By I. D. Reznik

The flowsheets of converter matte production from sulphide copper - nickel and oxide nickel ores on Severonickel and Yuzhuralnickel integrated ,;corks are given. The cobalt behaviour in electrosmelting and autogenous ore smelting, converting and converter slag cleaning is observed. A list of acticles published in the 80 th is given.

Jan 1, 1993

By Toshiaki Akahoshi

Keywords: Wasted catalyst, Hydrodesulfurization, Ammonium vanadate, Ammonium molyb-date, Hydrometallurgical process. The fundamental reactions have been investigated in order to develop a hydrometallurgical process for recovery of molybdenum and vanadium from wasted catalysts generated in the hy-drotreating desulfurization of heavy oil. The principal steps of the process are a mild oxidation roasting of the waste catalysts at temperature around 500°C, leaching of the target metal components with dilute ammoniacal aqueous leachates, selective precipitation of vanadic acid, and ammonium molybdate precipitation. The selective recovery of vanadium as vanadic acid is successfully performed using ammonium sulfate as a salting-out agent. Recovery of ammonium molybdate is based on large dependence of solubility of ammonium molybdate in ammoniacal solutions upon temperature and ammonium salt concentration. In this process, the solution after recovery of vanadium and molybdenum is recycled to the leaching stage of the roasted materials, and the ammonium salts in the process liquor is in the repeated use. Employment of am-moniacal system makes it possible to operate the roasting at much lower temperature than that for the currently operating process.

Jan 1, 2005

By Isrun Bohlinger

Resources recovery of brasses for semifinished products often results in the formation of hard spots impairing the quality of following abrasive and/or surface finishing processes. A short survey is given on the recycling processes, followed by the actual knowlegde of genesis, composition, and possibilities of avoidance of hard spots. Informations on genesis and composition of hard spots are completed by data from recent experiments.

Jan 1, 1998

By Gaballah I.

Elimination of arsenic, mercury and zinc from synthetic solutions containing H;\A.sD4. HgCI2 and ZnCI2 using modified barks was investigated. The pH range was varied from ?1 to 10. The initial concentrations of individual element were 10,100 and 1000 ppm. More than 99 % of mercury and 65 % of zinc cations were removed by the modified bark .. In this case, the modified bark reacts as a cation exchanger leading to the release of ' two protons for every HgII or ZnII fixed by this material. About 30 % of arsenic was eliminated from the solution. This 'low efficiency could be attributed to? the presence of arsenic ,as. anion. Decontamination of a treated industrial effluent containing 4 ppm of ion? metals was performed on a pilot plant scale by the modified bll(k. More than 70'% of these ion metals were eliminated.

Jan 1, 1995

By Alicia Esther Ares

This study was conducted to investigate the directional solidification of Zn-20%A1 and Zn20% A1-1O%Si-3o/oCu alloys under different conditions of heat transfer at the metal/mould interface. The type of structure obtained in both cases was analyzed and related to the solidification thermal parameters such as cooling rate, growth rate, thermal gradient and recalescence which were determined from the temperature versus time curves. These parameters were correlated with the structure-like length of columnar grains and size of equiaxed grains. The metallographic analyses were done performing quantitative metallography and composition analysis of the different alloying elements along the cast samples by SEM (Scanning Electron Microscopy) and EDXA (Energy Dispersive X-Ray Analysis). Correlations between properties, structures and thermal parameters were found.

Jan 1, 2008

By N. El-Kaddah, J. W. McKelliget

"A mathematical model for the analysis and design of hybrid plasma reactors for advanced materials synthesis is presented. The model is based upon a solution of the electromagnetic vector potential equation and is capable of predicting the two-dimensional velocity, temperature, and electromagnetic fields as well as the reaction kinetics inside the reactor for any axi-symmetric coil configuration. The model is used as a computer aided design tool for the design of hybrid plasma reactors consisting of a conventional DC torch augmented by an RF induction coil and it is demonstrated that the hybrid system possesses superior characteristics for materials synthesis over conventional DC or RF systems. The coupling between the RF and DC components is found to affect both the temperature field and the flow field and to have a significant effect on the reaction kinetics and on materials recovery. The model is used to study the thermal decomposition of silicon tetrachloride as a function of reactor design and operating parameters and it is demonstrated that through a CAD approach it is possible to significantly improve the operation of materials synthesis systems.IntroductionIn recent years there has been growing interest in the use of the inductively coupled plasma for chemical synthesis as a way of meeting the increasing demand for high quality, high performance materials for use in critical applications/l/. Although the basic feasibility of this approach has been demonstrated in the laboratory/2,3/ there still exists a number of operational problems that adversely affect system performance for some applications. In particular, the recirculation and back flow effects that arise from the electromagnetic forces in the plasma can result in the repulsion of the reactants from the hot plasma core and their subsequent deposition on the walls of the reactor. Another operational problem arises from the fact that the energy dissipated in the plasma has to compensate for the heat losses to the environment by conduction, convection, and radiation in order to maintain the ionization of the plasma and, hence, the stability of the plasma may be affected by the presence of the reactants and their products."

