By C. M. Tucker, K. R. Van Horn, W. P. Sykes

Recent investigations of the molybdenum-carbon alloys have been reported by Becker and Ebertl,‡ Westgren and Phragmén2, T. Takei3, and H. Tutiya4. Takei3 studied the Mo-C system by employing metal-lographic and X-ray methods, and the other publications described the determination of the crystal structure of the molybdenum carbides. In exploring this system by a technique previously applied to the tungsten-carbon series5, the results of Takei were confirmed with two definite exceptions; i.e., first the composition of the eutectic, and second the nature of the carbon-rich intermediate phase. Consequently, a more thorough examination of the molybdenum-carbon constitution was initiated in an effort to correlate the data supplied by the microstructures, diffraction patterns and chemical analyses. Metallographic Investigation A briquette of molybdenum powder when heated in a carburizing atmosphere at 1500" to 1600" C. for several hours develops the carbon-rich layer shown in Fig. 1. The carburization was accomplished by placing the briquette in a carbon tube, which was heated in the hydrogen atmosphere of an alundum muffle wound with tungsten resistor. While the macrostructure indicates two distinct shells, and suggests the possibility of two carbon-rich phases, no evidence of this condition could be detected by the microscope, which revealed but one high-carbon constituent. This carbide forms next to the molybdenum as a relatively dense, light-colored zone (Fig. 2) which passes abruptly into an outer layer of spongy texture. As will be noted later, only one intermediate phase was observed in the X-ray photograms prepared of different locations in the carburized zone. The metallographic structure at the inner border of the shell, reproduced in Fig. 3, shows a marked porosity accom-

Jan 1, 1935

By R. W. Waterfill

MANY existing ore deposits of valuable metals have been worked out in their upper surface levels and the continued productivity of these mines is dependent on their extension to greater depths in the earth. The maximum depths at present reached are about 6000 to 8000 ft. below the surface, with no evidence of an impoverished ore vein. These mines are widely distributed; some of the best known are in South Africa, Brazil, India and in the western sections of the United States. Among the factors which increase the difficulty of working these mines at increasing depths are hoisting, rock pressure and temperature. The manner and effectiveness with which these problems are met will, no doubt, determine in a large measure the ultimate depths to which any mine can be profitably worked. The most critical of these three factors at present is the increase in temperature with depth. The high temperature and humidity in many of these mines at present is severely detrimental to the health of the workers and greatly hampers their efficiency. Some have almost reached a condition in which the human system cannot survive. The problems involved in the cooling and ventilation of mines have all been ably analyzed and presented in previous articles. For this reason, only a resume of conditions affecting the cooling and conditioning of deep and hot mines will be given in this paper before attention is directed to possible methods of improving atmospheric conditions in the working levels.

Jan 1, 1929

By P. Payson

Intergranular corrosion in corrosion-resistant chromium-nickel steels has been widely discussed in the last few years. So far as the author knows, nothing has been published which definitely shows that this tendency can be eliminated, although suggestions have been made that a remedy is possible if certain specifications are satisfied. Strauss, Schottky and Hinnüberl suggested an increase in chromium content to an extent that would prevent the impoverishment of chromium on carbide precipitation sufficient to cause impaired corrosion resistance in the matrix. Pilling2 suggested an increase in nickel, so that the stability of the austenite matrix would be increased. Aborn and Bain3 say that "intergranular attack—may be eliminated by preventing carbide precipitation (e. g., by lowering the carbon content or somehow raising its solubility) or by precipitating it permanently under conditions which will not remove chromium from solid solution so drastically at any points." In a later paper Aborn and Bain4 state that many different metallic elements, tungsten, vanadium, copper, aluminum, molybdenum, titanium and zirconium, have been added in small percentages to increase the stability of these alloys, but that it has been reported that according to the copper sulfate test these added elements act only to retard the intergranular corrosion. and that increased nickel and chromium contents have similar effects. Newell5 showed that the lower the quenching temperature before reheating, the less severe was the intergranular attack.

