By V. Jiricny

The novel spouted-bed electrode (SBE) is a cathode system where copper is deposited at a high current density in a moving bed of copper particles. Preliminary results on the deposition of copper from acidic sulfate electrolytes using this novel cathode system were described during Copper '95 conference. Despite a high current density, the electrical energy consumption was equal to or lower than that in the conventional electrowinning. The present paper describes more investigations on SBE. The SBE consists of copper particles with approximately 1 mm diameter onto which copper is deposited from acidic sulfate electrolyte whose composition is similar to conventional electrowinning. Three types of anodes were used in conjunction with the spouted-bed cathode, namely, DSA anode for oxygen evolution, and two novel anodes. One anode is less expensive than DSA; however it showed much promise in energy consumption. At a superficial current density of 2200 A/m2, the energy consumption was around 1.0 kWh/kg copper. The research activities described in this paper were supported by BHP Copper.

Jan 1, 1999

By A. Siegmund, R. D. Prengaman

Lead anodes used in zinc electrowinning generally contain 0.5 - 1.0 % silver to reduce the rate of corrosion over the service life. For good quality zinc, the cathodes must contain less than 10 ppm lead. In order to reduce the lead contamination of the cathode, the lead anode must become coated with a protective layer of Pb02/Mn02. The formation of this layer may take as long as 30 - 60 days, during which time zinc production is substantially reduced and the cathodes are contaminated with lead. To improve the mechanical properties of Pb-Ag-anodes alloying elements such as calcium, strontium, barium and others are added. The production of cast lead-silver or lead-silver-calcium anodes often results in the formation of numerous holes, voids or laps in the anode surface that can initiate localized internal corrosion. Based on the experience as the major supplier of rolled anodes for copper electrowinning, RSR Technologies has developed an improved anode for zinc electrowinning. The anode consists of a rolled Pb- Ag-Ca-alloy with a controlled surface grain structure. It forms an adherent protective oxide coating within 2 - 3 days when placed in an electrowinning cell. The preferred calcium and silver contents of the alloy are 0.03 - 0.08 % and 0.3 - 0.4%, respectively. Rolling sheets significantly reduces the presence of internal porosity or laps. The lack of defects results in long anode life. The rolling also produces a uniform grain structure to which the corrosion product readily adheres, thus significantly reducing the conditioning period.

Jan 1, 2000

By Eiki Ono, Atsushi Yamatodani, Shigeru Sunagawa, Yasushi Takasaki, Atsushi Shibayama, Yasunori Higuchi

"During metallurgical processing of non-ferrous metals, smelting residue (inc. smelter slag, flue gas and so on) is inevitably generated as secondary product.In this research, some experimental feasibilities were investigated to recover/remove Cu and As from the residue. Primarily, the removal of As and volatilized materials from the residue was examined by pyrometallurgical treatment (dry-process). In the second stage after treating the residue with a dry-process, leaching and solvent extraction as hydrometallurgical treatments (wet-process) were also investigated by using H2SO4 solution as a two stage leaching treatment, to dissolve various metals from the leach residue. Then, solvent extraction was examined by using LIX-84I as an extractant to recover and separate Cu from impurities from the final (2nd) leached solution. For the leaching stages, the removal of 90 % As and the leaching rate of 85 % Cu could be achieved by 0.25 mol/l and 1.0 mol/l H2SO4 solution, respectively. On the other hand, the extraction of over 90 % Cu and stripping was carried out by solvent extraction. 1. IntroductionIn metallurgical process for non-ferrous metals, smelting residue (inc. smelter slag, flue gas and so on) is inevitably generated as secondary product, i.e., flue dust, slug and so on. The smelting residue includes some useful metals and undesired toxic materials; Cu, Pb, Ca and As, etc.In Japan there is one undisclosed place stockpiled with 10,000 ton of smelting residue from abandoned smelters about 25 years ago. Therefore it is necessary to reduce the residual amount for space and environmental protection including water treatment by separating and removing toxic materials."

