By Victor A. Phillips

A series of specimens of a Cu- 3.23 pct Co alloy were prepared with particle diameters from zero to 590A. The samples were then cold-rolled 95 pct and the effects of the particle size on the behavior on annealing for hr at temperatures between 100" and 900°C were studied (by hardness, light, and electron metallography). Particles, particularly for d r 105 to 590A, greatly impeded softening and vecvystallizn-tion, and tended to give elongated grains. Particles deformed fairly homogeneously with the ,matrix, be- IN a previous study by the author,' the growth of cobalt-rich precipitates was followed electron microscopically in Cu-3.12 Co alloy as a function of aging, typically at 650°C. The coherent spherical precipitates grew to 520 + lOOA average diam before spontaneously losing coherency and developing (111) facets. Stretching a few percent after precipitation 2aused loss of coherency to occur sooner at about 220A average particle diam. The particles apparently retained their fcc structure after loss of coherency. coming lau2ellae. For d = 55 to 180A, these lamellae gave streak-contrast effects apparently due to coherency strains , and spheroidized on annealing at 600" to 650°C, forming coherent particles. Particles of d = 250 ov 320A lost coherency during t-olling, giving incoherent lamellae. Recrystallization apparently occured by growth of new grains into unrecrystallized (recovered) material at temperatures below that at which cobalt atoms had much mobility. The present study was undertaken to explore the effect of cobalt-rjch particles of various average sizes from 50 to 600A diam on the isochronal annealing behavior of copper after heavy cold rolling. The previous work' was used as a guide in preparing the two-phase series of prerolling structures. The solution-treated alloy was also rolled for comparison. A further question of interest in the present study was whether dislocation and particle hardening were additive, since the prerolling structures covered the full range unaged - peak aged — overaged, and further precipitation might occur on annealing after cold rolling. Although there have been exhaustive studies of the isothermal2"6 and is~chronal annealing behavior of

Jan 1, 1967

By P. A. Beck, L. J. Demer

As reported in a previous publication,' isothermal grain growth in high purity aluminum and in an aluminum alloy with 2 pct magnesium can be adequately described by means of the empirical relation: Here, D is the average gain size after an annealing period 1. The annealing period includes the time for complete recrystal-lization R, and the time for gain growth 1,. D, is the pain size as recrystallized, n is a parameter depending on the temperature and on the material. The effect of 2 pet magnesium in solid solution was to decrease D, and to increase R, A and n at a given temperature. The present work was undertaken in order to investigate the above listed-effects of magnesium in solid solution, as functions of the magnesium content. The work also includes the study of certain anomalous effects observed in the recrystal-lization and grain growth of the 2 pct magnesium alloy at 350°C. Experimental Procedure The method of producing the ingots used in this work was described in detail1 and need not be reproduced here. The materials used were high purity aluminum, furnished by the Aluminum Co. of America, of lot analysis shown in Table r and magnesium from a high purity distilled stock of magnesium crystals. Table i—Lot Analysis of High Purity Aluminum Per CeNt Si.................................... 0.00~ Fe.................................... 0.002 Cu................................... 0.002 Mg................................... 0.003 Mn................................... o. oox Ingots were prepared for a series of binary aluminum-magnesium alloys of increasing alloy content. The numbers used to designate these ingots and their magnesium contents by chemical analysis are given in Table 2. Table 2—Ingot Numbers and Magnesium Contents Ingot Number Pct oa Magnesium aI 2.05 22 1.80 24 0.12 26 0 02s The analyses showed no difference in composition between the top and the bottom of the ingots. Spectrographic analysis of the ingots for elements other than magnesium showed, within the limits of accuracy of the method, no increase in impurities over the amounts given in the lot analysis for the high purity aluminum in Table I. Careful microscopic study of ingot 21 in the as-cast condition, at magnifications up to I 500X, revealed a cer-

