By W. C. Winegard, A. Galibois, C. J. Beingessner

The effects of solutes on the distribution of two-dimensional configurations of grains in zone-refined tin have been studied. When solutes with partition coefficients (ko) greater than unity are added, three-sided pains become more prevalent and the growth law changes. It is shown by electron-Probe micro-analysis that a solute buildup occurs ahead of a moving grain boundary when ko > 1. It has been found recently1, 2 that solutes with partition coefficients greater than unity have a larger retarding effect on grain growth than solutes with k, less than unity. ko is defined as the ratio of the concentration of solute in the solid to the concentration of solute in the liquid with which the solid is in equilibrium. Niessen and winegard2 have suggested that this effect is probably due to the complex shape changes which occur during the process of grain growth and that no theory based on single boundary motion3-5 can explain the results. They suggested that the dissociation of the unstable fourfold junction was delayed in alloys where ko was greater than 1 because the boundaries at the junction had to move into a region of high solute concentration. If indeed this mechanism were correct, it was felt that not only would the dissociation of fourfold junctions be affected by the solute buildup ahead of the boundaries, but the collapse of three-sided grains would be impaired. These combined effects would naturally lead to a modification in the distribution of the number of sides per grain seen on a two-dimensional section. The present investigation was undertaken to test these hypotheses by examining the grain-growth process in detail. EXPERIMENTS The Distribution of Grain Configurations in Zone-Refined Tin as Seen on a Two-Dimensional Section. Following the method of Bolling and Winegard,6 zone-refined tin was cast into button-shaped specimens and, subsequently, plastically deformed under a drop hammer at room temperature. The resulting flat coin-shaped samples were annealed at 200°C, some for 50 sec and others for 100 sec. The specimens were then examined to determine the distribution of the number of sides per grain, i.e., the num- ber of crystals adjacent to any particular grain in the section. For simplicity, the grains were classified as three-sided, four-sided, and so forth; this concept is schematically illustrated in Fig. 1. As indicated by smith,' it was necessary to examine every grain within an enclosed area to obtain a proper distribution of the relative frequency of each type. The distributions for the two annealing times are illustrated in Fig. 2. The total number of grains examined is also indicated on the figure. It is evi-

Jan 1, 1965

By J. T. McGrath, G. B. Craig

Tensile tests on aluminum single crystals, grown from the melt, revealed that the yield stress of these crystals was raised as the amount of striation substructure was increased. The number of striation-type boundaries was varied by changing the rate of growth of the crystals. The results are interpreted in terns of a blockage of dislocation movement by striation boundaries. IMPERFECTIONS are known to have a large effect on the mechanical properties of metals. Teghtsoonian and Chalmers 1 studied a block or striation-type substructure in tin and found that the formation of the striations depended upon rate of crystal growth and orientation. They found that the angular misorienta-tion between neighboring striations varied between 15 min and 5 deg. Atwater and chalmers2 investigated striations in tin and lead, and found that purity was another factor which influenced their formation. There was a limiting purity above which the striations were straight and regular. There is little information in the literature concerning how substructures in melt-grown crystals affect strength. washburn3 introduced small-angle boundaries into zinc by a shear process and found a subsequent increase in yield stress which he attributed to the presence of these boundaries. Lauriente and pond4 found the critical resolved shear stress in aluminium crystals grown from the melt, to increase with etch pit density. The etch pits were used as an indication of growth imperfections. In Hibbard's5 work on lineage structure in copper crystals grown from the melt, he tested one crystal containing interlineage boundaries, and found a 50 pct increase in the critical resolved shear stress. Fleischer and Chalmers6, in a recent paper, mention briefly that, in the production of aluminium crystals from the melt when the growth rate was raised from 1.2 to 18 cm per hr, the yield stress increased 50 pct. They felt that the increase in yield stress with rate of growth might be attributed to a higher concentration of impurities in the gage length and also might be affected by the increased number of small-angle boundaries (striations). The present investigation was undertaken to determine the effect of the striation substructure on the strength of aluminum single crystals. EXPERIMENTAL PROCEDURE Aluminum single crystals of 99.9992 purity were grown from the melt using a technique described by Chalmers.7 The growth rate was varied from 0.6 to 20 mm per min, thus producing crystals with varying numbers of striation boundaries. To avoid prior deformation, the crystals were chemically cut to the desired length with a saturated solution of cupric chloride. They were then annealed at 580°C for 24 hr and allowed to cool slowly in the furnace. Finally, the specimens were electropolished using an electrolyte of 5 parts ethyl alcohol and 1 part perchloric acid. Each specimen was approximately 5 in. in length and 0.125 sq in. in cross section. The average orientations of the 5 series of crystals studied are shown on the stereographic projection of Fig. 1. The crystals were strained approximately 2 pct in a soft tensile machine. The strain sensitivity was 3.6 x 10-4 cm over a 5-cm gage length.

Jan 1, 1960

By H. G. Sell, G. W. King

An investigation was made of the lensile proper-ties of recrystallized high-purity tungsten and a W-1 pel ThO2 dispersed-phase alloy over the temperature region of 800° to 2400°C. The thoria addition resulted in a modest strengthening effect over the entire temperature region. A decrease in ductility of both materials occurred above 0.5 Tm which was caused by void formation. Current theories of IT has long been recognized that a second phase of hard particles has a strengthening effect on a pure metal. At low or intermediate temperatures (<0.5 Tm), the strengthening effect is thought to arise mainly from the interaction of dislocations with dispersed particles. Above 0.5 Tm, dynamic recovery processes greatly alter the deformation mechanisms from those simply involving glide, and grain bound- strengthening by a dispersed second phase do not adequately explain the tensile results. Melallographic examination suggests that the improved strength of tire alloy results from the effect of thoria on the mierostructure. Stress-dependent thermally activated processes were found to occur high temperatures. aries may act as sources of weakness rather than strength because of grain boundary sliding. Grain boundary sliding at high temperatures has been postulated to be the primary factor giving rise to the formation of voids or cavities at grain boundaries1-3 which in turn cause premature failure and poor ductility.4 Voids, once formed, can grow by the condensation of vacancies from the equilibrium concentration&apos; or from the excess vacancies produced by the deformation.4,5 The high-temperature tensile properties of unalloyed tungsten have previously been investigated by Sikora and Ha116 and also by Taylor and Boone.7 The purpose of the present work was to investigate

