Search Documents

By Qingsheng Liu

A new method of recycling aluminum dross for preparation Al-Si-Ti alloy was studied in this paper. This was carried out in two processes. first the aluminum doss was pretreated by leaching and calcining process, the fine purity and phase of the intermediate oxide powder up to electrolysis demands, then, could be obtained when aluminum dross after washing have been leached for 2h at 100? in 20% hydrochloric acid and calcined for 2h at 1200?, which was treated by cryoite-based molten salt electrolysis. Finally, the Al-Si-Ti alloy was successfully obtained through electrochemical co-deposition in the cathode shows a typical as-cast microstructure. This new recycling method can produce high quality alloy and may bring remarkable economic and social benefits.

Jan 1, 2010

By Bowen Li

Andalusite is an excellent raw material for refractory applications due to its high aluminum oxide content and phase transformation to mullite at high temperature. Granular andalusite in particle sizes of about 1 to 2 mm was traditionally utilized for the manufacturing of refractory brick. However, if powder andalusite in micron particle size is utilized in high-alumina refractory products, reinforcement on the refractory brick can be obtained and the sintering temperature can be decreased. The phase transformation of powder andalusite plays a key role for the difference.

Jan 1, 2006

By Zhouhua Jinag

The attempt has been made to manufacture high nitrogen austenitic stainless steels by pressurized electro-slag remelting furnace with maximum nitrogen pressure of 7MPa. To obtain high nitrogen content in steels, the compound electrodes with different nitrogen sources (FeCrN, Si3N4) were prepared. Using the Si3N4 as the nitrogen alloying source, the silicon contents in ingots were prone to be out of the specification range, and the electric current fluctuated greatly and the surface qualities of the ingots were poor. The surface qualities of the ingots were improved using FeCrN as nitrogen alloying source. The sound and compact macrostructure ingot with the maximum nitrogen above 1.0wt% could be obtained. A series of high nitrogen austenitic stainless steels have been successfully developed by this method. The mechanical and pitting corrosion resistance properties of high nitrogen austenitic stainless steels were investigated. The results show that the steels exhibit excellent mechanical and pitting corrosion resistance properties.

Jan 1, 2009

By S. Uddin

An integrated device has been developed to measure sedimentation potential, conductivity and pH simultaneously of particulate systems. Maxwell?s model was used to calculate volume fraction of solid from the conductivity data. In this approach, all system variables are known and zeta potential can be calculated from Smoluchowski?s equation. The technique is validated by comparing zeta potential vs. pH for alumina and silica suspensions with electrophoresis measurements. The technique was extended to mixed alumina/silica systems. Sufficient column height along with size difference between the two minerals allowed gravity fractionation during settling. Sedimentation potential measured over time identified the transition from one mineral to the next. Using XRD analysis the results supported the correlation between surface charge and sample composition. This is a step towards characterizing surface charge of mixed systems of interest in mineral processing.

Jan 1, 2010

By Valerio Viti

In High Pressure Die Casting a molten metal is injected through a thin gate into the cast cavity. High injection pressures and high gate velocities create atomization phenomena which can negatively affect the final quality of the cast. In order to control atomization process it is essential to understand the atomization patterns and the two-phase flowfield that exist at the gate exit. In the present work, 2D numerical simulations of the flow of molten Magnesium through a high aspect-ratio rectangular gate are performed using a water analogue for an open and closed cavity. The numerical simulations made use of VOF-type (Eulerian) physical models and Lagrangian models. Further, a sub-grid scale model was implemented that, in conjunction with VOF-type equations can efficiently predict the general atomization pattern without the need for high-resolution grids. The numerical results were compared to experimental data for validation.