Jan 1, 1949

By R. L. Orr, J. D. G. Masse, Ralph Hultgren

The relative partial molar enthalpies of gold and tin in liquid Au-Sn alloys have been measured from Xsn = 0.474 to 0.510 at 696°K, slightly above the melting point of solid AuSn. Within an average precision of 6 cal per g-atom, the data are represented by two smooth curves, which satisfy the Gibbs-Duhem relationship and which do not show any anomalous behavior in the range of composition studied. The results give no support to the hypothesis that atomic associations in the equiatomic liquid alloy resemble those in solid AuSu. LITTLE has been firmly established as to the nature of atomic distribution in liquid metallic phases. A favored hypothesis assumes the existence of atomic groupings in the liquid phase which are similar to those in solid phases occurring at lower temperatures. Beginning with this hypothesis, it is often possible to adjust the values of certain parameters (such as degree of association) so that approximate agreement is achieved with certain features of the X-ray diffraction pattern of the liquid, even though many other possible structures might satisfy the data equally well. Thus, in this manner, the structure of liquid tin has been described as a dispersion of fragments of gray tin in a matrix of metallic tin.1 Four X-ray diffraction studies2"5 have been made of the liquid alloy of composition AuSn at temperatures slightly above the melting point of the solid. Each investigator concluded, on somewhat different grounds, that the liquid consisted to a large extent of arrays of atoms similar to the solid, with admixture of more disordered arrays. Solid AuSn has the nickel arsenide crystal structure: each tin atom has six nearest neighbors, all gold atoms; and each gold atom has six tin and two gold atoms as nearest neighbors. It remains highly ordered to the melting point. The liquid alloy has a large exothermic (?H700° K = -2700 cal per g-atom6) enthalpy of formation, favoring ordering and making the hypothetical molecular association not unreasonable. The possible existence of such solidlike arrays, or of a high degree of order that occurs preferentially at a specific composition in a liquid alloy, might also be revealed by thermodynamic behavior somewhat analogous to that in highly ordered solid alloy phases. The latter often exist over wide composition ranges, within which the highest degree of order occurs at the ideal composition for which the atomic fractions are equal to the fractions of sites which are "right" for each kind of atom. On departing from the ideal composition, the excess atoms occupy "wrong" positions, raising the internal energy and making it progressively easier for additional atoms to occupy "wrong" positions. Thus, on either side of the ideal composition, there should be a pronounced rise in the entropy and enthalpy, which would be shown particularly by the change in the relative partial molar enthalpies, ?Hi, since they depend strongly on d?H/dx. In the one case where accurate measurements have been made, the solid AuCu ordered phase, the structure becomes much less ordered as the composition deviates from the ideal, and relative partial molar enthalpies change sharply as shown by the data6 given in Table I. This suggests the possibility of finding similar pronounced changes in the relative partial molar enthalpies of gold and tin in liquid alloys near the composition AuSn if the postulated solidlike ar-

Jan 1, 1967

By LEE H. CORNELL

Drilling activity in Kansas during 1945 continued at an accelerated pace to meet the demands of war; 1810 tests were drilled as compared with 1856 tests the previous year, 1771 tests in 1943, and 1516 tests in 1942. During the year 31 new oil pools and 10 new gas pools were discovered. Of a total of 364 wildcats drilled, 323 were dry; and of 1446 tests drilled in pools, 825 were oil wells, 197 gas wells, and 425 dry holes.

Jan 1, 1946

By J. S. Koehler, F. Seitz

THE dislocation theory of plastic flow originated in 1928, when Prandtl1 suggested that the internal damping of metals of plastic origin might arise from the motion of a crystalline imperfection. Following this, Dehlinger2 employed a similar imperfection in a theory of recrystallization. The first detailed theoretical discussions were those of E. Orowan3 and G. I. Taylor4 in 1934. The resulting theory was gen- eralized by J. M. Burgers5 in 1939. Mott and Nabarro, in England, and Seitz and Read,6 in the United States, started an extensive examination of the atomic theory of dislocations in the period between 1939 and 1941. However, this development was arrested by the mar and was not taken up again until after 1945. Since 1946, the field has been the object of very intense activity, particularly in the United States and England. Dislocations are beautiful and intricate imperfections; they are sufficiently complicated to account for the great variety of phenomena encountered in the field of plastic flow. Above all, the dislocation concept enables us to understand how a metal or other plastic solid can deform inelastically under very small stresses at temperatures far below the melting point. Suppose we attempt to shear a perfect crystal plastically. This can be done by sliding one entire atomic plane simultaneously through one atomic distance with' respect to the near-