Jan 1, 1965

By D. I. Bardos, A. M. Bardos, Paul A. Beck

The approximate effective silicon radii in ternary Laves phase alloys with transition elements and silicon were found to range between 1.16 and 1.21A, i.e., considerably smaller than the atomic radius calculated for elemental silicon. The atomic radii were found to increase with the size of the transition element atoms in the structure. It has been noted by Aronsson1 that silicon in solid solution in iron, cobalt, and nickel has an effective CN 12 atomic radius of approximately 1.20Å, a value very much smaller than the CN 12 radius of 1.34Å derived from the interatomic distances in elemental silicon.7 The unusually short metal-silicon interatomic distances in transition element monosilicides and disilicides have been also pointed out by various investigators.1 A similar tendency was observed by Nevitt in Cr3O type silicides.2 Recent work on Laves phases in ternary systems of silicon with transition elements4"8 suggested that extensive Laves phase fields may occur in such systems.8 It has been pointed out by Laves7 that the MgCu2 and MgZn2 type structures lend themselves particularly well for the determination of the effective radii of the component atoms. In these AB2 phases the B atoms are arranged in close packed straight lines, and their distances are related in a simple manner to the lattice parameters.8 The present work was undertaken in order to find out whether or not the B transition element in such AB2 Laves phases can be replaced to an appreciable extent by silicon. In cases where extensive substitution proves to be possible, the "average atomic radius for the B site" at various silicon contents was to be determined, and the effective atomic radius of silicon calculated by extrapolation to complete replacement of the B component by silicon. The following ternary systems were studied: Ti-Mn-Si, Ti-Fe-Si, V-Co-Si, V-Ni-Si, Nb-Fe-Si, Nb-Co-Si, Ta-Fe-Si, Ta-Co-Si, and Mo-Fe-Si. In all of these alloy systems, the Laves phase solid solutions were found to extend over a considerable range of silicon content. As previously reported,4"8 in the V-Co-Si, V-Ni-Si, and Mo-Fe-Si ternary systems Laves phases do occur, even though there are no corresponding binary Laves phases. In stabilizing the Laves phase, silicon acts as if it were decreasing the effective electron concentration of the alloy.8 A more detailed study of the boundaries of the Laves phases in the V-Co-Si and V-Ni-Si systems has been made and will be published elsewhere. In both cases, the elongated Laves phase fields extend parallel to the B-Si side of the composition triangle, clearly showing that silicon is substituting for cobalt, respectively, nickel over a wide range of compositions. The binary Laves phases NbCo2 and TaCo2 have the cubic MgCu2-type structure. It was found that, in both ternary systems with silicon, again the MgZn2-type hexagonal Laves phase is stabilized and that this phase extends to high-silicon contents. In each ternary system at least three Laves phase alloys of the composition A(B1_xSix)2 were used, x here denoting the fractional substitution of the B-transition element atoms by silicon. The alloys, listed in Table I, were prepared by arc melting in argon. Each specimen was water quenched after a homogenizing anneal of 3 days at 110(FC, except for the Mo-Fe-Si alloys, which were annealed at 1200°C. Metallographic examination showed that most of the homogenized alloys consisted of a single phase, although some had minor amounts of a second phase, as shown in Table I. X-ray diffraction patterns were prepared using an asymmetrical focusing camera of large resolution and Fe Ka radiation. The patterns were indexed, and the lattice parameters of the hexagonal Laves phases were determined from the available diffraction lines of highest indices: (213), (205), and (313). The lat-

Jan 1, 1963

By F. Seitz

STAFF: Editor, Gerhard Derge Carnegie Institute of Technology Schenley Park Pittsburgh 13, Pa. Editorial Assistant, M. A. Redmerski Managing Editor, James J. Burke THE METALLURGICAL SOCIETY: John Chipman, President; W. R. Hibbard, Jr., Post-President; C. C. Long, Vice-President; T. D. Jones, Treasurer; R. W. Shearman, Secretary. PUBLICATIONS COMMITTEE OF THE METALLURGICAL SOCIETY: R. Maddin, Chairman; Dennis Carney, J. C. Fulton, J. H. Hollomon, T. B. King, C. C. Long, W. 0. Philbrook, J. D. Sullivan, David Swan, and F.L. Vogel. Review and selection of manuscripts is under the supervisian of the following Publications Committees: Extractive Metallurgy D ivis ion: T. 0. King, Chairman; S. J. Dick inson, R. P. Hermsdorf, R. Schuhmann, Jr., and H. H. Kel logg. Institute of Metals Division: F. L. Vogel, Choirmon; R. L. Smith, Vice Chairman; R.W. Balluffi, J. H. Bachtold, A Servi, C.D.Graham, Jr., C. G. Goetzel, F. E. Joumot, Jr., G. E. Pellissier, Paul Gordon, Jock Washburn, Harold Margol in, A. U. Seybolt, I. R. Kromer, R. A. Meussner, R. W. Guard, M. Harmon, J. N. Hobstetter, Dean Starr, P. Shewmon, R. Gordon, J. 0. Betterton, and E. Morgan. Iron and Steel Division: W. 0. Philbrook, Chairman; F. C. Langenberg, C. W. Sherman, J. Wagstaff, and E. J. Whittenberger. Published bimonthly by the American lnstitute of Mining, Metallurgical, and Petroleum Engineers, Inc., 29 West 39th Street, New York 18, N. Y. Telephone: PEnnsylvania 6-9220. Subscription $20 per year for non-AIME members in United States and North, South, and Central America; $25, foreign; $5 for AlME members. Single copies, $4.00, single copies foreign, $5.00. The AlME is not responsible for any statement made or opinion expressed in its publications . . . Copyright 1959 by the Americon Institute of Mining, Metallurgical, and Petroleum Engineers, Inc. . . . Registered cable address, AlME New York ... Indexed in Engineering Index, Industrial Arts Index, and Chemical Abstracts . . .Second class postage paid at New York, N. Y. , ond Ann Arbor, Mich. Volume 215, Number 3

Jan 1, 1960

By J. W. Cunningham, M. J. Stultzman

THE demand for improved materials for high-temperature service has increased during the last few years. Iron,- nickel,- and cobalt-base alloys have been investigated extensively and many alloys with outs&apos;tanding high-temperature strength have been developed. Considerable research has been directed toward improved methods of processing these alloys. The vacuum furnace as a tool for the purification and improved control of high-temperature alloys has been studied extensively and production units are in operation. The research covered by this paper studied the effects of casting in air, vacuum, or argon upon the elevated-temperature properties of two nickel- and two cobalt-base alloys. The alloys investigated were Stellite 31, He 1049, Udimet 500, and Guy Alloy. MELTING AND CASTING PROCEDURES Two heats of each of the four alloys under investigation were melted and investment cast under the following conditions: 1) Stellite 31 was melted and investment cast in air and in vacuum, with an argon atmosphere for pouring. 2) He 1049 was melted and investment cast in air and in vacuum, with an argon atmosphere for pouring. 3) Udimet 500 was melted and investment cast in vacuum with and without additions of zirconium and boron. 4) Guy Alloy was melted and investment cast in vacuum and in argon. The heats were all melted in induction furnaces equipped with preformed magnesia crucibles of 50-lb capacity. The air-melting furnace was powered by a spark-gap converter of 40 kw capacity. The vacuum-melting furnace was powered by a motor-generator set of 100 kw capacity. The argon heat of Guy alloy was melted in the vacuum melting furnace under an argon atmosphere. Virgin materials were used for preparing all heats except the air heats of Stellite 31 and He 1049. The charge for the air heat of Stellite 31 was a commercial blend of shot. The charge for the air heat of He 1049 was Stellite 6 shot plus those virgin materials necessary to give the desired composition. All of the materials used were of the same grade used com-