Jan 1, 2008

By John Hollow

The Fort Knox Mine is an open-pit operation, located in Alaska, which started commercial production in March 1997. A conventional Mill processes 38,000 tpd of a low grade (1.0 g/t Au) free milling gold ore with a low sulphide component (below 1%). Gold production (11% from gravity and 89% from cyanidation) exceeds 400,000 ounces per year. Short retention time (20h), low temperature (7oC) and low grade make high leaching kinetics critical for the performance of the process. In April 2001, the treatment of True North ore, which represented 14.4% of the mill throughput and contained more sulphide in the form of pyrite, arsenopyrite and stibnite, resulted in a substantial drop in the average gold extraction from 87% to 72.6%. Laboratory investigations indicated that the addition of lead nitrate increased gold extraction to 91.7%. Further investigations were initiated to determine the leaching parameters and the nature of the problem. Subsequently, a lead nitrate addition scheme was implemented at the Fort Knox Mill that resulted in 2002 gold production being in excess of 31,000 ounces higher than that estimated for the non-lead nitrate reagent scheme. This paper presents the results of laboratory investigations and modifications in plant operating practices.

Jan 1, 2003

By Douglas Robinson

This paper describes technical work done to develop a Spouted Bed Electrode Cell into a commercially viable Electrowinning Cell; (a previous paper has been presented at the ECS meeting in Paris in May of this year, with a more general overview of the cell, [1]). The studies have included hydrodynamic tests to understand the criteria for the circulating flow of metallic beads in the cell, particularly in the region at the entrance to the draft tube, and electrochemical tests to find a suitable diaphragm for extended time electrolysis. Various patent pending features were developed including a double nozzle to allow for automatic stopping and restarting of the bed, an arrowhead shaped draft tube to control the flow of beads into the entrance to the draft tube, a roof-top shaped device to control the flow of beads out of the top of the draft tube, an overflow weir to allow the continuous recovery of beads from the cell, and a family of diaphragm fabrics for extended operation. Prior to the identification of the diaphragm material, short circuits would develop within a few hours. A pilot scale cell was operated for three days, with continuous operator attention, and then for ten days with operator attention only on day shift. The cell is currently advancing to the next stage of development which will involve continuous testing in a commercial copper electrowinning facility.

Jan 1, 2003

By Daniel Kim, Ari Rantala

Efficient on-line monitoring of electrolytic cell performance in copper electro-refining has been challenging due to the need for complex electrical measurement systems and the management of the enormous volume of data. Based on Kennecott Utah Copper's innovation Outotec has developed a novel and innovative electrolytic cell monitoring system called CellSense™ System. As the system is based on self-powering from bus bars, wireless communication, on-line adaptive modeling and easy to access information and alarming, traditional obstacles of electrolytic cell monitoring are eliminated. With cell voltage and electrolyte temperature measurements, CellSense System enables real-time cell performance discovery and early reaction to critical production or quality disturbances such as short-circuiting, flow blockages, cold cathodes or electrolyte temperature excursions. During the past few years the system has been delivered to over 3500 commercial cells. In this paper the largest CellSense™ System ever delivered and recently adapted by Kennecott Utah Copper with 1412 cells monitored on-line for high tankhouse performance, cathode quality and optimized operator work flow is presented. Early results and benefits are discussed.

Jan 1, 2012

By V. Bojarevics, K. Pericleous

"A number of different methods have been developed for noncontact electromagnetic treatment of liquid metal and to investigate the melting/solidification processes. Applying AC magnetic field in terrestrial conditions, along with the buoyancy and thermo-capillary forces, results in turbulent flow. The use of a homogenous DC magnetic field allows damping both of the turbulence and the large scale flow at different rates leading to surprising results at some stages. The dynamic interaction of the turbulent flow with the oscillating interface needs to be accounted if it is required to levitate liquid metal of up to few kilograms without the contact to container walls. At the high values of magnetic field some oscillation modes are damped quickly, while others are modified with a considerable shift of the oscillating droplet frequencies and the damping constants from the non-magnetic case. Numerical models are used to investigate behavior of liquid metal suspended in high DC magnetic fields providing microgravity-like conditions with laminar viscosity and heat transfer to the surroundings.IntroductionSince the early Electro Magnetic (EM) levitation experiments [1] in AC magnetic field it became apparent that the levitated liquid metal is prone to oscillation and instability. The EM and electrostatic levitation experiments with liquid metal droplets show difficulties related to confinement stability and a need for complex correction functions to establish a correlation between the measurements and the droplet material properties [2,3]. Intense internal fluid flow is visually observed, apparently being in the turbulent regime for earthbound conditions."