Jan 1, 1954

By P. A. Beck, M. V. Nevitt

All binary and a number of ternary u alloys formed by first long period transition elements were examined and found to be ferromagnetic at low temperatures. The Curie temperatures for these alloys were measured. It was found that the correlation of the Curie temperature with composition may be described qualitatively in terms of the contributions of the various component atomic moments to the saturation moment of the alloy. Ternary Fe-Cr-Mo u phase alloys were also found to be ferromagnetic, with a Curie temperature dependent on the iron content and largely independent of the unit cell dimensions. Similar relations were found for the Co-Fe-Cr and the Co-Cr-Mo a alloys, where the Co + Fe content appears to determine the Curie temperature. RECENTLY, it has become increasingly evident that the u phase is some kind of an "electron compound." Several papers1-' discussed the empirical correlation between the composition of the various u phases in alloys of the transition elements and the distribution of electrons in the partially filled d-levels of the component atoms. However, a picture of the latter can be formed only in a more or less intuitive manner, as in the Pauling theory," and the rigorous treatment of these problems is at present prevented by lack of adequate knowledge of the electronic structure of the transition elements in the metallic state. It appeared reasonable to expect that investigation of the magnetic properties, which are related to d-shell electrons, may help in clarifying the physical nature of the foregoing empirical correlation. Qualitative tests of samples of various compositions have shown that certain u alloys become ferromagnetic at liquid nitrogen temperature." The present investigation was undertaken to determine whether or not low temperature ferromagnetism is characteristic of a large variety of u alloys and to establish how the Curie temperatures of ferromagnetic u alloys are influenced by changes in composition and in lattice parameter. In the first portion of the in- vestigation, Curie temperatures were measured for a series of u alloys containing either vanadium or chromium with one or two of the elements manganese, iron, cobalt, or nickel. In the second phase of the work, data were obtained on the Curie temperature of ternary (Fe, Co, Cr)a, (Fe, Cr, Mo)a, and (Co, Cr, MO)U alloys, as a function of composition and of interatomic spacing. Experimental Procedures High frequency vacuum melting in high purity re-crystallized alumina crucibles was employed in the preparation of the u alloys, using metals whose lot analyses are given in Table I. Approximately two-thirds of the alloys were analyzed chemically, the analytical results being in acceptable agreement with the intended compositions, as seen in Tables I1 and 111. The specimens were annealed for homogen-ization in an atmosphere of purified 92 pct He and 8 pct H, mixture or in evacuated and sealed Vycor tubes at temperatures from 780" to 1300°C, depending on the temperature range of the u phase field for the particular composition. The annealing temwerature and time for kach alloy are given in Tables 11 and 111. Curie points were determined by an induction method; the change with temperature of mutual inductance between two coils was observed when the i-u specimen was inserted into the flux path between the coils. The transformer consisted of three coils each containing 1200 turns of 0.0050 in. diam enameled copper wire. The center coil, P in Fig. 1, served as the primary coil, and was linked magnetically with each of the two secondary coils, S, and S? which were connected in series opposition. The primary coil, P, was energized by an audio-oscillator, set at a frequency of 500 cycles per sec, while the signal from the transformer secondary circuit,

Jan 1, 1956

By W. Joseph Schlitt, William D. Southard, Bruce P. Ream, Lawrence J. Haug

The operation of Kennecott's Bingham Canyon copper precipitation plant, one of the world's largest, is described. This description includes a brief historical review of precipitation at Bingham and the general layout and operation of the present cone cementation facility. Current practices are based on results of studies undertaken to define improvements needed in each unit operation. These improvements were required to meet changing plant conditions and were implemented primarily within the constraints of the existing facilities. Specific unit operations included were the cone precipitators, the cone discharge thickener, the cone effluent settling basins, and the plate and frame filter presses. As a result of these improvements, loss of precipitated copper decreased and the degree of precipitation increased, raising copper recovery by 9 t/d. At the same time, iron consumption was reduced by 22.5 t/d. Problems in drying the cement copper were also overcome so that a product containing 12 - 15% moisture could be consistently delivered for smelting.

Jan 6, 1979

By William D. Southard, Joseph W. Schlitt, Bruce P. Ream, Lawrence J. Haug

The operation of Kennecott 's Bingham Canyon copper precipitation plant, one of the world's largest, is described. This description includes a brief historical review of precipitation at Bingham and the general layout and operation of the present cone cementation facility. Current practices are based on results of studies undertaken to define improvements needed in each unit operation. These improvements were required to meet changing plant conditions and were implemented primarily within the constraints of the existing facilities. Specific unit operations included were the cone precipitators, the cone discharge thickener, the cone effluent settling basins, and the plate and frame filter presses. As a result of these improvements, loss of precipitated copper decreased and the degree of precipitation increased, raising copper recovery by 9 t/d. At the same time, iron consumption was reduced by 22.5 t/d. Problems in drying the cement copper were also overcome so that a product containing 12-15% moisture could be consistently delivered for smelting.

