By Jörn E. Fischer

Cracks were observed at the top of spray formed billets for some alloys. In this paper the effect of process parameters on crack probability is discussed. After the spray run the thermal conditions at the top of the billet change rapidly. A hot spot with melt residue] can occur inside the billet and shrinkage will be suppressed due to the solidified surface of the billet. In this situation hot cracks can be initialized. The temperature history of the billet during and after the spray run is calculated. The temperature difference between core and outside diameter of the billet is taken as indicator for hot crack probability. The effect of different process parameters on the hot crack probability is discussed. The results lead to a better understanding of the process. The calculations are taken as a tool to find process parameters in order to reduce or avoid hot cracks in spray formed billets.

Jan 1, 1999

By Cui Wang, Qian Li, Kexin Jiao, Haibin Zuo, Jianliang Zhang

Abstract：A rational cooling water system is the assurance for long campaign life of blast furnace．In the paper, the heat transfer of different furnace period and different furnace condition based on the water quality characteristics were analysed, and the reason of the heat flux over the normal from the hydrodynamics was analysed. The results showed that, the vapour-film and scale existence significantly influenced the hearth heat transfer, which accelerated the brick lining erosion. The water dynamic characteristics of the parallel inner pipe or among the pipes were the main reason for the abnormal heat flux and film boiling. As to the reasonable cooling water flow, the gas film and the scale should be controlled and the energy saving should be considered.

Jan 1, 2015

By Shize Jin

Effect of four polyols, namely ethylene glycol (EGL), glycerol (GCL), propanediol (PDL), butanediol (BDL) and three organic acids, namely oxalic acid (OA), malonic acid (MA) and succinic acid (SA) on the current efficiency (CE) and the cell voltage during zinc electrowinning was studied. Galvanostatic polarization was conducted in a supporting electrolyte (SE) containing 180 g dm-³ H2SO4, 60 g dm-³ Zn2+ and 8 g dm-³ Mn2+ at 38°C with magnetic stirring. The imposed current density was 50 mA cm-². The anodes were made of a Pb-Ag alloy and the cathodes were made of an aluminum alloy. The results showed that all the polyols tested in this study decreased the current efficiency and the cell voltage, but the decrease of the cell voltage was not important. Oxalic and succinic acids decreased the current efficiency to a less extent than the polyols, but did not decrease the cell voltage much. The only compound that increased the current efficiency was malonic acid, and its capacity of decreasing the cell voltage was the highest within the seven tested organic compounds.

Jan 1, 2003

By Harold R. Kokal

Lisakovsky is a 3-billion ton oolitic iron ore deposit in north-central Kazakhstan operated by Orken LLP, a subsidiary of Ispat Karmet and the LNM Group. The iron oxide minerals are goethite and limonite. The gangue occurs as discrete quartz grains and an unidentified form of colloidal silica-alumina. The concentrate produced contains about 49.5 percent iron (Fe) and 0.6-0.8 percent phosphorus (P) or 10-20 times the acceptable phosphorus level. The phosphorus is intimately associated with the iron oxide and colloidal gangue, no discrete phosphorus minerals are found, and beneficiation is not possible. Therefore, to reduce the phosphorus, a hydrometallurgical process that includes roasting followed by leaching in dilute sulfuric acid has been developed. Phosphorus extraction is 70-90 percent, with only a minor loss of iron. The process has been tested in the laboratory and in a pilot plant at 50-300 kg/h. Construction of a 900,000 t/y demonstration plant is underway.

Jan 1, 2003

By Tangstadm Merete, Eli Ringdalen

"This paper presents an overview of results from The Norwegian Research Institution SINTEF and the Norwegian University of Science and Technology, NTNU regarding new and ongoing research in silicon production. The main studies are related to condensation of SiO gas and cavity formation. If SiO gas condensation is increased at the top of the furnace resulting in SiO content in the off-gas closer to equilibrium, the Si yield will be increased significantly. Experimental work, simulating a cavity under industrial conditions, has shown that the cavity grows downwards from one layer. Physical appearance of zones in industrial furnaces, and selected reactions in these, are discussed based on results from excavation of industrial furnaces and results from laboratory experiments. Experimental studies of reaction rates for the formation of SiO are presented. Quartz properties are demonstrated to vary between differing quartz types and the effect of this is discussed.Introduction Both the theoretical and industrial issues associated with the production of silicon are described in detail in the textbook written by Schei et al [1]. This book covers the knowledge of silicon production process up to 1998. Together with the work by Myrhaug [1] and by Aasly[2], this is the main basis for this paper. Recent and ongoing research at SINTEF and NTNU focusing on production of Si and SiO in the high temperature zone, dissociation of SiO and condensate and cavity formation will be discussed."