Jan 1, 2006

By Clara María Lamus Molina

The following minerals found in the residual black sands from gold mining in El Bagre Antioquia (Colombia) were identified as having major economic interest: Ilmenite (FeTiO3), with an average of 49% of TiO2, frequently altered presenting crowns; lamellaes of rutile and alteration textures; titanomagnetite with up to 25% of TiO2; magnetite (Fe3O4) in individual grains or associated with others minerals as hematite and ferromagnesian silicates rutile (TiO2) with considerable quantities of Nb2O5(0.1-3.7%Wt); zircon (ZrSiO4) with 66%Wt of ZrO2 and monazite with an average of 63.43%Wt of REE, this frequently associated to xenotime and thorite forming textures as little drops. Analysis in EPMA and SEM/EDS showed percentages of minor elements and traces, thereby clearly establishing the applications of these minerals in diverse industries. Furthermore, a detailed granumetric study of the different minerals and textural relationships among them also allowed for establishing the basis for possible processing and exploitation.

Jan 1, 2006

By Changqing Su

A batch incubation experiment has been carried out to investigate the optimal condition for the microbial remediation of hexavalent chromium (Cr(VI)) in soils contaminated by chromate ore processing residue at Hunan Iron-Alloy Factory in China. The optimal condition was obtained by comparing the remediation efficiency of Cr (VI) by indigenous bacteria under different culture media, the quantity of nutrient sources, the pH and the temperature. The results indicated that glucose and yeast extract was the optimal component of culture medium and the quantities of the above components were 8 g L-1 and 13 g L-1, respectively. The optimal temperature and pH value were 30_ and 10.0, respectively. A bioreactor was operated under the optimal condition to evaluate the efficiency of Cr(VI) remediation in the contaminated soil. The result showed that water soluble Cr(VI) in soils was reduced from 320 mg kg-1 Cr(VI) of the initial concentration to below detection limit after 30 h in a bioreactor. Thus, there is a large potential to make bioremediation for the reduction of Cr(VI) to Cr(III) by the addition of optimal culture medium under aerobic condition.

Jan 1, 2010

By Igor Zh. Bunin

A model for developing electric discharges between sulfide mineral (pyrite) particles under high-voltage nanosecond pulses in a liquid medium (water) is considered. A possibility of electrical breakdowns of liquid gaps between particles under nanosecond pulses is shown. This probability and the energy released in discharge channels depend strongly on the sulfide conductivity.

Jan 1, 2010

By Junfeng Shen

Geosynthetic clay liner (GCL) is a kind of waterproofing material used widely in engineering. The waterproof mechanism is understood in terms of bentonite particles becoming a water-obstructcolloid layer after they absorb water and swell. The swell stress, however, has not been determined directly till now. In our experiment, the swell stresses of the GCL under saturated and water absorbing conditions are measured directly using a custom-made instrument. The results show that (1) the instrument designed by the authors performed satisfactorily and the test results are reproducible; and, (2) The trend line of swell stress variation with time can be divided into three segments. The first segment is characterized by a quick increase of the swell force in the first 0?50 hours. The swell stress increases by 7.00×10-4?1.00×10-3 Mpa / hour. The second segment shows a slow increase of the swell stress during the 50?1730 hours. The swell force increases by 7.54×10-6?2.02×10-5Mpa / hour. The third segment is characterized by little variation in the swell stress after 1730 hours. In this segment, the average value of the swell stress measurements is 0.0719Mpa and the maximum value is 0.0729Mpa. It is suggested that the swell stress is mainly raised by water entering the pores among montmorillonite particles and the interstitial layers in individual montmorillonite crystals, leading to an increase in volume and manifested as a stress on the surrounding materials.

Jan 1, 2006

By Zengjie Wang

Kinetic study of hydrochloric acid leaching of Panzhihua ilmenite from China is presented. Both temperature and concentration of hydrochloric acid have significant effects on the rate process of Fe dissolution from ilmenite ore, while the ratio of liquid to solid has little effect on the Fe dissolution. The Fe dissolution is found to follow the spherical model f (??) =1-(1- ??)1/3 and the apparent activation energy is calculated as 47.21 KJ/mol, suggesting a chemical reaction controlled mechanism. The dissolving behaviors vary at different kinetic stages. At the beginning the amount of the dissolved Fe and Ti increased monotonically with leaching time, while about 15 minutes later the dissolved Ti in the form of TiOCl2 began hydrolyzed into TiO2 fines reunited on the ilmenite ore surface, as observed by SEM and EDS technique. For the unreacted ilmenite particles covered by a layer of hydrolyzed TiO2, the leaching seemed to be as a selective leaching of iron and because Ti dissolved from and hydrolyzed rapidly again into the unreacted ilmenite particles. The leaching process can be ended 4 hour later when almost of Fe has dissolved into the solution and TiO2 remains as solid residues. The effects of acid concentration and leaching temperature were also investigated.

