By Albert Sauveur

This paper explains the possibility of using advantageously a boiling solution of sodium picrate to reveal dendritic segregation in steel. The mechanism of the action of the reagent is described. The failure of manganese alone to produce persistent dendritic segregation is also considered. IRON, like other metals, solidifies through the formation of dendritic crystals; iron alloys forming solid solutions, like other solid solutions, solidify likewise through the formation of dendritic crystals. The alloying elements or impurities as well as the inclusions segregate generally in the interstices, or "fillings," between the axes and branches of the dendrites; that is, in the portions last to solidify. This results in dendritic segregation or heterogeneity, which is generally persistent and makes possible the revelation of the dendritic crystallization of the metal through the selective action of a suitable etching reagent.1 For this purpose, a cupric solution, such as Le Chatelier's, is generally used, copper being deposited on the pure, or relatively pure, ferrite present in the axes while the fillings remain free, or relatively free., from copper deposition. The dendritic structure, formed on solidification in a steel containing 0.50 per cent. carbon, 0.37 per cent. manganese, 0.12 per cent. silicon, 0.07 per cent. sulfur, and 0.035 per cent. phosphorus is shown, after treatment with Le Chatelier reagent, in Fig. 1 under a magnification of 8 diameters. Commercial steel always contains inclusions of manganese sulfide, which are located in the fillings of the dendrites. Comstock has shown that boiling sodium picrate imparts a dark coloration to these inclusions. We find that this reagent likewise reveals dendritic segregations in commercial steel, as shown in Fig. 2, under a magnification of 8 diameters, which represents the same spot as that shown in Fig. 1. The fillings

Jan 2, 1924

By C. O. Burgess, W. D. Forgeng

DESPITE the increasing interest in and the technical importance of iron-chromium-manganese alloys, very little published information is available regarding their constitution. F. M. Becket's paper1 in 1930 represents the first correlated effort in the field of these alloys. The paper served particularly to draw attention to the commercial possibilities of iron-rich alloys containing chromium and manganese in balanced proportions. The duplex structure of alloys within the commercial range was briefly discussed, but exposition of their structural constitution was necessarily limited because the physical properties and corrosion resistance of the alloys were the main subjects of the paper. Both prior to and following the publication of F. M. Becket's paper, and at his instigation, an extensive investigation of the constitution of iron-chromium-manganese alloys of commercial purity was in progress at the Union Carbide and Carbon Research Laboratories, Inc. The present paper is based on the results of that investigation. In the last few years, investigations covering various portions of this alloy system have also been made in Europe. W. Koester briefly mentioned the effect of annealing on chromium-manganese steel2 and later3 constructed approximate sections of the iron-chromium-manganese equilibrium diagram. M. Schmidt and H. Legat14 even more recently studied this system, and their article and conclusions are of interest as representing an entirely independent study of a number of iron-chromium-manganese alloys. Koester's sections are shown in Fig. 1. The figures summarize the effect of manganese additions to iron alloys containing 5, 10, 15 and 20 per cent Cr as well as the effect of increasing chromium content on iron alloys containing 3, 8, 20 and 30 per cent Mn. These diagrams, within their composition limits, substantiated in some measure the results of our investigation. However, in our work some differences as regards the position of the mixed alpha-gamma fields were found as compared to Koester's work, and we were able to detect the presence of

Jan 1, 1938

By G. Krauss, W. Pitsch

The fine structure of the bcc martensite formed in an Fe-33 wt pct ATi single crystal of arrstenite is sho~on by transmission electron microscoPy to consist of combinations of transformation twins, stacking faults, deformation twins, and regular arrays of parallel screw dislocations. These structures constitute evidence for the multiple lattice-invariant deformations which operating during the formation of martensite could produce the real habit-plane scatter measured by a two-surface analysis of the plates formed in the single crystal of this investigation and reported in the literature for other Fe-Ni rnartensites. CRYSTALLOGRAPHIC theories1,2 of martensitic transformation show that the habit plane of martensite in a parent lattice is dependent in part upon an inhomogeneous distortion or lattice-invariant deformation which takes place on a fine scale within a martensite plate during its formation. Several recent theoretical papers3,4 have addressed themselves to an analysis of a wide variety of conceivable lat-tice-invarient deformations and the habit planes which they produce, while experimental investigation have been concerned with either the measurement of habit planes or the description and identification of the martensitic fine structure which reflects the nature of the lattice-invariant deformation operating during transformation. In Fe-Ni alloys with subzero Ms temperatures, the group of alloys with which this paper concerns itself, habit planes have often been found to scatter an amount greater than might be expected from possible experimental errors,5-7 and fine twinning has been identified as a major constituent of the fine structure of martensite.8-11 It has been suggested3,4 that more than one type of invariant shear occurs during martensitic transformation. This possibility has been experimentally supported12,13 by the observation of both dislocation configurations and twinning in a single martensite plate. The purpose of this paper is to report additional evidence for multiple lattice-invariant deformations in martensite and so to account for the real scatter in the habit planes of the martensite plates formed in Fe-Ni alloys. EXPERIMENTAL PROCEDURE The Fe-Ni single crystal was produced by pulling a high-purity iron and nickel charge through a single-crystal vacuum furnace in an alumina crucible. The crystal was double-melted to promote homogeneity and to increase its size by further additions on the second pass. In its final form the crystal was 4 cm in diam and 5 cm long. The nickel and carbon contents were analyzed at 32.9 and 0.006 wt pct, respectively. The austenite of this alloy first transformed to martensite by bursts at about -120°C, and, to preserve as much of the austenite as possible, all transformation was performed just below -120°C. Some observations were made on transformed samples which had been heated for 2 min at 340°C. It is assumed that the features of the martensite of these samples, Figs. 1 and 4, are the same as those of the as-quenched martensite. Orientation of the crystal by X-ray diffraction established 10.735 0.609 0.3161? as the axis of the crystal, an orientation that was checked within 2 deg by neutron diffraction. Further checks by electron diffraction of samples cut normal to the axis confirmed this orientation within the larger limits of error inherent in electron diffraction of thin foils. The X-ray orientation was the one used for the two-surface analysis of the martensite habit planes. A two-surface analysis was performed on the quadrant of the single crystal which had been oriented by both X-ray and neutron-diffraction techniques. Photomicrographs at X50 were made on two surfaces along an edge 2 cm long. Fiducial marks and the fact that many of the plates were almost completely surrounded by retained austenite made good matching of individual plates on two surfaces possible. The habit-plane trace on a surface was taken as the best line parallel to the long axis of a plate. A measure of the accuracy afforded by this criterion was provided by a family of very large plates which appeared at intervals along the entire 2 cm length of the edge. The plates all had habit-plane traces within 2 deg of one another. Many of the plates did not show midribs and, therefore, the use of midribs7 to represent habit-plane traces was not feasible in this investigation. The over-all experimental accuracy is estimated to be better than ±2 deg. Samples for transmission examination in a Siemens Elmiskop I at 100 kv were prepared by cutting 2-mm-thick discs from the single crystal, removing about 0.5 mm by chemical polishing,14 trans-