Jan 1, 2012

By Dinabandhu Ghosh

The stability diagram of the ternary system Ti-C-O is drawn in the present work for four temperatures, 1473 K, 1573 K, 1673 K and 1873 K, showing the stability fields of TiC, Ti, TiO, Ti2O3 and TiO2. An analysis of the system reveals that it is not possible to produce Ti in a carbon-saturated system; instead, the stable product is TiC. However, Ti can be an equilibrium product in a carbon-unsaturated system at prohibitively low values of pCO and pCO2; for example, at 1873 K, these limiting values are: pCO = 10-6.76 atm and pCO2 = 10-13.36 atm, which, when exceeded, produce TiC and TiO respectively. The magnesiothermic reduction is examined through the stability diagram (log pO2 vs. 1/T) of the system Ti-Mg-O, drawn for a number of pMg values, presenting the pairwise stability fields such as Mg(l) + Ti(s), Mg(v) + Ti(s), MgO(s) + Ti(s), etc. The diagram shows that magnesium reduction of TiO to Ti is possible only at T < 1641 K with pMg = 1 atm and only at T < 1569 K with pMg = 0.5 atm. An experimental scheme for Mg vapor reduction of TiO2 is proposed in which an argon stream is passed over a Mg(liquid) evaporator at temperature T1 (say, 1234 K); the resulting Ar-Mg mixture at 1 atm is subsequently flown over a bed of TiO2 at temperature T2. A thermodynamic analysis establishes that complete reduction to Ti is possible and that the best results are obtained when T1 = T2.

Jan 1, 2006

By Shigehito Isobe

The Li-N-H system composed of LiH and LiNH2 catalyzed by titanium compound desorbs ~6 mass% hydrogen and a quite small amount of ammonia in temperature range from 150 to 250 °C under He flow atmosphere. In this work, hydrogen desorption (H-desorption) mechanism in the reaction from LiH+LiNH2 to Li2NH+H2 in a non-equilibrium condition was clarified by TDMS, TG and FT-IR analyses for the products replaced by LiD or LiND2 for LiH or LiNH2,respectively. The results suggested that H-desorption reaction progresses through two-step elementary reactions mediated by ammonia. As a next step, we carefully determined the amount of the ammonia containing in desorbed hydrogen for the Li-N-H system in a closed system from the practical point of view. The results indicated that a quite small of ammonia thermodynamically coexisted in the desorbed hydrogen in closed system, although ammonia could not be almost detected in emitted hydrogen gas by TDMS under some non-equilibrium conditions. Moreover, for understanding the role of titanium, the chemical bonding state of the titanium compounds doped as catalyst in the mixture was examined by XAFS measurement. The results indicate that the Ti atoms, which can induce catalytic effect, are in a particular chemical bonding state.

Jan 1, 2006

By Peter Koh

The velocity solid charge attains when dropping down concentrate chutes is an important boundary condition when developing mathematical models of flash furnace burners and reaction shafts. In this work an experimental rig was developed to measure the velocity attained when nickel concentrate and sand were dropped down a vertical pipe 3m long. The velocity measurements showed that the nickel concentrate did not fall as individual particles. The measured values of the velocity approached, but did not attain, those calculated for solid bodies, the disparity being attributed to friction at the pipe wall and fluid drag losses. After falling 2 m velocities between 5-6 m/s were attained. The analysis was extended and applied to understanding the intermittent problem of puffing which sometimes occurs from the top of the concentrate chute. The pressure at the bottom of the chute is the net result of two opposing pressures, namely that developed by (a)the process air entering through the velocity control device, and (b) the solids falling down the concentrate chute. Flow back up the chute occurs when the former exceeds the latter. The process air pressures in the burner were obtained from CFD simulations of a full burner. Variables considered included air speed through the velocity control device, drop height and furnace draft. The analysis was useful in highlighting the operating conditions which were conducive to puffing and in establishing procedures to minimise its occurrence.