Jan 1, 2009

By Grigore Matei

The thermodynamic properties of CuzS-FeS system are important not only in the ease of copper smelting but also in the case of general pyro-metallurgy. However there arc not many reported activity data In this study, activities of FeS and CU2S in the Cu2S-FeS system were calculated using the Darken's method from the activity data of the Cu2S-FeS-Sb2S3 systems measured by the transportation method at 1050°C. The activities of Cu2S and FeS in the Cu2S-FeS system showed negative deviation from the ideal behaviour and satisfied the relation of the Gibbs-Duhem equation.

Jan 1, 2003

By Peter Ryan

A patented process for agglomeration of Smelter ESP dusts is described. Addition of suitable binders followed by compaction, transforms fine, difficult to handle material into a dry, flowable agglomerate suitable for plant reentry. Details for the agglomeration process metallurgy and laboratory pilot plant testing are discussed. An example of full scale plant operations is described.

Jan 1, 1999

By Xiaodong Wang

A liquid metal flow generated by a magnetic field whose traveling direction is periodically reversed, the Reversed Traveling Magnetic Field (R-TMF) is studied. The modulation frequency ranges from 0 to 6 Hz. Ultrasonic Doppler velocimetry probes the generated fluid flow. Depending on the modulation frequency, a number of characteristic flow features are exhibited. A transition frequency (approximately 4 Hz) exists, above which the flow is no longer sensitive to the force modulation. Below this transition point, the amplitude of the velocity oscillation increases, and then below fm = 0.05 Hz, it saturates around a value close to that observed without any modulation. A theoretical model to obtain an analytical solution of electromagnetic force and to predict flow motion is developed, which is fairly in agreement with the experiments.

Jan 1, 2009

By A. Krishnan

Keywords: Tantalum extraction, SOM Technology, inert anode, membrane stability The Solid Oxide Oxygen Ion conducting Membrane (SOM) technology offers great potential for environment friendly and energy efficient extraction of high-energy content metals. This work was performed to demonstrate the technical and commercial viability of the technology to produce tantalum metal directly from tantalum oxide and ore concentrates using a solid-oxide, oxygen-ion-conducting membrane (SOM). The process can be used to efficiently produce tantalum metal without expensive pre-processing of raw materials and without harmful by products. The work reported in this paper is: the proof that high purity tantalum metal can be produced, study of the electrochemical behavior of the cell and the method to increase membrane stability.

Jan 1, 2005

By Jewel Andrew Gomes

Arsenic is considered as one of the toxic materials being controlled by Environmental Protection Agencies in several developed and developing countries. It is found in the nature as constituents of the soil, minerals and also in various organic forms. It enters the air, water, and land from wind-blown dust and gets into water from runoff, leaching, soil erosion and anthropogenically from chemicals used for wood preservation, insecticides, medicine, military purpose, pigments, and electronic circuitries. There are several techniques available for removal of Arsenic, such as coagulation/filtration, lime softening, ion exchange, reverse osmosis, nanofiltration, wet chemical, and electrochemical. Electrocoagulation has been found as one of the most efficient techniques to remove inorganic arsenic with more than 99% efficiency. In this paper, we present our work on electrochemical treatment of both the inorganic and organic arsenic from water using various sacrificial electrode materials, i.e., iron, aluminum, copper, and combination of them. The floc produced by this method has been also characterized using XRD, SEM/EDS, FTIR, and cyclic voltammetry.

