By W. E. Wallace, J. A. Warren, D. Josell, D. Wheeler

"We present the results of experiments and modeling of flip-chip geometry solder joint shapes under shear loading. Modeling, using Surface Evolver, included development of techniques that use an applied vector force (normal and shear loading) as input to determine a vector displacement of the pads connected by the solder joint (standoff height and misalignment). Previous solutions solved the converse problem: fixed displacements used to determine required applied force. Such solutions were inconvenient for applications, where the applied force (chip weight) is known. Also, for geometric and materials studies of solder joint shapes involving multiple parameters, determining the equilibrium displacement from applied force by bracketing solutions could become computationally expensive. Measurements of solder joint standoff height and misalignment as functions of the applied force (normal and shear), solder volume and pad diameter are presented. Experiments were carried out for solder ball diameters from 0.38 mm (0.029 mm3 volume) to 0.15 mm (0.0019 mm3 volume) on pads of diameter 0.64 mm and 0.35 mm. Fitting of simulation to experimental results gave optimized values for the contact angle and surface tension of the solder which were consistent with measured and literature values. IntroductionIn packaging technology flip-chip has become an important method for attaching semiconductor devices to substrates. Generally, the chip and substrate are bumped with solder and then the chip is flipped onto the substrate and the solder reflowed to form conductive interconnects. An epoxy underfill is normally flowed between the substrate and chip to reduce the thermal fatigue on the solder joints. A flip-chip assembly is illustrated in Figure 1.In flip-chip applications, the use of an integrated underfill/solder bump system [1, 2) removes an extra process step, namely infiltration of the underfill. However, the presence of an underfill will retard the self-alignment of the flip-chip. A first step in understanding and predicting this retardation is to develop a model to describe normal and lateral force-displacements curves when underfill material is not present. At this stage it is unclear whether static surface tension theory is sufficient to describe a complete model for flip-chip realignment even without underfill."

Jan 1, 2001

By Chang Wei, Zhigan Deng, Minting Li, Cunxiong Li, Xingbin Li

A direct hydrometallurgical process of extraction molybdenum and nickel from molybdenum-nickel ore by pressure water leaching without reagent was studied. The extraction of Mo and Ni from molybdenum-nickel ore by oxygen pressure leaching, which exploit the characteristic of molybdenum-nickel minerals contain high concentration amorphous sulfide which has highly active, and make the most of easily oxide to sulfuric acid and sulfate at low temperature and excess oxygen presence of the amorphous sulfide. Under oxygen pressure conditions, considerable molybdenum and almost all the nickel were extracted into solution in the leaching process. The results show that with the leaching time for 3~4h, temperature at 150o C, liquid-to-solid ratio of 2mL/g, mineral granularity of 0.074mm, oxygen partial pressure of 0.4~0.5MPa without other reagent, molybdenum leaching percentage can be over 80% and nickel leaching percentage can be more than 97%. Furthermore, about 80% sulfur in the Mo-Ni ore has been transformed into sulfuric acid.

Jan 1, 2014

By Yuanbo Zhang, Zhixiong You, Guanghui Li, Peidan Wen, Tao Jiang

Sn-bearing iron ore containing small amount of Zn, Pb and As is one of the typical complex polymetallic ores in China. This kind of ore is not extensively utilized due to the complicated relationships between iron and other associated nonferrous metal minerals. Excessive contents of these elements would adversely affect the metallurgical operation as well as the quality of steel products. In this study, reduction behavior of Sn was detailedly investigated using H2 or mixed H2/CO as reductant. The results revealed Sn volatilization was improved in the presence of H2 than individual CO/CO2 atmosphere. Simultaneous volatilization of these elements was realized by roasting under weak H2/CO reducing potential, and metallization reduction was advantageous for further Zn volitilization. A metallic pellet (DRI) with Fe metallization greater than 90%, residual Sn, Zn, Pb and As content of 0.054%, 0.012%, 0.0045% and 0.09% was prepared via a simulated reducing gas of coal gasification.