Jan 1, 1960

By G. Krauss, W. Pitsch

The fine structure of the bcc martensite formed in an Fe-33 wt pct ATi single crystal of arrstenite is sho~on by transmission electron microscoPy to consist of combinations of transformation twins, stacking faults, deformation twins, and regular arrays of parallel screw dislocations. These structures constitute evidence for the multiple lattice-invariant deformations which operating during the formation of martensite could produce the real habit-plane scatter measured by a two-surface analysis of the plates formed in the single crystal of this investigation and reported in the literature for other Fe-Ni rnartensites. CRYSTALLOGRAPHIC theories1,2 of martensitic transformation show that the habit plane of martensite in a parent lattice is dependent in part upon an inhomogeneous distortion or lattice-invariant deformation which takes place on a fine scale within a martensite plate during its formation. Several recent theoretical papers3,4 have addressed themselves to an analysis of a wide variety of conceivable lat-tice-invarient deformations and the habit planes which they produce, while experimental investigation have been concerned with either the measurement of habit planes or the description and identification of the martensitic fine structure which reflects the nature of the lattice-invariant deformation operating during transformation. In Fe-Ni alloys with subzero Ms temperatures, the group of alloys with which this paper concerns itself, habit planes have often been found to scatter an amount greater than might be expected from possible experimental errors,5-7 and fine twinning has been identified as a major constituent of the fine structure of martensite.8-11 It has been suggested3,4 that more than one type of invariant shear occurs during martensitic transformation. This possibility has been experimentally supported12,13 by the observation of both dislocation configurations and twinning in a single martensite plate. The purpose of this paper is to report additional evidence for multiple lattice-invariant deformations in martensite and so to account for the real scatter in the habit planes of the martensite plates formed in Fe-Ni alloys. EXPERIMENTAL PROCEDURE The Fe-Ni single crystal was produced by pulling a high-purity iron and nickel charge through a single-crystal vacuum furnace in an alumina crucible. The crystal was double-melted to promote homogeneity and to increase its size by further additions on the second pass. In its final form the crystal was 4 cm in diam and 5 cm long. The nickel and carbon contents were analyzed at 32.9 and 0.006 wt pct, respectively. The austenite of this alloy first transformed to martensite by bursts at about -120°C, and, to preserve as much of the austenite as possible, all transformation was performed just below -120°C. Some observations were made on transformed samples which had been heated for 2 min at 340°C. It is assumed that the features of the martensite of these samples, Figs. 1 and 4, are the same as those of the as-quenched martensite. Orientation of the crystal by X-ray diffraction established 10.735 0.609 0.3161? as the axis of the crystal, an orientation that was checked within 2 deg by neutron diffraction. Further checks by electron diffraction of samples cut normal to the axis confirmed this orientation within the larger limits of error inherent in electron diffraction of thin foils. The X-ray orientation was the one used for the two-surface analysis of the martensite habit planes. A two-surface analysis was performed on the quadrant of the single crystal which had been oriented by both X-ray and neutron-diffraction techniques. Photomicrographs at X50 were made on two surfaces along an edge 2 cm long. Fiducial marks and the fact that many of the plates were almost completely surrounded by retained austenite made good matching of individual plates on two surfaces possible. The habit-plane trace on a surface was taken as the best line parallel to the long axis of a plate. A measure of the accuracy afforded by this criterion was provided by a family of very large plates which appeared at intervals along the entire 2 cm length of the edge. The plates all had habit-plane traces within 2 deg of one another. Many of the plates did not show midribs and, therefore, the use of midribs7 to represent habit-plane traces was not feasible in this investigation. The over-all experimental accuracy is estimated to be better than ±2 deg. Samples for transmission examination in a Siemens Elmiskop I at 100 kv were prepared by cutting 2-mm-thick discs from the single crystal, removing about 0.5 mm by chemical polishing,14 trans-

Jan 1, 1965

By C. H. Li, R. J. Stokes, T. L. Johnson

The effect of alumina particles on the nucleation and growth of cracks through a silver- chloride matrzx has been investigated. It has been found possible to promote fibrous cracking in dispersion-strengthened silver, chloride under notch-impact conditions at temperatures at which silver chloride alone cleaves brittlely The modification) of fracture beIzavzor is thought to be due to the relaxation of hydrostatrc stress beneath a notch by the nucleation of cavities near alumina particles. In recent years, composite or dispersion-strengthened materials have been studied primarily to understand their high resistance to plastic flow particularly at elevated temperatures. Dislocation models have been developed with which it is possible to deduce with fair success the effects of interparticle distance, particle size, temperature, upon yielding and creep behavior.l-4 Much less attention has been paid to the fracture behavior of these materials (with the notable exception of common structural steels) and little is known experimentally about the manner in which inclusions affect the nucleation and growth of cracks through a matrix. Nevertheless a beginning has been made in connection with fibrous cracking in ductile matrices where inclusions appear to play an essential ro1e.5-7 During the severe localized plastic deformation which accompanies necking in a tensile test, cavities are believed to develop at inclusions; these cavities subsequently grow and coalesce by plastic flow until separation is complete. It is of interest to consider whether inclusions can affect fracture behavior under loading conditions which restrict the plasticity of the matrix itself (for example, cleavage under conditions of a high imposed strain rate at low temperatures). It is particularly interesting to study these effects in a solid which shows a spectrum of behavior ranging from fully ductile to semi-brittle behavior. Such a solid is silver chloride whose mechanical behavior depends sensitively upon temperature and strain rate.&apos;," The present paper is concerned with a study of the influence of inclusions (in the form of alumina particles) on the fracture behavior of silver chloride loaded uniaxially at low strain rates at room temper- ature and also under notch impact conditions over a wide range of temperature. In particular, it will be shown that the alumina particles can exert a startling effect on the ductile-brittle transition temperature of notched silver chloride and that the magnitude and nature of the effect depends upon both the quantity of alumina and the shape of the alumina particles. 1. EXPERIMENTAL PROCEDURE 1.1 Materials Used. Silver chloride powder of analytical reagent (AR) quality having an average particle size 6 was supplied by the Mallinckrodt Chemical Works (st. Louis, MO.). Acid washed 900 mesh alumina powder, designated A38-900, was supplied by the Norton Co. (Cambridge, Mass.). This powder was added to silver chloride in two forms: a) the as-received condition in which the individual particles were of random irregular shape; their statistical average size was 7; b) in a condition in which each particle was spherically shaped by a fusion technique. In this case, the statistical average particle size determined with the optical microscope was approximately the same (about 5p) but electron micrographic evidence indicated that many ultra fine particles were present in the spheroidized powder. 1.2 Preparation of Composite Materials. Silver chloride-alumina composites containing 2.5, 5, and 15 pct by volume of alumina were produced by the extrusion of mechanically mixed powders blended in a ball mill for 24 hr at room temperature. The mixtures were compacted at 50,000 psi at room temperature in the form of billets 3/4 in. in diameter and 1 in. long which were then extruded with a 16:l reduction ratio at 370°C through a radius-type steel die having a 5 deg lead-in angle. An extrusion temperature of 370°C was selected to ensure that all composites had sufficient plasticity to be extruded. Apart from this general requirement, the choice was arbitrary. 1.3 Microstructure of Composites. Attempts were made to check the distribution of alumina metallo-graphically by polishing transverse and longitudinal sections of the extruded rod. Specimens were wet-ground to 600 emery paper and lapped successively with 5 and 0.25-p grades of diamond paste. They were etched for 10 sec in 10 pct sodium thiosulfate solution and lightly polished in concentrated ammonium hydroxide. The most effective way to render the alumina particles and grain boundaries visible was to radiate the surface with intense white light to decorate the grain boundaries and the particle-matrix interfaces photolytically.

