By H. W. Russell, H Pray, Paul D. MILLER

It is known that austenitic chromium-nickel steels that have free carbide in the grain boundaries are subject to intergranu-lar corrosion. It is difficult to detect such a susceptible condition in a fabricated article because present test methods require a sample section for examination and in most cases this is difficult to obtain. The question of the nature and prevention of intergranular corrosion in austenitic stainless steels has been ably discussed by Bain and co-workers1-3 and by other investigator4-10 The present methods of study subject samples to corrosive conditions in such reagents as the Strauss solution, a mixture of copper sulphate and sulphuric acid. Such tests usually require at least 72 hr. to run. Various methods of measuring the degree of sensitization have been employed, such as the measurement of electrical resistivity, magnetic measuremerits, measurement of the degree of cracking produced on bending over a malldrel, and microscopic studies. The detection of carbides at the grain boundaries by metallographic polishing and etching methods is tedious and requires a skilled operator. A recent report on such methods of carbide detection is given by the American Society for Testing Materials Subcommittee VI of Committee A.-1011 and by Arness.12 The present investigation was undertaken to develop a simple test procedure for detecting carbide precipitation or susceptibility to intergranular corrosion. The test is designed for use in the plant and for the testing of fabricated structures. Carbide precipitation, the factor leading to susceptibility to corrosion, is produced by heating the alloy in the temperature range 800° to 1600°F., as in welding, in improper annealing or in service where such temperatures are met. The connection between such precipitation and susceptibility to corrosion has been thoroughly discussed, as has been the use of stabilizing addition elements to prevent precipitation. Experimental Method A small area of the steel under test is subjected to an anodic treatment in a cell that can be 'lamped Onto a a Or an actual structure. The cell and electrical circuit used are illustrated in Fig. I. The cell C is lead, joined to the steel plate D and insulated from it by a short piece of rubber tubing E. The cell is forced tightly against the steel plate by a spring Or clamping device. The seal formed by the rubber against the steel plate is sufficient to retain the liquid bath inside the cell. The spot treated can be made any shape desired, depending on the shape of the rubber gasket. The cell illustrated polishes a circular spot about 3/8- diameter' The bath consists of 60 per cent (by weight) sulphuric acid to which is added 5 ml. per liter of Glycyrrhiza extract (U.S.P.). The cell requires about 2 to 2.5

Jan 1, 1941

By Wilbur H. Somerton

In order to evaluate the quantitative determination of porosity by various neutron logging systems, four test wells were constructed to simulate some of the possible variab1e.r found in field logging conditions. All of the test holes contain sections of limestone with one section of sandstone included in one well. Each well has a representative section of high, medium, and low porosity. Three borehole sizes are represented by three of the test wells, all containing fresh water. One test well contains saturated brine. Statistical and tune constant checks are made for each system evaluated. Runs and repeat runs are made with the sonde centered and eccentric. Factors evaluated are the effect of borehole size, sonde position, salinity, chemical composition of rock, and statistical variation. A semi-quantitative method of evaluation of these effects is used giving the average maximum per cent error possible for each. Drift and calibration procedures are also discussed. The effect of the various factors appears to be largely a function of the phenomena detected as well as the means of detection. Graphic illustrations of some of these effects are presented. It is concluded, that for accurate log interpretation, the hole size and sonde position should be known. INTRODUCTION The use of neutron logs for the derivation of porosity has become an accepted practice in many areas. In recent years, many different neutron logging systems have been offered to the industry. The neutron sources presently available are of the radium-beryllium or polonium -beryllium type. Detector types used are ionization chambers, Geiger-Mueller-type counters, proportional counters, or scintillation detectors used to detect or measure gamma rays, thermal neutrons, epithermal neutrons, fast neutrons or combinations of these. It is well-known that all systems do not respond alike in all environments. As a result, testing facilities and an evaluation method were developed for use in evaluating the porosity discriminating ability of neutron logging systems using conditions simulating those normally encountered in the field. With such an evaluation, the suitability of a logging system can be determined lor selected field conditions. TEST FACILITIES The testing facilities consist of wells containing rocks of various porosities, constructed to include as many parameters as practicable. Three pits were drilled to a depth of 20 ft and the fourth to a depth of 9 ft, all having 48-in. diameters. Rat holes were dug to a depth of 6 ft in the center of each pit and fitted with sections of pipe having appropriate diameters. The top of this pipe was located approximately 8 in. above the pit bottom. A 6-in, layer of cement was then poured on the bottom and while still wet, 42-in. OD corrugated, galvanized culvert pipe was set on bottom and centered in place. This pipe extends approximately 1 ft above the surface of the ground. The annulus around the culvert pipe was then filled with cement to the top. A 1- or 2-in. layer of sand was placed on the cement bottom to provide an adjustable bed on which to place the series of rocks set in each hole. A cross section of a typical test well containing the porous rocks is shown in Fig. 1.

