Search Documents

Jan 1, 1969

By W. H. Basssett

THE amount of oxygen present in refined copper bears an important relation to the effects of various impurities on physical properties of copper, as well as the effects of reducing gases at higher temperatures. It seems fitting at this time, when the effects of reducing gases on copper are being discussed, to describe methods that have proved satisfactory for the determination of oxygen and sulfur, and to present some results obtained by investigation of these methods in the authors' laboratory. The procedure for the determination of sulfur is closely interrelated with that for oxygen and has, therefore, been included. It was first proposed by Hamper that oxides in copper could be accurately determined by the loss in weight sustained by finely divided copper when reduced at red heat in pure hydrogen, or by the weight of water produced. Hampe's method was later modified by Archbutt,2 who established the accuracy of the method and demonstrated that equally accurate results were obtained by noting the loss in weight or by weighing the water formed. The determination of oxygen by heating in carbon monoxide has been proposed by West.3 In our hands this method has given slightly lower results than obtained by heating in hydrogen.

Jan 2, 1926

By A. E. Hunt

A GREAT deal that has been written heretofore about the properties of aluminum is of doubtful value, owing to the lack of knowledge we have of the purity of the aluminum referred to. Much of the metal heretofore sold in the markets as pure aluminum has been contaminated with from 4 to 10 per cent. of impurities. Indeed, it is only within a very few years that a purer metal than 96 per cent. alumium has been made upon any larger than a laboratory scale. The works of M. Pechinet,of the Societe Anonyme d' Aluminium, at Salindres (Gard), near Marseilles, in France, have long enjoyed the

Jan 1, 1890

By L. G. Austin

The procedure for scaling breakage parameters determined in a laboratory mill to values for a full-scale mill is briefly presented. A simulation model of a closed circuit mill also requires a model of residence time distribution, a mass transfer law to predict over-filling as a function of flow rate through the mill, and a model to describe classification action. For fine dry grinding, or viscous slurry grinding, it is necessary to allow for slowing-down of breakage rates for a fine mill charge. Four examples of comparing simulation models to actual plant data are presented. The first is wet grinding of copper ore in normal closed circuit at 50 tph (metric) production, under conditions where the mill does not overfill. The second is the wet grinding of copper ore in reversed closed circuit at production of 87, 102 and 108 tph, with flow through the mill of approximately 150, 200 and 300 tph. The third is dry grinding of coal with a hot air sweeping stream to remove all of the coal as air-borne material, in open and normal closed circuit. The fourth is grinding of cement clinker in a two-compartment, air-swept tube mill in normal closed circuit with two different classifiers, producing 120 tph of 3250 Blaine cement. In all cases the simulated capacities and product size distributions were in reasonable agreement with actual plant performance.

Jan 1, 1984

By J. O. Mack, J. B. Russell

IN recent years, solders containing 20 per cent tin with no bismuth or cadmium have been developed by a few companies, and personnel have been properly instructed in their use. In addition, since the tin shortage, a number of solders containing less than 10 per cent Sn, and some with no tin, are being used in special applications; however, a solder of this type has yet to be developed that is satisfactory for general use. [ ] The purpose of this investigation was to develop an alloy containing a maximum of 15 per cent tin, with no cadmium or bismuth, having solder properties equivalent to or better than those of substitute solders now specified containing i8 to 20 per cent tin (Table I), or even approaching the properties of the standard 40 to 60 tin-lead solder. The wartime restriction of bismuth and cadmium, elements that have beneficial effects on fluidity, solidification range and strength, makes it increasingly difficult to develop a general-purpose solder containing a maximum of 15 per cent tin. In the course of this investigation, 11 elements were used in various combinations with the basic 15-85 tin-lead alloy. These elements were antimony, silver, copper, indium, thallium, lithium, calcium, barium, potassium, sodium and arsenic. In all, 116 low-tin solders were investigated, with the idea of developing a solder that will give satisfactory working properties, specifically in regard to "wetting" of copper, brass and iron, solidification range, capillarity and shear strength of a soldered joint. The relative importance of these various properties plays an important role in the search for substitute solders, since it is almost impossible to retain all of the desired qualities of a high-tin solder and still make drastic changes in the alloy composition. Because of the expected uses of a general-purpose solder, it is necessary that it have properties, especially in regard to wettability, that will enable it to be used on the metals in common use. BASIC CONSIDERATIONS The maximum liquidus temperature of a solder is determined by the particular application involved and the temperature that can be obtained by the source of heat.