Jan 1, 1932

By G. A. Mancini, V. Bharucha, J. W. Spretnak, G. W. Powell

The characteristics of the motion of the a interface during the "down" transformation was studied in zone-refined iron and dilute binary alloys containing nickel and molybdenum by means of the thermionic emission microscope and high speed photography. The frontal movements were found in all cases to be definitely discontinuous with time and an appreciable number of incremental jumps were found to proceed in the reverse direction (a to b). Molybdenum was found to be particularly effective in increasing the frequency of the increments of transformation from the stable to the metastable phase. A knowledge of the mechanism by which alloying elements affect the hardenability of a steel is desirable from both the practical and scientific viewpoints. It is well established that microstructures consisting of tempered martensite and lower bainite exhibit the best performance in terms of toughness and resistance to crack propagation. The presence of some upper transformation products, namely ferrite and pearlite, is in general undesirable. Various researches have indicated that the ferrite matrix grain structure is a very important difference between the upper and lower transformation products, namely equi-axed vs acicular. Any comprehensive theory of the decomposition of austenite should explain the dependency of the morphology of the matrix on undercooling. The contribution of various alloying elements to hardenability has been determined experimentally and catalogued in considerable detail. A rationalization of the basic mechanism or mechanisms by which individual elements affect the kinetics of the decomposition of austenite to products other than the phase "martensite" has not been evolved as yet. Interest in this problem was stimulated by the effects of minute quantities of boron in hardenable steels. This paper deals with one aspect of this problem, namely the characteristics of the ?-a transformation in high-purity iron and in two carbon-free iron binary alloys. A detailed historical account of the scientific developments in the study of the decomposition of austenite would be a prodigious undertaking and will not be attempted here. There are several excellent reviews in the literature on the formation of pearlite, martensitic reactions, and kinetics of solid-state reactions. The thinking on reaction mechanisms has been influenced to a large degree by the "classical" Tammann nucleation and growth model, in which an embryo springs into being by a fluctuation, and grows to a critical size through atom by atom deposition. Such a process is expected, accordingly, to be diffusion controlled. Considerable research attempting to relate the contribution of alloying elements to hardenability on the basis of their effect on the diffusivity of carbon in iron has not been productive from a mechanistic viewpoint. The formation of pearlite and ferrite has been treated in terms of nucleation and growth processes in which presumably the lattice transformation also occurs by a diffusion process. The other prominently considered mechanism is the "martensitic" or cooperative shearing mechanism. It seems generally, but not entirely, agreed that the phase "martensite" forms by this mechanism, and that it is involved to some extent in

Jan 1, 1962

By Walter Harvey Weed

The notes given in this paper, the result of observations made during recent brief professional trips to the northern States of Mexico, are offered as a slight contribution to the geological knowledge of a region little known, but long famous for its rich gold- and silver-mines. They are not detailed geological studies, but they contain, I believe, the salient facts. The following districts were visited: 1. Santa Eulalia (silverlead) ; 2. Parral (silver-lead); 3. Las Vigas (copper); 4. Jimenez (copper); 5. Guadalupe y Calvo (gold); 6. La Cumbre (gold); 7. Palmarito (silver); 8. Cananea (copper); 9. Sierra Pinitos (gold); 10. Sierra Azul (gold). 1. The Santa Eulalia Silver-Lead Deposits. Seventeen miles SE. of Chihuahua is the mining district of Santa Eulalia, to which that city owes its origin and long prosperity. Discovered in 1703, this district has been, and still is, one of the great silver-lead producers of the world. For 86 years after its discovery, the total output upon which the crown tax was paid amounted to $112,000,000. Worked until within the last 20 years by the most primitive methods, without machinery of any kind, the deposits continued to yield a vast treasure of silver; at present the yearly tonnage far exceeds that of former times. A broad-gauge road runs from Chihuahua up the valley of a small creek to the village of Santa Eulalia, which is situated within the borders of the mountains of that name. A few miles out of Chihuahua a narrow-gauge railway, owned by the Chihuahua Mining Co., branches off to the mines. This road ascends a smooth but steeply-rising plain to the base of the mountains, and winds about the slopes until the mines are

Jan 1, 1902

By D. C. Seidel, E. F. Fitzhugh

Nickel sulfide ores lend themselves readily to concentration before smelting or pressure leaching, but neither of the major oxidized ore types-the iron-rich laterites and magnesium-rich, soft silicates-has been directly concentrated. Upgrading of crude ore in current practice is limited to cobbing lumps of the harder, lower grade rock (protore) from the softer, enriched silicate ore, because only a small percentage of the nickel in these ores occurs in discrete, contrasting mineral particles. There is no apparent mineralogical contrast in the superficial, iron-rich lateritic ores and, in fact, there is no firm assurance that the nickel atoms are within the lattices of the limonite minerals, or else irregularly adsorbed on the limonite. Within underlying, "rotten rock" silicates, occasional veinlets of garnierite and related nickeliferous silicates are found.1 The garnierite veinlets are only incidental, and the majority of the nickel atoms occur as erratic replacements of magnesium atoms in the micaceous chlorites of the ore mass.