By N. P. Goss

Asterism appearing in X-ray Laue diagrams is an extremely sensitive index of changes in the internal structures of individual grains of polycrystalline metals. It indicates the existence of various forms of subboundary structure or subdivision within the grain. The present viewpoint is that the grain is made up of lattice blocks having substantially the same size and shape.l-4 When these blocks all assume exactly the same orientation, the crystal is perfect and asterism is absent. Cleaves and Thompson5 observed that the hardness of iron is virtually constant over a range of grain sizes. It is quite possible that the subboundary structure caused this, and that the latter is just as important as grain size itself. While the experiments reported here are not conclusive, they do support this viewpoint. Metals can, under certain conditions, be prepared entirely free from asterism, but this preparation does not necessarily require long heating or slow cooling, as will be shown here. In this paper a distinction is made between mosaic and distorted grain structures but the difference is only a matter of degree. In a previous paper9 it was shown that the grains can become distorted even during heat-treatment. The block structure exists inherently, even in a perfect crystal; the size and shape of these crystallites, or lattice blocks, varies, depending upon a number of factors. Goetz, for example: has shown that a metal before crystallizing from the molten state must go through a paracrystalline phase with oriented groups of atoms about 10-l4 to 10-l5 c.c., or 10-15 cm. in size. These crystallites, or blocks, appear to survive the most drastic cold-working, for it has been shown, and more elaborately by Wood's recent work," that cold-working cannot reduce the size of these crystallites smaller than of the order 10-5 cm. The interesting correlation brought out by the experiments of Goetz and Wood is that the block size after severe cold-working is of the same order of magnitude as the groups that formed in the metal just before crystallizing from the molten state. The work of Ewald and Rennenger17 and the now classical experiments of Darwin and James12,13 all strongly suggest the existence of a periodic structure of crystal. lites smaller than the grain itself. Related to this effect is the appearance of veinlike markings in the microstructures. Ammer-man and Kornfeld,16 in their experiments, did not observe any evidence of veining in specimens of alpha iron annealed below A3 and believed that veining was not due to impurities in the iron, as Northcott16 suggested; veining was observed by them only in specimens annealed above A3. Hanemann,16 Schrader and Tangerding found that annealing in hydrogen did not diminish veining and so it could not be caused by oxides. They concluded that veining was due to a slight difference in the orientation of ferrite lattice blocks. This viewpoint is well supported by the evidence presented here.

Jan 1, 1941

By J. Weertman

It is shown that conditions suitable for the conversion of straight dislocations into helices are common in crystals hardened either through long-range dislocation interaction or by jog formation on dislocation lines. For dislocations other than screw dislocations or dislocations nearly screw in orientation, helices can be formed with the aid of core difhsion at temperatures low relative to the melting point of the material. It is assumed that, once formed, helices will degenerate into dislocation tangles. THE dislocation tangle is one major dislocation arrangement observed by the transmission electron microscope which had not been predicted previously from dislocation theory. Since first being observed, the tangle itself has become important in applied dislocation theory. The Cambridge school (P. Hirsch) bases part of its theory of work hardening upon this phenomenon.' In spite of the fact that the tangle obviously is a structure of prime importance to a cold-worked crystal, until recently relatively little attention has been paid to the question of exactly why or how tangles arise. It was generally assumed at first that cross slip and perhaps jog formation will lead to tangles. However Wilsdorf and schmitz2 concluded that cross slip cannot markedly contribute to the tangles. The Wilsdorfs and Maddin3'* have proposed that tangles arise by means of prismatic dislocation loops and superjogs which are produced by a precipitation of point defects. Dislocations with superjogs or which have joined with prismatic loops are themselves dislocation sources and they can produce new dislocations, a process they call "mushrooming", which then tangle with each other. There is no question that the Wilsdorfs et al. mechanism as well as the cross slip one can pro- duce tangles. However these may not be the only paths leading to tangle formation. In this paper we wish to consider another way tangles can form. Our work will be based on the theory of dislocation screw We wish to show that whenever a crystal is cold-worked there always is present a "driving force" leading to helix formation and thus to tangle formation. We do not expect to observe well-developed, regular helices in cold-worked metals. Rather we would expect that after a helix is formed random interactions with nearby dislocations will cause a well-developed helical dislocation to go over into an irregular form. A dislocation tangle is, of course, a grouping of dislocations with irregular forms. Therefore we feel that, in accounting for the formation of dislocation tangles, it is sufficient to show that many dislocations in a cold-worked crystal will take on helical form. The crucial step is helix formation. In order to have a straight dislocation assume a helical form, diffusion of vacancies, or interstitials, must occur. Our discussion of tangle formation therefore will be limited to crystals which have been deformed at temperatures ranging from about one fifth to half their absolute melting point. In this tem per a ture range appreciable core diffusion is possible. (There is no problem in explaining tangle formation at temperatures greater than half the melting point. At such temperatures dislocation climb through a bulk diffusion of point defects gives an extra degree of freedom to dislocation motion. This extra freedom of motion makes tangle formation easy.) At temperatures much below one fifth the absolute melting temperature diffusion processes are sufficiently slow that helix formation does not occur. Of course helix or tangle formation could occur in material deformed at very low tempera-tures which was subsequently warmed in order to make the thin specimen necessary for electron-microscope examination. Since within the temperature range of approximately one fifth to half the melting temperature the diffusion of point defects in the core of the dislocation is rapid, we can reasonably assume that within

Jan 1, 1963

By L. H. Dushak

DURING the war period of quicksilver activity there were a number of departures from what may be termed the classical quicksilver metallurgy. Attempts were made to beneficiate low-grade ores by gravity concentration and flotation; mechanical furnaces began to replace the Scott furnace and the vertical coarse-ore furnaces, and condensers of sewer tile and redwood tanks were used in place of the older brick and stone condensing chambers. Other developments that have occurred during the current period of quicksilver, activity are mainly in the nature of improvement and further refinement of those started during the war period. Each period of quicksilver activity has been accompanied by the proposal of various new processes, including wet methods for the treatment of quicksilver ores and innovations in furnaces, retorts and condenser equipment. As far as the author knows, nothing of economic significance in the way of "new processes" has been developed. There is in fact no real need for any essentially new process for the treatment of quicksilver ores; the direct furnace treatment is simple and inexpensive. Moreover, with fare exceptions, the quicksilver industry has no complex or refractory ore problems corresponding to those which are receiving more and more attention from metallurgists in other branches of the nonferrous field. Under these conditions improvements in quicksilver metallurgy must be looked for through the adaptation of current developments in engineering and metallurgy generally to the particular needs of quicksilver practice rather than through the invention of new processes.