Jan 1, 1965

By G. K. Manning, E. R. Stein, E. E. Underwood

Columbium, carbon. and nickel additions were made to iron-base alloys with 20 pct CY. The effects on microstructure, precipitation-hardening characteristics, and High-temperature properties were investigated by means of metallographic, hot-hardness, and magnetic measurements. An austenitic alloy consistilzg of Fe-20Cr-14Ni-0.8C-2.5Cb had higher hot-lzaciness at 1700°F than the other alloys investigated. Its favorable standing is attributed to an enhanced interaction of Cb and Cr4C particles dispersed within a stable austenitic matrix. FOR the past 20 years, cobalt- and nickel-base alloys have been used for the more stringent high-temperature applications because of their excellent creep resistance. Although their performance is quite satisfactory, other base materials must be considered for large tonnage, low-cost applications such as for the automotive gas turbine. Iron-base alloys are also used extensively, but at somewhat lower temperatures, primarily because of the instability of particles or because precipitation occurs at relatively low temperatures. Since unusual stability has been reported for Fe-Cb and Cb-C compounds.1-3 it was hoped that effective amounts of these compounds could be taken into solution at temperatures just below the melting range, then precipitated upon reheating. Actually, strengthening was found to occur by both precipitation hardening in some alloys and by phase transformations in others. Among the alloys investigated, that with the best high-temperature properties owes its strengthening to a combination of carbide particle interaction and a relatively stable austenitic matrix. EXPERIMENTAL PROCEDURES Small preliminary melts of about 100 g were made in a vertical Glotube furnace, using alundum crucibles and an argon atmosphere. Alloys weighing 35 lb were melted in a basic-lined induction furnace, also under argon. The compositions of the alloys are given in Table I. The nickel-free alloys were usually ferritic, while those containing nickel were generally austenitic. Depending upon the particular heat treatments, or the combination of alloying elements, two-phase alloys of ferrite and austenite could be obtained. In the following text, however, the nickel-free or nickel-bearing alloys are referred to simply as either ferritic or austenitic alloys respectively. The small ingots were swaged at 2000°F, in steps, to rods of approximately 3/16-in. diam. The large ingots were forged at 2100°F to 1-in. sq bars. No difficulties were encountered in swaging or forging any of the alloys to as much as 90 pct reduction in area. For heat treating at temperatures above 2000°F, specimens were sealed in quartz tubes under a partial pressure of helium. No special precautions were found to be necessary at lower temperatures. Intermetallic compounds in the preliminary alloys were identified by means of X-ray diffraction measurements. Correlation of these results with micro-structural characteristics (such as color, shape, size, and location) of the compounds aided in their identification. Magnetic susceptibilities were also obtained at room temperature with a Magne Gage instrument after the various heat treatments. To

