By Mei-le He, Min Chen, Xiang Shen, Lei Xu, Lei Liu, Nan Wang, Xue-liang Yin

In the current study, Al2O3-MgO-CaO refractories were prepared at 1400-1600 by the addition of MnO micro-powders, and the effect of MnO addition on densification behavior of the refractory was discussed. The results showed that the doped MnO dissolved to MgAl2O4 phase, and promoted the growth of MgAl2O4 grains by the formation of MgAl2O4 solid solution. As a result, the dense microstructure was obtained, with the apparent porosity decreased from 19.2% to 5.4% and the bulk density increased from 2.78g/cm3 to 3.15g/cm3 after firing at 1600 for 2h by the addition of 4% MnO. In addition, a texture microstructure was observed, which is considered to be favorable to improve mechanical properties and the service life of Al2O3-MgO-CaO system refractories.

Jan 1, 2016

By Jilai Xue, Jun Zhu, Yongqiang Liu

"Up-grading silicon feedstock by removing B and metal impurities can improve process efficiency and lower production cost in metallurgical processing for solar cells production. Hydrometallurgical study has been carried out in laboratory through alternative treatments of the metallurgical grade (MG) silicon (-200 mesh) by using hydrogen peroxide, hydrofluoric acid (4 mol/L) and NH4Cl-NH4 F (30:5) solution. The experiments were usually performed under mechanical agitation at 70 ? for 5 h. ICP-AES analysis showed that B content in MG silicon after the hydrometallurgical treatment has reduced by 92.4 %, and Fe, Al, and Ca contents by 98.8 %, 98.0 % and 81 %, respectively. Kinetics of these processes was also studied for better understanding of the effects of silicon powder size, acid concentration, leaching and oxidizing time on the processing chemistry.IntroductionAs one of the most clean and promising new energy, solar energy is used more and more in many countries all over the world, especially in United States, Japan and European Union. Most of industrialized states have made their national photovoltaic plans, which have stimulated further increase in use of solar energy. Photovoltaic Industry is at a high growth rate about 30 % [1-2]. For silicon solar cells to remain the mainstay for the photovoltaic industry it is necessary to develop a low-cost solar grade silicon feedstock [3]. At the same time, the availability of the currently M-G silicon from the semiconductor industries becomes limited [4]. With the advantages of low cost and low energy consumption, metallurgical routes to product solar–grade silicon get more attention [5]. These routes mainly include pickling, slagging, vacuum processing and directional solidification, etc [6]. Among them the most important processing step is the directional solidification, but it still can not satisfy the industrial demand for removing B. Removing B from Si remains as one of the most difficult and important processes in making M-G silicon [7]."

Jan 1, 2012

By Gennady I. Gulyayev

A mathematical model of plastic deformation occurring in cold plug drawing of mother tubes with initial cross-sectional wall thickness variations (CSWTV) has been developed. The main provision of the model is that eccentricity em is of such value that projection of all forces acting upon the plug in the deformation zone along the axis perpendicular to the drawing axis equals to zero. Calculations have proven that with other conditions being equal increase in the die cone angle and the deformation cycle number reduces CSWTV. Theoretical findings were confirmed by practical results. Keywords: cold, drawing, plug, die cone, plastic deformation.