Jan 1, 1988

By Zhao Hengxian

We studied the phase diagram of Na3AlFe-ZrO system, reduction of ZrO2 by aluminium and electrochemical behaviours of ZrO2 in the system. The results show that Na3ALF6-ZrO2 system is a simle eutectic one, that the velocity of reduction of ZrO2 in the system is rapid al 960'C and that the Zr content in the alloy abtained can reach as high as 2.5wt%. Potential scanning shows that there exist new current peaks on the potential scanning plats except for the cuurent peaks corresponding to the oxidation of aluminium. The method of making Al-Zr alloy in our paper has advantages over the traditional method of mixing metals.

Jan 1, 1992

By M. B. Sizgoric

Quantitative mineralogy is used in a study done on an Inco Metals Company nickel sulfide occurrence from 'the Thompson area in Northern Manitoba. The study included: a) determination of the variations in chemical composition of the ore minerals; b) determination of the liberation of the ore minerals for the various types of ore and for different feed grinds; c) assessment of the preliminary mill test results by comparing the mineral distribution in the different tailings. Preliminary mill test results had outlined three main problem areas: 1) unacceptabiy low grade concentrate with, 2) very high weight recovery and, 3) low pyrrhotite rejection resulting in a high sulfur concentrate. The mineralogical study readily explained these results by showing that: 1) between 20 and 40% of the nickel in the feeds and 55 and 75% of the nickel lost in the tailings is associated with pyrrhotite. This accounts in part for the low grade of the concentrates obtained at high recoveries: 2) hexagonal nonmagnetic pyrrhotite constitutes over 90 percent of pyrrhotite. Since hexagonal pyrrhotite floats more readily than monoclinic pyrrhotite, this could be part of the reason for the undesirable high pyrrhotite recoveries into the concentrates. Further test work to establish both the optimal grind and the best conditions for pyrrhotite rejection is therefore mandatory.

Jan 1, 1981

By I. S. Blair

The introduction of the 36 MVA smelting furnace at Mufulira, and the experience gained during the first five years of operation have been described previously (6). Based on this experience the furnace was rebuilt in 1977., Details of the modifications made during this rebuild are described. Subsequent to the rebuild, refractory failures, particularly in the electrode ring bricks of the sprung arch roof, continued to cause concern, and repair and improved roof control methods are described. Electrode breakages continued, but developments in casing design and electrode preparation have resulted in significant improvements. Modifications in the electric furnace gas handling system are outlined, together with details of further changes to be implemented in the near future. The systems developed for metallurgical control of the furnace and the thermo-dynamics of the process are discussed. The electric furnace at Mufulira is now operating at above design production levels, and has decisively justified the choice of this technology in situations with inexpensive electric power. The potential for further increases in production capacity from the Mufulira unit, and improvements in design for new units are discussed.

Jan 1, 1983

First, a classification of the various primary sources of feed materials for the production of cobalt is presented from a mineralogical point of view : sulfides, arsenides, sulfo-arsenides and oxide minerals. Each of these cate- gories will be characterized by its behaviour towards concentration methods, taking account of the presence of the associated minerals of other metals and of the nature of the gangue minerals. Then, for each category of cobalt bea- ring ores, typical flowsheets of treatment will be presented and discussed and the characteristics of the cobalt concentrates produced will be under- lined having in view their subsequent processing by pyro - and (or) hydrome- tallurgical methods.

Jan 1, 1988

By Thomas E. P. Wechsler

The limiting factor for most pyro-metallurgical processes in secondary cop- per melting is the time required to heat and melt the product. American Combustion's proprietary PYRETRON variable £uel/air/oxygen combustion system improves the throughput of existing scrap melting and heating furnaces for copper and copper alloy production by increasing the rate of heat transfer from the flame to the product. The increased productivity and energy savings obtained from this technology can result in sizable reductions in operating costs for smelting operations.