Jan 1, 1962

By F. E. Jaumot, R. L. Smith

Self-diffusion in zinc has been used as an instrument for comparison of the absorption and sectioning techniques as a means of studying diffusion. Single crystal as well as poly-crystal samples were used asanda the temperature range of diffusion extended from 200° to 415°C. For temperatures above 200°C, the data indicate that the results obtained from the absorption technique agree with those obtained from the sectioning technique. The effect on the values of the diffusion coefficient of electroplating vs evaporation as a means of applying the tracer was investigated and no significant difference observed. It was found that an excess or deficiency of tracer did not materially affect the results obtained from the sectioning technique, but invariably caused errors with the absorption technique. NEARLY all self-diffusion experiments and many alloy diffusion experiments have employed radioisotopes as the instrument for following the diffusion. Of the various techniques in which radioisotopes are applicable, the two most widely used are the sectioning and absorption techniques. In the former, the diffusion coefficient is obtained from a curve of log concentration vs the square of the mean penetration depth. In the latter, the diffusion coefficient is calculated from a knowledge of the decrease in activity at the surface after diffusion. In spite of the importance of knowing the reliability of the diffusion data and the widespread use of these two techniques, they had not been directly compared experimentally on the same samples. Thus, such a comparison was worthwhile. The specific system chosen for this comparison was the self-diffusion of zinc, since the metal was readily obtainable in high purity, single crystals were easily grown, and the anisotropic features of the diffusion added an additional factor of interest to the comparison. Self-diffusion in both single and polycrystals was investigated, since the possibility existed that grain boundaries and grain boundary diffusion might produce different effects for the different techniques. Also, the effects of electroplating vs evaporation as a means of applying the radioactive tracer, and the effects of applying an excess or deficiency of tracer material were studied. The general experimental procedures and the mathematical analyses of both techniques have been described previously in some detail, and only those points essential to an understanding of the present work will be discussed here. The mathematical analysis of the sectioning data requires only a knowledge of the solution of Fick's equation. where C,, is the initial concentration, C is the concentration at depth x, D is the diffusion coefficient, and p is the absorption coefficient of the solvent metal for the radiation from the solute. Having obtained F from the experiment, the value of z can be read from a plot of F vs In z, and D can then be calculated if is known. The necessity of knowing the absorption coefficient causes most of the criticism of the absorption technique. It is very difficult to measure accurately under the conditions existing in the diffusion experiment, but it is absolutely necessary, as will be indicated briefly later. Portions of this problem have been discussed in detail elsewhere." The difficulties involved in the measurement of the absorption coefficient arise from three principle factors: the physical characteristics of the absorber, the geometry, and complex radiation spectra. The first two are heavily dependent upon the third. If

Jan 1, 1957

By Charles C. Russell, Glenn C. South

A primary factor in the selection of coals for making coke at high temperatures is the amount of pressure the coal will exert upon the oven walls when carbonized in modem by-product ovens.l-3 This factor has become increasingly important in recent years because of demands for increased throughput and higher coke yields. As a result of the increasing necessity for assessing coals in regard to their carbonization pressures, more and more research work is being directed toward developing labora-tory-scale tests for predicting carbonization pressures and for showing how blends of coking coals may be modified to eliminate pressures liable to damage coke-oven walls. The specific reasons have never been defined as to why some blends of coking coals develop dangerous carbonization pressures and others do not, therefore specific procedures to eliminate dangerous pressures could not be prescribed. It is true that the major processes occurring during carbonization have been described by many writers,4 and there is a general agreement on the ideas of the changes that occur as coal is transformed into coke. However, there is little evidence relating the processes occurring during carbonization to the pressure developed and the available evidence is very incomplete and often contradictory. This deficiency arises in part from the fact that the fundamental causes of pressure development have not been defined, at least from experimental data, and in turn this is the result of the lack of satisfactory testing equipment for studying the problem. Operating experience has shown several ways of reducing or eliminating dangerous pressures,5 but probably none of these ways is applicable to all blends of coking coals, and such empirical methods often lead to production of inferior coke. They are trial-and-error methods, not designed to remedy specific causes of pressure development. The number of laboratory-scale testing devices designed to estimate the carbonization pressures that result when coals are carbonized in commercial ovens is probably well over a hundred.6 Few of these instruments have remained in use for any length of time, either because the predictions were not sufficiently accurate or, more often, because too many exceptions were found. Often testing devices are operated without any attempt at duplication of conditions in commercial ovens and erroneous and contradictory results are frequently obtained. Therefore, it has seemed desirable to study the properties of coal itself and to determine any relationships between the properties of the coal and the carbonization pressures developed. Relationship between Properties of Coal and Carbonization Pressure Attempts to determine relationships between various properties of coal and carbonization pressures, for the most parti have been indirect because no satisfactory and reliable laboratory testing device has

Jan 1, 1944

By Paul T. Allsman, E. W. Newman

Trenching, sampling, and core drilling in Stillwater and Sweetgrass Counties, Mont., by the Bureau of Mines have delimited over 5,000,000 tons of chromite ore containing more than 20 per cent chromic oxide. The Benbow and Mouat-Sampson mines have been developed and are fully equipped for mining and milling 500 tons and 2000 tons a day, respectively. Introduction The Montana chromite deposits were the first to be explored under the Strategic Minerals Act of 1939. In June of that year, the Bureau of Mines started exploration by trenching, test pitting, sampling and diamond drilling, and completed the project in March 1943. The U. S. Geological Survey cooperated by mapping the geology and logging the cores. The project was to determine the extent and grade of the chromite ore and to indicate sufficient reserves to justify development and exploitation of the deposits for the national emergency. Exploration has indicated that the district contains the largest and most important reserve of chromite ore in the United States. The Benbow and Mouat-Sampson mines have been developed and a 500-ton concentrating mill has been constructed on the Benhow property and a 2000-ton mill on the Mouat-Sampson property. Concentrates were produced from the Benbow mill three months after the attack on Pearl Harbor, when the nation's major chromite supplies from foreign sources were cut off. History It has been known for 50 to 60 years that some chromite deposits existed in an east-west belt along the north escarpment of the Beartooth Mountains about 25 miles north of Yellowstone Park, but nothing was known of their size and extent until the war demand of 1917 and 1918 stimulated the search. In those years two properties in the Stillwater region were actively developed, but no shipments were made. The Benbow property was located in 1918 by a local group. The property comprised seven claims along the strike at the east end of the belt. An adit was driven several hundred feet on the Eclipse claim. The seven claims were sold to the Chromium Products Corporation of Livingston, Mont., and were subsequently patented. In 1929, an eastern group obtained an option, installed some equipment, and erected several log cabins. The "crash" in the market in 1929 caused the operators to drop their lease, and the property remained inactive until 1939, when the Bureau of Mines began its exploration. Fourteen claims were located on the Boulder River in 1918 and subsequently patented by the U. S. Chrome Corporation.