Jan 1, 2003

By Masanori Abe, Yoshitaka Kitamoto, Kazuhiro Nishimura

"Ferrite plating is a chemical processing which utilizes Fe2+ - Fe3+ oxidation to synthesizing polycrystalline films of ferromagnetic spinels (MFe20 4, M = Fe, Co, Ni, Zn, Al, Cr, TI, etc:) directly from an aqueous solution at 24 - 100°C. This low temperature process allows us to fabricate new ferrite film devices on · substrates of such non-heat-resistant materials as plastics, GaAs integrated circuits, and biomaterials. Synthesized from an aqueous solution the ferrite plated ·films are highly biocompatible. Thus various magnetic device and biomedical applications have been proposed and realized using ferrite-plated films. Ferrite-encapsulated polymer microspheres are applied to antibody carries for enzyme immunoassay, and also to toners/carriers for photocopying. Perpendicular magnetic recording media utilizing plated CoNi ferrite films are proposed. The low-temperature synthesized films of NiZn and Co ferrites are potentially used as soft-magnetic and/or insulating layers, respectively at high/microwave frequencies.IntroductionFerrite plating is a processing which facilitates the formation of crystalline spinel ferrite films with various compositions, (Fe, M)30 4 (M = Fe, Co, Ni, Zn, Al, Cr, TI, etc.), directly from an aqueous solution at 60 - 100°C [1]. This opened the door to fabricating novel ferrite-film devices using substrates of such non-heat-resistant materials as plastics and GaAs integrated circuits [2-4]; conventional ferrite film preparation techniques such as sputtering, vacuum evaporation, MBE, LPE, etc., require high temperatures(> -600°C) for crystallization of ferrites, which deteriorates the non-heat-resistant substrates. Recently we extended ferrite plating to be preformed at room temperature [5, 6]. This enables us to use as substrates such organic materials as biomaterials (e.g. enzymes) having very low heat-resistance."

Jan 1, 2000

By Yuanpei LAN, Minren XU, Deliang NIU, Zhu WANG, Qingcai Liu, Shan Ren

Removal of gas is the major function of RH degasser. To optimize the RH refining craft in Chongqing Iron and Steel Co. Ltd, the degassing effect of RH degasser at different degrees of vacuum was investigated using a vacuum induction furnace. In addition, the effect of processing time on the gas content dissolved in molten steel was also studied. The results showed that degree of vacuum was one of the important factors that determined the degassing efficiency in RH refining process. High vacuum degree is helpful in the removal of gas, especially in the removal of [H] dissolved in molten steel. The processing time could be reduced from 25-30 min to 15 minutes and gas content could also meet the demand of RH refining

Jan 1, 2015

By A. Schönecker, P. Y. Pichon, B. Kraaijveld, Y. Meteleva-Fischer

"Ribbon-growth-on-substrate is a casting method, which offers a possibility to control heat flow, nucleation and subsequent crystal growth at the liquid-substrate interface. This technology allows for low-cost and high throughput shaping of silicon sheets with controlled crystal grain size and orientation for use in solar cells. In this work, sheets of silicon- metal silicide composite materials were produced and their microstructure was studied. It was shown that depending on the relevant phase diagram and casting conditions, a micro/nano-sized eutectic structure of the casted sheet can be formed. Such composite materials possess properties promising for various applications in energy generation, storage and conservation. The advantages, potential and challenges of the ribbon-growth-on-substrate technique for production of composite sheet materials as well as novel areas of application for such materials are discussed.IntroductionThe Ribbon Growth on Substrates (RGS) process is well known in the solar industry as a process to produce multicrystalline silicon wafers. An industrial size pilot production line for continuous casting of silicon wafer was developed by RGS Development B.V. in the Netherlands (Figure 1). A comprehensive review of this technology and properties of the produced silicon wafers were reported by Schönecker et al [1]. The principle of the RGS process is explained in Figure 2. The relatively cold substrate extracts the crystallization heat from the liquid silicon in the casting frame. This results in the growth of a silicon ribbon (Vc) in contact with the substrate. When the substrate (Vp) is transported from the casting zone into the cooling section, the crystal growth stops, the wafer can be removed and the substrate can be re-used. Last few years large work was done on the industrialization and market development of RGS wafers for the solar industry. Part of this work was discussed by Schönecker et al [2]. Although there is still a good perspective on the middle and long term solar market for the RGS wafers, the current market situation was found to be unfavorable for new entrants."

Jan 1, 2014

By Suresh Sundarraj

A diffusion mass transport model for predicting the microsegregation in a solidifying and coarsening dendritic mushy region of a binary alloy is presented. Two versions of this model are tested; one based on expressing the solute concentration in terms of mole fraction and the other on expressing the solute concentration in terms of mass fraction. On comparing previous model data sets and conditions, used in the analysis of Aluminum-Copper systems, a number of inconsistencies emerge. These inconsistencies are resolved on identifying a single set of data and conditions which take account of compositional density changes, "non-linear" thermodynamics and dynamic coarsening. An additional investigation is carried out to study the effect of assumed cooling mechanisms.