Jan 1, 2015

By P. H. Chang, J. E. Gould

"Solidification structures and austenite decomposition in some spot welded O.05%C - O.3%Mn steels have been studied with the aid of a numerical thermal model. The model is a one dimensional finite difference formulation, and accounts for melting, temperature dependent thermal properties, effective heat transfer in the liquid, and contact resistances. The model was used to predict solidification conditions during resolidification of the nugget. These solidification conditions were correlated with the primary dendrite spacing using available primary dendrite spacings modelling. The model was also used to predict cooling rates in the temperature regime for austenite decomposition. These cooling rates were used to interpret the underlying microstructure.INTRODUCTIONThe metallurgical transformations which occur during the spot welding of low carbon steels have traditionally been characterized only in the most general of fashions. This is most probably due to the similarity of spot welded microstructures to other welded microstructures, and that the mechanical integrity of spot welds has not been a concern. In addition, little information about the particular thermal cycles experienced during spot welding has been available. The introduction of HSLA (microalloyed) sheet steels has, however, raised new concerns about the integrity of spot welds. These steels have on occasion shown irregular weldability, as well as brittleness in the weld nugget on destructive testing l - 4 .In response to these concerns, considerable work has been done attempting to characterize thermal cycles in spot welds 5-12. This has largely taken the form of thermal modelling, with the end purpose generally to estimate the size of the nugget formed. This work uses the thermal model developed at Inland Steel 13 ,14 to try and understand, in a more fundamental way, microstructural evolution in spot welds. Two facets of this microstructural evolution are examined in detail:"

Jan 1, 1986

A novel process is being developed for metal recovery from waste electrical and electronic equipment involving a leach reactor coupled to an electrochemical reactor. Metals such as Ag, Au, Cu, Pb, Pd, Sn etc. are dissolved from shredded electronic scrap in an acidic aqueous chloride electrolyte by oxidising them with aqueous dissolved chlorine species. In the electrochemical reactor: (i) chlorine is generated at the anode for use as the oxidant in the leach reactor, and, simultaneously, (ii) at the cathode, the dissolved metals are electrodeposited from the leach solution. The extended Butler-Volmer equation was used to provide predictions of the electrode potential dependences of partial current densities and, hence, total current densities, current efficiencies and alloy compositions for acidic aqueous chloride electrolytes containing Ag(I), Au(III), Cu(II), Pb(II), Pd(IV) and Sn(IV) species, together with dissolved chlorine. With judicious choice of kinetic parameters, the predicted total current density ? electrode potential behaviour of such solutions was in good agreement with experimental data for a rotating Pt disc electrode. Reduction of dissolved chlorine at a Pt rotating disc electrode exhibited mass transport controlled behaviour, in agreement with Levich?s equation over the potential range 0.3-0.9 V (SHE). This could form the basis of a linear sensor, possibly using a microelectrode for measurement and control of the dissolved chlorine concentration in the efflux of leach reactors and inlet to electrowinning reactors in the envisaged process.

Jan 1, 2003

By Jong-Jip Kim, J. G. Byrne, W. Kim, In-Ok Shim, John E. Flinn

"Two rapid solidification processes for 304 stainless steel were studied: centrifugal atomization (CA) in a helium atmosphere and atomization by exposing argon-containing melt to vacuum (VGA). Positron annihilation and x-ray line broadening measurements of explosively consolidated monoliths were used to clarify microhardness measurements as a function of annealing temperature. Interesting differences in positron response between CA and VGA materials are ascribed to more carbide formation in the CA material than in the VGA material in the 600 0C range. In addition, hot isostatic pressing of the CA material was examined as to the relations between mechanical behavior, pore shape, and relative density. A variable stress concentration factor is introduced into the theory to allow for changing pore shape as relative density increases.IntroductionThere are many potential advantages of rapid solidification processing (RSP), such as a high degree of matrix supersaturation, finely dispersed microstructures, improved chemical homogeneity, and retention of metastable phases, which have been studied extensively. To consolidate rapidly solidified material which is in powder form into useful shapes often requires subjecting the material to elevated temperature for extended periods of time under mechanical forces, as in hot isostatic pressing or hot extrusion. In such cases, some of the characteristics of the rapid-cooling step can be strongly affected. An alternative is dynamic consolidation (1), for example by explosive forming, where the time frame at least is extremely short.In the present work, effects of the consolidation processes of hot isostatic pressing (HIP) and explosive forming in a die are examined. The particular material is 304 stainless steel. The characteristics of both RS and VGA 304 stainless-steel powders were described by Wright, Flinn, and Korth (2) earlier."