Jan 4, 1968

By D. L. Abata

This paper discusses recent technology dealing with the use of computer graphics in the mining industry. It presents a newly developed computer software package specifically designed for use in underground mining operations. This software package, developed under a US Bureau of Mines contract, 1) displays mine ventilation schematics and other representative illustrations for a real time data acquisition system and 2) uses the Bureau-owned Minefire and Ventilation Code for display of ventilation and contamination predictions on the microprocessor system. The package uses a unique system of display indexing that provides a simple yet efficient method of recalling a series of mine schematics detailing an underground operation and an alarm acknowledgment scheme that provides an effective method of identifying problem areas that may exist in the mine network. The package was written in Fortran for a 64-kilobyte, Z80-based microprocessor computer.

Jan 1, 1986

By Alfredo O. Del Campo

Copper concentrate smelting has been the subject of significant improvements during the last three decades. Several new processes are being successfully applied at industrial scale, and probably no new copper smelter will be built with the old-fashioned reverberatory furnace. However, because of financial reasons, the existing reverberatory furnaces, which smelt a significant part of the copper produced worldwide, are likely to last at least another decade. Some improvements have been introduced in reverberatory smelting practice, the best known being the use of oxyfuel burners. However, efforts to optimize the reverberatory furnace operation through automatic control have not been reported. The complex and semi-continuous nature of the process makes it dificult to find a suitable strategy for its automatic control. Many factors, like fuel economy, productivity, boiler capacity, refractory wear, converter slag return, copper losses in discard slag, etc. are interconnected. The chosen control strategy should take into account all these factors to achieve good economic results. A detailed discussion of these problems is presented.

Jan 1, 1984

By M. Cohen

THERE seems to be a natural urge for the human mind to wonder about the beginning of things. When an explosion occurs, we immediately inquire "what set it off?" If a person contracts a disease, we are likely to ask "how did it happen?" On a much loftier plane, when we reflect about the universe, there is the inevitable question "what, or rather Who, started it all?" In principle, these varied queries have at least one attribute in common: they are attempts, whether earnest or casual, to search out the origin of events in nature. Accordingly, they involve not only scientific, but philosophical and even re1igious matters of deep concern. It is evident that, in a broad sense, the phenomenon of nucleation is enmeshed in this enticing concept of "the beginning", but we must extract the scientific component of the problem for our present purposes. Nucleation, as in the case of phase transformations, is best regarded from the standpoint of kinetics. There are then two main steps, which may come in either order: (a) Experimentally, one attempts to measure the frequency with which transformation centers spring into existence; and (b) theoretically, one seeks a model that will account for this observed birth-rate. Temperature, composition, strain, and prior history are some of the important variables that must be considered both experimentally and theoretically when dealing with nucleation in the solid state. Such interaction of theory and observation is an integral part of science in general, but it is particularly significant in the nucleation problem because the very beginning of a phenomenon invariably occurs on too localized a scale in both space and time to be detected with available techniques. Thus, there is little hope of making direct measurements on the nucleus during its birth or to ascertain the exact nature of the process; one can only infer the details of nucleation from the model whose predicted behavior seems to harmonize best with the measured rate of nucleation and its dependence on known parameters. In the field of solid-state nucleation, both theory and experiment call for much ingenuity, but somehow the conceptual schemes have spawned faster than they can be tested by observation. This is not to say that there are many basically new ideas in modern nucleation theory; rather, as we shall see, it is because the required fine-scale measurements are of immense technical difficulty. Quite likely, some of the nucleation models existent today have survived only because of the latitude permitted by meager data. There is great need to bring theory and experiment into better balance in this important area of physical metallurgy. Although one can

Jan 1, 1959

By Oliver Smalley

EXCEPT for the work of Guillet, who conducted a systematic investigation on the zinc-replacing value of nickel in brass, and extended his investigation with a view to developing commercial high zinc content nickel brasses, the author does not know of any systematic research on the subject. The most promising commercial alloys and their physical properties obtained by Guillet are given below: Maximum Elonga- Reduction Copper Zinc Nickel Stress, tion, of Area, Brinell Tons Per Per Cent. Per Cent. Sq. In. 55.0 41.0 5.0 24.4 46.5 94 Sand cast. 22.6 27.0 90 Chill cast. 56.7 39.74 3.35 30.0 43.0 51.7 97 Casting annealed 2 hr. at 750° C. 33.9 33.0 50.7 144 Cold-drawn bar. 55.15 42.3 2.24 29.8 33.0 116 Casting annealed 2 hr. at 750° C. 32.3 29.0 151 Cold-drawn bar. These test results scarcely justify the use of such quantities of so expensive a metal, and could have been obtained from ordinary commercial brass. For purposes of comparison, the physical properties of ordinary brasses, ranging from 70 per cent. to 50.1 per cent. Cu in both the cast and normalized1 conditions are included in Table 1. These incidentally furnish a useful standard of the properties of castings and of rolled, extruded and forged brass when correctly annealed. A close study of some of the well-known special brasses containing nickel reveals a series of alloys which bewilder by their complexity, and one can only hazard a guess at the function and commercial value of each of the many elements used.