Jan 1, 1980

By E. H. Timmerman, A. F. van Everdingen, J. J. McMahon

The prevent paper contains a method which combines the material balance equation' with the water influx equation' to obtain reliable values for the active oil originally in place and a quantitative evaluation of the cumulative water influx. The method is illustrated by an application to a reservoir without original gas cap. In the absence of an original gas cap. results may be obtained using only field production and pressure data, PVT analyses. and a minimum of subsurface information. CHARACTERISTICS OF RESERVOIR AND RESERVOIR FLUIDS Production in the field under review is obtained from the top of the Wilcox formation of Eocene age, at a depth of approximately 8,100 ft subsea. The structural map, Fig. 1, shows that the accumulation, half elliptical in shape with the long axis in east-west direction, is trapped to the north and on the upthrown side of a normal fault. A number of east-west faults with additional minor faulting in random directions are found in the general area, and seismic information and production performance indicate in this particular case the existence of a second fault a short distance downdip, with a strike more or less parallel to the fault controlling the accumulation. It is estimated that 1,830 acres were originally underlain by oil and that the maximum thickness of the original oil column, about 37 ft, was only slightly greater than the maximum thickness of the oil-bearing sand. Maximum net sand thickness was estimated at approximately 26 ft. From logging and subsurface information the gross sand volume has been placed at 37.400 acre-ft. which reduces to about 27,500 acre-ft after probable non-productive intervals have been deducted. The following table presents laboratory analyse; data for the Wilcox sand cores. Average Average Samples Considered Permeability Porosity All Samples 236 md ..19.9percent Samples with k>l md 256 md 20.5 per cent Samples with k>8 md 275 md 20.9 per cent Interstitial water was estimated at 15 per cent. The initial gas-oil ratio was approximately 900 cu ft/bbl. and the initial shrinkage factor was determined by the laboratory to

Jan 1, 1953

By J. D. Price, W. M. Bertholf

In preparing a paper on coal washing in Colorado and New Mexico, it is difficult to refrain from entering into a discussion of the historical aspects of this subject, for the story of coal washing in these states goes hack well into the last century. This phase of the subject could well make a complete paper in itself, and of necessity this present discussion must be limited to current operations. Therefore, we are taking into consideration only those washing plants which have operated for some period during the years of 1947 and 1948. Summary Of the eight million tons of coal mined in the two states in 1947. ap- proximately two million tons were washed in wet washing plants, using concentrating tables or jigs. The one table plant accounted for 70 pct of the output of washed coal, and two large Baum jig plants accounted for an additional 26 pct, leaving only a small residual tonnage to be accounted for by other types of jigs The necessity for washing coal is occasioned by the desire or necessity of reducing the ash content of the coals— sulphur is not a problem in this area. All washeries, except the table plant, are at or near the tipple, hence wash only one kind of coal. At the table plant a large number of different coals are washed. Only at the table plant is there any occasion for drying any considerable quantity of fine coal— other plants size and/or dewater on shaking screens. The results of washing at the smaller plants are judged by the number (or lack) of complaints about the quality of the washed coal. This is probably as good a system as can he devised for small, intermittent operations. The efficiency of the Baum jig ap-pears to be quite high. This is to be expected as long as the automatic control of the refuse gate operates properly. The efficiency of the concentrating table is not as high as that of the Baum jig, especially when the "difficulty" of washing is taken into consideration. When dealing with coals in which the "bone" is larger than the "coal," the table appears to be at a definite disadvantage, because of its sizing action.

Jan 1, 1950

By Carleton C. Long, George F. Weaton

Two years ago the general features of the St. Joseph Lead Company's zine-smelting process were described.' At that time the discussion was limited to a description of the production of high-purity electrothermic zinc oxide. The present paper will describe the commercial production of electrothermic zinc metal. Since a fairly complete description of the plant of the Josephtowlz smelter was given in the earlier paper, the brief recapitulation given here will be limited to mention of additional equip-ment recently installed and a bare outline of the preparatory process. The raw material is zinc sulphide concentrate received from the company's mines in St. Lawrence County, New York. An average dry-weight analysis of this material is: Zn, 58.28 per cent; Pb, 0.56; insoluble, 1.6; SiO², 1.12; Fe, 6.4; CaO, 0.47; MgO, 0.27; S, 31.9; Cd, 0.1; Cu, 0.06; Mn, 0.24. Moisture content is usually about 3 per cent. Three 21-ft. 6-in. diameter, 12-hearth Nichols-Herreshoff furnaces roast the coacentrate to a calcine of average conlposition (first 10 months of 1938): Zn, 67.69 per cent; Pb, 0.06; insoluble, 1.75; SiO², 1.26; Fe, 7.24; CaO, 0.47; MgO, 0.36; S, 1.88; Cd, 0.1; Cu, 0.07'; Mn, 0.27. The sulphur dioxide gas, after passing through a waste-heat boiler, proceeds through a recently redesigned low-resistance gas-purification assembly to the contact sulphuric acid plant, of which the capacity is 200 tons of concentrates per day. The calcine is mixed with a portion of returned furnace residues and sintered on 42-in, by 44-ft. Dwight-Lloyd sintering machines, gas-fired. Wind-box gases pass through air coolers before filtering in a 1440-bag Dracco unit, and thence to stack. The Dracco fume is mixed with Cottrell dust, from roaster gas cleaning, and sent to the leach plant, where it is roasted (SO² to acid plant) and leached with sulphuric acid to recover, as end products, lead sulphate, zinc sulphate and cadmium.