Jan 1, 1988

By N. B. Gray, I. F. Taylor

"Gas injection to promote chemical reactions or mixing is a feature of many metallurgical processes. Often the aim of gas injection is to bring about a chemical reaction between the gas and liquid but most of the past physical and mathematical modelling work has ignored the influence of such reactions. In the work reported here, cold model studies have been conducted in which gas reacts with the liquid into which it was injected. The rate of liquid mixing has been measured as an indication of the mechanical energy transfer. It has been found that gas generated chemically within the liquid is significantly less effective at promoting mixing than the equivalent volume of inert gas. The relative ineffectiveness of chemically produced gas is thought to be due to smaller bubble sizes in comparison to the inert gas case. Small bubbles characteristic of chemically generated gas move with low slip velocities relative to the liquid and lead to different turbulence generation mechanisms.IntroductionIn processes such as steelmaking, copper conversion, bath smelting and ladle steel finishing gas is injected into liquid metal where it reacts chemically or simply serves as a source of agitation. An understanding of fluid flow phenomena in such situations is an essential pre-requisite to the calculation of process intensity and the optimisation of vessel productivity. Traditional physical cold modelling approaches to prediction of liquid flow in such situations are now often augmented by the techniques of computational fluid dynamics. Even with the availability of numerical modelling techniques cold physical models continue to have an important role for validation because it is generally difficult to obtain quantitative data from high temperature processes.Almost all previous cold modelling work has been based on the injection of an inert gas into water or some other non-reactive liquid. Such models do not include the significant increase in gas volume inherent in some processes. For example the oxidation of carbon in steelmaking leads to a twofold increase in molar gas flux through the reaction:"

Jan 1, 1996

By J. H. Corrigan

A series of six papers describing the Falconbridge Dominicana Ferronickel project were presented at the International Laterite Symposium held as a joint project of TMS-AIME in February 1979 at New Orleans. A review of the ore mineralogy, as well as. the processing and environmental practices as they exist today at Falcondo with emphasis on modifications put into practice since 1979 are presented in two papers: Part I.- Mineralogy and Ore Dressing E.W. Lithgow - General Superintendent ? Mines Falconbridge Dominicana, C. por A. Bonao, Dominican Republic Commercial volumes of nickeliferous laterite ores overlie part of a 90 km long belt of peridotites in central Dominican Republic. Protores are serpentinized harzburgites and dunites, with lesser serpentinite. The ore mineralogy consists mostly of goethite, serpentine-group minerals, quartz and poorly crystallized, X- ray amorphous materials. Minor constituents are hematite, gibsite, olivine and enstatite. In the Ore Dressing plant, the mine feed is subjected initially to proper sizing and blending to produce a homogenized mix. Subsequent drying and upgrading, by selective crushing and screening of rock kagments through a Barmac circuit, complete preparation of the ore for pyrometallurgical processing. Part II.- Pyrometallurgy, Fuel and Power Generation J.H. Comgan - Manager ? Production Falconbridge Dominicana, C. por A. Bonao, Dominican Republic Falcondo's energy requirements are based on oil which is refined on site to provide distillate to carry out drying and selective reduction of the nickeliferous ore in the shaft furnaces, plus bunker oil to produce electrical power for process melting, refining and ancillary use. The dryer product at 1.68% Ni is briquetted and passed counter current to hot reducing gas in 12 vertical shaft furnaces. The hot calcine discharge is melted in two high power electric furnaces at very high secondary voltage. The crude ferronickel is ladle refined and cast as 15 kg ingots or 125 gm ferrocones.

Jan 1, 1993

By Stanko Nikolic

One of the keys to success in process development is incremental scale-up, allowing for potential problems to be identified and rectified. The ISASMELT™top submerged lance (TSL) process was developed to maturity using this method by Mount Isa Mines, now owned by Glencore. Commercialization only occurred once the process had been proven on each scale and as a result the ISASMELT™ technology now operates successfully around the world. An important parameter in the evolution of the technology has been the furnace campaign life. The initial commercial scale furnaces had minimal water-cooling. Although this led to shorter campaign lives, an extended development program resulted in the achievement of four-year campaign lives, without any water cooling. In tandem to the refractory designs Glencore Technology, supplier of the TSL technology, has progressed cooled copper lining designs for application to both the ISASMELT™ and ISACONVERT™ furnaces allowing for ultimate flexibility in the lining choice. This allows each ISASMELT™ operating site to minimize their overall life-cycle costs by balancing their campaign life with lining costs, energy inputs, and other shutdown requirements.