Jan 10, 1925

By John H. G. Monypenny

The range of chromium content of stainless steel is, in most cases, included in the limits 11 to 14 per cent., or the middle part of the range, 9 to 16 per cent., specified by the discoverer. For some time after the steel was produced commercially, the carbon content was about 0.3 to 0.4 per cent. and occasionally higher; only rarely was material with 0.25 per cent. carbon or less produced. The reason for this is obvious from the nature of the alloys of chromium available for making such steels; as the lowest carbon content generally available was about 1 per cent., and this in conjunction with a chromium content of about 60 per cent., the production of a 12-per cent. chromium steel with less than 0.25 to 0.30 per cent. carbon was impossible. The advent, on a reasonable commercial scale, of carbonless ferrochromium has modified this condition, however, so that for the last three years stainless material containing 0.1 per cent. or less carbon and the normal amount of chromium has been on the market. As far as the author is aware, the material was first made on a commercial scale by the firm with which he is associated in June, 1920, when a 5- or 6-ton cast of material containing 0.07 per cent. carbon and 11.7 per cent. chromium was made and cast into 12-in. ingots. The necessity for using a totally different raw material, carbonless ferrochromium, instead of the ordinary low-carbon ferro (0.6 to 1.0 per cent. carbon) has led to the idea that stainless iron is a quite distinct product and quite different from stainless steel. While this may be true from a commercial aspect, it is wrong metallurgically. The name stainless iron is unfortunate as the material is a very mild stainless steel and forms the lowest carbon member of a series of steels of continuously varying content which are, in many respccts, the counterpart of the series of ordinary carbon steels ranging from "dead soft" to tool steels. In an article on stainless steel in the Journal of the Society of Chemical Industry, November, 1920, the author said "Just as in the far-off days 'steel' was regarded as a hard product of iron, and little or no attempt was made to grade it into harder or softer varieties, so at present stainless

Jan 1, 1924

By G. Ansel, J. P. Doan

THE important literature concerning zirconium in magnesium-base alloys is predominantly contained in patent references. Sauerwald, Eisenreich, and Holub1-4 discovered the profound grain-refining influence of small amounts of zirconium on cast magnesium and the attendant increases in strength, and ductility. They extended their work to reveal that limited amounts of certain other elements, including zinc, could be added for further improvement in strength and hardness. British. Patent 5111376 relates to the parent discoveries of Sauerwald, Eisen¬reich, and Holub. All of these references deal primarily with casting characteristics and properties in the cast state. Minor mention is made of desirable tensile strength, ductility, and toughness of wrought Mg-Zr alloys* modified by one or more additional elements. No extensive reference in the literature" has been found to the particular characteristics of wrought Mg-Zn-Zr alloys, with which the present paper is concerned. - The work to be discussed represents essentially an extrusion study of the Mg-Zn-Zr alloys and indicates that this system is highly interesting in the wrought state both academically and commercially. Accordingly, an important aim of this paper is to describe the hot-workability, tension and compression properties, metal¬lography, and toughness of these alloys. Compositional variations are limited to the ranges o to 7 per cent Zn and o to I per cent Zr. EXPERIMENTAL PROCEDURE Alloying and Casting Alloying ingredients were cell mag¬nesium, commercial zinc (intermediate grade), and a chloride salt containing approximately 50 per cent ZrCl2 and 50 per cent alkali chlorides. This salt is produced by Titanium Alloy Manu¬facturing Company. Melting, alloying, and pouring procedure essentially followed the crucible process as described by Nelson.6 The magnesium was melted using Dow No. 310 flux, and the temperature raised to 1350° to 1400°F for the alloying operations. After alloying of the zinc, the zirconium containing salt was added in small portions with vigorous stirring. This is an adaptation of the method described in British Patent 533264.7 The alloying efficiency of zir¬conium was approximately 30 per cent. During the alloying of zirconium, fluorspar was added in amount required as a flux¬inspissating agent. Next the melt was refined with Dow No. 310 flux and held quietly for 15 min. Finally billets were cast in a book-type permanent mold