Jan 1, 1992

By Rui-Qing Li, John G. Peacey, Peter J. Hancock

"Noranda has been investigating a pyrometallurgical process for the direct recovery of zinc from zinc concentrate and zinc and iron containing residues. The process consists of injecting dry zinc concentrate and secondary zinc materials into a molten iron oxysulphide bath, volatilizing metallic zinc into furnace off gas essentially free of sulphur or S02, fixing sulphur contained in the feed materials as iron oxysulphide matte which is disposed, and recovering metallic zinc in an ISP type lead splash condenser. Combustion of petroleum coke with air or oxygen enriched air inside the oxygen containing matte supplies part of the heat, and the products of combustion dilute the zinc-laden gas to a desired level.This paper describes the process concept, thermodynamic background, experimental tests, mass and heat balance calculation for a conceptual flowsheet, environmental stability of the residue and advantages and disadvantages of the process. Experimental tests have successfully proved the process concept and thermodynamic predictions. Direct smelting of zinc concentrate and residues inside an iron oxysulfide bath has a great potential to become a cost effective and flexible zinc smelting process.1. INTRODUCTIONZinc is mainly produced by a roast-leach-electrowinning process route, which accounts for about 80% of the world primary zinc production. This process produces high quality zinc with very high zinc recovery (>95%) but suffers from several major drawbacks such as using high cost electricity as reductant, producing environmentally problematic iron containing leach residue (jarosite or goethite) and the difficulty in treating secondary zinc feed materials containing high impurity levels, such as electric arc furnace dusts from the steel industry, and other complex sources. Also in some areas, markets for sulphuric acid are distant resulting in negative realizations on acid sales.The Imperial Smelting Furnace (ISF) process is the major pyrometallurgical process to treat zinc-lead concentrate. The advantage of this process over the electrolytic zinc process is its flexibility in treating high-lead, bulk concentrates with high recoveries of lead, copper and precious metals. However, this is a two-stage process involving sintering of Zn-Pb concentrates followed by blast furnace reduction. The process requires large amounts of high-quality coke which is a major operation cost, and the sintering process which results in serious environmental problems."

Jan 1, 1996

By Jorge Alberto Soares Tenório

Household zinc based batteries contain some heavy metals such as zinc, manganese and mercury. There is a large effort from manufacturers in order to eliminate the last one. As a municipal waste, the disposal of batteries has become an increasing worry. The aim of the present work was to characterize dry batteries scraps, and establish a flowsheet for their processing. This was done using unit operations of mineral processing and parameters and yields of each stage have been defined. Such procedures have been chosen due to their low cost. The operations were hammer mill grinding, size separation, magnetic separation and specific weight separation in water. The characterization step was done through chemical analysis and x-ray difiactometry. After size classification, it was verified that 76.6% of the total amount of zinc was over 1.70mm. This fiaction was constituted basically of zinc and some coarse pieces from the steel body, paper and plastics. This fraction was submitted to magnetic separation followed by specific weight separation in water. A visual examination showed that during the grinding process, graphite was concentrated in the finer fractions. Manganese concentration in the fractions over 6,35mm was less than 2%. This means that there was low contamination by the paste in this fraction. It was due to the entrapment of the paste by steel scraps (from the body) and zinc (from the cup) during grinding.