Jan 1, 2006

By Kwang-Ho Lee

The Onsan copper smelter of LS-Nikko Copper Inc. has operated the Mitsubishi continuous process along with Outokumpu process since 1997. Mitsubishi process is a bath smelting process which needs adequate melts for smelting reaction in the furnace. After a campaign shutdown it requires time to make a start melt. Onsan smelter has had much experience in flash smelting, including the improvement of the concentrate burner which is one of the most important parts in a flash smelting furnace. Based on this experience, the lances of the Mitsubishi smelting furnace were modified in order to making the starter melt with flash reaction. In 2004, the flash reaction in the Mitsubishi S-furnace was completed and was able to make the starter melt using these modified lances. Although at that time it was still under development it reduced the time required to make the initial bath-melt by about half.

Jan 1, 2006

By Jae-Chun Lee

Di-2-ethylhexyl phosphoric acid (D2EHPA) is widely used for separating rare-earth elements. In commercial plants, rare-earths are usually stripped from loaded extractant streams using mineral acid, then precipitated as oxalates. Many rare-earth uses demand specific powder characteristics, which are obtained by secondary processing. This paper demonstrates the feasibility of combining the stripping, precipitation and powder processing stages, thereby achieving considerable savings. MEHPA solutions were loaded with yttrium, then emulsified with oxalic acid-HC1 solutions to precipitate yttrium oxalate, which was readily calcined to yttrium oxide. The precipitation kinetics and yield were sensitive to process conditions. The morphology and size of the yttrium oxalate powders varied with the concentrations of D2EHPA and oxalic acid, and the presence of SPAN 60, which affected nucleation, growth, and the emulsion characteristics.

Jan 1, 1992

By Alex Moyano

At present, the Codelco Norte smelter processes in the Teniente Converter and the Flash smelting Furnace 1,420,000 t/y of its Chuquicamata concentrate with an arsenic content of up to 1.5%. In a near future Codelco-Chile is considering different processing options for a new projected concentrates from the Alejandro Hales mine (former Mansa Mina mine with an arsenic content of up to 6%). The main option is the possibility to process 3,000 t/d of mixing concentrates from the Alejandro Hales and the Chuquicamata mines, in the Teniente Converter. The main feature of this smelting unit will be high volatilization of arsenic when processing high arsenic-bearing concentrates. The CN smelter staff carried out a technical feasibility study to evaluate the processing of high arsenic-bearing concentrates directly in the Teniente Converter, thus the low arsenic-bearing concentrates can be processed in the FSF. Accordingly, laboratory scale tests were carried out at the Tohoku University facilities. The lab-scale results allowed an industrial scale test at the Codelco Norte smelter to smelt 2,300 tpd of high arsenic-bearing concentrates in the TC and evaluate the metallurgical impact in the smelting, converting and refining areas of the smelter. The main industrial-scale result confirmed the stabilization of the arsenic content at 0.5% in the 70% Cu produced white metal at the test condition.

Jan 1, 2006

By Marko Suput

Titanium is a high-strength, low-density metal nearly immune to corrosion, but limited in use by its high price. The high price is due to the cost of smelting and processing the ore. The research on titanium production using the Solid Oxide Membrane (SOM) process aims to consolidate most of the processing steps required for conventional titanium production into a single step making it an energy-efficient and cost-effective method for producing CP billet and ingot and possibly also powders used to make titanium alloys. In the SOM process experiment, a steel crucible contains MgF2-CaF2-TiO2 flux; an inert metal/carbon rod serves as the cathode; an oxygen-ion-conducting yttrium-stabilized-zirconia (YSZ) membrane in the form of a one-end-closed tube contains either a liquid metal that acts as the anode or liquid MgF2-CaF2 ionic flux that connects the YSZ membrane to an anode. During electrolysis, when the voltage between anode and cathode is higher than the reduction potential of titanium oxide, titanium ions are reduced at the cathode and the oxygen ions pass through the YSZ membrane and are oxidized at the anode. The oxygen ions are oxidized at the anode by a reducing agent, hydrogen gas or carbon, forming steam or CO(g), respectively. To date, a suitable MgF2-CaF2-TiO2 flux has been selected and the operating temperature for the SOM process has been determined. Several electrolysis experiments have been performed. As expected, lower valence deposits of titanium oxides have been witnessed at the cathode prior to depositing pure titanium. Continuing work will aim to extend the electrolysis time in order to pass enough charge to produce a significant amount (100 g) of titanium at the cathode.