By James W. Reeves

DuPont was the titanium metal pioneer who put the greatest effort into both R&D and commercial sponge and powder metallurgy production. This was concentrated in the period 1945 through 1963. The commercial results were development of the chloride process for TiCl4 using ilmenite, development and improvement of the Kroll process, development of a modified Hunter process to make titanium powder and commercial development of a direct powder process. The powder metallurgical process failed because of the inability to meet powder chloride specifications. All this work remained a trade secret until published in NMAB -392 by Mahla in 1983. There were other processes explored by DuPont, both improved sponge and powder processes. Much of this work has been continued by others but none, as of yet, resulting in new improved titanium metal capacity.

Jan 1, 2001

By G. Diáz

The PLACID process applied to the recycling of spent lead-acid batteries is being developed by an European Consortium within the Brite-Euram II programme. The status of the project entitled "Lead Recovery from Lead Oxide Secondaries" is described in this paper. The main laboratory and batch experimental results and the preliminary feasibility study are summarised. The description of the demonstration pilot plant and continuous campaigns programme for 1995 are also included. An interesting global approach is proposed, integrating the Placid process in the existing spent battery recycling pyrometallurgical facilities. This yields important improvements in the overall process. Grids would be easily treated by the conventional pyrometallurgical route, obtaining lead alloys,, while battery pastes, slags and fumes would be fed to the Placid process, obtaining pure electrolytic lead (>99.99 %), ideal for battery paste manufacturing. The implementation of the Placid process into the existing battery recycling pyrometallurgical facilities is analyzed from technical, environmental and economical viewpoints. Greater overall lead recovery, lower operating costs, reduced waste production, environmentally safer residues and much better lead product quality are the key advantages. The authors draw the following final conclusion : Integration of the Placid process with conventional pyrometallurgical treatment is a feasible and very attractive alternative route for spent lead-acid battery recycling.

Jan 1, 1995

By M. Tomita

One of the most essential factors for a custom smelter to strengthen its competitive power is to Improve its comparative standing in purchase of concentrates from the world market. It is especially critical for Japanese smelters who depend almost 90% of their raw materials on import. In order to accomplish this breakthrough, the development of the new technology which enables us to treat concentrates containing higher Impurities is inevitable. Nippon Mining Company Ltd. made an intensive research on processing complex ore for three years from 1979, and successfully developed an original hydrometallurgical process to treat converter dust for eliminating impurities from the copper smelting circuit. The commercial plant was constructed at the Saganoseki Smelter & Refinery in 1982, and its nine years operation has been satisfactorily proven the advantages of the technology. The concept of this process and its operational performance are discussed.

Jan 1, 1992

By M. M. Coleman

An investigation of the behaviour of sphalerite, chalcopyrite, galena and pyrite during flotation was conducted on selected circuits in the Brunswick Mining and Smelting Corporation Ltd. concentrator in Bathurst, NB. Samples were collected from 59 locations and analyzed for Zn, Pb, Cu, Ag, Fe, As, Sb, Sn, Bi and S. Metal balances were computed using the CAMP Material Balance Program (MATBAL 5) and the metal recoveries for each cell and circuit were calculated. An automated image analyzer interfaced with an electron microprobe was programmed to measure the size of sphalerite, chalcopyrite, galena and pyrite grains in each sample. The percentage of each mineral occurring as free grains and the relative amount of each mineral present in binary and ternary particles was calculated. The recoveries and losses of Pb, Zn and Cu are compared with the amount of liberated and unliberated galena, sphalerite and chalcopyrite present in the concentrates and tailings.