Jan 1, 1946

By Charles L. Mantell, George Ferment

This investigation determined the jeasibility of current-potential curves as an analytical tool for monitoving manganese electroicinning solutions for metallic impurities. Nine metallic impurities were studied: trickel, cobalt, silver, copper, zinc, molybdenum, catlmiun magnesium, and sodium. The individual effect of each metallic irzplrl,iLy on the standard point-izatiorr was determined for a range of 'concentration. Not all of Ihe impurities affected the polarization curve; correlation between transition current and cotrcetztration of impurity. Molybdenum had an uncorrelated effect on the polarization curie. The effects of binary mixtures of impurities were studied to see if the transition current of the mixture could be predicted. Interactions occurred between impurities which prei'etzted the pvecliction the transition current of tile rrlisLitr.e by additive laws. The polarization curve was shown to be sensitive to metallic impurities which affect the current efficiency of a manganese cell. THE application of current-potential curves in manganese electrowinning is not new but played an important part in the conversion of an inoperative large-scale pilot plant into a continuous comnercial operation.1"" The effects of trace metallic impurities in manganese electrowinning solutions on cathode current-potential curves,5-19 specifically nine impurities (nickel, cobalt, silver, copper, zinc, molybdenum, cadmium, magnesium, and sodium) were studied for a range of concentrations. Cadmium, magnesium, and sodium had no effect. Nickel, cobalt, silver, copper, and zinc yielded a correlation between transition current and concentration of impurity: molybdenum had an uncorrelated effect. Binary mixtures of impurities were studied to de-termine if the transition current could be predicted from the values for the individual constituents. Interactions between impurities prevented the prediction of the transition current of the mixtures by an additive law. The polarization curve was shown to be sensitive to metallic impurities which affected the rurrent efficiency of a manganese cell. The electrowinning of manganese relies upon maintaining a high-purity electrolyte. Purification schemes were developed to remove all of the heavy metals, the magnesium and calcium. Concentration limits have been established for single impurities. With high-purity electrolytes, favorable cell efficiencies are consistently obtained; but with impure solutions there is a reduction in efficiency. With the rapid rise to commercial prominence of electrochemical processes, there has been a lag in developing rapid methods for determining whether an electrolyte is sufficiently pure for efficient electrolysis. The most sensitive test for impurities is the behavior of the electrochemical cell. Impure electrolytes will cause a serious reduction in cell efficiency, and in many cases metal deposition will be prevented or reversed. The effects of impurities are not usually evident until after long periods of electrolysis, resulting in a disruption of the process. A method which could predict the behavior of an electrolyte in terms of cell efficiency prior to reaching the commercial cell is needed. Van Arsdale and Maier," Allmand and Campbell,a1'22 and others attempted to develop an electrochemical process for manganese,"3"29 but all met with some degree of difficulty. Jacobs et a studied the effects of metallic impurities in manganese electrowinning. Plant methods were based on a 2-hr plating in a small electrolytic cell. The final method was based on a 24-hr plating run, performed in a relatively large test cell. Here, current efficiencies were calculated with and without impurities in the electrolyte, and the critical concentration was established as the maximum amount of impurity that the electrolyte could tolerate before there was a serious loss in efficiency. The amount of impurity that could be tolerated decreased as the plating time increased, indicating deposition of the impurity. This test duplicated the conditions of commercial practire, and was sensitive to impurities. Small amounts of impurities significantly affect the hydrogen overvoltage at a metal surface, increasing or decreasing it depending upon the nature of the impurity. ockris established the limit for the onset of poisoning at 10-l moles per liter. The effects of impurities were studied by potential-time curves at a constant current density. The technique did not lend itself to rapid analysis in that several hours were needed to establish stable potential-time curves. Serfass and coworkers3' developed calorimetric and spectrophotometric techniques for analyzing for trace impurities. Our method4'" is based on current-cathode potential curves produced by continuously changing the cell voltage at a programmed rate. Starting with a clean stainless-steel cathode, the cell voltage was initially adjusted to yield zero current: the program was then started and the current was plotted as a function of the cathode potential. Fig. 1 is a typical current-potential curve. In initial region A the hydrogen-evolution reaction predominates and the polarization curve