Jan 1, 1949

By Bernhard Blumenthal

A melting process was developed by which high purity electrolytic uranium crystals can be converted into sound ingots without serious contamination. Careful preparation of the crystals, melting in a high vacuum, and directional solidification led to a metal of better than 99.993 wt pct purity. The metallographic examination showed a substantially clean metal with only residual amounts of a second phase which responded to heat treatment. The density of high purity uranium is 19.05 g per cu cm. FOR the study of the fundamental properties of uranium and its alloys, a base metal of high purity is needed, and an investigation was started at Argonne several years ago to examine various methods of preparing high purity uranium. Early success was achieved by the fused salt electrolysis process in preparing high purity metal in crystal form,' and the problem became that of melting the crystals into ingots without contamination. The electrolytic crystals contained a few ppm of heavy metals, less than 15 ppm C, and large quantities of potassium and lithium in the form of trapped fused salt electrolyte. On melting in vacuo in magnesia or urania crucibles, the metal picked up considerable quantities of carbon and some iron, copper, and silicon but lost most of the potassium and lithium. It was not metallographically clean, and much research work was necessary to determine the optimum melting conditions for minimum contamination. This work has resulted in the development of a melting procedure by which sound ingots can be prepared with only a limited contamination by carbon. In the section entitled "Melting of the Electrolytic Metal," the equipment and processes that have been developed for melting the electrolytic crystals are described in detail. The "Metallography" section is devoted to the metallography of high purity uranium, and the section "Density of High Purity Uranium" contains the first property measurement on high purity uranium—a density determination. Melting of the Electrolytic Metal Apparatus—Melting and Vacuum Equipment: Uranium may be melted in either resistance or induction-type electric furnaces. Resistance heating was found to be preferable to induction heating for melting down the electrolytic crystals, for several reasons: Although induction heating permits fast heating, this advantage cannot be utilized when crucibles with limited thermal shock resistance are used. Temperature control of induction-heated melts is poor, and the stirring effect increases the rate of contamination of the melt from the crucible, slag, or the furnace atmosphere; liquation and controlled solidification are difficult to carry out. Because of these objections, resistance heating was chosen. A 10 kw Globar resistance furnace of low heat capacity permitted uniform heating of a uranium charge to its melting point in 45 min. The furnace was insulated with a removable aluminum shield so that, after melting and removal of the shield, the furnace could be quickly cooled to room temperature. The furnace was equipped with an apparatus for directional solidification; see Fig. la. The crucible was suspended in the center of the furnace; and when the melting was complete, the crucible was slowly lowered into the cold end of the furnace tube. Solidification took place upward from the bottom; and when the rate of lowering was small, a sound ingot free from sink holes and shrinkage cavities was produced. To remove the large quantities of gas contained in the electrolytic crystals, melting in a high vacuum is mandatory. While, from the standpoint of contamination, melting in a highly purified argon atmosphere appeared feasible, lithium and potassium removal proved less efficient under such conditions. Also, a vacuum-melted ingot has a cleaner surface than one melted in an inert atmosphere. The vacuum system must be of very high pumping speed and leak tight so that a vacuum of less than 2x10-7 mm Hg is attainable when the system is pumped down cold. The system must have a high pumping speed, so that the pressure maximum which may rise to 1x10-4 mm during heating can be quickly reduced

Jan 1, 1956

By A. J. McEvily, R. C. Boettner, C. Laird

The processes leading to fatigue failure in the low-cycle range were studied to obtain an understanding of the basis of Coffin's law. Particular attention was paid to the manner of mack nucleation and to the determination of the portion of the total lifetime spent in crack propagation. It was observed that cracks are nucleated at surface notches meated during reversed plastic deformation, Principally at grain boundaries, and that crack growth occupies greater than 75 pct of the fatigue life. When inclusions are present, they are often the primary sites of crack initiation. From consideration of the incremental distances advanced by a crack in each cycle and of the lifetimes of different materials, it appears that the universality of Coffin's law arises from the similarity of crack-tip strain for a given applied strain amplitude, irrespecti7:e of material. STUDIES of low-cycle fatigue have been particularly rewarding in that a simple correlation between fatigue lifetime and plastic-strain range has been shown to exist. This empirical relationship takes the forml,2 Nner=C [1] where N is the number of cycles to failure, Er is the plastic-strain range defined as the total plastic strain per cycle (the sum of the tensile plastic strain plus the compressive plastic strain), n, the exponent, is a constant independent of the material to a first-order approximation and often has a value of about 0.5, and C is a constant which for a number of ductile and metallurgically stable materials is approximately 0.65 for fully reversed strain.3 This relationship has been shown to be valid for a wide variety of metals and alloys and is often referred to as Coffin's law. However, it is yet not clear why so many different metals and alloys exhibit the same over-all behavior in the low-cycle range. Less is known about the mechanisms of fatigue failure in the low-cycle range than in the high-cycle range, but it is expected that the processes would have much in common. For example, an important characteristic common to both high-and low-cycle ranges is that fatigue crack propagation can occupy a considerable portion of the total lifetime. This has been shown by Laird and smith4 by a count of the number of ripples present on the fracture surface of copper specimens, each ripple corresponding to one cycle of load. On the other hand, some marked differences have been noted. For example, in copper,5 nickel, and aluminum4 there is a greater tendency for grain boundary cracking to occur as the strain amplitude is increased. The purpose of the present work was to study further the processes leading to fatigue failure in the low-cycle range and to obtain an understanding of the basis for the validity of Coffin's law. Particular attention has been paid to the manner of crack initiation and to the determination of the portion of total lifetime spent in crack propagation. MATERIALS A number of metals and alloys were tested, although more attention was focused on a particular few, once general trends had become apparent. Alloys were selected so as to investigate the effects of crystal structure, number of phases, stacking-fault energy, and impurity content. The materials in this grouping were: high-purity copper OFHC copper 1100 aluminum (commercially pure) 70-30 brass (Cu-30 wt pct Zn)