Jan 1, 1999

By Xuewei Lv, Yuelin Qin, Guibao Qiu, Chenguang Bai

"Blast furnace slag (BF slag), is the main by-product in the ironmaking process, which contains large amounts of sensible heat. To recover the sensible heat, this paper described the hot experiments which were carried out in a rotary multi-nozzles cup atomizer, where the molten BFS was transformed into granules without water impingement; subsequently, a new method-pyrolysis the printed circuited board (PCB) with the hot BFS particle, was proposed for recovering the sensible heat in this study. The gaseous products were analyzed by gas analyzer. The residual of the PCB was analyzed by FT-IR and XRD respectively, and the obtained slag particles were analyzed by XRD.The results showed that it is a feasible process of pyrolyzing PCB powder with the hot BFS particle. The sensible heat of hot BF slag could be converted to chemical heat and a large amount of combustible gas could also be generated during the process.IntroductionDue to the rising of the product cost of blast furnace iron (BFI) and the increasing public awareness of environmental problems, the steel industries have to focus on the energy saving and emission reduction. Blast furnace slag (BF slag) is a byproduct from blast furnace exhaust temperature of 1450°C or so, is a high-quality waste heat resources. In China, the steel industry produces approximately 220Mt ofBFS per year, and the enthalpy of those slags is approximately equivalent to 13.3% of the whole energy consumption in the ironmaking process[!]. It can be seen, recycling waste heat is an important way of energy saving for iron and steel enterprises. The molten slag was treated by conventional water quenching method without any recovery of heat in spite of its huge potential. Also, the water quenching process consumes a plenty of water, pollutes the air and water[2]. Additionally, the extra energy is necessary for the drying process of slag to produce cement. As a kind of secondhand resource which can be reused, the BF slag contains a large amount of sensible heat. To recover the sensible heat of BF slag, three key problems should be considered, which refer to ( 1) the dry granulation of BFS without consuming water, (2) how to recover the heat of slag particles efficiently, (3) how to use the slag particles after heat recovery."

Jan 1, 2012

By James C. Foley

In-situ characterizations of green state part density and sintering state have long been desired in the powder metal community. Recent advances in non-contact electromagnetic acoustic transducer (EMAT) technology have enabled in-situ monitoring of acoustic amplitude and velocity as sintering proceeds. Samples were made from elemental powders of Al (99.99%), Al (99.7%), Ag, (99.99%), Cu (99.99%) and Fe (99.9%). The powders were pressed in a uniaxial die and examined with acoustic waves for changes in velocity and amplitude during sintering. The changes in acoustic properties were correlated with mechanical properties. Evolution of a series of reverberating echoes during sintering is shown to provide information on the state of sintering, changes in sintering kinetics as well as having the potential for detection of interior flaws.

Jan 1, 2001

By Fabiola Alvarez, Ana E. Bote, Daniel Pasquevich

"The oxidation of aluminum and its alloys was extensively studied for improving the corrosion resistance in structural materials having high specific strengths. But this reaction involves the formation of a very thin barrier layer on the metallic pieces. Furthermore, the ·recent development of the directed melt oxidation process for producing metal-ceramic; composites has renewed the interest in the study of interaction between gases and metals. Oxidation experiments in the presence of different chlorine partial pressures and at different temperatures were performed in ·a thermogravimetric balance, and microstructures were analyzed by electronic microscopy and X-ray diffraction. The oxy-chlorination kinetics was determined and the oxide formed W(IS amorphous at temperatures below 600 °C and crystalline .at higher temperatures. The appropriate experimental conditions for the fastest completed oxidation was further determined.IntroductionThe use of fine powders for the manufacture of ceramic components has significant advantages. They include excellent sinterability; low sintering temperature and better microstructure leading to improved mechanical properties. The conventional method of producing fine oxide powders involves controlled precipitation and pirolysis of suitable salts. The main limitation of the high temperature decomposition route is the evolution of environmentally unacceptable and corrosive gases. Controlled precipitation of hydroxides from solutions of salts, followed by thermal treatment involves large volumes of solutions and the calcination step that can induce grain growth (1).Direct oxidation of aluminum metal for producing alumina powder requires high temperatures for the direct oxidation of molten Al alloys by a vapor phase oxidant process (2, 3) or high technological process like thermal plasma reactor ( 4).Oxidation of high purity aluminum (5, 6) below the melting temperature· is initially characterized by a nearly linear reaction rate, followed by a rate which decreases rapidly with further weight gain. However, the oxidation rate of an aluminummagnesium alloy is much faster and it does not conform to any common oxidation law, but it is nearly parabolic at temperatures between 200 and 400 °C, an nearly linear· above 400 °C."