Jan 1, 1943

By George F. Weaton, Carleton C. Long

Two years ago the general features of the St. Joseph Lead Company's zine-smelting process were described.' At that time the discussion was limited to a description of the production of high-purity electrothermic zinc oxide. The present paper will describe the commercial production of electrothermic zinc metal. Since a fairly complete description of the plant of the Josephtowlz smelter was given in the earlier paper, the brief recapitulation given here will be limited to mention of additional equip-ment recently installed and a bare outline of the preparatory process. The raw material is zinc sulphide concentrate received from the company's mines in St. Lawrence County, New York. An average dry-weight analysis of this material is: Zn, 58.28 per cent; Pb, 0.56; insoluble, 1.6; SiO², 1.12; Fe, 6.4; CaO, 0.47; MgO, 0.27; S, 31.9; Cd, 0.1; Cu, 0.06; Mn, 0.24. Moisture content is usually about 3 per cent. Three 21-ft. 6-in. diameter, 12-hearth Nichols-Herreshoff furnaces roast the coacentrate to a calcine of average conlposition (first 10 months of 1938): Zn, 67.69 per cent; Pb, 0.06; insoluble, 1.75; SiO², 1.26; Fe, 7.24; CaO, 0.47; MgO, 0.36; S, 1.88; Cd, 0.1; Cu, 0.07'; Mn, 0.27. The sulphur dioxide gas, after passing through a waste-heat boiler, proceeds through a recently redesigned low-resistance gas-purification assembly to the contact sulphuric acid plant, of which the capacity is 200 tons of concentrates per day. The calcine is mixed with a portion of returned furnace residues and sintered on 42-in, by 44-ft. Dwight-Lloyd sintering machines, gas-fired. Wind-box gases pass through air coolers before filtering in a 1440-bag Dracco unit, and thence to stack. The Dracco fume is mixed with Cottrell dust, from roaster gas cleaning, and sent to the leach plant, where it is roasted (SO² to acid plant) and leached with sulphuric acid to recover, as end products, lead sulphate, zinc sulphate and cadmium.

Jan 1, 1943

By A. L. Holley

The first session was held in the rooms of the American Philosophical Society, on Tuesday evening, February 26th. The President, Dr. T. Sterry Hunt, called the meeting to order, and after a few introductory remarks concerning the importance of theoretical and speculative science, which often involves principles of the highest economic value, and, more than all that, serves to enlarge our conceptions of the universe, and ennoble us, by the cultivation which it affords to our most exalted faculties, proceeded to discuss some points in the chemistry of the atmosphere. It is known that there is in the crust of the earth a great amount of oxidized carbon, not only in the shape of coal, but also in the graphite or plunlbago of the crystalline rocks, in the various bituminous shales or pyroschists, which are found in all succeeding rock-formations, and also in the forms of bitumen and petroleum. All the analogies of nature lead us to conclude that these various carbonaceous substances have had an organic origin, and have been generated by the deoxidation of carbonic acid, a process effected by the growing plant, and attended with the liberation of oxygen. He showed that the carbon of a layer of coal covering the whole earth's surface to the thickness of one meter, would, in its production from carbonic dioxide, liberate an amount of oxygen equal to that now present in our atmosphere. But bituminous coal contains also a large amount of hydrogen, derived from the deoxidation of water, which implies the liberation of a farther portion of oxygen. The amount from this latter source would equal, for the various coals and asphalts, from one-eighth to one-fourth, and, for the petroleums, onehalf of that set free in the deoxidation of the carbon which these hydrocarbonaceous bodies contain. From what we know of the composition of the stratified rocks, it is probable that they include an amount of deoxidized carbon and hydrogen many times greater than that contained in a layer of coal one meter in thickness, and, consequently, that the disengaged oxygen in past ages must have far exceeded that now present in our atmosphere. To this must be added