Jan 1, 1965

By P. L. Russell

The use of nuclear explosives for excavation has been demonstrated to be feasible and practical. Application of nuclear explosives for overburden removal from large ore deposits appears to offer economic advantages over present methods, but under the present pricing schedule, high-yield devices must be used to obtain an economic advantage. The use of nuclear explosives presents problems not inherent in the use of conventional explosives, and thus they can be used only in areas where large explosions and associated phenomena can be tolerated. Stripping of coal with nuclear explosives does not appear practical at this time, but stripping overburden from copper or iron ore deposits may be a potential use. Even here, however, the use of nuclear explosives would require isolation, favorable topography, favorable ground-water conditions, and a low population density. If these basic requirements can be met, the use of nuclear explosives for overburden removal would offer both economic and time advantages. The possibility of using nuclear explosives for peaceful purposes was a subject for speculation as early as 1945. The PLOWSHARE Program was formally established by the AEC in June 1957 for the purpose of developing and demonstrating peaceful applications for nuclear explosives. The technical direction of the program is the responsibility of the Lawrence Radiation Laboratory, Livermore, Calif. Mining and excavation were two fields that received early consideration as areas in which nuclear explosives might be used. Knowledge gained from underground weapons testing increased this possibility, and the development of the thermonuclear device which has a small fission-to-fission ratio, reduced the hazard of radiation, and spurred interest. Nuclear explosives appear to have the greatest potential in the following mining operations: 1.— Surface Mining a) Stripping of waste for open-pit excavation b) Breaking of ore in open-pit mining c) Quarrying d) Blasting for production of aggregate, riprap, etc. 2. — Underground Mining a) Block caving application b) Crushing of ore for in-situ leaching, etc. c) Preparation of underground waste disposal areas Of the potential applications, excavation is perhaps the most obvious and the best understood, and probably the most practical for use in the near future. Large quantities of rock and earth can be moved by proper emplacement of nuclear explosives, but economic and practical relationship must be determined between the known capabilities of nuclear explosives and the required excavating to remove overburden. REMOVING OVERBURDEN IN OPEN-PIT MINING Removing the overburden is one of the largest jobs in open-pit mining. In 1960 open-pit mines produced approximately 130 million tons of coal, 108 million tons of copper ore, and 135 million tons of iron ore. To obtain this much production, an estimated 3-billion tons of overburden were removed from the coal, 216 million tons from the copper ore, and 135 million tons from the iron ore. These figures do not include the initial stripping required before ore production. For example, the ASARCO Mission mine started stripping operations in August 1959 and by mid-November 1961 had removed 46.3 million tons of material including 1.2 million tons of ore.* Initial excavation of this type offers the most favorable conditions for utilizing the earth-moving ability of nuclear explosives. EXPLOSIVE CASTING FOR REMOVING OVERBURDEN The use of explosives to remove overburden is not a new idea. Conventional explosives have been used for this purpose for many years with varying degrees of success. Several small coal strip operators have used this idea to increase production. At these mines about one-third or more of the overburden is thrown by explosives across the pit and onto spoil piles. The additional costs of drilling more blast holes and more explosives are more than compensated for by a reduction in the time required to uncover the coal, and by an increase in coal production.

Jan 1, 1964

By H. A. Koch, R. L. Slobod

This paper discusses a new oil recovery process called the "miscible slug process." This process involves the injection of propane or LPG into the reservoir prior to gas injection. The operating conditions are maintained so that the slug is miscible with both the reservoir oil and the injected gas phase. Thus, a miscible phase displacement is achieved, and high recoveries are obtained from the area of the reservoir contacted. The most striking discovery of the laboratory study which included displacements from cores up to 123 ft in length was that relatively small slugs of LPG are effective over reservoir distances in the miscible displacement of oil. This makes possible the commercial application of the process. The important factors controlling the size of the slug are: (I) reservoir length, (2) reservoir fluid composition, and (3) reservoir pressure at the displacement front. Of lesser importance are the effects of injection rate and porous medium type. Questions which have not been completely answered deal with the effects of gravity and reservoir inhomogeneities on the process. INTRODUCTION One of the major problems facing the oil industry today is recovery of the large fraction of the discovered oil which will remain unrecovered unless some new processes are found. Water flooding has been one successful method used to increase recovery over natural depletion. But even successful water floods may leave 25 to 40 per cent of the pore space filled with residual oil. Recently a process which involves the use of thermal energy has been reported1,'*' which may prove useful in increasing recovery from shallow reservoirs containing highly viscous crudes. This paper deals with a new oil recovery process involving use of miscible phases to displace the oil from the reservoir. Miscible phase displacement oil has been an intriguing idea because the elimination of capillary effects in the reservoir leads to 100 per cent recovery in the areas contacted by the miscible displacing phase. The big deterrent in the past to the practice of miscible phase displacement has been the high cost involved in using large volumes of solvent in the process. The use of high pressure gas to achieve a miscible phase displacement of reservoir oil has been reported4,5 as one economically feasible method. However, this process calls for the maintenance of pressures above 3,000 psi at the dis-placement front. The process described in this paper is not restricted to high reservoir pressures; the only qualification being that the slug of material which is injected into the reservoir must be miscible with both the displaced oil 2nd the displacing phase. Two such cases are the use of an alcohol slug followed by water to achieve a mis-cable water flood, and the use of a low boiling hydrocarbon slug such as propane followed by gas to achieve a miscible gas drive. This paper will deal specifically with the propane dug process. This process will obtain a miscible phase displacement at pressures as low as about 1,200 psi at a reservoir temperature 01 150°F. The process is very simple. The propane displaces oil completely at one front because it is miscible with the oil, and gas displaces the propane completely at a second or trailing front because it is miscible with the propane. A small band of propane should thus remain wedged between the gas and oil phases. This idea has been called the "miscible slug process."6 Unfortunately, the propane slug will become diluted as it flows through the reservoir. This results from a mixing action since the fluids flow through a complex reservoir porous medium rather than simple capillaries. Fig. 1 diagrams a miscible slug displacement. The effects of some of