Jan 1, 2000

By Cang Daqiang, Li Yu, Liu Xiaoming, Zong Yanbin

"Utilization of high-quality heat in melting slag is a great challenge for iron and steel industry. In the paper, a new method is put forward to concurrently utilize heat and slag by converting the melting slag directly into high valued materials, slag glass-ceramic. A glassceramic with a higher basicity of 0.7 than traditional basicity of 0.45 was prepared from steelmaking slag in order to utilize more hot melting slag. Effects of Alz03 on its crystallization processes were researched by XRF, DTA, XRD and SEM. Results show that Alz03 in glassceramic would have great effected on its property. When the Alz03 content ranges within 12%-15%, glass-ceramics with basicity of0.7 could reach the best performances. The change of dominant phase in glass ceramics from akermanite and wollastonite to akermanite and gehlenite would significantly degrade its mechanical property. An increase of Al2O3 content leads to a rise of the viscosity and crystallization activation energy of the glass, while results in increasing sintering temperature and crystallization temperature of glass, which contributed to its fully crystallization and densification process.IntroductionSteel slag is a by-product under a process of converting iron to steel at above 1600°C, and 0.1-0.15 ton molten steel slag would be discharged for producing per ton of steel in the process. The discharged steel slag at 1600°C has heat of 68 kgce/t. In 2012, China's steel output reached 716 million tons, and produces about 100 million tons of steel slag and 68,000 tee of heat in it [1,2]. But at present, utilization of both slag and its heat at 1600°C is a great challenge for iron and steel industry.Dry granulation of melting steel slag by air and then recovering the heat of the hot air are a traditional technology which have not yet been put into practice for very low heat conductivity of the slag and low efficient of heat exchange among the different processes [3,4]. Therefore, a new method for high efficient utilization of both steel slag and its high temperature sensible heat is put forward [5,6], which is on-line reducing and extracting iron from molten steel slag and then directly preparing glass-ceramic by use of the residual molten slag."

Jan 1, 2014

By Shu Bin, Lin Chen, Tian-zu Yang, Wei-feng Liu, Wan-da Bin

"Antimony resources are rich in china, its reserves and productions are ranking the first in the world. The Chinese antimony mineral resources are mainly existed in the form of three types, such as stibnite, antimony-gold ores andjamesonite. The antimonial dust that produced from lead smelting process is an important secondary antimony resource. The different process that was adopted to extract antimony depends on the different raw materials. The process of blast furnace volatilization smelting is mainly used to treat stibnite and antimony-gold ores. But jamesonite is treated by the process of roasting-sintering-blast furnace smelting. And antimonial dust is treated in the reverberatory furnace. Many new technologies that are applied in these traditional antimony smelting processes play important roles, such as deleading agent, antimony white production, air-oxidation method, direct-blowing method, bath smelting technology, and so on. At the same time, the development of antimony smelting technology in china is prospected according to the requirement of the state environmental protection.IntroductionThere are five countries that produce antimony in the world, such as china, Tajikistan, Bolivia, Russia, and South africa, but China is the largest country of antimony production in the world. In the world, the antimony productions of 2008, 2009, and 2010 are 182,000 tons, 154,000 tons, and 167.000 tons respectively, but Chinese antimony productions are 166.000 tons, 140,000 tons, and 150,000 tons respectively. So Chinese antimony production was accounted for more than 89% of the world in 2010. It indicates that China have irreplaceable advantages in antimony resource and production all over the world."

Jan 1, 2013

By May Nyman

Due to the vast diversity of chemical media in which metal separations are executed, a wide range of ion separation materials are employed, This ,results in an ongoing effort to discover new phases with novel ion exchange properties. We present here the synthesis of a novel class at, thermally and chemically stable microporous, niobate-based materials. Ion exchange studies show these new phases are highly selective for Sr2+ and other bivalent metals.