Jan 1, 1930

By George Krauss, Seth R. Thomas

One complete cycle, allstenite to martensite to aus-tenite, of Martensitic transformation was induced in a commercial 18 Cr-8 Ni stainless steel. Transmission electron microscopy showed that the reverse transfarmation, martensite to austenite, perpetuated the dense defect substructure of the martensite produced by the direct transformation, austenite to 'martensite, and reproduced the retained austenite matrix orientation. A general precipitation of lathlike M,,C, particles was noted to be present in, and is suggested as cause for, regions of martensite that Izad formed after a complete cycle of transformation. The habit plane of the precipitate particles was found to be within 5 a plane previously established as the habit of nitride precipitates of similar morphology in bcc iron. The direct transformation of austenite (y) to martensite (a) in metastable 300 series stainless steels has received considerable attention in the past,'-8 and the martensite product given special emphasis in recent years,9"*u but little information has been published about the reverse martensitic transformation during which bcc a martensite is converted to fcc y austenite."-" The reversal mechanism and the resulting crystallographic relationship between parent and product austenite are of fundamental concern. The reversal product, fully austenitic, and hereafter referred to as reversed austenite, exhibits a defect structure far different from its virgin counterpart. Some studies have been reported in which the structure of reversed austenite in iron nickel alloys is compared to annealed austenite with respect to austenite strengtheningM and Stabilization.' The martensite in these Fe-Ni alloys, however, shows a basic difference from that produced in stainless steels. Structurally, the Fe-Ni martensite is profusely twinned," while the (low-carbon) Fe-Cr-Ni martensite contains a high density of tangled dislocations and is apparently twin-free.I0 reediis" has recently shown in an Fe-16 Cr-12 Ni stainless alloy that this typical martensitic defect structure and the reverse transformation directly influence the structure of the reversal product. He found that much of the reversed austenite had returned to the orientation of the virgin austenite and that fine twins were formed in the austenite after the reverse transformation. This investigation was undertaken in order to describe as completely as possible the structural changes produced by a cycle of transformation in a typical 18-8 stainless steel. EXPERIMENTAL PROCEDURE The 301 stainless steel under investigation (17.44 Cr, 7.75 Ni, 0.80 Mn, 0.60 Si, 0.40 Mo, 0.40 Cu, 0.08 C, 0.03 N, bal Fe)was received as 0.060-in.-thick

Jan 1, 1968

By R. A. Morgen

THE binary system lead-antimony has been the subject of compre-hensive investigations in these laboratories by Dean1 and his associates. The effect of a third constituent on this system, particularly on the lead-rich alloys in which dispersion hardening ,was found, has a commercial value as well as an academic interest. This paper covers the effect of the addition of copper, bismuth and tin, all of which are likely to be found in commercial lead-antimony alloys, and is divided into three parts, as follows: I. The System Lead-Antimony-Copper II. The System Lead-Antimony-Bismuth III. The Lead Corner of the System Lead-Antimony-Tin These three systems are of three different types, and hence may be considered as covering three general kinds of additions. Bismuth forms no compounds with either lead or antimony and forms solid solutions with both. Copper forms several compounds with antimony as well as solid solutions but with lead it forms a two liquid layer system and no appreciable solid solution. Tin is soluble in both lead and antimony in the solid state and also forms a compound with antimony. The effect of small amounts of bismuth on the lead-antimony alloys is small, having no appreciable effect on the solubility of antimony. The temperature of the solidus floor is lowered appreciably by the presence of bismuth, cutting down the range of heat treatment. Copper, on the other hand, due to compound formation, increases the apparent solubility of antimony. The excess antimony is tied up with the copper finally and so is not available for dispersion hardening. The net result of addition of small amounts of copper is to shift the dispersion hardening peak of the