Jan 1, 2006

By T. J. Weitz, J. E. Micheletti

"Pegasus Gold's Beal Mountain Mine is located near the Continental Divide, SW Montana. Conventional surface mining utilizes crushing, heap-leaching, carbon absorption/desorption, electrowinning and refining to produce approximately 60,000 oz gold annually. A leach pad sits at 2,300 meters (7,500 ft) elevation. Winters are long and cold with average snow accumulations ofl-2 meters; temperatures fall below minus 40'C and wind chill temperatures below 70°C. The Beal Mountain staff has developed special tools and procedures for burying drip emitter lines, and managing the heap and process solutions to allow for uninterrupted gold recovery during the winter season. Management of water balance and spring runoff is critical to the operations' success, due to mountainous terrain, high precipitation and proximity to a fishery and elk herd. The mine has an extensive network of land application disposal (LAD) and stormwater control systems to assure environmental protection and regulatory compliance.ABSTRACT ONLY"

Jan 1, 1997

By Chai Liyuan

Chromium-containing slag was detoxified by the method of microbial treatment using Ch-1bacteria isolated from nature by our research group, belonging to achromobacter sp. and with the characteristic of reducing high concentration of Cr(VI) in alkaline solution. The detoxifying process of Ch-1 to chromium-containing slag was studied by column-leaching techniques respectively. The results indicate that Cr(VI) in leachate can not be detected when chromium-containing slag has been column-leached for 7 days, and Cr(OH)3 content in precipitate is up to 32.8% with great value of resource recycling. Flowchart of engineering experimentation was ascertained based on the parameters of column-leaching experiments. Using the technique of pelletization of chromium-containing slag heap-leaching by Ch-1,the leaching rate of water-soluble Cr(VI) existing in chromium-containing slag reaches up to 100%, while the leaching rate of full chromium is up to 90%, when the process has been operated for 7-10 days under the conditions of 25-40C and consecutive spray by circular leachate. The content of Cr(VI) in chromium-containing slag after detoxified meet the national identification standard for extraction procedure inxicity for hazardous wastes(GB5085-1996) in China, moreover approximately 90% of Cr(VI) existing in chromium-containing slag has been recycled.

Jan 1, 2006

By Viktor Ashikhin, Pavel Arkhipov, Yurii Zaikov

"Lead alloys electro-winning from chloride melts was under investigation. Impurities concentration in cathode lead is strongly depended on temperature, electrolyte composition, anode current density. The equilibrium electrode potentials of lead-antimony alloys with the various content of electropositive metal in the alloy were investigated in the wide temperature interval. Thermodynamic properties of Pb-Sb alloys containing 20-95 mol% of Pb were studied by EMF method in temperature interval 723-873K in molten mixture of potassium and lead chlorides. Partial and integral thermodynamic characteristics were calculated. Small negative deviations from Raul’s law were found. Anode processes were investigated. The lead dissolution was found to be the only process in certain interval of current densities and electropositive metal content in alloy.IntroductionAt present human race is facing the problem of pollution by lead and its compounds and also the pollution influence on population health all over the world. One of the solution ways is the recycling lead containing technical wastes by ecologically clean technologies.World scientific community pays much attention to the electrolysis of molten salts. The usage of salt mixtures, as electrolytes, discovers new possibilities in the production of metals, metal compounds and alloys. ?????????? of the electrolysis at the temperature 50 - 200 °? above the melting temperature of chosen salt mixture allow to unbreaks processes, that undergo in the pre-electrode layer. The rate of the electrodepositing of elements are much higher than in the water electrolytes. At present there are technologies developed for production of metals (Ta, Nb, Ti, Zr, Hf, Ca, Al, Mg, Be, Li and others) by the electrolysis of the melts. Electrolysis of melts might be used in order to convert different technological formations containing lead and other nonferrous metals, that produced by different enterprises. According to the level of the influence on the living organisms lead is in the group of highly dangerous substances alongside with arsenic, cadmium, mercury, selenium, zinc, etc. Toxity and ability to accumulate in the human organism are two main sources of danger for the human being."