Jan 1, 2010

By Khandaker M. Anwar Hossain

This paper presents the development of lightweight concrete (LWC) incorporating pumice aggregate and volcanic ash (VA) based ASTM Type I blended cement (PVAC). Fresh and mechanical properties of LWC mixtures such as slump, air content, compressive strength, tensile strength, density and modulus of elasticity are described. The durability characteristics are investigated by drying shrinkage (DS) and water permeability. The investigation suggests the production of LWCs incorporating blended PVAC and VPA having satisfactory strength/durability characteristics for structural applications. The use of PVAC induces the beneficial effect of reducing drying shrinkage and water permeability. Development of such non- expensive and environmentally friendly LWCs with acceptable strength and durability characteristics is extremely helpful for the sustainable development and rehabilitation of volcanic disaster areas around the world.

Jan 1, 2010

By M. Faraji

Inclusions formed in a high-carbon, manganese-silicon killed plain steel (Fe-0.77C wt%) were studied. Various techniques were used to characterise the inclusions, and the latter were classified according to their chemical composition, size and morphology. The main constituent elements entering the inclusions were Mn, S, Al, and oxygen. Alongside MnS and some Al2O3 inclusions many non-metallic inclusions appeared in complex forms, consisting of silicates, sulphides and oxides. Duplex oxy-sulphides, mainly MnS combined with Al2O3, or SiO2 were the most common complex multiphase inclusions in this steel. The nanoindentation technique was used to assess and rate different types of inclusions and data of the hardness and elastic modulus of individual inclusions at room temperature are presented.

Jan 1, 2010

By Z. Sun

Imposing a strong magnetic field is considered to be an attractive method to prepare materials with aligned or textured structures due to its intrinsic properties, e.g. non-contact and easily controllable. However, the nature of the strong magnetic field effect still remains unclear and further research is needed. In the present paper, the effect of a strong magnetic field on the solidification of a hypereutectic Al-Cu alloy was investigated. After magnetic field treatment, the primary phase was aligned parallel to the magnetic field direction. Meanwhile, the eutectic micro-structural constituent became elongated and thinner. A theoretical analysis was conducted to have a better understanding of the phenomena. During solidification, the magnetic Faraday and dipole-dipole interaction forces are considered to decrease the solute pile-up in front of the solid-liquid interface and modify the eutectic cell formation. The alignment of the phase is due to the shape magnetic anisotropy and crystal magnetic anisotropy.

Jan 1, 2010

By Lijuan Chen

During the detoxification of chromium-containing slag by Achromobacter sp. CH-1, anionic surfactant Sodium Dodecyl Sulphate(SDS) and its mixed systems with different Tween surfactants(Tween 20, Tween 60 and Tween 80) were used to promote the interaction between the bacteria and the chromiumcontaining slag and the rate of acid-soluble Cr( ? ) leached from the slag. The effects were evaluated by the surface tension, the pH of the leaching solution and the leaching rate of total Cr( ? ) from the slag. The results showed that the surfactants systems improved Cr(VI) leaching and its detoxification of chromium-containing slag. The mixed surfactants of SDS combined with Tween surfactant revealed better effectiveness of detoxification than SDS only. When the mass ratio of SDS to Tween 80 was 1:1, the rate of Cr( ? ) leached from the slag increased by 12%.

Jan 1, 2009

By R. Fragoudakis

AISI 4130 steel is a medium carbon Cr-Mo steel used in automotive, aeronautic and other general-purpose industries. In this study, 4130 steel fatigue specimens were carburized at 927oC to enhance the carbon content in the steel, raising it from approximately 0.30% (non-carburized) to 0.90% (carburized, oil quenched and tempered). Rotating bending fatigue tests were performed on the R. R. Moore Rotating Beam Fatigue Testing System, in order to determine the high cycle fatigue (HCF) life of 4130 steel and plot the corresponding S-N diagrams. A comparison of the results of carburized and non-carburized specimens shows that carburizing of steel: a) increases the surface hardness and b) improves the fatigue strength of the steel by at least two orders of magnitude.

Jan 1, 2010