Jan 1, 2012

By X. K. Lan

The greater demand for high-quality large-diameter crystals has led to the robust idea of a free- flying solar-powered furnace satellite, whereby the buoyancy-driven convection effects are almost nonexistent, and diffusion-controlled crystal growth with minimal radial segregation is promoted. In the proposed solar furnace, a paraboloid of revolution imaging concentrator is used to focus the sun's radiation onto an-ampoule which holds the solid charge to be processed. The charge will start melting in the vicinity of the focal point, after which it is translated in order for the melt to resolidify as a single crystal. A ray-trace method has been developed to determine the incident concentrated solar heat flux on the ampoule surface for a perfectly-aligned configuration with an incoming columnated beam. A transient 2- dimensional conduction problem with phase change is formulated, which is solved using the commercial code FIDAP. Results highlighting the feasibility of growing GaAs, Ge and Si crystals with diameters of the order of 20 cm using the solar furnace satellite concept are presented. The transient temperature fields within various charge materials are quantified.

Jan 1, 1994

By Basak Anameric

Pig iron nugget process was developed by Kobe Steel as an environmentally friendlier, economical alternative to traditional blast furnace process. The process aimed to produce highly metallized, slag free pig iron nuggets throughout a single stage heat treatment, utilizing coal as a reducing ? carburizing agent. The objective of this work was to determine whether the pig iron nuggets produced at the laboratory conditions had comparable physical and chemical properties with the blast furnace pig iron. The physical and chemical properties of the pig iron nuggets were determined utilizing x-ray fluorescence spectroscopy, x-ray diffraction, optical microscopy, scanning electron microscopy, energy dispersive spectroscopy and apparent density measurements. The pig iron nuggets had similar chemical composition and apparent density values (6.7 ? 7 g/cm3) with blast furnace pig iron and they had microstructures similar to low carbon white cast iron. These properties make them a competitive alternative to blast furnace pig iron.

Jan 1, 2006

By Ignacy A. Lipiec

The advantage of microorganisms used in bioleach systems to conventional chemical reaction systems is that these apply the available energy more precisely where it is needed, either directly onto the mineral of interest or by efficiently catalyzing the production of a reactant. The literature cover the range from empirical models used in describing macro heat balance in heaps to detailed studies relating the micro heat effects of bacteria adhesion energy to the surface of minerals. In this paper, the heat effects are reviewed in a general way describing bioleaching in two macro systems, heap leaching and slurry bioreactors. The micro scale heat effects is the reactions and conditions at the microorganism scale, including the mechanism of leaching and bacterial behavior.

Jan 1, 1998

By M. O. Lai

"Metal matrix composite (MMC) with composition of Al-4.Swt.%Cu reinforced by IOwt.%TiB2 or ISwt.%SiC particulate has been successfully fabricated using powder metallurgy technique. Disk, compression and beam specimens were prepared with (a) layered structure containing ductile Al-4.Swt.%Cu with brittle Al-4.Swt.%Cu/TiB2 or Al-4.Swt.%Cu/SiC layers, and (b) homogenous constituent with composition of Al-4.Swt.%Cu/lOwt.%TiB2' The specimens for the fracture toughness measurement were built through three ductile-brittle-ductile alternating layers. For the beam specimens, the layers were built through brittle-ductile-brittle sequence. The brittle layer consisted of Al-4.S%Cu with fixed amount of reinforcement. Fracture toughness testing revealed an increase for layered composites although the total amount of the reinforcement was the same for all disk specimens. The increase in fracture toughness is due to the existence of ductile layers which manifests a strong influence on delaying the occurrence of fracture. It acts as a barrier to resist the propagation of crack and hence increases the fracture toughness of the layered MMC specimens, Delamination in the beam specimens was observed to be due to shear stresses. Fracture surfaces of both disk, compress and beam specimens were characterized using the SEM. IntroductionMechanical and thermal properties can be achieved by the incorporation of refractory secondary phases to constrain the plastic flow of the matrix in a metal matrix composite (MMC). The size of the reinforcement particulate incorporated must be in the range larger than the dislocation cell size and strongly bonded to the matrix (I). Particulate reinforced metal matrix composites hence provide high modulus, improved wear resistance and strength (2-4). Because of the incorporation of refractory phases which are generally brittle, the major limitation in the mechanical properties of MMCs is their limited ductility in comparison to their base metals. Cracks normally initiate from the reinforcement and voids (4, 5). Due to the lack of ductility, cracks propagate rapidly with increase in load. As a result, the interactions between reinforcement particles and propagating cracks have recently been of great research interest (6). In addition, volume fraction of reinforcement and aging condition of the matrix significantly affect the mechanical behaviour of MMCs. In the case of AI-3.5%Cu reinforced with varying volume fractions of SiC particulate, it has been found that the probability of particle fracture increased with increasing volume fraction of reinforcement (7)."