Jan 1, 1962

By A. A. Bauer

The ?-to-? transformation has been studied in zirconium alloys containing 22 to 70 wt pct U. In this range of compositions the ? phase can be retained by quenching. Transformation to ? occurs by a nucleation-and-growth process. The diffusion of atoms to preferred lattice sites to yield a partially ordered structure apparently controls the rate of reaction. Alpha uranium and a zirconium precipitate from the supersaturated E phase initially formed in alloys outside the equilibrium E phase composition limits. ZIRCONIUM-Uranium alloys have long been of interest for reactor-fuel applications because of the low thermal-neutron cross section of zirconium. Considerable information is available on the various properties and behavior of these alloys1 although there had been a number of areas where information was incomplete. As part of a program to provide more detailed knowledge in these areas, the presently reported investigation was undertaken. The constitutional diagram of the zirconium-uranium system is shown in Fig. 1.&apos; The system is distinguished by a region of complete solid solubility between the body-centered cubic ß-zirconium and ? uranium phases and the existence of an intermediate phase in the vicinity of 50 wt pct U. This intermediate phase, designated as E, is reported3 to have a primitive hexagonal structure with a = 5.03 and c = 3.08A. The structure is partially ordered with zirconium atoms at the 0, 0, 0 position and zirconium and uranium atoms located randomly at the 1/3, 2/3, 1/2, and 2/3, 1/3, 1/2 positions. While the E phase may be nominally designated as of UZr2 stoichio-metry, the random distribution of uranium and zirconium atoms permit a considerable range in composition. Of interest in the research performed were alloys in the range from 20 wt pct (10 at. pct) to 70 wt pct (47 at. pct) U. In this range of compositions the body-centered-cubic ? phase can be retained either completely or partially on quenching. The nature and kinetics of transformation of the ? phase were the subject of study. Proceeding concurrently with the presently reported work was an investigation by Kearns4 which has since been reported. Kearns studied alloys containing 50 to 60 wt pct U prepared from sponge zirconium. While the work reported here is for alloys prepared from crystal-bar zirconium and the techniques of study are to some extent dissimilar to those employed by Kearns, general agreement so far as results and interpretation can be reported. Experimental Techniques—Alloys were prepared and the transformation of the ? phase studied during interrupted-quench and quench-and-temper isothermal heat treatments by means of hardness measurements and X-ray diffraction and metallographic techniques. The isothermal transformation of the ? phase on quenching and tempering was investigated further employing dynamic-modulus measurements. Electrical resistivity and limited Hall coefficient measurements were also obtained as part of the study. Alloy Preparation and Heat Treatment— Alloys containing 15, 20, 22, 30, 40, 45, 50, 55, 60, and 70 wt pct U were prepared from as-reduced uranium and crystal-bar zirconium. The alloys were double arc melted by consumable-electrode are-melting techniques. The final ingots were forged and rolled at temperatures between 790" and 840oC to 1/4-in. rod and 1/8-in. sheet. Chemical analyses of the fabricated alloys were

Jan 1, 1961

By S. Weinig, J. Winter

The grain boundary adsorption of solutes as a function of bulk concentration and solution temperature was studied using internal-frictimz techniques. From the variation of the cor-responding energy of activation for the Phenomenon, the inter-actior2 energy between a solute atom and a high-angle boundary was calculated. Interaction energies in the range of 0.3 ev were obtained, and were used to obtain the actual concentration of solute at the grain boundary. In corroboralory creel, studies the direct grain boundary contribution to the total creep strain was measured. It was found that the interface creep varied with the type and magnitude of the solute adsorbed. Subscribing to the theory of their being energetically favorable sites at the grain boundary for solutes of both Positive and negative size deviations, ternaries were investigated in Which solutes of both types were present. A marked increase in the resistance to grain boundary creep was manifested. THE major difficulty which has been encountered in investigations of the grain boundary segregation of solutes has been the lack of a sufficiently sensitive method of measuring the amount of adsorbed solute at the boundary. For the general case of a high-angle boundary, no direct method of measuring the adsorption at the boundary has been found to date. Internal friction has been used in several studies of grain boundary adsorption1-3 and although it is somewhat indirect, it was demonstrated to have the necessary sensitivity. In this investigation the authors have used internal-friction techniques in conjunction with a study of the grain boundary contribution to the total creep strain. As both parts of the investigation were performed on the same specimens it was possible to combine a highly sensitive technique with a somewhat more direct method in order to obtain information about the adsorption phenomenon. From internal-friction studies the rate of increase of the activation energy was observed to be a function of the difference in size between the solute and solvent atoms. It was proposed that if Gibbs&apos; adsorption isotherm is considered, i.e., where r is the excess solute at the boundary, c is the bulk concentration, and ay/ac is the change in grain boundary energy with bulk concentration, then AH b/ac must vary in the same way as ay/ac and therefore In this way a relative measure of the grain boundary adsorption of solutes is directly obtainable from in-ternal-friction studies. If the previous work in the field of grain boundary adsorption of solutes is examined, certain apparent information is desirable if the phenomenon is to be understood. The most important questions that must be asked are as follows: 1) Is the adsorption of solutes at the grain boundary an equilibrium process? 2) Can the Mott model of the grain boundary be used as a basis of setting up an elastic interaction between the grain boundary and solute atoms? 3) Is it possible to obtain an exact measure of the excess solute at the grain boundary as a function of temperature and bulk concentration rather than merely a relative measure of the adsorption 4) Are the conclusions obtained from an indirect method such as internal-friction studies meaningful in considering gross grain boundary effects such as creep? EXPERIMENTAL PROCEDURE The material used in this investigation was Bureau of Mines "superpurity" titanium (79 Bhn—1500 kg