Jan 1, 1958

By Glenn C. South, Charles C. Russell

A primary factor in the selection of coals for making coke at high temperatures is the amount of pressure the coal will exert upon the oven walls when carbonized in modem by-product ovens.l-3 This factor has become increasingly important in recent years because of demands for increased throughput and higher coke yields. As a result of the increasing necessity for assessing coals in regard to their carbonization pressures, more and more research work is being directed toward developing labora-tory-scale tests for predicting carbonization pressures and for showing how blends of coking coals may be modified to eliminate pressures liable to damage coke-oven walls. The specific reasons have never been defined as to why some blends of coking coals develop dangerous carbonization pressures and others do not, therefore specific procedures to eliminate dangerous pressures could not be prescribed. It is true that the major processes occurring during carbonization have been described by many writers,4 and there is a general agreement on the ideas of the changes that occur as coal is transformed into coke. However, there is little evidence relating the processes occurring during carbonization to the pressure developed and the available evidence is very incomplete and often contradictory. This deficiency arises in part from the fact that the fundamental causes of pressure development have not been defined, at least from experimental data, and in turn this is the result of the lack of satisfactory testing equipment for studying the problem. Operating experience has shown several ways of reducing or eliminating dangerous pressures,5 but probably none of these ways is applicable to all blends of coking coals, and such empirical methods often lead to production of inferior coke. They are trial-and-error methods, not designed to remedy specific causes of pressure development. The number of laboratory-scale testing devices designed to estimate the carbonization pressures that result when coals are carbonized in commercial ovens is probably well over a hundred.6 Few of these instruments have remained in use for any length of time, either because the predictions were not sufficiently accurate or, more often, because too many exceptions were found. Often testing devices are operated without any attempt at duplication of conditions in commercial ovens and erroneous and contradictory results are frequently obtained. Therefore, it has seemed desirable to study the properties of coal itself and to determine any relationships between the properties of the coal and the carbonization pressures developed. Relationship between Properties of Coal and Carbonization Pressure Attempts to determine relationships between various properties of coal and carbonization pressures, for the most parti have been indirect because no satisfactory and reliable laboratory testing device has

Jan 1, 1944

By Paul T. Allsman, E. W. Newman

Trenching, sampling, and core drilling in Stillwater and Sweetgrass Counties, Mont., by the Bureau of Mines have delimited over 5,000,000 tons of chromite ore containing more than 20 per cent chromic oxide. The Benbow and Mouat-Sampson mines have been developed and are fully equipped for mining and milling 500 tons and 2000 tons a day, respectively. Introduction The Montana chromite deposits were the first to be explored under the Strategic Minerals Act of 1939. In June of that year, the Bureau of Mines started exploration by trenching, test pitting, sampling and diamond drilling, and completed the project in March 1943. The U. S. Geological Survey cooperated by mapping the geology and logging the cores. The project was to determine the extent and grade of the chromite ore and to indicate sufficient reserves to justify development and exploitation of the deposits for the national emergency. Exploration has indicated that the district contains the largest and most important reserve of chromite ore in the United States. The Benbow and Mouat-Sampson mines have been developed and a 500-ton concentrating mill has been constructed on the Benhow property and a 2000-ton mill on the Mouat-Sampson property. Concentrates were produced from the Benbow mill three months after the attack on Pearl Harbor, when the nation's major chromite supplies from foreign sources were cut off. History It has been known for 50 to 60 years that some chromite deposits existed in an east-west belt along the north escarpment of the Beartooth Mountains about 25 miles north of Yellowstone Park, but nothing was known of their size and extent until the war demand of 1917 and 1918 stimulated the search. In those years two properties in the Stillwater region were actively developed, but no shipments were made. The Benbow property was located in 1918 by a local group. The property comprised seven claims along the strike at the east end of the belt. An adit was driven several hundred feet on the Eclipse claim. The seven claims were sold to the Chromium Products Corporation of Livingston, Mont., and were subsequently patented. In 1929, an eastern group obtained an option, installed some equipment, and erected several log cabins. The "crash" in the market in 1929 caused the operators to drop their lease, and the property remained inactive until 1939, when the Bureau of Mines began its exploration. Fourteen claims were located on the Boulder River in 1918 and subsequently patented by the U. S. Chrome Corporation.