Jan 1, 1991

By René Winand

A new process was studied at large laboratory scale at Université Libre de Bruxelles, under contract with Metallurgie Hoboken-Overpelt. A two cathodes (1m long ; 0.2 m high) channel cell was used at 2000 A/m2, with an electrolyte flow rate up to 1.8 m/sec. The main results may be summarized as follows : cathodes are electro¬refined grade in analysis ; metallographic structure and surface roughness are kept under control up to 1.3 cm (one side deposits) ; silver in cathode is controlled by CI and Br ions in solution ; organics must be used at very low concentrations (in the range of 0.1 mg/1, with a consumption of about 0.01 mg/lh).

Jan 1, 1987

By O. Forsén

In the first part of this paper is studied the behaviour of small amounts of impurity elements? in the solidification of copper anodes. In the second part the dissolution of these impure anodes in sulphate based electrolysis is discussed. The first part is introduced with practical examples, the .model of solidification of impurities during the solidification of anode copper. According to this model the solidification structures of anode copper are strongly influenced by both thermodynamic and kinetic factors. Thermodynamics determine the microstructure of anode copper, but kinetics can alter the composition of melt to such that there is formed unequilibrium structures during the solidification, especially when the residual melt is solidified. The electrolysis experiments have clarified the behaviour of impuririties in the electrochemical dissolution in sulphate. Based copper electrolysis. In this study it is widely investigated to what extent any impurity elements or oxides will dissolve. In copper electrorefining. With the aid of the electrochemtcal experiments it was possible to fulfil quantitatively the qualitative results accomplished by microstructure studies.

Jan 1, 1985

By J. M. Skeaff

As much as 100% of the gold and 67% of the silver in a sulphur-bearing hydrometallurgical leach residue have been transferred to copper metal at copper smelting temperatures by dissolving the partially calcined residue in an iron-bearing slag maintained in equilibrium with the liquid copper metal and matte phases. The precious metals can then be recovered by conventional refining techniques. Copper can be recycled at least four times without any detrimental effects on gold and silver transfers and recoveries. Apparent copper recovery in the .process can be over 100% because of the copper content of the residue. Based on slag analys.es, the overal1 recovery of gold in the copper metal and matte phases varies from 94% to 100% under all conditions investigated. On the? same basis, silver recovery varies .from 9S% ?to 99% under optimum conditions, but is only 4S% to 73% under other, less attractive conditions. Unaccounted for silver losses of' about 30% make it difficult to determine the major factors affecting ?silver transfer and recovery. A method for implementing the technology on a commercial scale at a Canadian copper/zinc smelter has been proposed. A preliminary economic assessment and comparison of the proposed pyrometallurgical process with conventional cyanidation indicates that either process is economically attractive for recovering gold and silver from leach residues. Although the capital costs are higher, the pyrometallurgical process is simpler, has higher recoveries, lower operating costs and no .potential environmental problems related to cyanide disposal.

Jan 1, 1989

By G. Barbery

The models for particle composition prediction that have been put forward are limited to simple textures and lead to an independance of grade with respect to particle size in broken ore. A presentation is made of a modification in texture description; binary textures, in which each subeonstituent has its own breakage characteristics are introduced. The calibration of the textural model can be made using heavy liquid separation results. The application to the case of coal is presented. Coal washability data present spe¬cial difficulty due to the distribution in the specific gravity of coal, which must be taken into account. Coal s.g. distribution is taken as a generalized exponential distribution. Model calibration is then possible and is shown to be in good agreement with experimental data.

Jan 1, 1987

By R. Leiby

Prior to March 1992, the only component of the lead acid battery that was not recycled by East Penn Manufacturing Company was the sulfuric acid electrolyte. This acid was unusable in new batteries because the iron level was found to exceed new product specifications. The development of a liquid ion exchange process to remove the iron from the acid allows East Penn to currently recover over three million gallons of sulfuric acid annually. The process is based upon the use of an iron selective liquid ion exchange material or solvent to extract iron from the sulfuric acid electrolyte followed by regeneration of the solvent. Equilibrium and kinetic data for the extraction and regeneration steps were collected in order to scale up the process to commercial scale. An electrochemical process for the treatment of the acid used in the regeneration step was, also developed which significantly reduces the volume of strip acid required in the process.

Jan 1, 1995

By Yuanbo Zhang, Bin Xu, Guanghui Li, Xiao Kang, Chen Liu, Tao Jiang

Iron-bearing dusts, containing valuable constituents such as Fe, CaO, MgO, C, etc., are generally utilized as raw material in iron ore sintering. However, the dusts characterized by low granulating and refractory performances always lead to negative effects on sintering indexes. As we know, the innovative process named composite agglomeration process (CAP) has a series of advantages compared to traditional sintering process (TSP). In CAP, part or all of the iron-bearing dusts is made into green pellets with 5-15mm in diameter, while the rest of iron-bearing dusts and all of the other fine ores is granulated after mixing with fuels, fluxes and return fines. Compared with TSP, CAP could increase the ratio of iron-bearing dusts from 5% to over 20%. Meanwhile, the yield, ISO tumbler index and productivity reached 75.82%, 65.13% and 1.531t·m-2·h -1, respectively.