Jan 1, 1944

COMPLYING with your frequently expressed wish and, your persistent request, I have decided to prepare a brief little book on metallic ores, based on ,the books of the ancient philosophers and on the experience of practicing miners, that will instruct you how to judge from promising indications which rock forma¬tions, which veins, stringers, or mineral matter are likely to bring. forth metallic ores so that it would be promising and gainful to work them. It explains according to the best of my ability, in separate chapters, as much as you need to :know for your, chosen profession or business, about such things as the favorable characteristics of the terrain, the strike, and dip* and outcrop of veins in general, and also about each metal in particular. Young Knappius: † Then it will be explained to me logically in. this little book and I shall be given a reasonable understanding which mines can be worked gainfully so that my investment will not be wasted but will show a profit. Daniel: Everybody should, of course, use his intelligence and should educate himself well and diligently to become able to understand, [2]‡ as far as that is. possible, from what matter, by what means, and where metals are generated by. Nature; and as a mere side issue he should not spurn the profit that ensues there from. But if his aim is solely and predominantly profit and gain rather

Jan 1, 1949

By Charles J. Potter

There are many sources of energy available for consumption. Some available are solar, tide and wind. However, in terms of relatively large usage, only four principal sources are used for primary energy today. They are coal, oil, natural gas and water power. Such additional items as wood and nuclear energy, although supplying quantities of energy today, do not in the aggregate amount to any real significant quantity, but nuclear energy must be considered for future use. In addition, such a thing as gas from distillation of coal and oil is not considered primary energy. The principal markets for primary energy are the electric power utilities, space heating, industrial uses and transportation. The electric utility use of energy is primarily from coal, followed by natural gas and water power. Space heating is primarily a gas market, followed by oil and then coal. Space heating by electricity is only considered in the generation of electric power. Transportation's principal source of energy is oil. Coal has practically no market left in this field.

Jan 4, 1962

By P. A. Boeck

The thermal insulation of high-temperature equipment for industrial purposes is a subject that has not received from engineers and designers the attention its importance deserves. This may be attributed to a number of causes: In the first place, heat flow is a rather difficult factor to measure under the working conditions of an industrial furnace, and until the comparatively recent introduction into certain operations of the heat balance sheet, with a systematic attempt to account for the discrepancies in the totals, the various causes of heat losses and the reasons for their existence were not brought to light. Moreover, such rapid advancement and radical changes in the design of equipment, especially in metallurgical lines, have occurred that practice has apparently outdistanced the theory of design. In the modern tendency toward greatly increased size of units, effort has seemingly been made to utilize the heat of fuel gases without proper attention having been paid to conserving heat energy and confining it strictly to the points of maximum activity. The systematic study of the thermal properties of structural materials, which is being carried out by various government bureaus and also by a number of technical societies, is forming the basis for more intelligent and consistent work in the economically important subject of prevention of fuel waste. Advantages of Insulation It is not necessary in this practical and utilitarian age to enlarge upon the need of prevention of heat losses, but attention may advantageously be called to the other benefits derived simultaneously with the saving in fuel and the increase in thermal capacity of furnaces when properly insulated. In most industrial furnaces—which are here spoken of in the broadest sense, indicating general high-temperature equipment for any purpose and heated in any manner—the operations are generally carried on through a temperature range which has been found by practice to give the most ef-