Jan 1, 1996

By Dinesh Agrawal

Microwave energy has been in use for variety of applications for over 50 years. These applications include communication, food processing, wood drying, rubber vulcanization, medical therapy, polymers, etc. In the last two decades microwave heating has been also applied very effectively and efficiently to heat and sinter ceramic materials. Microwave heating is recognized for its various advantages, such as: time and energy saving, very rapid heating rates, considerably reduced processing cycle time and temperature, fine microstructures and improved mechanical properties, better product performance, etc. The most recent application of microwaves has been in the field of metallic materials for sintering, brazing/joining and melting. Several common steel compositions, pure metals and refractory metals have been sintered in microwaves to nearly full density with improved mechanical properties. Many commercial powder-metal components of various alloy compositions including iron and steel, copper, aluminum, nickel, Mo, Co, Ti, W, Sn, etc., and their alloys have also been sintered in microwaves producing better properties than their conventional counterparts by using a 2.45 GHz multimode microwave system. This work has been further extended to join and braze bulk metal pieces, especially super alloy based turbine blades. Further, in a specially designed microwave cavity, even the bulk metals can be made to couple with the microwave field and melted. The implications of these findings are obvious in the field of powder metal technology.

Jan 1, 2006

By Caisa Samuelsson, Fredrik Engström, Bo Björkman, Margareta Lidström Larsson

"Large amounts of by-products are generated by the Swedish steel industry each year. The EAF-process generates about 400 000 ton of slag, from which 80% is deposit. An alternative to deposit is to use slag as road construction material. However, metal content in the slag can be a problem, due to the leaching. The aim of this work was to investigate how stable these materials are when ageing and kept outside. Five different EAF-slags from domestic steel plants were used in this study. The materials were characterised after 0, 6, 12, 18 and 24 month to evaluate the ageing process. Scanning electron microscope (SEM), x-ray diffraction pattern (XRD) and a standard test for leaching were used. The changes in behaviour differ between the five materials. The total leachability decreases with time for all samples. CaCO3 is formed on slag surfaces as CaO reacts with moister and CO2 in the air. Introduction The slag generation in the Swedish steel industry is about 1.5 million tonnes annually, of which more than 500 000 ton is generated in EAF (Electric Arc Furnace), AOD- (Argon Oxygen Decarburization) converters and during the refining of steel in the ladle metallurgy. Some of the slags are used in different applications, but most of the steelmaking slags produced in Sweden are landfilled today. The chemistry, mineralogy and physical characteristics of slags make it a suitable material in construction, replacing for example, gravel and rock [1]. In some respects, in road construction, it may even be technically superior to virgin material. Slag from scrapbased steelmaking is used for road construction in Europe. The reason for the low utilization in Sweden is mainly due to potential leaching of harmful elements, legislations and competition with easily available natural raw materials. Except the potential leaching, the technical obstacles for not using some slags in construction include:"