Jan 1, 1960

By C. G. Rhodes, D. Kramer

High-field critical transport current density (J) measurements at 4.2 °K as a Junction of applied magnetic field (H) were made on samples of cold-rolled and annealed columbium with H parallel to J. Microscopic examination of the samples revealed a well-defined planar fiber structure produced by the cold rolling. J was found to he lower when fibers are parallel to the direction of magnetic field penetration than when they are perpendicular. This effect may he a consequence of the interaction of flux movement with fiber boundaries. THE severe changes in microstructure brought about by cold working superconductors leads to profound changes in their superconducting behavior. In particular, the ability of a superconductor to carry a transport current with zero resistance (the maximum value of this current density will be called "J" in the presence of large external magnetic fields (to be referred to as "H") is greatly influenced by the microstructure. In the case of columbium, LeBlanc and Little1 and Autler et a1.2 have observed an increase in J due to cold work. LeBlanc and Little also observed an anisotropy in J in cold-rolled columbium strips, which Hake et al.3-6 have shown to depend upon the angle between H (H ? J) and the rolling plane. An increase in J due to cold work has been found in a variety of high-field superconducting alloys3&apos;4&apos;7-9 as has the anisotropy effect.10 First explanations of why cold work raised J invoked the idea that dislocations carried the high-field supercurrents,8,11 since cold working drastically increases the dislocation density and presumably the number of supercurrent paths. However, recent ideas on the nature of high-field superconductivity together with new experimental evidence reveal that the bulk of certain superconductors can remain superconducting in high fields while carrying high transport currents. These later developments have been discussed by Berlin-court and Hake12 and a comprehensive review has been prepared by Berlincourt.13 According to the ideas of Gorter14 and Anderson,15 one would expect that the influence of microstructure on high-field supercurrent density will depend on tine interaction between microstructure and penetrating flux and on the direction of the Lorentz

Jan 1, 1965

By M. Cohen, D. J. Blickwede

Quantitative observations concerning the carbide phases in high speed steel are of importance for two general reasons: (1) the carbides, being inevitable constituents of the final structure, exert a direct influence on the properties of the steel; and (2) a substantial proportion of the total alloy content is tied-up in the carbides, and hence the extent of their solution on austenitizing governs the composition of the steel matrix. The latter relationship has a vital bearing on the response of the steel to tempering as well as on its performance in subsequent service. Accordingly, in the course of a long-term study of the behavior of high speed steels, the authors were confronted with the problem of securing quantitative data on the carbide phases. The obvious method for acquiring such information is to isolate the car-bides from the steel and subject them to chemical, X ray diffraction and other measurements. There are well-known extraction techniques which involve the chemical or electrolytic solution of the less noble matrix (ferrite, marten-site or austenite), thus leaving a residue of the carbide phases. However, the results obtained must be scrutinized carefully1,2 since the carbides may be affected by the chemical or electrolytic action. It is the purpose of the present paper to describe the experiments leading to an electrolytic-extraction technique for quantitatively isolating the carbides from both I and hardened high speed steel. Particular attention is paid to the amount, as well as the composition, of the carbides so that the matrix analysis becomes ascertainable by subtraction from the overall steel composition. Illustrative results are given for the M-2 grade of tungsten-molybdenum steel. Review of the Literature The chemical method of dissolving the matrix selectively with respect to the carbides makes use of dilute non- oxidizing reagents such as hydrochloric or sulphuric acid. Although this simple procedure has led to the determination of the cementite composition,3,4 it achieved only limited success because of the interaction between the acid and the carbide residue. Some of the carbides may not only be destroyed in this way, but the hydrogen released is likely to remove part of their carbon as hydrocarbon gases. The electrolytic technique of isolating carbides has the advantage of rapidly dissolving the specimen (anode) in the presence of less reactive solutions than are practicable with the chemical method. This reduces the possibility of chemical attack on the carbides, and furthermore, the hydrogen evolved during the electrolysis is released at the cathode which is not in close proximity to the carbides. The common electrolytes adopted for this purpose are hydrochloric and sulphuric acids.5-l1 Aqueous solutions of ferrous salts have also been used.12,13 A considerable advance in experimental technique was introduced by Treje and Benedicks14 who developed a double-compartment cell for electrolytic extraction, the anode and cathode chambers being separated by a porous diaphragm. A solution of 15 pct sodium citrate, 2 pct potassium bromide and 1 pct potassium iodide was selected for the anolyte, while the catholyte consisted of a 10 pct solution of copper sulphate, with copper serving as the cathode. This type of cell has a number of desirable characteristics: 1. The anolyte has a pH value close to 7, at least at the beginning of the run. 2. The iron that dissolves from the anode-specimen forms a water-soluble complex ion with the citrate, thereby preventing the precipitation of iron hydroxide (which would contaminate the carbide residue) despite the neutrality of the solution. 3. Copper deposition instead of hydrogen evolution occurs at the cathode, and this avoids an increasing concentration of hy-droxyl ions which (in an otherwise neutral solution) might cause the precipitation of insoluble hydroxides. 4. Contamination of the anode chamber by copper sulphate is inhibited by the porous diaphragm. Houdremont and coworkers15 applied the above method (with the further refinement of excluding oxygen during the electrolysis, washing and drying) to the extraction of carbides from a series of plain carbon steels after various heat treatments. They had quantitative success only with specimens in the annealed condition, and concluded that the size and shape of the carbide particles play an important role in the isolation process, with large spheroids exhibiting the least tendency to decompose during the electrolysis. Up to the present time, the citrate double-cell has not been used to any extent for isolating the carbides of high alloy steels, apparently on the grounds that the complex carbides are more resistant than cementite to attack in the simpler acid electrolytes. In particular, Bain and Grossmann7 and Gulyaev10.10a have employed the hydrochloric acid cell for their investigations of the carbides in high speed steel.* It will be demonstrated here that this type of cell is capable of yielding quantitative results in the case of high speed steel, and actually has certain advantages over the more complicated double cell. However, in order to provide a rigorous test of the quanti-tativeness of electrolytic procedures for the problem at hand, both methods were studied in considerable detail.