Jan 1, 1916

By T. A. Rickard

In a previous paper (ante, p. 411) some description was given of the occurrence of the auriferous alluvium, extensive deposits of which lie among the highlands of the province of Otago, New Zealand. The present paper will describe some of the methods by which that alluvium is exploited. The alluvial mining of New Zealand is not yet hindered by " debris legislation." The mines are for the most part situated in a country of little agricultural value, and large rivers with rapid currents act as tailings conveyors. In time, however, steps will have to be taken to restrict the discharge into the Clutha of the tailings which are slowly raising the river-bottom. The methods of California have been followed in Otago with such alterations as peculiar local conditions require. The distinctive feature of the alluvial mining of Otago is the prominence given to the hydraulic elevator. The all-important factor in this form of mining is the control of an abundant water-supply at a suitable height above the level where it is to be utilized; and in this respect the gold-fields of the south island of New Zealand are most favora-

Jan 1, 1893

By Zay Jeffries

The object of the present paper is to enlarge somewhat on the general principles advanced in my discussion1 of Mathewson and Phillips' article on The Recrystallization of Cold-Worked Alpha Brass on Anneal-- ing.2 It will also serve as an acknowledgment of Prof. Howe's most important remarks on my contribution. In this paper the writer has adopted Prof. Howe's suggestion to substitute the term "germinative temperature'' for "critical temperature for grain growth." Instead of being an exact or certain temperature it should be considered that the germinative temperature phenomenon exists throughout a small temperature range. v Factors Influencing Fast Growth Phenomena The development of grains of macroscopic size at the germinative temperature should be considered the extreme condition of a general rule. When considered in this light it is not strange that the development of these large grains should be the exception and not the rule. The principal factors influencing the operation of the laws of fast growth temperature are as follows: . 1. Rate of heating. In the original paper,' the germinative temperature was defined as "the minimum temperature at which two adjacent grains can coalesce to form one larger grain, provided that this larger grain will have sufficiently increased its power of attack, to enable it to absorb adjacent grains which cannot coalesce with each other. Time is always to be understood as a factor governing the first stage of grain growth." If the time of heating is short, the germinative temperature is raised. The formation of large grains in metals may occur at relatively high temperatures when the rate of heating is rapid. It is to be understood that in such cases, grain growth

Jan 1, 1917

By Edmund Kirby

THE results to come from the application of cheap oxygen to industry in general will be so great that it is not possible to enumerate them beforehand and still less to estimate them. We naturally think first of the fuel to be saved; yet this is only a minor item. The main results will be changes in methods of manufacture or of operation. The speed of operation will be greatly increased, with consequent savings in labor and fixed charges, and also, in most cases, in the cost of fuel. High temperature will be brought within the reach of every manufacturer, whereas it is now available only to those operating expensive electric furnaces located within reach of large water power. New speeds and new temperatures mean improvements and processes not thought of at present. Incidentally the changes in methods will probably change the location of important world industries, the tendency being to concentrate at the fuel centers. The whole subject is so new that most of the data which an engineer requires for definite estimates do not exist. All that is possible now is to obtain a general view of the subject with rough and fragmentary estimates for some of the industries with which we are specially concerned. Most of the figures presented deal with fuel saving merely because there are available no data from which to estimate the effect on speed of operation. When working out the practical problems involved in substituting oxygen for air, in most cases the change will be made step by step; by trying out air enriched with increasing percentages of oxygen. Such partial applications of oxygen will be temporary expedients during the transition and there will be no stopping place short of the complete substitution of air by oxygen. This final stage is therefore the one discussed in this paper.1

Jan 11, 1924

By Charles C. Russell

Pressures developed by the coal during the coking process have been responsible for serious trouble to many companies that operate or build by-product coke ovens. The insidious nature of this trouble is indicated by the fact that oven operators, unless they have ascertained the characteristics of the coals they use, cannot determine the existence of dangerous pressures until after the damage has been done. A rather popular misconception is that ease of pushing of the charge at the completion of the coking period indicates that no dangerous pressure has been developed, but this is far from the truth; pressures developed during the coking period are often completely dissipated by the shrinkage of the charge in the completion of coking, and so any criterion based on the ease of pushing is futile. However, methods of testing coals are available that will definitely distinguish the dangerous coals from those that are safe, and such methods have been brought to a high degree of certainty. The operator should take no risk that involves either a lack of knowledge of the behavior of coals during coking or the failure to believe that certain of the coals or coal mixtures can cause damage to the oven structure. This merely tends to minimize the problem and leads to claims that coking coals of all kinds may be carbonized with no danger of damage to the oven structure provided some particular kind of byproduct oven is used. This lack of appreciation of the true situation is in itself one of the main factors leading to damage of coke-oven structures. Coals that develop more than a certain safe pressure cannot be used in by-product coke ovens without causing damage to the side flue walls. The following paper presents a highly certain method for the measurement of the pressures developed during the carbonization of coal—a method that is the culmination of many years of work on the problem in which a number of methods for the purpose were investigated and used. While actual pressures found may appear to be small when expressed in pounds per square inch, the number of square inches in each oven wall is so large that the total pressure on the oven wall becomes an enormous load.