Jan 1, 2008

By Serdar Aksu, Fiona M. Doyle

"CMP will be an essential process in the production of integrated circuits containing copper interconnects. This study aims to improve our mechanistic understanding of the role that organic chelating agents might play in the reactive slurries used in copper CMP. Copper dissolution behavior in EDTA arid glycine was first examined by producing potential-pH diagrams for the copper-water-EDTA and copper-water-glycine 'systems. The results of potentiodynamic polarization experiments were then considered in light of these diagrams. . In-situ polarization experiments were conducted to gain insight into the electrochemistry of copper during dynamic polishing in slurries prepared from EDT A and glycine.IntroductionCopper has recently started to replace aluminum as the interconnect metal in integrated circuits. Copper interconnection offers faster and more reliable integrated circuits due to its higher electrical conductivity and superior electromigration resistance (1). The damascene method is used to form multilevel interconnects in the manufacture of integrated circuit devices with copper metallization (2, 3). Copper is deposited by CVD or electroplating into vias and trenches etched in the interlayer dielectric (IDL), over a diffusion barrier usually made from titanium, tantalum or their nitrides. Chemical mechanical planarization (CMP) then prepares the wafer for the next deposition step, by removing excess copper and planarizing the surface. During CMP, the wafer is rotated and pressed against a rotating platen covered with a polishing pad. Chemically active slurries containing submicron size abrasive particles (Si02, Al20 3, ceria, diamond, etc.) are applied. Both the mechanical action of the abrasive particles and the chemical action of slurry constituents remove material from the wafer surface. Planarization results because material is removed faster from protruding regions on the surface than from recessed regions. Since CMP can globally planarize .the entire wafer, it has become one of the key technologies for producing integrated circuits with copper metallization."

Jan 1, 2000

By R. H. Rubisov

Sulphuric acid pressure leaching of nickeliferous laterites has attracted considerable attention from the nickel industry during the past five years. The process is especially advantageous for limonitic laterites that mostly contain goethite, because iron precipitates releasing acid and thus rendering low acid consumption. It is also applicable to mixtures of limonites and saprolites, although at higher acid consumption due to magnesium. Effective process design requires the solubility of metals that precipitate during the process to be known. In the present work, determination of metal solubilities is based on a simple speciation program that assumes the presence of only one dominant complex for each metal. The thermodynamic data for the precipitation reactions are extracted from high-temperature experiments with monometallic systems published previously. The validity of the approach is then tested against mixed bimetallic systems, and finally applied to calculate the solubility of aluminium, iron and magnesium in laterite leaching effluents "at temperature". In both cases of limonitic feed and limoniticfsaprolitic blends, the prediction closely follows metal solubilities measured experimentally at temperatures from 230 to 270°C and at terminal he acidities ranging from 10 to 75 g/L.

Jan 1, 1999

By Garry W. Warren

The brass foundry industry produces a significant amount of waste sand containing Cu, Zn and Pb which is often classified as a hazardous waste due to Pb content. The potential application of a hydrometallurgical process to treat the sand by extracting metal values and thus detoxifying the material has been investigated. The process involves leaching of metal values followed by cementation. The emphasis of this investigation was on the leaching step, although some preliminary cementation experiments have been performed. In order for any alternative treatment scheme to be successful, the smaller size fractions of the sand must be addressed. Experiments have been performed on five individual size fractions using various lixiviants HCI, acetic acid and HCI/NaCI. Cu extraction was found to be slower than either Zn or Pb. Results obtained in this investigation indicate that copper is present in two forms, an oxide form which dissolves rapidly and is insensitive to the level of oxygen, and a less soluble form, probably metallic which dissolves more slowly and requires an oxidizing agent. The presence or absence of oxygen had no influence on the rate of Zn dissolution indicating that zinc is present mostly in oxide form. Toxicity Characteristic Leaching Procedure (TCLP) tests showed that residues could be produced which meet the toxicity limit for lead. Preliminary cementation experiments have also demonstrated the feasibility of Cu and Pb recovery.

Jan 1, 1991

By Jan G. H. du Preez, C. Viviers, B. J. A. M. van Brecht, H. E. Rohwer, Nicole M. Sumter