Jan 1, 1950

By F. W. Schaller

TETRAGONALITY is an important aspect of the models of transformation, strengthening, and tempering of ferrous martensite. When the c/a

Jan 1, 1963

By D. L. Ritter, N. J. Grant, B. C. Giessen

Forty-six alloys covering the complete concentration range of the Nb-Rh system were examined by metallographic and X-ray methods; solubility limits of terminal ad intermediate phases and transformation and solidus temperatures were determined. There are nine intermediate phases; two eutectic, five peritectic, two eutectoid, and three peritectnid reactions were encountered. The experimental methods and the constitution diagram are described in Part I. Part 11 deals with the crys -tallography and relation of the intermediate phases. The Nb-Rh system was selected for study for three reasons: first, it was hoped that the anticipated similarity of the Nb-Rh phase diagram to the Ta-Rh1 and Ta-Ir2 diagrams treated earlier (see also Ref. 3) and to the Nb-1r4 diagram treated simultaneously would allow a crystallographic and comparative evaluation of the intermediate phases in these related systems; second, it was likely that the previous experimental methods could be carried over without significant change; and third, it was expected that the interesting mechanical properties of the a1 phase of the Ta-Rh and Ta-Ir systems would also be encountered in similar phases of the new systems, and that these phases could be investigated more closely. The phase diagram had not been treated fully in the literature; only brief surveys of some intermediate phases were found.5-7 It was attempted to cover the details of the phase boundaries, Part I, as well as to present the crystallography of the intermediate phases, Part 11. EXPERIMENTAL METHODS Specimen Preparation and Treatment. The following high-purity starting materials were used. 1) Niobium powder, 99.8 pct pure, mesh size -60 +200, from Wah Chang Corp., Albany, Ore. The analysis furnished by the supplier showed the following major impurities: Ta, <500 ppm; Zr, <500 ppm; 0, 300 ppm; Fe, 280 ppm; Ti, <I50 ppm; W, Si, <100 ppm; C, N, 30 ppm; all other impurities, <30 ppm. 2) Rhodium powder, ground sponge, 99.9+ pct pure, mesh size -80, from J. Bishop Co., Malvern,

Jan 1, 1964

By R. D. Reiswig, J. M. Dickinson

The 0s-Ir equilibrium diagram was determined. The diagram is of the simple peritectic type, with a peritectic temperature of about 2660°C. The solid miscibility gap is narrower than previously reported, the nearly vertical solvus lines occurring at about 42 and 63 wt pct 0s. Widmanstaetten figures resembling martensite in some of the two-phase alloys account for a previously suspected transformation. In view of the long history of use of such alloys, it is surprising that the 0s-Ir equilibrium diagram has not yet been completely determined. The boundaries of the miscibility gap in this system have been estimated to be between 24 and 39 wt pct 0s and 79 and 100 wt pct OS. It has been predicted3 that alloys of ruthenium, osmium, and rhenium with the fcc platinum metals should solidify peritectically in their two-phase regions. The metallographic examination of natural osmiridium alloys has been said4 to indicate, by the presence of a martensitic structure, the existence of a transformation or a phase separation. On the basis of superconducting transition temperature measurements, a 70 at. pct 0s alloy was found5 to be two-phase prior to annealing. EXPERIMENTAL The elemental components used in this work were obtained from several suppliers as sponge. The purities, stated by each supplier to be in excess of 99.8 pct, were confirmed in each case by a semiquantitative spectrographic analysis. The pure components were premelted in an inert-gas tungsten arc furnace with the evolution of some fume, crushed, and pickled for use as alloy melting stock. Upon arc melting to the final compositions, no fume evolution was observed. Because weight losses of the order of 15 mg or less were observed in preparing alloy buttons weighing 15 g, "synthetic analyses" were used in determining the compositions of the alloys. Alloys used in this investigation contained 15, 20, 33, 40, 42, 43, 45, 50, 55, 60, 63, 64, 66, 70, 79, and 80 wt pct 0s. Heat treatments of the alloy buttons and pieces thereof were performed in a previously described6 tungsten tube furnace under pressures of 105 torr or less. It was found that homogenization treatments on the specimens were essential to remove the severe coring which was present, a 3-hr treatment above 2300°C removing all the metallographi-cally visible evidence of coring. Following the various heat treatments, the specimens were "vacuum-quenched" by melting a tungsten fuse wire and allowing them to drop onto a water-cooled copper plate. In a few instances, specimens were quenched into molten tin for comparison, but no difference was apparent. Vacuum-quenched specimens cooled from 2400°C to below a red heat in less than 60 sec. Typical equilibration times varied from 3 hr above 2300°C to 88 hr near 1100°C. The utilization of successively longer equilibration times and the approach to equilibrium from both directions indicated that the times used were sufficient to give a close approach to true equilibrium. Heat-treatment temperatures were measured with a calibrated Leeds and Northrup optical pyrometer through a 0.120-in. lateral sight hole in the tungsten heater tube. It was known that the assumption of black-body conditions inside the 1-in.-diam by 10-in.-long tube was unwarranted. The empirical results of work with thermocouples and melting

Jan 1, 1964

By S. T. Wlodek

The scale md subscale reaction products were identified and their rates of formation were studied in air over the range 1600" to 2000°F (871 " to 1149°C) for periods of up to 400 hr and for hoth the solution-annealed and aged conditions. The effect of prior sltrface preparation on suhscale oxidation was also studied The general oxidation behavior of both Ni-Cr-Mo-Al-Ti type alloys was similar. A surface film of a, Al2O3, forms immediately on exposure Subsequent oxidation continued at a linear rate (QL = 55 * 5 kcal per mole) as colonies of Cr2O3 nucleated at the A12O3/gas interface Further oxidation proceeded at a paraholic rate zvhiclz could he fitted to two successive rate constants. During paraholic oxidation, and depending on temperature, the scale consisted of Cr2O3, NiCr2O4 , and TiO2 with traces of NiO. In the case of Rene 41, the activation energy of both paraholic processes was 66 * 3 kcal per mole suggesting that diffusion of cations tlzrozrgh Cr2O3 was the rate -determining process. An unusual decrease in the oxidation of Udimet 700 at 1900°F where a spinel of Ni(A1,Crh0, zuas the predominant reaction product prevented the accurate assignment of activation energies for this composition. In both alloys internal oxidation of Al2O3 commenced shortly after parabolic scaling was observed. Prolonged exposure prod7tced intemal oxidation of TiN, and in Udimet 700 a complex Mo-Ni nitride was also found. At 1900oF, the subscale reactions in Udimet 700 undergo an inversion which parallels the decrease in surface oxidation; internal oxidation ceases hut is replaced by the formation of "spherodized" 3.&apos; colonies. Surface-preparation techniqtles which introduce appreciable working, such as coarse surface grinding or grit blasting. increase the amount of alloy depletion and internal oxidation in Reni 41. The reverse is true of Udimet 700 for which electropolished or mechanically polished specimens show much more subscale oxidation than strongly worked stirfaces. The strongest commercial nickel-base alloys presently available are generic to the Ni-Cr-Mo-A1-Ti base which exploits the precipitation of Ni3(A1,Ti) as the main strengthening mechanism, while relying on solid-solution strengthening by molybdenum and chromium reinforced by the pre- cipitation of carbides to attain maximum properties. This study characterizes the oxidation behavior of Rene 41, the strongest alloy of the Ni-Cr-A1-Ti type commercially available in sheet form, and Udimet 700, whose higher aluminum and titanium content allows it to exhibit one of the more attractive combinations of high-temperature properties available in a wrought product. The scaling processes of complex, type nickel-base alloys have received relatively little attention. Malamand and vidal as well as Poulignier et al.2&apos;3 have determined the composition gradients across the metal/oxide interface produced by high-temperature oxidation and considered the effect of surface perature, Limited weight-gain data has also been published by Fere 5 for alloys of this type and Radavich6 has identified the reaction products on Udimet 500 and Inco 702 after oxidation at 1832°F. Reference can, of course, be made to the excellent reviews of Kubaschewski and Hopkins7 or Ignatov and Shamgunova8 for a summary of the data available on the oxidation of binary and ternary alloy systems which are related to the more complex alloys considered here. EXPERIMENTAL The analyses of the different commercial heats studied are given in Table I. Using the experimental procedures previously established,9 continuous weight-gain data were obtained on both heats of Rene 41 sheet (A and B) and 150-mil-thick slices of cast Udimet 700. Subscale oxidation reactions were followed by static exposure of cylindrical specimens obtained from swaged Rene 41 (Heat C) and Udimet 700 (Heats E and F). In brief, continuous weight-gain tests were performed on specimens with a surface area of 10 to 12 sq cm. These were abraded through 600 grit Sic paper, electropolished to 2p rms in an electrolyte of 10 pct H2So4 in ethanol, and lightly etched in 10 pct HCl in ethanol before final washing and rinsing in ethanol. All continuous weight-gain data were obtained in dried (-70°F dew point) flowing (1 liter per min) air to an accuracy of +0.1 mg. Subscale oxidation processes were followed by the metallographic examination of 0.5-in-diam by 1.0-in.-long specimens. After an initial center-less grinding, various additional surface treatments were employed to determine the effect of surface preparation on subscale oxidation processes. Before exposure in zirconia crucibles, all samples were lightly etched in 10 pct HCl-ethanol, washed in ethanol, and dried. The depth of internal oxidation was measured to ±0.00025 in. on unetched specimens mounted so as to provide a taper mag-