Jan 1, 1927

By Carl J. McHargue

Rods of 99.99 + pct Al which had initial orientatzons of <001>, <118>, <115>, <111>, and random were swaged at room temperature. Changes in orientation as a function of deformation were studied on axis distribution charts. The <001> orientation appeared to be relatively stable due to the inhomogeneity of the deformation process. near the <100> zone were quickly reoriented towards <001>. Orientations on the <110> zone between <118> and <115> appeared to be stable to reductions of about 50 pct, then were reoriented toward <001>. At very high reductzotzs. movement away from the <111> orientation was observed. the requirement that a circular cross section be maintained. In addition to these mechanical factors, there are grain-boundary effects in poly crystalline materials which are not yet understood. Hartmann and Macherauch conclude, for example, that multiple slip occurs for all orientations in fine-grained aluminum and copper and that the choice of operative slip systems has no simple relationship to orientation.? Many investigators have attempted to avoid problems of interpretation caused by an initial texture by treating the starting material to obtain as ran- IT has been generally accepted that the deformation texture obtained at high reductions, e.g. 90 pct, will not be noticeably affected by a prior texture; whereas, that obtained at reductions of 40 to 50 pct may be significantly influenced by the specimen history.&apos; Some recent studies, however, have been interpreted as showing that an initial texture strongly influenced the deformation textures in rods at reductions greater than 90 pct. Freda and Cullity suggested that the <001> texture in a heavily cold-worked copper rod was due to a <001> texture in the original casting. McHargue, Jetter? and Ogle concluded that the <001> component in an aluminum rod extruded at liquid nitrogen temperature was remanent from a <001> texture in the cast extrusion billet.3 Most of the published work on the effect of initial orientation on deformation textures has been for cold-rolled or compressed single crystals,4-6 The primary interest in these studies was to examine various orientations with regard to their stability under flow? thus determining the possibility of such orientations being stable end orientations. There appears to be no published studies on the effect of initial orientation on fiber textures in polycrystalline specimens. A recent study, however, is concerned with the reorientation of individual grains in polycrystalline specimens pulled in tension.? Although the reorientation of single crystals loaded in simple tension is well known, the movements in the forming of wires and rods would be expected to be different due to the circular array of radial-compressive stresses exerted by the die walls or the rolls, and to

Jan 1, 1962

By Henry Lewelling

An experimental investigation of the relative effectiveness of standard bullets and "shaped charges" in perforating dense, hard formations is reported. A method is described which simulates the conditions under which a shot is normally fired. Results are evaluated on the basis of depth of penetration, extent 01 Fracturing. extent and nature of formation damage, and other physical characteristics. INTRODUCTION A study was made of the relative merits of bullets and "shaped charges&apos;&apos; as applied to well completions in hard, dense formations such as those encountered in the Permian Basin. The planning of the laboratory program stipulated that core samples should be prepared and mounted in such a way that perforation shots of either kind"" could be fired into them, keeping the factors pertinent to good shooting practice similar to what they would be in a well. The shooting was done in a buried tank. with the sample and shooting equipment covered with water. The depth of water was calculated to he sufficient to simulate the inertial effects of well fluids for the duration of an explosion (a few micro-seconds). Flow measurements were attempted on the specimens after perforation. Due to the lack of uniformity of the limestone, shale breaks. etc., these measurements proved to be of little value to the study. The mounting materials were removed. so that the character of the penetration. fracturing, etc., could be observed. METHOD Laboratory samples were selected from the hard. dolomitic sand cores from Block 31 Field. Core pieces having a 3 3/4 in. diameter and a useful length of 10 to 12 in. were used. Selection was aimed at those pieces having a minimum of shale streaks and other irregularities. The ends were cut off square Manuscript received in the Petroleum Branch office June 28, 1951. Paper presented at the Petroleum Branch Fall Meeting in Oklahoma City, Okla., Oct. 3-5, 1951. with the diamond saw. Prior to lbeing mounted. the cores were soaked in water to prevent them from absorbing water out of the wet concrete, thus weakening it. A set of steel capsules was fabricated for holding the core Samples. Seven-in. casing was cut in two-ft lengths. of which one end was closed by "orange-peeling" and welding, and the other was threaded to accept a standard bull plug. The bull plugs were fitted with copper tube connections .so that pressure could be applied when the capsules were made up. The cores were mounted in the capsules by means of wire centralizers whose function was to hold the Core in proper position while concrete was poured and set. A special aggregate was prepared wing a graded sand and gravel mixture

Jan 1, 1952

By Charles E. Mann, Douglas J. Lootens, Rufino B. Bomasang

INTRODUCTION The economy of the Philippines, like that of many other developing nations, has been severely strained by the rapid escalation of imported crude oil prices over the past decade. In an effort to reduce its dependence on imported crude, significantly increased emphasis, both in the public and private sectors, is being placed on the rapid development of Philippine coal resources. This paper is designed to present an overview of the Philippine coal industry, its historical development, present status, and future potential. COAL RESOURCES AND RESERVES In 1977, a British consulting firm collated all available data on Philippine coal resources and estimated the total coals potential at about 0.9 to 1.4 billion metric tons (mt). In 1981, using more recent data the Philippine Bureau of Energy Development (BED) estimated the potential at 1.7 billion mt. The BED estimated the proven coal reserves at 257 million mt. These coal resources are scattered throughout the major islands comprising the Philippine archipelago. However, about 52 percent of the currently proven reserves are located in the tiny island of Semirara between the islands of Mindoro and Panay. About 25 percent is located in the Cagayan Valley in northeastern Luzon while 13 percent is located in Mindanao. The remaining 10 percent is scattered in the islands of Cebu, Samar, Mindoro, Negros, Polillo, Batan, and Catanduanes. The bulk of Philippine coal is sub-bituminous in rank. Some bituminous coal with coking properties has been reported in Malangas, Zamboanga del Sur in western Mindanao, and in Catanduanes, but the exact tonnages have not been accurately established. It is believed, however, to be at most 5 million tons. A little semi-anthracite coal exists in Malangas with the remaining unmined reserves estimated at a little more than one million tons. Table 1 shows the quality ranges of Philippine coal deposits.. Figure 1 shows the distribution of known Philippine coal resources PHILIPPINE COAL PRODUCTION In 1981, total coal production was 330,720 mt. Though modest by world standards, this was the highest production figure in Philippine coal mining history. This came from 25 mines, mainly small scale underground mines of capacities varying from 10 to 100 tons per day (tpd). The actual production capability was about 800,000 mt in 1981, but the producers had to scale down production to the level of local demand. Even then, some 50,000 tons of coal remained unused by year-end. The 1981 production came from the following areas: Cebu 224,751 mt (68%) Zamboanga del Sur 57,095 mt (17%) Semirara 13,222 mt (4%) Polillo 17,132 mt (5%) Cebu has always been the main source of Philippine coal production. Coal mining has been carried out in Cebu for the last 50 years, although it has been characterized by a very crude mining technology. Due to the limited size of coal deposits and complicated geology, however, Cebu&apos;s share of the total national production is expected to go down to only 10 percent by 1985. Except for Semirara&apos;s open-pit production, the balance of Philippine coal production comes from underground mines. These underground mines generally use room-and-pillar methods, except for those at Zamboanga del Sur and Polillo which use modified longwall methods patterned after those used in Taiwan. Due to the much higher mining recovery, most underground mines are now planning on switching to longwall. At Semirara, an open pit mine is now being developed for a one million ton per year capacity by 1984, and will then be the largest Philippine coal mine. While present earthmoving work is done with bulldozers, loaders, and trucks, the main coal extraction equipment will be bucket wheel excavators imported from Austria. PRESENT COAL UTILIZATION Existing coal production is sold mainly to coal- fired cement plants and power plants. The balance is sold to a sugar central, a coconut oil mill, a food processing plant, and two plants producing carbide and ferro-silicon alloys.