Jan 1, 1989

By Ann M. Hagni

Reflected Light Microscopy (RLM) And Scanning Electron Microscopic-Energy Dispersive Spectroscopic Analysis (SEM-EDS) Study Of Electric Arc Furnace (EAF) Dusts Have Shown That Their Mineralogy Is Complex And Varied. The Particles Are Largely Spherical, And Can Be Seen In RLM Sections To Be Composed Of Franklinite, And Zincite, But They Show Significant Solid Solution With Each Other And May Contain Small Amounts Of Chromium. These Crystalline Phases Occur As Crystals And Skeletal Growths Within Ca-Fe-Si Glass. Because Chlorine Is A Deleterious Constituent In Recovered Zinc Products From EAF Dusts, Special Attention Has Been Given To Chlorine-Bearing Phases, And They Include Hydrophylite (Cacl2), Lime (Cao), And Organic Phases. Pyrohydrolysis-Treated EAF Dusts With Silica (Si02), Tungstite (W03), Alumina (A1203), And Bunsenite (Nio) Additives Contain Franklinite, Scheelite (Cawo4), Willemite (Zn2SiO4), And Hematite (Fe2O3)

Jan 1, 1992

By H. -Peter Sattler

The laser sorting technique for replacing the handpicking of the non-ferrous metal scrap from auto shredders was first introduced 1990, The process is based on the use of atomic emission spectroscopy induced by lasers to identify the scrap particles and sort them with adequate systems into main fractions of Al-, Zn-and Cu-alloys, stainless steel and lead, In the meantime the handling technique for the scrap, i.e. the singling and sorting technique as well as the analytical detector were further developed for more efficiency and higher reliability, i,e. less maintenance, minor sorting errors etc. These developments were mainly based, on and initiated by operational experiences from the startup phase of a first production plant. Part of the on going research work was the development of an ,aluminium detector which makes it the first time possible to sort mixed aluminium scrap automatically into specific alloy fractions.

Jan 1, 1995

By Batric Pesic

Silver dissolution with thiourea was studied by using the rotating disk technique. The major parameters studied were: thiourea concentration (0-0.5M), ferric sulfate concentration (0-0.5M), sulfuric acid concentration (0-0.5M), and the effect of many foreign ions (Mn, o.i, Co, Ca, Na, etc.). Temperature effect was studied in the range 5-35 .C. The activation energy was 5.4 Kcal/mole. The dissolution of silver was first order with respect to ferric sulfate, and the secord order with respect to thiourea. Among the additives, copper had a dramatically negative effect. The strong oxidants such as hydrogen peroxide and manganese dioxide were also detrimental for silver dissolution. Silver does not dissolve with thiourea in the absence of ferric ions. Sulfuric acid does not participate in the dissolution reaction either. Chemically, the most important parameter for silver dissolution is the ferric sulfate/thiourea ratio. Thus, in the solutions with excess of ferric sulfate, a solid silver-thiourea complex is formed, which precludes transfer of silver into solution. In the solutions with the excess of thiourea, the free thiourea reacts with formed solid silver-thiourea complex and silver goes into the solution. The solid silver-thiourea complex was characterized according to its chemical composition. The complex contains 6.54%C, 2.49\H, 14.77%N, 16.09%0, 21.62%8, and 37.13% Ag. This composition corresponds to a Ag2so4.3'1U.2ff:i0 compound The soluble silver species are present in the solution as the dimers of AgTU+3 complexes.

Jan 1, 1989

By J. Borlée, J. P. Birat

"ULCOS is a large European program launched by a consortium of 48 partners led by arcelor and a core group of steel producers, which was started in 2004 with the support of the European Commission (RFCS and 6FP programs) to search for breakthrough process routes that could, in the future, when fully developed, demonstrate the potential of large cuts in CO2 emissions for the production of steel from iron ore.The timescale for commercial implementation is the post-Kyoto period, i.e. 15 to 20 years from today.The present paper presents the progress made in the first 2 years of this 5 year program.Several concepts are being investigated in parallel: re-engineering of the blast furnace to incorporate CCS in the core of the process, smelting reduction with CCS capabilities, massive use of natural with more CO2-lean technologies than today, hydrogen steelmaking and electrolysis of iron ore. Biomass also offers very attractive perspectives, while raising major challenges.None of these new steelmaking routes are ""no regret"", which means that the European Steel Industry has already incorporated extensive energy saving steps in its present process technology and is working as close to thermodynamics limits as is cinematically and economically feasible, and that decreasing GHG emissions further means introducing breakthrough technologies that add significant costs to the operation of the Steel Mills.They will also require much research and development before they can be proven and implemented commercially.IntroductionThe ULCOS program (Ultra Low CO2 Steelmaking) is a large research program of the European Steel Industry and its industrial and research partners launched in September 2004 to investigate steelmaking technologies that have the potential of reducing the CO2 emission of the Industry by a large amount, typically in the order of 50%. It is supported in the European Community by the 6th Framework and the RFCS programs through 3 complementary European projects [1,2].The present paper summarizes the work carried out in the phase 1 of ULCOS and in framing the program of phase 2."