Jan 1, 1940

By R. L. Wilcox, M. L. Fuller

Owing to the nature of the die-casting process, fresllly cast alloys are undoubtedly not at equilibrium from the standpoint of alloy phase relationships. After casting, therefore, they tend to undergo phase changes, with the ultimate effeet of reaching a state of equilibrium at the aging temperature, beyond which no fnrther change takes place. This phase alteration undoubtedly is one of the primary causes of the changes in dimensions and physical properties that zinc-alloy die castings undergo during aging. It is planned to report on this problem in a series of papers of which this is the first. The writers have made a study of commercial zinc die-casting alloys over a period of several years, utilizing the X-ray diffraction technic of determining the phase composition changes in the alloys. Up to the present, two principal phase changes have been observed which are capable of causing dimensional changes: (I) the segregation of secondary constituents from the zinc-base solid solution and (2) the beta aluminum-zinc decomposition. The latter is the subject of the present paper and studies on the former will be reported upon at a future time. Scope of Study In the present investigation a special technic for the study of the beta phase in zinc-alloy die castings has been developed, making possible the determination of the period of existence of the beta phase after casting. The pure beta constituent and its decomposition have been studied in detail. The effect of magnesium and copper on the velocity of the decomposition is reported. The heat of decomposition, the eutectoid temperature arid the accompanying density change have been measured. The density change lias been calculated from data on crystal structure and the result thus obtained has been compared with the actual change.

Jan 1, 1935

By E. C. Babson

In order to explore the possibility of predicting reservoir performance from laboratory data, behavior of a hypothetical low-permeability reservoir has been estimated by applying data and methods currently available in the literature. A method of calculating decline in productivity index is discussed, and recoveries by internal gas drive, external gas drive and water drive are estimated. Introduction During the life of a producing oil property an operator is faced with many perplexing problems. Any attempt to determine proper well spacing, optimum rate of production, or the desirability of pressure maintenance requires the evaluation not only of a host of economic and practical operating factors but also of the future performance of the reservoir. Although in some cases economic or operating con-siderations may be of primary importance in planning a development or production program, the anticipated effect on ultimate recovery is more likely to be the decisive factor. The soundest basis for evaluating reservoir performance is past experience with oil fields, but pertinent data are difficult to obtain or apply under conditions normally encountered in California fields. Many of these fields are characterized by thick sections of alternating sands and shales complicated by faulting and rapidly changing lithologic conditions. Further compli- cations are introduced by haphazard development and production practices resulting from competitive conditions, changing demand for oil, and insufficient knowledge of structural conditions during early development. Even in the rare cases where development has been systematic and adequate, production policy has usually been controlled by economic and competitive factors rather than a desire to obtain information for use in future operations. In other words, comparable reservoirs in which development and production practices have been systematically varied are seldom found. In the light of these conditions, conclusions based on experiences usually lack the certainty required for decisions involving large sums of money. Some other method of attacking these problems is needed to supplement and orient field experience. Progress in laboratory investigations of the flow of oil, gas, and water through sands has been so rapid in recent years that these data may furnish such a supplementary approach in the near future. In order to explore this possibility the author has attempted to predict the behavior of one type of reservoir by applying published data and methods. Basic Data and Assumptions Calculations outlined in this paper are dependent upon a detailed knowledge of the properties of oil, gas, and water present in the reservoir and the portion of the total pore space originally filled by each. It is also necessary to know how the permeability of the sand to oil, gas, and water varies with the saturations of these fluids 20