Jan 1, 1964

By C. G. Rhodes, D. Kramer

The kinetics of precipitation of transient a phase during the transformation in U-16 wt pct Mo between 400° and 550°C were studied using quantitative metallography and electrica1 resistiuity measurements. The volume percent of a phase goes through a maximum in time, corresponding to a critical degree of progress of y&apos; formation. prior to its re-solution after prolonged annealing. The fastest rate of a precipitation oc-cuvs at 500°C with a concomittant lowest peak of 9.5 vol pct a. At 450°C, 14 vol pct a, greatest fov any temperature, was observed after 24 hr witlz an associated slowest rate of formation. a precipitation at 400°C ceases after approximately 160 hr and the amount of a present remains unchanged after long times at temperature; no y&apos; was observed metallographically at this temperature. IN the U-Mo system at 16 wt pct Mo, an ordering reaction takes place below 600°C, see Fig. 1, whereupon the random bcc solid solution, y, transforms to the ordered bct phase, y&apos;."2 The new unit cell is constructed of three old unit cells somewhat distorted. While attempting to study the kinetics of this transformation it was observed that an unexpected phase was precipitating out early during the transformation anneal reaching appreciable amounts before disappearing after long times. The y&apos; appeared in the presence of this new phase and after long times constituted the whole sample. Owing to the high optical activity of this unexpected phase under polarized light, it was suspected to be the a phase. Subsequent X-ray powder pictures confirmed this belief. The kinetics of a phase formation and disappearance is the subject of this paper. EXPERIMENTAL PROCEDURE A) Alloy Preparation. Alloys for this study were prepared by vacuum induction melting normal reactor grade uranium and 99.5 wt pct Mo pellets in thoria crucibles. Two ingots were prepared, and sections of the top and bottom of each ingot were chemically analyzed for uranium and molybdenum content. The results of the analyses appear in Table I. B) Metallography. Samples of 16M were wrapped in tantalum foil, sealed in evacuated (5 X 10"6 mm of Hg) quartz capisules, and annealed at 1110"C prior to being transferred directly to the transformation temperature. They were examined metallographically after increasing times to determine the progress of the transformation at 400°, 450°, 500°, and 550°C. The samples were prepared for metallographic examination by mechanical polishing with diamond paste and electrolytic polishing with a solution of glacial acetic acid and chromic acid. Since the y&apos; phase is tetragonal, its presence can be detected by viewing the sample in polarized light. To increase the contrast between y&apos; plates, the samples were electro-etched in a 10 pct oxalic acid solution. To reveal a phase in bright field (it can be seen in polarized light in the "as-polished" state), the samples were electro-etched in a solution of citric acid and nitric acid. To determine the vol pct a phase, a variation of the one dimensional systematic point count method as described by Hilliard and cahn3 was used. The

Jan 1, 1962

By Allan T. Gwathmey, J. Bruce Wagner, Kenneth R. Lawless

Between 250°and 550°C in oxygen pressures of 10 to 760 mm Hg, the relative oxide thicknesses formed per unit time on the (100), (111), (110), and (320), decreased in this order. The predominant oxide orientation was (001)Fe3O4 and [110] Fe304 A small amount of a-Fe2O3 which exhibited a fiber pattern was observed in all oxides except those formed at 250°c in low oxygen pressures. IN order to understand the properties and behavior of thin films, particularly their role in oxidation reactions, there is needed more experimental information on their structure, composition, and kinetics of formation on clean surfaces of known geometry. The present study was undertaken to obtain such information for thin oxide films formed on single crystals of a body centered cubic metal, iron. Crystals in the form of spheres were used in order to expose all possible crystal planes to the reactant gases simultaneously. Using this procedure the relative rates of oxidation of all planes could be estimated, and those exhibiting, maximum or minimum oxidation rates could be selected for a more intensive study of composition and expitaxy. Since the three types of information were obtained from the same experiment using a single crystal substrate, any differences between rate, composition, and expitaxy on the several planes may be attributed to the influence of the substrate structure. EXPERIMENTAL The starting material for this study was Armco iron rods, 6 in. long and 3/8 or 1/2 in. in diam. The analysis was reported to be 99.8 pct Fe, with major impurities listed as carbon 0.018 pct, manganese 0.027 pct, phosphorous 0.005 pct, sulfur 0.029 pct, silicon 0.005 pct, and copper 0.11 pct. These rods were cleaned with ether and heated in an atmosphere of moist hydrogen at 950°C for three days. The purpose of this treatment was to decarburize the iron and to provide a consistent, uniform grain size for the growth of single crystals. Crystals in the form of rods, up to 1/2 in. in diam and 2 in. long, were prepared by a method similar to that reported by Leidheiser and Buck.2 Spherical crystals, 3/8 and 1/2 in. in diam and having a handle about 1/4 in. in diam by 112 in. long, were machined from the single-crystal rods. After machining, each crystal was etched in aqueous nitric acid to remove the cold-worked metal at the surface. Before each experiment, the crystal was polished mechanically with metallographic papers through number 4/0, and electropolished in a perchloric acid-acetic anhydride mixture by the method of Jacquet and Rocquet.3 The crystal was washed in running distilled water for at least 5 min. The excess water was blotted with a soft paper tissue, and the crystal was placed in an all-glass reaction vessel (See Fig. 1). The crystal was heated at 550°C in hydrogen for at least 8 hr prior to the oxidation in order to reduce any surface oxides and to help relieve any stresses in the metal. For the structure and composition studies, flat faces were cut parallel to (loo), (111), and (110) planes on the iron crystal spheres. The orientation of these faces was checked by a back-reflection X-ray diffraction technique. The faces were within 2 deg of the desired orientation. The flat faces were treated as described above except that prior to electropolishing they were given an additional polish on metallographic felt saturated with twenty-minute levigated alumina. After the crystal was heated in hydrogen for at least 8 hr, the temperature was adjusted to the desired value, and the hydrogen was evacuated. Commercial oxygen which had been purified by successively passing through tubes containing magnesium perchlorate, Ascarite and magnesium perchlorate was admitted to the desired pressure as measured by a mercury manometer. A resistance-wound furnace surrounded the oxidation chamber, and a temperature controller maintained the temperature within ±3°C. The furnace was provided with a small window for observing the crystal. The changes in thickness of the oxide films were followed by observing the interference colors. The oxidation was allowed to proceed until the desired oxide thickness was attained on a given crystal plane. The experiment was terminated by evacuating the oxidation