Jan 1, 2008

By Samson Adeosun, Sanmbo Balogun, David Esezobor

"Iron and steel making processes give rise to large amounts of usable and unusable materials, the latter generally being termed wastes. It is sometimes difficult to distinguish between re-usable by-products and wastes which cannot be sold or land-filled. Much depends on circumstances such as the local market for the material. This can itself vary from time to time with by-products which cannot be used or sold becoming wastes and vice versa. This paper defines the concept of “waste-free technology”, discusses its development in the steel industry and highlights the benefits of the technology to the manufacturing sector and the environment. The paper also articulates how the “waste-free” technology could be applied in the proposed Ajaokuta integrated steel plant in Nigeria.IntroductionIn the past, nature was considered an inexhaustible store. Its resources were consequently exploited and waste products therefrom were discarded. Today, attitudes have not changed appreciably even as raw materials cost rise by the year to pose a series of socio-economic problems, which, among others, may include the rational and optimum utilization of resources, environmental protection and reduction of waste formation. Consequently, industrialists now face unexpected regulatory pressure in areas of pollution prevention, waste minimization and hazardous waste disposal.Iron and steel making processes give rise to significant amounts of usable and un-usable materials, the latter generally being termed waste. It is sometimes difficult to distinguish between re-usable by-products and wastes which cannot be sold or land-filled. Much depends on circumstances such as the local market for the material. This can itself vary from time to time with by-products which cannot be used or sold becoming wastes and vice versa. In this paper, the term waste refers to those materials that are either irrationally utilized or, land-filled and part of the byproducts that are not utilized. It includes that part of used materials which is not incorporated into the products manufactured during a process stage and which in contrast to reuseable materials, is considered not suitable for any further use, owing to technical or economic factors. In general, these materials are inorganic and parts of them are either utilized or passed to the other processes; the other part should be disposed of using well-established waste disposal practices to avoid any environmental threat.Thus, creative methods must be developed to modify the manufacturing processes to reduce emissions and process wastes by fully utilizing all resources. One method of eliminating the negative effect of waste formation is the use of purification and cleaning structures (pollution control system, PCS). These are, however, quite expensive."

Jan 1, 2008

By N. J. Tannyan

Laboratory bath smelting tests were conducted to determine the feasibility of smelting nickel- copper concentrate directly to a low iron matte in one step. Concentrate, air/oxygen and a silica flux were fed to a matte-slag bath kept in MgO crucibles at I 300°C. Various oxygen enrichments and smelting rates were used to maintain 0.5 to 2 wt% iron in the product matte. The slag losses are comparable to those obtained under similar industrial conditions. Due to the highly oxidizing conditions required to produce mattes with low iron contents, it is not recommended to target iron contents below about 2% in the matte. The specific bath smelting rates were equal to or higher than those in various industrial bath smelting processes.

Jan 1, 2003

By V. Yahorava

Mintek has developed a non-destructive Resin-in-Leach method for the recovery of Rare Earth Elements (REE) from phosphogypsum (PG) waste dumps. However, PG from different sources was found to be highly variable in terms of REE recovery and physical properties. Development of a pre-treatment process was initiated to improve the robustness of the current REE recovery process in order to render it effective for any type of PG. Extensive research into the mineralogy of REE associations with PG revealed that the majority of REE are trapped inside phosphogypsum clusters which inhibits their recovery. Hydrothermal treatment of PG-containing slurry was found to result in re-crystallisation of gypsum with the release of REE phases encapsulated in it. This process was tested on various PG samples and subsequent REE recoveries improved from 5 to 80%. This approach carries a large potential for unlocking value associated with gypsum dumps worldwide.