Jan 1, 1967

By M. A. Hosmer, Job Goostray, R. F. Harringon

In this paper, as in so many discussions of an historical nature, there is little chance for original material and much has had to be rewritten from older papers, documents, accounts, reports, and the like, some of which are of doubtful authorship or contain conflicting statistics. Fully aware of these pitfalls, the authors have tried to quote the origin where possible, and also to seek further confirmation when the statement warranted it, but they cannot assume responsibility for certain facts and dates. The Encyclopedia Britannica was frequently consulted. The authors wish to acknowledge assistance from Mackintosh-Hemp-hill Co. (formerly the Fort Pitt Works) and also from officials of the Watertown Arsenal who loaned valuable books and gave much necessary information. They are particularly indebted to Colonel Dickson of that institution. The data on modern guns were furnished by Mr. F. Brauer of the Watertown Arsenal; Mr. H. S. Chaffee assisted by obtaining records and data of work carried on by the Builders' Iron Foundry of Providence, R. I. Three Epochs in History of Cannon Among the great industries of New England, the manufacture of iron was the first to receive attention. Iron ore in considerable quantities was known to exist within the territory of the Massachusetts Bay Colony; and as early as 1629 some steps appear to have been taken toward the manufacture of iron by the Court of Assistants in London, under whose patronage the colony was founded. During the next ten years, deposits of bog ore were found in numerous ponds in the Plymouth Colony; and, in 1652, iron manufacture was begun at Raynham. The "Old Colony" was known as the main seat of this industry in New England, out of which grew a concern which was later to become one of the principal

Jan 1, 1925

By John H. G. Monypenny

The range of chromium content of stainless steel is, in most cases, included in the limits 11 to 14 per cent., or the middle part of the range, 9 to 16 per cent., specified by the discoverer. For some time after the steel was produced commercially, the carbon content was about 0.3 to 0.4 per cent. and occasionally higher; only rarely was material with 0.25 per cent. carbon or less produced. The reason for this is obvious from the nature of the alloys of chromium available for making such steels; as the lowest carbon content generally available was about 1 per cent., and this in conjunction with a chromium content of about 60 per cent., the production of a 12-per cent. chromium steel with less than 0.25 to 0.30 per cent. carbon was impossible. The advent, on a reasonable commercial scale, of carbonless ferrochromium has modified this condition, however, so that for the last three years stainless material containing 0.1 per cent. or less carbon and the normal amount of chromium has been on the market. As far as the author is aware, the material was first made on a commercial scale by the firm with which he is associated in June, 1920, when a 5- or 6-ton cast of material containing 0.07 per cent. carbon and 11.7 per cent. chromium was made and cast into 12-in. ingots. The necessity for using a totally different raw material, carbonless ferrochromium, instead of the ordinary low-carbon ferro (0.6 to 1.0 per cent. carbon) has led to the idea that stainless iron is a quite distinct product and quite different from stainless steel. While this may be true from a commercial aspect, it is wrong metallurgically. The name stainless iron is unfortunate as the material is a very mild stainless steel and forms the lowest carbon member of a series of steels of continuously varying content which are, in many respccts, the counterpart of the series of ordinary carbon steels ranging from "dead soft" to tool steels. In an article on stainless steel in the Journal of the Society of Chemical Industry, November, 1920, the author said "Just as in the far-off days 'steel' was regarded as a hard product of iron, and little or no attempt was made to grade it into harder or softer varieties, so at present stainless

Jan 1, 1924

By A. C. Heath, E. H. Dix

The importance of aluminum-silicon alloys in thc light alloy field is now generally recognized. Where silicon was once considered detrimental to the properties of aluminum, useful alloys now contain as much as 13 per cent. Furthermore, silicon is present as an impurity in aluminum of even the purest grades. Iron is another important impurity in aluminum and likc silicon is found in small quantities in the purest aluminum available today. The manner of occurrence of iron and silicon in commercially pure aluminum and many of its alloys exerts a very pronounced influence upon their properties. The effect of large quantities of iron in aluminum-silicon alloys is so detrimental that it has been found necessary to limit the allowable maximum percentage to as low a figure as is consistent with quantity production and satisfactory physical properties. The intimate relation existing between iron and silicon in aluminurn and alurninum alloys makes necessary a more complete knowledge of this ternary system. This paper is divided into two principal parts, dealing respectively with aluminum-silicon solubility equilibria and the constitution of aluminum-iron-silicon alloys. Part I.—Aluminum-silicon Alloys The early work on this system was largely confined to determining the general form of thc diagram and in this respect the results are in good agreement. Briefly, alulninunl and silicon form a simple eutectifcrous series without compounds. Until recently the solid solubility of silicon in aluminum had not been accurately determined. Ipraenkell (1908) stated that aluminum will retain 0.5 per cent. silicon in solid solu-t'ion. Rosenhain, Archbutt and Hanson2 gave the maximum solubility as about 1.50 per cent. and added that "this solubility docs not appear