Jan 1, 1944

By A. A. Jr. Smith, J. S. Smart

The controlled amounts of phosphorus, arsenic, sulphur or selenium found in commercial coppers perform a variety of highly useful functions. Indeed, a large segment of modern copper technology is essentially dependent upon the presence of one or more of these elements. Consequently, the literature contains many references to their effects but the scope is broad and has been only partly covered. New data are presented herewith directed toward a better understanding of the basic behavior of these elements in copper, with particular emphasis on the composition range o to 0.05 per cent. These data are a part of a general program of research on the effects of impurities on the properties of oxygen-bearing and oxygen-free copper, other portions of which have been reported previously. Schematically, the behavior of individual elements is determined from measurements of conductivity and softening temperature,'v2 and the binary alloys employed are synthesized from high-purity copper in order to eliminate interference from the effects of extraneous impurities. Alloys of selected composition were first prepared in the oxygen-free form by continuously casting the melts in the form of %-in. diameter rod. Oxygen was added subsequently to portions of the alloys, either by remelting or by diffusion at 8jo°C. from a surface scale. Test wires wcre drawn one B. and S. number per pass, using four 30-min. 600°C. anneals at 0.3125, 0.257, 0.204 and 0.162 in., and a final cold reduction of 75 per cent to 0.081 in. Oxygen-bearing slugs made by remelting nere hot-rolled to 4ia in.. drawn to 0.162 in., annealed for 30 min. at 6o0°C. and cold-drawn 75 per cent to 0.081 inch. The alloys containing phosphorus, having been compounded very early in the program, were prepared in the form of 3i6-in. rod, and processed to wire with only the last three intermediate anneals listed above, all of these having been conducted in commercial nitrogen. In addition, the conductivity anneals on these alloys were also performed in the same atmosphere, and the small amount of oxygen present as an impurity in the gas resulted in some loss of accuracy at temperatures of 700' to 8o0°C., as will be shown later. Subsequently, the anneals for all oxygen-free alloys were conducted in hydrogen to prevent oxidation, and purified nitrogen was employed only for oxygen-bearing samples. All conductivity anneals wcre of one hour duration followed by a rapid quench in 10 per cent HZSO*. Effect of Phosphorus The widespread use of phosphorus as a deoxidant has resulted in universal appreci-

Jan 1, 1946

By W. E. Foreman, James A. Redding

INTRODUCTION Screening is a mechanical process that separates particles by size. Modern coal preparation is made possible by efficient sizing. Sizing of coal is defined in terms of the opening through which an individual particle will or will not pass, or as two openings, the larger of which passes the particle and the smaller of which retains the particle. Screening accomplishes sizing by passing coal of a wide range of sizes through a series of screens, each of a decreasing size. The individual screen discharges are then directed into different screen products for subsequent sale or processing. Screening in modern preparation plants is done for the following reasons: 1 ) Removal of fine coal before a size reduction step. 2) Size separation of the coal into a coarse and fine fraction for sized products or processing in coarse and fine coal circuits. 3) Recovery of heavy media from heavy media coal cleaning circuits. 4) Dewatering. 5) Rock and trash removal by handpicking on a screen. Fig. 8-1 is a generalized flowsheet of a plant showing the use of screens in the coal preparation process. Table 8-1 shows the vibrating screen equipment utilized in Fig. 8-1