Jan 1, 1999

By Godwin J. Igwe

For soil remediation technology to be effective, a thorough understanding of the interactions between a targeted contaminant and the soil matrix is crucial. Proper selection of remediation technology, based on understanding the bonding/binding characteristics of the soil and contaminant, can often result in significant remediation cost savings. Contaminated soil cleanup is complicated by both the physical nature of the soil formation and the behavior of contaminants introduced into the formation. Contaminants can exist in the subsurface in different phase attached to the soil surfaces, dissolved in the ground water, or occupying pore spaces as a separate gaseous or liquid phase. Contaminants properties and how they exist in the subsurface influence their toxicity, mobility and treatability with different remediation technologies A soil characterization study was performed to provide information for remediation technology selection for an inorganic lead contaminated soil. The soil pH, TCLP analysis, thermogravimetric analysis, the soluble anions and cations present, equilibrium leaching tests, analysis by x-ray fluorescence, sequential extractions and speciation analysis using scanning electron microscopy, were all used. Results provided many insights into contaminant behavior in the soil, indicating ultimately whether soil washing or solidification/ stabilization remediation technologies were applicable.

Jan 1, 1994

By Joseph Goodwill

1. PURPOSE The objective of this paper is to summarize a study undertaken by the EPRI Center for Metals Production (CMP). The overall purpose of the study was to identify electrolytic opportunities that might merit consideration for joint development by industry and EPRI. 2. SCOPE The electrolytic technologies of interest to this study include: Electrorefining, Electrowinning, and Fused-salt electrolysis. Recovery from primary, secondary, and waste materials were included in this effort; however, we excluded from consideration: Plating and coating operations, such as electrogalvanizing; Mining and milling operations in which electric energy is predominantly used for comminution; Electrothermal processes in which submerged-arc, open electric-arc, and plasma-based smelting processes use electric energy largely to provide a melting or refining ("heating") capability; and Aluminum electrotechnologies since these were the subject of a separate study (CMP 86-2). We recognize that there may be some "gray areas" between these excluded areas and the electrolytic sectors of interest. For this reason, a secondary criterium was used, namely, if the major use of electric energy was to extract or refine the

Jan 1, 1990

By Autumn Fjeld

The filling and solidification of an industrial scale composite casting has been simulated to investigate the re-melting of the outer shell material during casting. Production of a composite requires a two-step casting process which includes centrifugal casting of a hard outer shell material and subsequent conventional ingot casting of a tough core material into the shell-mold assembly. During casting of the core, a thin layer of the shell material re-melts and mixes with the core material producing a bonding layer of intermediate composition. The present numerical model employs the volume of fluid method and an enthalpy-porosity technique to couple the filling of the core material and re-melting of the shell material. The interface between the two materials is tracked and can be used as a guide to examine the extent of melting and, to some degree, mixing of the two fluids and species diffusion.

Jan 1, 2008

By Richard D. Hagni

The techniques of reflected light microscopy and cathodoluminescence microscopy are uniquely suited to the study of the products from many important industrial problems. Ref1 ected 1 ight microscopy provides the means to rapidly identify the mineralogy of an industrial sample, determine the abundance of each phase, and examine the mineral intergrowths or textures. Cathodoluminescence microscopy is a relatively new instrument that provides the means to cause many minerals to cathodoluminescence under the microscopy. The cathodoluminescence of a mineral allows it to be readily distinguished from other phases that differ in cathodoluminescence but are similar in optical properties. Cathodoluminescence microscopy is especially useful to detect cathodoluminescence minerals that are present in only small quantities. Reflected 1ight microscopy and cathodoluminescence microscopy have been successfully applied in studies of beneficiation products, prediction of beneficiation and leaching problems, phosphatic iron ores and mill products, pyrometallurgical products, roasted refractory gold-bearing sulfides, ceramic build-ups, electric arc furnace and smelter dusts, and other industrial products.

Jan 1, 1993

By J. R. Odekirk

The nature of mineral distributions and locking characteristics in mill products are important factors in understanding mill performance. Such data are obtained by microscopic point counting methods. Reduction 'of point-count data from volume to weight percentages, and reduction of data for each size fraction back to a head sample requires lengthy hand calculations. The use of computer processing for such data reduction results in obtaining information on a realistic time basis. An example of computer processed point-count data is presented.

Jan 1, 1981