Jan 1, 1879

By Francis B. Foley

In examining steel under the microscope, one is constantly confronted with structures that are difficult to interpret. Recently, in a collection of samples for exhibition purposes, the writer found a piece of open-hearth runner metal, 2 in. (50 mm.) in diameter, that had been fractured for use as a sample of cast-steel structure. On polishing and etching a section for the purpose of photographing a field to typify the microstructure of steel in the "as cast" condition, a variety of structures was found (Fig. 1) so arranged as to arouse interest at once. For a distance of about 0.065 in. (1.6 mm.) from the skin of the runner, normal ingot structure was found (Fig. 2); this was followed by a zone, about 0.215 in. (5.5 mm.) wide, of considerably lower carbon content in which occurred a most pronounced Widmannstattian structure (Fig. 3); from this point on to the center of the runner, the metal was again of normal ingot structure (Fig. 4). Representative samples taken from the metal in the three zones showed the following analysis: Carbon Nickel Chromium Per Cent. Per Cent. PeR Cent. Metal from skin........................... 0.34 1.26 0.63 Widmannstattian zone.................... 0.21 1.18 0.63 Metal from center......................... 0.34 1.32 0.67 Such a condition might result from decarburization followed by recarburization of the skin. This section came from one of the branch runners to the bottom of the mold, not from the main runner, and it is difficult to conceive of decarburization occurring in this portion of a runner. If the metal were stripped while quite hot, some oxidation would take place but the recarburization is unaccounted for. It could not occur by segregation after solidification—the tendency then is for diffusion and homogeneity. The following seems to fit the conditions and is offered as an explanation. The outside layer of normal structure 0.065 in. (1.6 mm.) thick was chilled on the walls of the runner brick when the molten metal first entered the runner. As the molten metal flows by, the outside of the stream

Jan 1, 1920

By Walter McKee

WHEN mixed with common cast steel in quantities ranging from 11 to 13 ½ per cent. and properly treated, manganese increases the ductility of the metal and adds greatly to its toughness and resistance to abrasive action, which properties comprise the distinctive characteristics that make manganese steel so valuable for many purposes at the present time. Manganese steel has been manufactured for about 26 years. .It was first made in a small way in England and subsequently produced in the United States in 1892. At present the manganese-steel foundries of this country have an annual capacity of about 60,000 tons and most of the growth has occurred within the past 10 years. In the early days of the industry it was impracticable to make manganese castings weighing over a few thousand pounds, but at present crusher heads, rolling-mill pinions, and similar castings weighing up to 30,000 lb. each are produced, and it does not appear that the limit of weight has been reached by a considerable margin. Manganese steel is similar in analysis to ordinary first-class converter metal except that it is high in carbon and contains from 11 to 13 ½ per cent. of manganese. From one standpoint manganese steel is similar to malleable iron in that the casting as it comes out of the sand is hard and brittle and must be made ductile by a heat-treating process. The heat treatment is an essential part of the process of making manganese-steel castings and must be properly carried out to secure satisfactory results. The necessity for heat treatment limits the thickness of sections which may be made of manganese steel. Originally the annealing depth was comparatively small, but researches carried on during the past few years have resulted in an increase in the thickness of section up to 5 ½ in., which it is possible to treat successfully. Large castings are cored out to a minimum thickness of 5 ½ in., thus not only eliminating some of the internal stresses which are invariably set up in a very thick casting, but also reducing the weight and inertia of the piece, an