Jan 1, 1982

By Walter Kauzmann

All viscous or plastic flow of incompressible matter is the result of shear strain; the changing shape of any body that is being plastically deformed can be completely described in terms of the shear strain occurring at each point in the body.† Furthermore, the relative amounts of shear strain occurring in different parts of a body under stress depend upon the relative rates of shear strain at those different points, so that if the dependence of the shear rate of any material on the temperature, shear stress, previous history, etc., were understood, the principles of plastic deformation would be known, and we could calculate how a body made of a given material, having a given shape, and subject to a specified system of forces, would change its shape with time. It may be said, then, that the problem of plasticity resolves itself into, first, the problem of the rates of pure shear processes, and second, the application of what is known about pure shear to actual cases. It is the purpose of this work to investigate the former problem —i.e., the dependence of shear rates on temperature, stress, etc.—from the standpoint of .recent developments in the field of chemical-rate theory and with particular reference to the phenomena occurring in the creep of metals and in the plastic flow of crystalline solids in general. It is left for the mechanical engineer, and perhaps the expert in hydrodynamics, to deal with the problem of app1ications.l Resolution of Macroscopic Shear into Microscopic Movements; Resemblance to Chemical Reactions Just as any large body is made up of many small units, or atoms, so macro-scopically observable shear is the result of many microscopic unit shear processes; just as the understanding of the behavior of large bodies demands the understanding of the atoms of which it is made, so the understanding of macroscopic shear demands the understanding of these fundamental unit processes. The study of shear from this "atomistic" point of view has made considerable progress. There has been fairly complete understanding of shear processes in gases for a long time, at least for non-turbulent flow, as a chapter on gaseous viscosity in any text on the kinetic theory of gases will prove&apos; In recent years Andrade2 and Eyring3 have presented important theories for the flow of liquids and amorphous solids. Becker14 Orowan,5 Taylor,6 Burgers,7 and Kanter8 have considered the plastic flow of crystalline solids from this

Jan 1, 1941

By Harry H. Angst, Reuel A. Cochrane

THE successful exploitation by opencut methods of the low-grade porphyry copper deposits is due to the economical handling of large tonnages. Large tonnages are possible only if the rock material is broken so that the large power shovels can operate with minimum delays. This is particularly true at the New Cornelia mine, where the dense, hard, tough rock material creates problems not encountered in most of the porphyry copper mines. The introduction of churn drills at the New Cornelia for primary drilling, in 1936, necessitated a complete change in the methods of breaking ground as formerly air drills had been used. The blasting operations are of particular interest because of the handling of great quantities of high explosives in safely and efficiently fragmenting the hard rock material. ROCK FORMATIONS At the New Cornelia mine the rocks are quartz monzonite with a diorite border facies intruding a rhyolitic series. Overlying these formations is a fanglomerate formation composed of boulders of monzonite, diorite, rhyolite, and other types of rock of unknown derivation. (The word "fanglomerate" is used in this paper in referring to the local conglomerate type of rock formations.) The ore body is approximately 4800 ft. long and 2800 ft. wide, and is of the disseminated type. Mineralization occurs principally the quartz monzonite and to some extent in the adjacent diorite and rhyolite. The principal ore minerals are chalcopyrite, bornite, and a small amount of chalcocite. Over a considerable area the quartz monzonite is extremely hard and siliceous in character, owing to pegmatitic zones of alteration. The hardness of the ground depends on the intensity of the silicification. In a small area in-the pit, the monzonite contains an abundance of pyrite accompanied by sericitization and is soft and easily fragmented. This is true also in the remaining oxidized portion of the ore body. The diorite and rhyolite formations, like the monzonite, vary from extremely hard to very soft material, but on the whole are easier to fragment than the monzonite. jointing is prevalent in all the rock formations and plays an important role in the blasting efficiencies. In the fanglomerate formation, numerous well-defined joints, widely spaced, tend to make the ground blocky when blasted. This is a deterrent to good fragmentation. In the other rocks the joints are more numerous and are closely spaced, except in localized areas where the formations are extremely hard. These descriptions indicate that the lowest blasting efficiency will be obtained in the harder formations, from which the major portion of the mine production is obtained; namely, the monzonite and rhyolite. All rock formations mined at the New Cornelia pit are so hard that excavation