Jan 1, 1949

By H. E. Lee, P. C. Feddersen, D. R. Gittinger, G. W. Dunn, J. B. Schuettenhelm

The new Bunker Hill slag-treatment plant, designed ior, a capacity of 300 to 400 tons of hot slag per day, was "blown in" April 5, 1943. In the ensuing I5-months period, 157,530 tons of slag was processed, with an average recovery of over go per cent of the zinc and practically all of the lead contained. In addition to this high metal recovery, utilization of the waste heat in the gas and fume venting, the process has enabled the generation of 231,376 tons of steam at 250-lb, gauge. Over the first six months opcration the volume of slag treated averaged somewhat under 300 tons per day. Reclaimed dump slag made up only about 1 5 per cent of the plant feed. In October 1943, preparations for the smelting of additional tonnages of dump slag were completed and the plant capacity was increased to an average of about 420 tons of slag per day. During the nine-months interval since that date, monthly averages of 450 toils per operating day have been maintained several times. The new plant (Fig. I) is constructed in close proximity to blast-furnace operations. The fuming furnace and other necessary equipment are housed in an eastward extension of the existing blast-furnace building. Beyond this housed extension the dust-laden gas is conveyed about the perimeter of a large rectangle formed by the flues, cooling towers and baghouses. The course of a 10-ft. balloon flue, which transports the fuming furnace gas, describes the west and south perimeters. This flue connects with a set of cooling towers located at the southeast comer. The flue and cooling-tower system serving the deleading kiln constitute the north side and the two baghouses, serving the kiln and furnace operations, -border the east side. From these baghouses the several discharge gas flows are come biped and conveyed in to the rectangle, being vented to atmosphere by means of a fan through a centrally located zoo-ft. brick stack. In general, the plant design and operation follow quite closely that dictated by experience gained in years of slag-fuming practice by the Anaconda Copper Mining Go., at East Helena, Mont., and the Consolidated Mining and Smelting Co. of Canada, Ltd., at Trail, B.C., and more recently by the International Smelting and Refining Co. at Toocle, Utah. : Fuming operations at the East Helena and the Tooele plants are more or less identical. Trail practice differs chiefly in the methods employed for the storage of the hot feed slag and in the methods utilized for the handling and cooling of the fuming furnace gas. The new Bunker Hill fuming plant closely follows Trail procedure in the treatment of the furnace discharge gas while East Hclcna methods have been adopted for the storage of feed slag.

Jan 1, 1944

By Graham Bright

Before the arrival of central-station power, all coal and metal mines generated their own power and, in many cases, these isolated power plants gave a fair continuity of service. In coal mines that produce considerable gas, it is essential that power be available at all times for operating the ventilating fan and the hoist, if the mine is of the shaft type. In the case of an isolated power plant, if trouble should develop with the fan the men can be hoisted quickly when the mine is of the shaft type. On the other hand, if trouble develops with the hoist, the fan can be kept in operation, and there will be no necessity of haste in getting the men from the mine. Now that central-station power is being used so extensively for mine service, the continuity of service with gaseous mines is very important. : Inherently, the central station is much more reliable than any isolated plant, but trouble may occur on the transmission lines which may prevent the transmission of power for a considerable time. : Some mines have kept their steam equipment intact and ready for operation in case the purchased power should fail. This is expensive procedure, for the boiler plant must be fired at all times so that the emergency power will be quickly available. In a number of instances, gasoline-engine driven generators have been installed to furnish emergency power for the service hoist. As most service hoists are of the alternating-current type, the generator of the gasoline-engine driven set is usually of the a.c. type and is arranged to drive the service hoist motor at full speed, or an extra motor that can be thrown into gear on either the main or service hoist and the hoist operated at a greatly reduced speed. This arrangement is used because it is difficult and expensive to obtain and install large gasoline-engine driven units. The author has recently developed a plan by which the main hoist and the fan can both be operated at reduced speeds, in case of loss of power from a central-station power system. In this plan a gasoline-engine

Jan 1, 1923

By H. D. Strain

Potash is a generic term used to describe a number of compounds containing the element potassium (K), which is one of the three major plant nutrients. Potash content of these compounds is commonly expressed as percentage potassium oxide (K20), and the market value of the products is usually dependent on contained K20. Most of the potash produced (approximately 95%) is used in agriculture as fertilizer. Potash products today are shipped by producing countries all over the world to meet the need for increased food production. WORLD POTASH RESERVES Apparent world potash reserves are shown in Table 15.2B.1 and total some 96 billion mt of recoverable potassium oxide. The Canadian reserves account for approximately one-half the known world reserves. The reserves shown represent the potassium oxide content of a variety of potash-bearing ores. The major ore is sylvinite (a mechanical mixture of KC1 and NaCl) from which KC1 or sylvite is recovered (63.2% K20 equivalent). Other ores, such as langbeinite (potassium, magnesium sulfate-22.7% K20) and carnallite (potassuim magnesuim chloride-17.0% K20) are also mined in various parts of the world, mainly for the potassium content. Theoretically, potassium is available in almost unlimited qualities from brines and saline waters. To date, the cost of recovery from salt brines has been greater than the costs by mining operations, but new technology could make brines and seawater an increasingly important source. POTASH PRODUCTION Potash production dates back to the 1860s in Germany, which was the only recorded producing country until 1912. By 1912 Germany was producing approximately 1 million tpy of K2O equivalent. Production began in France in 1913 and in the United States in 1915. World potash production and consumption are shown in Table 15.2B.2 for the years 1950-51 through 1967-68. In 1967 and 1968 the major potash-pro¬ducing countries in order of importance were those listed in Table 15.2B.3. By 1972 Canadian production had outstripped U.S. production. WORLD CONSUMPTION World consumption of potash for the years 1950-51 through 1967-68 is shown in Table 15.2B.2. Table 15.2B.4 shows total world consumption of potassium materials in 1967-68 by country. More than 70% of the world's potash is

Jan 1, 1976

By John V. Beall

THIS is not simply the story of how a water filled shaft was developed into a million-ton- a-year producing mine in the space of four critical years, although it is reason enough for telling it, but it is also the saga of an engineering achievement in which knowledge nurtured by years of experience in coal and ore mines was blended together and the best from each type of mining selected. The entire system of mining was detailed on maps by the mining engineering department before the shaft was unwatered, and subsequent development followed these plans nearly to perfection. The selection of machinery was particularly critical as it was necessary to push production from only a few headings in the early stages of development and metal mine machinery was being used in a coal panel-system of mining.