Jan 1, 1979

By Maxwell Gensamer, Vsevolod N. Krivobok

It is generally recognized that "low temperatures" have a definite effect on the properties of metals and alloys. Furthermore, it is also generally understood that the effect is decidedly adverse. The possibility that the same low-temperature treatment might be employed for the purpose of improving certain properties of the alloys has received less attention until recently, and the experimental and theoretical knowledge consequently is meager. The effect of low temperatures may be studied in two ways: by studying such properties as tensile strength, hardpess, impact resistance, etc., at low temperature, and by studying the properties of alloys at room temperature after these alloys have been subjected to a low-temperature treatment. Even in the latter case, certain properties will differ materially from the same properties obtained on identical material but without cold treatment. In other words, subjecting alloys to cold treatment results in an irreversible change in mechanical properties. Changes of this character are usually indications of the appearance of a new phase or phases, and would be likely to occur in alloys which, either by virtue of their composition or by heat treatment, are retained at room temperature in a metastable condition. Consequently, studies of the effect of low temperatures logically should be conducted from the physicochemical point of view, since the results of such studies not only would furnish metallurgists with interesting theoretical data but would clearly indicate the classes of alloys that would hold promise of improvement, and, possibly, of new applications. As the present investmigation deals with chromium and chromium-nickel alloys of iron of the stainless variety, it has been thought desirable to present the data concerning low-temperature properties of these alloys, available from the most recent and most comprehensive work of H. S. Russell.l A summary of these data is given in Table 1. The data are confined to a limited number of alloys of the type dealt with in the present

Jan 1, 1931

By Kenneth K. Humphreys, J. W. Leonard, T. S. Spicer

INTRODUCTION Reasons for Thermal Drying The continuing increase in the percentage of - '/4 in. ( -6.3 mm) coal produced as a result of the increased use of mechanical mining methods has, over the years, tended to shift considerable portions of the work of producing salable coal to the fine coal cleaning section of the preparation

Jan 1, 1979

By Edward Wichers

THE purpose of this paper is to set forth the matters of principal interest in connection with work done in the past few years on the purification of the metals of the platinum group, including the study and modification of methods already in the literature and the development of new procedures. For the most part, the results will be given in summary form, reserving the publication of detailed data and directions for a forthcoming paper to be issued by the Bureau of Standards. In recent years increasing interest has been shown in the preparation of the pure platinum metals, both by those concerned with the manufacture of the metals and their alloys for scientific and industrial purposes and those who are engaged in the study of the chemical or physical properties of the elements. The purification of the metals usually has been regarded as a matter so involved and difficult as to require the attention of specialists. It is hoped that this paper will show that any of the metals can be prepared in any desired degree of purity by relatively simple straightforward chemical methods. For the most part, it is thought that the methods given are suitable for small-scale refineries as well as for the laboratory; also, that they will bring the time required for the purification of any of the metals within reasonable limits. The new procedure suggested for purifying platinum should prove to be much shorter than any methods described in the literature.

Jan 1, 1928

By G. Sachs, Jr. Brown W. F., Ebert L. J.

It is a generally recognized fact that a steel quenched from the austenitic range and tempered to yield a structure composed of tempered martensite becomes increasingly more ductile with increasing tempering temperature. However, the conventional tensile test fails to yield any value that is sensitive to differences in behavior on tempering among the various low-alloy steels or among different heats of a particular steel. The notched impact bending test, on the other hand, has been recognized for a considerable length of time as capable of revealing differences in impact properties among various steels tempered to 'the same strength level (i.e., the same tensile strength in a conventional tensile test). However, this test is very complex and its significance has not been clarified up to the present time. Of its three characteristic features—the high speed, the notch, and the bending—the notch has been found by Davidenkov2 to be the most potent embrittling factor. Recent investigations on low-alloy steels have shown static notch-bar tensile tests to be more lucid and to evaluate the metal properties in much the same manner as impact tests. In an attempt to analyze the fundamental nature of this test, it was found possible to separate the effects of the two basic characteristics of the stress pattern introduced by the presence of a circumferential notch, the stress state and the high initial stress concentration at the notch bottom. The major conclusions drawn from these previous investigations were as follows: I. The magnitude of the triaxiality at fracture depends primarily on the initial notch depth. Its effect is a great reduction in the average ductility (contraction in area at fracture in the notched section) as compared with that observed in uniaxial tension. This triaxial stress state occurs at a point in the interior of the notch specimen. It determines the notch ductility if the notch is mild and/or the metal possesses a considerable ductility. On the contrary, brittle specimens probably fracture on the metal surface (at the notch bottom) at which point biaxial stress state is present. This biaxiality also considerably reduces the ductility of the metal. For small notch ductilities the notch strength and the notch ductility become very sensitive to embrittling factors. This is contrary to the behavior. of the ductility values derived from a conventional tensile test, which are comparatively insensitive.

Jan 1, 1947