Jan 12, 1915

By Robert C. Stephenson

Large deposits of titaniferous magnetite occur associated with anorthosite and gabbro in the Lake Sanford area, Essex County, New York. The ore, gabbro, and anortbosite show consanguineous relations. Anorthosite grades through gabbroic anortbosite into gabbro but is locally intruded by gabbro. Structural and petrographic evidence suggests that gabbro was differentiated from anorthosite by filter pressing. Field and laboratory study of ore occurrences indicates that an ore residuum concentrated in the gabbro through magmatic segregation' by normal crystallization and flowage. Ore occurs as bands which grade into gabbro, and also as large masses which replace anorthosite. Ore in the gabbro is finer grained and richer in ilmenite than ore in anorthosite. Introduction The Lake Sanford area lies in the heart of the Adirondack Mountains, in the southeast portion of the Santanoni Quadrangle (Fig. I), and there are four ore bodies in the area immediately surrounding Lake Sanford. The area lies 30 miles by highway from the railroad at North Creek. The deposits were discovered in 1826, and from then until 1858 iron was produced in small quantities. They were idle from 1858 to 1906. Between 1906 and 1913, extensive development work was carried on. These early attempts to produce iron ore were thwarted by transportation difficulties and by the titanium content of the ore, which, ironically, has been the element responsible for the present development. In 1941 the National Lead Co., Titanium Division, developed the Sanford Hill ore body and is now producing ilmenite and magnetite concentrates.18 The Defense Plant Corporation is extending the railroad to the property from North Creek and is building a sintering plant to treat the magnetite concentrate. Investigations OF the Deposits* Early studies of the Lake Sanford titaniferous magnetite deposits were made by Emmons in 1842,l2 by Kemp, in 1897-98'0 and by Newland in 1908.22 Singewald26 and Osborne23 considered these deposits along with numerous other titaniferous magnetite deposits in 1913 and 1928, respectively. None of these reports entailed a detailed study of the ore occurrence in this area. The present study was begun in 1940. Seven months were spent in the field, and considerable time was spent in labora-

Jan 1, 1949

By Robert C. Stephenson

Large deposits of titaniferous magnetite occur associated with anorthosite and gabbro in the Lake Sanford area, Essex County, New York. The ore, gabbro, and anortbosite show consanguineous relations. Anorthosite grades through gabbroic anortbosite into gabbro but is locally intruded by gabbro. Structural and petrographic evidence suggests that gabbro was differentiated from anorthosite by filter pressing. Field and laboratory study of ore occurrences indicates that an ore residuum concentrated in the gabbro through magmatic segregation' by normal crystallization and flowage. Ore occurs as bands which grade into gabbro, and also as large masses which replace anorthosite. Ore in the gabbro is finer grained and richer in ilmenite than ore in anorthosite. Introduction The Lake Sanford area lies in the heart of the Adirondack Mountains, in the southeast portion of the Santanoni Quadrangle (Fig. I), and there are four ore bodies in the area immediately surrounding Lake Sanford. The area lies 30 miles by highway from the railroad at North Creek. The deposits were discovered in 1826, and from then until 1858 iron was produced in small quantities. They were idle from 1858 to 1906. Between 1906 and 1913, extensive development work was carried on. These early attempts to produce iron ore were thwarted by transportation difficulties and by the titanium content of the ore, which, ironically, has been the element responsible for the present development. In 1941 the National Lead Co., Titanium Division, developed the Sanford Hill ore body and is now producing ilmenite and magnetite concentrates.18 The Defense Plant Corporation is extending the railroad to the property from North Creek and is building a sintering plant to treat the magnetite concentrate. Investigations OF the Deposits* Early studies of the Lake Sanford titaniferous magnetite deposits were made by Emmons in 1842,l2 by Kemp, in 1897-98'0 and by Newland in 1908.22 Singewald26 and Osborne23 considered these deposits along with numerous other titaniferous magnetite deposits in 1913 and 1928, respectively. None of these reports entailed a detailed study of the ore occurrence in this area. The present study was begun in 1940. Seven months were spent in the field, and considerable time was spent in labora-

Jan 1, 1949

By David Keys

THE object of this investigation was to determine with a vertical magnetic variometer the extent of the titaniferous ore deposit that occurs not far from Ivry in Terrebonne County, Quebec, about 70 miles north of Montreal. The Ivry mine, on lots 37 and 38 of range V, Beres-ford township, Quebec, is one of the largest and most accessible to transportation of the deposits of ilmenite in Quebec. The ore consists of an aggregate of ilmenite anhedra serving as host for numerous fine plaques of hematite. No magnetite is known from any occurrence near this lot, and in this way the deposit differs from many others that contain a large percentage of magnetite with the ilmenite. The deposit at Ivry thus has much lower magnetic susceptibility than those containing abun-dant magnetite, and a sensitive magnetometer was necessary for the work, although a body of magnetite with ilmenite about a mile from the Ivry mine was successfully prospected with a dip needle. The principal orebody is exposed in a quarry known as the Ivry mine, from which about 16,000 tons of ore have been shipped. Small exposures of ilmenite isolated by drift serve to show the presence at the surface of some of the bodies indicated by the magnetometer,- but most of the hill is covered with glacial till and second growth hardwood. At the lower levels the till gives place to fluvioglacial sands and gravels from which the forest has been cleared. The increasing thickness of the sand and gravel as the hill descends makes the tracing outward of the deposits from the rocky knob of anorthosite a difficult matter. Within the orebodies too, some masses of anorthosite persist, which may account for some local irregularities. Fig. 1 is a photomicrograph, taken by reflected light, of a typical specimen of the ore. The dark patches are hematite and the light parts are ilmenite. No trace of magnetite was found. Fig. 2 is a photo-micrograph of a thin section of the country rock showing the texture of the anorthosite. The mean of four analyses quoted by Robinson1 is: titanium, 19.26 per cent; iron 45:41 per cent.