Jan 1, 1941

By S. F. Shaw

In 1913, the Tiro General mine, at Charcas, S.L.P., Mexico, which had been making from 125 to 150 gal. of water per min., was allowed to become flooded, after all the pumps had been removed, and in 1918 the problem of unwatering it came up for solution. There are two vertical shafts, the Tiro General, 1390 ft., and the San Fernando, 1225 ft. in depth, with five connecting levels between them. The San Fernando shaft had been partly retimbered, while the Tiro General had been newly timbered from the collar to 1090 ft. in depth. It had been possible to place guides in only one compartment of the Tiro General, from the collar to the seventh or 850-ft. level, to which it was necessary to lower the water before station pumps could be installed. Soundings indicated that compartments in the Tiro General were open to 1082 and 428 ft., and in the San Fernando shaft to 471, 488, and 586 ft. The water had risen to a point 140 ft. below the collar of the Tiro General shaft.. Pumping Equipment The steam plant at the Tiro General shaft includes one 300-hp., one 150-hp. and one 100-hp. Erie City water-tube boiler, and two 160-hp. Heine water-tube boilers. All but one of these boilers were supposed to be in good shape, but it was soon discovered that six years of idleness in a climate that is foggy for several months of the year had left them in poor condition. The compressed-air plant comprises one Nordberg cross-compound compressor with piston displacement of approximately 2500 cu. ft.of free air compressed to 96 Ib. per sq. in.; and another Nordberg cross-compound with piston displacement of 1235 cu. ft. of free air, to the same pressure. The main pump station is on the seventh level where had been installed a Prescott pot-valve plunger pump with capacity of 200 gal. per min.; also a Gould triplex plunger pump with capacity of 135 gal. per min., driven by a 6 1/2 by 10 by 12 in. steam engine. From the lower levels, the water had been raised to the seventh level by small station pumps and sinking pumps.

Jan 1, 1920

By P. Hazebroek, C. S. Mathews, E. E. Allen, H. C. Lefkovits

A rigorous study was made of the behavior of reservoirs composed of horizontal layers, unconnected except at the well and filled with a compressible fluid. The report is presented in two parts. Part I deals with the practical implications of the results obtained; Part 11 contains the mathematical derivation of the solution. The main portion of Part I is concerned with application of the results to reservoirs composed of two layers. Relative rates of depletion of the layers are studied, and it is shown that differential depletion between layers exists in the transient stage of the reservoir, which generally is of an order of magnitude longer than the transient stage in a single-layer reservoir. In the transient stage, the more permeable layer is depleted faster than the less permeable. However, the reservoir approaches a steady-state situation where both layers contribute equally to production. Theoretical build-up curves from such reservoirs are presented, and the influence of a skin effect and flow into casing and tubing are also evaluated. The build-up curves are predicted to have, first, the familiar logarithmic straight-line section and, subsequently, a rising and flattened section. The results found are compared with an extension of an approximate theory, and it is found that this simplified theory is applicable over most of the life of the reservoir. Extensions to reservoirs containing more than two layers are indicated, and examples of the performance and build-up curves for three-layered reservoirs are presented. The theoretical results on build-up curves were applied to field examples of such reservoirs, and satisfactory results were obtained. From the build-up curve, the pemeability-thickness product, the wellbore damage and the static pressure are obtained. However, it apparently is not possible to determine the properties of the individual layers from the combined build-up curve. A large number of reservoirs have been found where the producing formation is composed of two or more layers of differing physical characteristics, such as permeability and porosity, and where also the thicknesses of the layers differ. Since in general a differential depletion should exist between the layers of such reservoirs, it would be advantageous to know the amount of the differential depletion under a given production history. It also would be valuable to know the pressure behavior, because it could be undesirable to produce a reservoir in such a manner that the pressure in one of the layers would have fallen below the bubble point of the oil at a time when another layer might still be virtually undepleted. The determination of static pressures in shut-in wells with slow build-up is another feature of importance in layered reservoirs. If the behavior of the reservoir differs appreciably from the predicted behavior of a single-layer reservoir, the type of analysis for build-up curves suggested for single-layer reservoirs is not applicable. Several authors have treated the problem of finding the pressure and production characteristics of multilayer reservoirs. Horner treated the problem of n layers in an infinite field, the layers being connected only at the well. Tempelaar-Lietz2 has presented an approximate treatment of the characteristics of a bounded reservoir composed of two layers of different permeabilities and equal thicknesses. Homer gave no information on differential depletion between layers, and the treatment of Tempelaar-Lietz was not applicable for prediction of pressure build-up behavior. In addition, it was thought that a more rigorous treatment than the one by Tempelaar-Lietz would be valuable in determining the range of validity of this solution. The present study, therefore, was made of a bounded reservoir composed of two or more layers,