By Carl Benedicks

IT is well known by every one who has had to deal with boiler tubes that these are often seriously affected by a sort of corrosion, occurring as a local pitting, that frequently causes a perforation of the tube in a rather short time. The characteristic appearance of this corrosion is shown in Fig. 1. A very similar corrosion occurs in condenser tubes (Fig. 2).1 A study of the microstructure or local chemical composition of the metal (iron; 70 :30 brass) fails to reveal any cause for this pitting. Of course one might possibly assume the starting point-to be some oxide particle, causing an electrolytic local action, but this in no way explains the continued corrosion, progressing even when the assumed oxide particle must have disappeared. By the excellent work done by the Corrosion Research Committee of the Institute of Metals, and communicated, in October, 1923, to the Institution of Engineers and Shipbuilders in Newcastle-on-tyne, stress was laid on the fact that a content of entangled air has a very obnoxious effect. In the following correspondence, Sir George Goodwin stated that "engineers have, for a long time past, regarded air as the big enemy to be fought against in all questions of corrosion"2 and Kenneth Fraser pointed out that the most vital point is "the avoidance or removal of possibly the chief cause of present day corrosion, i. e. entrapped air and gases brought out of solution."' In their reply, however, the authors state that they had "never for a moment believed that entangled air was responsible for the beginnings of corrosion, and express the opinion that the gradual liberation of air could not account for localized corrosion."4 On consulting the many textbooks on corrosion, as that

Jan 4, 1925

By T. G. Digges, C. L. Vold, M. R. Achter

A study was made of the effect of the growth conditions on the perfection of single crystals of niobium (columbium). Dislocation densities, determined by means of double-crystal diffractometer measurements , were not greatly affected by the method of crystal preparation but could be reduced by annealing treatments. However, the size, sharpness, and tilt angles of the substructures, observed with X-ray reflection macrograph, were sensitive to variations in growth procedures as well as to subsequent thermal treatments. Although the dislocation density was the same in both types, there were more low-angle bound-aries in crystals grown by zone melting than in those prepared by strain anneal. Mechanisms to account for these observations are discussed in terms of dislocation movements. A planned study of the structure-sensitive properties of refractory metals required the use of single crystals of a high degree of structural perfection and, for ease of handling, of large cross section. It appeared that the strain-anneal technique could satisfy both of these requirements. First, crystals grown in the solid state have been reported to be more perfect than those obtained from the melt.' Second, the diameters of rods which may be produced by zone melting should have a theoretical limit determined by specific gravity, thermal conductivity, and surface tension, while the diameter of strain-annealed rods is limited only by practical considerations. Previously it was shown that niobium (columbium) single crystals of 1 in. diam2 may be grown by strain anneal, compared to the 0.5 in. maximum diameter achieved by zone melting, as reported for molybdenum by Belk.3 The current research was undertaken to investigate and optimize the effect of various process variables on the perfection of 1/4 and 1/2-in.-diam niobium single crystals grown by strain annealing and to compare their perfection to those grown by zone melting. Characterization of these crystals was more conveniently accomplished by means of X-ray than by metallo-graphic techniques. EXPERIMENTAL PROCEDURE Specimen Preparation. Zone-melted crystals of 1/4 in. diam were produced by the standard electron-beam zone-melting technique. The swaged and cleaned rods were outgassed, in the solid state at a temperature near its melting point, at a rate of 12 in. per hr, and single crystals were grown by making two molten passes at 2 in. per hr. By maintaining a zone length of 4 to % in., very uniform single crystals several inches long were obtained. For the strain-annealed crystals, an induction heater was used, in preference to other types of heating, to take advantage of the good penetration of large sections. A five-turn coil, 1 in. long, operating at 10 kc and powered by a motor generator, was contained in a vacuum chamber. The rod, suspended from the upper end, was raised through the coil for both recrystallization and crystal growth. In preliminary work single crystals of the same material were also grown with single and multiturn coils powered by a 450-kc generator. A vacuum of 2 X 10-6 Torr was maintained at temperatures up to 2400°C. Starting with electron-beam-melted ingots of 21/2 in. diam, the analysis for which is given in Table I, the material was cold-swaged to the desired cross section of 1/4 and 1/2 in. diam and then recrystallized. The rods were then strained in a tensile machine and converted to single crystals by passing through the induction coil. As with zone melting, control of orientation is possible by the use of special procedures. Other investigators, see for example Williamson and smallman,4 have reported that orientation control may be achieved by a bending technique. In the present work the strained rod is partially lowered through the coil to start the growth of the crystal. Then it is removed and bent at a point in the poly crystalline portion. Finally, it is returned to the chamber and growth is continued "around the corner". This procedure has certain limitations. If the bending operation exceeds the critical strain, recrystallization may take place. Also, the amount of bending which can be imparted to the rod is limited by coil geometry, and up to now has been 10 deg. However, by repeating the bending and growing operations it should be possible to attain any desired orientation. In preparation for X-ray examination, single crystals were sectioned and planed by means of the spark-erosion technique. To obtain the maximum reflected intensity, the (110) plane was exposed for examination. They were then etched 3 to 5 min in a mixture of con-

