct arcing caused losses of important flux additions. The slag compositions under study at that time were such that losses due to surface arcing sometimes caused viscous slags to be formed. Forcing the electrodes into the slag bath by manual control to prevent surface arcing resulted in excessive power input and lack of control. Suitable low voltages were not available. Measurement of the electrical resistivity of titanium slags at various operating temperatures and slag compositions was undertaken. It was believed that this information would be of use in the design of electric furnaces suitable for smelting ilmenite, with voltages, electrode sizes, and electrode spacing adapted specifically to titanium slags.

Jan 1, 1951

By T. J. Woods

This paper deals with the origin, definition and prevention of scabs on semifinished rolled-steel product. Mold coatings, which are considered essential in scab prevention, were found to be effective only in relation to the ingot surface of semikilled and killed steels and not necessary for the rolled product. That is to say, the scabs on ingots caused by having been cast in uncoated molds are eliminated in the soaking and rolling operations, therefore are not present on the rolled product. This fact, which is contrary to the average opinion, was established after extensive and thorough experiments had proved the ordinary conception of the origin of scabs to be incorrect. This subject may be of little or no concern to steel plants producing small ingots for the manufacture of small billets and bars, except as it may be of interest in showing why their surface troubles with scabs do not exist on the product of heats with normal pouring practice. But to the producer of large ingots to be rolled into slabs for large plates used in shipbuilding, it is a very important subject. Definition of a Scab The generally accepted opinion is that the individual scabs present on rolled products (as shown by Fig. I) are considered to have been individual splashes on the ingot surface. This opinion was found to be incorrect. Experiments showed that there were no individual scabs on the product that had appeared as individuals on the ingot surface. The single scabs seen are either pieces of a shell that is present near the bottom of all top-cast ingots, or a veneer that may be present on any part of an ingot improperly poured, as when the stream strikes the mold wall. This definition is based on a detailed study of scabs and their characteristics in which the following have been found true: Location.—On the product of heats poured without trouble, scabs, if present, are always on the product that corresponds to the bottom end of the ingot, and usually occur in clusters. This is true whether molds are coated or not. Shape.—There is no regularity as to shape, size or thickness. It is sometimes possible to separate a few pieces and place them together, like pieces of a jigsaw puzzle, indicating that at one time they had been united as one piece. If individual splashes were the origin of scabs, the foregoing would not be true. Instead, the splashes, which occur throughout the pouring of the ingots, would be present uniformly over the entire product and there would be considerable similarity in the shape and thickness of the scabs. Experimental Work Our experimental work was conducted on 200-ton heats of semikilled plate steel tapped into an oval ladle 15 ft. high. All ingots were top-cast direct into 24 by 54 by 82-in. molds, straight-sided, set on flat stools. Two separate studies were made about one year apart, each study extending

Jan 1, 1943

By Joseph C. Buchen

In principle, productiorl of salt from sea water is a simple operation. The sun and wind cause evaporation of sea water trapped in ponds, and what is left is principally salt. Commercial production, however, requires consideration of many factors. First is a high consistent annual rate of evaporation, as well as large areas of suitable low-lying ground close to economical shipping facilities. The south end of San Francisco Bay has these requisites. Large ponds are built, by using clamshell dredges to build up levees to a height of approximately 3 ft. on ground usually lower than sea level, so that the water may be taken in through tide gates without pumping. Ponds are divided into extremely large concentrating ponds and smeller crystallizing ponds. Approximately ten times more area is required for concentrating than for crystallizing. The concentrating ponds are irregular in shape and size but the crystallizing ponds are rectangular and fairly regular in size, to aid in harvesting. The ocean water is taken into the first of a series of concentrating ponds and gradually moved forward from pond to pond as it increase:: in density, reaehing the crystallizing area as a saturated brine. This brine is pumped into the crystallizer at the beginning of the net evaporating season, usually in May, and further evaporation causes its sodium chloride content to deposit on the bottoms of the ponds. The brine must be drawn off and a fresh supply added from time to time to prevent other undesirable salts from depositing with the sodium chloride. Harvesting usually begins near the end of August and now is accomplished almost entirely by mechanical means. After harvesting, the salt is stored in large sbockpiles until required for shipping or refining. The greatest amount is used for industrial purposes and is shipped without any processing other than screening, but all salt for domestic use produced by the Leslie Salt Co. is refined by the racuum process, giving a produet consistently testing over 09.9 per cent sodium chloride.