By S. Le Fevre

The application of electricity to the mining and beneficiation of the magnetic iron ores of the Mineville, N. Y., district, on Lake Champlain, has resulted,in economies and enhanced quality of product, without which only a comparatively small quantity of the present output could be marketed. The output of the Witherbee, Sherman & Co. mines is about 700,000 tons per annum, and of this about four-fifths is treated by magnetic separation to increase the iron content and reduce the phosphorus. The use of electricity for the magnetic separation of the ore from the gangue is therefore of primary importance, and makes possible the application of electric power for mining and preparing the ore for concentration. The fact which speaks loudest in favor of the application of electricity is this: It is possible for about 25c. per ton of shipping ore to furnish all the power required to put the ore on cars. This includes mining a hard ore underground, from a depth of 900 ft., hoisting to surface, crushing to $ or 8 in. in size, and separating from the gangue. This also includes lights about the works, and all miscellaneous power, such as about the shops. The first plant for the generation of electric power for use at Mineville was completed in 1903, and was one of the first for the application of electricity to mining iron ore. This was a Nordberg compound condensing steam engine, direct connected to a 750-kw. alternating-current generator, 3,300 volts, 3 phase, 25 cycles. All the plants added later use the same current but with higher voltage. The map, Fig. 1, shows the power plants and the transmission system; Figs. 2 and 3 are views of the shaft houses and the mills. The power from the first plant was distributed to Mills 1 and 2, one 2,500 cu. ft. compressor, and to the Harmony hoist, which was driven by a 300-h.p. motor operating four 10-ft. drums. Our experience with the hoist covers largely the development of electric hoisting from 1903 to date, and in some cases improvements were worked out to satisfy our needs. The motor is still operating as installed, but the control apparatus has been radically changed several times. When installed, the iron re-

Jan 1, 1915

By R. L. Loofbourow

Trends in the metal mining industry were definitely down in 1954. With a record in 1953 of $1.8 billion output, the last year dropped to $1.5 billion, the lowest value since 1950. The decrease in iron ore production alone accounted for at least 10 pct of the decline. PROBABLY more than any previous year, political debates of 1954 marked a new high for the mining industry. Lead and zinc prices gave forth with minor rallies producing no real improvements. An anticipated drop in copper prices never came to be. Early in the year arguments for more free trade versus tariffs to restrict imports were voiced eloquently by Charles P. Taft, president, Committee for a National Trade Policy, and Andrew Fletcher, president, St. Joseph Lead Co.

Jan 3, 1955

By S. K. Tarby, W. O. Philbrook

Limited experimental data and a critical review of the literature are given to indicate that the true equilibrium distribution of manganese between carbon-saturated iron and blast-furnace type slags has not yet been satisfactorily established as a function of the composition, temperature, and pressure of the system. THE distribution of manganese between carbon-saturated iron and blast-furnace type slags has been studied by a number of investigators.1-7 Generalization of the results of these works indicates that the weight percent distribution ratio, (%Mno)/[%Mn], decreases with increasing temperature and slag basicity, in accord with thermodynamic data and practical observation. However, where comparisons among these studies can be made for similar slag compositions and temperatures, the reported values of the manganese distribution ratio are discordant. The variations are attributed to failure of the experimenters to bring their systems completely to equilibrium with graphite and CO at 1 atm, as judged by departures from silicon equilibrium. Even in the most recent work,5-7 this problem was recognized but the authors made the questionable assumption that equilibrium could prevail for manganese distribution even though other reactions were still in progress. Manganese equilibrium values for three particular slag compositions were required incidental to a kinetic study8 and were determined experimentally. Special pains were taken to approach concurrent equilibrium with respect to silicon. Although the results were not completely definitive, they indicate that the true manganese equilibrium distribution ratios are lower than have heretofore been reported. The data are presented together with a brief commentary on the literature to suggest the need for further work in this area. EXPERIMENTAL METHOD Equilibrium runs were carried out in a stationary, induction-heated graphite crucible closed by a graphite lid and flushed continuously by a slow flow of carbon monoxide at 1 atm pressure. Temperature was controlled manually within ±3 deg C with the aid of immersed thermocouples in mullite tubes protected against slag attack by graphite sleeves. The desired temperature was established by a calibrated Pt vs Pt-10 pct Rh thermocouple and control was then maintained using a more stable W-Mo couple. Runs were made at 1500º and 1575ºC for durations of 7.5 to 10.5 hr. The charges were calculated to yield 400 g of metal and 100 g of slag. The primary slag compositions and designation numbers were as follows:

Jan 1, 1963

By G. Derge, W. Peifer, J. H. Richards

A WIDE Variety of metallurgical defects in steel have commonly been attributed to the presence of excessive amounts of hydrogen. These defects include flakes in rails and forgings, cracks in welds, and blisters in enameled ware, They have been related to hydrogen largely by circumstantiat evidence because the proper sampling and analysis of steel for hydrogen has been known to be difficult and because no general agreement has existed with regard to the relative suitability and accuracy of available methods. The need for a direct approach to these problems has been widely recognized. This general situation has been well described in the publications of the British committee on the Heterogeneity of Steel Ingots,&apos; and current approaches to the problem were reviewed in a recent symposium of the AIME.I2 The plans described by the present authors at that meeting have now matured satisfactorily and will form the basis of this paper. The principal object of this paper will be to describe the methods of sampling and analysis which have been developed and to illustrate the usefulness and limitations of these methods by citing their application to a specific problem, The first problem selected for investigation was the behavior of hydrogen in rail steel. This was chosen because the occurrence of shatter cracks in rails has received a great deal of study over a long period of time. The defect can be controlled by the expensive procedure of slow in However, it may be hoped that a better understanding of the factors influencing the hydrogen content of rails will lead to a more efficient control of this problem. Rails provide a good starting point for a more general study of hydrogen in steel because they provide a cross-section large enough to develop cracks, Yet small enough for convenient handling and sampling. Rails were also selected because they arc made from plain carbon steel and it was felt that the initial work should not be complicated by the effects introduced by alloying elements. The considerations which determined the original planning of this study should be reviewed. The inherently complex nature of most hydrogen problems requires that a large amount of data must be collected for any particular case. This in turn means that any analytical procedure should be as rapid and simple as possible. The same objective of speed is indicated by the fact that it may finally become desirable to use hydrogen analysis in process control. It is also known that hydrogen is highly fugitive and that any procedure which facilitat~s early analysis of the sample without prolonged or irregular storage has distinct advantages. The most important previously reported methods of analysis may be classified into three general groups: (I) Vacuum fusion, (2) Vacuum extraction (without melting), (3) Total combustion.

Jan 1, 1949

By T. B. Counselman

PROBABLY the earliest concentration of iron ore in this country was carried on in the northeastern magnetite areas. Magnetic concentration was relatively simple and gave a concentrate that, after agglomeration, and in spite of being high in phosphorus because of the dry concentrating methods then in use, was satisfactory blast-furnace feed. Production from the northeastern magnetite area languished after the discovery and development of the Lake Superior ores, where there was seemingly an unlimited tonnage of high-grade ore, first the Michigan ores, and subsequently the still larger deposits of Minnesota. For years only the higher grade, direct shipping ores of the Lake Superior district were mined. Those of Michigan, and of the Vermilion Range in Minnesota, were hard ores and came principally from underground mines. The softer ores of the Mesabi came partly from underground mines, but mostly from the enormous deposits that could be worked by open-pit methods. The costs of ore from these open-pit deposits, even with the high initial cost of stripping, were so low that the underground mines of the Mesabi could hardly compete. The so-called Old Range ores, of Michigan and of the Vermilion Range of Minnesota, were hard and lumpy, and opened up the burden in the blast furnace, therefore making possible harder driving with greater output. Also, some of these ores were of such grade and physical characteristics that they were suitable for charge ore in the open hearth. These ores, therefore, commanded a price premium, and could compete with the softer, finer, but cheaper, Mesabi ores. The big tonnage reserves, however, are on the Mesabi, and it is these big open-pit deposits that constitute our stock pile of iron ore, from which we are drawing so heavily during this war period. On the western end of the Mesabi the ore was found to be high in silica, and not suitable as furnace feed. As early as 1902, attempts were made to concentrate this so-called wash ore and by 1910 the first washing plant was put into operation. The process was very simple, consisting essentially of a sizing and washing operation, with scalping screens, logwashers, and tables, which later were replaced by classifiers. Ore particles finer than 100 mesh were deliberately wasted, because these fines were undesirable in the furnace. Fortunately, these tailings were impounded, and already are being reworked. Before long some of the low-grade ores began to require more elaborate treatment than the simple washing operation and, tables having been discarded because of their low capacity, in favor of classifiers, jigs were next introduced. These were able to discard coarser pieces of tailing than classifiers. Jigs are in active use today, various improvements having been made in their design and application. Various other machines and methods of concentration have been tried from time to time, and have in turn been discarded for more improved processes. The latest and most important process that has been

Jan 1, 1943

By B. H. Kear, S. M. Copley

A dynamic theory of precipitation hardening in alloys containing cohevenl, stvess-.free, ordered particles is developed. The yield stvess is predicted from the stress dependence of the plastic strain vale, which is related to a derived dislocation velocity-stress function. The theory is shown to predict the magnilude and temperature dependence of the yield stress of a commercial nickel-base superalloy as well as many details of its slip structure. GLEITER and Hornbogen have developed a theory of the yield stress in alloys hardened by coherent, stress-free ordered ptrticles based on the observation that dislocations (b = a/2 (110)) glide in pairs.&apos; When a dislocation pair shears through an ordered particle, the glide motion of the leading dislocation is impeded since it must create antiphase boundary (APB), whereas the motion of the trailing dislocation is assisted because it annihilates APB produced by the first one. Taking into account the APB energy, the size, and spacing of the particles, G-H predict the observed yielding behavior in Ni/18.8 Cr/6.2 A1 alloys composed of a matrix phase y &apos;(nickel-solid solution) and particles of y&apos; (basically Ni3A1). The G-H theory, as well as all previous theories of hardening by coherent ordered particles, do not include the details of dislocation motion; the present dynamic theory is an attempt to overcome this limitation. In the dynamic theory, the yield stress is predicted from the stress dependence of the plastic strain rate, which is related to a derived dislocation velocity-stress function. This function can be evaluated if the structure of the alloy, the APB energy of the ordered phase, and the characteristic drag or frictional stresses of the matrix and precipitate phases are known. The theory is shown to account for the observed temperature dependence of the yield stress in a commercial nickel-base superalloy. 1) NICKEL-BASE SUPERALLOYS Although their compositions are complex, the nickel-base superalloys have remarkably simple structures. A detailed examination of the commercial superalloy

Jan 1, 1968