Jan 12, 1950

By P. H. Mell

AMONG the minerals exhibited at the Atlanta Exhibition of 1881, soapstone, kaolin, and asbestos were well represented. The first two occur in large quantities, of very pure quality, throughout the South. The last is somewhat limited in amount, get in certain localities it exists in masses sufficiently large to pay for working; in North Carolina, Georgia, and Alabama it has ken mined with some profit. I would, in this paper, call special attention to the minerals soapstone and kaolin, because their many valuable qualities seem to have been almost entirely overlooked by our Southern manufacturers. Steatite, particularly, occurs in such large quantities, and generally in such close proximity to the great iron regions of Alabama and Georgia, that it is anlazing that the iron companies will persist in sending abroad under heavy expense for firebrick. It would require a much smaller sum of money to quarry this rock and place it at the various furnaces ; and the results obtained, I am sure, would prove its superiority over the majority of firebrick brought into this region. Soapstone, as well as kaolin, is found throughout the metamorphic regions of Alabama, Georgia, South Carolina, and North Carolina. Below will be found seven analyses that I have made of this mineral, taken from various points in the four States above mentioned. I have also subjected these same specimens to severe fire-tests, and the results were very satisfactory. The tests mere canducted in the following manner: Small portions of the compact variety were carefully weighed and placed in a Fletcher's new crucible furnace for gas, and subjected for half an hour to a heat that will in 12 minutes fuse iron. The only effect upon these specimens was a slight change in color to a darker shade, a small loss in weight, due evidently to the evaporation of water, and, in one or two specimens, a slight degree of fusion on the sharp edges. The first specimen subjected to investigation was taken from a large outcropping in Tallapoosa County, Alabama. Specific gravity, 2.88 ; hardness, 1.9; color, blue gray. Composition: Water,....2.68 Silica,..........65.48 Iron oxide,.........2.10 Alumina,.........15.02 Magnesia,... 15.35 10061

Jan 1, 1882

By E. Cortese

Phosphate occurs in many places in Egypt, in two main zones: one in Upper Egypt, along the Nile Valley, principally on the right side, and one near the Red Sea coast. In the Nile zone, the principal layers of phosphate rock are to be found: in the mountains east of Mahamid (right side of the valley); in the hills near Sibaiya, also called Sebaieh (both sides); in the hills of Agula, Hagaza and Gurn (right side); and further on, along the camel road leading from Kena to Kosseir, a few miles east of Legheita's Oasis. Following that track, after having crossed the watershed, underlain by rocks like granite, serpentine, porphyry, and diabase, one comes again to the Cretaceous formation containing considerable quantities of phosphate, at Gebel Duwi, Gebel Nakheil, and Gebel Kosseir El Kadim, not far from the coast. More to the north, in the hills near Safaga Bay (Um El Uettat El Wasif) is another rich bed of the same formation. There are reports of phosphate existing near Suez and in the Sinai peninsula, and possibly some other zones can be traced or discovered in the future. The mines are well developed on the right bank of the Nile at Sharawna (near Sebaieh Station) and along the Red Sea coast, at Safaga and near Kosseir. Prospecting work has been done at Gebel Duwi, Gebel Gurn, Agula, Hagaza, and near Mahamid. The phosphatic formation in Egypt is quite variable, not only from place to place, but even within small areas. The phosphate is all of Cretaceous age, as is proved by the fossils found in it. It is considered to belong to the Campanian or, more appropriately, to the Maestrichtian series. The principal fossils are: Alectryonia Villei Coq. sp.; Roudereia Aures-sensis Coq. sp. = R. Drui Mun. Chalm.; Trigonoarca multidentata, Newton.; Cardita libyca, Zittel; Libycoceras Ismaely, Zittel; Nautilus sp.; Ancystrodon libycum Dam.; Corax pristodontus Ag.; Lamma biauriculata Zittel sp. Above the Maestrichtian beds, we have the Danian series, unconform-ably covered by Lower Eocene beds. Under the phosphate is a grayish marly clay, and beneath this, bluish-gray scaly shales resting on the Nubian sandstone (Santonian).

Jan 1, 1918

By George Langford

THE McIntyre mine is in the Pearl Lake section of the Porcupine gold area. The rocks are Keewatin lavas intruded by quartz porphyries and albitite dikes of Algoman age. Gold-bearing quartz veins are found in the Keewatin rocks near the porphyry stocks. The whole area has been highly compressed by forces acting along a N. 20°W. line. These forces folded the Keewatin rocks before the intrusion of the Algoman rocks, and later schisted both the Keewatin and Algoman rocks. Vein fractures were developed after the folding but before the development of the schist by the compres-sive forces being locally broken up into couples. These couples were set up by the differential resistance to deformation of porphyries and basalts, and also by the competency of the dacites and incompetency of the tuffs and fragmental rocks. During the important period of vein formation, two zones were developed-an inner productive zone in which the quartz veins are ankerite-bearing and an outer barren zone in which the quartz veins are calcite-bearing. The vein solutions originated in the same magma that supplied the albitite dikes.

Jan 1, 1938