Jan 1, 1967

By A. B. Parsons

NOT every organization on reaching the relatively ripe age of three score and fifteen can say with truth that its purpose and objects remain precisely the same as prescribed by its founding fathers. Of course, constancy of purpose may be something else than unalloyed virtue. It could merely reflect slavish worship of tradition, intellectual stagnation, or sheer inertia. On the other hand, it could establish the fact that the founders were men possessed of broad outlook, of prophetic vision, and of an acute sense of direction. In addition to charting the course with precision, the founders of the A.I.M.E. surely showed a flair for expressing clearly in a few words what others might say obscurely in many words. To quote verbatim from the "call" for the meeting, in 1871, the proposed organization was to have: "two great objectives: "First, the more economical production of the useful minerals and metals. "Second, the greater safety and welfare of those employed in these industries." This text underwent some refining on several subsequent occasions but today the ultimate product, as set forth in the Constitution reads: "to promote the arts and sciences connected with the economic production of the useful minerals and metals and the welfare of those employed in these industries by all lawful means." The original call was dated "Wilkes-Barre, Pa., April, 1871," and was signed by Eckley B. Coxe, of Jeddo, and by R. P. Rothwell and Martin Coryell, both of Wilkes-Barre, each of the three subscribing himself as "mining engineer." The authors proceeded to explain briefly just how it was proposed to achieve these objectives: "In European countries, where the arts of mining and metallurgy have long been the subject of the most careful study, no means have been found so effectual in attaining the end above proposed, as the free interchange of experience among those actually engaged in these industries; and this object has been accomplished mainly through the medium of `Institutes,' `Associations,' or `Societies,' composed of those engaged in these occupations, and by the periodical publication of `essays' or `papers' communicated to such societies by their members. "It must be evident to all practical men that the interchange of the varied experience

Jan 1, 1947

W. 0. HOTCHKISS, * Madison, Wis.-It was fortunate, in a way, that this subject of income taxation came up during the war when the government could appeal, on the basis of patriotism, to men of large, business experience to undertake the work of formulating this matter and practically donate their services. At any other time the government would have been unable to secure the necessary number of men of like ability. There is one thing that must not be forgotten. In all cases, except the very largest and most important, the application of this income tax law to a mine is going to be made by clerks whose salaries are fixed by a Congress that appropriated a half billion of dollars for a war purpose and provided that $4000 should be the highest salary paid in the adminis-tration of that great sum. The Congress of the United States unfor-tunately seems almost entirely unaware of the fact that men of ability and experience are worth money and must be paid adequately if proper public service is to be secured. While the formulation of the broad plans for administering the law have been in the hands of. men of unusual ability, we have the future to guard, and, if possible, the mining industry should see to it that the Internal Revenue Department is permitted by Congress to pay salaries that will enable it to secure men of the ability and experience necessary to insure proper consideration of the industry. Another fact to which I would call attention is the difference between the business and the economic, or economists', points of view as to what a mine is. The economists have properly, from their point of view, classed a mine as a wasting asset, but the average metal mine is not a wasting asset if it is a real mine. The economists are correct in a broad sense in that every ton of ore taken out diminishes the orebody by that amount. When it comes to the consideration of an individual mine from the business standpoint, the future of that mine rests on unfore-seeable events-the discovery of new orebodies or the development of old bodies beyond the point of probable expectations. Every going mine must develop new ore each year to replace that extracted, and, .during all but the last one or two years of its activity, actually does so. Instead of being a "wasting asset" such a mine, from the practical stand-point which must control valuation, is an "increasing asset." From

Jan 12, 1919