Jan 1, 1962

By J. L. Lytton

The flow-stress recovery of high-purity aluminurn following a 10 pct tensile prestrain was studied in terms of a fractional flow-stress recovery parameter fr. The flow-stress recovery behavior was related to the dislocation arrangements using transmissiort electron rnicvoscopy. During recovery at 120° and 160°C, nearly stable strength levels were attained, the strength level for 120°C recovery being greater than that for 160°C. This stabilization of flow stress was related to the formation of meta-stable dislocation networks bounding nearly perfect cells. Both network formation and the annealing of dislocation loops were found to be recovery mechanisms, and the stronger metastable strength level joy 120°C recovery was related to a smaller average cell size. Analysis of the networks was consistent with the reaction of sets of dislocations with a/2 (110) Burgers vector to give product Burgers DURING isothermal annealing of cold-worked metals, a degree of softening occurs without re-crystallization, and the processes responsible for this change are termed recovery processes. During recovery annealing, the dislocations generated during cold work become rearranged into low-energy configurations, and as much as 50 pct of the stored energy is released."&apos; The relationship between this rearrangement of dislocations and mechanical behavior is of considerable importance, since the dislocation substructures formed during recovery provide a significant degree of low-temperature strength3j4 and can favorably alter the course of primary creep at high temperatures.4 The purpose of the present study was to relate the flow-stress recovery behavior of high-purity aluminum to the substructural modifications that occur. Electron transmission microscopy was therefore employed for direct observation of dislocation substructures at various stages of recovery following 10 pct prestrain. Several investigators5-&apos; have proposed that dislocations can become rearranged or lost during the preparation of thin foils. It was found early in the present study that the dislocation structures in the thicker regions of the foils changed in a systematic way during the course of recovery. Therefore, it is unlikely that substantial losses or rearrangements occurred during thinning. This point will be discussed in more detail later. The results of various investigators indicate that recovery processes in fcc metals can result in release of 50 pct or more of the total energy stored in the as-prestrained metal, this percentage decreasing with increasing prestrain.&apos; Alloying elements or impurities tend to increase this percentage. The release of stored energy of fcc metals during recovery appears to occur by 1) annealing of point defects if the deformation occurred at sufficiently low temperaturesg and 2) rearrangement of dislocations into low-energy Configurations.1,2In bcc metals, the annealing of dislocation loops has also been observed during recovery after prestrain,10-12 and it has been proposed that this is a recovery mechanism for unidirectionally strained fcc metals.&apos; The density of dislocations in bcc metals has not been observed to decrease appreciably during recovery,10 although the formation of regular dislocation networks has been observed. has shown that the formation of such networks can result in elimination of long-range stresses and can lead to significant release of stored energy without dislocation annihilation. It might thus be expected that network formation is a significant recovery mechanism in fcc metals, although extensive network formation has apparently not been reported in controlled recovery experiments. The formation of sub-boundaries in aluminum has been observed by various investigators13&apos;17 during recovery studies of aluminum, but the structure of these boundaries was not resolved. In this regard, it is significant to note that Bailey and Hirsch,&apos; using transmission electron microscopy, detected no network or sub-boundary formation during recovery of 99.99 pct Ag. Furthermore, Clarebrough et al.2 found no such rearrangements during recovery of copper. EXPERIMENTAL PROCEDURE The high-purity aluminum used in this investigation was obtained in the form of 0.125-in.-thick sheet. Spectrographic analysis revealed that the sheet was 99.995 pct A1 with the following weight-percent impurities: 0.001 Cu, 0.002 Fe, 0.001 Si, and 0.0004 Mg. The as-received sheet was in the heavily cold-rolled condition. The as-received sheet was cold-rolled at room temperature to 0.040-in.-thick sheet in the longitudinal direction, which was the original rolling

Jan 1, 1965

By J. B. Clark

In 1933, R. paris1 published a phase diagram for the entire Mg-Ca-Zn system. He reported the existence of a ternary intermetallic phase, Mg5Zn5Ca2, which formed a quasi-binary with the magnesium solid solution. Since then, no extensive work has been reported on the system. Recently however, indications of the existence of a second ternary in-termetallic phase in equilibrium with the magnesium solid solution led to a reinvestigation of the solid phase equilibria involving the magnesium solid solution. The 335°C (635°F) isothermal section was chosen for study. Metallography and powder X-ray diffraction were selected as the best mutually corroborating methods for determining the solid phase constitution. Seventy-six alloys were prepared from singly sublimed (99.95 pct) magnesium, electrolytic (99.95 pct) zinc and USP calcium. The analyses of some of the alloys are shown in Fig. 1. The alloys were melted in a graphite crucible under a chloride flu and chill cast in a split graphite mold. Dif-fusion couples (see Fig. 2) were prepared by casting molten Mg-20 wt pct Zn alloy around a cylinder of Mg-30 wt pct Ca alloy. The alloy samples and the diffusion couples were sealed under argon in Pyrex vials and annealed in a furnace capable of controlling within 1/2°C of 335°C. At the conclusion of the anneal, the alloy samples were quenched in ice water and the diffusion couples were air cooled. Procedures standard for magnesium alloys were used for metallographic examination. Powder X-ray diffraction patterns were taken on a G. E. camera with a 14.32 cm dim using nickel-filtered copper radiation. The redetermined 335°C (635°) section of the Mg-Ca-Zn phase diagram is shown in Fig. 1. TWO ternary intermetallic phases, designated w and

Jan 1, 1962