Jan 1, 1938

THE education of adolescents to perform the duties and assume the responsibilities of maturity has been a characteristic of human society since the dawn of history. In the beginning the members of the immediate family performed this function, and in modern life they still have an important part in it. Possibly religion was the first field in which education began to be functional; young people were sent for instruction to a teacher who had a broader and deeper knowledge of the subject than was possessed by the family. It does not seem necessary for our purpose to attempt to determine how, when, or where instruction in the practical arts first began to become functional, and the brief outline which follows must suffice. The discovery and utilization of mineral substances to improve and maintain the conditions of human living is a practical art, which must have had an almost accidental origin and have been developed by empirical experiments. We do not know, nor would it be useful to try to fancy, how men first learned that they could make use of mineral substances to their benefit, but however that knowledge was initially gained it was certainly trans- mitted through instruction in the family. At fist such activities must have been merely a minor part of the making of a living, bit in time those who excelled found it better to devote them-

Jan 1, 1941

By Joseph C. Buchen

In principle, productiorl of salt from sea water is a simple operation. The sun and wind cause evaporation of sea water trapped in ponds, and what is left is principally salt. Commercial production, however, requires consideration of many factors. First is a high consistent annual rate of evaporation, as well as large areas of suitable low-lying ground close to economical shipping facilities. The south end of San Francisco Bay has these requisites. Large ponds are built, by using clamshell dredges to build up levees to a height of approximately 3 ft. on ground usually lower than sea level, so that the water may be taken in through tide gates without pumping. Ponds are divided into extremely large concentrating ponds and smeller crystallizing ponds. Approximately ten times more area is required for concentrating than for crystallizing. The concentrating ponds are irregular in shape and size but the crystallizing ponds are rectangular and fairly regular in size, to aid in harvesting. The ocean water is taken into the first of a series of concentrating ponds and gradually moved forward from pond to pond as it increase:: in density, reaehing the crystallizing area as a saturated brine. This brine is pumped into the crystallizer at the beginning of the net evaporating season, usually in May, and further evaporation causes its sodium chloride content to deposit on the bottoms of the ponds. The brine must be drawn off and a fresh supply added from time to time to prevent other undesirable salts from depositing with the sodium chloride. Harvesting usually begins near the end of August and now is accomplished almost entirely by mechanical means. After harvesting, the salt is stored in large sbockpiles until required for shipping or refining. The greatest amount is used for industrial purposes and is shipped without any processing other than screening, but all salt for domestic use produced by the Leslie Salt Co. is refined by the racuum process, giving a produet consistently testing over 09.9 per cent sodium chloride.

Jan 1, 1938

By E. M. Wise

MANY of the platinum metal alloys are hot-forged in the early stages of reduction from ingot and substantial quantities of platinum alloys are commercially employed at very high temperatures in ammonia oxidation units, orifices for forming glass rods and fibers and as cathodes in long-life thermionic amplifiers. They are used also for electrical heating resistors, safety blowout disks, thermocouples and crucibles. The tensile prop-erties at elevated temperatures are important in many of these situations but data on the subject are limited. Creep data also are important, but will not be covered at this time. SCOPE AND CONCLUSIONS Tensile tests were carried out at room temperature and elevated temperatures up to 1100° C. on previously well annealed samples of platinum, palladium and several of their important alloys with composi-tions shown in Table 1. The results are presented graphically in Figs. 1 to 4. The tensile strengths of platinum and the platinum-base alloys (with the exception of the 10 per cent rhodium-platinum alloy) at 1100° C. are from 16.6 to 18.8 per cent of the strengths of the same alloys (well annealed) at room temperature. The strength ratio of the 10 per cent rhodium-platinum alloy is 22.3 per cent, which is appreciably higher than that of the other materials tested.

Jan 1, 1938

By Rebecca Mae Summer

Increasing urbanization and industrial activity require increased supplies of sand and gravel. This means expanded surface mining and despoiled land near population centers. Highly competitive land use demands justify serious consideration of premining planning for multiple land use and reclamation concurrent with mining. 1-5 Formulating solutions to environmentally and economically sound uses requires a comprehensive approach based on properties of the natural resource base--geology, soils, and water. A study of sand and gravel mining within Pleistocene-Holocene fluvial deposits in Colorado County. Texas [(Fig. 1)] illustrates how physical limitations imposed by the resource base are determined.6,7 Data from drillers, logs of water wells, test boreholes, field observations, and laboratory analyses are used to evaluate these physical controls. Knowledge of the thickness and composition of overburden aids in developing optimum reclamation and revegetation plans. Most of the overburden in the study area [(Fig. 2, 3)] is a clayey mud with variable amounts of silt and fine sand. A comparative textural analysis of overburden and native soil is used to assess changes incurred by mining and for evaluating other physical characteristics, e.g., ability to support crops, permeability. and shrink-swell potential. Textures are correlated with soil types found in the area [(Table 1)] to get an approximation of probable surface properties expected from these mined materials. Results of textural analyses [(Table 2)] indicate that separating topsoils from overburden during mining is not necessary because the range of overburden textures is about that of native soils. However, more data is needed on nutrient deficiencies to evaluate fertilizer requirements for successful revegetation.*6