"At the basis of metal ion separation lies some particularly metal ion specific chemical property which lends itself towards exploitation. This could be in the form of an anionic complex or a neutral chelate complex. In the former a cationic centre with a particularly high affinity for the complex will have to be designed. In the latter case a stereospecific chelate ligand containing the correct symmetry and type of donor atoms will have to be designed. In both above cases the ""active centre"" can be entered in a from that it can function in different media of hydrophobicity, eg a precipitant, a resin or a solvent extractant. Recent results obtained in this laboratory will be used to illustrate how the above variables can be exploited to develop improved processes for the separation of base metal and platinum group metals.IntroductionThe separation of metal ions in hydrometallurgy can be performed broadly speaking with two major aims. Firstly the separation/removal of a certain group of metal ions, either as a means of preconcentration or as a removal from effluent as part of a purification process and, secondly the removal of a specific metal ion from an industrial stream in order to produce a specific metal in a pure form. This latter operation is by far the most difficult of the two and is becoming more so in the light of the fact that the world is moving in the direction of lower grade ores and increasing pollution. Such a process can be divided into three essential parts, firstly the molecular one in which an active centre is required to obtain specificity, secondly a matrix within which this active centre must function, i.e. as part of a resin or solvent extractant and thirdly the design of the total system to optimize the realization of the operation."

Jan 1, 1996

By Guo Gongyi

An extraction chromatography by which 99.99 % pure scandium oxide can be prepared from the starting materiel containing about 70% scandium oxide has been developed by taking advantage of some peculiar properties of the complex chemistry and extraction chemistry of scandium. The purification of scandium was performed at room temperature with relatively fast rates in two chromatographic columns. The preliminary separation of scandium from impurities was done by extraction chromatography using tri-butyl phosphate as the stationery phase in the presence of citric acid, and the nearly complete separation in the presence of perchloric acid. The scandium recovery was greater than 90 %.

Jan 1, 1989

By Seong-Jong Kim

The formation behavior and corrosion characteristics of anodic oxide films on pure Mg and Mg-AI alloys were investigated focusing on the effects of anodizing potential, Al content, temperature and NaOH concentration. Pure Mg and Mg-AI alloys were anodized for 10 min at 3, 10, 40, and 80 V in NaOH solutions. Mg(OH)2 was generated by an active dissolution reaction at the surface of the specimen and the product was affected by temperature while MgO generation increased with NaOH concentration. Moreover, the current density after anodizing for 10 min at a constant potential decreased with increasing AI content in Mg-AI alloys,

Jan 1, 2003

By Kohei Yajima

The dusts and fly ash generated from the steelmaking processes and municipal solid waste incineration processes contain metallic elements such as Fe, Zn, Pb and Cd with considerable amount of halogens. In Japan, zinc in dusts is recovered by Waelz kiln or MF process, etc. However, the presence of halogen in the dust affects the evaporation and condensation behavior of zinc and other metals, and disturbs the direct recycling of dust to steelmaking processes, because alkali or heavy metals reacted with halogen vaporize easily as halides and/or oxyhalide compounds in pyrometallurgical process. Recently, the formation mechanism of zinc oxychloride vapor was investigated and the formation of zinc oxychloride such as ZnOCl was proposed. However, considering the practical operation, the effect of water vapor on the evaporation behavior of oxychloride is not fully clarified yet. This study is focused on the investigation of evaporation behavior of ZnO with Ar- O2-HCl-H2O atmosphere.

Jan 1, 2008

By Thomas Niehoff

Many industrial processes require energy. Energy is required for melting or heating purposes. The heat can be generated by electrical heating or combustion/oxidation of hydrocarbons. Oxygen supports the combustion process. Oxygen is naturally contained in air with about 21 vol.-percent. The use of technical oxygen will allow an increase to the natural oxygen concentration of combustion air. Altering the combustion process by increasing the oxygen content has various effects. These effects are described and analyzed with regard to heat transfer, emissions and energy consumption. Industrial processes requiring oxyfuel are described and discussed regarding energy aspects.

Jan 1, 2008

By Zhuoqing An, Qi Li, Zhancheng Guo, Yanling Zhang

Fluidized bed is an important iron-making reactor, especially for the finely sized iron-bearing materials. However, defluidization caused by sticking between particles extremely limited its wide spread commercialization. In this paper, apparent viscosity was put forward to express the ability of particles to resist movement, which is reasonably considered as the comprehensive results of interaction between particles. Meanwhile, an experimental measuring method of apparent viscosity of particles was proposed, during which the torque exerted on the rotating blade in a particle layer is measured, and then the apparent viscosity is obtained based on the motion equations of powder particles. Further, the apparent viscosity of iron particles was measured by using of this method, and the effects of shape, size, and temperature were examined. The data can provide important information for understanding when and why defluidization happened.

Jan 1, 2015