Jan 1, 2008

By E. J. Peuraniemi

Recently commissioned Kennecott-Outokumpu flash converting was developed to replace the approved but environmentally outdated Peirce-Smith -converting to satisfy the globally tightening emission regulations. In the present study, dust formation and reaction mechanisms of two copper mattes with different experimental parameters were studied in lean suspension conditions. Both mattes had very high copper content of approximately 75 wt% and low iron content of 4.5 wt% and 1.2 wt% Fe. A laboratory scale, vertical laminar-flow furnace with a low feeding rate was used to simulate the phenomena taking place in the reaction shaft of a flash converter. Experimental conditions included temperature of 1300 °C with reaction gas oxygen contents of 20 vol%, 50 vol%, and 75 vol%. In the experiments, sieved particle fractions were fed to the furnace and sampled after short reaction time intervals by quenching them into a water film. Collected particles were analysed chemically for their main elements to define their removal rates. Also, optical and scanning electron microscopy with EDS-analyser were applied to determine phenomena occurring during reactions. Kinetics of oxidation as well as ignition of particles are discussed. Changes in particle morphology, size, and composition are reviewed to describe dust formation and reaction mechanisms.

Jan 1, 1999

By Vittorio Basilico, Marco Quattrone, Mario Bassan

"In Italian building market one of the reasons that often stop building contractors from not taking into consideration the possibility to recycle rubble from building is represented by the increase of costs for rubble separation. However the recycling of C&DW can also allow a decrease in disposal costs and a reduction in raw materials requirement.In this paper the results of a testing conducted on a case study through economic and technical analyses are presented.Results highlight that a wise management of demolition and disposal processes can generate a remarkable saving and that it is possible, on the other side, to achieve environmental benefits such as reduction of raw material consumption and dump life lengthening.IntroductionTwo major factors have been found to have considerably influenced the market of recycled aggregates in Europe and Italy: the EU and national regulations and environmental awareness. The market of recycled aggregate has grown in countries with limited natural resources.Waste disposal has also been one of the top EU political and environmental priorities. In the complex interaction between human activities and the environment, waste is proved to be one of the most environment-degrading products.In 1972 the European Commission introduced measures on waste reduction, reuse and recycling. In 2006, directive 2006/12/EC (European Commission) on waste was issued. It covers the scope of minimizing the waste, prevent hazardous waste, maximize reclamation, reuse, recycling and energy-recovery.No specific directive refers to management and recycling of construction and demolition wastes. However, in 1992 the European Commission listed debris among waste management priorities because of its growing amount.Only recently, effective environmental policies have been implemented in Italy, even though relevant environmental issues started rising as early as the beginning of the 1970s. In the 1980s the Government undertook the first significant measures to handle the waste management."

Jan 1, 2008

By J. P. Ibáñez

The uptake of copper from extremely dilute aqueous solutions by alginate in the form of protonated dry alginate beads was investigated. Barium was used to cross link the alginate forming the beads. The effect of various experimental parameters such as pH and metal ions concentration on the uptake of copper were studied. The uptake was strongly dependent on the Cu-bearing solution pH up to a value of 4.5. A removal of 100% o was achieved when the initial concentration of copper was as low as 8.0 mg/L. The maximum uptake, i, e., the loading capacity, was found to be 167 mg of copper per g of beads. The mechanism governing the removal of copper was found to be ion exchange between protons of the alginate beads and cupric ions of the solution. For this ion exchange process a molar ratio, d[H+]/d[Cu2+], of 2.0 was determined. EPMA-EDX analysis of the Cu-loaded beads showed a uniform distribution of the ions throughout the structure of the alginate, regardless the solution pH. This may suggest that this sorbent material is a porous ion exchanger having high permeability and capacity. The uptake of copper and of the heavy metals cadmium and zinc by this sorbent is compared.

Jan 1, 1999