Jan 1, 1979

By B. Silliman

THESE ores occur in the Laurentian rocks in the town of Clifton, St. Lawrence County, New York. The Clifton Mining Company have opened these magnetites upon their estate of 23,000 acres, on the waters of the Grasse River, an affluent of the St. Lawrence, which flows for about nine miles across the estate, exposing a section of the formation, and affording ample water-power at numerous points. In approaching this district from De Kalb Junction, upon the Watertown and Ogdensburg Railway, the observer passes from the zone of the specular ores, which abound to a great extent in Jefferson County, across a belt of non-metal-liferous limestones, continuing for some miles intermingled with metamorphic rocks, and gradually giving place to heavy beds of granitic and porphyritic gneiss, the weathered surfaces of which present a gray and rough appearance, from the washing out of the feldspar; leaving the quartz very prominent, and completely disguising the real character of the rock, which, when freshly broken, has a lively reddish appearance from the predominance of flesh-colored and red feldspar. Beds of fine-grained quartzite appear also intercalated in the granitic gneiss. These are the dominating rocks of the magnetite region, but the magnetite is always found, so far as the speaker's observation extended, associated with beds of calcite, carrying hornblende, black and green, biotite, and brown garnet interspersed with yellow and magnetic pyrites. The strike of these rocks is about northeast, and their dip about 40° to 45° southeast.

Jan 1, 1873

The Library of the above-named Societies is open from 9 A.M. to 9 P.M. on all week-days, except holidays, from September 1 to June 30, and from 9 A.M. to 6 P.M. during July and August. The Library contains about 55,000 volumes, including sets of technical periodicals and the publications of scientific and technical societies. Members of the Institute, with few exceptions, are forced to spend a portion of their time in localities isolated from sources of information. To these the Library can render valuable service through correspondence; letters requesting information will receive special attention. The Library is prepared to furnish references and copies of articles on mining and metallurgical subjects; to determine the existence of mining-maps, and to furnish general information as to the geology and mineral resources of all countries. All communications should be made as definite as possible so that the information received may be what is desired and not include collateral matter which may not be of interest. The time spent in searching for such collateral matter will be saved, and the information will be sent more promptly and in more usable-shape. The members of the Institute can be of service to the Library by forwarding copies of mining-reports, maps privately issued, and similar material, which will be classified, indexed, and made available to other members. Suggestions for additions to the Library, either by purchase or personal solicitation as gifts, will be welcomed. It is hoped that members while in the city will use the Library freely, and assurance is given that most careful service will be rendered to them.

Jan 2, 1914

By Robert M. Dreyer

During the past two decades, synthetic abrasives have taken over successively greater percentages of the high-grade abrasive market, so that now, with the exception of natural diamonds (discussed in section 3.15.4C of this chapter), the importance of natural high-grade abrasives is negligible. The predominance of synthetic abrasives is indicated in Table 15.4A.1. This shows that the 1968 value of domestically produced synthetic abrasives (excluding synthetic diamonds) was over $80 million, whereas the value of garnet, the largest domestically produced, natural high-grade abrasive, was less -than $2 million. The major synthetic abrasives (other than synthetic diamonds) are: alumina, silicon carbide, boron carbide, tungsten carbide, and metallic oxides, including various iron oxides. A major advantage of synthetic abrasives is that the size and shape of grain can be closely controlled during manufacture. Although Table 15.4A.1 gives the average price of synthetic abrasives, such averages are of somewhat limited value. This is because the actual price varies within wide limits, depending on composition, hardness, size, and shape of grain. In 1968 the approximate total consumption of abrasives in the United States was valued at about $200 million, of which about two-fifths was in the form of synthetic abrasives (other than diamonds), one-third in synthetic diamonds, and the remainder in natural diamonds. Natural abrasive products, such as silica sand, tripoli, and pumice, are important in the low-cost abrasive field. Of the low-cost abrasives, silica sand continues to be the most important, with domestic production of about 300,000 tons at a value of $1.8 million (see Table 15.4A.1). In general, the lower the sales price of the abrasive product, the more limited is the market which can be served from a given production center. Each abrasive has applications for which it is especially useful, but there is a continual struggle among abrasive suppliers to induce substitution of one product for another. Such substitution can be stimulated by changes in method of preparation affecting hardness, shape, and size of grain.

Jan 1, 1976