Jan 1, 2015

By Guohua Bai, Lin Zhang, Shan He, Xuling Chen, Min Gan, Xiaohui Fan, Yanbin Tang

"For reducing the dust content in flue gas during copper smelting in the Ausmelt, technologies and mechanism of strengthening the pelletizing of copper concentrate were studied. The results show that adding bentonite, organic binder or composite binder can effectively enhance the strength of green pellet and reduce the rate of shedding powder in drying process, and composite binder works best. When adding 1 % of composite binder, the drop strength of green pellet increased from 1.9 times/P to 4.5 times/P, the rate of damage dropping from 2 m reduced from 50.12% to 13.08% and the rate of shedding powder reduced from 60.28% to 25.13% at drying temperature of 400111. In addition, the mechanism of binder absorbed in the surface of mineral was investigated by infrared spectroscopy. The results showed that composite binder absorbed in the surface of copper concentrate was in the form of chemisorptions, which made hydrophilic enhanced, while bentonite absorbed in the surface of copper concentrate was physisorption.IntroductionWith the technologies of copper smelting developing, the equipment of copper smelting steps into a large-scale and efficient level in recent years. As Ausmelt smelting is characterized by being efficient, environmentally-friendly and energy-saving, it is generally recognized by the enterprises of copper smelting [l]. The process of Ausmelt smelting starts with materials mixing, and then pelletizing. From this point onwards, pelletized balls are charged to the top of the furnace, undergoing drying and smelting reaction[2]. Since copper concentrate is fine-grained, directly adding into smelting furnace can make it blown out of the furnace together with the airflow upwards, rendering flue gas high in flue dust, which can cause the loss of concentrate greatly, and make smelting environment poor as well. The concentrate transported into the furnace and smelted after disc balling is conducive to improve the capacity of melting furnace during copper concentrate smelting, reduce the powder shedding rate and improve enterprise benefits."

Jan 1, 2013

By John Hanna

The University of Alabama Mineral Resources Institute (MRI) has developed a unique process for selective fatty acid flotation of carbonate gangue from sedimentary apatites (francolite) in the pH range of 4-6, without collector conditioning of the pulp. The process, which does not require an apatite depressant, was modified to beneficiate a high MgO siliceous phosphate matrix from South Florida. The modified process includes two flotation stages, one for carbonate removal, as mentioned above, and the other for phosphate recovery from the siliceous gangue. The selective flotation separation of the carbonate and phosphate from siliceous constituents of the matrix at various pH levels and collector dosages are discussed. In the carbonate flotation stage, about 70% of the MgO was rejected in the froth, and the phosphate flotation stage produced concentrates analyzing about 31% P20S' 0.7% MgO and 4% acid insolubles. The overall P20S recovery in the two stages is about 85%.

Jan 1, 1989

By Zhao Guangwen, Wu Tan, Qiuzhan Tian, Duan Shuzhen

"A thorough study of lost currents in bipolar cells has been made for the development of the great potential of bipolar cells in energy saving. A proper equivalent circuit for bipolar cells has been found, and mathematic methods for computing lost currents at all kinds of polarization have been developed.At linear polarization, the lost currents can be computed by solving either a tridiagonal matrix or an ordinary differential equation of second order. This kind of values can be used to evaluate the minimal lost currents at given conditions. At other kinds of polarization, the lost currents can be computed by the same methods as above if the necessary experiments of measuring the cell voltages of every electrolytic compartment have been made. This kind of values can be used to design bipolar cells at practical conditions.Extensive experiments have been made to evaluate the effects of electrode polarization, emf of galvanic cell for the formation of electrolyzed substance, gaseous products, geometric dimensions of electrolytic cells, special resistance of electrolyte used, and the total and ordinal number of electrolytic compartments on lost currents. It is the first time to make such a systematic research by experiments in the world. Experiments showed that theoretic models were in good agreement with measured data. Experiments also showed that D.C. energy consumption of 0.45 kwh/kg of Pb for lead electrolysis from molten chlorides could be achieved in a cell with 7 bipolar electrodes.IntroductionIt is very promising to apply bipolar electrolytic cells to electrolysis of aluminum, magnesium, lead, zinc and perchlorinates for their great potential of energy saving for example, bipolar cells had been used in the production of magnesium and saved more than 30% of energy, being one of the three main techniques of energy saving in the production of titanium sponge (1)."

Jan 1, 1988