Jan 1, 1936

US 4,132,635 -In the froth flotation beneficiation of low- grade siliceous iron oxide ore, an aqueous pulp of undeslimed ore is conditioned first with a reagent formed by incorporating a water-soluble polyvalent metal salt into an aqueous solution of sodium silicate and then with oleic acid or other anionic collector and optionally pine 011 or other frother. The conditioned pulp is subjected to flotation to concentrate Iron oxide values in the froth D. C. Yang, assigned to Michigan Technological University Jan 2, 1979 7 pp (209-1 66) Filed 1-1 3-77 (759,094) Drawing below.) [ ] US 4,133,038-In the froth flotation beneficiation of copper sulfide ore or other ores, an aqueous suspension of a mineral sample of uniform grain size and composition is conditioned with a strongly adsorbable collector in an amount which is a fraction of the amount sufficient to create a monomolecular layer on the mineral grains, and the conditioning continued until the entire amount of collector is adsorbed The conditioned pulp is subjected to flotation, the floated particles separated at timed intervals, and the flotation rate coefficient determined. By varying the degree of adsorption in repeated treatments, the dependence of the flotation rate coefficient on the degree of adsorption may be determined A Nieml Jan 2, 1979 10 pp (364-502) Filed 12-7-77 (858,353) Priority Finland, 5-26-75 (75/1,525) Same: British 1,533,723, dated Nov 29, 1978 Same Canadian 1,065,066, dated Oct 23, 1979 US 4,133,746System and method for maintaining substantially steady state conditions in the froth flotation beneficiation of copper ore, molybdenum ore, or other metal ores The mass flow of flotation concentrate from the cell is monitored continuously, and the rate of admission of aeration air into the pulp in the cell is varied inversely with respect to variations in the mass flow control of rougher flotation cells is accomplished with a single valve G W Dopson, assigned to Magma Copper Co Jan 9, 1979 6 pp (209-1) Filed 11- 23-76 (744,306

Jan 1, 1980

By Frederic Benard

Recovery of selenium and tellurium at Copper Cliff by the Ontario Refining Co. has been previously described by the writer.l During 1935 a new building was erected to house this operation and description of the new plant and process form the subject of this paper. The building, of modern steel and tile construction, covers an area of 5900 sq. ft. with a volume of approximately 166,000 cu. ft. The large monitored center bay is flanked by two smaller outside bays, one of which is devoted to the tellurium section. All equipment, ceilings and upper walls, are treated with aluminum paint, giving good illumination and facilitating good housekeeping, essential from a health standpoint in handling material of this nature. Equipment Layout and type of equipment conforms to the requirements of the process as described below. In the selenium section, storage tanks, neutralizing tanks and precipitators are of steel construction, lead-lined and arranged for gravity flow (Fig. 1). The neutralizing tanks are equipped with water-cooled lead coils for controlling solution temperature, agitation being accomplished with compressed air. The precipitators are provided with mechanical agitators, and sulphur dioxide is introduced into the solution through 1/2-in. lead pipes leading from a manifold attached to the cover of the precipitator. Each precipitator has internal cooling coils and an air-jet exhauster to carry off fumes. Neutralized solutions are filtered in a 29-plate wooden filter press using heavy cotton duck as a filter medium, forced feed being maintained by a Welmet centrifugal pump. Dilute solutions are concentrated by evaporation in a vacuum evaporator, constructed of cast hard lead. Heat is supplied by an outside steam chest operating under 15 Ib. steam pressure. The solution is circulated through the steam chest by a pump of antimonial lead at a rate approximating 400 cu. ft. per min. The evaporator is evacuated by a water-jet condenser that creates a vacuum of 26 in. of mercury under normal operating conditions. The capacity of the vessel is 60 cu. ft. and the rate of evaporation 25 cu. ft. per hour.

Jan 1, 1943